CN101724193B - 一种运动鞋底用超轻塑胶配方 - Google Patents
一种运动鞋底用超轻塑胶配方 Download PDFInfo
- Publication number
- CN101724193B CN101724193B CN2008100719866A CN200810071986A CN101724193B CN 101724193 B CN101724193 B CN 101724193B CN 2008100719866 A CN2008100719866 A CN 2008100719866A CN 200810071986 A CN200810071986 A CN 200810071986A CN 101724193 B CN101724193 B CN 101724193B
- Authority
- CN
- China
- Prior art keywords
- weight
- mass parts
- parts
- super
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种运动鞋底用超轻塑胶配方,其按如下质量份配方:乙烯-醋酸乙烯共聚物:59—69质量份;聚烯烃弹性体:11—21质量份;茂金属聚乙烯:5—15质量份;酸性的乙烯共聚物:5—15质量份;滑石粉:6—8质量份;氧化锌:0.7-1.0质量份;硬脂酸:0.5-0.8质量份,硬脂酸锌:0.6—1.0质量份;流动剂A:0.5-0.8质量份;加速架桥剂:0.3—0.6质量份;架桥剂:0.25-0.5质量份;发泡剂:4.8—5.4质量份。以此技术方案制作的运动鞋的塑胶鞋底,具有普通塑胶配方所无法比拟的超轻性能和舒适性,大降低了运动员体能消耗,并且具有持久舒适和持久抗缓冲性能等多种性能。
Description
技术领域
本发明涉及一种橡胶配方,特别是指一种运动鞋底用塑胶的配方。
背景技术
运动鞋由于其特殊的用途,为提高运动舒适性,及提高运动员的成绩,还具有良好的抗缓冲性能,所以运动鞋超轻化并保持期优异的性能成为塑胶发展的一个趋性。由于配方的不合理性,出现了许多缺点,运动鞋在反复的弹跳、奔跑过程中,鞋底很快就会变形、破裂、脱胶等,失去弹性、缓冲性能变差。消耗运动员的体能,降低运动成绩。
发明内容
针对现有技术中存在的缺陷,本发明提供一种轻便、抗缓冲优异,具有持久舒适和持久抗缓冲性能的运动鞋底用超轻塑胶配方。
为实现上述目的,本发明技术方案为:
一种运动鞋底用超轻塑胶配方,其特征在于按质量份配方如下:
乙烯-醋酸乙烯共聚物:59—69质量份,聚烯烃弹性体:11—21质量份,茂金属聚乙烯:5—15质量份,酸性的乙烯共聚物:5—15质量份,填充剂:8.35—11.9质量份,流动剂A:0.5-0.8质量份,发泡剂:4.8—5.4质量份。
所述的填充剂为滑石粉、氧化锌、硬脂酸、硬脂酸锌、加速架桥剂和架桥剂,上述组分在运动鞋底用超轻塑胶配方中的质量份如下:滑石粉:6—8质量份,氧化锌:0.7-1.0质量份,硬脂酸:0.5-0.8质量份,硬脂酸锌:0.6—1.0质量份,加速架桥剂:0.3—0.6质量份,架桥剂:0.25-0.5质量份。
上述技术方案的有益之处在于:
采用上述的运动鞋底用塑胶配方后,可获得理想的原料功能组合,该配方采用聚烯烃弹性体:12-21质量份,茂金属聚乙烯:5-15质量份二者并用提高配方整体性能,可提高配方整体的回弹性能和抗紫外线功能。
酸性的乙烯共聚物Fusabond 514D:5—15质量份,酸性的乙烯共聚物Fusabond514D是一种高硬度和高强度的酸性的乙烯共聚物,有利于增大发泡倍率,减轻材料的比重。
针对酸性的乙烯共聚物Fusabond 514D在加工时受热后易与金属粘在一起(即粘密炼机和开炼机),还有成品在脱模易粘模,配方中增加了硬脂酸St:0.5-0.8质量份,硬脂酸锌ZnSt:0.6—1.0质量份进行改性,硬脂酸和硬脂酸锌均是良好的加工剂,同时可软化物料,使配方中配合剂完全分散、以达到最佳加工效果,有利于成品物料脱模,还能降低发泡分解温度。
氧化锌ZnO:0.7-1.0质量份与发泡剂808B:4.8—5.4质量份,氧化锌ZnO属于碱性氧化物,刚好与配方中属酸性的硬脂酸和硬脂酸锌产生中和,中和整个配方体系的酸性,并降低发泡剂分解温度,氧化锌ZnO有利于闭孔材料气孔结构均匀细密,提高超轻塑胶发泡材料的理化性能,故在配方中选用中温发泡剂808B。使发泡剂完全分解,达到最佳的发泡效果。
因为硬脂酸锌是属于酸性,使活性游离子被转移,从而延缓交联,架桥剂DCP过少会影响硫化交联不足,架桥剂DCP过量,导致过硫化,物料变脆变硬,其它也随之下降低,加速架桥剂T—144:0.3—0.6质量份与架桥剂DCP:0.25-0.5质量份并用后促进交联和发泡顺利进行,其交联强度大增强,达到最佳力学性能效果。
具体实施方式
本发明运动鞋底用超轻塑胶配方及一批中最佳重量组合如下表:
实施上述配方后运动鞋用塑胶的检测结果如下表:
检测项目 | 检测结果 |
硬度(Asker C) | 52-58 |
密度(g/cm3) | 0.16以下 |
回弹性(%) | 40%以上 |
撕裂强度(N/mm) | 25以上 |
拉伸强度(MPa) | 2.0以上 |
压缩变形(%) | 35%以下 |
热收缩(%) | 1.5%以下 |
以此技术方案制作的运动鞋的塑胶鞋底,具有普通塑胶配方所无法比拟的超轻性能和舒适性,大降低了运动员体能消耗,并且具有持久舒适和持久抗缓冲性能等多种性能。
Claims (2)
1.一种运动鞋底用超轻塑胶组合物,其特征在于按质量份如下:
乙烯-醋酸乙烯共聚物:59-69质量份,
聚烯烃弹性体:11-21质量份,
茂金属聚乙烯:5-15质量份,
酸性的乙烯共聚物:5-15质量份,
填充剂:8.35-11.9质量份,
流动剂:0.5-0.8质量份,
发泡剂:4.8-5.4质量份,
其中,所述的酸性的乙烯共聚物为Fusabond 514D;所述的填充剂为滑石粉、氧化锌、硬脂酸、硬脂酸锌、加速架桥剂和架桥剂,上述组分在运动鞋底用超轻塑胶中的质量份如下:
滑石粉:6-8质量份,
氧化锌:0.7-1.0质量份,
硬脂酸:0.5-0.8质量份,
硬脂酸锌:0.6-1.0质量份,
加速架桥剂:0.3-0.6质量份,
架桥剂:0.25-0.5质量份。
2.如权利要求1所述的一种运动鞋底用超轻塑胶组合物,其特征在于:所述的乙烯-醋酸乙烯共聚物为EVA460;茂金属聚乙烯为GH030或CB0002。