CN107129268A - 德化葱根白瓷器及其制备工艺 - Google Patents
德化葱根白瓷器及其制备工艺 Download PDFInfo
- Publication number
- CN107129268A CN107129268A CN201710474640.XA CN201710474640A CN107129268A CN 107129268 A CN107129268 A CN 107129268A CN 201710474640 A CN201710474640 A CN 201710474640A CN 107129268 A CN107129268 A CN 107129268A
- Authority
- CN
- China
- Prior art keywords
- green onion
- onion root
- dehua
- parts
- ceramic whiteware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于陶瓷制品领域，具体地说，本发明涉及一种德化葱根白瓷器及制备工艺。本发明提供的德化葱根白瓷器，所制备的德化葱根白瓷器白度在83‑85度之间、吸水率为0、透光度大于15％(1毫米)，白色纯净、釉面滋润，该德化葱根白瓷器精选德化本地的原料作为烧制葱根白瓷器的原料，并对原料的化学组分进行严格的把控，坯体和釉料的原料中引入蔷薇水晶，不但可提高原料中的二氧化硅含量，而且蔷薇水晶有的天然微量的Mn和Ti可提升坯体和釉面的温润度，使得颜色滋润、釉面柔和，具有与传统的德化葱根白瓷器最为接近的艺术效果。
Description
技术领域
本发明属于陶瓷制品领域，具体地说，本发明涉及一种德化葱根白瓷器及制备工艺。
背景技术
德化白瓷，萌芽于宋元，弛誉于明代，延制于清初，在我国白瓷系统中具有独特的风格，在陶瓷发展史上占有重要地位，在国际上有“东方艺术”之声誉。明清时期的德化白瓷，以含铁量低的瓷坯施以透明釉烧制而成。明代德化白瓷胎骨洁白，坚实致密，其胎釉的技术工艺极力追求玉器质感的完美性，在琳琅满目的瓷坛上独树一帜。根据瓷色的不同，又分别为葱根白、象牙白、葱根白、等。
葱根白瓷是的德化白瓷中较小众的品种之一，大多的德化白瓷如葱根白、象牙白的瓷色白中蕴黄、润如油脂，而葱根白瓷色纯白洁净，宛如葱根，其白度更高、透光率好，明代时葱根白就是德化白瓷中的珍品，但存世量极少。传统葱根白瓷的原料及烧制工艺失传，而现有白瓷器通过化学釉料的组合虽然能在白度上达到传统葱根白瓷的白度甚至更高，但在色泽上缺乏德化白瓷传统的润度、发色呆板，而且传统的葱根白瓷也非白度越高越好。
通过对陶瓷原料控制和烧成工艺上的改良是传承和推广传统德化葱根白瓷器的必要手段，在改良的过程中必须最大限度的保证经改良所生产出的瓷器与传统的德化葱根白瓷器具有最为接近的艺术效果，同时降低葱根白瓷器的成本、提高烧成率，在改良的过程中对原料的选择和烧制工艺的控制是必须解决的技术难题。
发明内容
为了解决上述问题，提供一种与传统德化白瓷中葱根白瓷器的釉面效果最为接近的陶瓷制品。
为实现上述目的，德化葱根白瓷器，其特征在于，包括葱根白坯体和葱根白釉料，所述葱根白坯体，其重量份如下：德化金竹坑高岭土52-55份、钾长石27-30份、德化石英10-13份、蔷薇水晶1-5份、骨灰1-5份；且坯体配方化学组分如下：K2O 3.5-3.8％、Na2O 1.0-1.3％、Al2O3 24-25％、Fe2O3 0.01-0.03％、SiO2 65-68％、Mn 0.01-0.03％、Ti 0.02-0.03％、I.L 5-6％；所述葱根白釉料，其重量份如下：钾长石42-45份、石英32-35份、德化阳山石灰石12-14份、蔷薇水晶6-8份、德化高岭土2-5份。
优化的，葱根白釉料，其化学成份如下：K2O 4.7-4.9％、Na2O 1.5-1.7％、CaO 7-7.3％、Al2O3 11-12％、Fe2O3 0.03-0.05％、SiO2 67-69％、Mn 0.03-0.05％、Ti 0.03-0.05％、I.L 7.5-8％。
