WO2021132172A1 - 撥水剤組成物、撥水剤組成物の製造方法、および、繊維製品 - Google Patents
撥水剤組成物、撥水剤組成物の製造方法、および、繊維製品 Download PDFInfo
- Publication number
- WO2021132172A1 WO2021132172A1 PCT/JP2020/047714 JP2020047714W WO2021132172A1 WO 2021132172 A1 WO2021132172 A1 WO 2021132172A1 JP 2020047714 W JP2020047714 W JP 2020047714W WO 2021132172 A1 WO2021132172 A1 WO 2021132172A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- compound
- water
- water repellent
- polyurethane resin
- Prior art date
Abstract
撥水剤組成物は、ポリウレタン樹脂化合物と、非フッ素撥水性化合物と、界面活性剤と、液体媒体とを含む。ポリウレタン樹脂化合物は、第1ポリウレタン樹脂化合物と、第2ポリウレタン樹脂化合物と、第3ポリウレタン樹脂化合物とからなるからなる群から選択される少なくとも1種を含む。
Description
本発明は、撥水剤組成物、撥水剤組成物の製造方法、および、繊維製品に関し、詳しくは、撥水剤組成物、その撥水剤組成物の製造方法、その撥水剤組成物による撥水処理物である繊維製品に関する。
従来、撥水剤として、フッ素化合物を含むフッ素系撥水剤が知られている。この撥水剤を、繊維製品などの基材に対して処理すると、良好な撥水性を示す。
一方、近年、フッ素による環境負荷に対する影響を考慮して、フッ素化合物を含まない非フッ素系撥水剤の需要が高まっている。
このような非フッ素系撥水剤として、例えば、非フッ素重合体と、界面活性剤と、液体媒体とを含む表面処理剤が提案されている(例えば、特許文献1参照。)。
近年、非フッ素系撥水剤には、撥水性のさらなる向上が要求されている。
本発明は、撥水性に優れる撥水剤組成物、その撥水剤組成物の製造方法、および、その撥水剤組成物による撥水処理物である繊維製品を提供することにある。
本発明[1]は、ポリウレタン樹脂化合物と、非フッ素撥水性化合物と、界面活性剤と、液体媒体とを含み、前記ポリウレタン樹脂化合物が、下記(A)第1ポリウレタン樹脂化合物と、下記(B)第2ポリウレタン樹脂化合物と、下記(C)第3ポリウレタン樹脂化合物とからなる群から選択される少なくとも1種を含む、撥水剤組成物である。
(A)平均イソシアネート基数2以上の第1脂肪族ポリイソシアネート誘導体と、炭素数12以上30以下の炭化水素基および活性水素基を併有する第1長鎖活性水素化合物と、活性水素基およびカチオン性基を併有するカチオン性活性水素化合物と、カチオン性基と塩を形成する酸化合物との反応生成物であり、前記炭化水素基の濃度が、30%以上85%以下である第1ポリウレタン樹脂化合物。
(B)イソシアネート化合物と、炭素数12以上30以下のアルキル基を有するアルキルソルビタン、炭素数12以上30以下のアルキル基を有するアルキルシトレートおよび炭素数12以上30以下のアルキル基を有するペンタエリスリトールエステルからなる群から選択される少なくとも1種との反応生成物を含む第2ポリウレタン樹脂化合物。
(C)平均イソシアネート基数2以上の第2脂肪族ポリイソシアネート誘導体と、炭素数12以上30以下の炭化水素基および活性水素基を併有する第2長鎖活性水素化合物との反応生成物を含む第3ポリウレタン樹脂化合物。
(A)平均イソシアネート基数2以上の第1脂肪族ポリイソシアネート誘導体と、炭素数12以上30以下の炭化水素基および活性水素基を併有する第1長鎖活性水素化合物と、活性水素基およびカチオン性基を併有するカチオン性活性水素化合物と、カチオン性基と塩を形成する酸化合物との反応生成物であり、前記炭化水素基の濃度が、30%以上85%以下である第1ポリウレタン樹脂化合物。
(B)イソシアネート化合物と、炭素数12以上30以下のアルキル基を有するアルキルソルビタン、炭素数12以上30以下のアルキル基を有するアルキルシトレートおよび炭素数12以上30以下のアルキル基を有するペンタエリスリトールエステルからなる群から選択される少なくとも1種との反応生成物を含む第2ポリウレタン樹脂化合物。
(C)平均イソシアネート基数2以上の第2脂肪族ポリイソシアネート誘導体と、炭素数12以上30以下の炭化水素基および活性水素基を併有する第2長鎖活性水素化合物との反応生成物を含む第3ポリウレタン樹脂化合物。
本発明[2]は、前記ポリウレタン樹脂化合物および前記非フッ素撥水性化合物の総量100質量部に対して、前記非フッ素撥水性化合物の配合割合が、0.1質量部以上99質量部以下である、上記[1]に記載の撥水剤組成物を含んでいる。
本発明[3]は、前記非フッ素撥水性化合物が、下記式(1)に示す長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび/または下記式(2)に示すアミド基含有モノマーに由来する構成単位を含む重合体である、上記[1]または[2]に記載の撥水剤組成物を含んでいる。
(上記式(1)中、R1は、水素原子またはメチル基を示し、R2は、炭素数18以上炭素数30以下の直鎖状または分岐状の長鎖脂肪族炭化水素基を示す。)
(上記式(2)中、R3は、エチレン性不飽和二重結合基を有する有機残基を示し、R4は、炭素数7以上30以下の1価の炭化水素基を示し、R5は、炭素数1以上5以下の2価の炭化水素基を示す。)
本発明[4]は、前記非フッ素撥水性化合物が、反応性乳化剤に由来する構成単位を含む重合体である、上記[3]に記載の撥水剤組成物を含んでいる。
本発明[4]は、前記非フッ素撥水性化合物が、反応性乳化剤に由来する構成単位を含む重合体である、上記[3]に記載の撥水剤組成物を含んでいる。
本発明[5]は、前記反応性乳化剤が、下記式(3)で示される、上記[4]に記載の撥水剤組成物を含んでいる。
(上記式(3)中、R10は、炭素数12以上20以下のエチレン性不飽和二重結合基を有する有機残基を示し、R11は、炭素数2以上10以下のオキシアルキレン基を示す。)
本発明[6]は、前記非フッ素撥水性化合物が、デンドリマー系撥水剤である、上記[1]または[2]に記載の撥水剤組成物を含んでいる。
本発明[7]は、ブロックイソシアネート化合物、シリコーン重合体およびワックスからなる群から選択される少なくとも1種以上を含む、上記[1]~[6]のいずれか一項に記載の撥水剤組成物を含んでいる。
本発明[8]は、前記第1脂肪族ポリイソシアネート誘導体が、脂肪族ポリイソシアネートのイソシアヌレート誘導体を含む、上記[1]~[7]のいずれか一項に記載の撥水剤組成物を含んでいる。
本発明[9]は、前記第1ポリウレタン樹脂化合物の前記カチオン性活性水素化合物において、前記カチオン性基が、3級アミノ基であり、前記活性水素基が、水酸基であり、前記カチオン性活性水素化合物は、1分子あたり2つ以上の水酸基を有する、上記[1]~[8]のいずれか一項に記載の撥水剤組成物を含んでいる。
本発明[10]は、上記[3]に記載の撥水剤組成物の製造方法であって、前記ポリウレタン樹脂化合物と前記界面活性剤と前記液体媒体との存在下において、前記モノマー成分を重合することにより、前記非フッ素撥水性化合物を生成する、撥水剤組成物の製造方法を含んでいる。
本発明[11]は、上記[1]~[8]のいずれか一項に記載の撥水剤組成物による撥水処理物である、繊維製品を含んでいる。
本発明の撥水剤組成物は、第1ポリウレタン樹脂化合物と、第2ポリウレタン樹脂化合物と、第3ポリウレタン樹脂化合物とからなる群から選択される少なくとも1種を含むポリウレタン樹脂化合物と、非フッ素撥水性化合物とを含む。
そのため、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。
本発明の撥水剤組成物の製造方法は、ポリウレタン樹脂化合物と界面活性剤と液体媒体との存在下において、モノマー成分を重合することにより、非フッ素撥水性化合物を生成する。
そのため、撥水性に優れる撥水剤組成物を製造することができる。
本発明の繊維製品は、本発明の撥水剤組成物による撥水処理物である。
そのため、この繊維製品は、撥水性に優れる。
本発明の撥水剤組成物は、ポリウレタン樹脂化合物と、非フッ素撥水性化合物と、界面活性剤と、液体媒体とを含む。
以下、各成分について詳述する。
1.ポリウレタン樹脂化合物
ポリウレタン樹脂化合物は、第1ポリウレタン樹脂化合物と、第2ポリウレタン樹脂化合物と、第3ポリウレタン樹脂化合物とからなる群から選択される少なくとも1種を含む。
1-1.第1ポリウレタン樹脂化合物
第1ポリウレタン樹脂化合物は、第1脂肪族ポリイソシアネート誘導体と、第1長鎖活性水素化合物と、カチオン性活性水素化合物と、酸化合物との反応生成物である。
1.ポリウレタン樹脂化合物
ポリウレタン樹脂化合物は、第1ポリウレタン樹脂化合物と、第2ポリウレタン樹脂化合物と、第3ポリウレタン樹脂化合物とからなる群から選択される少なくとも1種を含む。
1-1.第1ポリウレタン樹脂化合物
第1ポリウレタン樹脂化合物は、第1脂肪族ポリイソシアネート誘導体と、第1長鎖活性水素化合物と、カチオン性活性水素化合物と、酸化合物との反応生成物である。
第1脂肪族ポリイソシアネート誘導体は、脂肪族ポリイソシアネートの誘導体である。
脂肪族ポリイソシアネートとしては、例えば、ヘキサメチレンジイソシアネート(ヘキサンジイソシアネート)(HDI)、ペンタメチレンジイソシアネート(ペンタンジイソシアネート)(PDI)、テトラメチレンジイソシアネート、トリメチレンジイソシアネート、1,2-、2,3-または1,3-ブチレンジイソシアネート、2,4,4-または2,2,4-トリメチルヘキサメチレンジイソシアネートなどの脂肪族ジイソシアネートが挙げられる。
また、脂肪族ポリイソシアネートには、脂環族ポリイソシアネートが含まれる。
脂環族ポリイソシアネートとしては、例えば、3-イソシアナトメチル-3,5,5-トリメチルシクロヘキシルイソシアネート(イソホロンジイソシアネート、IPDI)、4,4′-、2,4′-または2,2′-メチレンビス(シクロヘキシルイソシアネート)もしくはその混合物(H12MDI)、1,3-または1,4-ビス(イソシアナトメチル)シクロヘキサンもしくはその混合物(H6XDI)、ビス(イソシアナトメチル)ノルボルナン(NBDI)、1,3-シクロペンテンジイソシアネート、1,4-シクロヘキサンジイソシアネート、1,3-シクロヘキサンジイソシアネート、メチル-2,4-シクロヘキサンジイソシアネート、メチル-2,6-シクロヘキサンジイソシアネートなどの脂環族ジイソシアネートが挙げられる。
脂肪族ポリイソシアネートとして、好ましくは、ヘキサメチレンジイソシアネート、1,3-ビス(イソシアナトメチル)シクロヘキサン(以下、単に、ビス(イソシアナトメチル)シクロヘキサンとする。)、より好ましくは、ヘキサメチレンジイソシアネートが挙げられる。
第1脂肪族ポリイソシアネート誘導体としては、例えば、上記した脂肪族ポリイソシアネートの多量体(例えば、2量体、3量体(例えば、イソシアヌレート誘導体、イミノオキサジアジンジオン誘導体)、5量体、7量体など)、アロファネート誘導体(例えば、上記した脂肪族ポリイソシアネートと、1価アルコールまたは2価アルコールとの反応より生成するアロファネート誘導体など)、ポリオール誘導体(例えば、上記した脂肪族ポリイソシアネートと3価アルコール(例えば、トリメチロールプロパンなど)との反応より生成するポリオール誘導体(アルコール付加体、好ましくは、トリメチロールプロパン付加体)など)、ビウレット誘導体(例えば、上記した脂肪族ポリイソシアネートと、水またはアミン類との反応により生成するビウレット誘導体など)、ウレア誘導体(例えば、上記した脂肪族ポリイソシアネートとジアミンとの反応により生成するウレア誘導体など)、オキサジアジントリオン誘導体(例えば、上記した脂肪族ポリイソシアネートと炭酸ガスとの反応により生成するオキサジアジントリオンなど)、カルボジイミド誘導体(上記した脂肪族ポリイソシアネートの脱炭酸縮合反応により生成するカルボジイミド誘導体など)、ウレトジオン誘導体、ウレトンイミン誘導体などが挙げられる。
第1脂肪族ポリイソシアネート誘導体として、好ましくは、イソシアヌレート誘導体が挙げられる。
第1脂肪族ポリイソシアネート誘導体が、イソシアヌレート誘導体を含むと、風合いが良好になる。
