CN101824184A - 运动鞋底用发泡塑胶 - Google Patents

运动鞋底用发泡塑胶 Download PDF

Info

Publication number
CN101824184A
CN101824184A CN201010178534A CN201010178534A CN101824184A CN 101824184 A CN101824184 A CN 101824184A CN 201010178534 A CN201010178534 A CN 201010178534A CN 201010178534 A CN201010178534 A CN 201010178534A CN 101824184 A CN101824184 A CN 101824184A
Authority
CN
China
Prior art keywords
ethylene
agent
shoe sole
plastic foam
sport shoe
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201010178534A
Other languages
English (en)
Other versions
CN101824184B (zh
Inventor
丁世忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anta China Co Ltd
Original Assignee
Anta China Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anta China Co Ltd filed Critical Anta China Co Ltd
Priority to CN2010101785345A priority Critical patent/CN101824184B/zh
Publication of CN101824184A publication Critical patent/CN101824184A/zh
Application granted granted Critical
Publication of CN101824184B publication Critical patent/CN101824184B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种运动鞋底用发泡塑胶，包括以下重量份成分：乙烯-醋酸乙烯共聚物70～74、乙烯-辛烯共聚物8～12、三元乙丙橡胶6～10、乙烯-丙烯酸共聚物8～12、耐磨剂8～9、填充剂4～6、氧化锌1.0～1.2、硬脂酸0.5～0.6、硬脂酸锌0.8～1.0、加速架桥剂0.5～0.7、架桥剂0.8～0.9、发泡剂3.2～3.8；其中，三元乙丙橡胶为乙烯-丙烯及非共轭二烯烃的三元共聚物。本发明运动鞋的塑胶鞋底，具有普通IP射出发泡塑胶配方所无法比拟的轻量性能，耐磨耗性能和舒适性，大大降低了运动员体能消耗，并且具有持久舒适和持久抗缓冲性能等多种性能。

