WO2023089655A1 - 半導体光電極 - Google Patents

半導体光電極 Download PDF

Info

Publication number
WO2023089655A1
WO2023089655A1 PCT/JP2021/042036 JP2021042036W WO2023089655A1 WO 2023089655 A1 WO2023089655 A1 WO 2023089655A1 JP 2021042036 W JP2021042036 W JP 2021042036W WO 2023089655 A1 WO2023089655 A1 WO 2023089655A1
Authority
WO
WIPO (PCT)
Prior art keywords
thin film
semiconductor
semiconductor thin
moth
substrate
Prior art date
Application number
PCT/JP2021/042036
Other languages
English (en)
French (fr)
Inventor
裕也 渦巻
紗弓 里
晃洋 鴻野
武志 小松
Original Assignee
日本電信電話株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本電信電話株式会社 filed Critical 日本電信電話株式会社
Priority to PCT/JP2021/042036 priority Critical patent/WO2023089655A1/ja
Publication of WO2023089655A1 publication Critical patent/WO2023089655A1/ja

Abstract

半導体光電極は、表面にモスアイ構造を有する導電性または絶縁性の基板１１と、基板１１のモスアイ構造を有する面上に配置された半導体薄膜１２と、半導体薄膜１２上に配置された触媒層１３と、基板１１のモスアイ構造を有する面に対向する裏面に配置された反射層１４を備える。