そして、第1脂肪族ポリイソシアネート誘導体として、より好ましくは、ヘキサメチレンジイソシアネートのイソシアヌレート誘導体が挙げられる。
第1脂肪族ポリイソシアネート誘導体は、単独使用または2種類以上併用することができる。
また、第1脂肪族ポリイソシアネート誘導体は、公知の方法により製造することができる。
第1脂肪族ポリイソシアネート誘導体の平均イソシアネート基数は、2以上、好ましくは、2.5、より好ましくは、2.9であり、また、例えば、3.8以下である。
上記平均イソシアネート基数が、上記下限以上であれば、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。
なお、平均イソシアネート基数の測定方法は、後述する実施例において、詳述する。
また、第1脂肪族ポリイソシアネート誘導体が、2種類以上併用される場合の上記の平均イソシアネート基数は、第1脂肪族ポリイソシアネート誘導体の重量比とその平均イソシアネート官能基数とにより、算出される。
第1長鎖活性水素化合物は、炭素数12以上30以下の炭化水素基、および、第1脂肪族ポリイソシアネート誘導体と反応する活性水素基を併有する。
炭素数12以上30以下の炭化水素基としては、例えば、炭素数12以上30以下の直鎖状または分岐鎖状の飽和炭化水素基(例えば、アルキル基など)、例えば、炭素数12以上30以下の直鎖状または分岐鎖状の不飽和炭化水素基(例えば、アルケニル基など)などが挙げられる。
活性水素基としては、例えば、水酸基が挙げられる。
このような炭化水素基および活性水素基を併有する第1長鎖活性水素化合物としては、例えば、直鎖状飽和炭化水素基含有活性水素化合物、分岐鎖状飽和炭化水素基含有活性水素化合物、直鎖状不飽和炭化水素基含有活性水素化合物、分岐鎖状不飽和炭化水素基含有活性水素化合物などが挙げられる。
直鎖状飽和炭化水素基含有活性水素化合物は、炭素数12以上30以下の直鎖状飽和炭化水素基を含有する活性水素化合物であって、例えば、n-トリデカノール、n-テトラデカノール、n-ペンタデカノール、n-ヘキサデカノール、n-ヘプタデカノール、n-オクタデカノール(ステアリルアルコール)、n-ノナデカノール、エイコサノールなどの直鎖状飽和炭化水素基含有アルコール、例えば、ソルビタントリステアレートなどの直鎖状飽和炭化水素基含有ソルビタンエステルなどが挙げられる。
分岐鎖状飽和炭化水素基含有活性水素化合物は、炭素数12以上30以下の分岐鎖状の飽和炭化水素基を含有する活性水素化合物であって、例えば、イソミリスチルアルコール、イソセチルアルコール、イソステアリルアルコール、イソイコシルアルコールなどの分岐鎖状飽和炭化水素基含有アルコールなどが挙げられる。
直鎖状不飽和炭化水素基含有活性水素化合物は、炭素数12以上30以下の直鎖状不飽和炭化水素基を含有する活性水素化合物であって、例えば、テトラデセニルアルコール、ヘキサデセニルアルコール、オレイルアルコール、イコセニルアルコール、ドコセニルアルコール、テトラコセニルアルコール、ヘキサコセニルアルコール、オクタコセニルアルコールなどの直鎖状不飽和炭化水素基含有アルコールなどが挙げられる。
分岐鎖状不飽和炭化水素基含有活性水素化合物は、炭素数12以上30以下の分岐鎖状の不飽和炭化水素基を含有する活性水素化合物であって、例えば、フィトールなどが挙げられる。
第1長鎖活性水素化合物として、好ましくは、直鎖状飽和炭化水素基含有活性水素化合物、直鎖状不飽和炭化水素基含有活性水素化合物が挙げられる。
第1長鎖活性水素化合物は、単独使用または2種類以上併用することができ、好ましくは、直鎖状飽和炭化水素基含有活性水素化合物および直鎖状不飽和炭化水素基含有活性水素化合物の併用、より好ましくは、直鎖状飽和炭化水素基含有アルコールおよび直鎖状不飽和炭化水素基含有アルコールの併用、さらに好ましくは、ステアリルアルコールおよびオレイルアルコールの併用が挙げられる。
直鎖状飽和炭化水素基含有アルコールおよび直鎖状不飽和炭化水素基含有アルコールの併用する場合には、直鎖状飽和炭化水素基含有アルコールの配合割合は、直鎖状飽和炭化水素基含有アルコールおよび直鎖状不飽和炭化水素基含有アルコールの総量100質量部に対して、例えば、40質量部以上、好ましくは、55質量部以上、より好ましくは、70質量部以上であり、また、例えば、90質量部以下、好ましくは、80質量部以下である。また、直鎖状不飽和炭化水素基含有アルコールの配合割合は、直鎖状飽和炭化水素基含有アルコールおよび直鎖状不飽和炭化水素基含有アルコールの総量100質量部に対して、例えば、10質量部以上、好ましくは、20質量部以上であり、また、例えば、60質量部以下、好ましくは、45質量部以下、より好ましくは、30質量部以下である。
直鎖状飽和炭化水素基含有アルコールの配合割合が、上記下限以上であれば、炭化水素基の結晶性が向上し、その結果、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。
カチオン性活性水素化合物は、活性水素基、および、カチオン性基を併有する。
活性水素基は、上記したように、第1脂肪族ポリイソシアネート誘導体と反応する活性水素基であって、例えば、水酸基が挙げられる。
また、カチオン性活性水素化合物は、好ましくは、1分子あたり2つ以上の水酸基を有する。
カチオン性基としては、例えば、3級アミノ基が挙げられる。
つまり、カチオン性活性水素化合物は、好ましくは、活性水素基として、1分子あたり2つ以上の水酸基と、カチオン性基として、3級アミノ基とを併有する。
このようなカチオン性活性水素化合物によれば、第1ポリウレタン樹脂化合物の水への良好な分散性を付与でき、また、繊維製品(後述)に親和性を持つカチオン基を樹脂に導入することができるため洗濯耐久性(後述)を向上させることができる。
より好ましくは、カチオン性活性水素化合物は、活性水素基として、1分子あたり2つの水酸基と、カチオン性基として、3級アミノ基とを併有する。
このようなカチオン性活性水素化合物としては、例えば、N-メチルジエタノールアミン、N-エチルジエタノールアミン、N-プロピルジエタノールアミン、N-ブチルジエタノールアミン、N-メチルジプロパノールアミンなどのアルキルジアルカノールアミンなどが挙げられ、好ましくは、N-メチルジエタノールアミンが挙げられる。
カチオン性活性水素化合物は、単独使用または2種類以上併用することができる。
酸化合物は、カチオン性基と塩を形成する化合物である。
酸化合物としては、例えば、有機酸、無機酸などが挙げられる。
有機酸としては、例えば、酢酸、乳酸、酒石酸、リンゴ酸などが挙げられ、好ましくは、酢酸、乳酸、より好ましくは、酢酸が挙げられる。
無機酸としては、例えば、塩酸、硫酸、リン酸などが挙げられ、好ましくは、塩酸が挙げられる。
酸化合物としては、好ましくは、有機酸が挙げられる。
酸化合物が有機酸を含めば、熱処理により酸が揮発することにより、イオン性が低下し耐水性が向上する観点から、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。また、熱処理により酸が揮発することにより、カチオン基が繊維製品に吸着しやすくなる観点から、繊維製品(後述)に対する洗濯耐久性を向上させることができる。
酸化合物は、単独使用または2種類以上併用することができる。
そして、第1ポリウレタン樹脂化合物を得るには、第1脂肪族ポリイソシアネート誘導体と、第1長鎖活性水素化合物と、カチオン性活性水素化合物と、酸化合物とを反応させる。
第1脂肪族ポリイソシアネート誘導体と、第1長鎖活性水素化合物と、カチオン性活性水素化合物と、酸化合物とを反応させるには、まず、第1脂肪族ポリイソシアネート誘導体に、第1長鎖活性水素化合物を配合し、第1脂肪族ポリイソシアネート誘導体と、第1長鎖活性水素化合物とを反応させる。
このとき、第1長鎖活性水素化合物は、例えば、脂肪族ポリイソシアネートのイソシアヌレート誘導体の平均イソシアネート基数が3の場合には、好ましくは、脂肪族ポリイソシアネートのイソシアヌレート誘導体のうち、2つのイソシアネート基が、第1長鎖活性水素化合物によって、炭素数12以上30以下の炭化水素基に変性され、脂肪族ポリイソシアネートのイソシアヌレート誘導体のうち、1つのイソシアネート基が残存するように、かつ、未反応の脂肪族ポリイソシアネートのイソシアヌレート誘導体が残存しないように、配合される。
具体的には、活性水素基に対するイソシアネート基の当量比(イソシアネート基/活性水素基)が、例えば、1.2以上、好ましくは、1.5以上、また、例えば、2.0以下となるように、第1脂肪族ポリイソシアネート誘導体に、第1長鎖活性水素化合物を配合する。
これによって、第1脂肪族ポリイソシアネート誘導体と第1長鎖活性水素化合物との反応生成物(以下、第1中間反応生成物とする)の分子末端が、炭素数12以上30以下の炭化水素基およびイソシアネート基となる。
また、上記の反応は、窒素雰囲気下で実施される。また、反応条件は、反応温度が、例えば、70℃以上120℃以下であり、また、反応時間が、1時間以上6時間以下である。
また、上記の反応は、第1中間反応生成物のイソシアネート濃度が、所定の計算値に到達するまで、実施する。
なお、イソシアネート濃度は、電位差滴定装置を用いて、JIS K-1556に準拠したn-ジブチルアミン法により、測定することができる。
また、上記の反応において、メチルエチルケトンなどの公知の溶媒(溶剤)を、適宜の割合で配合することもできる。
次いで、第1中間反応生成物を含む反応液に、カチオン性活性水素化合物を配合し、第1中間反応生成物と、カチオン性活性水素化合物とを反応させる。
このとき、カチオン性活性水素化合物は、カチオン性活性水素化合物の活性水素基に対するイソシアネート基の当量比(イソシアネート基/活性水素基)が、例えば、0.95以上、また、例えば、1.05以下となるように第1中間反応生成物に、配合される。
また、上記の反応は、窒素雰囲気下で実施される。また、反応条件は、反応温度が、例えば、70℃以上120℃以下であり、また、反応時間が、0.5時間以上4時間以下である。
また、上記の反応は、第1中間反応生成物と、カチオン性活性水素化合物との反応が完結するまで、実施する。
また、上記の反応において、メチルエチルケトンなどの公知の溶媒を、適宜の割合で配合することもできる。
これにより、第1中間反応生成物と、カチオン性活性水素化合物との反応生成物(以下、第2中間反応生成物とする。)が得られる。
第2中間反応生成物は、炭素数12以上30以下の炭化水素基およびカチオン性基を有する。
次いで、第2中間反応生成物に、酸化合物を配合する。
酸化合物の配合割合は、カチオン性活性水素化合物のカチオン性基1モルに対して、例えば、0.5モル以上、好ましくは、3モル以上であり、また、例えば、10モル以下、好ましくは、4モル以下である。
これにより、酸化合物は、第2中間反応生成物のカチオン性基と塩を形成し、第1脂肪族ポリイソシアネート誘導体と、第1長鎖活性水素化合物と、カチオン性活性水素化合物と、酸化合物との反応生成物を含む反応液が得られる。
上記の反応生成物は、炭素数12以上30以下の炭化水素基を有し、かつ、カチオン性基を有する。
また、上記の反応生成物は、炭素数12以上30以下の炭化水素基を有するため、分散剤(乳化剤)によらず、水中で、自己分散(自己乳化)することができる。換言すれば、上記の反応生成物は、内部乳化することができる。
次いで、この反応液の温度を、例えば、50℃以上100℃以下に保ちながら、この反応液に、水を加えて、乳化する。
その後、この反応液から、溶媒を除去する。
これにより、上記の反応生成物を含む水分散液(第1ポリウレタン樹脂化合物の水分散液)が得られる。
水分散液の固形分濃度は、例えば、10質量%以上であり、また、例えば、30質量%以下である。
また、このようなポリウレタン樹脂化合物において、炭化水素基の濃度は、30%以上であり、また、85%以下、好ましくは、50%である。
炭化水素基の濃度が上記下限以上であれば、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。
一方、炭化水素基の濃度が上記下限未満であれば、この撥水剤組成物で処理される撥水処理物の撥水性が低下する。
また、炭化水素基の濃度が上記上限以下であれば、ポリウレタン樹脂の安定性を向上させることができる。
一方、炭化水素基の濃度が上記上限を超過すると、ポリウレタン樹脂の安定性が低下する。
なお、上記の炭化水素基の濃度は、上記した各成分の仕込み量から算出することができる。
