WO2023127204A1 - ポリビニルアセタール樹脂組成物、無機微粒子分散用ビヒクル組成物、無機微粒子分散スラリー組成物、及び、積層セラミクスコンデンサ - Google Patents
ポリビニルアセタール樹脂組成物、無機微粒子分散用ビヒクル組成物、無機微粒子分散スラリー組成物、及び、積層セラミクスコンデンサ Download PDFInfo
- Publication number
- WO2023127204A1 WO2023127204A1 PCT/JP2022/034186 JP2022034186W WO2023127204A1 WO 2023127204 A1 WO2023127204 A1 WO 2023127204A1 JP 2022034186 W JP2022034186 W JP 2022034186W WO 2023127204 A1 WO2023127204 A1 WO 2023127204A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyvinyl acetal
- acetal resin
- weight
- inorganic fine
- less
- Prior art date
Abstract
本発明は、有機溶剤への溶解性が高く、また、有機溶剤に溶解した場合に微細な未溶解物が少ないポリビニルアセタール樹脂組成物を提供する。更に、未溶解物由来の酸素欠陥が発生し難く、優れた特性を有するセラミクス積層体を製造することが可能であるポリビニルアセタール樹脂組成物を提供する。また、該ポリビニルアセタール樹脂組成物を含む無機微粒子分散用ビヒクル組成物、無機微粒子分散スラリー組成物、該無機微粒子分散スラリー組成物を用いてなる積層セラミクスコンデンサを提供する。 本発明は、ポリビニルアセタール樹脂及び陽イオン界面活性剤を含有する組成物であって、前記ポリビニルアセタール樹脂の一次粒子径が0.01μm以上10μm以下であり、陽イオン界面活性剤を、前記ポリビニルアセタール樹脂100重量部に対して1×10-6重量部以上10000×10-6重量部以下含有する、ポリビニルアセタール樹脂組成物である。
Description
本発明は、ポリビニルアセタール樹脂組成物、無機微粒子分散用ビヒクル組成物、無機微粒子分散スラリー組成物、及び、積層セラミクスコンデンサに関する。
近年、種々の電子機器に搭載される電子部品の小型化、積層化が進んでおり、多層回路基板、積層コイル、積層セラミクスコンデンサ等の積層型電子部品が広く使用されている。
なかでも、積層セラミクスコンデンサは、一般に次のような工程を経て製造されている。
まず、ポリビニルブチラール樹脂やポリ(メタ)アクリル酸エステル系樹脂等のバインダー樹脂を有機溶剤に溶解した溶液に可塑剤、分散剤等を添加した後、セラミック原料粉末を加え、ビーズミル、ボールミル等の混合装置により均一に混合し、脱泡後に一定粘度を有するセラミックスラリー組成物を得る。このスラリー組成物をドクターブレード、リバースロールコーター等を用いて、離型処理したポリエチレンテレフタレートフィルム又はSUSプレート等の支持体面に流延して、加熱等により溶剤等の揮発分を溜去させた後、支持体から剥離してセラミックグリーンシートを得る。
次に、得られたセラミックグリーンシート上に、内部電極となる導電ペーストをスクリーン印刷により塗布したものを交互に複数枚積み重ね、加熱圧着して積層体を作製する。その後、積層体中に含まれるバインダー樹脂成分等を熱分解して除去する処理、いわゆる脱脂処理を行い、更に焼成して得られるセラミック焼結体の端面に外部電極を焼結する工程を経て積層セラミクスコンデンサが得られる。
なかでも、積層セラミクスコンデンサは、一般に次のような工程を経て製造されている。
まず、ポリビニルブチラール樹脂やポリ(メタ)アクリル酸エステル系樹脂等のバインダー樹脂を有機溶剤に溶解した溶液に可塑剤、分散剤等を添加した後、セラミック原料粉末を加え、ビーズミル、ボールミル等の混合装置により均一に混合し、脱泡後に一定粘度を有するセラミックスラリー組成物を得る。このスラリー組成物をドクターブレード、リバースロールコーター等を用いて、離型処理したポリエチレンテレフタレートフィルム又はSUSプレート等の支持体面に流延して、加熱等により溶剤等の揮発分を溜去させた後、支持体から剥離してセラミックグリーンシートを得る。
次に、得られたセラミックグリーンシート上に、内部電極となる導電ペーストをスクリーン印刷により塗布したものを交互に複数枚積み重ね、加熱圧着して積層体を作製する。その後、積層体中に含まれるバインダー樹脂成分等を熱分解して除去する処理、いわゆる脱脂処理を行い、更に焼成して得られるセラミック焼結体の端面に外部電極を焼結する工程を経て積層セラミクスコンデンサが得られる。
セラミックグリーンシートの作製に用いられるポリビニルアセタール樹脂は、一般にメチルエチルケトン、トルエン、アルコール及びこれらの混合物等の有機溶剤に溶解された溶液として用いられる。しかしながら、従来のポリビニルアセタール樹脂は、有機溶剤に溶解した場合に微量の未溶解物が生じていた。このような未溶解物が存在すると、積層セラミクスコンデンサに用いた場合に、脱脂工程及び焼成工程においてボイドが残りやすくなったり、セラミック粉末等の分散性が低下したりすることにより、得られる製品の電気特性が低下していた。
このため、ポリビニルアセタール樹脂をセラミックグリーンシートの用途に使用する際には、有機・無機化合物等を配合し、有機溶剤で溶解した後、濾過工程を行うことにより、未溶解物を除去する必要があった。
このため、ポリビニルアセタール樹脂をセラミックグリーンシートの用途に使用する際には、有機・無機化合物等を配合し、有機溶剤で溶解した後、濾過工程を行うことにより、未溶解物を除去する必要があった。
これに対して、特許文献1では、メチルエチルケトン及び/又はトルエンとエタノールとの1:1混合溶剤に溶解して5重量%溶液としたポリビニルアセタール樹脂溶液を、目開き5μmのフィルタを用い、濾過温度25℃、濾過圧10mmHgの条件で濾過したときの濾過流量の低下率が10%未満であるポリビニルアセタール樹脂が提案されている。また、このようなポリビニルアセタール樹脂を用いることで、有機溶剤に溶解した場合に未溶解物が少なく、濾過時間を短縮できることにより、生産性を向上できるとされている。
一方、近年では、電子機器の多機能化、小型化に伴い、積層セラミクスコンデンサは、大容量化小型化が求められている。このような要求に対応するためには、より微細な未溶解物を充分に除去する必要があるが、特許文献1に記載のポリビニルアセタール樹脂であっても、より微細な未溶解物を充分に除去することができず、未溶解物を濾過等により除去する必要があり、生産性が低下するという問題がある。また、一次粒子径が0.1~1μm程度の微小な未溶解物は濾過濃縮できないという問題がある。
本発明は、有機溶剤への溶解性が高く、また、有機溶剤に溶解した場合に微細な未溶解物が少ないポリビニルアセタール樹脂組成物を提供することを目的とする。更に、未溶解物由来の酸素欠陥が発生し難く、優れた特性を有するセラミクス積層体を製造することが可能であるポリビニルアセタール樹脂組成物を提供することを目的とする。また、該ポリビニルアセタール樹脂組成物を含む無機微粒子分散用ビヒクル組成物、無機微粒子分散スラリー組成物、該無機微粒子分散スラリー組成物を用いてなる積層セラミクスコンデンサを提供することを目的とする。
本開示(1)は、ポリビニルアセタール樹脂及び陽イオン界面活性剤を含有する組成物であって、前記ポリビニルアセタール樹脂の一次粒子径が0.01μm以上10μm以下であり、陽イオン界面活性剤を、前記ポリビニルアセタール樹脂100重量部に対して1×10-6重量部以上10000×10-6重量部以下含有する、ポリビニルアセタール樹脂組成物である。
本開示(2)は、ポリビニルアセタール樹脂は、重合度が1500以上2000以下、水酸基量が25.0モル%以上35.0モル%以下、アセタール基量が60.0モル%以上70.0モル%以下、アセチル基量が0.1モル%以上0.5モル%以下である、本開示(1)のポリビニルアセタール樹脂組成物である。
本開示(3)は、陽イオン界面活性剤は、エタノールへの溶解度が0.001g/100g以上である、本開示(1)又は(2)のポリビニルアセタール樹脂組成物である。
本開示(4)は、パラトルエンスルホン酸又はその塩を、ポリビニルアセタール樹脂100重量部に対して1×10-6重量部以上500×10-6重量部以下含有する、本開示(1)~(3)のいずれかとの任意の組み合わせのポリビニルアセタール樹脂組成物である。
本開示(5)は、ポリビニルアセタール樹脂は、レーザー回折散乱式粒度分布測定法により二次粒子径を測定し小粒径側から体積基準累積10%、50%、90%の粒子径をそれぞれD10、D50、D90としたとき、(D90-D10)/D50が0.7以上1.5以下である、本開示(1)~(4)のいずれかとの任意の組み合わせのポリビニルアセタール樹脂組成物である。
本開示(6)は、ポリビニルアセタール樹脂は、重量平均分子量Mwと数平均分子量Mnとの比率である分子量分布(Mw/Mn)が1.8以上2.6以下である、本開示(1)~(5)のいずれかとの任意の組み合わせのポリビニルアセタール樹脂組成物である。
本開示(7)は、本開示(1)~(6)のいずれかのポリビニルアセタール樹脂組成物、及び、有機溶剤を含有する、無機微粒子分散用ビヒクル組成物である。
本開示(8)は、本開示(7)の無機微粒子分散用ビヒクル組成物、無機微粒子、及び、可塑剤を含有する、無機微粒子分散スラリー組成物である。
本開示(9)は、本開示(8)の無機微粒子分散スラリー組成物を用いてなる、積層セラミクスコンデンサである。
以下に本発明を詳述する。
本開示(2)は、ポリビニルアセタール樹脂は、重合度が1500以上2000以下、水酸基量が25.0モル%以上35.0モル%以下、アセタール基量が60.0モル%以上70.0モル%以下、アセチル基量が0.1モル%以上0.5モル%以下である、本開示(1)のポリビニルアセタール樹脂組成物である。
本開示(3)は、陽イオン界面活性剤は、エタノールへの溶解度が0.001g/100g以上である、本開示(1)又は(2)のポリビニルアセタール樹脂組成物である。
本開示(4)は、パラトルエンスルホン酸又はその塩を、ポリビニルアセタール樹脂100重量部に対して1×10-6重量部以上500×10-6重量部以下含有する、本開示(1)~(3)のいずれかとの任意の組み合わせのポリビニルアセタール樹脂組成物である。
本開示(5)は、ポリビニルアセタール樹脂は、レーザー回折散乱式粒度分布測定法により二次粒子径を測定し小粒径側から体積基準累積10%、50%、90%の粒子径をそれぞれD10、D50、D90としたとき、(D90-D10)/D50が0.7以上1.5以下である、本開示(1)~(4)のいずれかとの任意の組み合わせのポリビニルアセタール樹脂組成物である。
本開示(6)は、ポリビニルアセタール樹脂は、重量平均分子量Mwと数平均分子量Mnとの比率である分子量分布(Mw/Mn)が1.8以上2.6以下である、本開示(1)~(5)のいずれかとの任意の組み合わせのポリビニルアセタール樹脂組成物である。
本開示(7)は、本開示(1)~(6)のいずれかのポリビニルアセタール樹脂組成物、及び、有機溶剤を含有する、無機微粒子分散用ビヒクル組成物である。
本開示(8)は、本開示(7)の無機微粒子分散用ビヒクル組成物、無機微粒子、及び、可塑剤を含有する、無機微粒子分散スラリー組成物である。
本開示(9)は、本開示(8)の無機微粒子分散スラリー組成物を用いてなる、積層セラミクスコンデンサである。
以下に本発明を詳述する。
本発明者らは、一次粒子径が所定範囲のポリビニルアセタール樹脂を合成することで溶剤への溶解性が向上し、未溶解物が少なくなることを見出した。更に所定量の陽イオン界面活性剤を添加することで、小粒径のポリビニルアセタール樹脂を凝集させることができることを見出した。また、一次粒子径が従来のポリビニルアセタール樹脂よりも小さいため、溶解時間も短縮できることを見出した。また、このようなポリビニルアセタール樹脂組成物を用いることにより、シート欠陥が発生し難く信頼性の高い積層セラミクスコンデンサを得ることができるセラミックグリーンシートを作製することができることを見出し、本発明を完成させるに至った。
本発明のポリビニルアセタール樹脂組成物は、ポリビニルアセタール樹脂を含有する。
