CN108367924B - 用于固体钠离子电池组的具有nasicon结构的电解质材料及其制造方法 - Google Patents

用于固体钠离子电池组的具有nasicon结构的电解质材料及其制造方法 Download PDF

Info

Publication number
CN108367924B
CN108367924B CN201680054870.4A CN201680054870A CN108367924B CN 108367924 B CN108367924 B CN 108367924B CN 201680054870 A CN201680054870 A CN 201680054870A CN 108367924 B CN108367924 B CN 108367924B
Authority
CN
China
Prior art keywords
sio
powder
sodium
process according
calcined
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201680054870.4A
Other languages
English (en)
Chinese (zh)
Other versions
CN108367924A (zh
Inventor
Q.马
F.蒂茨
S.纳卡什
O.吉永
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Forschungszentrum Juelich GmbH
Original Assignee
Forschungszentrum Juelich GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Forschungszentrum Juelich GmbH filed Critical Forschungszentrum Juelich GmbH
Publication of CN108367924A publication Critical patent/CN108367924A/zh
Application granted granted Critical
Publication of CN108367924B publication Critical patent/CN108367924B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Images

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/056—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes
    • H01M10/0561—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes the electrolyte being constituted of inorganic materials only
    • H01M10/0562—Solid materials
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B25/00—Phosphorus; Compounds thereof
    • C01B25/16—Oxyacids of phosphorus; Salts thereof
    • C01B25/26—Phosphates
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B33/00—Silicon; Compounds thereof
    • C01B33/20—Silicates
    • C01B33/32—Alkali metal silicates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/16—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/447—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on phosphates, e.g. hydroxyapatite
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/62605—Treating the starting powders individually or as mixtures
    • C04B35/62645—Thermal treatment of powders or mixtures thereof other than sintering
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/64—Burning or sintering processes
    • C04B35/645—Pressure sintering
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B1/00—Conductors or conductive bodies characterised by the conductive materials; Selection of materials as conductors
    • H01B1/06—Conductors or conductive bodies characterised by the conductive materials; Selection of materials as conductors mainly consisting of other non-metallic substances
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/054—Accumulators with insertion or intercalation of metals other than lithium, e.g. with magnesium or aluminium
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/058—Construction or manufacture
    • H01M10/0585—Construction or manufacture of accumulators having only flat construction elements, i.e. flat positive electrodes, flat negative electrodes and flat separators
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3201—Alkali metal oxides or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3224—Rare earth oxide or oxide forming salts thereof, e.g. scandium oxide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3244—Zirconium oxides, zirconates, hafnium oxides, hafnates, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3418—Silicon oxide, silicic acids or oxide forming salts thereof, e.g. silica sol, fused silica, silica fume, cristobalite, quartz or flint
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/44—Metal salt constituents or additives chosen for the nature of the anions, e.g. hydrides or acetylacetonate
    • C04B2235/442—Carbonates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/44—Metal salt constituents or additives chosen for the nature of the anions, e.g. hydrides or acetylacetonate
    • C04B2235/443—Nitrates or nitrites
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/44—Metal salt constituents or additives chosen for the nature of the anions, e.g. hydrides or acetylacetonate
    • C04B2235/447—Phosphates or phosphites, e.g. orthophosphate or hypophosphite
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/44—Metal salt constituents or additives chosen for the nature of the anions, e.g. hydrides or acetylacetonate
    • C04B2235/449—Organic acids, e.g. EDTA, citrate, acetate, oxalate
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/48—Organic compounds becoming part of a ceramic after heat treatment, e.g. carbonising phenol resins
    • C04B2235/483—Si-containing organic compounds, e.g. silicone resins, (poly)silanes, (poly)siloxanes or (poly)silazanes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/60—Aspects relating to the preparation, properties or mechanical treatment of green bodies or pre-forms
    • C04B2235/604—Pressing at temperatures other than sintering temperatures
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/74—Physical characteristics
    • C04B2235/77—Density
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M2300/00—Electrolytes
    • H01M2300/0017—Non-aqueous electrolytes
    • H01M2300/0065—Solid electrolytes
    • H01M2300/0068—Solid electrolytes inorganic
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
    • Y02P70/50—Manufacturing or production processes characterised by the final manufactured product

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Organic Chemistry (AREA)
  • Ceramic Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Structural Engineering (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • General Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Conductive Materials (AREA)
  • Secondary Cells (AREA)
  • Silicon Compounds (AREA)
CN201680054870.4A 2015-10-09 2016-08-27 用于固体钠离子电池组的具有nasicon结构的电解质材料及其制造方法 Active CN108367924B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
DE102015013155.9 2015-10-09
DE102015013155.9A DE102015013155A1 (de) 2015-10-09 2015-10-09 Elektrolytmaterial mit NASICON-Struktur für Feststoff-Natriumionenbatterien sowie Verfahren zu deren Herstellung
PCT/DE2016/000332 WO2017059838A1 (de) 2015-10-09 2016-08-27 Elektrolytmaterial mit nasicon-struktur für feststoff-natriumionenbatterien sowie verfahren zu deren herstellung