Description

半導体光電極
　本発明は、半導体光電極に関する。
　半導体光電極を用いた水の分解反応により水素を生成する装置は、プロトン交換膜を介してつながっている酸化槽と還元槽を有し、酸化槽に水溶液と酸化電極を入れ、還元槽に水溶液と還元電極を入れる。酸化電極と還元電極とは導線で電気的に接続される。
　光触媒を用いた水の分解反応は、水の酸化反応とプロトンの還元反応からなる。ｎ型の光触媒材料に光を照射すると、光触媒中で電子と正孔が生成分離する。正孔は光触媒材料の表面に移動し、水の酸化反応に寄与する。一方、電子は還元電極に移動し、プロトンの還元反応に寄与する。理想的には、このような酸化還元反応が進行し、水分解反応が生じる。
　酸化反応：２Ｈ2Ｏ＋４ｈ+→Ｏ2＋４Ｈ+
　還元反応：４Ｈ+＋４ｅ-→２Ｈ2
S. Yotsuhashi, et al., "CO2 Conversion with Light and Water by GaN Photoelectrode", Japanese Journal of Applied Physics, The Japan Society of Applied Physics, 2012, Volume 51, pp. 02BP07-1-02BP07-3 "MPSS", [online], El-Seed Corp., インターネット〈URL：http://elseed.com/products/mpss/〉
　半導体光電極表面での酸素生成反応量は、半導体中で生成する正孔数に従う。そのため、半導体中で生成する正孔数を増加させること、つまり、半導体で吸収する光をできる限り最大化することが高効率化に重要である。半導体薄膜に光を照射した際、物性上吸収可能な波長域であったとしても、およそ３０％程度の光が半導体薄膜を透過する。透過する３０％の光を再度利用することができれば、光エネルギー変換効率を向上することができる。そこで、半導体薄膜の裏面に反射層を設けることで、透過した光を反射し、再度半導体薄膜で吸収させる構造が提案されている。
　しかし、透過した光はバルク内を散乱しており、半導体薄膜に届くまでに大部分がバルク内で吸収されてしまい、効率的に反射光を利用できていないという問題があった。
　本発明は、上記に鑑みてなされたものであり、半導体光電極の光エネルギー変換効率の向上を目的とする。
　本発明の一態様の半導体光電極は、表面にモスアイ構造を有する導電性または絶縁性の基板と、前記基板の前記モスアイ構造を有する面上に配置された半導体薄膜と、前記半導体薄膜上に配置された触媒層と、前記基板のモスアイ構造を有する面に対向する面に配置された反射層を備える。
　本発明によれば、半導体光電極の光エネルギー変換効率を向上できる。
図１は、本実施形態の半導体光電極の構成の一例を示す断面図である。 図２は、本実施形態の半導体光電極の構成の一例を示す断面図である。 図３は、図１の半導体光電極の製造方法の一例を示すフローチャートである。 図４は、図２の半導体光電極の製造方法の一例を示すフローチャートである。 図５は、酸化還元反応試験を行う装置の概要を示す図である。 図６は、本実施形態の半導体光電極のモスアイ構造を通過した光の拡散性が一方向に制御される様子を説明するための図である。 図７は、従来の半導体光電極に入射した光が基板内を散乱する様子を説明するための図である。
　以下、本発明の実施の形態について図面を用いて説明する。なお、本発明は以下で説明する実施の形態に限定されるものではなく、本発明の趣旨を逸脱しない範囲内において変更を加えても構わない。
　［半導体光電極の構成］
　図１は、本実施形態の半導体光電極の構成の一例を示す断面図である。図１に示す半導体光電極は、表面にモスアイ構造を有する絶縁性または導電性の基板１１、基板１１のモスアイ構造面上に配置された半導体薄膜１２、半導体薄膜１２上に配置された触媒層１３、およびモスアイ構造面に対向する基板１１の下面に配置された反射層１４を備える。
　基板１１には、一方の面にモスアイ構造を形成した、サファイア基板、ＧａＮ基板、ガラス基板、あるいはＳｉ基板などの絶縁性または導電性の基板を用いる。モスアイ構造は、入射した光を回折効果により垂直方向に透過する構造である。例えば、基板１１として、非特許文献２に記載のものを用いることができる。