上記ポリビニルアセタール樹脂は微粒子形状を有するものである。
上記ポリビニルアセタール樹脂は、一次粒子径が0.01μm以上10μm以下である。
このようなポリビニルアセタール樹脂を用いることで、溶媒に溶解した際にも未溶解物が非常に少なくなり、溶解時間を短縮することができる。また、ポリビニルアセタール樹脂の粒子径等の形状や組成にバラつきが少なくなり、信頼性の高い積層セラミクスコンデンサを得ることができる。
上記ポリビニルアセタール樹脂の一次粒子径は、濾液中に含まれる微細な粒子を少なくできることから、0.05μm以上であることが好ましく、0.1μm以上であることがより好ましい。また、溶解時間を短縮できることから、5μm以下であることが好ましく、3μm以下であることがより好ましく、1μm以下であることが更に好ましい。
なお、一次粒子とは凝集前の粒子1個を意味し、二次粒子とは凝集した粒子を意味する。
上記ポリビニルアセタール樹脂の一次粒子径のCV値は15%以上であることが好ましく、20%以上であることがより好ましく、40%以下であることが好ましく、35%以下であることがより好ましい。
上記の範囲とすることで溶剤への溶解性を高め、不溶成分を少なくすることができる。
上記ポリビニルアセタール樹脂の一次粒子径は、走査型電子顕微鏡(例えば、日立ハイテクノロジーズ社製「Regulus8220」)を用いて観察し、100個の一次粒子の最大フェレー径を測定し、その平均値により求めることができる。最大フェレー径とは、粒子の対向する輪郭線に接した平行する接線間の最大距離のことである。
上記一次粒子径は、ポリビニルアセタール樹脂を製造する際に用いる陰イオン界面活性剤の種類と量を調整することでミセルのサイズを制御することにより調整することができる。
上記ポリビニルアセタール樹脂は微粒子形状を有するものである。
上記ポリビニルアセタール樹脂は、一次粒子径が0.01μm以上10μm以下である。
このようなポリビニルアセタール樹脂を用いることで、溶媒に溶解した際にも未溶解物が非常に少なくなり、溶解時間を短縮することができる。また、ポリビニルアセタール樹脂の粒子径等の形状や組成にバラつきが少なくなり、信頼性の高い積層セラミクスコンデンサを得ることができる。
上記ポリビニルアセタール樹脂の一次粒子径は、濾液中に含まれる微細な粒子を少なくできることから、0.05μm以上であることが好ましく、0.1μm以上であることがより好ましい。また、溶解時間を短縮できることから、5μm以下であることが好ましく、3μm以下であることがより好ましく、1μm以下であることが更に好ましい。
なお、一次粒子とは凝集前の粒子1個を意味し、二次粒子とは凝集した粒子を意味する。
上記ポリビニルアセタール樹脂の一次粒子径のCV値は15%以上であることが好ましく、20%以上であることがより好ましく、40%以下であることが好ましく、35%以下であることがより好ましい。
上記の範囲とすることで溶剤への溶解性を高め、不溶成分を少なくすることができる。
上記ポリビニルアセタール樹脂の一次粒子径は、走査型電子顕微鏡(例えば、日立ハイテクノロジーズ社製「Regulus8220」)を用いて観察し、100個の一次粒子の最大フェレー径を測定し、その平均値により求めることができる。最大フェレー径とは、粒子の対向する輪郭線に接した平行する接線間の最大距離のことである。
上記一次粒子径は、ポリビニルアセタール樹脂を製造する際に用いる陰イオン界面活性剤の種類と量を調整することでミセルのサイズを制御することにより調整することができる。
上記ポリビニルアセタール樹脂は、薄膜セラミックグリーンシートを作製する場合に機械的強度を充分に高めることができるため、重合度が300以上であることが好ましく、600以上であることがより好ましく、1500以上であることが更に好ましい。また、有機溶剤への溶解性や溶解粘度の観点から、重合度が8000以下であることが好ましく、7000以下であることがより好ましく、2000以下であることが更に好ましい。
上記ポリビニルアセタール樹脂は、下記式(1)で表されるアセタール基を有する構成単位、下記式(2)で表される水酸基を有する構成単位、下記式(3)で表されるアセチル基を有する構成単位を有することが好ましい。
上記式(1)中、R1は水素原子又は炭素数1~20のアルキル基を表す。
上記式(1)中、R1が炭素数1~20のアルキル基である場合、該アルキル基としては、例えば、メチル基、エチル基、n-プロピル基、イソプロピル基、n-ブチル基、iso-ブチル基、sec-ブチル基、tert-ブチル基、ペンチル基、へキシル基、へプチル基、2-エチルヘキシル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、オクタデシル基等が挙げられる。なかでも、メチル基、n-プロピル基が好ましい。
上記ポリビニルアセタール樹脂において、上記式(1)で表されるアセタール基を有する構成単位の含有量(以下、「アセタール基量」ともいう)は、有機溶剤への溶解性の観点から、45.0モル%以上であることが好ましく、50.0モル%以上であることがより好ましく、55.0モル%以上であることが更に好ましく、60.0モル%以上であることが特に好ましい。また、強靭性に優れたポリビニルアセタール樹脂とできることから、80.0モル%以下であることが好ましく、78.0モル%以下であることがより好ましく、76.0モル%以下であることが更に好ましく、70.0モル%以下であることが特に好ましい。
上記アセタール基量は、例えば、NMRにより測定することができる。
なお、アセタール基量の計算方法については、ポリビニルアセタール樹脂のアセタール基がポリビニルアルコールの2個の水酸基をアセタール化して得られたものであることから、アセタール化された2個の水酸基を数える方法を採用する。
上記アセタール基量は、例えば、NMRにより測定することができる。
なお、アセタール基量の計算方法については、ポリビニルアセタール樹脂のアセタール基がポリビニルアルコールの2個の水酸基をアセタール化して得られたものであることから、アセタール化された2個の水酸基を数える方法を採用する。
上記ポリビニルアセタール樹脂において、上記式(2)で表される水酸基を有する構成単位の含有量(以下、「水酸基量」ともいう)は、強靭性に優れたポリビニルアセタール樹脂とできることから、18.0モル%以上であることが好ましく、20.0モル%以上であることがより好ましく、22.0モル%以上であることが更に好ましく、25.0モル%以上であることが特に好ましい。また、有機溶剤への溶解性の観点から、40.0モル%以下であることが好ましく、39.0モル%以下であることがより好ましく、38.0モル%以下であることが更に好ましく、35.0モル%以下であることが特に好ましい。
上記水酸基量は、例えば、NMRにより測定することができる。
上記水酸基量は、例えば、NMRにより測定することができる。
上記ポリビニルアセタール樹脂において、上記式(3)で表されるアセチル基を有する構成単位の含有量(以下、「アセチル基量」ともいう)は、ポリビニルアセタール樹脂中の水酸基の分子内及び分子間の水素結合によるセラミックグリーンシート用組成物の高粘度化を抑制できることから、0.01モル%以上であることが好ましく、0.05モル%以上であることがより好ましく、0.1モル%以上であることが更に好ましい。また、ポリビニルアセタール樹脂合成時のミセル径を小さくでき、より微小な粒子とできるため、5.0モル%以下であることが好ましく、3.0モル%以下であることがより好ましく、1.0モル%以下であることが更に好ましく、0.5モル%以下であることが特に好ましい。
上記アセチル基量は、例えば、NMRにより測定することができる。
上記アセチル基量は、例えば、NMRにより測定することができる。
上記ポリビニルアセタール樹脂は、重量平均分子量(Mw)が200,000以上であることが好ましく、250,000以上であることがより好ましく、450,000以下であることが好ましく、400,000以下であることがより好ましい。上記の範囲とすることでグリーンシートの強度を向上させつつ溶解性を向上させることができる。
上記ポリビニルアセタール樹脂は、数平均分子量(Mn)が10,000以上であることが好ましく、11,000以上であることがより好ましく、180,000以下であることが好ましく、170,000以下であることがより好ましい。上記の範囲とすることでグリーンシートの強度を向上させつつ溶解性を向上させることができる。
上記ポリビニルアセタール樹脂は、重量平均分子量(Mw)と数平均分子量(Mn)との比率である分子量分布(Mw/Mn)が1.0以上であることが好ましく、1.8以上であることがより好ましく、2.0以上であることが更に好ましく、2.6以下であることが好ましく、2.5以下であることがより好ましく、2.4以下であることが更に好ましい。上記範囲とすることで、溶解性を向上させることができる。
上記Mw、Mnは例えば、適切な標準(例えば、ポリスチレン標準)を用いたゲル浸透クロマトグラフィー(GPC)によって測定することができる。上記Mw、Mnを測定する際に用いるカラムとしては、例えば、TSKgel SuperHZM-H等が挙げられる。
上記ポリビニルアセタール樹脂は、数平均分子量(Mn)が10,000以上であることが好ましく、11,000以上であることがより好ましく、180,000以下であることが好ましく、170,000以下であることがより好ましい。上記の範囲とすることでグリーンシートの強度を向上させつつ溶解性を向上させることができる。
上記ポリビニルアセタール樹脂は、重量平均分子量(Mw)と数平均分子量(Mn)との比率である分子量分布(Mw/Mn)が1.0以上であることが好ましく、1.8以上であることがより好ましく、2.0以上であることが更に好ましく、2.6以下であることが好ましく、2.5以下であることがより好ましく、2.4以下であることが更に好ましい。上記範囲とすることで、溶解性を向上させることができる。
上記Mw、Mnは例えば、適切な標準(例えば、ポリスチレン標準)を用いたゲル浸透クロマトグラフィー(GPC)によって測定することができる。上記Mw、Mnを測定する際に用いるカラムとしては、例えば、TSKgel SuperHZM-H等が挙げられる。
上記ポリビニルアセタール樹脂は、レーザー回折散乱式粒度分布測定法により二次粒子径を測定し小粒径側から体積基準累積10%、50%、90%の粒子径をそれぞれD10、D50、D90としたとき、(D90-D10)/D50が0.7以上であることが好ましく、0.8以上であることがより好ましく、0.9以上であることが更に好ましい。また、1.5以下であることが好ましく、1.4以下であることがより好ましく、1.3以下であることが更に好ましい。
上記範囲とすることで、溶解性を向上させることができる。
レーザー回折散乱式粒度分布測定法によるD10、D50、D90の測定は、例えば、堀場製作所社製レーザー回折/散乱式粒子径分布測定装置 LA-950を用いて、ポリビニルアセタール樹脂を分散させた水溶液を装置に供給することにより行うことができる。
上記範囲とすることで、溶解性を向上させることができる。
レーザー回折散乱式粒度分布測定法によるD10、D50、D90の測定は、例えば、堀場製作所社製レーザー回折/散乱式粒子径分布測定装置 LA-950を用いて、ポリビニルアセタール樹脂を分散させた水溶液を装置に供給することにより行うことができる。
上記ポリビニルアセタール樹脂は、製造時の濾過工程において目詰まりを防止するという観点から、D10が40μm以上であることが好ましく、50μm以上であることがより好ましく、60μm以上であることが更に好ましい。また、溶解時間の短縮という観点から、D10が140μm以下であることが好ましく、130μm以下であることがより好ましく、120μm以下であることが更に好ましい。
上記ポリビニルアセタール樹脂は、製造時の濾過工程において目詰まりを防止するという観点から、D50が100μm以上であることが好ましく、110μm以上であることがより好ましく、120μm以上であることが更に好ましい。また、溶解時間の短縮という観点から、D50が200μm以下であることが更に好ましく、190μm以下であることがより好ましく、180μm以下であることが更に好ましい。
