CN114874744A - 一种室内装修用防霉美容胶及其制备方法 - Google Patents
一种室内装修用防霉美容胶及其制备方法 Download PDFInfo
- Publication number
- CN114874744A CN114874744A CN202210511110.9A CN202210511110A CN114874744A CN 114874744 A CN114874744 A CN 114874744A CN 202210511110 A CN202210511110 A CN 202210511110A CN 114874744 A CN114874744 A CN 114874744A
- Authority
- CN
- China
- Prior art keywords
- parts
- mildew
- polydimethylsiloxane
- proof
- terminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种室内装修用防霉美容胶及其制备方法，通过采用烷氧基封端乙基聚二甲基硅氧烷为基础聚合，与市场常见的脱肟型和脱酸型硅酮胶相比，在交联固化时无酮肟型有毒有味气体释放，产品绿色环保，生产过程中与传统脱醇型比，生产工艺简单，无粘度高峰，并采用三官能硅氧烷聚合物与二官能硅氧烷聚合物复配，再加上通过不同分子量的复配物能有效的调节美容胶的强度和伸长率，可得到力学性能较优的产品，拉伸强度大于0.75Mpa，断裂伸长率大于200％，另外，本发明的防霉美容胶制备工艺简单，在生产过程中无粘度高峰且安全环保，无有机溶剂加入，无有毒气体释放，使用方便，单组分固化，直接打胶到需要粘接或美缝的区域，应用范围广，色彩亮丽丰富可调。
Description
技术领域
本发明涉及建筑装饰材料技术领域，特别涉及一种室内装修用防霉美容胶及其制备方法。
背景技术
美容胶主要用于室内装饰装修时瓷砖、马赛克、石材等材料之间的缝隙填充和基材粘接密封，需要具有丰富艳丽的色彩，区别于传统的密封填充材料单调色彩；与传统填缝剂现场加水搅拌时出现的跑灰、漏浆现象，长期使用后易掉落；该美容胶可有效填充和粘接装饰材料，绿色环保，无异味，色泽亮丽，颜色丰富可调，防霉性好，耐候性佳，能很好运用于室内装饰材料的填充和密封粘接。
专利CN201910054716.2公开了一种真瓷型厨卫防霉胶及其制造方法，该发明基础聚合物为硅烷改性聚醚树脂；专利CN201811600114.4公开了一种硅烷改性防霉胶及其制备方法，该发明专利使用的基础聚合物是硅烷改性树脂920R；专利CN201710908269.3公开了一种防霉美容胶，所述美容胶的基础聚合物为三甲氧基硅烷封端聚醚；以上三个专利都是防霉胶，采用的都是硅烷改性聚醚为基础聚合，其主链是碳基聚合物，不仅不够绿色环保，而且防霉性和耐候性较差。
发明内容
(一)要解决的技术问题
为了解决现有技术的上述问题，本发明提供一种室内装修用防霉美容胶及其制备方法，能够解决以上技术问题。
(二)技术方案
为了达到上述目的，本发明采用的技术方案为：
一种室内装修用防霉美容胶，其特征在于，其成分组成按重量份比包括：烷氧基封端乙基聚二甲基硅氧烷100份、聚二甲基硅油10-30份、白炭黑8-15份、除水剂0.5-2份、交联剂4-8份、硅烷偶联剂0.5-2份、色浆3-10份、防霉剂1-3份和催化剂0.1-2份。
为了达到上述目的，本发明采用的另一种技术方案为：
一种室内装修用防霉美容胶的制备方法，包括以下步骤：
