CA1216993A - Continuous preparation of nylons - Google Patents

Continuous preparation of nylons

Info

Publication number
CA1216993A
CA1216993A CA000456498A CA456498A CA1216993A CA 1216993 A CA1216993 A CA 1216993A CA 000456498 A CA000456498 A CA 000456498A CA 456498 A CA456498 A CA 456498A CA 1216993 A CA1216993 A CA 1216993A
Authority
CA
Canada
Prior art keywords
zone
prepolymer
evaporator
nylon
salt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
CA000456498A
Other languages
English (en)
French (fr)
Inventor
Franz Schmidt
Gunter Pipper
Josef G. Floss
Franz Zahradnik
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Original Assignee
BASF SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF SE filed Critical BASF SE
Application granted granted Critical
Publication of CA1216993A publication Critical patent/CA1216993A/en
Expired legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G69/00—Macromolecular compounds obtained by reactions forming a carboxylic amide link in the main chain of the macromolecule
    • C08G69/02—Polyamides derived from amino-carboxylic acids or from polyamines and polycarboxylic acids
    • C08G69/26—Polyamides derived from amino-carboxylic acids or from polyamines and polycarboxylic acids derived from polyamines and polycarboxylic acids
    • C08G69/28—Preparatory processes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
    • B29B7/00—Mixing; Kneading
    • B29B7/80—Component parts, details or accessories; Auxiliary operations
    • B29B7/86—Component parts, details or accessories; Auxiliary operations for working at sub- or superatmospheric pressure

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Polyamides (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
CA000456498A 1983-06-15 1984-06-13 Continuous preparation of nylons Expired CA1216993A (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE3321581A DE3321581A1 (de) 1983-06-15 1983-06-15 Verfahren zur kontinuierlichen herstellung von polyamiden
DEP3321581.2 1983-06-15

Publications (1)

Publication Number Publication Date
CA1216993A true CA1216993A (en) 1987-01-20

Family

ID=6201544

Family Applications (1)

Application Number Title Priority Date Filing Date
CA000456498A Expired CA1216993A (en) 1983-06-15 1984-06-13 Continuous preparation of nylons

Country Status (5)

Country Link
US (1) US4537949A (2)
EP (1) EP0129195B1 (2)
JP (1) JPS608319A (2)
CA (1) CA1216993A (2)
DE (2) DE3321581A1 (2)

