CN108841175A - 多孔活性碳/MnS/聚吡咯三元复合纳米纤维的制备方法及用途 - Google Patents
多孔活性碳/MnS/聚吡咯三元复合纳米纤维的制备方法及用途 Download PDFInfo
- Publication number
- CN108841175A CN108841175A CN201810515517.2A CN201810515517A CN108841175A CN 108841175 A CN108841175 A CN 108841175A CN 201810515517 A CN201810515517 A CN 201810515517A CN 108841175 A CN108841175 A CN 108841175A
- Authority
- CN
- China
- Prior art keywords
- active carbon
- mns
- porous active
- polypyrrole
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (8)