将烷氧基封端乙基聚二甲基硅氧烷100份、聚二甲基硅油10-30份、白炭黑8-15份、除水剂0.5-2份、交联剂4-8份加入高速分散机，真空脱泡搅拌20-30分钟，待分散均匀制成透明半成品后再加入色浆3-10份调色，得到所需颜色后再加入硅烷偶联剂0.5-2份、防霉剂1-3份、催化剂0.1-2份，在真空搅拌15-30分钟，待混合均匀后出料，制得单组分湿气固化防霉美容胶。
(三)有益效果
本发明的有益效果在于：通过采用烷氧基封端乙基聚二甲基硅氧烷为基础聚合，与市场常见的脱肟型和脱酸型硅酮胶相比，在交联固化时无酮肟型有毒有味气体释放，产品绿色环保，生产过程中与传统脱醇型比，生产工艺简单，无粘度高峰，并采用三官能硅氧烷聚合物与二官能硅氧烷聚合物复配，再加上通过不同分子量的复配物能有效的调节美容胶的强度和伸长率，可得到力学性能较优的产品，拉伸强度大于0.75Mpa，断裂伸长率大于200％，采用气相白炭黑为主要填料，能够提高硅橡胶的拉伸强度和断裂伸长率，同时产品透明度高，在透明体系中加入色浆调色，生产出来的产品光泽亮丽，外观好看，与室内装修用陶瓷、瓷砖、金属等多种建材色彩相近，再通过添加环保长效防霉剂，能满足室内装修用密封胶对外观美丽色彩的需求同时还能长效防霉，应用范围广泛，另外，本发明的防霉美容胶制备工艺简单，在生产过程中无粘度高峰，且安全环保，无有机溶剂加入，无有毒气体释放，使用方便，单组分固化，直接打胶到需要粘接或美缝的区域，应用范围广，色彩亮丽丰富可调。
具体实施方式
为了更好的解释本发明，以便于理解，下面通过具体实施方式，对本发明作详细描述。
实施例一
一种室内装修用防霉美容胶，其成分组成按重量份比包括：烷氧基封端乙基聚二甲基硅氧烷100份、聚二甲基硅油10-30份、白炭黑8-15份、除水剂0.5-2份、交联剂4-8份、硅烷偶联剂0.5-2份、色浆3-10份、防霉剂1-3份和催化剂0.1-2份。
上述烷氧基封端乙基聚二甲基硅氧烷由乙烯基硅氧烷与端含氢聚二甲基硅油通过加成反应制得；
所述乙烯基硅氧烷的分子式为：
所述端含氢聚二甲基硅油的分子式为：
所述烷氧基封端乙基聚二甲基硅氧烷的分子式为：
上述端含氢聚二甲基硅油以及烷氧基封端乙基聚二甲基硅氧烷分子式中，R基为甲基，乙基或者甲氧基；其中，n需要保证端含氢聚二甲基硅油和烷氧基封端乙基聚二甲基硅氧烷复配物的粘度为5000～200000mPa·s。
所述烷氧基封端乙基聚二甲基硅氧烷由端三甲氧基硅烷封端乙基聚二甲基硅氧烷、甲基二甲氧基硅烷封端乙基聚二甲基硅氧烷和乙基二甲氧基硅烷封端乙基聚二甲基硅氧烷组成，其中三官能硅氧烷聚合物与二官能硅氧烷聚合物比例为1:1-3，在25℃时其复配物的粘度，5000～200000mPa·s。
所述聚二甲基硅油的粘度为50～2000mPa·s；
所述白炭黑为气相法白炭黑。
具体地，优选采用疏水型气相白炭黑。
所述除水剂为乙烯基三甲氧基硅烷、苯基三甲氧基硅烷中中的一种或两种。
所述交联剂为甲基三甲氧基硅烷、正硅酸甲酯、正硅酸乙酯、乙烯基三乙氧基硅烷和甲基三乙氧基硅烷中的一种或两种以上。
具体地，优选采用甲基三甲氧基硅烷和正硅酸甲酯两种。
所述硅烷偶联剂为氨丙基三甲氧基硅烷、氨丙基三乙氧基硅烷、氨乙基氨丙基三甲氧基硅烷、氨乙基氨丙基三乙氧基硅烷、氨乙基氨甲基三乙氧基硅烷、γ-缩水甘油醚氧丙基三甲氧基硅烷、γ-缩水甘油醚氧丙基三乙氧基硅烷、异氰酸酯基丙基三乙氧基硅烷和脲基丙基三甲氧基硅烷中的一种或者两种以上。
具体地，优选采用γ-缩水甘油醚氧丙基三甲氧基硅烷、异氰酸酯基丙基三乙氧基硅烷和脲基丙基三甲氧基硅烷三种；
所述色浆为色粉与聚二甲基硅油经高温除水混合均匀的膏状体。
所述防霉剂为聚季铵盐-39、醋酸氯氯已定、五氯苯芬钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、N，N-二甲基-N'-苯基(氟二氯甲基硫代)磺酰胺和纳米银中的一种或者两种以上。