Families Citing this family (177)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3526931A1 (de) * 1985-07-27 1987-02-05 Bayer Ag Verfahren zur herstellung von poly(tetramethylenadipamid)
US5252661A (en) * 1987-07-17 1993-10-12 Basf Aktiengesellschaft Impact modifying rubber and partly aromatic copolyamides
US5298595A (en) * 1987-07-17 1994-03-29 Basf Aktiengesellschaft Partly aromatic copolyamides of reduced triamine content
DE3723688A1 (de) * 1987-07-17 1989-01-26 Basf Ag Teilaromatische copolyamide mit verringertem triamingehalt
DE3804392A1 (de) * 1988-02-12 1989-08-24 Basf Ag Fuellstoffhaltige polyamid-formmassen mit verbesserter oberflaeche und lackierbarkeit
US5504146A (en) * 1988-02-12 1996-04-02 Basf Aktiengesellschaft Toughened partly aromatic copolyamides
DE3804372A1 (de) * 1988-02-12 1989-08-24 Basf Ag Schlagzaeh modifizierte teilaromatische copolyamide
DE3820361A1 (de) * 1988-06-15 1989-12-21 Basf Ag Verfahren zur kontinuierlichen herstellung von aromatischen polykondensaten
DE3912769A1 (de) * 1989-04-19 1990-10-25 Basf Ag Verfahren zur herstellung von linearen polyamiden mit etherbruecken in der polymerkette
DE3912770A1 (de) * 1989-04-19 1990-10-25 Basf Ag Verfahren zur kontinuierlichen herstellung von nylon-4,6
DE3912768A1 (de) * 1989-04-19 1990-10-25 Basf Ag Verfahren zur kontinuierlichen herstellung von copolyamiden aus caprolactam und salzen aus diaminen und dicarbonsaeuren
US5218080A (en) * 1990-06-01 1993-06-08 Basf Corporation Constant composition recycle of nylon 6 polymerization wash water
US5077381A (en) * 1990-06-01 1991-12-31 Basf Corporation Constant compositioin recycle of nylon 6 polymerization wash water
DE4120007A1 (de) * 1991-06-18 1992-12-24 Basf Ag Thermoplastische formmassen auf der basis von teilaromatischen copolyamiden und polyolefinen
DE4121705A1 (de) * 1991-07-01 1993-01-07 Basf Ag Thermoplastische formmassen auf der basis von polyarylenethern und teilaromatischen copolyamiden
DE4202004C2 (de) * 1992-01-25 1994-03-24 Basf Ag Verfahren zur Herstellung füllstoffhaltiger thermoplastischer Formmassen und derart erhältliche Formmassen und deren Verwendung
DE4216042A1 (de) * 1992-05-15 1993-11-18 Basf Ag Thermoplastische Formmassen auf der Basis von Polyamiden und carboxylgruppenhaltigen Polyethylenwachsen
DE4403452A1 (de) * 1993-04-26 1994-10-27 Zimmer Ag Diskontinuierliches katalytisches Verfahren zur Herstellung von Polyamid-6.6
DE4429107A1 (de) 1994-08-17 1996-02-22 Basf Ag Formmassen aus Polyarylenethern und Copolyamiden
DE4430480A1 (de) 1994-08-27 1996-02-29 Basf Ag Hochmolekulare Polyamide aus Nitrilen
DE19514145A1 (de) * 1995-04-15 1996-10-17 Basf Ag Verfahren zur Herstellung eines Polyamids auf der Basis einer Dicarbonsäure und eines Diamins
DE19526855A1 (de) * 1995-07-22 1997-01-23 Basf Ag Verfahren zur Herstellung von Polyarylenethern mit Anhydridendgruppen
DE19543161A1 (de) 1995-11-18 1997-05-22 Basf Ag Verfahren zur Herstellung von verzweigten Polyamiden
DE19546417B4 (de) * 1995-12-12 2005-12-22 Karl-Heinz Wiltzer Verfahren und Vorrichtung zur vereinheitlichten, kontinuierlichen Herstellung von Polyamiden
US6169162B1 (en) 1999-05-24 2001-01-02 Solutia Inc. Continuous polyamidation process