优化的，所述葱根白坯体，其重量份如下：葱根白坯体，其重量份如下：德化金竹坑高岭土53份、钾长石28份、德化石英12份、蔷薇水晶4份、骨灰3份；且坯体配方化学组分如下：K2O 3.5％、Na2O 1.1％、Al2O3 24.5％、Fe2O3.0.03％、SiO2.65.5％、Mn 0.02％、Ti0.03％、I.L 5.32％。
优化的，葱根白釉料，其重量份如下：钾长石44份、石英33份、德化阳山石灰石13份、蔷薇水晶7份、德化高岭土3份。
优化的，葱根白釉料，化学成份如下：K2O 4.8％、Na2O 1.5％、CaO 7.1％、Al2O311.1％、Fe2O3.0.03％、SiO2.67.5％、Mn 0.03％、Ti 0.05％、I.L 7.89％。
德化葱根白瓷器的制备工艺，其特征在于，制备上述的德化葱根白瓷器，具体步骤如下：
步骤1，按葱根白坯体和葱根白釉料原料配方称重配料，原料分别粉碎、混合、湿法球磨，制得葱根白坯浆和葱根白釉浆；
步骤2，将步骤1制得的葱根白坯浆和葱根白釉浆经过磁选机多次除铁，至葱根白坯浆和葱根白釉浆中的含铁量低于0.05％；
步骤3，使用步骤2制得的葱根白坯浆原料制成陶瓷坯体；
步骤4，将陶瓷坯体放入窑炉中素烧，获得陶瓷素坯；
步骤5，在陶瓷素坯表面施葱根白釉料；
步骤4，待陶瓷素坯上的釉料干燥后放入窑炉中，在氧化气氛中烧制成型，烧成温度为1350-1360℃。
进一步的，步骤1中葱根白坯体湿球磨时，原料在球磨机中湿法研磨3-5小时，研磨介质为水，原料：球：水＝0.8:1:1-1.2。
进一步的，步骤1中葱根白釉料湿球磨时候，原料在球磨机中湿法研磨4-6小时，研磨介质为水，原料：球：水＝0.8-1:1.2-1.5:2。
进一步的，步骤2中磁选机的磁场强度为20000GS。
进一步的，所述步骤4中烧成控制如下：
低温阶段：窑炉内由常温升至300℃，烧窑时间0.3-0.5小时；
分解氧化阶段：窑炉内升温至950℃，烧窑时间4-6小时；
高温强还原阶段：窑炉内升温至1350℃，烧窑时间3-4小时；
高火保温阶段：窑炉内升温至1355±5℃，烧窑时间1-2小时；
自然冷却阶段：窑炉内冷却至60-30℃，冷却时间延长至8小时以上。
由上述对本发明的描述可知，本发明提供的德化葱根白瓷器，所制备的德化葱根白瓷器白度在83-85度之间、吸水率为0、透光度大于15％(1毫米)，白色纯净、釉面滋润，该德化葱根白瓷器精选德化本地的原料作为烧制葱根白瓷器的原料，并对原料的化学组分进行严格的把控，坯体和釉料的原料中引入蔷薇水晶，不但可提高原料中的二氧化硅含量，而且蔷薇水晶有的天然微量的Mn和Ti可提升坯体和釉面的温润度，使得颜色滋润、釉面柔和，具有与传统的德化葱根白瓷器最为接近的艺术效果。
具体实施方式
以下通过具体实施方式对本发明作进一步的描述。
德化葱根白瓷器，其特征在于，包括葱根白坯体和葱根白釉料；
葱根白坯体，其重量份如下：德化金竹坑高岭土52-55份、钾长石27-30份、德化石英10-13份、蔷薇水晶1-5份、骨灰1-5份；且坯体配方化学组分如下：K2O 3.5-3.8％、Na2O1.0-1.3％、Al2O3 24-25％、Fe2O3 0.01-0.03％、SiO265-68％、Mn 0.01-0.03％、Ti 0.02-0.03％、I.L 5-6％；
葱根白釉料，其重量份如下：钾长石42-45份、石英32-35份、德化阳山石灰石12-14份、蔷薇水晶6-8份、德化高岭土2-5份；且釉料其化学成份如下：K2O 4.7-4.9％、Na2O 1.5-1.7％、CaO 7-7.3％、Al2O3 11-12％、Fe2O3 0.03-0.05％、SiO2 67-69％、Mn 0.03-0.05％、Ti 0.03-0.05％、I.L 7.5-8％。
具体实施例一：
德化葱根白瓷器，其特征在于，包括葱根白坯体和葱根白釉料；
其葱根白坯体，其重量份如下：葱根白坯体，其重量份如下：德化金竹坑高岭土53份、钾长石28份、德化石英12份、蔷薇水晶4份、骨灰3份；且坯体配方化学组分如下：K2O3.5％、Na2O 1.1％、Al2O3 24.5％、Fe2O3.0.03％、SiO2.65.5％、Mn 0.02％、Ti 0.03％、I.L5.32％；