上記ポリビニルアセタール樹脂は、製造時の濾過工程において目詰まりを防止するという観点から、D90が180μm以上であることが好ましく、190μm以上であることがより好ましく、200μm以上であることが更に好ましい。また、溶解時間の短縮という観点から、D90が280μm以下であることが好ましく、270μm以下であることがより好ましく、260μm以下であることが更に好ましい。
上記D10、D50、D90、(D90-D10)/D50はポリビニルアセタール樹脂を製造する際に用いる陽イオン界面活性剤の種類及び量により調整することができる。
本発明のポリビニルアセタール樹脂組成物における上記ポリビニルアセタール樹脂の含有量は、95重量%以上であることが好ましく、97重量%以上であることがより好ましく、100重量%以下であることが好ましく、99重量%以下であることがより好ましい。
上記ポリビニルアセタール樹脂は、通常、ポリビニルアルコール樹脂をアセタール化することにより製造することができる。
上記ポリビニルアルコール樹脂としては、例えば、ポリ酢酸ビニル系樹脂をアルカリ、酸、アンモニア水等によりけん化することにより製造された樹脂等の従来公知のポリビニルアルコール樹脂を用いることができる。
上記ポリビニルアルコール樹脂は、完全けん化されていてもよいが、少なくとも主鎖の1カ所にメソ、ラセモ位に対して2連の水酸基を有するユニットが最低1ユニットあれば完全けん化されている必要はなく、部分けん化ポリビニルアルコール樹脂であってもよい。
上記ポリビニルアルコール樹脂は、完全けん化されていてもよいが、少なくとも主鎖の1カ所にメソ、ラセモ位に対して2連の水酸基を有するユニットが最低1ユニットあれば完全けん化されている必要はなく、部分けん化ポリビニルアルコール樹脂であってもよい。
上記ポリビニルアルコール樹脂は、ケン化度が90.0モル%以上であることが好ましく、95.0モル%以上であることがより好ましく、99.5モル%以上であることが更に好ましく、99.99モル%以下であることが好ましく、99.95モル%以下であることがより好ましく、99.9モル%以下であることが更に好ましい。
上記範囲とすることで、有機スルホン酸触媒、陰イオン界面活性剤と組み合わせることで均一で小さなミセルを形成することができ、それらミセル内でアセタール化させることで未溶解成分を少なくすることができる。
上記範囲とすることで、有機スルホン酸触媒、陰イオン界面活性剤と組み合わせることで均一で小さなミセルを形成することができ、それらミセル内でアセタール化させることで未溶解成分を少なくすることができる。
上記アセタール化は、例えば、水中、水と水との相溶性のある有機溶剤との混合溶剤中、又は有機溶剤中にポリビニルアルコール樹脂を加えて溶解し、更に、陰イオン界面活性剤、有機スルホン酸触媒等の酸触媒、アルデヒドを加えてホモジナイザー等で攪拌し、乳化させたミセルを形成して、ミセル中で反応を進行させることにより行うことができる。上記ミセルはポリビニルアルコール樹脂と陰イオン界面活性剤と酸触媒とアルデヒドから形成されるものである。
上記のような方法を用いることで微細であり、粒子径等の形状や組成にバラつきが少ないポリビニルアセタール樹脂とすることができる。また、酸触媒として有機スルホン酸触媒を用いることで、塩酸触媒等を用いる場合等に必要となる低温への冷却の必要がなく、高品質のポリビニルアセタール樹脂を効率的に生産することができる。
上記のような方法を用いることで微細であり、粒子径等の形状や組成にバラつきが少ないポリビニルアセタール樹脂とすることができる。また、酸触媒として有機スルホン酸触媒を用いることで、塩酸触媒等を用いる場合等に必要となる低温への冷却の必要がなく、高品質のポリビニルアセタール樹脂を効率的に生産することができる。
上記水との相溶性のある有機溶剤としては、例えば、アルコール系有機溶剤を用いることができる。
上記有機溶剤としては、例えば、アルコール系有機溶剤、芳香族有機溶剤、脂肪族エステル系溶剤、ケトン系溶剤、低級パラフィン系溶剤、エーテル系溶剤、アミド系溶剤、アミン系溶剤等が挙げられる。
上記アルコール系有機溶剤としては、例えば、メタノール、エタノール、n-プロパノール、イソプロパノール、n-ブタノール、tert-ブタノール等が挙げられる。
上記芳香族有機溶剤としては、例えば、キシレン、トルエン、エチルベンゼン、安息香酸メチル等が挙げられる。
上記脂肪族エステル系溶剤としては、例えば、酢酸メチル、酢酸エチル、酢酸ブチル、プロピオン酸メチル、プロピオン酸エチル、酪酸メチル、酪酸エチル、アセト酢酸メチル、アセト酢酸エチル等が挙げられる。
上記ケトン系溶剤としては、例えば、アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン、メチルシクロヘキサノン、ベンゾフェノン、アセトフェノン等が挙げられる。
上記低級パラフィン系溶剤としては、ヘキサン、ペンタン、オクタン、シクロヘキサン、デカン等が挙げられる。
上記エーテル系溶剤としては、ジエチルエーテル、テトラヒドロフラン、エチレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、プロピレングリコールジエチルエーテル等が挙げられる。
上記アミド系溶剤としては、N,N-ジメチルホルムアミド、N,N-ジメチルテセトアミド、N-メチルピロリドン、アセトアニリド等が挙げられる。
上記アミン系溶剤としては、アンモニア、トリメチルアミン、トリエチルアミン、n-ブチルアミン、ジn-ブチルアミン、トリn-ブチルアミン、アニリン、N-メチルアニリン、N,N-ジメチルアニリン、ピリジン等が挙げられる。
これらは、単体で用いることもできるし、2種以上の溶剤を混合で用いることもできる。これらのなかでも、樹脂溶解性及び精製時の簡易性の観点から、エタノール、n-プロパノール、イソプロパノール、テトラヒドロフランが特に好ましい。
上記有機溶剤としては、例えば、アルコール系有機溶剤、芳香族有機溶剤、脂肪族エステル系溶剤、ケトン系溶剤、低級パラフィン系溶剤、エーテル系溶剤、アミド系溶剤、アミン系溶剤等が挙げられる。
上記アルコール系有機溶剤としては、例えば、メタノール、エタノール、n-プロパノール、イソプロパノール、n-ブタノール、tert-ブタノール等が挙げられる。
上記芳香族有機溶剤としては、例えば、キシレン、トルエン、エチルベンゼン、安息香酸メチル等が挙げられる。
上記脂肪族エステル系溶剤としては、例えば、酢酸メチル、酢酸エチル、酢酸ブチル、プロピオン酸メチル、プロピオン酸エチル、酪酸メチル、酪酸エチル、アセト酢酸メチル、アセト酢酸エチル等が挙げられる。
上記ケトン系溶剤としては、例えば、アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン、メチルシクロヘキサノン、ベンゾフェノン、アセトフェノン等が挙げられる。
上記低級パラフィン系溶剤としては、ヘキサン、ペンタン、オクタン、シクロヘキサン、デカン等が挙げられる。
上記エーテル系溶剤としては、ジエチルエーテル、テトラヒドロフラン、エチレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、プロピレングリコールジエチルエーテル等が挙げられる。
上記アミド系溶剤としては、N,N-ジメチルホルムアミド、N,N-ジメチルテセトアミド、N-メチルピロリドン、アセトアニリド等が挙げられる。
上記アミン系溶剤としては、アンモニア、トリメチルアミン、トリエチルアミン、n-ブチルアミン、ジn-ブチルアミン、トリn-ブチルアミン、アニリン、N-メチルアニリン、N,N-ジメチルアニリン、ピリジン等が挙げられる。
これらは、単体で用いることもできるし、2種以上の溶剤を混合で用いることもできる。これらのなかでも、樹脂溶解性及び精製時の簡易性の観点から、エタノール、n-プロパノール、イソプロパノール、テトラヒドロフランが特に好ましい。
上記水、混合溶剤又は有機溶剤の添加量は、ポリビニルアルコール樹脂100重量部に対して500重量部以上であることが好ましく、600重量部以上であることがより好ましく、2000重量部以下であることが好ましく、1800重量部以下であることがより好ましい。
上記範囲とすることで、アセタール化の際に安定したミセルを形成することができる。
上記範囲とすることで、アセタール化の際に安定したミセルを形成することができる。
上記陰イオン界面活性剤は、乳化重合の際に添加される乳化剤として用いられるものが挙げられ、例えば、アルキルスルホン酸塩等が挙げられる。
上記アルキルスルホン酸塩としては、オクチルスルホン酸、デシルスルホン酸、ドデシルスルホン酸等のナトリウム塩、カリウム塩、アンモニウム塩等が挙げられる。
上記アルキルスルホン酸塩としては、オクチルスルホン酸、デシルスルホン酸、ドデシルスルホン酸等のナトリウム塩、カリウム塩、アンモニウム塩等が挙げられる。
上記陰イオン界面活性剤の添加量は、ポリビニルアルコール樹脂100重量部に対して0.5重量部以上であることが好ましく、2重量部以上であることがより好ましく、200重量部以下であることが好ましく、70重量部以下であることがより好ましい。
上記範囲とすることで、アセタール化の際に安定したミセルを形成することができる。
上記範囲とすることで、アセタール化の際に安定したミセルを形成することができる。
上記酸触媒としては、硫酸、塩酸、硝酸、リン酸等の鉱酸や、ギ酸、酢酸、プロピオン酸等のカルボン酸や、ドデシルスルホン酸、ラウリルスルホン酸等のアルキルスルホン酸、ベンゼンスルホン酸、パラトルエンスルホン酸等の芳香族スルホン酸、ポリオキシエチレンスルホン酸等の有機スルホン酸等のスルホン酸等が挙げられる。なかでも、スルホン酸が好ましく、乳化剤としても作用することからパラトルエンスルホン酸、ベンゼンスルホン酸等の芳香族スルホン酸、ドデシルスルホン酸、ラウリルスルホン酸等のアルキルスルホン酸、ミセル形成性に優れたポリオキシエチレンスルホン酸等が好ましい。また、パラトルエンスルホン酸がより好ましい。
酸触媒として塩酸を用いる方法では、粒子径を制御するために低温で触媒を添加する必要があるが、酸触媒としてスルホン酸を用いる場合、反応系を低温とする必要がない。
酸触媒として塩酸を用いる方法では、粒子径を制御するために低温で触媒を添加する必要があるが、酸触媒としてスルホン酸を用いる場合、反応系を低温とする必要がない。
上記酸触媒の添加量は、ポリビニルアセタール樹脂100重量部に対して5重量部以上であることが好ましく、20重量部以上であることがより好ましく、200重量部以下であることが好ましく、70重量部以下であることがより好ましい。
上記範囲とすることで、アセタール化の際に安定したミセルを形成することができる。
上記範囲とすることで、アセタール化の際に安定したミセルを形成することができる。
上記ポリビニルアセタール樹脂の製造方法では、溶剤中にポリビニルアルコール樹脂を添加した後、90℃以上の温度で2時間以上攪拌することでポリビニルアルコール樹脂を溶解させることが好ましい。また、その後、常温に戻し、アルデヒド、陰イオン界面活性剤、スルホン酸触媒等の酸触媒を添加し、高速撹拌機で乳化させ、30~50℃に加熱することでアセタール化を反応させることが好ましい。
上記操作を行うことで、ポリビニルアルコール樹脂が充分に溶解し、アセタール基量を充分に高くして、未溶解物の発生を抑制することができる。
上記操作を行うことで、ポリビニルアルコール樹脂が充分に溶解し、アセタール基量を充分に高くして、未溶解物の発生を抑制することができる。
上記アセタール化に用いられるアルデヒドは、特に限定されるものではなく、例えば、脂肪族アルデヒド、芳香族アルデヒド等が挙げられる。
上記脂肪族アルデヒドとしては、ホルムアルデヒド、アセトアルデヒド、プロピオンアルデヒド、n-ブチルアルデヒド、イソブチルアルデヒド、n-バレルアルデヒド、n-ヘキシルアルデヒド、2-エチルブチルアルデヒド、2-エチルヘキシルアルデヒド、n-ヘプチルアルデヒド、n-オクチルアルデヒド、n-ノニルアルデヒド、n-デシルアルデヒド、アミルアルデヒド等が挙げられる。
上記芳香族アルデヒドとしては、ベンズアルデヒド、シンナムアルデヒド、2-メチルベンズアルデヒド、3-メチルベンズアルデヒド、4-メチルベンズアルデヒド、p-ヒドロキシベンズアルデヒド、m-ヒドロキシベンズアルデヒド、フェニルアセトアルデヒド、β-フェニルプロピオンアルデヒド等が挙げられる。
これらのアルデヒドは、1種を単独で使用してもよく、2種以上を併用してもよい。