DE10259266A1 (de) * 2002-12-17 2004-07-01 Basf Ag Thermoplastische Formmassen
DE102004029935B4 (de) * 2004-06-21 2007-08-09 Pe Polymer Engineering Gmbh & Co Forschungs Kg Verfahren zur kontinuierlichen Herstellung von Copolyamiden mit Schmelzpunkten oberhalb von 265 C
JP2006316493A (ja) * 2005-05-12 2006-11-24 Sekisui Chem Co Ltd 樋装置
DE102005049297A1 (de) * 2005-10-12 2007-04-19 Basf Ag Flammgeschützte Formmassen
EP1998944B1 (de) 2006-03-22 2015-10-28 Basf Se Verfahren zur granulierung von leichtsiederhaltigen polymerschmelzen
EP1998948B2 (de) 2006-03-22 2017-06-07 Basf Se Verfahren und vorrichtung zur granulierung von treibmittelhaltigen polymerschmelzen
DE502007002951D1 (de) 2006-07-26 2010-04-08 Basf Se Thermoplastische formmassen mit hoher steifigkeit
US7960477B2 (en) 2006-12-13 2011-06-14 Basf Se Polyamides with acrylate rubbers
CN101573413A (zh) 2006-12-19 2009-11-04 巴斯夫欧洲公司 具有改进延性的热塑性模塑组合物
DE102006062270A1 (de) * 2006-12-22 2008-06-26 Eckart Gmbh & Co. Kg Aluminiumgrieß für dünne, plättchenförmige Effektpigmente, Verfahren zu dessen Herstellung und Verwendung desselben
DE102006062269A1 (de) 2006-12-22 2008-06-26 Eckart Gmbh & Co. Kg Verwendung von sphärischen Metallpartikeln als Lasermarkierungs- oder Laserschweißbarkeitsmittel sowie lasermarkierbarer und/oder laserschweißbarer Kunststoff
MX2009008817A (es) 2007-02-19 2009-10-07 Basf Se Compuestos para moleado con reducida anisotropia respecto a la resistencia a choques.
FR2914308B1 (fr) * 2007-03-27 2009-05-01 Rhodia Recherches & Tech Procede de fabrication de polyamide
EP1988113B1 (de) 2007-05-03 2009-10-14 Ems-Patent Ag Teilaromatische Polyamidformmassen und deren Verwendungen
WO2008155281A1 (de) 2007-06-20 2008-12-24 Basf Se Verfahren zur herstellung von polyamiden
DE502007006117D1 (de) 2007-08-24 2011-02-10 Ems Patent Ag Mit flachen Glasfasern verstärkte Hochtemperatur-Polyamidformmassen
DE102008038411A1 (de) 2007-09-11 2009-03-12 Basf Se Flammgeschützte Polyamide
US8309221B2 (en) * 2007-10-01 2012-11-13 Jay Plaehn Reinforced foam panel
EP2060607B2 (de) 2007-11-16 2019-11-27 Ems-Patent Ag Gefüllte Polyamidformmassen
DE102008043863A1 (de) 2007-11-19 2009-05-20 Basf Se Teilaromatische Polyamide mit hyperverzweigten Polyoxazolinen
DE502007001931D1 (de) 2007-11-30 2009-12-17 Eckart Gmbh Verwendung einer Mischung mit sphärischen Metallpartikeln und Metallflakes als Lasermarkierungs- oder Laserschweissbarkeitsmittel sowie lasermarkierbarer und/oder laserschweissbarer Kunststoff
CN101903469B (zh) 2007-12-18 2014-08-20 巴斯夫欧洲公司 含有聚醚胺的热塑性聚酰胺
EP2247649B1 (de) 2008-01-31 2013-04-10 Basf Se Faserverstärkte polyamid[5,10] formmassen
CN101970555B (zh) 2008-02-11 2014-05-28 巴斯夫欧洲公司 由合成聚合物制备多孔结构的方法
WO2009101032A1 (de) 2008-02-11 2009-08-20 Basf Se Verfahren zur herstellung von polyamiden
DE102009011668A1 (de) 2008-03-05 2009-09-10 Basf Se Polyamid und hyperverzweigte Polyesster enthaltende Formmasse
KR20110028519A (ko) 2008-06-27 2011-03-18 바스프 에스이 규조토를 갖는 열 전도성 폴리아미드
WO2010000572A1 (de) * 2008-07-02 2010-01-07 Basf Se Schäumbare polyamide
DE102008046682A1 (de) 2008-09-10 2010-03-11 Basf Se Amorphe Polyamide
DE102008058246A1 (de) 2008-11-19 2010-05-20 Basf Se Hochmolekulare Polyamide
EP2379644B1 (de) 2008-12-16 2018-08-22 Basf Se Wärmealterungsbeständige polyamide