葱根白釉料，其重量份如下：钾长石44份、石英33份、德化阳山石灰石13份、蔷薇水晶7份、德化高岭土3份；且葱根白釉料化学成份如下：K2O 4.8％、Na2O 1.5％、CaO 7.1％、Al2O3 11.1％、Fe2O3.0.03％、SiO2.67.5％、Mn 0.03％、Ti0.05％、I.L 7.89％。
具体实施例二：
德化葱根白瓷器，其特征在于，包括葱根白坯体和葱根白釉料；
葱根白坯体，其重量份如下：德化金竹坑高岭土54份、钾长石28份、德化石英11份、蔷薇水晶3份、骨灰4份；且坯体配方化学组分如下：K2O 3.7％、Na2O 1.2％、Al2O3 24.3％、Fe2O3 0.02％、SiO2 65％、Mn 0.03％、Ti 0.02％、I.L 5.73％；
葱根白釉料，其重量份如下：钾长石44份、石英33份、德化阳山石灰石13份、蔷薇水晶7份、德化高岭土3份；且釉料其化学成份如下：K2O 4.75％、Na2O 1.66％、CaO 7.2％、Al2O3 11.5％、Fe2O3 0.04％、SiO2 67.2％、Mn 0.04％、Ti 0.05％、I.L 7.56％。
德化葱根白瓷器的制备工艺，其特征在于，制备上述的德化葱根白瓷器，具体步骤如下：
步骤1，按葱根白坯体和葱根白釉料原料配方称重配料，原料分别粉碎、混合、湿法球磨，制得葱根白坯浆和葱根白釉浆，葱根白坯体湿球磨时，原料在球磨机中湿法研磨3-5小时，研磨介质为水，原料：球：水＝0.8:1:1-1.2，葱根白釉料湿球磨时候，原料在球磨机中湿法研磨4-6小时，研磨介质为水，原料：球：水＝0.8-1:1.2-1.5:2；
步骤2，将步骤1制得的葱根白坯浆和葱根白釉浆经过磁选机多次除铁，至葱根白坯浆和葱根白釉浆中的含铁量低于0.05％，磁选机的磁场强度为20000GS；
步骤3，使用步骤2制得的葱根白坯浆原料制成陶瓷坯体；
步骤4，将陶瓷坯体放入窑炉中素烧，获得陶瓷素坯；
步骤5，在陶瓷素坯表面施葱根白釉料；
步骤4，待陶瓷素坯上的釉料干燥后放入窑炉中，在氧化气氛中烧制成型，烧成温度为1350-1360℃，烧成控制如下：
低温阶段：窑炉内由常温升至300℃，烧窑时间0.3-0.5小时；
分解氧化阶段：窑炉内升温至950℃，烧窑时间4-6小时；
高温强还原阶段：窑炉内升温至1350℃，烧窑时间3-4小时；
高火保温阶段：窑炉内升温至1355±5℃，烧窑时间1-2小时；
自然冷却阶段：窑炉内冷却至60-30℃，冷却时间延长至8小时以上。
具体实施例一：
步骤1，按葱根白坯体和葱根白釉料原料配方称重配料，原料分别粉碎、混合、湿法球磨，制得葱根白坯浆和葱根白釉浆，葱根白坯体湿球磨时，原料在球磨机中湿法研磨4小时，研磨介质为水，原料：球：水＝0.8:1:1.1，葱根白釉料湿球磨时候，原料在球磨机中湿法研磨6小时，研磨介质为水，原料：球：水＝0.8:1.4:2；
步骤2，将步骤1制得的葱根白坯浆和葱根白釉浆经过磁选机多次除铁，至葱根白坯浆和葱根白釉浆中的含铁量低于0.05％，磁选机的磁场强度为20000GS；
步骤3，使用步骤2制得的葱根白坯浆原料制成陶瓷坯体；
步骤4，将陶瓷坯体放入窑炉中素烧，获得陶瓷素坯；
步骤5，在陶瓷素坯表面施葱根白釉料；
步骤4，待陶瓷素坯上的釉料干燥后放入窑炉中，在氧化气氛中烧制成型，烧成温度为1360℃，烧成控制如下：
低温阶段：窑炉内由常温升至300℃，烧窑时间0.5小时；
分解氧化阶段：窑炉内升温至950℃，烧窑时间5小时；
高温强还原阶段：窑炉内升温至1350℃，烧窑时间4小时；
高火保温阶段：窑炉内升温至1360℃，烧窑时间1小时；
自然冷却阶段：窑炉内冷却至60-30℃，冷却时间延长至8小时以上。
具体实施例一、二所制备的德化葱根白瓷器白度在83-85度之间、吸水率为0、透光度大于15％(1毫米)，白色纯净、釉面滋润，该德化葱根白瓷器精选德化本地的原料作为烧制葱根白瓷器的原料，并对原料的化学组分进行严格的把控，坯体和釉料的原料中引入蔷薇水晶，不但可提高原料中的二氧化硅含量，而且蔷薇水晶有的天然微量的Mn和Ti可提升坯体和釉面的温润度，使得颜色滋润、釉面柔和，具有与传统的德化葱根白瓷器最为接近的艺术效果。
