CN101027341B - 具有高粘接性的聚酰亚胺薄膜的制造方法 - Google Patents

具有高粘接性的聚酰亚胺薄膜的制造方法 Download PDF

Info

Publication number
CN101027341B
CN101027341B CN2005800321181A CN200580032118A CN101027341B CN 101027341 B CN101027341 B CN 101027341B CN 2005800321181 A CN2005800321181 A CN 2005800321181A CN 200580032118 A CN200580032118 A CN 200580032118A CN 101027341 B CN101027341 B CN 101027341B
Authority
CN
China
Prior art keywords
polyimide
film
component
thermoplastic polyimide
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN2005800321181A
Other languages
English (en)
Chinese (zh)
Other versions
CN101027341A (zh
Inventor
金城永泰
菊池刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kaneka Corp
Original Assignee
Kaneka Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kaneka Corp filed Critical Kaneka Corp
Publication of CN101027341A publication Critical patent/CN101027341A/zh
Application granted granted Critical
Publication of CN101027341B publication Critical patent/CN101027341B/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/18—Manufacture of films or sheets
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G73/00—Macromolecular compounds obtained by reactions forming a linkage containing nitrogen with or without oxygen or carbon in the main chain of the macromolecule, not provided for in groups C08G12/00 - C08G71/00
    • C08G73/06—Polycondensates having nitrogen-containing heterocyclic rings in the main chain of the macromolecule
    • C08G73/10—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
    • C08G73/1003—Preparatory processes
    • C08G73/1007—Preparatory processes from tetracarboxylic acids or derivatives and diamines
    • C08G73/101—Preparatory processes from tetracarboxylic acids or derivatives and diamines containing chain terminating or branching agents
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G73/00—Macromolecular compounds obtained by reactions forming a linkage containing nitrogen with or without oxygen or carbon in the main chain of the macromolecule, not provided for in groups C08G12/00 - C08G71/00
    • C08G73/06—Polycondensates having nitrogen-containing heterocyclic rings in the main chain of the macromolecule
    • C08G73/10—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
    • C08G73/1003—Preparatory processes
    • C08G73/1007—Preparatory processes from tetracarboxylic acids or derivatives and diamines
    • C08G73/1028—Preparatory processes from tetracarboxylic acids or derivatives and diamines characterised by the process itself, e.g. steps, continuous
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G73/00—Macromolecular compounds obtained by reactions forming a linkage containing nitrogen with or without oxygen or carbon in the main chain of the macromolecule, not provided for in groups C08G12/00 - C08G71/00
    • C08G73/06—Polycondensates having nitrogen-containing heterocyclic rings in the main chain of the macromolecule
    • C08G73/10—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
    • C08G73/1042—Copolyimides derived from at least two different tetracarboxylic compounds or two different diamino compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G73/00—Macromolecular compounds obtained by reactions forming a linkage containing nitrogen with or without oxygen or carbon in the main chain of the macromolecule, not provided for in groups C08G12/00 - C08G71/00
    • C08G73/06—Polycondensates having nitrogen-containing heterocyclic rings in the main chain of the macromolecule
    • C08G73/10—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
    • C08G73/1046—Polyimides containing oxygen in the form of ether bonds in the main chain
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G73/00—Macromolecular compounds obtained by reactions forming a linkage containing nitrogen with or without oxygen or carbon in the main chain of the macromolecule, not provided for in groups C08G12/00 - C08G71/00
    • C08G73/06—Polycondensates having nitrogen-containing heterocyclic rings in the main chain of the macromolecule
    • C08G73/10—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
    • C08G73/1046—Polyimides containing oxygen in the form of ether bonds in the main chain
    • C08G73/105—Polyimides containing oxygen in the form of ether bonds in the main chain with oxygen only in the diamino moiety
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G73/00—Macromolecular compounds obtained by reactions forming a linkage containing nitrogen with or without oxygen or carbon in the main chain of the macromolecule, not provided for in groups C08G12/00 - C08G71/00
    • C08G73/06—Polycondensates having nitrogen-containing heterocyclic rings in the main chain of the macromolecule
    • C08G73/10—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
    • C08G73/1067—Wholly aromatic polyimides, i.e. having both tetracarboxylic and diamino moieties aromatically bound
    • C08G73/1071—Wholly aromatic polyimides containing oxygen in the form of ether bonds in the main chain
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K1/00—Printed circuits
    • H05K1/02—Details
    • H05K1/03—Use of materials for the substrate
    • H05K1/0313—Organic insulating material
    • H05K1/032—Organic insulating material consisting of one material
    • H05K1/0346—Organic insulating material consisting of one material containing N
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K1/00—Printed circuits
    • H05K1/02—Details
    • H05K1/03—Use of materials for the substrate
    • H05K1/0393—Flexible materials
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2379/00—Characterised by the use of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing nitrogen with or without oxygen, or carbon only, not provided for in groups C08J2361/00 - C08J2377/00
    • C08J2379/04—Polycondensates having nitrogen-containing heterocyclic rings in the main chain; Polyhydrazides; Polyamide acids or similar polyimide precursors
    • C08J2379/08—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K2201/00—Indexing scheme relating to printed circuits covered by H05K1/00
    • H05K2201/01—Dielectrics
    • H05K2201/0137—Materials
    • H05K2201/0154—Polyimide
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/28—Web or sheet containing structurally defined element or component and having an adhesive outermost layer
    • Y10T428/2813—Heat or solvent activated or sealable
    • Y10T428/2817—Heat sealable
    • Y10T428/2826—Synthetic resin or polymer
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31678—Of metal
    • Y10T428/31681—Next to polyester, polyamide or polyimide [e.g., alkyd, glue, or nylon, etc.]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Materials Engineering (AREA)
  • Macromolecular Compounds Obtained By Forming Nitrogen-Containing Linkages In General (AREA)
  • Manufacture Of Macromolecular Shaped Articles (AREA)
  • Moulding By Coating Moulds (AREA)
  • Laminated Bodies (AREA)
CN2005800321181A 2004-09-24 2005-09-20 具有高粘接性的聚酰亚胺薄膜的制造方法 Expired - Lifetime CN101027341B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP276766/2004 2004-09-24
JP2004276766 2004-09-24
PCT/JP2005/017283 WO2006033324A1 (ja) 2004-09-24 2005-09-20 高い接着性を有するポリイミドフィルムの製造方法