WO2010089241A1 (de) 2009-02-04 2010-08-12 Basf Se Schwarze, uv-stabile thermoplastische formmassen
US8889767B2 (en) 2009-02-06 2014-11-18 Styrolution GmbH Thermoplastic molding compounds based on styrene copolymers and polyamides having improved weathering resistance
EP2393877B1 (de) 2009-02-06 2012-12-05 Styrolution GmbH Styrolcopolymere und polyamide enthaltende thermoplastische formmassen
EP2401079B1 (de) 2009-02-26 2013-01-02 Styrolution GmbH Selbstreinigende polymere
DE102010028550A1 (de) 2009-05-05 2010-11-11 Basf Se Verfahren zur Herstellung von Eisen-Nanopartikel enthaltenden thermoplastischen Polymerformmassen
EP2435231B1 (de) 2009-05-26 2014-02-12 Basf Se Wasser als treibmittel für polyurethane
US9080259B2 (en) 2009-06-30 2015-07-14 Basf Se Polyamide fibers with dyeable particles and production thereof
WO2011000816A1 (de) 2009-07-03 2011-01-06 Basf Se Nanokompositblends enthaltend polyamide und polyolefine
WO2011009798A1 (de) 2009-07-21 2011-01-27 Basf Se Nanokompositblends auf basis von polyamiden und polyarylenethersulfonen
WO2011009877A1 (de) 2009-07-24 2011-01-27 Basf Se Flammgeschützte polyamidformmassen
DE102009035974A1 (de) 2009-08-04 2011-02-17 Basf Se Amorphe Polyamide
CN102666693A (zh) 2009-10-27 2012-09-12 巴斯夫欧洲公司 具有阻燃性的耐热老化性聚酰胺
PH12012500717A1 (en) 2009-10-27 2012-10-29 Basf Se Polyamide resistant to heat aging
WO2011069942A1 (de) 2009-12-08 2011-06-16 Basf Se Teilaromatische copolyamidformmassen auf der basis von octamethylendiamin
ES2639062T3 (es) 2009-12-08 2017-10-25 Basf Se Proceso para la preparación de poliamidas
BR112012013905B1 (pt) 2009-12-09 2019-09-24 Basf Se Composição de moldagem de copoliamida semiaromática, semicristalina, uso das composições de moldagem de copoliamida, e, corpo moldado
DE102010062886A1 (de) 2009-12-16 2011-06-22 Basf Se, 67063 Polyarylenethersulfone als Schlagzähmodifier
EP2526152B1 (de) 2010-01-18 2014-01-08 Styrolution GmbH Verfahren zur herstellung von thermoplastischen formmassen auf basis von styrolcopolymeren und polyamid mit verbesserter zähigkeit
US20110178205A1 (en) 2010-01-18 2011-07-21 Martin Weber Process for producing thermoplastic molding compositions based on styrene copolymers and polyamide with improved toughness
US8466221B2 (en) 2010-03-09 2013-06-18 Basf Se Polyamides that resist heat-aging
CN102791798B (zh) 2010-03-09 2015-09-09 巴斯夫欧洲公司 耐热老化性聚酰胺
US20110237693A1 (en) * 2010-03-23 2011-09-29 Basf Se Blends made of polyarylene ethers and of polyarylene sulfides
WO2011134930A1 (de) 2010-04-30 2011-11-03 Basf Se Langfaserverstärkte polyamide mit polyolefinen
EP2388293B1 (de) 2010-05-17 2012-12-26 Ems-Patent Ag Polyamidformmasse und deren Verwendung zur Herstellung von LED-Gehäusekomponenten
DE102010023770A1 (de) 2010-06-15 2011-12-15 Basf Se Glühdrahtbeständige Formmassen
BR112012031898B1 (pt) 2010-06-15 2019-12-24 Basf Se composição de moldagem termoplástica, uso das composições de moldagem, e, fibra, folha metálica ou peça moldada
US8563680B2 (en) 2010-06-15 2013-10-22 Basf Se Heat-aging-resistant polyamides
WO2012013564A1 (de) 2010-07-30 2012-02-02 Basf Se Flammgeschützte formmassen
EP2415827A1 (de) 2010-08-04 2012-02-08 Basf Se Flammgeschützte Polyamide mit Schichtsilikaten