上記脂肪族アルデヒドとしては、ホルムアルデヒド、アセトアルデヒド、プロピオンアルデヒド、n-ブチルアルデヒド、イソブチルアルデヒド、n-バレルアルデヒド、n-ヘキシルアルデヒド、2-エチルブチルアルデヒド、2-エチルヘキシルアルデヒド、n-ヘプチルアルデヒド、n-オクチルアルデヒド、n-ノニルアルデヒド、n-デシルアルデヒド、アミルアルデヒド等が挙げられる。
上記芳香族アルデヒドとしては、ベンズアルデヒド、シンナムアルデヒド、2-メチルベンズアルデヒド、3-メチルベンズアルデヒド、4-メチルベンズアルデヒド、p-ヒドロキシベンズアルデヒド、m-ヒドロキシベンズアルデヒド、フェニルアセトアルデヒド、β-フェニルプロピオンアルデヒド等が挙げられる。
これらのアルデヒドは、1種を単独で使用してもよく、2種以上を併用してもよい。
上記アルデヒドの添加量は、ポリビニルアセタール樹脂のアセタール基量にあわせて適宜設定することができる。特に、ポリビニルアルコール樹脂100重量部に対して300重量部以上であることが好ましく、400重量部以上であることがより好ましく、1500重量部以下であることが好ましく、1000重量部以下であることがより好ましい。
上記範囲とすることで、アセタール化度を好ましい範囲に調整とすることができる。
上記範囲とすることで、アセタール化度を好ましい範囲に調整とすることができる。
上記アセタール化は、反応槽にポリビニルアルコール、陰イオン界面活性剤、有機スルホン酸触媒、アルデヒドを計量した状態で混合液を乳化させることが好ましい。
乳化させる手段については特に限定されないが、ホモジナイザーやディスパー等の高速撹拌機や真空乳化装置等があげられる。
上記乳化装置を用いると激しく泡立つことがあるので、消泡剤を添加してもよい。消泡剤は特に限定されないが、シリコーン系消泡剤、ポリアセチレン系消泡剤、低極性アルコール消泡剤等が挙げられる。なかでも、少量で効果の高い、シリコーン系消泡剤が好ましい。
乳化させる手段については特に限定されないが、ホモジナイザーやディスパー等の高速撹拌機や真空乳化装置等があげられる。
上記乳化装置を用いると激しく泡立つことがあるので、消泡剤を添加してもよい。消泡剤は特に限定されないが、シリコーン系消泡剤、ポリアセチレン系消泡剤、低極性アルコール消泡剤等が挙げられる。なかでも、少量で効果の高い、シリコーン系消泡剤が好ましい。
上記アセタール化反応の反応温度は、15℃以上であることが好ましく、20℃以上であることがより好ましく、30℃以上であることが更に好ましく、50℃以下であることが好ましく、40℃以下であることがより好ましい。
また、反応時間は1.5時間以上であることが好ましく、2時間以上であることが好ましく、8時間以下であることが好ましく、7時間以下であることがより好ましい。
また、反応時間は1.5時間以上であることが好ましく、2時間以上であることが好ましく、8時間以下であることが好ましく、7時間以下であることがより好ましい。
上記ポリビニルアセタール樹脂の製造方法では、アルカリによる中和を行うことが好ましい。
上記アルカリとしては、例えば、水酸化ナトリウム、水酸化カリウム、アンモニア、酢酸ナトリウム、炭酸ナトリウム、炭酸水素ナトリウム、炭酸カリウム、炭酸水素カリウム等が挙げられる。
また、上記中和工程の前後に、水等を用いて得られたポリビニルアセタール樹脂を洗浄することが好ましい。なお、洗浄水中に含まれる不純物の混入を防ぐため、洗浄は純水で行うことがより好ましい。
上記アルカリとしては、例えば、水酸化ナトリウム、水酸化カリウム、アンモニア、酢酸ナトリウム、炭酸ナトリウム、炭酸水素ナトリウム、炭酸カリウム、炭酸水素カリウム等が挙げられる。
また、上記中和工程の前後に、水等を用いて得られたポリビニルアセタール樹脂を洗浄することが好ましい。なお、洗浄水中に含まれる不純物の混入を防ぐため、洗浄は純水で行うことがより好ましい。
本発明において、得られたポリビニルアセタール樹脂は一次粒子径が0.01μm以上10μm以下の微粒子形状で水中に分散している。
この状態では濾布による濾過が難しく、更に、後述する陽イオン界面活性剤を添加して凝集させる必要がある。
この状態では濾布による濾過が難しく、更に、後述する陽イオン界面活性剤を添加して凝集させる必要がある。
本発明のポリビニルアルコール樹脂組成物は、上記ポリビニルアセタール樹脂100重量部に対して、陽イオン界面活性剤を1×10-6重量部以上10000×10-6重量部以下含有する。
上記ポリビニルアセタール樹脂に対して、所定量の陽イオン界面活性剤を加えることで、微細なポリビニルアセタール樹脂を凝集させることができ、微細な未溶解物を少なくすることができる。また、陰イオン界面活性剤や有機スルホン酸触媒等の酸触媒を濾過洗浄により容易に除去することができる。
上記陽イオン界面活性剤の含有量は、5×10-6重量部以上であることが好ましく、10×10-6重量部以上であることがより好ましく、500×10-6重量部以下であることが好ましく、100×10-6重量部以下であることがより好ましい。
上記陽イオン界面活性剤の含有量は、例えば、DART-MS(直接イオン化質量分析)により確認することができる。
上記ポリビニルアセタール樹脂に対して、所定量の陽イオン界面活性剤を加えることで、微細なポリビニルアセタール樹脂を凝集させることができ、微細な未溶解物を少なくすることができる。また、陰イオン界面活性剤や有機スルホン酸触媒等の酸触媒を濾過洗浄により容易に除去することができる。
上記陽イオン界面活性剤の含有量は、5×10-6重量部以上であることが好ましく、10×10-6重量部以上であることがより好ましく、500×10-6重量部以下であることが好ましく、100×10-6重量部以下であることがより好ましい。
上記陽イオン界面活性剤の含有量は、例えば、DART-MS(直接イオン化質量分析)により確認することができる。
上記陽イオン界面活性剤としては、第4級アンモニウム塩、脂肪族アミン塩、芳香族アミン塩、複素環式アミン塩等のアミン塩、ホスホニウム塩等が挙げられる。
上記第4級アンモニウム塩としては、例えば、テトラエチルアンモニウムクロリド、テトラエチルアンモニウムブロミド、テトラブチルアンモニウムブロミド、テトラブチルアンモニウムクロリド、ヘキシルトリメチルアンモニウムブロミド、n-オクチルトリメチルアンモニウムブロミド、n-オクチルトリメチルアンモニウムクロリド、ノニルトリメチルアンモニウムブロミド、デシルトリメチルアンモニウムクロリド、デシルトリメチルアンモニウムブロミド、ドデシルトリメチルアンモニウムクロリド、ドデシルトリメチルアンモニウムブロミド、テトラデシルトリメチルアンモニウムブロミド、テトラデシルトリメチルアンモニウムクロリド、ヘキサデシルトリメチルアンモニウムクロリド、ヘキサデシルトリメチルアンモニウムブロミド、ヘキサデシルトリメチルアンモニウムヘキサフルオロホスファート、ヘキサデシルトリメチルアンモニウムテトラフルオロボラート、過塩素酸ヘキサデシルトリメチルアンモニウム、ヘキサデシルトリメチルアンモニウムヒドロキシド、ヘキサデシルトリメチルアンモニウム硫酸水素塩、ヘプタデシルトリメチルアンモニウムブロミド、オクタデシルトリメチルアンモニウムクロリド、オクタデシルトリメチルアンモニウムブロミド、ベンジルドデシルジメチルアンモニウムクロリド、ベンジルドデシルジメチルアンモニウムブロミド、ベンジルジメチルテトラデシルアンモニウムクロリド、ベンジルヘキサデシルジメチルアンモニウムクロリド、ベンジルジメチルオクタデシルアンモニウムクロリド、塩化ベンザルコニウム、ベンゼトニウムクロリド、ドデカン-1-イル(エチル)(ジメチル)アンモニウム=エチル=スルファート、ジステアリルジメチルアンモニウムクロライド、ドコシルトリメチルアンモニウムクロライド、1-ドデシルピリジニウムクロリド、ヘキサデシルピリジニウムクロリド、ヘキサデシルピリジニウムブロミド、1-ヘキサデシル-4-メチルピリジニウムクロリド、塩化1-エチル-3-メチルイミダゾリウム、塩化セチルピリジニウム、塩化ベンゼトニウム等が挙げられる。
上記アミン塩としては、n-オクチルアンモニウムクロリド、n-オクチルアンモニウムブロミド、ドデシルアミン塩酸塩、ドデシルアンモニウムブロミド、オクタデシルアミン塩酸塩等が挙げられる。
上記ホスホニウム塩としては、例えば、trans-2-ブテン-1,4-ビス(トリフェニルホスホニウムクロリド)、トリブチル(シアノメチル)ホスホニウムクロリド、(2-カルボキシエチル)トリフェニルホスホニウムブロミド、トリブチルドデシルホスホニウムブロミド、トリブチルヘキサデシルホスホニウムブロミド、トリブチル-n-オクチルホスホニウムブロミド、テトラキス(ヒドロキシメチル)ホスホニウムクロリド、テトラフェニルホスホニウムブロミド、テトラキス(ヒドロキシメチル)ホスホニウムスルファート、テトラブチルホスホニウムブロミド、テトラフェニルホスホニウムクロリド、テトラエチルホスホニウムブロミド、テトラブチルホスホニウムクロリド、テトラ-n-オクチルホスホニウムブロミド、テトラエチルホスホニウムヘキサフルオロホスファート、テトラエチルホスホニウムテトラフルオロボラート、テトラブチルホスホニウムテトラフルオロボラート、テトラブチルホスホニウムヘキサフルオロホスファート、テトラブチルホスホニウムテトラフェニルボラート、トリブチルヘキシルホスホニウムブロミド等が挙げられる。
なかでも、第4級アンモニウム塩、複素環式アミン塩、ホスホニウム塩が好ましく、第4級アンモニウム塩がより好ましく、塩化1-エチル-3-メチルイミダゾリウム、塩化セチルピリジニウム、テトラブチルアンモニウムブロミド、テトラブチルアンモニウムクロリド、ヘキシルトリメチルアンモニウムブロミド、n-オクチルトリメチルアンモニウムブロミド、n-オクチルトリメチルアンモニウムクロリド、ノニルトリメチルアンモニウムブロミド、デシルトリメチルアンモニウムクロリド、デシルトリメチルアンモニウムブロミド、ドデシルトリメチルアンモニウムクロリド、ドデシルトリメチルアンモニウムブロミド、テトラデシルトリメチルアンモニウムブロミド、テトラデシルトリメチルアンモニウムクロリド、ヘキサデシルトリメチルアンモニウムクロリド、オクタデシルトリメチルアンモニウムクロリド、ベンジルドデシルジメチルアンモニウムクロリド、ドデカン-1-イル(エチル)(ジメチル)アンモニウム=エチル=スルファート、ヘキサデシルトリメチルアンモニウムブロミド、テトラエチルアンモニウムブロミド、塩化ベンゼトニウムが更に好ましい。
上記第4級アンモニウム塩としては、例えば、テトラエチルアンモニウムクロリド、テトラエチルアンモニウムブロミド、テトラブチルアンモニウムブロミド、テトラブチルアンモニウムクロリド、ヘキシルトリメチルアンモニウムブロミド、n-オクチルトリメチルアンモニウムブロミド、n-オクチルトリメチルアンモニウムクロリド、ノニルトリメチルアンモニウムブロミド、デシルトリメチルアンモニウムクロリド、デシルトリメチルアンモニウムブロミド、ドデシルトリメチルアンモニウムクロリド、ドデシルトリメチルアンモニウムブロミド、テトラデシルトリメチルアンモニウムブロミド、テトラデシルトリメチルアンモニウムクロリド、ヘキサデシルトリメチルアンモニウムクロリド、ヘキサデシルトリメチルアンモニウムブロミド、ヘキサデシルトリメチルアンモニウムヘキサフルオロホスファート、ヘキサデシルトリメチルアンモニウムテトラフルオロボラート、過塩素酸ヘキサデシルトリメチルアンモニウム、ヘキサデシルトリメチルアンモニウムヒドロキシド、ヘキサデシルトリメチルアンモニウム硫酸水素塩、ヘプタデシルトリメチルアンモニウムブロミド、オクタデシルトリメチルアンモニウムクロリド、オクタデシルトリメチルアンモニウムブロミド、ベンジルドデシルジメチルアンモニウムクロリド、ベンジルドデシルジメチルアンモニウムブロミド、ベンジルジメチルテトラデシルアンモニウムクロリド、ベンジルヘキサデシルジメチルアンモニウムクロリド、ベンジルジメチルオクタデシルアンモニウムクロリド、塩化ベンザルコニウム、ベンゼトニウムクロリド、ドデカン-1-イル(エチル)(ジメチル)アンモニウム=エチル=スルファート、ジステアリルジメチルアンモニウムクロライド、ドコシルトリメチルアンモニウムクロライド、1-ドデシルピリジニウムクロリド、ヘキサデシルピリジニウムクロリド、ヘキサデシルピリジニウムブロミド、1-ヘキサデシル-4-メチルピリジニウムクロリド、塩化1-エチル-3-メチルイミダゾリウム、塩化セチルピリジニウム、塩化ベンゼトニウム等が挙げられる。