上述仅为本发明的几个具体实施方式，但本发明的设计构思并不局限于此，凡利用此构思对本发明进行非实质性的改动，均应属于侵犯本发明保护范围的行为。
Claims (10)
1.德化葱根白瓷器，其特征在于，包括葱根白坯体和葱根白釉料，
所述葱根白坯体，其重量份如下：德化金竹坑高岭土52-55份、钾长石27-30份、德化石英10-13份、蔷薇水晶1-5份、骨灰1-5份；
且坯体配方化学组分如下：K2O 3.5-3.8％、Na2O 1.0-1.3％、Al2O3 24-25％、Fe2O30.01-0.03％、SiO2 65-68％、Mn 0.01-0.03％、Ti 0.02-0.03％、I.L 5-6％；
所述葱根白釉料，其重量份如下：钾长石42-45份、石英32-35份、德化阳山石灰石12-14份、蔷薇水晶6-8份、德化高岭土2-5份。
2.根据权利要求1所述的德化葱根白瓷器，其特征在于，所述葱根白釉料，其化学成份如下：K2O 4.7-4.9％、Na2O 1.5-1.7％、CaO 7-7.3％、Al2O3 11-12％、Fe2O3 0.03-0.05％、SiO2 67-69％、Mn 0.03-0.05％、Ti 0.03-0.05％、I.L 7.5-8％。
3.根据权利要求1或2所述的德化葱根白瓷器，其特征在于，所述葱根白坯体，其重量份如下：葱根白坯体，其重量份如下：德化金竹坑高岭土53份、钾长石28份、德化石英12份、蔷薇水晶4份、骨灰3份；且坯体配方化学组分如下：K2O 3.5％、Na2O 1.1％、Al2O3 24.5％、Fe2O3.0.03％、SiO2.65.5％、Mn 0.02％、Ti 0.03％、I.L 5.32％。
4.根据权利要求3所述的德化葱根白瓷器，其特征在于，所述葱根白釉料，其重量份如下：钾长石44份、石英33份、德化阳山石灰石13份、蔷薇水晶7份、德化高岭土3份。
5.根据权利要求4所述的德化葱根白瓷器，其特征在于：葱根白釉料，化学成份如下：K2O4.8％、Na2O 1.5％、CaO 7.1％、Al2O3 11.1％、Fe2O3.0.03％、SiO2.67.5％、Mn 0.03％、Ti0.05％、I.L 7.89％。
6.德化葱根白瓷器的制备工艺，其特征在于，制备权利要求1-5所述的德化葱根白瓷器，具体步骤如下：
步骤1，按葱根白坯体和葱根白釉料原料配方称重配料，原料分别粉碎、混合、湿法球磨，制得葱根白坯浆和葱根白釉浆；
步骤2，将步骤1制得的葱根白坯浆和葱根白釉浆经过磁选机多次除铁，至葱根白坯浆和葱根白釉浆中的含铁量低于0.05％；
步骤3，使用步骤2制得的葱根白坯浆原料制成陶瓷坯体；
步骤4，将陶瓷坯体放入窑炉中素烧，获得陶瓷素坯；
步骤5，在陶瓷素坯表面施葱根白釉料；
步骤4，待陶瓷素坯上的釉料干燥后放入窑炉中，在氧化气氛中烧制成型，烧成温度为1350-1360℃。
7.根据权利要求6所述的德化葱根白瓷器的制备工艺，其特征在于：所述步骤1中葱根白坯体湿球磨时，原料在球磨机中湿法研磨3-5小时，研磨介质为水，原料：球：水＝0.8:1:1-1.2。
8.根据权利要求6或7所述的德化葱根白瓷器的制备工艺，其特征在于：所述步骤1中葱根白釉料湿球磨时候，原料在球磨机中湿法研磨4-6小时，研磨介质为水，原料：球：水＝0.8-1:1.2-1.5:2。
9.根据权利要求6所述的德化葱根白瓷器的制备工艺，其特征在于：所述步骤2中磁选机的磁场强度为20000GS。
10.根据权利要求6所述的德化葱根白瓷器的制备工艺，其特征在于：所述步骤4中烧成控制如下：
低温阶段：窑炉内由常温升至300℃，烧窑时间0.3-0.5小时；
分解氧化阶段：窑炉内升温至950℃，烧窑时间4-6小时；
高温强还原阶段：窑炉内升温至1350℃，烧窑时间3-4小时；
高火保温阶段：窑炉内升温至1355±5℃，烧窑时间1-2小时；
自然冷却阶段：窑炉内冷却至60-30℃，冷却时间延长至8小时以上。