WO2012062594A1 (de) 2010-11-11 2012-05-18 Basf Se Wärmealterungsbeständige polyamide
WO2012065977A1 (de) 2010-11-18 2012-05-24 Basf Se Thermoplastische formmassen auf basis von styrolcopolymeren und polyamiden; verfahren zu deren herstellung und deren verwendung
DE102010051726A1 (de) 2010-11-19 2012-05-24 Basf Se Amorphe Polyamide mit bicyclischen aliphatischen Diaminen
DE102010051708A1 (de) 2010-11-19 2012-05-24 Basf Se Amorphe Polyamide mit dialkylsubstituierten Diaminen
KR101905206B1 (ko) 2010-11-23 2018-10-05 바스프 에스이 표면 상에 나노입자를 갖는 폴리아미드
US9296896B2 (en) 2010-11-23 2016-03-29 Basf Se Polyamides with nanoparticles on the surface
KR101950360B1 (ko) 2010-12-16 2019-02-21 바스프 에스이 글로우 와이어 내성 폴리아미드
US8575295B2 (en) 2010-12-16 2013-11-05 Basf Se Glow-wire resistant polyamides
US20130345353A1 (en) 2010-12-20 2013-12-26 Basf Se Thermoplastic molding compounds on the basis of styrene copolymers and polyamides having improved low-temperature toughness
EP2468811A1 (de) 2010-12-21 2012-06-27 Basf Se Thermoplastische Formmasse
EP2468812A1 (de) 2010-12-21 2012-06-27 Basf Se Thermoplastische Formmasse
ES2542007T3 (es) 2011-01-18 2015-07-29 Basf Se Masas moldeables termoplásticas
US8629220B2 (en) 2011-01-18 2014-01-14 Basf Se Hydrolysis-resistant polyamides
JP5959536B2 (ja) 2011-01-18 2016-08-02 ビーエーエスエフ ソシエタス・ヨーロピアＢａｓｆ Ｓｅ 加水分解安定性のポリアミド
US8629206B2 (en) 2011-01-20 2014-01-14 Basf Se Flame-retardant thermoplastic molding composition
DE102011103882A1 (de) 2011-03-25 2012-09-27 Eckart Gmbh Kupferhaltige Metallpigmente mit Metalloxidschicht und Kunststoffschicht, Verfahren zu deren Herstellung, Beschichtungsmittel und beschichteter Gegenstand
CN103492778A (zh) 2011-04-21 2014-01-01 巴斯夫欧洲公司 用于将传热介质管固定至容器的装置
BR112013027454A2 (pt) 2011-04-28 2019-09-24 Basf Se composição de moldagem termoplástica, uso das composições de moldagem termoplástica, e, fibra, folha ou moldagem
US8653168B2 (en) 2011-05-10 2014-02-18 Basf Se Flame-retardant thermoplastic molding composition
EP2527402A1 (de) 2011-05-27 2012-11-28 Basf Se Thermoplastische Formmasse
US8987357B2 (en) 2011-05-27 2015-03-24 Basf Se Thermoplastic molding composition
DE102011104303A1 (de) 2011-06-03 2012-12-06 Basf Se Photovoltaik-System zur Installation auf Dächern mit Kunststoffträger und Photovoltaik-Modul
EP2535365B1 (de) 2011-06-17 2013-09-25 Ems-Patent Ag Teilaromatische Formmassen und deren Verwendungen
JP6049730B2 (ja) 2011-09-15 2016-12-21 ビーエーエスエフ ソシエタス・ヨーロピアＢａｓｆ Ｓｅ 赤リン含有難燃性ポリアミド用の安定剤としての銀／酸化亜鉛混合物
US8883904B2 (en) 2011-09-15 2014-11-11 Basf Se Mixtures of silver and zinc oxide as stabilizer for flame-retardant polyamides
EP2573138A1 (de) 2011-09-21 2013-03-27 Basf Se Polyamid-Formmassen
US20150291793A1 (en) 2011-09-29 2015-10-15 Styrolution GmbH Stabilized moulding compounds consisting of polyamide and asa-copolymers
WO2013053649A1 (de) 2011-10-13 2013-04-18 Styrolution GmbH Stabilisierte polyamid-abs formmassen
CN103073716B (zh) * 2011-10-26 2016-02-03 江苏文凤化纤集团有限公司 一种尼龙66连续聚合余热利用方法
JP6124910B2 (ja) 2011-11-25 2017-05-10 ビーエーエスエフ ソシエタス・ヨーロピアＢａｓｆ Ｓｅ ブロー成形可能なポリアミド成形材料
WO2013083508A1 (de) 2011-12-07 2013-06-13 Basf Se Flammgeschützte polyamide mit flüssigkristallinen polyestern
KR20140117459A (ko) 2012-01-11 2014-10-07 스티롤루션 유럽 게엠베하 스티렌 공중합체 및 폴리아미드를 기재로 한 향상된 인성을 갖는 내후성 열가소성 성형 배합물