上記アミン塩としては、n-オクチルアンモニウムクロリド、n-オクチルアンモニウムブロミド、ドデシルアミン塩酸塩、ドデシルアンモニウムブロミド、オクタデシルアミン塩酸塩等が挙げられる。
上記ホスホニウム塩としては、例えば、trans-2-ブテン-1,4-ビス(トリフェニルホスホニウムクロリド)、トリブチル(シアノメチル)ホスホニウムクロリド、(2-カルボキシエチル)トリフェニルホスホニウムブロミド、トリブチルドデシルホスホニウムブロミド、トリブチルヘキサデシルホスホニウムブロミド、トリブチル-n-オクチルホスホニウムブロミド、テトラキス(ヒドロキシメチル)ホスホニウムクロリド、テトラフェニルホスホニウムブロミド、テトラキス(ヒドロキシメチル)ホスホニウムスルファート、テトラブチルホスホニウムブロミド、テトラフェニルホスホニウムクロリド、テトラエチルホスホニウムブロミド、テトラブチルホスホニウムクロリド、テトラ-n-オクチルホスホニウムブロミド、テトラエチルホスホニウムヘキサフルオロホスファート、テトラエチルホスホニウムテトラフルオロボラート、テトラブチルホスホニウムテトラフルオロボラート、テトラブチルホスホニウムヘキサフルオロホスファート、テトラブチルホスホニウムテトラフェニルボラート、トリブチルヘキシルホスホニウムブロミド等が挙げられる。
なかでも、第4級アンモニウム塩、複素環式アミン塩、ホスホニウム塩が好ましく、第4級アンモニウム塩がより好ましく、塩化1-エチル-3-メチルイミダゾリウム、塩化セチルピリジニウム、テトラブチルアンモニウムブロミド、テトラブチルアンモニウムクロリド、ヘキシルトリメチルアンモニウムブロミド、n-オクチルトリメチルアンモニウムブロミド、n-オクチルトリメチルアンモニウムクロリド、ノニルトリメチルアンモニウムブロミド、デシルトリメチルアンモニウムクロリド、デシルトリメチルアンモニウムブロミド、ドデシルトリメチルアンモニウムクロリド、ドデシルトリメチルアンモニウムブロミド、テトラデシルトリメチルアンモニウムブロミド、テトラデシルトリメチルアンモニウムクロリド、ヘキサデシルトリメチルアンモニウムクロリド、オクタデシルトリメチルアンモニウムクロリド、ベンジルドデシルジメチルアンモニウムクロリド、ドデカン-1-イル(エチル)(ジメチル)アンモニウム=エチル=スルファート、ヘキサデシルトリメチルアンモニウムブロミド、テトラエチルアンモニウムブロミド、塩化ベンゼトニウムが更に好ましい。
上記陽イオン界面活性剤は、エタノールへの溶解度が0.001g/100g以上であることが好ましく、0.005g/100g以上であることがより好ましい。
エタノールへの溶解度が上記下限値以上である陽イオン界面活性剤を用いることで、陽イオン界面活性剤の樹脂への多大な残留を防ぐことができる。
上記エタノールへの溶解度は、25℃での溶解度を用いることができる。
エタノールへの溶解度が上記下限値以上である陽イオン界面活性剤を用いることで、陽イオン界面活性剤の樹脂への多大な残留を防ぐことができる。
上記エタノールへの溶解度は、25℃での溶解度を用いることができる。
本発明のポリビニルアセタール樹脂組成物は、パラトルエンスルホン酸又はその塩を含有していてもよい。
本発明のポリビニルアセタール樹脂組成物における上記パラトルエンスルホン酸又はその塩の含有量は、上記ポリビニルアセタール樹脂100重量部に対して1×10-6重量部以上であることが好ましく、500×10-6重量部以下であることが好ましい。
上記範囲とすることで、上記陰イオン界面活性剤との相互作用により2次凝集が維持され、使用段階で微粉の発生を抑えることができる。
上記パラトルエンスルホン酸又はその塩の含有量は、1×10-6重量部以上であることがより好ましく、300×10-6重量部以下であることがより好ましい。
上記パラトルエンスルホン酸又はその塩の含有量は、例えば、DART-MS(直接イオン化質量分析)により確認することができる。
本発明のポリビニルアセタール樹脂組成物における上記パラトルエンスルホン酸又はその塩の含有量は、上記ポリビニルアセタール樹脂100重量部に対して1×10-6重量部以上であることが好ましく、500×10-6重量部以下であることが好ましい。
上記範囲とすることで、上記陰イオン界面活性剤との相互作用により2次凝集が維持され、使用段階で微粉の発生を抑えることができる。
上記パラトルエンスルホン酸又はその塩の含有量は、1×10-6重量部以上であることがより好ましく、300×10-6重量部以下であることがより好ましい。
上記パラトルエンスルホン酸又はその塩の含有量は、例えば、DART-MS(直接イオン化質量分析)により確認することができる。
本発明のポリビニルアセタール樹脂組成物は、陰イオン界面活性剤を含有していてもよい。
陰イオン界面活性剤としては、上述したポリビニルアセタール樹脂の製造の際に用いられる陰イオン界面活性剤が挙げられる。
本発明のポリビニルアセタール樹脂組成物における上記陰イオン界面活性剤の含有量は、上記ポリビニルアセタール樹脂100重量部に対して0重量部以上であることが好ましく、10×10-6重量部以上であることがより好ましく、500×10-6重量部以下であることが好ましく、300×10-6重量部以下であることがより好ましい。
陰イオン界面活性剤としては、上述したポリビニルアセタール樹脂の製造の際に用いられる陰イオン界面活性剤が挙げられる。
本発明のポリビニルアセタール樹脂組成物における上記陰イオン界面活性剤の含有量は、上記ポリビニルアセタール樹脂100重量部に対して0重量部以上であることが好ましく、10×10-6重量部以上であることがより好ましく、500×10-6重量部以下であることが好ましく、300×10-6重量部以下であることがより好ましい。
本発明のポリビニルアセタール樹脂組成物を作製する方法としては、例えば、上記ポリビニルアセタール樹脂を作製して得られたポリビニルアセタール樹脂を含む溶液に陽イオン界面活性剤を添加して混合し乾燥する方法が挙げられる。また、上記ポリビニルアセタール樹脂を作製する際のアセタール化工程において陽イオン界面活性剤を添加し、中和、水洗及び乾燥する方法が挙げられる。
また、本発明のポリビニルアセタール樹脂組成物は、ポリビニルアルコール樹脂、陰イオン界面活性剤から形成されるミセル中でアセタール反応させて合成されたものであることが好ましい。
また、本発明のポリビニルアセタール樹脂組成物は、ポリビニルアルコール樹脂、陰イオン界面活性剤から形成されるミセル中でアセタール反応させて合成されたものであることが好ましい。
本発明のポリビニルアセタール樹脂組成物、及び、有機溶剤を用いて、無機微粒子分散用ビヒクル組成物を作製することができる。
本発明のポリビニルアセタール樹脂組成物及び有機溶剤を含有する無機微粒子分散用ビヒクル組成物もまた本発明の1つである。
本発明のポリビニルアセタール樹脂組成物及び有機溶剤を含有する無機微粒子分散用ビヒクル組成物もまた本発明の1つである。
本発明の無機微粒子分散用ビヒクル組成物は、上記ポリビニルアセタール樹脂を含有する。
本発明の無機微粒子分散用ビヒクル組成物における上記ポリビニルアセタール樹脂の含有量は、3重量%以上であることが好ましく、5重量%以上であることがより好ましく、10重量%以下であることが好ましく、8重量%以下であることがより好ましい。
本発明の無機微粒子分散用ビヒクル組成物における上記ポリビニルアセタール樹脂の含有量は、3重量%以上であることが好ましく、5重量%以上であることがより好ましく、10重量%以下であることが好ましく、8重量%以下であることがより好ましい。
本発明の無機微粒子分散用ビヒクル組成物は、陽イオン界面活性剤を含有する。
本発明の無機微粒子分散用ビヒクル組成物における上記陽イオン界面活性剤の含有量は、上記ポリビニルアセタール樹脂100重量部に対して、1×10-6重量部以上であることが好ましく、10×10-6重量部以上であることがより好ましく、10000×10-6重量部以下であることが好ましく、2500×10-6重量部以下であることがより好ましい。
本発明の無機微粒子分散用ビヒクル組成物における上記陽イオン界面活性剤の含有量は、上記ポリビニルアセタール樹脂100重量部に対して、1×10-6重量部以上であることが好ましく、10×10-6重量部以上であることがより好ましく、10000×10-6重量部以下であることが好ましく、2500×10-6重量部以下であることがより好ましい。
本発明の無機微粒子分散用ビヒクル組成物は、有機溶剤を含有する。
上記有機溶剤は特に限定されないが、例えば、エタノール、イソプロパノール、ブタノール、トルエン、キシレン、N-メチル-2-ピロリドン、アセトン、酢酸エチル、酢酸ブチル、酢酸ペンチル、酢酸ヘキシル、酪酸エチル、酪酸ブチル、酪酸ペンチル、酪酸ヘキシル、メチルイソブチルケトン、メチルエチルケトン、エチレングリコールエチルエーテル、エチレングリコールモノブチルエーテル、エチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノイソブチルエーテル、ブチルカルビトール、ブチルカルビトールアセテート、テルピネオール、テルピネオールアセテート、ジヒドロテルピネオール、ジヒドロテルピネオールアセテート、テキサノール、イソホロン、乳酸ブチル、ジオクチルフタレート、ジオクチルアジペート、ベンジルアルコール、フェニルプロピレングリコール、クレゾール等が挙げられる。なお、これらの有機溶剤は単独で用いてもよく、2種以上を併用してもよい。
上記有機溶剤は特に限定されないが、例えば、エタノール、イソプロパノール、ブタノール、トルエン、キシレン、N-メチル-2-ピロリドン、アセトン、酢酸エチル、酢酸ブチル、酢酸ペンチル、酢酸ヘキシル、酪酸エチル、酪酸ブチル、酪酸ペンチル、酪酸ヘキシル、メチルイソブチルケトン、メチルエチルケトン、エチレングリコールエチルエーテル、エチレングリコールモノブチルエーテル、エチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノイソブチルエーテル、ブチルカルビトール、ブチルカルビトールアセテート、テルピネオール、テルピネオールアセテート、ジヒドロテルピネオール、ジヒドロテルピネオールアセテート、テキサノール、イソホロン、乳酸ブチル、ジオクチルフタレート、ジオクチルアジペート、ベンジルアルコール、フェニルプロピレングリコール、クレゾール等が挙げられる。なお、これらの有機溶剤は単独で用いてもよく、2種以上を併用してもよい。
上記有機溶剤の沸点は70℃以上であることが好ましい。
上記沸点が70℃以上であると、蒸発が早くなりすぎず、取り扱い性に優れたものとできる。
また、上記沸点は、90℃以上であることがより好ましく、230℃以下であることが好ましい。
上記範囲とすることで、得られるシートの強度を向上させることができる。
上記沸点が70℃以上であると、蒸発が早くなりすぎず、取り扱い性に優れたものとできる。
また、上記沸点は、90℃以上であることがより好ましく、230℃以下であることが好ましい。
上記範囲とすることで、得られるシートの強度を向上させることができる。
上記無機微粒子分散用ビヒクル組成物における上記有機溶剤の含有量は、40重量%以上であることが好ましく、50重量%以上であることがより好ましく、95重量%以下であることが好ましく、90重量%以下であることがより好ましい。
上記無機微粒子分散用ビヒクル組成物を作製する方法は特に限定されず、具体的には、例えば、本発明のポリビニルアセタール樹脂組成物、有機溶剤を従来公知の方法により攪拌混合する方法等が挙げられる。
また、本発明のポリビニルアセタール樹脂組成物及び有機溶剤を含有する本発明の無機微粒子分散用ビヒクル組成物、無機微粒子、及び、可塑剤を用いて無機微粒子分散スラリー組成物を作製することができる。また、必要に応じて、更に有機溶剤を添加してもよい。
本発明の無機微粒子分散用ビヒクル組成物、無機微粒子、及び、可塑剤を含有する無機微粒子分散スラリー組成物もまた本発明の1つである。
本発明の無機微粒子分散用ビヒクル組成物、無機微粒子、及び、可塑剤を含有する無機微粒子分散スラリー組成物もまた本発明の1つである。
本発明の無機微粒子分散スラリー組成物における上記ポリビニルアセタール樹脂の含有量は特に限定されないが、2重量%以上であることが好ましく、3重量%以上であることがより好ましく、30重量%以下であることが好ましく、12重量%以下であることがより好ましい。
