CN104130738A - 一种对不锈钢粘接良好的酸性硅酮密封胶及其制备方法 - Google Patents

一种对不锈钢粘接良好的酸性硅酮密封胶及其制备方法 Download PDF

Info

Publication number
CN104130738A
CN104130738A CN201410322563.2A CN201410322563A CN104130738A CN 104130738 A CN104130738 A CN 104130738A CN 201410322563 A CN201410322563 A CN 201410322563A CN 104130738 A CN104130738 A CN 104130738A
Authority
CN
China
Prior art keywords
parts
stainless steel
silicone sealant
sealant
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410322563.2A
Other languages
English (en)
Other versions
CN104130738B (zh
Inventor
袁强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Saint Gobain Huijie (Hangzhou) new material Co.,Ltd.
Original Assignee
ZHEJIANG JOINLEADER SILICON Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG JOINLEADER SILICON Co Ltd filed Critical ZHEJIANG JOINLEADER SILICON Co Ltd
Priority to CN201410322563.2A priority Critical patent/CN104130738B/zh
Publication of CN104130738A publication Critical patent/CN104130738A/zh
Application granted granted Critical
Publication of CN104130738B publication Critical patent/CN104130738B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种对不锈钢粘接良好的酸性硅酮密封胶及其制造方法，包括以下重量份数计的各组分：a、w-二羟基聚硅氧烷：20～90份、增塑剂：2～10份、填料：10～50份、触变剂：3～10份、交联剂：2～10份、增粘剂：1～5份、催化固化剂：0.1～5份，与现有技术相比，本发明加入了新型增粘剂，对不锈钢具有良好的粘接性能，由酸性透明体系加入银灰色浆调制而成，所以颜色闪光与不锈钢颜色基本没有差别，由于是酸性硅酮密封胶所以固化速度快，能显著提高生产效率，提高粘接性能，避免玻璃与不锈钢的脱落，在生产过程中能耗水耗低，无三废产生，对环境无污染，有显著的经济效益和社会效益。