Related Child Applications (1)

Application Number Title Priority Date Filing Date
CN201210097682.3A Division CN102675634B (zh) 2004-09-24 2005-09-20 具有高粘接性的聚酰亚胺薄膜的制造方法

Publications (2)

Publication Number Publication Date
CN101027341A CN101027341A (zh) 2007-08-29
CN101027341B true CN101027341B (zh) 2012-06-06

Family

ID=36090083

Family Applications (2)

Application Number Title Priority Date Filing Date
CN2005800321181A Expired - Lifetime CN101027341B (zh) 2004-09-24 2005-09-20 具有高粘接性的聚酰亚胺薄膜的制造方法
CN201210097682.3A Expired - Lifetime CN102675634B (zh) 2004-09-24 2005-09-20 具有高粘接性的聚酰亚胺薄膜的制造方法

Family Applications After (1)

Application Number Title Priority Date Filing Date
CN201210097682.3A Expired - Lifetime CN102675634B (zh) 2004-09-24 2005-09-20 具有高粘接性的聚酰亚胺薄膜的制造方法

Country Status (6)

Country Link
US (1) US8513373B2 (cg-RX-API-DMAC7.html)
JP (2) JP5054976B2 (cg-RX-API-DMAC7.html)
KR (2) KR100981852B1 (cg-RX-API-DMAC7.html)
CN (2) CN101027341B (cg-RX-API-DMAC7.html)
TW (1) TWI382040B (cg-RX-API-DMAC7.html)
WO (1) WO2006033324A1 (cg-RX-API-DMAC7.html)

