CN106140196B - Byd加氢制备bdo的加氢催化剂及byd加氢制备bdo的方法 - Google Patents
Byd加氢制备bdo的加氢催化剂及byd加氢制备bdo的方法 Download PDFInfo
- Publication number
- CN106140196B CN106140196B CN201510198978.8A CN201510198978A CN106140196B CN 106140196 B CN106140196 B CN 106140196B CN 201510198978 A CN201510198978 A CN 201510198978A CN 106140196 B CN106140196 B CN 106140196B
- Authority
- CN
- China
- Prior art keywords
- byd
- metal alloy
- aqueous solution
- alloy particle
- hydrogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
实施例 | 催化剂组成 | BYD转化率(%) | BDO选择性(%) |
实施例1 | Ni<sub>55.6</sub>Al<sub>44.4</sub> | 99.1 | 95.1 |
实施例2 | Ni<sub>52.7</sub>Al<sub>45.1</sub>Cr<sub>2.2</sub> | 99.5 | 96.5 |
实施例3 | Ni<sub>53.1</sub>Al<sub>44.8</sub>Fe<sub>2.1</sub> | 99.6 | 96.4 |
实施例4 | Ni<sub>52.8</sub>Al<sub>45.1</sub>Co<sub>2.1</sub> | 99.7 | 96.6 |
实施例5 | Ni<sub>53.3</sub>Al<sub>45.0</sub>Mo<sub>1.7</sub> | 99.7 | 97.0 |
实施例6 | Ni<sub>53.0</sub>Al<sub>44.6</sub>Cr<sub>1.1</sub>Mo<sub>1.3</sub> | 100 | 98.5 |
实施例7 | Ni<sub>52.2</sub>Al<sub>43.3</sub>Fe<sub>2.7</sub>Mo<sub>1.8</sub> | 100 | 98.4 |
实施例8 | Ni<sub>52.7</sub>Al<sub>42.6</sub>Co<sub>2.8</sub>Mo<sub>1.9</sub> | 100 | 98.6 |
实施例9 | Ni<sub>52.3</sub>Al<sub>45.2</sub>Cr<sub>2.2</sub>Mo(浸)<sub>0.3</sub> | 99.9 | 98.1 |
实施例10 | Ni<sub>53.3</sub>Al<sub>44.3</sub>Fe<sub>2.1</sub>Mo(浸)<sub>0.3</sub> | 99.9 | 98.2 |
实施例11 | Ni<sub>52.5</sub>Al<sub>45.1</sub>Co<sub>2.1</sub>Mo(浸)<sub>0.3</sub> | 99.9 | 98.2 |
Claims (6)