Description

一种对不锈钢粘接良好的酸性硅酮密封胶及其制备方法
【技术领域】
本发明涉及一种酸性硅酮不锈钢密封胶及其制备方法，属于高分子建筑材料领域。
【背景技术】
硅酮密封胶具有优异的耐气候、湿热、紫外线及其臭氧老化性能。它具有非常好的物理性能、粘接性和硫化性能。近几年硅酮胶在许多方面得到了迅速的发展。尤其在不锈钢门方面的应用。现在人们对于美的追求越来越要求完美，不锈钢门需要用银灰色的密封胶，然而中性碳酸钙体系的胶对不锈钢虽然具有良好的粘接性能，但是它很难调处闪亮的银灰色，而且固化速度慢。中性二氧化硅体系的硅酮密封胶固化速度慢。生产不锈钢时由于是流水线作业要求固化速度快尤其是在冬天低温的情况下。所以酸性硅酮密封胶有着非常明显的优势。但是普通的酸性硅酮密封胶对不锈钢不具有非常好的粘接性能。尤其在运输过程中由于粘接性不好经常造成玻璃脱落而造成各种麻烦。所以要解决酸性硅酮胶的粘接性问题。
【发明内容】
本发明的目的就是解决现有技术中的问题，提出一种对不锈钢粘接良好的酸性硅酮密封胶及其制备方法，其特点是采用a、w-二羟基聚硅氧烷为a、w-二羟基聚二甲基硅氧烷为基料，引入新的增粘剂，制造对不锈钢粘接良好的酸性硅酮密封胶。
为实现上述目的，本发明提出了一种对不锈钢粘接良好的酸性硅酮密封胶及其制备方法，包括以下重量份数计的各组分：a、w-二羟基聚硅氧烷：20～90份、增塑剂：2～10份、填料：10～50份、触变剂：3～10份、交联剂：2～10份、增粘剂：1～5份、催化固化剂：0.1～5份。
作为优选，所述a、w-二羟基聚硅氧烷为a、w-二羟基聚二甲基硅氧烷、a、w-二羟基聚二乙基硅氧烷或a、w-二羟基聚二苯基硅氧烷中的至少一种。
作为优选，所述增塑剂为a、w-甲基羟基聚二甲基硅氧烷、a、w乙基羟基聚二甲基硅氧烷或a、w苯基羟基聚二甲基硅氧烷中的至少一种。
作为优选，所述填料为透明硅微粉或白油中的至少一种。
作为优选，所述触变剂为气相白炭黑、氢化蓖麻油或聚乙烯蜡中的至少一种。
作为优选，所述交联剂为甲基三乙酰氧基硅烷、乙基三乙酰氧基硅烷或丙基三乙酰氧基硅烷中的至少一种。
作为优选，所述增粘剂为苯二甲酸酐与r-氨丙基三乙氧基硅烷的反应产物，琥珀酸酐与r-氨丙基三乙氧基硅烷的反应产物，异氰酸酯与r-氨丙基三乙氧基硅烷的反应产物或巯基硅烷中的至少一种。
作为优选，所述催化固化剂为二月硅酸二丁基锡、二醋酸二丁基锡或氧化锡乙酰乙酸乙酯络合物中的至少一种。
为实现上述目的，本发明还提出了一种对不锈钢粘接良好的酸性硅酮密封胶的制备方法，其特征在于：依次包括以下步骤：
a)将a、w-二羟基聚硅氧烷20～90份，增塑剂2～10份，填料50～10份加入高速分散机，真空度为0.09～0.095MPa，转速为200～400rpm，高速分散20～40分钟；
b)将交连剂2～10份加入高速分散机，真空度为0.09～0.095MPa,转速为200～400rpm,高速分散20～40分钟；
c)将触变剂3～10份加入高速分散机，转速为700～900rpm，高速分散35～55分钟；
d)将增粘剂1～5份，催化固化剂0.1～5份加入高速分散机，真空度为0.09～0.095MPa,转速为300～500rpm，进行化学反应20～40分钟，制得酸性硅酮不锈钢密封胶，其反应式为：
本发明的有益效果：
1.该产品加入了新型增粘剂，对不锈钢具有良好的粘接性能。
2.该产品是由酸性透明体系加入银灰色浆调制而成，所以颜色闪光与不锈钢颜色基本没有差别。
3.由于是酸性硅酮密封胶所以固化速度快，能显著提高生产效率，提高粘接性能，避免玻璃与不锈钢的脱落。
4.在生产过程中能耗水耗低，无三废产生。对环境无污染。有显著的经济效益和社会效益。
本发明的特征及优点将通过实施例进行详细说明。
【具体实施方式】
下面通过实施例对本发明进行具体的描述，有必要在此指出的是以下实施例只用于对本发明的进一步说明，不能理解为本发明的保护范围的限制，该领域的技术熟练人员可以根据上本发明内容对本发明作出一些非本质的改进和调整。
实施例：
1.将a、w-二羟基聚二甲硅氧烷36KG和a、w-甲基羟基聚二甲基硅氧烷15KG白油15KG加入高速分散机内，真空度为0.09-0.095MPa,转速300rpm,混合30分钟。将甲基三乙酰氧基硅烷4.2KG加入高速分散机内，真空度为0.09-0.095MPa,转速300rpm,混合30分钟，加入气相白炭黑6KG，转速800rpm高速分散45分钟，将二醋酸二丁基锡0.04kg，真空度为0.09-0.095MPa,转速400rpm,进行化学反应30分钟。制得普通酸性硅酮密封胶产品，产品和产品在不同状态的性能测试结果详情见表1所示。
2.将a、w-二羟基聚二甲硅氧烷36KG和a、w-甲基羟基聚二甲基硅氧烷15KG白油15KG加入高速分散机内，真空度为0.09-0.095MPa,转速300rpm,混合30分钟。将甲基三乙酰氧基硅烷4.2KG加入高速分散机内，真空度为0.09-0.095MPa,转速300rpm,混合30分钟，加入气相白炭黑6KG，转速800rpm高速分散45分钟，将二醋酸二丁基锡0.04kg，苯二甲酸酐与r-氨丙基三乙氧基硅烷的反应产物0.3kg，真空度为0.09-0.095MPa,转速400rpm,进行化学反应30分钟。制得不锈钢酸性硅酮密封胶产品，产品和产品在不同状态的性能测试结果详情见表1所示。
3.将a、w-二羟基聚二甲硅氧烷36KG和a、w-甲基羟基聚二甲基硅氧烷15KG白油15KG加入高速分散机内，真空度为0.09-0.095MPa,转速300rpm,混合30分钟。将甲基三乙酰氧基硅烷4.2KG加入高速分散机内，真空度为0.09-0.095MPa,转速300rpm,混合30分钟，加入气相白炭黑6KG，转速800rpm高速分散45分钟，将二桂酸二丁基锡0.04kg，巯基硅烷0.3kg，真空度为0.09-0.095MPa,转速400rpm,进行化学反应30分钟。制得不锈钢酸性硅酮密封胶产品，产品和产品在不同状态的性能测试结果详情见表1所示。
该产品加入了新型增粘剂，对不锈钢具有良好的粘接性能，由酸性透明体系加入银灰色浆调制而成，所以颜色闪光与不锈钢颜色基本没有差别，由于是酸性硅酮密封胶所以固化速度快，能显著提高生产效率，提高粘接性能，避免玻璃与不锈钢的脱落，在生产过程中能耗水耗低，无三废产生，对环境无污染，有显著的经济效益和社会效益。
上述实施例是对本发明的说明，不是对本发明的限定，任何对本发明简单变换后的方案均属于本发明的保护范围。