Description

运动鞋底用发泡塑胶
技术领域
本发明涉及塑胶技术领域，特别是指一种运动鞋底用发泡塑胶。
背景技术
运动鞋由于其特殊的用途性质，需要轻巧便捷而且具有弹性。现有的普通IP射出发泡塑胶运动鞋，其底部耐磨大但是密度也相应较大，从而增加整体的重量；同时为了要达到一定耐磨要求，硬度普遍做的较高。主要原因是由于目前的运动鞋底的材料为单一材质，这样就存在不合理性，无法改变鞋底的性质，导致出现了许多不足之处：材质僵硬，密度大，弹性差，耐磨损性差，运动鞋在反复的弹跳、奔跑过程中，鞋底很快失去弹性、缓冲性能变差，磨损严重，同时消耗运动员的体能，降低运动成绩。
发明内容
本发明针对不足，提出一种轻量、抗缓冲优异，抗磨损优异，弹性好，具有持久舒适和持久抗缓冲性能的运动鞋底用塑胶。
为了实现上述发明目的，本发明提供以下技术方案：一种运动鞋底用发泡塑胶，包括以下重量份成分：
乙烯-醋酸乙烯共聚物   70～74
乙烯-辛烯共聚物       8～12
三元乙丙橡胶          6～10
乙烯-丙烯酸共聚物     8～12
耐磨剂                8～9
填充剂        4～6
氧化锌        1.0～1.2
硬脂酸        0.5～0.6
硬脂酸锌      0.8～1.0
加速架桥剂    0.5～0.7
架桥剂        0.8～0.9
发泡剂        3.2～3.8
其中，三元乙丙橡胶为乙烯-丙烯及非共轭二烯烃的三元共聚物。
优选的，所述耐磨剂为乙烯基三甲氧基硅烷及树脂共聚合物。
优选的，所述填充剂为水合硅酸镁超细粉。
优选的，所述硬脂酸为十八烷酸。
优选的，所述硬脂酸锌为游离酸与氧化锌共聚合物。
优选的，所述架桥剂为过氧化二异丙苯。
优选的，所述加速架桥剂为活性剂及矽酸盐共聚合物。
优选的，所述发泡剂为偶氮二甲酰胺。
优选的，各成分的重量份分别为：
乙烯-醋酸乙烯共聚物  72
乙烯-辛烯共聚物      10
三元乙丙橡胶         8
乙烯-丙烯酸共聚物    10
耐磨剂               8～9
填充剂               4～6
氧化锌               1.0～1.2
硬脂酸               0.5～0.6
硬脂酸锌             0.8～1.0
加速架桥剂    0.5～0.7
架桥剂        0.8～0.9
发泡剂        3.2～3.8。
采用上述成分的运动鞋底用发泡塑胶，乙烯-辛烯共聚物，以及三元乙丙橡胶，二者并用可提高配方整体性能，可提高配方整体的回弹性能、以及材料柔软性能和抗压缩变形性能。
乙烯-丙烯酸共聚物是一种高硬度和高强度的酸性的乙烯-丙稀酸共聚物，有利于增大发泡倍率，减轻材料的比重的功能；
耐磨剂是可以提高EVA材料耐磨耗性能的乙烯基三甲氧基硅烷及树脂共聚合物质。
针对酸性的乙烯-丙烯酸共聚物在加工时，受热后易与金属粘在一起(即粘密炼机和开炼机)，还有成品在脱模易粘模，配方中增加了硬脂酸和硬脂酸锌进行改性，硬脂酸和硬脂酸锌均是良好的加工剂，同时可软化物料，使配方中配合剂完全分散、以达到最佳加工效果，有利于成品物料脱模，还能降低发泡分解温度。
氧化锌与发泡剂：氧化锌属于碱性氧化物，刚好与配方中属酸性的硬脂酸和硬脂酸锌产生中和，中和整个配方体系的酸性，并降低发泡剂分解温度，氧化锌有利于闭孔材料气孔结构均匀细密，提高超轻塑胶发泡材料的理化性能，故在配方中使用偶氮二甲酰胺发泡剂，可使发泡达到最佳效果；
因为硬脂酸锌是属于酸性，使活性游离子被转移，从而延缓交联，架桥剂过少会影响硫化交联不足，架桥剂过量，导致过硫化，物料变脆变硬，其它也随之下降低。加速架桥剂与架桥剂并用后促进交联和发泡顺利进行，其交联强度大大增强，达到最佳力学性能效果。
本发明运动鞋的塑胶鞋底，具有普通IP射出发泡塑胶配方所无法比拟的轻量性能，耐磨耗性能和舒适性，大大降低了运动员体能消耗，并且具有持久舒适和持久抗缓冲性能等多种性能。
具体实施方式
一种运动鞋底用发泡塑胶，包括以下重量份成分：
乙烯-醋酸乙烯共聚物      70～74
乙烯-辛烯共聚物          8～12
三元乙丙橡胶             6～10
乙烯-丙烯酸共聚物        8～12
耐磨剂                   8～9
填充剂                   4～6
氧化锌                   1.0～1.2
硬脂酸                   0.5～0.6
硬脂酸锌                 0.8～1.0
加速架桥剂               0.5～0.7
架桥剂                   0.8～0.9
发泡剂                   3.2～3.8
其中，三元乙丙橡胶为乙烯-丙烯及非共轭二烯烃的三元共聚物。
上述运动鞋底用发泡塑胶的制备方法为：分别称取各成分，混匀；在灌注机中进行产品熟化及固化成型。
下面结合具体实施例对本发明进行详细描述，本部分的描述仅是示范性和解释性，不应对本发明的保护范围有任何的限制作用。
实施例1至实施例4的运动鞋底用发泡塑胶，其成分及其重量分别如下表1所示：
表1
Figure GSA00000110168900051
其中，EVA树脂为乙烯-醋酸乙烯共聚物；Fusabond树脂为乙烯-丙稀酸共聚物；聚烯烃弹性体为乙烯-辛烯共聚物；三元乙丙橡胶为乙烯-丙烯及非共轭二烯烃的三元共聚物；耐磨剂为乙烯基三甲氧基硅烷及树脂共聚合物；填充剂为水合硅酸镁超细粉；硬脂酸为十八烷酸；硬脂酸锌为游离酸与氧化锌共聚合物；架桥剂为过氧化二异丙苯；加速架桥剂为活性剂及矽酸盐共聚合物；发泡剂为偶氮二甲酰胺。
对上述实施例1至实施例4的发泡塑胶进行性能检测，按国家标准GB/T 19250--2003测试方法进行，结果如下表2：
表2
  检测项目   实施例1   实施例2   实施例3   实施例4
  硬度(Asker C)   57   57   56   55
  密度(g/cm3)   0.18   0.18   0.17   0.16
  回弹性(％)   46   47   48   47
  DIN耐磨(mm3)   119   146   135   141
  拉伸强度(MPa)   3.4   3.5   3.6   3.5
  耐磨性能(mm)   7.5   7.7   7.6   7.5
  热收缩(％)   1.2   0.8   0.9   1.0
  压缩变形(％)   32   33   33   34
  断裂伸长率(％)   269   313   305   298
  裤形撕裂强度(N/mm)   5.1   4.8   4.9   5.0
本发明的运动鞋底发泡塑胶，具有轻量(密度小)、抗缓冲优异，抗磨损优异，弹性好，具有持久舒适和持久抗缓冲性能。
根据生产需要，本发明产品中还可添加一些常规的辅料，如颜料等；当然对于其中的功能性添加剂，可根据本领域的常规选择进行替换，同样也能实现相同的作用或功效。
以上仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (9)