なお、上記した説明では、まず、第1脂肪族ポリイソシアネート誘導体と、第1長鎖活性水素化合物とを反応させ、第1中間反応生成物を含む反応液を得、次いで、第1中間反応生成物と、カチオン性活性水素化合物とを反応させ、第2中間反応生成物を含む反応液を得、次いで、第2中間反応生成物と、酸化合物とを反応させたが、反応の順序は特に制限されず、例えば、第1脂肪族ポリイソシアネート誘導体とカチオン性活性水素化合物とを反応させ他後に、第1長鎖活性水素化合物と酸化合物とを反応させることでもきる。また、第1脂肪族ポリイソシアネート誘導体と、第1長鎖活性水素化合物と、カチオン性活性水素化合物と、酸化合物とを一括で配合して、これらを反応させることもできる。
1-2.第2ポリウレタン樹脂化合物
第2ポリウレタン樹脂化合物は、イソシアネート化合物と、炭素数12以上30以下のアルキル基を有するアルキルソルビタン(以下、単に、アルキルソルビタンと称する場合がある。)、炭素数12以上30以下のアルキル基を有するアルキルシトレート(以下、単に、アルキルシトレートと称する場合がある。)および炭素数12以上30以下のアルキル基を有するペンタエリスリトールエステル(以下、単に、ペンタエリスリトールエステルと称する場合がある。)からなる群から選択される少なくとも1種との反応生成物を含む。
1-2-1.イソシアネート化合物
イソシアネート化合物としては、例えば、芳香族ポリイソシアネート、芳香脂肪族ポリイソシアネート、脂肪族ポリイソシアネートなどのポリイソシアネートなどが挙げられる。
1-2.第2ポリウレタン樹脂化合物
第2ポリウレタン樹脂化合物は、イソシアネート化合物と、炭素数12以上30以下のアルキル基を有するアルキルソルビタン(以下、単に、アルキルソルビタンと称する場合がある。)、炭素数12以上30以下のアルキル基を有するアルキルシトレート(以下、単に、アルキルシトレートと称する場合がある。)および炭素数12以上30以下のアルキル基を有するペンタエリスリトールエステル(以下、単に、ペンタエリスリトールエステルと称する場合がある。)からなる群から選択される少なくとも1種との反応生成物を含む。
1-2-1.イソシアネート化合物
イソシアネート化合物としては、例えば、芳香族ポリイソシアネート、芳香脂肪族ポリイソシアネート、脂肪族ポリイソシアネートなどのポリイソシアネートなどが挙げられる。
芳香族ポリイソシアネートとしては、例えば、4,4′-、2,4′-または2,2′-ジフェニルメタンジイソシアネートもしくはその混合物(MDI)、2,4-または2,6-トリレンジイソシアネートもしくはその混合物(TDI)、o-トリジンジイソシアネート、1,5-ナフタレンジイソシアネート(NDI)、m-またはp-フェニレンジイソシアネートもしくはその混合物、4,4′-ジフェニルジイソシアネート、4,4′-ジフェニルエーテルジイソシアネートなどの芳香族ジイソシアネートが挙げられる。
芳香脂肪族ポリイソシアネートとしては、例えば、1,3-または1,4-ビス(イソシアナトメチル)ベンゼン(別名:1,3-または1,4-キシリレンジイソシアネート)もしくはその混合物(XDI)、1,3-または1,4-テトラメチルキシリレンジイソシアネートもしくはその混合物(TMXDI)、ω,ω′-ジイソシアネート-1,4-ジエチルベンゼンなどの芳香脂肪族ジイソシアネートが挙げられる。
脂肪族ポリイソシアネートとしては、例えば、上記した第1ポリウレタン樹脂化合物の脂肪族ポリイソシアネートなどが挙げられる。
ポリイソシアネートとしては、好ましくは、脂肪族ポリイソシアネート、より好ましくは、ヘキサメチレンジイソシアネートが挙げられる。
また、ポリイソシアネートとしては、ポリイソシアネート誘導体も挙げられ、このようなポリイソシアネート誘導体としては、例えば、上記した第1ポリウレタン樹脂化合物のポリイソシアネート誘導体などが挙げられ、好ましくは、ビウレット誘導体が挙げられる。
そして、イソシアネート化合物としては、より好ましくは、ヘキサメチレンジイソシアネートのビウレット誘導体が挙げられる。
イソシアネート化合物は、単独使用または2種類以上併用することができる。
1-2-2.アルキルソルビタン
アルキルソルビタンは、ソルビタンと、炭素数12以上30以下のアルキル基を有するカルボン酸との反応生成物(ソルビタンエステル)である。
1-2-2.アルキルソルビタン
アルキルソルビタンは、ソルビタンと、炭素数12以上30以下のアルキル基を有するカルボン酸との反応生成物(ソルビタンエステル)である。
ソルビタンとしては、例えば、1,4-ソルビタン、2,5-ソルビタン、3,6-ソルビタンなどが挙げられ、好ましくは、1,4-ソルビタンが挙げられる。
ソルビタンは、単独使用または2種類以上併用することができる。
炭素数12以上30以下のアルキル基を有するカルボン酸としては、例えば、ラウリン酸(ドデカン酸)、ミリスチン酸(デトラデカン酸)、パルミチン酸(ヘキサデカン酸)、ステアリン酸(オクタデカン酸)、ベヘン酸(ドコサン酸)などの炭素数12以上30以下のアルキル基を有する直鎖状の飽和カルボン酸、例えば、イソステアリン酸(2-ヘプチルウンデカン酸)などの炭素数12以上30以下のアルキル基を有する分岐状の飽和カルボン酸などが挙げられ、好ましくは、炭素数12以上30以下のアルキル基を有する直鎖状の飽和カルボン酸、より好ましくは、ステアリン酸が挙げられる。
炭素数12以上30以下のアルキル基を有するカルボン酸は、単独使用または2種類以上併用することができる。
そして、アルキルソルビタンは、ソルビタンと炭素数12以上30以下のアルキル基を有するカルボン酸とをエステル化反応させることにより得られる。
詳しくは、上記の反応では、ソルビタンの4つの水酸基のうち、1つ以上3つ以下の水酸基と、12以上30以下のアルキル基を有するカルボン酸のカルボキシル基とが反応するように、ソルビタンの水酸基と、カルボン酸のカルボキシル基との当量比を調整する。
そのため、得られたアルキルソルビタンは、少なくとも1つの水酸基を有する。
そのため、得られたアルキルソルビタンは、少なくとも1つの水酸基を有する。
そして、このようなアルキルソルビタンとして、好ましくは、ソルビタンモノステアレート(好ましくは、1,4-ソルビタンモノステアレート)、ソルビタントリステアレート(好ましくは、1,4-ソルビタントリステアレート)が挙げられる。
アルキルソルビタンは、単独使用または2種類以上併用することができ、好ましくは、ソルビタンモノステアレートおよびソルビタントリステアレートを併用する。
ソルビタンモノステアレートおよびソルビタントリステアレートを併用する場合には、ソルビタンモノステアレートおよびソルビタントリステアレートの総量100質量部に対して、ソルビタンモノステアレートの配合割合は、例えば、10質量部以上であり、また、例えば、50質量部以下である。また、ソルビタンモノステアレートおよびソルビタントリステアレートの総量100質量部に対して、ソルビタントリステアレートの配合割合は、例えば、10質量部以上であり、また、例えば、50質量部以下である。
1-2-2.アルキルシトレート
アルキルシトレートは、クエン酸と、炭素数12以上30以下のアルキル基を有するアルコールとの反応生成物(クエン酸エステル)である。
1-2-2.アルキルシトレート
アルキルシトレートは、クエン酸と、炭素数12以上30以下のアルキル基を有するアルコールとの反応生成物(クエン酸エステル)である。
炭素数12以上30以下のアルキル基を有するアルコールとしては、例えば、ラウリルアルコール、セチルアルコール、ステアリルアルコール、ベヘニルアルコール、ラノリンアルコールなどの炭素数12以上30以下のアルキル基を有する直鎖状の1価のアルコール、例えば、イソステアリルアルコール、2-オクチルドデカノール、2-デシルテトラデカノールなどの炭素数12以上30以下のアルキル基を有する分岐状の1価のアルコールなどが挙げられる。
そして、アルキルシトレートは、クエン酸と炭素数12以上30以下のアルキル基を有するアルコールとを、公知の方法でエステル化反応させることにより得られる。
1-2-3.ペンタエリスリトールエステル
ペンタエリスリトールエステルは、ペンタエリスリトールと、炭素数12以上30以下のアルキル基を有するカルボン酸との反応生成物である。
1-2-3.ペンタエリスリトールエステル
ペンタエリスリトールエステルは、ペンタエリスリトールと、炭素数12以上30以下のアルキル基を有するカルボン酸との反応生成物である。
上記した炭素数12以上30以下のアルキル基を有するカルボン酸は、アルキルソルビタンにおいて挙げた炭素数12以上30以下のアルキル基を有するカルボン酸と同様である。
そして、ペンタエリスリトールエステルは、ペンタエリスリトールと炭素数12以上30以下のアルキル基を有するカルボン酸とを、公知の方法でエステル化反応させることにより得られる。
詳しくは、上記の反応では、ペンタエリスリトールエステルの4つの水酸基のうち、1つ以上3つ以下の水酸基と、12以上30以下のアルキル基を有するカルボン酸のカルボキシル基とが反応するように、ペンタエリスリトールエステルの水酸基と、12以上30以下のアルキル基を有するカルボン酸のカルボキシル基との当量比を調整する。
。そのため、得られたペンタエリスリトールエステルは、少なくとも1つの水酸基を有する。
1-2-4.イソシアネート化合物と、アルキルソルビタン、アルキルシトレートおよびペンタエリスリトールエステルからなる群から選択される少なくとも1種との反応
イソシアネート化合物と、アルキルソルビタン、アルキルシトレートおよびペンタエリスリトールエステルからなる群から選択される少なくとも1種とを反応させるには、活性水素基(水酸基)に対するイソシアネート基の当量比(イソシアネート基/活性水素基(水酸基))が、例えば、0.9以上、1.2以下となるように、アルキルソルビタン、アルキルシトレートおよびペンタエリスリトールエステルからなる群から選択される少なくとも1種に、イソシアネート化合物を配合する。
。そのため、得られたペンタエリスリトールエステルは、少なくとも1つの水酸基を有する。
1-2-4.イソシアネート化合物と、アルキルソルビタン、アルキルシトレートおよびペンタエリスリトールエステルからなる群から選択される少なくとも1種との反応
イソシアネート化合物と、アルキルソルビタン、アルキルシトレートおよびペンタエリスリトールエステルからなる群から選択される少なくとも1種とを反応させるには、活性水素基(水酸基)に対するイソシアネート基の当量比(イソシアネート基/活性水素基(水酸基))が、例えば、0.9以上、1.2以下となるように、アルキルソルビタン、アルキルシトレートおよびペンタエリスリトールエステルからなる群から選択される少なくとも1種に、イソシアネート化合物を配合する。
これにより、イソシアネート化合物と、アルキルソルビタン、アルキルシトレートおよびペンタエリスリトールエステルからなる群から選択される少なくとも1種との反応生成物が得られる。
上記の反応では、必要により、公知の触媒(好ましくは、ジブチルスズジラウレートなど錫触媒)を適宜の割合で配合することができる。
また、上記の反応では、必要により公知の有機溶媒(好ましくは、4-メチル-2-ペンタノン)を適宜の割合で配合することができる。このような場合には、イソシアネート化合物と、アルキルソルビタン、アルキルシトレートおよびペンタエリスリトールエステルからなる群から選択される少なくとも1種との反応生成物を含む反応液が得られる。
また、上記の反応において、反応条件として、反応温度は、例えば、40℃以上であり、また、例えば、90℃以下であり、また、反応時間は、例えば、1時間以上であり、また、例えば、6時間以下である。
次いで、この反応液の温度を、例えば、50℃以上100℃以下に保ちながら、この反応液に、水および乳化剤(好ましくは、カチオン性乳化剤)を加えて、乳化する。
その後、この反応液から、溶媒を除去する。
これにより、イソシアネート化合物と、アルキルソルビタン、アルキルシトレートおよびペンタエリスリトールエステルからなる群から選択される少なくとも1種との反応生成物を含む水分散液が得られる。
上記の分散液の固形分濃度は、例えば、10質量%以上であり、また、例えば、40質量%以下である。
このような反応生成物のうち、好ましくは、イソシアネート化合物と、アルキルソルビタンとの反応生成物が挙げられる。
1-3.第3ポリウレタン樹脂化合物
第3ポリウレタン樹脂化合物は、第2脂肪族ポリイソシアネート誘導体と、第2長鎖活性水素化合物との反応生成物を含む。
1-3.第3ポリウレタン樹脂化合物
第3ポリウレタン樹脂化合物は、第2脂肪族ポリイソシアネート誘導体と、第2長鎖活性水素化合物との反応生成物を含む。