KR101925174B1 (ko) 2012-02-20 2018-12-04 바스프 에스이 난연성 폴리아미드를 위한 안정화제로서 CuO/ZnO 화합물
EP2641939A1 (de) 2012-03-21 2013-09-25 Basf Se Hellgefärbte flammgeschützte Polyamide
EP2644647B1 (de) 2012-03-26 2014-10-29 LANXESS Deutschland GmbH Thermoplastische Formmassen mit erhöhter Hydrolyse-Beständigkeit
EP2650331A1 (de) 2012-04-11 2013-10-16 Basf Se Polyamide für Trinkwasseranwendungen
EP2666803B1 (de) 2012-05-23 2018-09-05 Ems-Patent Ag Kratzfeste, transparente und zähe Copolyamidformmassen, hieraus hergestellte Formkörper und deren Verwendung
JP6203255B2 (ja) 2012-06-18 2017-09-27 ビーエーエスエフ ソシエタス・ヨーロピアＢａｓｆ Ｓｅ ポリアクリロニトリルのホモポリマーを有する難燃性ポリアミド
DK2898009T3 (en) 2012-09-19 2017-01-30 Basf Se FIRE-RESISTANT POLYAMIDS WITH LIGHT COLOR
EP2716716B1 (de) 2012-10-02 2018-04-18 Ems-Patent Ag Polyamid-Formmassen und deren Verwendung bei der Herstellung von Formkörpern
EP2746339B1 (de) 2012-12-18 2014-11-12 Ems-Patent Ag Polyamid-Formmasse und hieraus hergestellte Formkörper
EP2778190B1 (de) 2013-03-15 2015-07-15 Ems-Patent Ag Polyamidformmasse sowie hieraus hergestellter Formkörper
BR112015020979B8 (pt) 2013-04-15 2020-07-07 Basf Se uso de compostos termoplásticos de moldagem e corpo de moldagem
EP2796870A1 (de) 2013-04-24 2014-10-29 Basf Se Verfahren zur Bestimmung der Dicke von Ablagerungen
CN113830951A (zh) * 2013-05-01 2021-12-24 英威达纺织（英国）有限公司 用于从聚酰胺合成工艺回收水的方法和系统
EP2813530A1 (de) 2013-06-12 2014-12-17 Basf Se Teilaromatische Copolyamide auf Basis von Terephthalsäure und Hexamethylendiamin
WO2014198764A1 (de) 2013-06-12 2014-12-18 Basf Se Verfahren zur herstellung teilaromatischer copolyamide mit hohem diaminüberschuss
CN105308096B (zh) 2013-06-12 2019-10-15 巴斯夫欧洲公司 具有高玻璃化转变温度和高结晶度的半芳族共聚酰胺
WO2015024913A1 (de) 2013-08-21 2015-02-26 Basf Se Verfahren zur herstellung eines compositkunststoffteils (ck)
US10030110B2 (en) 2013-08-21 2018-07-24 Basf Se Composite plastic part with improved resistance to heat aging
JP6169280B2 (ja) 2013-08-21 2017-07-26 ビーエーエスエフ ソシエタス・ヨーロピアＢａｓｆ Ｓｅ 部材に含まれるプラスチック構成部分間の付着が改善された複合プラスチック部材
DE102014215370A1 (de) 2013-09-05 2015-03-05 Basf Se Langfaserverstärkte flammgeschützte Polyamide
EP2878630B1 (de) 2013-11-28 2019-11-20 LANXESS Deutschland GmbH Polyamidzusammensetzungen
KR20160101998A (ko) 2013-12-18 2016-08-26 이네오스 스티롤루션 그룹 게엠베하 3-d 프린팅용의 비닐방향족/디엔 블록 공중합체에 기초한 몰딩 재료들의 용도
EP3083824B1 (de) 2013-12-18 2017-09-27 INEOS Styrolution Group GmbH Formmassen basierend auf vinylaromat-copolymeren für den 3d druck
EP2886605B2 (de) 2013-12-20 2021-09-01 Ems-Chemie Ag Kunststoffformmasse und deren Verwendung
EP2902444B1 (de) 2014-01-31 2018-01-17 Ems-Patent Ag Polyamid-Formmassen mit flammhemmenden Eigenschaften und sehr guter Langzeitwärmealterungsbeständigkeit
DE102015215118A1 (de) 2014-08-26 2016-03-03 Basf Se Polyamide mit 2,6-BAMP-Derivaten
EP3006506B9 (de) 2014-10-08 2017-07-19 Ems-Patent Ag Fliessfähige Polyamide
WO2016087324A1 (de) 2014-12-01 2016-06-09 Basf Se Flammgeschützte polyamide mit sulfonsäuresalzen
GB201421293D0 (en) 2014-12-01 2015-01-14 Xeros Ltd New cleaning method, apparatus and use
BR112017011157B1 (pt) 2014-12-01 2022-10-11 Basf Se Partículas de poliamida termoplástica, método para produzir partículas de poliamida termoplástica e uso de partículas de poliamida termoplástica