　半導体薄膜１２には、窒化ガリウム（ＧａＮ）、窒化アルミニウムガリウム（ＡｌＧａＮ）、または窒化インジウムガリウム（ＩｎＧａＮ）を用いる。あるいは、半導体薄膜１２には、光触媒機能を有する酸化チタン（ＴｉＯ2）、酸化タングステン（ＷＯ3）等の金属酸化物、もしくは窒化タンタル（Ｔａ3Ｎ5）、硫化カドミウム（ＣｄＳ）等の化合物半導体を用いてもよい。
　触媒層１３には、Ｎｉ、Ｃｏ、Ｃｕ、Ｗ、Ｔａ、Ｐｄ、Ｒｕ、Ｆｅ、Ｚｎ、Ｎｂのうち１種類以上の金属あるいは金属からなる酸化物を用いる。触媒層１３の膜厚は、１ｎｍから１０ｎｍ、特に、光を十分に透過することができる１ｎｍから３ｎｍが望ましい。触媒層１３は半導体薄膜１２の表面の一部のみを被覆してもよい。
　反射層１４には、例えばアルミニウムを用いる。反射層１４には光反射率の高い金属を用いることができる。
　また、図２に示すように、半導体薄膜１２と触媒層１３の間に、第２の半導体薄膜１５を備えてもよい。つまり、図２の半導体光電極は第２の半導体薄膜１５上に触媒層１３を備える。触媒層１３は第２の半導体薄膜１５の表面の一部のみを被覆してもよい。
　［半導体光電極の製造方法］
　図３を参照し、図１の半導体光電極の製造方法の一例について説明する。
　工程１にて、基板１１の裏面（モスアイ構造面に対向する平らな面）に反射層１４を形成する。反射層１４は、基板１１の裏面に反射層１４を構成する金属を真空蒸着して形成してよい。
　工程２にて、絶縁性または導電性の基板１１のモスアイ構造面上に半導体薄膜１２を形成する。半導体薄膜１２は、有機金属気相成長法（ＭＯＣＶＤ）を用いて形成してよい。
　工程３にて、触媒層１３のもととなる金属層を半導体薄膜１２上に形成する。金属層は、半導体薄膜１２の表面に金属を真空蒸着して形成してよい。
　工程４にて、金属層を形成した半導体薄膜を熱処理する。
　図４を参照し、図２の半導体光電極の製造方法の一例について説明する。図４の半導体光電極の製造方法は、図３の半導体光電極の製造方法に、第２の半導体薄膜を形成する工程を追加したものである。
　工程１にて、基板１１の裏面に反射層１４を形成する。
　工程２－１にて、絶縁性または導電性の基板１１のモスアイ構造面上に半導体薄膜１２を形成する。
　工程２－２にて、半導体薄膜１２上に第２の半導体薄膜１５を形成する。第２の半導体薄膜１５は、ＭＯＣＶＤ法を用いて形成してよい。
　工程３にて、触媒層１３のもととなる金属層を半導体薄膜１２上に形成する。
　工程４にて、金属層を形成した半導体薄膜を熱処理する。
　［実施例と比較対象例の作製］
　以下、本実施形態の半導体光電極を作製した実施例１から３について説明する。また、モスアイ構造面を持たない基板を用いた比較対象例１から３についても説明する。
　＜実施例１＞
　実施例１の半導体光電極は図３の製造方法を用いて作製した。
　工程１にて、表面にモスアイ構造を持つサファイア基板の裏面に、反射層１４として金属Ａｌを真空蒸着した。
　工程２にて、サファイア基板のモスアイ構造面上に、ｎ－ＧａＮ半導体薄膜をＭＯＣＶＤ法によりエピタキシャル成長させた。成長原料には、アンモニアガス、トリメチルガリウムを用い、成長炉内に送るキャリアガスには水素を用いた。ドーパント元素としてＳｉを用いた。ｎ－ＧａＮの膜厚は２μｍとした。キャリア密度は３×１０18ｃｍ-3であった。
　工程３にて、ｎ－ＧａＮ半導体薄膜上に、膜厚約１ｎｍのＮｉを真空蒸着した。
　工程４にて、Ｎｉ層を形成した半導体薄膜を、空気中で１時間、３００℃で熱処理し、ＮｉＯ層を形成した。試料断面をＴＥＭ観察すると、ＮｉＯの膜厚は２ｎｍであった。
　以上の工程により、実施例１の半導体光電極を得た。
　＜実施例２＞
　実施例２の半導体光電極は図４の製造方法を用いて作製した。
　工程１にて、表面にモスアイ構造を持つサファイア基板の裏面に、反射層１４として金属Ａｌを真空蒸着した。
　工程２－１にて、サファイア基板のモスアイ構造面上に、ｎ－ＧａＮ半導体薄膜をＭＯＣＶＤ法によりエピタキシャル成長させた。成長原料には、アンモニアガス、トリメチルガリウムを用い、成長炉内に送るキャリアガスには水素を用いた。ドーパント元素としてＳｉを用いた。ｎ－ＧａＮの膜厚は２μｍとした。キャリア密度は３×１０18ｃｍ-3であった。
　工程２－２にて、ｎ－ＧａＮ半導体薄膜上に、Ａｌ0.1Ｇａ0.9Ｎ半導体薄膜をＭＯＣＶＤ法によりエピタキシャル成長させた。成長原料には、アンモニアガス、トリメチルガリウム、トリメチルアルミニウムを用い、成長炉内に送るキャリアガスには水素を用いた。