上記ポリビニルアセタール樹脂の含有量を上記範囲内とすることで、焼成後の残渣を少なくすることができる。
上記ポリビニルアセタール樹脂の含有量を上記範囲内とすることで、焼成後の残渣を少なくすることができる。
本発明の無機微粒子分散スラリー組成物は、陽イオン界面活性剤を含有する。
本発明の無機微粒子分散スラリー組成物における陽イオン界面活性剤の含有量は、上記ポリビニルアセタール樹脂100重量部に対して、1×10-6重量部以上であることが好ましく、10×10-6重量部以上であることがより好ましく、10000×10-6重量部以下であることが好ましく、2500×10-6重量部以下であることがより好ましい。
本発明の無機微粒子分散スラリー組成物における陽イオン界面活性剤の含有量は、上記ポリビニルアセタール樹脂100重量部に対して、1×10-6重量部以上であることが好ましく、10×10-6重量部以上であることがより好ましく、10000×10-6重量部以下であることが好ましく、2500×10-6重量部以下であることがより好ましい。
本発明の無機微粒子分散スラリー組成物は、上記有機溶剤を含有する。
本発明の無機微粒子分散スラリー組成物における上記有機溶剤の含有量としては特に限定されないが、10重量%以上であることが好ましく、15重量%以上であることがより好ましく、60重量%以下であることが好ましく、55重量%以下であることがより好ましい。
上記範囲内とすることで、塗工性、無機微粒子の分散性を向上させることができる。
本発明の無機微粒子分散スラリー組成物における上記有機溶剤の含有量としては特に限定されないが、10重量%以上であることが好ましく、15重量%以上であることがより好ましく、60重量%以下であることが好ましく、55重量%以下であることがより好ましい。
上記範囲内とすることで、塗工性、無機微粒子の分散性を向上させることができる。
本発明の無機微粒子分散スラリー組成物は、無機微粒子を含有する。
上記無機微粒子は特に限定されず、例えば、セラミック粉末、ガラス粉末、金属微粒子等が挙げられる。
上記無機微粒子は特に限定されず、例えば、セラミック粉末、ガラス粉末、金属微粒子等が挙げられる。
上記セラミック粉末は特に限定されず、セラミックの製造に使用される金属または非金属の酸化物、炭化物、窒化物、ホウ化物、または硫化物等の粉末が挙げられる。その具体例として、Li、K、Mg、B、Al、Si、Cu、Ca、Sr、Ba、Zn、Cd、Ga、In、Y、ランタノイド、アクチノイド、Ti、Zr、Hf、Bi、V、Nb、Ta、W、Mn、Fe、Co、Ni等の酸化物、炭化物、窒化物、ホウ化物、硫化物等が挙げられる。これらのセラミック粉体は、単独で用いても、または2種類以上の混合物として用いてもよい。
例えば、チタン酸バリウム、窒化アルミ(AlN)、窒化珪素(Si3N4)、炭化珪素(SiC)、アルミナ(Al2O3)、酸化銅(CuO)、及びスピネル系化合物、フェライト、ジルコニア、ジルコン、ジルコン酸バリウム、ジルコン酸カルシウム、酸化チタン、チタン酸バリウム、チタン酸ストロンチウム、チタン酸カルシウム、チタン酸マグネシウム、チタン酸亜鉛、チタン酸ランタン、チタン酸ネオジウム、チタン酸ジルコン鉛、窒化アルミナ、窒化ケイ素、窒化ホウ素、炭化ホウ素、錫酸バリウム、錫酸カルシウム、珪酸マグネシウム、ムライト、ステアタイト、コーディエライト、フォルステライト等が挙げられる。
例えば、チタン酸バリウム、窒化アルミ(AlN)、窒化珪素(Si3N4)、炭化珪素(SiC)、アルミナ(Al2O3)、酸化銅(CuO)、及びスピネル系化合物、フェライト、ジルコニア、ジルコン、ジルコン酸バリウム、ジルコン酸カルシウム、酸化チタン、チタン酸バリウム、チタン酸ストロンチウム、チタン酸カルシウム、チタン酸マグネシウム、チタン酸亜鉛、チタン酸ランタン、チタン酸ネオジウム、チタン酸ジルコン鉛、窒化アルミナ、窒化ケイ素、窒化ホウ素、炭化ホウ素、錫酸バリウム、錫酸カルシウム、珪酸マグネシウム、ムライト、ステアタイト、コーディエライト、フォルステライト等が挙げられる。
上記ガラス粉末は特に限定されず、例えば、酸化ビスマスガラス、ケイ酸塩ガラス、鉛ガラス、亜鉛ガラス、ボロンガラス等のガラス粉末や、CaO-Al2O3-SiO2系、MgO-Al2O3-SiO2系、LiO2-Al2O3-SiO2系等の各種ケイ素酸化物のガラス粉末等が挙げられる。
また、上記ガラス粉末として、SnO-B2O3-P2O5-Al2O3混合物、PbO-B2O3-SiO2混合物、BaO-ZnO-B2O3-SiO2混合物、ZnO-Bi2O3-B2O3-SiO2混合物、Bi2O3-B2O3-BaO-CuO混合物、Bi2O3-ZnO-B2O3-Al2O3-SrO混合物、ZnO-Bi2O3-B2O3混合物、Bi2O3-SiO2混合物、P2O5-Na2O-CaO-BaO-Al2O3-B2O3混合物、P2O5-SnO混合物、P2O5-SnO-B2O3混合物、P2O5-SnO-SiO2混合物、CuO-P2O5-RO混合物、SiO2-B2O3-ZnO-Na2O-Li2O-NaF-V2O5混合物、P2O5-ZnO-SnO-R2O-RO混合物、B2O3-SiO2-ZnO混合物、B2O3-SiO2-Al2O3-ZrO2混合物、SiO2-B2O3-ZnO-R2O-RO混合物、SiO2-B2O3-Al2O3-RO-R2O混合物、SrO-ZnO-P2O5混合物、SrO-ZnO-P2O5混合物、BaO-ZnO-B2O3-SiO2混合物等も用いることができる。なお、Rは、Zn、Ba、Ca、Mg、Sr、Sn、Ni、Fe及びMnからなる群より選択される元素である。
特に、PbO-B2O3-SiO2混合物のガラス粉末や、鉛を含有しないBaO-ZnO-B2O3-SiO2混合物又はZnO-Bi2O3-B2O3-SiO2混合物等の無鉛ガラス粉末が好ましい。
また、上記ガラス粉末として、SnO-B2O3-P2O5-Al2O3混合物、PbO-B2O3-SiO2混合物、BaO-ZnO-B2O3-SiO2混合物、ZnO-Bi2O3-B2O3-SiO2混合物、Bi2O3-B2O3-BaO-CuO混合物、Bi2O3-ZnO-B2O3-Al2O3-SrO混合物、ZnO-Bi2O3-B2O3混合物、Bi2O3-SiO2混合物、P2O5-Na2O-CaO-BaO-Al2O3-B2O3混合物、P2O5-SnO混合物、P2O5-SnO-B2O3混合物、P2O5-SnO-SiO2混合物、CuO-P2O5-RO混合物、SiO2-B2O3-ZnO-Na2O-Li2O-NaF-V2O5混合物、P2O5-ZnO-SnO-R2O-RO混合物、B2O3-SiO2-ZnO混合物、B2O3-SiO2-Al2O3-ZrO2混合物、SiO2-B2O3-ZnO-R2O-RO混合物、SiO2-B2O3-Al2O3-RO-R2O混合物、SrO-ZnO-P2O5混合物、SrO-ZnO-P2O5混合物、BaO-ZnO-B2O3-SiO2混合物等も用いることができる。なお、Rは、Zn、Ba、Ca、Mg、Sr、Sn、Ni、Fe及びMnからなる群より選択される元素である。
特に、PbO-B2O3-SiO2混合物のガラス粉末や、鉛を含有しないBaO-ZnO-B2O3-SiO2混合物又はZnO-Bi2O3-B2O3-SiO2混合物等の無鉛ガラス粉末が好ましい。
上記金属微粒子は特に限定されず、例えば、銅、ニッケル、パラジウム、鉄、白金、金、銀、アルミニウム、タングステンやこれらの合金等からなる粉末等が挙げられる。
また、金属錯体のほか、種々のカーボンブラック、カーボンナノチューブ等を使用してもよい。また、ITO、FTO、酸化ニオブ、酸化バナジウム、酸化タングステン、ランタンストロンチウムマンガナイト、ランタンストロンチウムコバルトフェライト、イットリウム安定化ジルコニア、ガドリニウムドープセリア、酸化ニッケル、ランタンクロマイト等も使用することができる。
また、金属錯体のほか、種々のカーボンブラック、カーボンナノチューブ等を使用してもよい。また、ITO、FTO、酸化ニオブ、酸化バナジウム、酸化タングステン、ランタンストロンチウムマンガナイト、ランタンストロンチウムコバルトフェライト、イットリウム安定化ジルコニア、ガドリニウムドープセリア、酸化ニッケル、ランタンクロマイト等も使用することができる。
本発明の無機微粒子分散スラリー組成物における上記無機微粒子の含有量としては特に限定されないが、10重量%以上であることが好ましく、15重量%以上であることがより好ましく、90重量%以下であることが好ましく、85重量%以下であることがより好ましい。上記範囲とすることで、充分な粘度を有し、優れた塗工性を有するものとでき、また、無機微粒子の分散性に優れるものとできる。
本発明の無機微粒子分散スラリー組成物は、可塑剤を含有する。
上記可塑剤としては、例えば、例えば、アジピン酸モノメチル、アジピン酸ジ(ブトキシエチル)、アジピン酸ジブトキシエトキシエチル、トリエチレングリコールビス(2-エチルヘキサノエート)、トリエチレングリコールジヘキサノエート、アセチルクエン酸トリエチル、セチルクエン酸トリブチル、セバシン酸ジブチル、フタル酸ブチル化ベンジル、アジピン酸ジイソノニル、フタル酸ジイソデシル、トリプロピオニン、ペンタエリスリトールテトラアセテート、フタル酸ジ-2-エチルヘキシル、トリアセチン等が挙げられる。
なかでも、トリエチレングリコールビス(2-エチルヘキサノエート)、フタル酸ブチル化ベンジル、アジピン酸ジイソノニル、フタル酸ジイソデシル、トリプロピオニン、ペンタエリスリトールテトラアセテート、フタル酸ジ-2-エチルヘキシル等が好ましい。
上記可塑剤としては、例えば、例えば、アジピン酸モノメチル、アジピン酸ジ(ブトキシエチル)、アジピン酸ジブトキシエトキシエチル、トリエチレングリコールビス(2-エチルヘキサノエート)、トリエチレングリコールジヘキサノエート、アセチルクエン酸トリエチル、セチルクエン酸トリブチル、セバシン酸ジブチル、フタル酸ブチル化ベンジル、アジピン酸ジイソノニル、フタル酸ジイソデシル、トリプロピオニン、ペンタエリスリトールテトラアセテート、フタル酸ジ-2-エチルヘキシル、トリアセチン等が挙げられる。
なかでも、トリエチレングリコールビス(2-エチルヘキサノエート)、フタル酸ブチル化ベンジル、アジピン酸ジイソノニル、フタル酸ジイソデシル、トリプロピオニン、ペンタエリスリトールテトラアセテート、フタル酸ジ-2-エチルヘキシル等が好ましい。
上記可塑剤の沸点は240℃以上であることが好ましく、390℃未満であることが好ましい。上記沸点を240℃以上とすることで、乾燥工程で蒸発しやすくなり、成形体への残留を防止できる。また、390℃未満とすることで、残留炭素が生じることを防止できる。なお、上記沸点は、常圧での沸点をいう。
本発明の無機微粒子分散スラリー組成物における上記可塑剤の含有量は特に限定されないが、0.1重量%以上であることが好ましく、0.2重量%以上であることがより好ましく、3重量%以下であることが好ましく、2.5重量%以下であることがより好ましい。上記範囲内とすることで、可塑剤の焼成残渣を少なくすることができる。
本発明の無機微粒子分散スラリー組成物の粘度は特に限定されないが、20℃においてB型粘度計を用いプローブ回転数を5rpmに設定して測定した場合の粘度が0.1Pa・s以上であることが好ましく、100Pa・s以下であることが好ましい。
上記粘度を0.1Pa・s以上とすることで、ダイコート印刷法等により塗工した後、得られる無機微粒子分散シートが所定の形状を維持することが可能となる。また、上記粘度を100Pa・s以下とすることで、ダイの塗出痕が消えない等の不具合を防止して、印刷性に優れるものとできる。
上記粘度を0.1Pa・s以上とすることで、ダイコート印刷法等により塗工した後、得られる無機微粒子分散シートが所定の形状を維持することが可能となる。また、上記粘度を100Pa・s以下とすることで、ダイの塗出痕が消えない等の不具合を防止して、印刷性に優れるものとできる。
本発明の無機微粒子分散スラリー組成物を作製する方法は特に限定されず、従来公知の攪拌方法が挙げられ、具体的には、例えば、本発明のポリビニルアセタール樹脂組成物、上記無機微粒子、必要に応じて添加される有機溶剤、可塑剤及びその他の成分をビーズミル等で攪拌する方法等が挙げられる。
本発明の無機微粒子分散スラリー組成物を、片面離型処理を施した支持フィルム上に塗工し、有機溶剤を乾燥させ、シート状に成形することで、無機微粒子分散シートを製造することができる。
上記無機微粒子分散シートは、厚みが0.5μm以上であることが好ましく、3μm以下であることが好ましい。