1.一种运动鞋底用发泡塑胶，包括以下重量份成分：
乙烯-醋酸乙烯共聚物     70～74
乙烯-辛烯共聚物         8～12
三元乙丙橡胶            6～10
乙烯-丙烯酸共聚物       8～12
耐磨剂                  8～9
填充剂                  4～6
氧化锌                  1.0～1.2
硬脂酸                  0.5～0.6
硬脂酸锌                0.8～1.0
加速架桥剂              0.5～0.7
架桥剂                  0.8～0.9
发泡剂                  3.2～3.8
其中，三元乙丙橡胶为乙烯-丙烯及非共轭二烯烃的三元共聚物。
2.根据权利要求1所述的运动鞋底用发泡塑胶，其特征在于：所述耐磨剂为乙烯基三甲氧基硅烷及树脂共聚合物。
3.根据权利要求1所述的运动鞋底用发泡塑胶，其特征在于：所述填充剂为水合硅酸镁超细粉。
4.根据权利要求1所述的运动鞋底用发泡塑胶，其特征在于：所述硬脂酸为十八烷酸。
5.根据权利要求1所述的运动鞋底用发泡塑胶，其特征在于：所述硬脂酸锌为游离酸与氧化锌共聚合物。
6.根据权利要求1所述的运动鞋底用发泡塑胶，其特征在于：所述架桥剂为过氧化二异丙苯。
7.根据权利要求1所述的运动鞋底用发泡塑胶，其特征在于：所述加速架桥剂为活性剂及矽酸盐共聚合物。
8.根据权利要求1所述的运动鞋底用发泡塑胶，其特征在于：所述发泡剂为偶氮二甲酰胺。
9.根据权利要求1所述的运动鞋底用发泡塑胶，其特征在于：各成分的重量份分别为：
乙烯-醋酸乙烯共聚物            72
乙烯-辛烯共聚物                10
三元乙丙橡胶                   8
乙烯-丙烯酸共聚物              10
耐磨剂                         8～9
填充剂                         4～6
氧化锌                         1.0～1.2
硬脂酸                         0.5～0.6
硬脂酸锌                       0.8～1.0
加速架桥剂                     0.5～0.7
架桥剂                         0.8～0.9
发泡剂                         3.2～3.8。
CN2010101785345A 2010-05-13 2010-05-13 运动鞋底用发泡塑胶 Active CN101824184B (zh)