BR112017022063B1 (pt) 2015-04-16 2022-10-11 Basf Se Usos de composições de moldagem termoplástica e de moldagens transparentes
CN107810239A (zh) 2015-06-19 2018-03-16 巴斯夫欧洲公司 具有高的熔体流动和良好的机械性能的聚酰胺组合物
EP3118247A1 (de) 2015-07-15 2017-01-18 Basf Se Polyamide mit besseren optischen eigenschaften
EP3130633A1 (de) 2015-08-13 2017-02-15 Basf Se Polyamide mit guter mechanik und schwindung
EP3135730A1 (de) 2015-08-27 2017-03-01 Basf Se Polyamide mit niedrigem kristallisationspunkt und geringer schwindung
EP3448916B1 (en) 2016-04-26 2020-10-14 Basf Se Thermoplastic polyamide particles
WO2017216023A1 (de) 2016-06-15 2017-12-21 Basf Se Schlagzähmodifier basierend auf polyisobuten für polyamide
JP7082605B2 (ja) 2016-07-13 2022-06-08 エーエムエス－パテント アクチェンゲゼルシャフト 伝導性熱可塑性ポリアミド成形コンパウンド
CN109844001B (zh) 2016-10-13 2022-03-11 巴斯夫欧洲公司 阻燃性聚酰胺
WO2018141552A1 (en) 2017-02-01 2018-08-09 Basf Se Polyarylene ether sulfone comprising naphthalic acid anhydride endgroups
US11685832B2 (en) 2017-03-01 2023-06-27 Basf Se Fire-retardant polyamides comprising PVP
JP7196107B2 (ja) 2017-06-22 2022-12-26 ビーエーエスエフ ソシエタス・ヨーロピア リン及びＡｌ－ホスホネートを有するポリアミド
EP3827035B1 (en) 2018-07-24 2022-06-15 INEOS Styrolution Group GmbH Polyacrylate graft rubber copolymer and impact modified thermoplastic molding composition
MX2021000725A (es) 2018-07-24 2021-04-12 Ineos Styrolution Group Gmbh Copolimero de caucho de injerto de poliacrilato y composicion de moldeo termoplastica.
EP3808810B1 (de) 2019-10-16 2023-03-29 INEOS Styrolution Group GmbH Thermoplastische formmassen für rotomolding-verfahren
EP4110869B1 (en) 2020-02-26 2024-04-10 Basf Se Heat-aging resistant polyamide molding compositions
US20230203304A1 (en) 2020-03-20 2023-06-29 Basf Se Plasticized polyamide molding compositions
US20230129664A1 (en) 2020-03-25 2023-04-27 Basf Se Heat-aging resistant polyamide molding compositions
US20240010792A1 (en) 2020-12-07 2024-01-11 Basf Se Aqueous lactam solution of lignin
EP4063091A1 (de) * 2021-03-26 2022-09-28 Starlinger & Co Gesellschaft m.b.H. Vorrichtung und verfahren zur wärmebehandlung von thermoplastischen kunststoffschmelzen
EP4337453A1 (de) 2021-05-11 2024-03-20 Basf Se LASERBESCHRIFTETE UND LASERVERSCHWEIßTE FORMKÖRPER UND DEREN HERSTELLUNG
US20240239936A1 (en) 2021-05-25 2024-07-18 Ineos Styrolution Group Gmbh Acrylic rubber for thermoplastic material with good low temperature impact strength
WO2022248262A1 (en) 2021-05-26 2022-12-01 Basf Se Process for preparing polyamides
US20250019542A1 (en) 2021-11-23 2025-01-16 Basf Se Compositions comprising polyarylene(ether)sulfones
WO2023237603A1 (en) 2022-06-08 2023-12-14 Basf Se Recycling method for producing a polyamide compound
EP4594423A1 (en) 2022-09-27 2025-08-06 Basf Se Thermoplastic moulding compositions having an improved colour stability-1
CN120322498A (zh) 2022-11-17 2025-07-15 巴斯夫欧洲公司 混合金属氧化物组合物作为阻燃聚酰胺的稳定剂
WO2025049564A1 (en) 2023-08-29 2025-03-06 Basf Se Polyamide molding compositions with improved heat-aging resistance
WO2025252781A1 (en) 2024-06-05 2025-12-11 Basf Se Flame retardant polyamides for improved lsr compression set
EP4722289A1 (en) 2024-10-02 2026-04-08 Evonik Oxeno GmbH & Co. KG Polyamide composition