上記無機微粒子分散シートは、厚みが0.5μm以上であることが好ましく、3μm以下であることが好ましい。
上記無機微粒子分散シートを製造する際に用いる支持フィルムは、耐熱性及び耐溶剤性を有するとともに可撓性を有する樹脂フィルムであることが好ましい。支持フィルムが可撓性を有することにより、ロールコーター、ブレードコーターなどによって支持フィルムの表面に無機微粒子分散スラリー組成物を塗布することができ、得られる無機微粒子分散シート形成フィルムをロール状に巻回した状態で保存し、供給することができる。
上記支持フィルムを形成する樹脂としては、例えばポリエチレンテレフタレート、ポリエステル、ポリエチレン、ポリプロピレン、ポリスチレン、ポリイミド、ポリビニルアルコール、ポリ塩化ビニル、ポリフロロエチレン等の含フッ素樹脂、ナイロン、セルロース等が挙げられる。
上記支持フィルムの厚みは、例えば、20μm以上であることが好ましく、100μm以下であることが好ましい。
また、支持フィルムの表面には離型処理が施されていることが好ましく、これにより、転写工程において、支持フィルムの剥離操作を容易に行うことができる。
上記支持フィルムの厚みは、例えば、20μm以上であることが好ましく、100μm以下であることが好ましい。
また、支持フィルムの表面には離型処理が施されていることが好ましく、これにより、転写工程において、支持フィルムの剥離操作を容易に行うことができる。
また、本発明の無機微粒子分散スラリー組成物、無機微粒子分散シートを、誘電体グリーンシート、電極ペーストに用いることで積層セラミクスコンデンサを製造することができる。本発明の無機微粒子分散スラリー組成物を用いてなる積層セラミクスコンデンサもまた本発明の1つである。
上記積層セラミクスコンデンサの製造方法は、本発明の無機微粒子分散シートに導電ペーストを印刷、乾燥して、誘電体シートを作製する工程、及び、前記誘電体シートを積層する工程を有することが好ましい。
上記導電ペーストは、導電粉末を含有するものである。
上記導電粉末の材質は、導電性を有する材質であれば特に限定されず、例えば、ニッケル、パラジウム、白金、金、銀、銅及びこれらの合金等が挙げられる。これらの導電粉末は、単独で用いてもよく、2種以上を併用してもよい。
上記導電粉末の材質は、導電性を有する材質であれば特に限定されず、例えば、ニッケル、パラジウム、白金、金、銀、銅及びこれらの合金等が挙げられる。これらの導電粉末は、単独で用いてもよく、2種以上を併用してもよい。
上記導電ペーストに使用されるバインダー樹脂、有機溶剤としては、本発明の無機微粒子分散スラリー組成物と同様のものを用いることができる。
上記導電ペーストを印刷する方法は特に限定されず、例えば、スクリーン印刷法、ダイコート印刷法、オフセット印刷法、グラビア印刷法、インクジェット印刷法等が挙げられる。
上記積層セラミクスコンデンサの製造方法では、上記導電ペーストを印刷した誘電体シートを積層し、脱脂、焼成後、外部電極を設置することで積層セラミクスコンデンサが得られる。
本発明によれば、有機溶剤への溶解性が高く、また、有機溶剤に溶解した場合に微細な未溶解物が少ないポリビニルアセタール樹脂組成物を提供できる。更に、無機微粒子分散シートを作製する際の取り扱い性に優れ、低温で優れた分解性を有するとともに、未溶解物由来の酸素欠陥が発生し難く、優れた特性を有するセラミクス積層体を製造することが可能であるポリビニルアセタール樹脂組成物を提供できる。また、該ポリビニルアセタール樹脂組成物を含む無機微粒子分散用ビヒクル組成物、無機微粒子分散スラリー組成物、該無機微粒子分散スラリー組成物を用いてなる積層セラミクスコンデンサを提供できる。
以下に実施例を掲げて本発明を更に詳しく説明するが、本発明はこれら実施例のみに限定されない。
(実施例1)
(1)ポリビニルアセタール樹脂組成物の調製
ポリビニルアルコール樹脂(重合度1500、ケン化度99.9モル%)200重量部を純水3050重量部に加え、温度を90℃として約2時間攪拌し溶解させることでポリビニルアルコール樹脂水溶液を得た。得られた水溶液を室温に冷却し、酸触媒としてパラトルエンスルホン酸(東京化成工業社製)15重量部、n-ブチルアルデヒド1200重量部、陰イオン界面活性剤25重量部を加え、高速撹拌機で乳化させて、ポリビニルアルコール樹脂と陰イオン界面活性剤と酸触媒とアルデヒドによるミセルを形成した。その後、液温を37℃に上げてこの温度を保持してアセタール化反応を行い、反応生成物を析出させた。その後、更に3時間保持して反応を完了させ、更に陽イオン界面活性剤1重量部を加えた。その後、常法により中和、水洗、及び、乾燥を行い、ポリビニルアセタール樹脂組成物を得た。
なお、陰イオン界面活性剤としては、NS-1(ドデシル硫酸ナトリウム、東京化成工業社製)を用いた。また、陽イオン界面活性剤としては、CS-1(n-オクチルアンモニウムブロミド(脂肪族アミン塩)、東京化成工業社製、エタノールへの溶解度0.001g/100g)を用いた。
(1)ポリビニルアセタール樹脂組成物の調製
ポリビニルアルコール樹脂(重合度1500、ケン化度99.9モル%)200重量部を純水3050重量部に加え、温度を90℃として約2時間攪拌し溶解させることでポリビニルアルコール樹脂水溶液を得た。得られた水溶液を室温に冷却し、酸触媒としてパラトルエンスルホン酸(東京化成工業社製)15重量部、n-ブチルアルデヒド1200重量部、陰イオン界面活性剤25重量部を加え、高速撹拌機で乳化させて、ポリビニルアルコール樹脂と陰イオン界面活性剤と酸触媒とアルデヒドによるミセルを形成した。その後、液温を37℃に上げてこの温度を保持してアセタール化反応を行い、反応生成物を析出させた。その後、更に3時間保持して反応を完了させ、更に陽イオン界面活性剤1重量部を加えた。その後、常法により中和、水洗、及び、乾燥を行い、ポリビニルアセタール樹脂組成物を得た。
なお、陰イオン界面活性剤としては、NS-1(ドデシル硫酸ナトリウム、東京化成工業社製)を用いた。また、陽イオン界面活性剤としては、CS-1(n-オクチルアンモニウムブロミド(脂肪族アミン塩)、東京化成工業社製、エタノールへの溶解度0.001g/100g)を用いた。
(2)無機微粒子分散用ビヒクル組成物の調製
得られたポリビニルアセタール樹脂組成物に対して、有機溶剤としてエタノールとトルエンとの混合溶剤(重量比1:1、沸点100℃)をポリビニルアセタール樹脂100重量部に対して900重量部添加し、均一になるまで攪拌して、無機微粒子分散用ビヒクル組成物を得た。
得られたポリビニルアセタール樹脂組成物に対して、有機溶剤としてエタノールとトルエンとの混合溶剤(重量比1:1、沸点100℃)をポリビニルアセタール樹脂100重量部に対して900重量部添加し、均一になるまで攪拌して、無機微粒子分散用ビヒクル組成物を得た。
(3)無機微粒子分散スラリー組成物の調製
得られた無機微粒子分散用ビヒクル組成物に対して、無機微粒子としてチタン酸バリウム(「BT-02」、堺化学工業社製、平均粒子径0.2μm)、可塑剤としてPL-1(トリエチレングリコールビス(2-エチルヘキサノエート))、有機溶剤としてエタノールとトルエンとの混合溶剤(重量比1:1)を表2に示す配合となるように添加して、ビーズミルで分散処理を行い、無機微粒子分散スラリー組成物を得た。
得られた無機微粒子分散用ビヒクル組成物に対して、無機微粒子としてチタン酸バリウム(「BT-02」、堺化学工業社製、平均粒子径0.2μm)、可塑剤としてPL-1(トリエチレングリコールビス(2-エチルヘキサノエート))、有機溶剤としてエタノールとトルエンとの混合溶剤(重量比1:1)を表2に示す配合となるように添加して、ビーズミルで分散処理を行い、無機微粒子分散スラリー組成物を得た。
(実施例2~13、比較例1~11)
ポリビニルアルコール樹脂、陰イオン界面活性剤、陽イオン界面活性剤の種類及び添加量、水、アルデヒド、酸触媒の添加量を表1の通りとした以外は実施例1と同様にしてポリビニルアセタール樹脂組成物を得た。
また、得られたポリビニルアセタール樹脂組成物を用い、可塑剤の種類を表2の通りとした以外は実施例1と同様にして無機微粒子分散スラリー組成物を得た。
なお、陽イオン界面活性剤、陰イオン界面活性剤、可塑剤としては以下のものを用いた。
<陽イオン界面活性剤>
CS-2:ドデシルアンモニウムブロミド(東京化成工業社製、脂肪族アミン塩、エタノールへの溶解度0.002g/100g)
CS-3:トリブチルドデシルホスホニウムブロミド(東京化成工業社製、ホスホニウム塩、エタノールへの溶解度0.001g/100g)
CS-4:(2-カルボキシエチル)トリフェニルホスホニウムブロミド(東京化成工業社製、ホスホニウム塩、エタノールへの溶解度0.001g/100g)
CS-5:ヘキサデシルトリメチルアンモニウムブロミド(東京化成工業社製、第4級アンモニウム塩、エタノールへの溶解度0.004g/100g)
CS-6:テトラエチルアンモニウムブロミド(東京化成工業社製、第4級アンモニウム塩、エタノールへの溶解度0.002g/100g)
CS-7:塩化1-エチル-3-メチルイミダゾリウム(東京化成工業社製、複素環式アミン塩、エタノールへの溶解度0.005g/100g)
CS-8:塩化セチルピリジニウム(東京化成工業社製、複素環式アミン塩、エタノールへの溶解度0.006g/100g)
CS-9:ドデシルトリメチルアンモニウムブロミド(東京化成工業社製、第4級アンモニウム塩、エタノールへの溶解度0.006g/100g)
CS-10:塩化ベンゼトニウム(東京化成工業社製、芳香族アミン塩、エタノールへの溶解度0.005g/100g)
CS-11:テトラブチルアンモニウムブロミド(東京化成工業社製、第4級アンモニウム塩、エタノールへの溶解度0.026g/100g)
CS-12:テトラブチルアンモニウムクロリド(東京化成工業社製、第4級アンモニウム塩、エタノールへの溶解度0.35g/100g)
CS-13:ドデカン-1-イル(エチル)(ジメチル)アンモニウム=エチル=スルファート(第一工業製薬社製、第4級アンモニウム塩、エタノールへの溶解度0.5g/100g)
<陰イオン界面活性剤>
NS-2:ドデシルベンゼンスルホン酸ナトリウム、東京化成工業社製
<可塑剤>
PL-2:フタル酸ブチル化ベンジル、東京化成工業社製
PL-3:アジピン酸ジイソノニル、東京化成工業社製
PL-4:フタル酸ジイソデシル、東京化成工業社製
PL-5:トリプロピオニン、東京化成工業社製
PL-6:ペンタエリスリトールテトラアセテート、東京化成工業社製
PL-7:フタル酸ジ-2-エチルヘキシル、東京化成工業社製
ポリビニルアルコール樹脂、陰イオン界面活性剤、陽イオン界面活性剤の種類及び添加量、水、アルデヒド、酸触媒の添加量を表1の通りとした以外は実施例1と同様にしてポリビニルアセタール樹脂組成物を得た。
また、得られたポリビニルアセタール樹脂組成物を用い、可塑剤の種類を表2の通りとした以外は実施例1と同様にして無機微粒子分散スラリー組成物を得た。
なお、陽イオン界面活性剤、陰イオン界面活性剤、可塑剤としては以下のものを用いた。
<陽イオン界面活性剤>
CS-2:ドデシルアンモニウムブロミド(東京化成工業社製、脂肪族アミン塩、エタノールへの溶解度0.002g/100g)
CS-3:トリブチルドデシルホスホニウムブロミド(東京化成工業社製、ホスホニウム塩、エタノールへの溶解度0.001g/100g)
CS-4:(2-カルボキシエチル)トリフェニルホスホニウムブロミド(東京化成工業社製、ホスホニウム塩、エタノールへの溶解度0.001g/100g)
CS-5:ヘキサデシルトリメチルアンモニウムブロミド(東京化成工業社製、第4級アンモニウム塩、エタノールへの溶解度0.004g/100g)
CS-6:テトラエチルアンモニウムブロミド(東京化成工業社製、第4級アンモニウム塩、エタノールへの溶解度0.002g/100g)
CS-7:塩化1-エチル-3-メチルイミダゾリウム(東京化成工業社製、複素環式アミン塩、エタノールへの溶解度0.005g/100g)
CS-8:塩化セチルピリジニウム(東京化成工業社製、複素環式アミン塩、エタノールへの溶解度0.006g/100g)
CS-9:ドデシルトリメチルアンモニウムブロミド(東京化成工業社製、第4級アンモニウム塩、エタノールへの溶解度0.006g/100g)
CS-10:塩化ベンゼトニウム(東京化成工業社製、芳香族アミン塩、エタノールへの溶解度0.005g/100g)