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2006033272A1 (ja) * 2004-09-24 2006-03-30 Kaneka Corporation 接着性の改良された新規なポリイミドフィルム
CN101098909B (zh) * 2005-01-18 2010-07-28 株式会社钟化 粘合性经改良的新的聚酰亚胺薄膜
JP4957487B2 (ja) * 2007-09-28 2012-06-20 東レ株式会社 ポリアミック酸の製造方法
CN103772704A (zh) * 2013-11-12 2014-05-07 天津市天缘电工材料有限责任公司 一种低摩擦系数高粘结力聚酰亚胺薄膜的制备方法
KR101668059B1 (ko) * 2014-12-30 2016-10-20 에스케이씨코오롱피아이 주식회사 가교형 수용성 열가소성 폴리아믹산 및 이의 제조방법
CN105175722B (zh) * 2015-09-02 2017-05-10 无锡高拓新材料股份有限公司 一种芳香族高相对分子质量和分子量分布窄的聚酰胺酸的制备方法
JP2019093548A (ja) * 2016-03-30 2019-06-20 株式会社カネカ 長尺ポリイミド積層体およびその製造方法
WO2018181496A1 (ja) * 2017-03-30 2018-10-04 日産化学株式会社 剥離層形成用組成物及び剥離層
KR102345722B1 (ko) * 2019-11-07 2022-01-03 피아이첨단소재 주식회사 고내열 저유전 폴리이미드 필름 및 이의 제조방법
KR102347588B1 (ko) * 2019-11-07 2022-01-10 피아이첨단소재 주식회사 고내열 저유전 폴리이미드 필름 및 이의 제조방법
KR102347633B1 (ko) * 2019-11-07 2022-01-10 피아이첨단소재 주식회사 유전특성이 개선된 폴리이미드 필름 및 그 제조방법

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2003097725A1 (en) * 2002-05-21 2003-11-27 Kaneka Corporation Polyimide film and method for production thereof, and polyimide/metal laminate using polyimide

Family Cites Families (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0276405B1 (en) * 1986-11-29 1994-03-09 Kanegafuchi Chemical Industry Co., Ltd. Polyimide having a thermal dimensional stability
JPS6461428A (en) * 1987-08-28 1989-03-08 Ajinomoto Kk Preventing agent against arrhythmia
JPH04161428A (ja) 1990-10-24 1992-06-04 Kanegafuchi Chem Ind Co Ltd ポリイミドフィルム
JPH04161437A (ja) 1990-10-24 1992-06-04 Kanegafuchi Chem Ind Co Ltd ポリイミドフィルム
JP2910796B2 (ja) 1991-04-19 1999-06-23 鐘淵化学工業株式会社 ポリアミック酸共重合体及びそれからなるポリイミドフィルム並びにそれらの製造方法
JP2955724B2 (ja) * 1991-04-24 1999-10-04 鐘淵化学工業株式会社 ポリイミドフィルムの製造方法
JP3022625B2 (ja) * 1991-05-10 2000-03-21 鐘淵化学工業株式会社 ポリアミック酸共重合体、それからなるポリイミド共重合体、及びポリイミドフィルム、並びにそれらの製造方法
JP3048702B2 (ja) 1991-09-13 2000-06-05 鐘淵化学工業株式会社 ポリアミック酸共重合体、ポリイミド共重合体、ポリイミドフィルム及びそれらの製造方法
JP2889976B2 (ja) 1992-02-10 1999-05-10 鐘淵化学工業株式会社 ポリイミドフィルム及びその製造方法
JPH0632926A (ja) 1992-07-16 1994-02-08 Shin Etsu Chem Co Ltd ポリイミドフィルムの表面改質方法
US5502143A (en) * 1992-12-25 1996-03-26 Pi Material Research Laboratory Process for preparing polyimide resins
US5412066A (en) * 1994-03-03 1995-05-02 Ther United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Phenylethynyl terminated imide oligomers
US5691876A (en) * 1995-01-31 1997-11-25 Applied Materials, Inc. High temperature polyimide electrostatic chuck
US5906886A (en) * 1996-05-31 1999-05-25 Ube Industries, Ltd. Aromatic polyimide article having amorphous layer
JP3982895B2 (ja) * 1997-04-09 2007-09-26 三井化学株式会社 金属ベース半導体回路基板
JP3446560B2 (ja) * 1997-10-20 2003-09-16 日立電線株式会社 ブロックポリイミド樹脂及びその製造方法
US6129982A (en) 1997-11-28 2000-10-10 Ube Industries, Ltd. Aromatic polyimide film having improved adhesion
JP3438556B2 (ja) 1997-11-28 2003-08-18 宇部興産株式会社 接着性の改良されたポリイミドフィルム、その製法およびその積層体
JP2000080178A (ja) 1998-09-02 2000-03-21 Du Pont Toray Co Ltd 共重合ポリイミドフィルム、その製造方法およびこれを基材とした金属配線板
JP2000119521A (ja) 1998-10-16 2000-04-25 Du Pont Toray Co Ltd 共重合ポリイミドフィルム、その製造方法およびこれを基材とした金属配線回路板
US6350844B1 (en) * 1998-11-05 2002-02-26 Kaneka Corporation Polyimide film and electric/electronic equipment bases with the use thereof
TWI295966B (cg-RX-API-DMAC7.html) * 2000-10-27 2008-04-21 Kaneka Corp
JP2002180044A (ja) * 2000-12-07 2002-06-26 Toray Eng Co Ltd 熱可塑性ポリイミド樹脂用エッチング液
CN1307260C (zh) * 2002-01-15 2007-03-28 株式会社Pi技术研究所 溶剂可溶的嵌段共聚聚酰亚胺组合物及其制造方法
US7267883B2 (en) * 2002-09-25 2007-09-11 Kaneka Corporation Polyimide film and laminate having metal layer and same
KR20050085331A (ko) * 2002-12-05 2005-08-29 가부시키가이샤 가네카 적층체, 인쇄 배선판 및 이들의 제조 방법