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
NL129670C (2) * 1961-04-26
NL129245C (2) * 1964-06-01
CA1015894A (en) * 1973-03-05 1977-08-16 Du Pont Of Canada Limited Preparation of polyamides by continuous polymerization
US4019866A (en) * 1973-03-05 1977-04-26 Du Pont Of Canada Limited Recirculating reaction apparatus for continuous preparation of a polyamide
US3948862A (en) * 1974-05-06 1976-04-06 E. I. Du Pont De Nemours And Company Continuous process for preparing aliphatic polycarbonamides

Also Published As

Publication number Publication date
EP0129195A2 (de) 1984-12-27
EP0129195B1 (de) 1987-12-23
DE3468224D1 (en) 1988-02-04
JPH0460138B2 (2) 1992-09-25
EP0129195A3 (en) 1985-12-18
DE3321581A1 (de) 1984-12-20
US4537949A (en) 1985-08-27
JPS608319A (ja) 1985-01-17

Similar Documents

Publication Publication Date Title
CA1216993A (en) Continuous preparation of nylons
US4540772A (en) Continuous preparation of nylon from aqueous salt solution in precondensation zone having baffles
US5081222A (en) Partly aromatic copolyamide of reduced triamine content
US5039786A (en) Continuous preparation of copolyamides from caprolactam and salt of diamine and dicarboxylic acid
JP3459067B2 (ja) 低分子ポリアミドの連続的製造法
US5596070A (en) High molecular weight polyamides obtained from nitriles
JP5174143B2 (ja) ポリアミドの製造方法
KR101672066B1 (ko) 락탐 및 디아민과 디카르복실산의 염으로부터 코폴리아미드의 연속 제조 방법
CN1207746A (zh) 统一连续制备聚酰胺的方法和设备
US4539391A (en) Continuous hydrolytic preparation of polylactams
US4327208A (en) Continuous process for the hydrolytic production of polycaprolactam having a low-monomer and low-dimer content
CN105013196B (zh) 用于制备聚酰胺的装置、原料浓缩方法、以及聚酰胺的生产设备、生产方法
US5298595A (en) Partly aromatic copolyamides of reduced triamine content
US5030709A (en) Continuous preparation of copolyamides
CN1219944A (zh) 连续制备聚酰胺的方法和装置
JP2001514281A (ja) ポリアミドの調製方法
EP0160337B1 (en) Process for the preparation of polytetramethylene adipamide
US5218082A (en) Partly aromatic copolyamide of reduced triamine content
US5051491A (en) Process for the preparation of a linear polyamide having ether bridges in the polymer chain
US6258926B1 (en) Process and device for producing high-viscosity or highly stabilized reaction-stable polyamides, and for continuously demonomerizing polyamides
CN105085904B (zh) 一种用于制备聚酰胺5x的装置、终聚方法及聚酰胺5x的生产设备、方法
US20050209436A1 (en) Method and device for the continuous production of polyamide 6, 6 and copolyamides thereof
US4994550A (en) Process for the continuous preparation of nylon 4,6 from aqueous salt solution

Legal Events

Date Code Title Description
MKEX Expiry