　工程３にて、ＡｌＧａＮ半導体薄膜上に、膜厚約１ｎｍのＮｉを真空蒸着した。
　工程４にて、Ｎｉ層を形成した半導体薄膜を、空気中で３００℃、１時間熱処理し、ＮｉＯ層を形成した。試料断面をＴＥＭ観察すると、ＮｉＯの膜厚は２ｎｍであった。
　以上の工程により、実施例２の半導体光電極を得た。
　＜実施例３＞
　実施例３の半導体光電極は図４の製造方法を用いて作製した。実施例２とは、第２の半導体薄膜１５の材料が異なる。
　工程１にて、表面にモスアイ構造を持つサファイア基板の裏面に、反射層１４として金属Ａｌを真空蒸着した。
　工程２－１にて、サファイア基板のモスアイ構造面上に、ｎ－ＧａＮ半導体薄膜をＭＯＣＶＤ法によりエピタキシャル成長させた。成長原料には、アンモニアガス、トリメチルガリウムを用い、成長炉内に送るキャリアガスには水素を用いた。ドーパント元素としてＳｉを用いた。ｎ－ＧａＮの膜厚は２μｍとした。キャリア密度は３×１０18ｃｍ-3であった。
　工程２－２にて、ｎ－ＧａＮ半導体薄膜上に、Ｉｎ0.05Ｇａ0.95Ｎ半導体薄膜をＭＯＣＶＤ法によりエピタキシャル成長させた。成長原料には、アンモニアガス、トリメチルガリウム、トリメチルインジウムを用い、成長炉内に送るキャリアガスには水素を用いた。
　工程３にて、ＩｎＧａＮ半導体薄膜上に、膜厚約１ｎｍのＮｉを真空蒸着した。
　工程４にて、Ｎｉ層を形成した半導体薄膜を、空気中で３００℃、１時間熱処理し、ＮｉＯ層を形成した。試料断面をＴＥＭ観察すると、ＮｉＯの膜厚は２ｎｍであった。
　以上の工程により、実施例３の半導体光電極を得た。
　＜比較対象例１＞
　比較対象例１の半導体光電極は、実施例１と比較して、モスアイ構造を持たない平坦なサファイア基板を用いた点で相違する。
　工程１にて、サファイア基板の一方の面に金属Ａｌを真空蒸着し、工程２にて、サファイア基板の他方の面にｎ－ＧａＮ半導体薄膜をＭＯＣＶＤ法によりエピタキシャル成長させた。その他の点においては実施例１と同様である。
　＜比較対象例２＞
　比較対象例２の半導体光電極は、実施例２と比較して、モスアイ構造を持たない平坦なサファイア基板を用いた点で相違する。
　工程１にて、サファイア基板の一方の面に金属Ａｌを真空蒸着し、工程２にて、サファイア基板の他方の面にｎ－ＧａＮ半導体薄膜をＭＯＣＶＤ法によりエピタキシャル成長させた。その他の点においては実施例２と同様である。
　＜比較対象例３＞
　比較対象例３の半導体光電極は、実施例３と比較して、モスアイ構造を持たない平坦なサファイア基板を用いた点で相違する。
　工程１にて、サファイア基板の一方の面に金属Ａｌを真空蒸着し、工程２にて、サファイア基板の他方の面にｎ－ＧａＮ半導体薄膜をＭＯＣＶＤ法によりエピタキシャル成長させた。その他の点においては実施例３と同様である。
　［酸化還元反応試験］
　実施例１から３と比較対象例１から３について図５の装置を用いて酸化還元反応試験を行った。
　図５の装置は、酸化槽１１０と還元槽１２０を備える。酸化槽１１０には、水溶液１１１が入れられ、酸化電極１１２が水溶液１１１中に入れられる。還元槽１２０には、水溶液１２１が入れられ、還元電極１２２が水溶液１２１中に入れられる。
　酸化槽１１０の水溶液１１１には、１ｍｏｌ／ｌの水酸化ナトリウム水溶液を用いた。水溶液１１１として、水酸化カリウム水溶液または塩酸を用いてもよい。
　酸化電極１１２には、試験対象の半導体光電極を用いた。具体的には、実施例１から３および比較対象例１から３のそれぞれについて、ｎ－ＧａＮ表面をけがき、表面の一部に導線を接続し、インジウムを用いてはんだ付けし、インジウム表面が露出しないようにエポキシ樹脂で被覆したものを酸化電極１１２として設置した。
　還元槽１２０の水溶液１２１には、０．５ｍｏｌ／ｌの炭酸水素カリウム水溶液を用いた。水溶液１２１として、炭酸水素ナトリウム水溶液、塩化カリウム水溶液、または塩化ナトリウム水溶液を用いてもよい。
　還元電極１２２には白金（ニラコ製）を用いた。還元電極１２２は金属または金属化合物であればよい。還元電極１２２として、例えば、ニッケル、鉄、金、銀、銅、インジウム、またはチタンを用いてもよい。