Claims (9)

1.一种对不锈钢粘接良好的酸性硅酮密封胶，其特征在于：包括以下重量份数计的各组分：a、w-二羟基聚硅氧烷：20～90份、增塑剂：2～10份、填料：10～50份、触变剂：3～10份、交联剂：2～10份、增粘剂：1～5份、催化固化剂：0.1～5份。
2.如权利要求1所述的一种对不锈钢粘接良好的酸性硅酮密封胶，其特征在于：所述a、w-二羟基聚硅氧烷为a、w-二羟基聚二甲基硅氧烷、a、w-二羟基聚二乙基硅氧烷或a、w-二羟基聚二苯基硅氧烷中的至少一种。
3.如权利要求1所述的一种对不锈钢粘接良好的酸性硅酮密封胶，其特征在于：所述增塑剂为a、w-甲基羟基聚二甲基硅氧烷、a、w乙基羟基聚二甲基硅氧烷或a、w苯基羟基聚二甲基硅氧烷中的至少一种。
4.如权利要求1所述的一种对不锈钢粘接良好的酸性硅酮密封胶，其特征在于：所述填料为透明硅微粉或白油中的至少一种。
5.如权利要求1所述的一种对不锈钢粘接良好的酸性硅酮密封胶，其特征在于：所述触变剂为气相白炭黑、氢化蓖麻油或聚乙烯蜡中的至少一种。
6.如权利要求1所述的一种对不锈钢粘接良好的酸性硅酮密封胶，其特征在于：所述交联剂为甲基三乙酰氧基硅烷、乙基三乙酰氧基硅烷或丙基三乙酰氧基硅烷中的至少一种。
7.如权利要求1所述的一种对不锈钢粘接良好的酸性硅酮密封胶，其特征在于：所述增粘剂为苯二甲酸酐与r-氨丙基三乙氧基硅烷的反应产物，琥珀酸酐与r-氨丙基三乙氧基硅烷的反应产物，异氰酸酯与r-氨丙基三乙氧基硅烷的反应产物或巯基硅烷中的至少一种。
8.如权利要求1至7中任一项所述的一种对不锈钢粘接良好的酸性硅酮密封胶，其特征在于：所述催化固化剂为二月硅酸二丁基锡、二醋酸二丁基锡或氧化锡乙酰乙酸乙酯络合物中的至少一种。
9.一种对不锈钢粘接良好的酸性硅酮密封胶的制备方法，其特征在于：依次包括以下步骤：
a)将a、w-二羟基聚硅氧烷20～90份，增塑剂2～10份，填料10～50份加入高速分散机，真空度为0.09～0.095MPa，转速为200～400rpm，高速分散20～40分钟；
b)将交连剂2～10份加入高速分散机，真空度为0.09～0.095MPa,转速为200～400rpm,高速分散20～40分钟；
c)将触变剂3～10份加入高速分散机，转速为700～900rpm，高速分散35～55分钟；
d)将增粘剂1～5份，催化固化剂0.1～5份加入高速分散机，真空度为0.09～0.095MPa,转速为300～500rpm，进行化学反应20～40分钟，制得酸性硅酮不锈钢密封胶，其反应式为：
CN201410322563.2A 2014-07-08 2014-07-08 一种对不锈钢粘接良好的酸性硅酮密封胶及其制备方法 Active CN104130738B (zh)