CS-11:テトラブチルアンモニウムブロミド(東京化成工業社製、第4級アンモニウム塩、エタノールへの溶解度0.026g/100g)
CS-12:テトラブチルアンモニウムクロリド(東京化成工業社製、第4級アンモニウム塩、エタノールへの溶解度0.35g/100g)
CS-13:ドデカン-1-イル(エチル)(ジメチル)アンモニウム=エチル=スルファート(第一工業製薬社製、第4級アンモニウム塩、エタノールへの溶解度0.5g/100g)
<陰イオン界面活性剤>
NS-2:ドデシルベンゼンスルホン酸ナトリウム、東京化成工業社製
<可塑剤>
PL-2:フタル酸ブチル化ベンジル、東京化成工業社製
PL-3:アジピン酸ジイソノニル、東京化成工業社製
PL-4:フタル酸ジイソデシル、東京化成工業社製
PL-5:トリプロピオニン、東京化成工業社製
PL-6:ペンタエリスリトールテトラアセテート、東京化成工業社製
PL-7:フタル酸ジ-2-エチルヘキシル、東京化成工業社製
<評価>
実施例及び比較例で得られたポリビニルアセタール樹脂、ポリビニルアセタール樹脂組成物、無機微粒子分散スラリー組成物について、以下の評価を行った。結果を表2及び3に示した。
実施例及び比較例で得られたポリビニルアセタール樹脂、ポリビニルアセタール樹脂組成物、無機微粒子分散スラリー組成物について、以下の評価を行った。結果を表2及び3に示した。
(1)ポリビニルアセタール樹脂
(1-1)水酸基量、アセタール基量、アセチル基量
得られたポリビニルアセタール樹脂をDMSO-D6に10重量%の濃度で溶解し、13C-NMRを用いて、水酸基量、アセタール基量、アセチル基量を測定した。
(1-1)水酸基量、アセタール基量、アセチル基量
得られたポリビニルアセタール樹脂をDMSO-D6に10重量%の濃度で溶解し、13C-NMRを用いて、水酸基量、アセタール基量、アセチル基量を測定した。
(1-2)分子量
得られたポリビニルアセタール樹脂について、カラムとしてTSKgel SuperHZM-Hを用い、ゲルパーミエーションクロマトグラフィーにより、ポリスチレン換算による重量平均分子量(Mw)、数平均分子量(Mn)、分子量分布(Mw/Mn)を測定した。
得られたポリビニルアセタール樹脂について、カラムとしてTSKgel SuperHZM-Hを用い、ゲルパーミエーションクロマトグラフィーにより、ポリスチレン換算による重量平均分子量(Mw)、数平均分子量(Mn)、分子量分布(Mw/Mn)を測定した。
(1-3)粒子径
得られたポリビニルアセタール樹脂について、走査型電子顕微鏡(日立ハイテクノロジーズ社製「Regulus8220」)を用いて観察し、100個の一次粒子の最大フェレー径を測定し、その平均値を計算することにより1次粒子径とCV値を測定した。
また、得られたポリビニルアセタール樹脂粒子について、レーザー回折散乱式粒度分布測定装置(Mastersizer3000)を用いて2次粒子径を測定し、小粒径側から体積基準累積10%、50%、90%の粒子径をそれぞれD10、D50、D90として粒子径を求めた。また、測定したD10、D50、D90から粒度分布ε[(D90-D10)/D50]を算出した。
得られたポリビニルアセタール樹脂について、走査型電子顕微鏡(日立ハイテクノロジーズ社製「Regulus8220」)を用いて観察し、100個の一次粒子の最大フェレー径を測定し、その平均値を計算することにより1次粒子径とCV値を測定した。
また、得られたポリビニルアセタール樹脂粒子について、レーザー回折散乱式粒度分布測定装置(Mastersizer3000)を用いて2次粒子径を測定し、小粒径側から体積基準累積10%、50%、90%の粒子径をそれぞれD10、D50、D90として粒子径を求めた。また、測定したD10、D50、D90から粒度分布ε[(D90-D10)/D50]を算出した。
(2)ポリビニルアセタール樹脂組成物
陽イオン界面活性剤、陰イオン界面活性剤、パラトルエンスルホン酸又はその塩の含有量をDART-OS(エーエムアール社製)を用いてDART-MS(直接イオン化質量分析)により確認した。
陽イオン界面活性剤、陰イオン界面活性剤、パラトルエンスルホン酸又はその塩の含有量をDART-OS(エーエムアール社製)を用いてDART-MS(直接イオン化質量分析)により確認した。
(3)パーティクル
得られたポリビニルアセタール樹脂組成物を、樹脂量が2重量%になるようにエタノールとトルエンとの混合溶剤(重量比1:1)にて希釈し、この溶液10mL中のポリビニルアセタール樹脂の粒子径分布を、パーティクルカウンター(「KL-11A」、リオン社製)を用いて測定した。溶液1mL当たりの直径0.5~1.0μmの粒子の個数を確認した。また、直径0.5~1.0μmの粒子について、直径0.75μmの真球と仮定して粒子の体積を算出し、得られた測定結果に基づいて直径0.5~1.0μmの粒子の割合(体積%)を算出した。
得られたポリビニルアセタール樹脂組成物を、樹脂量が2重量%になるようにエタノールとトルエンとの混合溶剤(重量比1:1)にて希釈し、この溶液10mL中のポリビニルアセタール樹脂の粒子径分布を、パーティクルカウンター(「KL-11A」、リオン社製)を用いて測定した。溶液1mL当たりの直径0.5~1.0μmの粒子の個数を確認した。また、直径0.5~1.0μmの粒子について、直径0.75μmの真球と仮定して粒子の体積を算出し、得られた測定結果に基づいて直径0.5~1.0μmの粒子の割合(体積%)を算出した。
(4)溶解時間
500mLのビーカーに有機溶剤としてエタノールとトルエンとの混合溶剤(重量比1:1)192gを入れ、温度を25℃に保ち、2枚の攪拌翼を用い、回転数200rpmで攪拌しながら、得られたポリビニルアセタール樹脂組成物48.0g(濃度20重量%)を添加し、ポリビニルアセタール樹脂組成物を溶解させた。目視で観察し、得られたポリビニルアセタール樹脂組成物を添加してから不溶解樹脂がなくなるまでの溶解時間を測定し、以下の基準で評価した。
A:120分以上160分未満
B:160分以上220分未満
C:220分以上550分未満
D:550分以上
500mLのビーカーに有機溶剤としてエタノールとトルエンとの混合溶剤(重量比1:1)192gを入れ、温度を25℃に保ち、2枚の攪拌翼を用い、回転数200rpmで攪拌しながら、得られたポリビニルアセタール樹脂組成物48.0g(濃度20重量%)を添加し、ポリビニルアセタール樹脂組成物を溶解させた。目視で観察し、得られたポリビニルアセタール樹脂組成物を添加してから不溶解樹脂がなくなるまでの溶解時間を測定し、以下の基準で評価した。
A:120分以上160分未満
B:160分以上220分未満
C:220分以上550分未満
D:550分以上
(5)積層セラミクスコンデンサ(MLCC)性能評価
(グリーンシートの作製)
離型処理されたポリエチレンテレフタレート(PET)フィルム上に、得られたスラリー組成物を乾燥後の膜厚が1μmとなるように塗工、乾燥してセラミックグリーンシートを作製した。
(グリーンシートの作製)
離型処理されたポリエチレンテレフタレート(PET)フィルム上に、得られたスラリー組成物を乾燥後の膜厚が1μmとなるように塗工、乾燥してセラミックグリーンシートを作製した。
得られたセラミックグリーンシートを用いて、生の積層体を形成した。具体的には、セラミックグリーンシート上に、Niを主成分として含む導電ペーストをスクリーン印刷し、内部電極となる導電ペースト膜を形成した。そして、導電ペースト膜が形成されたセラミックグリーンシートを、導電ペースト膜の引き出されている側が互い違いになるように複数枚を積層した後に圧着して、生の積層体を得た。次に、生の積層体を焼成した。具体的には、まず、還元雰囲気下で500℃に加熱して、バインダーを燃焼させた。その後、酸素分圧が10-10MPaのH2-N2-H2Oガスからなる還元性雰囲気中にて、1250℃の温度で3時間焼成した。その後、銀、テルピネオール、エチルセルロースからなる導電ペーストを作製した。ディップ法を用いて得られた焼成体に導電ペーストを塗布し、1250℃で3時間焼成し、積層セラミクスコンデンサを作製した。
(5-1)誘電体層中のボイドの個数
得られた積層セラミクスコンデンサの誘電体層の断面をSEMを用いて観察した。焼結性について、以下の基準で評価した。
A:不溶解樹脂塊起因のボイドが見られなかった。
B:不溶解樹脂塊起因のボイドが1個以上5個未満見られた。
C:不溶解樹脂塊起因のボイドが5個以上10個未満見られた。
D:不溶解樹脂塊起因のボイドが10個以上見られた。
得られた積層セラミクスコンデンサの誘電体層の断面をSEMを用いて観察した。焼結性について、以下の基準で評価した。
A:不溶解樹脂塊起因のボイドが見られなかった。
B:不溶解樹脂塊起因のボイドが1個以上5個未満見られた。
C:不溶解樹脂塊起因のボイドが5個以上10個未満見られた。
D:不溶解樹脂塊起因のボイドが10個以上見られた。
(5-2)等価直列抵抗(ESR)
上記の方法で積層セラミクスコンデンサを10個作製し、積層セラミクスコンデンサを空気雰囲気下、150℃で1時間の熱処理を行い、その後、測定用基板に実装し、熱処理完了後24±2時間後に、ネットワークアナライザを用いて等価直列抵抗(ESR)を測定した。測定周波数は、10MHzとした。最後に、10個分(条件ごと)の値を平均値化し、48mΩ未満のものを良(〇)、48mΩ以上のものを不良(×)、とした。
上記の方法で積層セラミクスコンデンサを10個作製し、積層セラミクスコンデンサを空気雰囲気下、150℃で1時間の熱処理を行い、その後、測定用基板に実装し、熱処理完了後24±2時間後に、ネットワークアナライザを用いて等価直列抵抗(ESR)を測定した。測定周波数は、10MHzとした。最後に、10個分(条件ごと)の値を平均値化し、48mΩ未満のものを良(〇)、48mΩ以上のものを不良(×)、とした。
本発明によれば、有機溶剤への溶解性が高く、また、有機溶剤に溶解した場合に微細な未溶解物が少ないポリビニルアセタール樹脂組成物を提供できる。更に、未溶解物由来の酸素欠陥が発生し難く、優れた特性を有するセラミクス積層体を製造することが可能であるポリビニルアセタール樹脂組成物を提供できる。また、該ポリビニルアセタール樹脂組成物を含む無機微粒子分散用ビヒクル組成物、無機微粒子分散スラリー組成物、該無機微粒子分散スラリー組成物を用いてなる積層セラミクスコンデンサを提供できる。
Claims (9)
- ポリビニルアセタール樹脂及び陽イオン界面活性剤を含有する組成物であって、
前記ポリビニルアセタール樹脂の一次粒子径が0.01μm以上10μm以下であり、
陽イオン界面活性剤を、前記ポリビニルアセタール樹脂100重量部に対して1×10-6重量部以上10000×10-6重量部以下含有する、ポリビニルアセタール樹脂組成物。 - ポリビニルアセタール樹脂は、重合度が1500以上2000以下、水酸基量が25.0モル%以上35.0モル%以下、アセタール基量が60.0モル%以上70.0モル%以下、アセチル基量が0.1モル%以上0.5モル%以下である、請求項1に記載のポリビニルアセタール樹脂組成物。
- 陽イオン界面活性剤は、エタノールへの溶解度が0.001g/100g以上である、請求項1又は2に記載のポリビニルアセタール樹脂組成物。
- パラトルエンスルホン酸又はその塩を、ポリビニルアセタール樹脂100重量部に対して1×10-6重量部以上500×10-6重量部以下含有する、請求項1~3の何れかに記載のポリビニルアセタール樹脂組成物。
- ポリビニルアセタール樹脂は、レーザー回折散乱式粒度分布測定法により二次粒子径を測定し小粒径側から体積基準累積10%、50%、90%の粒子径をそれぞれD10、D50、D90としたとき、(D90-D10)/D50が0.7以上1.5以下である、請求項1~4の何れかに記載のポリビニルアセタール樹脂組成物。
- ポリビニルアセタール樹脂は、重量平均分子量Mwと数平均分子量Mnとの比率である分子量分布(Mw/Mn)が1.8以上2.6以下である、請求項1~5の何れかに記載のポリビニルアセタール樹脂組成物。
- 請求項1~6の何れかに記載のポリビニルアセタール樹脂組成物、及び、有機溶剤を含有する、無機微粒子分散用ビヒクル組成物。
- 請求項7に記載の無機微粒子分散用ビヒクル組成物、無機微粒子、及び、可塑剤を含有する、無機微粒子分散スラリー組成物。
- 請求項8に記載の無機微粒子分散スラリー組成物を用いてなる、積層セラミクスコンデンサ。