Publications (2)

Publication Number Publication Date
CN108367924A CN108367924A (zh) 2018-08-03
CN108367924B true CN108367924B (zh) 2022-02-22

Family

ID=57178173

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201680054870.4A Active CN108367924B (zh) 2015-10-09 2016-08-27 用于固体钠离子电池组的具有nasicon结构的电解质材料及其制造方法

Country Status (6)

Country Link
US (1) US10566654B2 (enExample)
EP (1) EP3359487A1 (enExample)
JP (1) JP6936790B2 (enExample)
CN (1) CN108367924B (enExample)
DE (1) DE102015013155A1 (enExample)
WO (1) WO2017059838A1 (enExample)

Families Citing this family (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110635164B (zh) * 2018-06-22 2021-07-20 比亚迪股份有限公司 一种固态电解质以及制备方法和锂离子电池
CN108695552B (zh) * 2018-07-11 2021-04-20 中国科学院宁波材料技术与工程研究所 Nasicon结构钠离子固体电解质、其制备方法及固态钠离子电池
CN108933282B (zh) * 2018-07-11 2021-01-22 中国科学院宁波材料技术与工程研究所 Nasicon结构钠离子固体电解质、其制备方法及固态钠离子电池
CN109860700B (zh) * 2019-01-16 2022-07-01 广东工业大学 一种Nasicon结构钠离子固体电解质及其制备方法和应用
DE102019000841A1 (de) * 2019-02-06 2020-08-06 Forschungszentrum Jülich GmbH Festkörperbatterie sowie Verfahren zur Herstellung derselben
ES2955404T3 (es) 2020-03-24 2023-11-30 Evonik Operations Gmbh Procedimiento para la producción de alcoholatos de metal alcalino en una célula electrolítica de tres cámaras
EP3885471B1 (de) 2020-03-24 2023-07-19 Evonik Operations GmbH Verbessertes verfahren zur herstellung von natriumalkoholaten
CN113683119A (zh) * 2020-05-18 2021-11-23 天津理工大学 具有nasicon结构的钠离子固态电解质的制备方法和其应用
DE102020214769A1 (de) 2020-11-25 2022-05-25 Forschungszentrum Jülich GmbH Festkörperzelle und zugehöriges Herstellungsverfahren
ES2958263T3 (es) 2021-02-11 2024-02-06 Evonik Operations Gmbh Procedimiento de producción de alcoholatos de metales alcalinos en una celda electrolítica de tres cámaras
CN113113664B (zh) * 2021-03-09 2023-04-28 北京理工大学 一种改性nasicon型钠离子陶瓷电解质及其制备方法和应用
EP4112780B1 (de) 2021-06-29 2023-08-02 Evonik Operations GmbH Dreikammerelektrolysezelle zur herstellung von alkalimetallalkoholaten
EP4112778B8 (de) 2021-06-29 2024-01-17 Evonik Operations GmbH Dreikammerelektrolysezelle zur herstellung von alkalimetallalkoholaten
HUE064033T2 (hu) 2021-06-29 2024-02-28 Evonik Operations Gmbh Háromkamrás elektrolízis cella alkálifémalkoholátok elõállítására
EP4124677A1 (de) 2021-07-29 2023-02-01 Evonik Functional Solutions GmbH Bruchstabile trennwand umfassend festelektrolytkeramiken für elektrolysezellen
EP4124675B1 (de) 2021-07-29 2024-07-10 Evonik Operations GmbH Bruchstabile trennwand umfassend festelektrolytkeramiken für elektrolysezellen
EP4134472A1 (de) 2021-08-13 2023-02-15 Evonik Functional Solutions GmbH Verfahren zur herstellung von alkalimetallalkoholaten in einer elektrolysezelle
EP4144890A1 (de) 2021-09-06 2023-03-08 Evonik Functional Solutions GmbH Verfahren zur herstellung von alkalimetallalkoholaten in einer elektrolysezelle
EP4144888A1 (de) 2021-09-06 2023-03-08 Evonik Functional Solutions GmbH Verfahren zur herstellung von alkalimetallalkoholaten in einer elektrolysezelle
EP4144889A1 (de) 2021-09-06 2023-03-08 Evonik Functional Solutions GmbH Verfahren zur herstellung von alkalimetallalkoholaten in einer elektrolysezelle
CN114105155B (zh) * 2021-11-29 2023-06-27 四川龙蟒磷化工有限公司 一种复合钠离子电池材料的制备方法
CN114267872A (zh) * 2021-12-13 2022-04-01 溧阳天目先导电池材料科技有限公司 改性nasicon结构钠离子固态电解质材料及其制备方法和应用
EP4504829A1 (de) 2022-04-04 2025-02-12 Evonik Operations GmbH Verbessertes verfahren zur depolymerisierung von polyethylenterephthalat
CN114824216B (zh) * 2022-04-28 2024-10-29 武汉工程大学 一种多元素掺杂的钠离子电池正极材料及其制备方法和应用
CN120390831A (zh) 2022-10-19 2025-07-29 赢创运营有限公司 用于聚对苯二甲酸乙二醇酯解聚的改进方法
JPWO2024128127A1 (enExample) * 2022-12-15 2024-06-20
JP2025018308A (ja) * 2023-07-26 2025-02-06 日本化学工業株式会社 Ｎａｓｉｃｏｎ構造を有するナトリウム化合物
CN117246988A (zh) * 2023-09-21 2023-12-19 东营昆宇电源科技有限公司 一种Sc掺杂NASICON型钠离子电池正极材料的制备方法及应用
CN117438641B (zh) * 2023-12-19 2024-03-01 江苏蓝固新能源科技有限公司 一种固态电解质材料及其制备方法和应用
CN119029160B (zh) * 2024-08-22 2025-05-09 湖北宜化化工科技研发有限公司 一种具有高首效、长循环的黑磷基储钠负极片的制备方法及应用