第2脂肪族ポリイソシアネート誘導体としては、上記した第1ポリウレタン樹脂化合物の第1脂肪族ポリイソシアネート誘導体と同様の脂肪族ポリイソシアネート誘導体が挙げられ、好ましくは、ヘキサメチレンジイソシアネートのビウレット誘導体が挙げられる。
第2脂肪族ポリイソシアネート誘導体は、単独使用または2種類以上併用することができる。
第2脂肪族ポリイソシアネート誘導体の平均イソシアネート基数は、2以上、好ましくは、2.5、より好ましくは、2.9であり、また、例えば、3.8以下である。
上記平均イソシアネート基数が、上記下限以上であれば、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。
第2長鎖活性水素化合物は、炭素数12以上30以下の炭化水素基、および、第2脂肪族ポリイソシアネート誘導体と反応する活性水素基を併有する。
炭素数12以上30以下の炭化水素基としては、例えば、上記した第1ポリウレタン樹脂化合物の炭素数12以上30以下の炭化水素基と同様の炭化水素基などが挙げられる。
活性水素基としては、例えば、水酸基が挙げられる。
第2長鎖活性水素化合物として、例えば、上記した第1ポリウレタン樹脂化合物の第1長鎖活性水素化合物と同様の長鎖活性水素化合物が挙げられ、好ましくは、直鎖状飽和炭化水素基含有活性水素化合物、より好ましくは、ステアリルアルコールが挙げられる。
そして、第2脂肪族ポリイソシアネート誘導体と、第2長鎖活性水素化合物とを反応させるには、活性水素基(水酸基)に対するイソシアネート基の当量比(イソシアネート基/活性水素基(水酸基))が、例えば、0.9以上、1.2以下となるように、第2長鎖活性水素化合物に、第2脂肪族ポリイソシアネート誘導体を配合する。
これにより、第2脂肪族ポリイソシアネート誘導体と、第2長鎖活性水素化合物との反応生成物が得られる。
また、上記の反応では、必要により、公知の有機溶媒(メチルエチルケトン)を適宜の割合で配合することができる。このような場合には、第2脂肪族ポリイソシアネート誘導体と、第2長鎖活性水素化合物との反応生成物を含む反応液が得られる。
また、上記の反応において、反応条件として、反応温度は、例えば、40℃以上であり、また、例えば、90℃以下であり、また、反応時間は、例えば、1時間以上であり、また、例えば、6時間以下である。
次いで、この反応液の温度を、例えば、50℃以上100℃以下に保ちながら、この反応液に、水および乳化剤(好ましくは、カチオン性乳化剤)を加えて、乳化する。
その後、この反応液から、溶媒を除去する。
これにより、第2脂肪族ポリイソシアネート誘導体と、第2長鎖活性水素化合物との反応生成物を含む水分散液が得られる。
上記の分散液の固形分濃度は、例えば、10質量%以上であり、また、例えば、40質量%以下である。
そして、上記したように、ポリウレタン樹脂化合物は、上記第1ポリウレタン樹脂化合物、上記第2ポリウレタン樹脂化合物および上記第3ポリウレタン樹脂化合物からなる群から選択される少なくとも1種を含み、好ましくは、上記第1ポリウレタン樹脂化合物、上記第2ポリウレタン樹脂化合物および上記第3ポリウレタン樹脂化合物からなる群から選択されるいずれか1種を含み、さらに好ましくは、この撥水剤組成物で処理される撥水処理物の撥水性を向上させる観点から、ポリウレタン樹脂化合物は、第1ポリウレタン樹脂化合物を含む。
とりわけ、ポリウレタン樹脂化合物が、第1ポリウレタン樹脂化合物を含む場合において、非フッ素撥水性化合物が、アクリル系重合体(具体的には、長鎖脂肪族炭化水素基含有(メタ)アクリレート(後述)に由来する構成単位を含む重合体)である場合には、ウレタン/ポリエステル混紡生地などへの撥水性が向上する。
ポリウレタン樹脂化合物の配合割合は、ポリウレタン樹脂化合物および非フッ素撥水性化合物の総量100質量部に対して、例えば、0.1質量部以上、好ましくは、2質量部以上、より好ましくは、4質量部以上であり、また、例えば、99.9質量部以下、好ましくは、70質量部以下、より好ましくは、50質量部以下、さらに好ましくは、30質量部以下、とりわけ好ましくは、15質量部以下である。
2.非フッ素撥水性化合物
非フッ素撥水性化合物は、フッ素原子を含まない撥水性を有する化合物であって、例えば、長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび/またはアミド基含有モノマーに由来する構成単位を含む重合体である。
2.非フッ素撥水性化合物
非フッ素撥水性化合物は、フッ素原子を含まない撥水性を有する化合物であって、例えば、長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび/またはアミド基含有モノマーに由来する構成単位を含む重合体である。
このような非フッ素撥水性化合物は、長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび/またはアミド基含有モノマーを含むモノマー成分を重合させることにより得られる。
長鎖脂肪族炭化水素基含有(メタ)アクリレートは、長鎖脂肪族炭化水素基含有メタクリレートおよび/または長鎖脂肪族炭化水素基含有アクリレートであり、下記式(1)で示される。
上記式(1)中、R1は、水素原子またはメチル基を示す。
また、上記式(1)中、R2は、炭素数18以上炭素数30以下の直鎖状または分岐状の長鎖脂肪族炭化水素基、好ましくは、炭素数18以上炭素数30以下の直鎖状のアルキル基を示す。
このような長鎖脂肪族炭化水素基含有(メタ)アクリレートとして、具体的には、ステアリル(メタ)アクリレート、ベヘニル(メタ)アクリレートなどが挙げられ、好ましくは、ステアリル(メタ)アクリレート、より好ましくは、ステアリルアクリレートが挙げられる。
長鎖脂肪族炭化水素基含有(メタ)アクリレートは、単独使用または2種類以上併用することができる。
アミド基含有モノマーは、下記式(2)で示される。
上記式(2)中、R3は、エチレン性不飽和二重結合基を有する有機残基であり、炭素同士の二重結合があれば特に限定されない。
R3としては、例えば、-C(=O)CR21=CH2、-CHR21=CH2、-CH2CHR21=CH2などが挙げられ、R21は、水素原子または炭素数1以上4以下のアルキル基が挙げられる。
つまり、R21が、水素原子の場合には、-C(=O)CR21=CH2は、アクリロイル基であり、-CHR21=CH2は、ビニル基であり、-CH2CHR21=CH2は、アリル基である。
また、R3として、エチレン性不飽和二重結合基を少なくとも含むが、それ以外に種々の有機基を併有することもでき、例えば、エチレン性不飽和二重結合基と、例えば、鎖状炭化水素基、環状炭化水素基、ポリオキシアルキレン基、ポリシロキサン基などの有機基(種々の置換基で置換されているものを含む。但し、フッ素原子を含むものを除く。)とを併有してもよい。
上記式(2)中、R4は、炭素数7以上30以下(好ましくは、11以上、より好ましくは、15以上、また、好ましくは、27以下、より好ましくは、23以下)の1価の炭化水素基であり、好ましくは、鎖状炭化水素基、環状炭化水素基、より好ましくは、鎖状炭化水素基、さらに好ましくは、直鎖状の飽和炭化水素基が挙げられる。
上記式(2)中、R5は、炭素数1以上5以下の2価の炭化水素基であり、好ましくは、鎖状炭化水素基、より好ましくは、直鎖状の炭化水素基(飽和炭化水素基または不飽和炭化水素基)、分岐状の炭化水素基(飽和炭化水素基または不飽和炭化水素基)などが挙げられる。
このようなアミド基含有モノマーとして、例えば、パルミチン酸アミドエチル(メタ)アクリレート、ステアリン酸アミドエチル(メタ)アクリレート、ベヘニン酸アミドエチル(メタ)アクリレート、ミリスチン酸アミドエチル(メタ)アクリレート、ラウリン酸アミドエチル(メタ)アクリレート、イソステアリン酸エチルアミド(メタ)アクリレート、オレイン酸エチルアミド(メタ)アクリレート、t-ブチルシクロヘキシルカプロン酸アミドエチル(メタ)アクリレート、アダマンタンカルボン酸エチルアミド(メタ)アクリレート、ナフタレンカルボン酸アミドエチル(メタ)アクリレート、アントラセンカルボン酸アミドエチル(メタ)アクリレート、パルミチン酸アミドプロピル(メタ)アクリレート、ステアリン酸アミドプロピル(メタ)アクリレートなどのアミド基含有(メタ)アクリレート、例えば、パルミチン酸アミドエチルビニルエーテル、ステアリン酸アミドエチルビニルエーテルなどのアミド基含有ビニルエーテル、例えば、パルミチン酸アミドエチルアリルエーテル、ステアリン酸アミドエチルアリルエーテルなどのアミド基含有アリルエーテルが挙げられ、好ましくは、アミド基含有(メタ)アクリレート、より好ましくは、パルミチン酸アミドエチル(メタ)アクリレート、ステアリン酸アミドエチル(メタ)アクリレートまたはそれらの併用が挙げられる。
パルミチン酸アミドエチル(メタ)アクリレートおよびステアリン酸アミドエチル(メタ)アクリレートが併用される場合には、ステアリン酸アミドエチル(メタ)アクリレートは、それらの総量に対して、例えば、55質量%以上、好ましくは、60質量%以上、より好ましくは、65質量%以上であり、また、例えば、99質量%以下、好ましくは、85質量%以下、より好ましくは、80質量%以下である。
アミド基含有モノマーは、単独使用または2種類以上併用することができる。
また、上記モノマー成分は、必要により、短鎖脂肪族炭化水素基含有(メタ)アクリレートを含むこともできる。
短鎖脂肪族炭化水素基含有(メタ)アクリレートは、下記式(3)で示される。
上記式(3)中、R6は、水素原子またはメチル基を示す。
また、上記式(1)中、R7は、炭素数17以下の直鎖状または分岐状の短鎖脂肪族炭化水素基(例えば、炭素数17以下の直鎖状のアルキル基、炭素数17以下の分岐状のアルキル基)を示す。
このような短鎖脂肪族炭化水素基含有(メタ)アクリレートとして、具体的には、メチル(メタ)アクリレート、エチル(メタ)アクリレート、イソプロピル(メタ)アクリレート、t-ブチル(メタ)アクリレート、ラウリル(メタ)アクリレート、ミリスチル(メタ)アクリレート、セチル(メタ)アクリレートなどが挙げられる。
短鎖脂肪族炭化水素基含有(メタ)アクリレートは、単独使用または2種類以上併用することができる。
また、上記モノマー成分は、必要により、環状炭化水素基含有(メタ)アクリレートを含むこともできる。
環状炭化水素基含有(メタ)アクリレートは、下記式(4)で示される。
上記式(4)中、R8は、水素原子またはメチル基を示す。
また、上記式(4)中、R9は、炭素数4以上30以下の環状炭化水素基(例えば、脂環基、芳香族基など)を示す。
このような環状炭化水素基含有(メタ)アクリレートとして、例えば、シクロヘキシル(メタ)アクリレート、t-ブチルシクロヘキシル(メタ)アクリレート、イソボルニル(メタ)アクリレート、ジシクロペンタニル(メタ)アクリレート、ジシクロペンテニル(メタ)アクリレート、ジシクロペンタニルオキシエチル(メタ)アクリレート、トリシクロペンタニル(メタ)アクリレート、アダマンチル(メタ)アクリレート、2-メチル-2-アダマンチル(メタ)アクリレート、2-エチル-2-アダマンチル(メタ)アクリレートなどの脂環基含有(メタ)アクリレート、例えば、ベンジル(メタ)アクリレートなどの芳香族基含有(メタ)アクリレートなどが挙げられる。
環状炭化水素基含有(メタ)アクリレートは、単独使用または2種類以上併用することができる。
また、モノマー成分は、必要により、上記したモノマー成分(長鎖脂肪族炭化水素基含有(メタ)アクリレート、アミド基含有モノマー、短鎖脂肪族炭化水素基含有(メタ)アクリレートおよび環状炭化水素基含有(メタ)アクリレート)と共重合可能な非フッ素共重合性モノマーを含むこともできる。
非フッ素共重合性モノマーとしては、例えば、(メタ)アクリル酸などのカルボキシル基含有モノマー、例えば、酢酸ビニルなどのビニルエステルモノマー、例えば、スチレン、ビニルトルエンなどの芳香族ビニルモノマー、例えば、アクリル酸2-ヒドロキシエチル、アクリル酸4-ヒドロキシブチルなどのヒドロキシル基含有モノマー、例えば、塩化ビニル、臭化ビニル、ヨウ化ビニルなどのハロゲン化ビニルモノマー(フッ素原子を含むものを除く。)などが挙げられ、好ましくは、ハロゲン化ビニルモノマー(フッ素原子を含むものを除く。)、より好ましくは、塩化ビニルが挙げられる。
非フッ素共重合性モノマーは、単独使用または2種類以上併用することができる。
モノマー成分は、好ましくは、長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび/またはアミド基含有モノマーを含み、より好ましくは、長鎖脂肪族炭化水素基含有(メタ)アクリレートのみを含む。
