CN1077032C - 阻气层压制品及其生产方法 - Google Patents
阻气层压制品及其生产方法 Download PDFInfo
- Publication number
- CN1077032C CN1077032C CN95101790A CN95101790A CN1077032C CN 1077032 C CN1077032 C CN 1077032C CN 95101790 A CN95101790 A CN 95101790A CN 95101790 A CN95101790 A CN 95101790A CN 1077032 C CN1077032 C CN 1077032C
- Authority
- CN
- China
- Prior art keywords
- film
- thin film
- acrylic acid
- methyl
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
组份(wt.%) | 透氧度(30℃,80%RH,3μm)ml(STP)/m2·day·atm{Pa} | ||||
PVA | PAANa | DN=0% | DN=5% | DN=10% | DN=20% |
1009080706050403020100 | 0102030405060708090100 | 10039191921161617351350>5000 | 10049146.63.02.22.50.71.214>5000 | 10064225.51.30.70.30.10.54.0>5000 | 100180120120794028355364>5000 |
热处理条件 | 透氧度ml(STP)/m2·day·atm{Pa}(30℃,80%RH,3μm) | |
温度 | 时间 | |
120℃ | 2小时4小时8小时16小时31小时 | N.D.*N.D.*1010280100 |
140℃ | 1小时2小时4小时8小时16小时 | 15704301103514 |
160℃ | 30分钟1小时2小时4小时 | 33052229 |
180℃ | 15分钟30分钟1小时2小时 | 27054146 |
200℃ | 3分钟5分钟10分钟15分钟 | 12002605521 |
230℃ | 3分钟5分钟10分钟 | 33148 |
热处理条件 | 透氧度ml(STP)/m2·day·atm{Pa}(30℃,80%RH,3μm) | |
温度 | 时间 | |
120℃ | 2小时4小时8小时16小时32小时 | N.D.*N.D.*100040054 |
140℃ | 1小时2小时4小时8小时16小时 | 43019040113.3 |
160℃ | 30分钟1小时2小时4小时 | 7.43.20.830.44 |
180℃ | 15分钟30分钟1小时2小时 | 2.90.440.380.17 |
200℃ | 10分钟15分钟 | 0.40.1 |
层合结构 | 热处理 | 透氧度(*1) | (*2)封合强度 | |||||
第一层(μm) | 第二层(μm) | 第三层(μm) | 温度(℃) | 时间(min) | 层压薄膜 | Gerbo试验后 | ||
实施例1 | PET(12) | PVA+PAANa(3) | LLDPE(50) | 200 | 15 | 0.1 | 0.5 | 4.3 |
实施例2 | PET(12) | PVA+PAANa(3) | CPP(50) | 200 | 15 | 0.1 | 0.5 | 3.0 |
实施例3 | PET(12) | PVA+PAANa(3) | LLDPE(50) | 180 | 15 | 2.8 | 5 | 4.3 |
实施例4 | PET(12) | PVA+PAANa(3) | LLDPE(50) | 160 | 30 | 7.0 | 10 | 4.3 |
实施例5 | PET(12) | PVA+PAA(3) | CPP(50) | 200 | 15 | 13 | 25 | 3.0 |
实施例6 | PET(12) | PVA+PAANa(3) | - | 200 | 15 | 0.1 | 1.5 | 0.4 |
实施例7 | PET(25) | PVA+PAANa(3) | - | 200 | 15 | 0.1 | 0.8 | 1.4 |
实施例8 | ONy(15) | PVA+PAANa(3) | - | 160 | 30 | 6.6 | 9.7 | 0.6 |
实施例9 | ONy(15) | PVA+PMAANa(3) | - | 200 | 15 | 17 | 30 | 0.6 |
对比例1 | PET(12) | - | - | 未进行热处理 | 140 | 140 | 0.7 | |
对比例2 | - | PVA+PAANa(30) | - | 200 | 15 | 0.1 | 断裂 | 0 |
Claims (24)