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3330697A (en) 1963-08-26 1967-07-11 Sprague Electric Co Method of preparing lead and alkaline earth titanates and niobates and coating method using the same to form a capacitor
JP2009523192A (ja) * 2006-01-11 2009-06-18 セラマテック・インク アルカリイオン伝導セラミックス膜を使用したバイオディーゼルの製造方法
US8338038B2 (en) 2008-09-12 2012-12-25 Ceramatec, Inc Electrochemical cell comprising ionically conductive membrane and porous multiphase electrode
US8246863B2 (en) * 2009-06-26 2012-08-21 Ceramatec, Inc. Alkali metal super ionic conducting ceramic
US20150364787A1 (en) * 2011-12-06 2015-12-17 Hui Zhang Composite Electrolytes for Low Temperature Sodium Batteries
WO2014052439A1 (en) 2012-09-25 2014-04-03 University Of Maryland, College Park High conductivity nasicon electrolyte for room temperature solid- state sodium ion batteries
US9039918B2 (en) * 2013-01-16 2015-05-26 Ceramatec, Inc. Lithium-ion-conducting materials
KR20250122538A (ko) * 2013-10-07 2025-08-13 퀀텀스케이프 배터리, 인코포레이티드 Li 이차 전지용 가넷 물질

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
"Sol–gel synthesis of NASICON discs from aqueous solution";Youichi Shimizu等;《Journal of Materials Chemistry》;19970101;第7卷(第8期);第1487页左栏倒数第一段，第1489页左栏第二段 *
"The Preparation, Structure, and Conductivity of Scandium-Substituted NASICONs";M. A. SUBRAMANIAN等;《Journal of Solid State Chemistry》;19851115;第60卷(第2期);第172页摘要，第174页表1，第176页左栏最后一段至右栏第一段 *
Youichi Shimizu等."Sol–gel synthesis of NASICON discs from aqueous solution".《Journal of Materials Chemistry》.1997,第7卷(第8期),第1487-1490页. *

Also Published As

Publication number Publication date
US10566654B2 (en) 2020-02-18
DE102015013155A1 (de) 2017-04-13
WO2017059838A1 (de) 2017-04-13
CN108367924A (zh) 2018-08-03
JP6936790B2 (ja) 2021-09-22
EP3359487A1 (de) 2018-08-15
US20180254521A1 (en) 2018-09-06
JP2018538653A (ja) 2018-12-27

Similar Documents

Publication Publication Date Title
CN108367924B (zh) 用于固体钠离子电池组的具有nasicon结构的电解质材料及其制造方法
EP3135634B1 (en) Method for producing garnet-type compound
EP3244474B1 (en) Oriented apatite-type oxide ion conductor and method for manufacturing same
CN107848894A (zh) 石榴石型氧化物烧结体和其制造方法
EP2838836B1 (de) Verfahren zur herstellung li-ionenleitender lithiumaluminiumtitanphosphate und deren verwendung als festkörperelektrolyte
KR102316442B1 (ko) 세라믹 분말 재료, 세라믹 분말 재료의 제조 방법 및 전지
CN101786873A (zh) 锂离子电池电解质陶瓷膜的制备方法
KR20220024859A (ko) 비정질 리튬 이온 전도 산화물 분말 및 그 제조 방법, 그리고, nasicon형 결정 구조를 갖는 리튬 이온 전도 산화물 분말의 제조 방법
US11637316B2 (en) Ceramic powder material, sintered body, and battery
Dandeneau et al. Rapid fabrication of Ga-doped Li7La3Zr2O12 powder via microwave-assisted solution combustion synthesis
TWI786267B (zh) 配向性磷灰石型氧化物離子傳導體及其製造方法
EP4005999B1 (en) Ceramic powder material and method for producing ceramic powder material

Legal Events

Date Code Title Description
PB01 Publication
PB01 Publication
SE01 Entry into force of request for substantive examination
SE01 Entry into force of request for substantive examination
GR01 Patent grant
GR01 Patent grant