また、モノマー成分は、好ましくは、長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび/またはアミド基含有モノマーと、非フッ素共重合性モノマーとを含み、より好ましくは、長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび非フッ素共重合性モノマーのみを含むか、または、長鎖脂肪族炭化水素基含有(メタ)アクリレートと、アミド基含有モノマーと、非フッ素共重合性モノマーとを含み、さらに好ましくは、長鎖脂肪族炭化水素基含有(メタ)アクリレート、アミド基含有モノマーおよび非フッ素共重合性モノマーのみを含む。
そして、非フッ素撥水性化合物は、上記モノマー成分を重合することにより得られる。
詳しくは、非フッ素撥水性化合物は、長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび/またはアミド基含有モノマーと、必要により配合される短鎖脂肪族炭化水素基含有(メタ)アクリレートと、必要により配合される環状炭化水素基含有(メタ)アクリレートと、必要により配合される非フッ素共重合性モノマーとを、後述する条件に基づいて、重合させることにより得られる。
これにより、非フッ素撥水性化合物が得られる。
そして、このような非フッ素撥水性化合物は、長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび/またはアミド基含有モノマーに由来する構成単位を含む重合体である。
非フッ素撥水性化合物が、長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび/またはアミド基含有モノマーに由来する構成単位を含む重合体であれば、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。
また、詳しくは後述するが、上記モノマー成分の重合は、好ましくは、撥水剤組成物を調製するときに実施する。
また、非フッ素撥水性化合物として、デンドリマー系撥水剤も採用することができる。
デンドリマー系撥水剤としては、放射状でかつ中心から規則的に分枝した構造を持つ鎖状高分子化合物などが挙げられる。
鎖状高分子化合物としては、例えば、エコプラス(ルドルフ社製)などが挙げられる。
非フッ素撥水性化合物の配合割合は、ポリウレタン樹脂化合物および非フッ素撥水性化合物の総量100質量部に対して、例えば、0.1質量部以上、好ましくは、30質量部以上、より好ましくは、50質量部以上、さらに好ましくは、70質量部以上、とりわけ好ましくは、85質量部以上であり、また、例えば、99質量部以下、好ましくは、96質量部以下、より好ましくは、90質量部以下である。
非フッ素撥水性化合物の配合割合は、撥水剤組成物に対して、例えば、15質量%以上であり、また、例えば、30質量%以下である。
非フッ素撥水性化合物の配合割合が、上記した範囲内であれば、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。
3.界面活性剤
界面活性剤は、ポリウレタン樹脂化合物および非フッ素撥水性化合物を分散させる観点から、撥水剤組成物に配合される。
3.界面活性剤
界面活性剤は、ポリウレタン樹脂化合物および非フッ素撥水性化合物を分散させる観点から、撥水剤組成物に配合される。
界面活性剤としては、例えば、ノニオン性界面活性剤、アニオン性界面活性剤、両性界面活性剤などが挙げられる。
ノニオン性界面活性剤としては、例えば、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェニルエーテル、ポリオキシエチレン脂肪酸エステル、ソルビタン脂肪酸エステル、ポリオキシエチレンソルビタン脂肪酸エステル、ポリオキシエチレンソルビトール脂肪酸エステル、グリセリン脂肪酸エステル、ポリオキシエチレングリセリン脂肪酸エステル、ポリグリセリン脂肪酸エステル、ショ糖脂肪酸エステル、ポリオキシエチレンアルキルアミン、ポリオキシエチレン脂肪酸アミド、脂肪酸アルキロールアミド、アルキルアルカノールアミド、アセチレングリコール、アセチレングリコールのオキシエチレン付加物、ポリエチレングリコールポリプロピレングリコールブロックコポリマーなどが挙げられ、好ましくは、グリセリン脂肪酸エステルが挙げられる。
カチオン性界面活性剤としては、ドデシルトリメチルアンモニウムアセテート、トリメチルテトラデシルアンモニウムクロライド、ヘキサデシルトリメチルアンモニウムブロマイド、トリメチルオクタデシルアンモニウムクロライド、(ドデシルメチルベンジル)トリメチルアンモニウムクロライド、ベンジルドデシルジメチルアンモニウムクロライド、メチルドデシルジ(ヒドロポリオキシエチレン)アンモニウムクロライド、ベンジルドデシルジ(ヒドロポリオキシエチレン)アンモニウムクロライドなどが挙げられる。
両性界面活性剤としては、例えば、アラニン化合物、イミダゾリニウムベタイン化合物、アミドベタイン化合物、ラウリルベタイン、酢酸ベタインなどの脂肪酸ベタイン化合物などが挙げられる。
界面活性剤として、好ましくは、ノニオン性界面活性剤が挙げられる。
界面活性剤は、単独使用または2種類以上併用することができる。
界面活性剤の配合割合は、ポリウレタン樹脂化合物および非フッ素撥水性化合物の総量100質量部に対して、例えば、10質量部以上であり、また、例えば、40質量部以下である。
界面活性剤の配合割合は、撥水剤組成物に対して、例えば、0.01質量%以上であり、また、例えば、1質量%以下である。
4.液体媒体
液体媒体は、必須成分として、水を含む。
4.液体媒体
液体媒体は、必須成分として、水を含む。
また、液体媒体は、必要により、さらに、溶剤を含む。
溶剤としては、例えば、アセトン、メチルエチルケトン、シクロヘキサノンなどのケトン類、例えば、アセトニトリルなどのニトリル類、例えば、酢酸メチル、酢酸エチル、酢酸ブチル、酢酸イソブチルなどのアルキルエステル類、例えば、n-ヘキサン、n-ヘプタン、オクタンなどの脂肪族炭化水素類、例えば、シクロヘキサン、メチルシクロヘキサンなどの脂環族炭化水素類、例えば、トルエン、キシレン、エチルベンゼンなどの芳香族炭化水素類、例えば、エタノール、プロピレングリコールなどのアルコール類、例えば、ジプロピレングリコール、ジプロピレングリコールモノメチルエーテル、トリプロピレングリコールなどのグリコールエーテル類などが挙げられ、好ましくは、グリコールエーテル類が挙げられる。
溶剤の配合割合は、液体媒体に対して、例えば、5質量%以上、好ましくは、15質量%以上であり、また、例えば、30質量%以下である。
溶剤は、単独使用または2種類以上併用することができる。
液体媒体の配合割合は、ポリウレタン樹脂化合物および非フッ素撥水性化合物の総量100質量部に対して、例えば、150質量部以上であり、また、例えば、400質量部以下である。
液体媒体の配合割合は、撥水剤組成物に対して、例えば、50質量%以上であり、また、例えば、80質量%以下である。
5.その他の成分
撥水剤組成物は、必要により、ブロックイソシアネート化合物、シリコーン重合体およびワックスからなる群から選択される少なくとも1種以上を含む。
5.その他の成分
撥水剤組成物は、必要により、ブロックイソシアネート化合物、シリコーン重合体およびワックスからなる群から選択される少なくとも1種以上を含む。
ブロックイソシアネート化合物は、イソシアネート化合物のイソシアネート基がブロック剤によってブロックされた化合物である。
撥水剤組成物が、ブロックイソシアネート化合物を含めば、後述する洗濯耐久性を向上させることができる。
ブロックイソシアネート化合物としては、具体的には、特開2017-222827号公報に挙げられる疎水性化合物などが挙げられ、好ましくは、ブロック化剤として3,5-ジメチルピラゾールを有するウレタン化合物が挙げられる。
なお、ブロックイソシアネート化合物は、例えば、乳化剤(後述)と混合して乳化させた水分散液として用いることもできる。
このような場合には、水分散液の固形分濃度は、例えば、10質量%以上であり、また、例えば、40質量%以下である。
ブロックイソシアネート化合物は、単独使用または2種類以上併用することができる。
シリコーン重合体は、SiH基を有するシリコーンと、ビニル基を有する芳香族化合物および/またはα-オレフィンとの反応生成物(ヒドロシリル化反応生成物)である。
撥水剤組成物が、シリコーン重合体を含めば、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。
SiH基を有するシリコーンとしては、例えば、メチルハイドロジェンシリコーン(重合度10以上200以下)、ジメチルシロキサンとメチルハイドロジェンシロキサンとの共重合体などが挙げられ、好ましくは、メチルハイドロジェンシリコーンが挙げられる。
SiH基を有するシリコーンは、単独使用または2種類以上併用することができる。
ビニル基を有する芳香族化合物としては、例えば、スチレン、α-メチルスチレン、ビニルナフタレン、アリルフェニルエーテル、アリルナフチルエーテル、アリル-p-クミルフェニルエーテル、アリル-o-フェニルフェニルエーテル、アリル-トリ(フェニルエチル)-フェニルエーテル、アリル-トリ(2-フェニルプロピル)フェニルエーテルなどが挙げられる。
ビニル基を有する芳香族化合物は、単独使用または2種類以上併用することができる。
α-オレフィンとしては、例えば、エテン、プロペン、1-ブテン、1-ペンテン、1-へキセン、1-ヘプテン、1-オクテン、1-ノネン、1-デセン、1-ウンデセン、1-ドデセン、1-テトラデセン、1-ヘキサデセン、1-オクタデセン、1-ヘキサコセンなどの炭素数2以上30以下のα-オレフィンなどが挙げられ、好ましくは、エテン、1-ヘキサコセン、より好ましくは、この撥水剤組成物で処理される撥水処理物の撥水性を向上させる観点から、1-ヘキサコセンが挙げられる。
α-オレフィンは、単独使用または2種類以上併用することができる。
そして、SiH基を有するシリコーンと、ビニル基を有する芳香族化合物および/またはα-オレフィンとをヒドロシリル化反応させるには、SiH基を有するシリコーンに、ビニル基を有する芳香族化合物および/またはα-オレフィンを配合する。
SiH基を有するシリコーン、ビニル基を有する芳香族化合物およびα-オレフィンの配合割合はそれぞれ、SiH基を有するシリコーンのSiH基当量、または、数平均分子量などに応じて適宜選択される。
なお、ビニル基を有する芳香族化合物および/またはα-オレフィンは、全部また分割して配合することができる。
上記のヒドロシリル化反応では、必要により、ヒドロシリル化触媒を適宜の割合で配合することができる。
ヒドロシリル化触媒としては、例えば、白金、パラジウムなどが挙げられ、好ましくは、白金が挙げられる。
ヒドロシリル化触媒は、単独使用または2種類以上併用することができる。
また、上記のヒドロシリル化反応では、必要により、公知の有機溶媒を適宜の割合で配合することができる。
上記のヒドロシリル化反応において、反応条件として、反応温度は、例えば、50℃以上であり、また、例えば、90℃以下であり、また、反応時間は、例えば、1時間以上であり、また、例えば、6時間以下である。
上記のヒドロシリル化反応は、SiH基を有するシリコーンの、赤外分光法によるSiH基のピークが消失するまで実施する。
これにより、シリコーン重合体が得られる。
このようなシリコーン重合体のうち、好ましくは、SiH基を有するシリコーンとα-オレフィンとの反応生成物、より好ましくは、メチルハイドロジェンシリコーンと、エテンとの反応生成物(ジメチルポリシロキサン)、メチルハイドロジェンシリコーンと1-ヘキサコセンとの反応生成物、さらに好ましくは、この撥水剤組成物で処理される撥水処理物の撥水性を向上させる観点から、メチルハイドロジェンシリコーンと1-ヘキサコセンとの反応生成物が挙げられる。
なお、シリコーン重合体は、上記した界面活性剤(好ましくは、ソルビタン脂肪酸エステル)、水、上記した溶剤、乳化剤(好ましくは、ポリオキシエチレンアルキルエーテル)(後述)と混合して乳化させた水分散液として用いることもできる。
このような場合には、水分散液の固形分濃度は、例えば、10質量%以上であり、また、例えば、40質量%以下である。
シリコーン重合体は、単独使用または2種類以上併用することができる。
ワックスとしては、例えば、例えば、天然ワックス、合成ワックスなどが挙げられる。