所述催化剂为二月桂酸二丁基锡、二丁基二辛酸锡、二丁基二乙酸锡、辛酸亚锡、钛酸正丁酯或钛酸四异丙酯中的任意一种。
具体地，优选采用二月桂酸二丁基锡或钛酸四异丙酯中的一种。
实施例二
一种室内装修用防霉美容胶的制备方法，包括以下步骤：
将烷氧基封端乙基聚二甲基硅氧烷100份、聚二甲基硅油10-30份、白炭黑8-15份、除水剂0.5-2份、交联剂4-8份加入高速分散机，真空脱泡搅拌20-30分钟，待分散均匀制成透明半成品后再加入色浆3-10份调色，得到所需颜色后再加入硅烷偶联剂0.5-2份、防霉剂1-3份、催化剂0.1-2份，在真空搅拌15-30分钟，待混合均匀后出料，制得单组分湿气固化防霉美容胶。
实施例三
将粘度为20000mPa·s的端三甲氧基硅烷封端乙基聚二甲基硅氧烷与甲基二甲氧基硅烷封端乙基聚二甲基硅氧烷聚合物比例为1:2复配物100份，粘度为350mPa·s的聚二甲基硅油30份、气相白炭黑12份、乙烯基三甲氧基硅烷1份、甲基三甲氧基硅烷6份加入高速分散机，真空脱泡搅拌25分钟，得透明膏状物；在透明膏状物中再加入白色色浆6份调色，得到瓷白色胶体后再加入γ-缩水甘油醚氧丙基三甲氧基硅烷1份、五氯苯芬钠2份、二月桂酸二丁基锡0.3份，再真空搅拌20分钟，待混合均匀后出料，制得瓷白色单组分湿气固化防霉美容胶，产品性能的测试结果详情见表1所示。
实施例四
将粘度为50000mPa·s的端三甲氧基硅烷封端乙基聚二甲基硅氧烷与甲基二甲氧基硅烷封端乙基聚二甲基硅氧烷聚合物比例为1:1.5复配物100份，粘度为100mPa·s的聚二甲基硅油20份、气相白炭黑10份、乙烯基三甲氧基硅烷1.5份、甲基三甲氧基硅烷3份、正硅酸甲酯2份加入高速分散机，真空脱泡搅拌20分钟，得透明膏状物；在透明膏状物中再加入炭黑色浆5份调色，得到亮黑色胶体后再加入γ-缩水甘油醚氧丙基三甲氧基硅烷1份、氨丙基三乙氧基硅烷0.5、纳米银2份、钛酸四异丙酯2份，再真空搅拌18分钟，待混合均匀后出料，制得亮黑色单组分湿气固化防霉美容胶，产品性能的测试结果详情见表1所示。
实施例五
将粘度为10000mPa·s的端三甲氧基硅烷封端乙基聚二甲基硅氧烷与乙基二甲氧基硅烷封端乙基聚二甲基硅氧烷聚合物比例为1:2.5复配物100份，粘度为2000mPa·s的聚二甲基硅油15份、气相白炭黑8份、苯基三甲氧基硅烷2份、正硅酸甲酯4份、乙烯基三乙氧基硅烷2份加入高速分散机，真空脱泡搅拌30分钟，得透明膏状物；在透明膏状物中再加入闪银色浆6份调色，得到闪银胶体后再加入异氰酸酯基丙基三乙氧基硅烷1份、2，2'-二羟基-5，5'-二氯二苯基甲烷2份、二月桂酸二丁基锡0.5份，再真空搅拌15分钟，待混合均匀后出料，制得闪银色单组分湿气固化防霉美容胶，产品性能的测试结果详情见表1所示。
实施例六
将粘度为80000mPa·s的端三甲氧基硅烷封端乙基聚二甲基硅氧烷与乙基二甲氧基硅烷封端乙基聚二甲基硅氧烷聚合物比例为1:2复配物100份，粘度为500mPa·s的聚二甲基硅油30份、气相白炭黑10份、苯基三甲氧基硅烷2份、正硅酸甲酯4份、乙烯基三乙氧基硅烷2份加入高速分散机，真空脱泡搅拌30分钟，得透明膏状物；在透明膏状物中再加入红色浆8份调色，得到红色胶体后再加入脲基丙基三甲氧基硅烷1份、纳米银2份、二丁基二乙酸锡0.5份，再真空搅拌25分钟，待混合均匀后出料，制得红色单组分湿气固化防霉美容胶，产品性能的测试结果详情见表1所示。
对比例1
将将粘度为10000mPa·s的α,ω-二羟基聚二甲基硅氧烷100份、轻质碳酸钙100份加入真空高速分散机中，升温到120℃，抽真空脱水混合2小时，得到基胶；将基胶在真空环境下冷却至室温，再加入白油25份、甲基三丁酮肟基硅烷10份、氨丙基三甲氧基硅烷2份、二月桂酸二丁基锡0.5份加入真空高速分散机中搅拌30分钟，得到脱肟型硅酮胶，产品性能的测试结果详情见表1所示。
