CN104350118B - 制备可流动非晶态聚α‑烯烃粘合剂粒料的方法 - Google Patents
制备可流动非晶态聚α‑烯烃粘合剂粒料的方法 Download PDFInfo
- Publication number
- CN104350118B CN104350118B CN201380027096.4A CN201380027096A CN104350118B CN 104350118 B CN104350118 B CN 104350118B CN 201380027096 A CN201380027096 A CN 201380027096A CN 104350118 B CN104350118 B CN 104350118B
- Authority
- CN
- China
- Prior art keywords
- pellet
- binding agent
- temperature
- recrystallization
- health
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
粘合剂 | 冷结晶温度(℃) |
样品A | 38 |
样品B | 25 |
样品C | 35 |
对比样品D | 无 |
对比样品E | 无 |
粘合剂 | 温度(°F) | 达到Tanδ=1时的保持时间(秒) |
样品A | 40 | 4630 |
80 | 3670 | |
85 | 2051 | |
90 | 1631 | |
100 | 1691 | |
105 | 2890 | |
样品B | 77 | 1090 |
85 | 791 | |
90 | 491 |
样品C | 77 | 1211 |
85 | <100 | |
95 | 491 |
粘合剂 | 工艺条件 | 观察结块 | 评级 |
样品A | T2=40°F,具有表面活性剂 | 完全结块 | 不合格 |
样品A | T2=60°F,具有表面活性剂 | 24小时后部分未结块 | 不合格 |
样品A | T2=90°F,具有表面活性剂 | 2小时候完全没有结块 | 合格 |
Claims (7)