天然ワックスとしては、例えば、パラフィンワックス、マイクロクリスタリンワックスなどの石油ワックス、例えば、カルナバワックス、キャンデリラワックスなどの植物ワックスなどの天然ワックスなどが挙げられる。
合成ワックスとしては、例えば、ポリエチレンワックスなどが挙げられる。
ワックスとしては、好ましくは、天然ワックス、より好ましくは、パラフィンワックスが挙げられる。
なお、ワックスは、上記した界面活性剤(好ましくは、ソルビタン脂肪酸エステル)、水、乳化剤(好ましくは、ポリオキシエチレンアルキルエーテル)(後述)と混合して乳化させた水分散液として用いることもできる。
このような場合には、水分散液の固形分濃度は、例えば、10質量%以上であり、また、例えば、40質量%以下である。
撥水剤組成物が、ワックスを含めば、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。
ワックスは、単独使用または2種類以上併用することができる。
ブロックイソシアネート化合物、シリコーン重合体およびワックスからなる群から選択される少なくとも1種の配合割合は、ポリウレタン樹脂化合物および非フッ素撥水性化合物の総量100質量部に対して、例えば、5質量部以上であり、また、例えば、20質量部以下である。
また、ブロックイソシアネート化合物、シリコーン重合体およびワックスからなる群から選択される少なくとも1種の配合割合は、撥水剤組成物に対して、1質量%以上であり、また、例えば、10質量%以下である。
そして、撥水剤組成物が、ブロックイソシアネート化合物を含む場合には、ブロックイソシアネート化合物の配合割合は、ポリウレタン組成物、非フッ素撥水性化合物およびブロックイソシアネート化合物の総量に対して、例えば、5質量%以上であり、また、例えば、20質量%以下である。
また、撥水剤組成物が、シリコーン重合体を含む場合には、シリコーン重合体の配合割合は、ポリウレタン組成物、非フッ素撥水性化合物およびシリコーン重合体の総量に対して、例えば、5質量%以上であり、また、例えば、20質量%以下である。
また、撥水剤組成物が、ワックスを含む場合には、ワックスの配合割合は、ポリウレタン組成物、非フッ素撥水性化合物およびワックスの総量に対して、例えば、5質量%以上であり、また、例えば、20質量%以下である。
6.撥水剤組成物の製造方法
撥水剤組成物は、ポリウレタン樹脂化合物と、非フッ素撥水性化合物と、界面活性剤と、液体媒体とを混合することにより得られる。
6.撥水剤組成物の製造方法
撥水剤組成物は、ポリウレタン樹脂化合物と、非フッ素撥水性化合物と、界面活性剤と、液体媒体とを混合することにより得られる。
具体的には、撥水剤組成物は、好ましくは、ポリウレタン樹脂化合物と界面活性剤と液体媒体との存在下で、上記した非フッ素撥水性化合物を構成するモノマー成分を重合することで、非フッ素撥水性化合物を生成する方法(以下、第1方法とする。)により得られる。
重合方法としては、例えば、懸濁重合、乳化重合などが挙げられ、好ましくは、非フッ素撥水性化合物のエマルションを得る観点から、乳化重合が挙げられる。
乳化重合を採用する場合には、まず、上記モノマー成分(詳しくは、長鎖脂肪族炭化水素基含有(メタ)アクリレートおよび/またはアミド基含有モノマーと、必要により配合される短鎖脂肪族炭化水素基含有(メタ)アクリレートと、必要により配合される環状炭化水素基含有(メタ)アクリレートと、必要により配合される非フッ素共重合性モノマー)の全部または一部と、ポリウレタン樹脂化合物と界面活性剤と液体媒体とを混合し、混合液を調製する。
界面活性剤の配合割合は、モノマー成分の総量100質量部に対して、例えば、1質量部以上、好ましくは、3質量部以上であり、また、例えば、10質量部以下、好ましくは、5質量部以下である。
液体媒体の配合割合は、モノマー成分の総量100質量部に対して、例えば、100質量部以上、好ましくは、200質量部以上であり、また、例えば、400質量部以下、好ましくは、300質量部以下である。
次いで、この混合液に、乳化剤を配合する。
乳化剤としては、公知の乳化剤が挙げられ、例えば、カチオン性乳化剤、アニオン性乳化剤などが挙げられる。
また、乳化剤としては、上記の界面活性剤を用いることもできる。
また、乳化剤は、好ましくは、反応性乳化剤を含む。乳化剤が、反応性乳化剤を含む場合には、非フッ素撥水性化合物(上記モノマー成分の重合体)は、反応性乳化剤に由来する構成単位を含む重合体となる。
非フッ素撥水性化合物が、反応性乳化剤に由来する構成単位を含む重合体であれば、撥水性を低下させることなくして、水分散体(撥剤剤組成物)の製品安定性が改良される。
反応性乳化剤は、ラジカル反応性を有する乳化分散剤、すなわち、分子内に1つ以上の重合性不飽和基を有する乳化剤であり、上記したモノマー成分と共重合可能な乳化剤である。
反応性乳化剤として、例えば、特開2017-25440号公報の反応性乳化剤などが挙げられ、好ましくは、下記式(5)で示される反応性乳化剤が挙げられる。
上記式(5)中、R10は、炭素数12以上20以下のエチレン性不飽和二重結合基を有する有機残基を示す。
R11は、炭素数2以上10以下のオキシアルキレン基を示し、好ましくは、オキシエチレン基を示す
反応性乳化剤が、上記式(5)で示される反応性乳化剤であれば、撥水性を低下させることなくして、水分散体(撥剤剤組成物)の製品安定性が改良される。
反応性乳化剤が、上記式(5)で示される反応性乳化剤であれば、撥水性を低下させることなくして、水分散体(撥剤剤組成物)の製品安定性が改良される。
上記式(5)で示される反応性乳化剤として、好ましくは、ポリオキシエチレンアルキルフェノールなどが挙げられる。
乳化剤は、単独使用または2種類以上併用することができる。
乳化剤の配合割合は、モノマー成分の総量100質量部に対して、例えば、5質量部以上であり、また、例えば、18質量部以下である。
また、乳化剤の配合割合は、ポリウレタン樹脂化合物および非フッ素撥水性化合物の総量100質量部に対して、例えば、8質量部以上であり、また、例えば、20質量部以下である。
また、乳化剤の配合割合は、撥水剤組成物に対して、例えば、0.5質量%以上であり、また、例えば、5質量%以下である。
そして、上記した各成分を混合した後、この混合液を撹拌し、混合液に超音波を与え、混合液を乳化する。
撹拌する方法として、例えば、ホモミキサー(ホモミクサー)、超音波ホモジナイザー、加圧式ホモジナイザー、マイルダー、多孔膜圧入分散機などの分散機が用いられ、好ましくは、ホモミキサーが用いられる。
攪拌条件は、適宜設定され、ホモミキサーを用いる場合には、その回転数を、例えば、500rpm以上に、例えば、10000rpm以下に設定する。攪拌時間は、例えば、0.5分間以上であり、また、例えば、10分以下、好ましくは、5分以下である。攪拌温度は、例えば、50℃以上であり、また、例えば、90℃以下である。
次いで、この混合液に、上記の混合液を調製するときに、モノマー成分の一部を配合した場合には、上記のモノマー成分の残部を配合する。
次いで、この混合液に、重合開始剤を配合する。
重合開始剤としては、例えば、アゾビスイソブチルアミジン-二塩酸塩、アゾビスイソブチロニトリルなどのアゾ化合物、例えば、過硫酸カリウム、過硫酸アンモニウムなど過硫酸物などの水溶性重合開始剤、例えば、ベンゾイルパーオキシド、ジ-t-ブチルパーオキシド、ラウリルパーオキシド、クメンヒドロパーオキシド、t-ブチルパーオキシピバレート、ジイソプロピルパーオキシジカーボネートなどの有機パーオキシドなどの油溶性重合開始剤などが挙げられ、好ましくは、アゾ化合物、より好ましくは、アゾビスイソブチロニトリルが挙げられる。
重合開始剤の配合割合は、モノマー成分100質量部に対して、例えば、0.01質量部以上であり、例えば、10質量部以下である。
また、この混合液には、必要により、連鎖移動剤を配合することができる。
連鎖移動剤としては、例えば、ラウリルメルカプタン、チオグリコール、チオグリセロールなどのメルカプタン基含有化合物(特に、(例えば炭素数1以上30以下の)アルキルメルカプタン)、次亜リン酸ナトリウム、亜硫酸水素ナトリウムなどの無機塩などが挙げられ、好ましくは、ラウリルメルカプタンが挙げられる。
連鎖移動剤の配合割合は、モノマー成分100質量部に対して、例えば、0.01質量部以上であり、また、例えば、10質量部以下である。
そして、この混合液を、加熱して、モノマー成分を重合する。
加熱条件として、加熱温度が、例えば、40℃以上であり、また、例えば、80℃以下であり、また、加熱時間は、例えば、1時間以上であり、また、例えば、6時間以下である。
これにより、非フッ素撥水性化合物のエマルションが得られ、ポリウレタン樹脂化合物と、非フッ素撥水性化合物(エマルション)と、界面活性剤と、液体媒体とを含む撥水剤組成物の分散液が得られる。
第1方法では、ポリウレタン樹脂化合物と界面活性剤と液体媒体との存在下で、上記した非フッ素撥水性化合物を構成するモノマー成分を重合するが、界面活性剤と液体媒体との存在下で、モノマー成分を重合した後に、ポリウレタン樹脂化合物を配合することもできる(第2方法)。
また、まず、モノマー成分を重合し、非フッ素撥水性化合物を調製した後、得られた非フッ素撥水性化合物と、ポリウレタン樹脂化合物、界面活性剤および液体媒体とを配合することもできる(第3方法)。
第3方法において、重合方法としては、例えば、溶液重合、懸濁重合、乳化重合などが挙げられる。
溶液重合を採用する場合には、上記した重合開始剤の存在下で、モノマー成分を有機溶媒に溶解させ、窒素置換後、撹拌しながら加熱する。
重合開始剤の配合割合は、モノマー成分100質量部に対して、例えば、0.01質量部以上であり、また、例えば、20質量部以下、好ましくは、10質量部以下である。
有機溶媒としては、上記した液体媒体で挙げた溶剤などが挙げられる。
有機溶媒の配合割合は、モノマー成分100質量部に対して、例えば、10質量部以上、好ましくは、50質量部以上であり、また、例えば、2000質量部以下、好ましくは、1000質量部以下である。
加熱条件として、加熱温度は、例えば、30℃以上であり、また、例えば、120℃以下であり、加熱時間は、例えば、1時間以上であり、また、例えば、10時間以下である。
これにより、非フッ素撥水性化合物が得られる。
そして、溶液重合により非フッ素撥水性化合物を生成した後に、有機溶媒を除去し、非フッ素撥水性化合物を、ポリウレタン樹脂化合物とともに、界面活性剤および液体媒体に配合することによって、非フッ素撥水性化合物のエマルションを調製することができる。
上記した撥水剤組成物の製造方法のうち、好ましくは、この撥水剤組成物で処理される撥水処理物の撥水性を向上させる観点から、第1方法が採用される。
そして、この撥水剤組成物は、第1ポリウレタン樹脂化合物と、第2ポリウレタン樹脂化合物と、第3ポリウレタン樹脂化合物とからなる群から選択される少なくとも1種を含むポリウレタン樹脂化合物と、非フッ素撥水性化合物とを含む。
そのため、この撥水剤組成物で処理される撥水処理物の撥水性を向上させることができる。
そして、撥水剤組成物は、例えば、水(イオン交換水)で希釈した撥水性処理液として用いることができる。
このような撥水性処理液に、繊維製品(繊維製品)を含浸させることによって、繊維製品に、撥水性を付与することができる。
つまり、繊維製品は、上記撥水剤組成物による撥水処理物である。
繊維としては、例えば、綿または羊毛などなどの天然繊維、例えば、ビスコースレーヨン、レオセルなどの化学繊維、例えば、ポリエステル、ポリアミド、アクリル、ポリウレタン繊維などの合成繊維などが挙げられる。また、繊維製品は、上記の繊維を材料とする製品であって、例えば、布(織物、編物および不織布)などが挙げられる。
この繊維製品は、上記の撥水剤組成物により、撥水処理されているので、撥水性に優れる。
なお、上記した説明では、繊維製品を撥水処理したが、この撥水剤組成物で撥水処理される撥水処理物は、特に限定されず、例えば、紙、石材、ガラス、金属、セメントなどが挙げられる。
以下の記載において用いられる配合割合(含有割合)、物性値、パラメータなどの具体的数値は、上記の「発明を実施するための形態」において記載されている、それらに対応する配合割合(含有割合)、物性値、パラメータなど該当記載の上限値(「以下」、「未満」として定義されている数値)または下限値(「以上」、「超過」として定義されている数値)に代替することができる。また、以下の記載において特に言及がない限り、「部」および「%」は質量基準である。
1.第1脂肪族ポリイソシアネート誘導体の調製
合成例1(ヘキサメチレンジイソシアネートのイソシアヌレート誘導体)