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2003097725A1 (en) * 2002-05-21 2003-11-27 Kaneka Corporation Polyimide film and method for production thereof, and polyimide/metal laminate using polyimide

Also Published As

Publication number Publication date
US8513373B2 (en) 2013-08-20
CN102675634B (zh) 2015-06-17
JP2012214807A (ja) 2012-11-08
KR20100017883A (ko) 2010-02-16
TW200619270A (en) 2006-06-16
WO2006033324A1 (ja) 2006-03-30
US20080287642A1 (en) 2008-11-20
JP5054976B2 (ja) 2012-10-24
TWI382040B (zh) 2013-01-11
KR20070056128A (ko) 2007-05-31
JPWO2006033324A1 (ja) 2008-05-15
CN102675634A (zh) 2012-09-19
CN101027341A (zh) 2007-08-29
JP5514861B2 (ja) 2014-06-04
KR100981852B1 (ko) 2010-09-13

Similar Documents

Publication Publication Date Title
JP5514861B2 (ja) 高い接着性を有するポリイミドフィルムの製造方法
JP5694891B2 (ja) 高い接着性を有するポリイミドフィルムおよびその製造方法
WO2005111165A1 (ja) 接着フィルムの製造方法
CN101163734B (zh) 新型聚酰亚胺膜及其利用
CN101018817B (zh) 具有高粘接性的聚酰亚胺薄膜及其制造方法
JP2008188954A (ja) 片面金属張積層板用基材及び片面金属張積層板の製造方法
CN101146850B (zh) 聚酰亚胺薄膜
CN101068851B (zh) 聚酰亚胺、聚酰亚胺膜和层压体
WO2005115752A1 (ja) ポリイミド積層体およびその製造方法
JP2008188843A (ja) ポリイミド前駆体溶液の多層膜、多層ポリイミドフィルム、片面金属張積層板、および多層ポリイミドフィルムの製造方法
JP4901509B2 (ja) ポリイミド前駆体溶液の多層膜、多層ポリイミドフィルム、片面金属張積層板、および多層ポリイミドフィルムの製造方法
CN101258212B (zh) 耐热性粘接片
TWI392699B (zh) 接著性經改良之新穎聚醯亞胺膜
JP2011195771A (ja) 接着フィルムの製造方法ならびにフレキシブル金属張積層板
JP2005305968A (ja) 接着フィルムの製造方法
JP5297573B2 (ja) 高い接着性を有するポリイミドフィルム
CN100562427C (zh) 粘接膜及其应用
JP5069844B2 (ja) プリント配線板用絶縁フィルムの製造方法、ポリイミド／銅積層体及びプリント配線板
JP5355993B2 (ja) 接着フィルム
JP5261563B2 (ja) 高い接着性を有するポリイミドフィルムの製造方法

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
CX01 Expiry of patent term

Granted publication date: 20120606

CX01 Expiry of patent term