　酸化槽１１０と還元槽１２０はプロトン膜１３０を介して繋がっている。酸化槽１１０で生成したプロトンはプロトン膜１３０を介して還元槽１２０へ拡散する。プロトン膜１３０には、ナフィオン（登録商標）を用いた。ナフィオンは、炭素－フッ素からなる疎水性テフロン骨格とスルホン酸基を持つパーフルオロ側鎖から構成されるパーフルオロカーボン材料である。
　酸化電極１１２と還元電極１２２は導線１３２で電気的に接続されており、酸化電極１１２から還元電極１２２へ電子が移動する。
　光源１４０として、３００Ｗの高圧キセノンランプ（照度５ｍＷ／ｃｍ2）を用いた。光源１４０は、酸化電極１１２として設置する半導体光電極を構成する材料が吸収可能な波長の光を照射できればよい。例えば、酸化電極１１２が窒化ガリウムで構成される場合、酸化電極１１２が吸収可能な波長は３６５ｎｍ以下の波長である。光源１４０としては、キセノンランプ、水銀ランプ、ハロゲンランプ、疑似太陽光源、または太陽光などの光源を用いてもよいし、これらの光源を組み合わせてもよい。
　酸化還元反応試験では、各反応槽において窒素ガスを１０ｍｌ／ｍｉｎで流し、試料面積を１ｃｍ2とし、撹拌子とスターラーを用いて２５０ｒｐｍの回転速度で各反応槽の底の中心位置で水溶液１１１，１２１を攪拌した。
　反応槽内が窒素ガスに十分に置換された後、光源１４０を酸化電極１１２として設置した試験対象の半導体光電極のＮｉＯが形成されている面を向くように固定し、半導体光電極に均一に光を照射した。
　光照射１時間後に、各反応槽内のガスを採取し、ガスクロマトグラフにて反応生成物を分析した。その結果、酸化槽１１０では酸素が、還元槽１２０では水素が生成していることを確認した。
　なお、実施例では目的生成物を水素としたが、還元電極の金属（例えば、Ｎｉ、Ｆｅ、Ａｕ、Ｐｔ、Ａｇ、Ｃｕ、Ｉｎ、Ｔｉ、Ｃｏ、Ｒｕ）あるいはセル内の雰囲気を変えることで、二酸化炭素の還元反応による炭素化合物の生成、または窒素の還元反応によるアンモニアの生成も可能である。
　［試験結果］
　実施例１から３および比較対象例１から３における、光照射１時間後の酸素・水素ガスの生成量を表１に示す。各ガスの生成量は、半導体光電極の表面積で規格化して示した。どの例でも光照射時に、酸素と水素が生成していることがわかった。
Figure JPOXMLDOC01-appb-T000001
　実施例１は比較対象例１に比べて、光照射から１時間後の生成量は約１．３倍程度となった。これは、図６に示すように、モスアイ構造を通過した光の拡散性が一方向（垂直方向）に制御され、基板内での光吸収が抑えられ、半導体薄膜に最大限反射できたためと考える。一方、比較対象例１では、図７に示すように、半導体薄膜を透過した光は基板内を散乱しており、反射層で反射した光は、半導体薄膜に届くまでに大部分が基板内で吸収されてしまい、効率的に反射光を利用できていない。
　実施例２，３および比較対象例２，３についても同様の結果であった。
　以上説明したように、本実施形態の半導体光電極は、表面にモスアイ構造を有する導電性または絶縁性の基板１１と、基板１１のモスアイ構造を有する面上に配置された半導体薄膜１２と、半導体薄膜１２上に配置された触媒層１３と、基板１１のモスアイ構造を有する面に対向する裏面に配置された反射層１４を備える。表面にモスアイ構造を有する基板上に半導体薄膜と触媒層を形成し、裏面に反射層を形成することで、照射光の拡散性を垂直方向に制御し、基板内での光吸収を抑制できるので、半導体光電極の光エネルギー変換効率を向上できる。
　１１　基板
　１２　半導体薄膜
　１３　触媒層
　１４　反射層
　１５　半導体薄膜

Claims (3)

  1. 　表面にモスアイ構造を有する導電性または絶縁性の基板と、
    　前記基板の前記モスアイ構造を有する面上に配置された半導体薄膜と、
    　前記半導体薄膜上に配置された触媒層と、
    　前記基板のモスアイ構造を有する面に対向する面に配置された反射層を備える
    　半導体光電極。
  2. 　請求項１に記載の半導体光電極であって、
    　前記半導体薄膜と前記触媒層の間に配置された第２の半導体薄膜を備える
    　半導体光電極。
  3. 　請求項１または２に記載の半導体光電極であって、
    　前記半導体薄膜はｎ型半導体である
    　半導体光電極。
PCT/JP2021/042036 2021-11-16 2021-11-16 半導体光電極 WO2023089655A1 (ja)