温度計、攪拌装置、窒素導入管および冷却管が装着された反応器において、窒素雰囲気下、1,6-ヘキサメチレンジイソシアネート(HDI、三井化学社製、商品名:タケネート700)500質量部、2,6-ジ(tert-ブチル)-4-メチルフェノール(別名:ジブチルヒドロキシトルエン、BHT、ヒンダードフェノール系酸化防止剤)0.25質量部、テトラフェニル・ジプロピレングリコール・ジホスファイト(有機亜リン酸エステル、助触媒)0.25質量を混合した後、この混合液に1,3-ブタンジオール10.7質量部を加え、窒素を、その液相に1時間導入した。その後、混合液を80℃に昇温し3時間反応後、60℃に降温した。その後、イソシアヌレート化触媒として、トリメチル-N-2-ヒドロキシプロピルアンモニウム・2-エチルヘキサノエート 0.2質量部加え、1.5時間反応させた。その後、HDI 100質量部に対して、o-トルエンスルホンアミド 0.04質量部を添加した。その後、この反応混合液を、薄膜蒸留装置(温度150℃、真空度93.3Pa)に通液して、残存HDIモノマー量が0.5%以下になるまで蒸留し、第1脂肪族ポリイソシアネート誘導体(ヘキサメチレンジイソシアネートのイソシアヌレート誘導体)を得た。得られた第1脂肪族ポリイソシアネート誘導体の、イソシアネート基含有率は20.9%、平均イソシアネート官能基数は3.0であった。
2.ポリウレタン樹脂化合物の調製
製造例1(第1ポリウレタン樹脂化合物)
攪拌機、温度計、冷却器および窒素ガス導入管を備えた反応器に、第1脂肪族ポリイソシアネート誘導体として、合成例1の第1脂肪族ポリイソシアネート誘導体100.20g、第1長鎖活性水素化合物として、カルコール8098(ステアリルアルコール、花王株式会社製)67.60gおよびオレインアルコール22.30gを混合し、窒素雰囲気化110℃で、イソシアネート基の濃度が3.67%になるまで4時間反応させた。
1.第1脂肪族ポリイソシアネート誘導体の調製
合成例1(ヘキサメチレンジイソシアネートのイソシアヌレート誘導体)
温度計、攪拌装置、窒素導入管および冷却管が装着された反応器において、窒素雰囲気下、1,6-ヘキサメチレンジイソシアネート(HDI、三井化学社製、商品名:タケネート700)500質量部、2,6-ジ(tert-ブチル)-4-メチルフェノール(別名:ジブチルヒドロキシトルエン、BHT、ヒンダードフェノール系酸化防止剤)0.25質量部、テトラフェニル・ジプロピレングリコール・ジホスファイト(有機亜リン酸エステル、助触媒)0.25質量を混合した後、この混合液に1,3-ブタンジオール10.7質量部を加え、窒素を、その液相に1時間導入した。その後、混合液を80℃に昇温し3時間反応後、60℃に降温した。その後、イソシアヌレート化触媒として、トリメチル-N-2-ヒドロキシプロピルアンモニウム・2-エチルヘキサノエート 0.2質量部加え、1.5時間反応させた。その後、HDI 100質量部に対して、o-トルエンスルホンアミド 0.04質量部を添加した。その後、この反応混合液を、薄膜蒸留装置(温度150℃、真空度93.3Pa)に通液して、残存HDIモノマー量が0.5%以下になるまで蒸留し、第1脂肪族ポリイソシアネート誘導体(ヘキサメチレンジイソシアネートのイソシアヌレート誘導体)を得た。得られた第1脂肪族ポリイソシアネート誘導体の、イソシアネート基含有率は20.9%、平均イソシアネート官能基数は3.0であった。
2.ポリウレタン樹脂化合物の調製
製造例1(第1ポリウレタン樹脂化合物)
攪拌機、温度計、冷却器および窒素ガス導入管を備えた反応器に、第1脂肪族ポリイソシアネート誘導体として、合成例1の第1脂肪族ポリイソシアネート誘導体100.20g、第1長鎖活性水素化合物として、カルコール8098(ステアリルアルコール、花王株式会社製)67.60gおよびオレインアルコール22.30gを混合し、窒素雰囲気化110℃で、イソシアネート基の濃度が3.67%になるまで4時間反応させた。
次いで、反応液を80℃に冷却し、カチオン性活性水素化合物として、N-メチルジエタノールアミン9.90gを加え、80℃で1時間反応させた。
次いで、溶剤として、メチルエチルケトン 50.00gを加え、80℃で、赤外吸収スペクトルによりイソシアネート基が消失したことが確認できるまで反応させた。
次いで、反応液にメチルエルケトン 57.69gを加え、80℃に昇温し、反応液が完全に溶解するまで混合した後、75℃に冷却した。
その後、酸化合物として酢酸 18.96gを加えて中和させた。
次いで、反応液を75℃に保ちながら、70℃に加温したイオン交換水 800.0gを徐々に加えて乳化(内部乳化)させた。
次いで、エバポレーターにて、水浴温度60℃減圧下で、固形分濃度が20質量%以上となるまで脱溶剤した。
次いで、酸化合物(酢酸)を除く固形分濃度が20質量%となるようにイオン交換水にて調整することにより、第1ポリウレタン樹脂化合物を含む水分散液を得た。
製造例2(第2ポリウレタン樹脂化合物)
攪拌棒、温度計、還流管を備えた500mLの四つ口フラスコに、ソルビタントリステアレート116g、4-メチル-2-ペンタノン(MIBK)150gを仕込んだ。次いで、この混合液の余分な水蒸気を除去するために、混合液の温度を70℃に維持しながら、混合液を撹拌し、混合液を1時間還流し、その後、50℃まで放冷した。そして、撹拌を維持しながら、混合液に、デスモジュールN-100(ヘキサメチレンジイソシアネートのビウレット誘導体、コベストロ社)30gを滴下ロートで滴下した。滴下終了後、触媒として、ジブチルスズジラウレートを1滴加えて、80℃で1時間反応させた。次いで、ソルビタンモノステアレート25gを加えて、さらに、80℃で4時間反応させた。
攪拌棒、温度計、還流管を備えた500mLの四つ口フラスコに、ソルビタントリステアレート116g、4-メチル-2-ペンタノン(MIBK)150gを仕込んだ。次いで、この混合液の余分な水蒸気を除去するために、混合液の温度を70℃に維持しながら、混合液を撹拌し、混合液を1時間還流し、その後、50℃まで放冷した。そして、撹拌を維持しながら、混合液に、デスモジュールN-100(ヘキサメチレンジイソシアネートのビウレット誘導体、コベストロ社)30gを滴下ロートで滴下した。滴下終了後、触媒として、ジブチルスズジラウレートを1滴加えて、80℃で1時間反応させた。次いで、ソルビタンモノステアレート25gを加えて、さらに、80℃で4時間反応させた。
次いで、60℃に冷却後、反応液を回収し、反応液と、任意量のカチオン性乳化剤およびポリオキシエチレンアルキルエーテルを含む60℃の水とをゆっくり混和させた。混和液を、ホモミキサーを用いて、1分6000rpmで撹拌後、超音波で15分間、乳化分散した。その後、減圧操作で溶剤(MIBK)を除去した後、純水を加えて濃度調製し、固形分濃度が20%の第2ポリウレタン樹脂化合物を含む水分散液を得た。
製造例3(第3ポリウレタン樹脂化合物)
攪拌棒、温度計、還流管を備えた500mLの四つ口フラスコに、メチルエチルケトン(MEK)150g、ステアリルアルコール51gを仕込んだ。次いで、この混合液の余分な水蒸気を除去するために、混合液の温度を70℃に維持しながら、混合液を撹拌し、混合液を1時間還流し、その後、50℃まで放冷した。そして、混合液に、デスモジュールN3200A(ヘキサメチレンジイソシアネートのビウレット誘導体、コベストロ社製)30gを加え、さらに、80℃で4時間反応させた。
攪拌棒、温度計、還流管を備えた500mLの四つ口フラスコに、メチルエチルケトン(MEK)150g、ステアリルアルコール51gを仕込んだ。次いで、この混合液の余分な水蒸気を除去するために、混合液の温度を70℃に維持しながら、混合液を撹拌し、混合液を1時間還流し、その後、50℃まで放冷した。そして、混合液に、デスモジュールN3200A(ヘキサメチレンジイソシアネートのビウレット誘導体、コベストロ社製)30gを加え、さらに、80℃で4時間反応させた。
次いで、60℃に冷却後、反応液を回収し、反応液と、任意量のポリオキシエチレンアルキルエーテルを含む60℃の水とをゆっくり混和した。この混和液を、ホモミキサーで1分6000rpmで撹拌後、超音波で15分間、乳化分散した。
次いで、減圧操作で溶剤(MEK)を除去した後、純水を加えて濃度調製し、固形分濃度が20%の第3ポリウレタン樹脂化合物を含む水分散液を得た。
3.非フッ素撥水性化合物と界面活性剤と液体媒体とを含む分散液の調製
製造例4
500mlのプラスチック製容器に、液体媒体として、水溶性グリコール系溶剤30gおよび純水120g、長鎖脂肪族炭化水素基含有(メタ)アクリレートとして、ステアリルアクリレート40g、界面活性剤として、ソルビタン脂肪酸エステル2g、乳化剤として、カチオン性乳化剤2gおよびポリオキシエチレンアルキルエーテル6gを仕込み、80℃に加熱し、ホモミキサーで1分、2000rpmで攪拌した後、超音波で15分間、乳化分散させた。
3.非フッ素撥水性化合物と界面活性剤と液体媒体とを含む分散液の調製
製造例4
500mlのプラスチック製容器に、液体媒体として、水溶性グリコール系溶剤30gおよび純水120g、長鎖脂肪族炭化水素基含有(メタ)アクリレートとして、ステアリルアクリレート40g、界面活性剤として、ソルビタン脂肪酸エステル2g、乳化剤として、カチオン性乳化剤2gおよびポリオキシエチレンアルキルエーテル6gを仕込み、80℃に加熱し、ホモミキサーで1分、2000rpmで攪拌した後、超音波で15分間、乳化分散させた。
次いで、この混合物を500mlのオートクレーブに移し、窒素置換後、連鎖移動剤として、ラウリルメルカプタン0.2g、非フッ素共重合性モノマーとして、塩化ビニルを20g仕込んだ。さらに、重合開始剤として、アゾ基含有水溶性開始剤1gを添加し、60℃で昇温し、4時間反応させて重合体(非フッ素撥水性化合物)の水分散液を得た。この分散液を、さらに、純水で希釈して固形分濃度30%の非フッ素撥水性化合物の水分散液(詳しくは、非フッ素撥水性化合物と界面活性剤と液体媒体とを含む分散液)を調製した。
製造例5~製造例7
表1に従って、配合処方を変更した以外は、製造例4と同様にして、非フッ素撥水性化合物と界面活性剤と液体媒体とを含む分散液を調製した。
4.シリコーン重合体の調製
製造例8
攪拌棒、温度計、還流管を備えた200mLの四つ口フラスコに、メチルハイドロジェンシリコーンオイル(1H NMRにより測定したSiH:SiCH3モル比=50:50)12gおよび白金触媒0.02gを仕込んだ。次いで、1-ヘキサコセン36gを滴下ロートに仕込み、70℃に維持しながら、滴下ロートから1-ヘキサコセンを滴下した。滴下終了後、さらに、70℃3時間反応させた。赤外分光法(IR)によりSiHのピークが消失したことを確認し、固体状のシリコーン重合体47gを得た。
表1に従って、配合処方を変更した以外は、製造例4と同様にして、非フッ素撥水性化合物と界面活性剤と液体媒体とを含む分散液を調製した。
4.シリコーン重合体の調製
製造例8
攪拌棒、温度計、還流管を備えた200mLの四つ口フラスコに、メチルハイドロジェンシリコーンオイル(1H NMRにより測定したSiH:SiCH3モル比=50:50)12gおよび白金触媒0.02gを仕込んだ。次いで、1-ヘキサコセン36gを滴下ロートに仕込み、70℃に維持しながら、滴下ロートから1-ヘキサコセンを滴下した。滴下終了後、さらに、70℃3時間反応させた。赤外分光法(IR)によりSiHのピークが消失したことを確認し、固体状のシリコーン重合体47gを得た。
次いで、シリコーン重合体28g、水溶性グリコール系溶剤5.6g、純水60g、ソルビタン脂肪酸エステル1.7g、ポリオキシエチレンアルキルエーテル0.7g、カチオン性乳化剤0.6gを250mlガラス製容器へ仕込み、75℃に加熱し、ホモミキサーで1分、2000rpmで攪拌した後、超音波で10分間、乳化分散させ、シリコーン重合体の水分散液を得た。その後、純水を追加し、固形分濃度が30質量%のシリコーン重合体の水分散液を調製した。
5.ワックスの調製
製造例9
圧反応容器にパラフィンワックス(融点 75℃)150g、純水350g、ポリオキシエチレンアルキルエーテル4.5g、ソルビタン脂肪酸エステル3gを入れて密封し、攪拌しながら、110~120℃に昇温後、高圧下で30分間高圧乳化することにより、ワックスの水分散液を調製した。その後、純水を追加し、固形分を30%のワックスの水分散液を調製した。
6.撥水剤組成物
<第2方法により撥水剤組成物を製造>
実施例1
製造例1のポリウレタン組成物(固形分濃度20質量%)2.5gと、製造例4の非フッ素撥水性化合物と界面活性剤と液体媒体とを含む分散液(固形分濃度30質量%)31.7gとを混合し、撥水剤組成物を調製した。