采用上述方法制得的防霉美容胶，按JC-T 885-2016建筑用防腐密封胶标准测试以下性能。
表1防霉美容胶性能测试结果
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等同变换，或直接或间接运用在相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (10)
1.一种室内装修用防霉美容胶，其特征在于，其成分组成按重量份比包括：烷氧基封端乙基聚二甲基硅氧烷100份、聚二甲基硅油10-30份、白炭黑8-15份、除水剂0.5-2份、交联剂4-8份、硅烷偶联剂0.5-2份、色浆3-10份、防霉剂1-3份和催化剂0.1-2份。
2.根据权利要求1所述的室内装修用防霉美容胶，其特征在于，所述烷氧基封端乙基聚二甲基硅氧烷由乙烯基硅氧烷与端含氢聚二甲基硅油通过加成反应制得；
所述乙烯基硅氧烷的分子式为：
所述端含氢聚二甲基硅油的分子式为：
所述烷氧基封端乙基聚二甲基硅氧烷的分子式为：
上述分子式中，R基为甲基，乙基或者甲氧基；
所述烷氧基封端乙基聚二甲基硅氧烷由三官能硅氧烷封端聚合物与二官能硅氧烷封端聚合物组成，且三官能硅氧烷封端聚合物与二官能硅氧烷封端聚合物比例为1:1-3，在25℃时其复配物的粘度为5000～200000mPa·s；
其中，三官能硅氧烷封端聚合物为端三甲氧基封端乙基聚二甲基硅氧烷；
所述二官能硅氧烷封端聚合物为甲基二甲氧基硅烷封端乙基聚二甲基硅氧烷和乙基二甲氧基硅烷封端乙基聚二甲基硅氧烷。
3.根据权利要求1所述的室内装修用防霉美容胶，其特征在于，所述聚二甲基硅油的粘度为50～2000mPa·s；
所述白炭黑为气相法白炭黑。
4.根据权利要求1所述的室内装修用防霉美容胶，其特征在于，所述除水剂为乙烯基三甲氧基硅烷、苯基三甲氧基硅烷中的一种或两种。
5.根据权利要求1所述的室内装修用防霉美容胶，其特征在于，所述交联剂为甲基三甲氧基硅烷、正硅酸甲酯、正硅酸乙酯、乙烯基三乙氧基硅烷和甲基三乙氧基硅烷中的一种或两种以上。
6.根据权利要求1所述的室内装修用防霉美容胶，其特征在于，所述硅烷偶联剂为氨丙基三甲氧基硅烷、氨丙基三乙氧基硅烷、氨乙基氨丙基三甲氧基硅烷、氨乙基氨丙基三乙氧基硅烷、氨乙基氨甲基三乙氧基硅烷、γ-缩水甘油醚氧丙基三甲氧基硅烷、γ-缩水甘油醚氧丙基三乙氧基硅烷、异氰酸酯基丙基三乙氧基硅烷和脲基丙基三甲氧基硅烷中的一种或者两种以上。
7.根据权利要求1所述的室内装修用防霉美容胶，其特征在于，所述色浆为色粉与聚二甲基硅油经高温除水混合均匀的膏状体。
8.根据权利要求1所述的室内装修用防霉美容胶，其特征在于，所述防霉剂为聚季铵盐-39、醋酸氯氯已定、五氯苯芬钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、N，N-二甲基-N'-苯基(氟二氯甲基硫代)磺酰胺和纳米银中的一种或者两种以上。
9.根据权利要求1所述的室内装修用防霉美容胶，其特征在于，所述催化剂为二月桂酸二丁基锡、二丁基二辛酸锡、二丁基二乙酸锡、辛酸亚锡、钛酸正丁酯或钛酸四异丙酯中的任意一种。
10.一种室内装修用防霉美容胶的制备方法，其特征在于，包括以下步骤：
将烷氧基封端乙基聚二甲基硅氧烷100份、聚二甲基硅油10-30份、白炭黑8-15份、除水剂0.5-2份、交联剂4-8份加入高速分散机，真空脱泡搅拌20-30分钟，待分散均匀制成透明半成品后再加入色浆3-10份调色，得到所需颜色后再加入硅烷偶联剂0.5-2份、防霉剂1-3份、催化剂0.1-2份，在真空搅拌15-30分钟，待混合均匀后出料，制得单组分湿气固化防霉美容胶。