5.ワックスの調製
製造例9
圧反応容器にパラフィンワックス(融点 75℃)150g、純水350g、ポリオキシエチレンアルキルエーテル4.5g、ソルビタン脂肪酸エステル3gを入れて密封し、攪拌しながら、110~120℃に昇温後、高圧下で30分間高圧乳化することにより、ワックスの水分散液を調製した。その後、純水を追加し、固形分を30%のワックスの水分散液を調製した。
6.撥水剤組成物
<第2方法により撥水剤組成物を製造>
実施例1
製造例1のポリウレタン組成物(固形分濃度20質量%)2.5gと、製造例4の非フッ素撥水性化合物と界面活性剤と液体媒体とを含む分散液(固形分濃度30質量%)31.7gとを混合し、撥水剤組成物を調製した。
実施例2~実施例30、実施例35および実施例36
表2~表5に従って、配合処方を変更した以外は、実施例1と同様にして、撥水剤組成物を調製した。
表2~表5に従って、配合処方を変更した以外は、実施例1と同様にして、撥水剤組成物を調製した。
なお、表2~表5には、ポリウレタン組成物、非フッ素撥水性化合物、シリコーン重合体、ワックスおよびブロックイソシアネート化合物の総量に対する各成分(ポリウレタン組成物、非フッ素撥水性化合物、シリコーン重合体、ワックス、ブロックイソシアネート化合物)の有効量の配合割合(質量%)を示す。
また、表2~表5中、ステアリル基含有アミドアクリレートとは、ステアリン酸アミドエチルアクリレートである。
また、表2~表5中、ポリオキシエチレンアルキルフェノールは、花王株式会社製ラムテルPD-420である。
また、表2~表5中、デンドリマー系撥水剤とは、具体的には、エコプラス(ルドルフ社製)である。
また、表2~表5中、ブロックイソシアネート組成物とは、具体的には、ブロック化剤として3,5-ジメチルピラゾールを有するウレタン化合物である。
<第1方法により撥水剤組成物を製造>
実施例31
500mlのプラスチック製容器に、液体媒体として、水溶性グリコール系溶剤25.5g、純水113g、長鎖脂肪族炭化水素基含有(メタ)アクリレートとして、ステアリルアクリレート34g、界面活性剤として、ソルビタン脂肪酸エステル1.7g、乳化剤として、カチオン性乳化剤1.7gおよびポリオキシエチレンアルキルエーテル5.1g、シリコーン重合体として、製造例8のシリコーン重合体11g、および、ポリウレタン組成物として、製造例1の第1ポリウレタン組成物(固形分濃度20質量%)の水分散液28gを仕込み、80℃に加熱し、ホモミキサーで1分、2000rpmで攪拌した後、超音波で15分間、乳化分散させた。この分散液を500mlのオートクレーブに移し、窒素置換後、連鎖移動剤として、ラウリルメルカプタン0.17g、非フッ素共重合性モノマーとして、塩化ビニル17gを、仕込んだ。さらに、重合開始剤として、アゾ基含有水溶性開始剤0.85gを添加し、60℃で昇温し、4時間、反応させることにより、撥水剤組成物の水分散液を調製した。次いで、その後、純水を追加し、固形分を30%の水剤組成物の水分散液を調製した。
<第1方法により撥水剤組成物を製造>
実施例31
500mlのプラスチック製容器に、液体媒体として、水溶性グリコール系溶剤25.5g、純水113g、長鎖脂肪族炭化水素基含有(メタ)アクリレートとして、ステアリルアクリレート34g、界面活性剤として、ソルビタン脂肪酸エステル1.7g、乳化剤として、カチオン性乳化剤1.7gおよびポリオキシエチレンアルキルエーテル5.1g、シリコーン重合体として、製造例8のシリコーン重合体11g、および、ポリウレタン組成物として、製造例1の第1ポリウレタン組成物(固形分濃度20質量%)の水分散液28gを仕込み、80℃に加熱し、ホモミキサーで1分、2000rpmで攪拌した後、超音波で15分間、乳化分散させた。この分散液を500mlのオートクレーブに移し、窒素置換後、連鎖移動剤として、ラウリルメルカプタン0.17g、非フッ素共重合性モノマーとして、塩化ビニル17gを、仕込んだ。さらに、重合開始剤として、アゾ基含有水溶性開始剤0.85gを添加し、60℃で昇温し、4時間、反応させることにより、撥水剤組成物の水分散液を調製した。次いで、その後、純水を追加し、固形分を30%の水剤組成物の水分散液を調製した。
なお、表4には、実施例31の、ポリウレタン組成物、非フッ素撥水性化合物およびシリコーン重合体に対する各成分(ポリウレタン組成物、非フッ素撥水性化合物およびシリコーン重合体)の有効量の配合割合(質量%)を示す。
実施例32~実施例34
表6に従って、配合処方を変更した以外は、実施例31と同様にして、撥水剤組成物を調製した。
表6に従って、配合処方を変更した以外は、実施例31と同様にして、撥水剤組成物を調製した。
なお、表4には、実施例32~実施例34の、ポリウレタン組成物、非フッ素撥水性化合物およびシリコーン重合体に対する各成分(ポリウレタン組成物、非フッ素撥水性化合物およびシリコーン重合体)有効量の配合割合(質量%)を示す。
<比較例>
比較例1~比較例17
表4および表5に従って、配合処方を変更した以外は、実施例1と同様にして、撥水剤組成物を調製した。
7.評価
(平均イソシアネート官能基数)
各合成例の脂肪族ポリイソシアネート誘導体の平均イソシアネート官能基数は、脂肪族ポリイソシアネート誘導体のイソシアネート基濃度A、固形分濃度B、および、以下の装置および条件にて測定されるゲルパーミエーションクロマトグラフィーの数平均分子量Cから、下記式(6)により算出した。
<比較例>
比較例1~比較例17
表4および表5に従って、配合処方を変更した以外は、実施例1と同様にして、撥水剤組成物を調製した。
7.評価
(平均イソシアネート官能基数)
各合成例の脂肪族ポリイソシアネート誘導体の平均イソシアネート官能基数は、脂肪族ポリイソシアネート誘導体のイソシアネート基濃度A、固形分濃度B、および、以下の装置および条件にて測定されるゲルパーミエーションクロマトグラフィーの数平均分子量Cから、下記式(6)により算出した。
平均イソシアネート官能基数=A/B×C/42.02 (6)
(式中、Aは、脂肪族ポリイソシアネート誘導体のイソシアネート基濃度を示し、Bは、固形分濃度を示し、Cは、数平均分子量を示す。)
(数平均分子量の測定条件)
装置:HLC-8220GPC(東ソー製)
カラム:TSKgelG1000HXL、TSKgelG2000HXL、およびTSKgelG3000HXL(東ソー製)を直列に連結した
検出器:示差屈折率計
注入量:100μL
溶離液:テトラヒドロフラン
流量:0.8mL/min
温度:40℃
検量線:106~22450の範囲の標準ポリエチレンオキシド(東ソー製、商品名:TSK標準ポリエチレンオキシド)
(撥水性評価)
<試験用布の準備>
各実施例および各比較例の撥水剤組成物を、水道水によって希釈して、固形分濃度1.0質量%の試験液1000gを調製した。
(式中、Aは、脂肪族ポリイソシアネート誘導体のイソシアネート基濃度を示し、Bは、固形分濃度を示し、Cは、数平均分子量を示す。)
(数平均分子量の測定条件)
装置:HLC-8220GPC(東ソー製)
カラム:TSKgelG1000HXL、TSKgelG2000HXL、およびTSKgelG3000HXL(東ソー製)を直列に連結した
検出器:示差屈折率計
注入量:100μL
溶離液:テトラヒドロフラン
流量:0.8mL/min
温度:40℃
検量線:106~22450の範囲の標準ポリエチレンオキシド(東ソー製、商品名:TSK標準ポリエチレンオキシド)
(撥水性評価)
<試験用布の準備>
各実施例および各比較例の撥水剤組成物を、水道水によって希釈して、固形分濃度1.0質量%の試験液1000gを調製した。
次いで、この試験液1に、試験用布(ウレタン/ポリエステル混紡生地、ウレタン/ナイロン混紡生地、ポリエステル生地およびナイロン生地)を含浸した後、マングルに通し、試験用布を160℃で1分間、ピンテンターに通し、乾燥、キュアリングした。
<スプレー法による撥水性評価>
上記した各試験用布を、JIS-L-1092(AATCC-22)のスプレー法に準じて処理布の撥水性を評価した。
<スプレー法による撥水性評価>
上記した各試験用布を、JIS-L-1092(AATCC-22)のスプレー法に準じて処理布の撥水性を評価した。
以下に示す基準で撥水性を評価した。なお、点数が大きいほど、撥水性が良好であることを意味する。その結果を表2~表5に示す。
100 表面に湿潤や水滴の付着が観測されなかった。
90 表面に湿潤しないが、小さな水滴の付着が観測された。
80 表面に小さな個々の水滴上の湿潤が観測された。
70 表面の半分に湿潤を示し、小さな個々の湿潤が布を浸透する状態が観測された。
50 表面全体に湿潤が観測された。
0 表面および裏面が全体に湿潤が観測された。
<ブンデスマン試験>
上記した各試験用布について、JIS-L-1092(C)法に記載のブンデスマン試験に従って、降雨量を80cc/分、降雨水温を20℃、降雨時間を1分とする条件で降雨させ、漏水量(mL)を測定した。なお、漏水量とは、ブンデスマン試験中に生地表面を通過した水分量(ml)を示す。その結果を表2~表5に示す。
<洗濯耐久性>
上記した各試験用布について、JIS L-0217 103に従い、20回洗濯した後、タンブラー(60℃で30分)で乾燥された試験布の撥水性を評価した。その結果を表2~表5に示す。
100 表面に湿潤や水滴の付着が観測されなかった。
90 表面に湿潤しないが、小さな水滴の付着が観測された。
80 表面に小さな個々の水滴上の湿潤が観測された。
70 表面の半分に湿潤を示し、小さな個々の湿潤が布を浸透する状態が観測された。
50 表面全体に湿潤が観測された。
0 表面および裏面が全体に湿潤が観測された。
<ブンデスマン試験>
上記した各試験用布について、JIS-L-1092(C)法に記載のブンデスマン試験に従って、降雨量を80cc/分、降雨水温を20℃、降雨時間を1分とする条件で降雨させ、漏水量(mL)を測定した。なお、漏水量とは、ブンデスマン試験中に生地表面を通過した水分量(ml)を示す。その結果を表2~表5に示す。
<洗濯耐久性>
上記した各試験用布について、JIS L-0217 103に従い、20回洗濯した後、タンブラー(60℃で30分)で乾燥された試験布の撥水性を評価した。その結果を表2~表5に示す。
なお、上記発明は、本発明の例示の実施形態として提供したが、これは単なる例示にすぎず、限定的に解釈してはならない。当該技術分野の当業者によって明らかな本発明の変形例は、後記請求の範囲に含まれるものである。
本発明の撥水剤組成物、および、撥水剤組成物の製造方法は、各種産業製品に利用でき、例えば、表面処理剤用途に好適に用いることができる。本発明の繊維製品は、各種産業製品の製造に好適に用いられる。
Claims (11)
- ポリウレタン樹脂化合物と、非フッ素撥水性化合物と、界面活性剤と、液体媒体とを含み、
前記ポリウレタン樹脂化合物が、
下記(A)第1ポリウレタン樹脂化合物と、
下記(B)第2ポリウレタン樹脂化合物と、
下記(C)第3ポリウレタン樹脂化合物とからなる群から選択される少なくとも1種を含むことを特徴とする、撥水剤組成物。
(A)平均イソシアネート基数2以上の第1脂肪族ポリイソシアネート誘導体と、
炭素数12以上30以下の炭化水素基および活性水素基を併有する第1長鎖活性水素化合物と、
活性水素基およびカチオン性基を併有するカチオン性活性水素化合物と、
カチオン性基と塩を形成する酸化合物との反応生成物であり、
前記炭化水素基の濃度が、30%以上85%以下である第1ポリウレタン樹脂化合物。
(B)イソシアネート化合物と、
炭素数12以上30以下のアルキル基を有するアルキルソルビタン、炭素数12以上30以下のアルキル基を有するアルキルシトレートおよび炭素数12以上30以下のアルキル基を有するペンタエリスリトールエステルからなる群から選択される少なくとも1種との反応生成物を含む第2ポリウレタン樹脂化合物。
(C)平均イソシアネート基数2以上の第2脂肪族ポリイソシアネート誘導体と、炭素数12以上30以下の炭化水素基および活性水素基を併有する第2長鎖活性水素化合物との反応生成物を含む第3ポリウレタン樹脂化合物。 - 前記ポリウレタン樹脂化合物および前記非フッ素撥水性化合物の総量100質量部に対して、前記非フッ素撥水性化合物の配合割合が、0.1質量部以上99質量部以下であることを特徴とする、請求項1に記載の撥水剤組成物。
- 前記非フッ素撥水性化合物が、反応性乳化剤に由来する構成単位を含む重合体であることを特徴とする、請求項3に記載の撥水剤組成物。
- 前記非フッ素撥水性化合物が、デンドリマー系撥水剤であることを特徴とする、請求項1に記載の撥水剤組成物。
- ブロックイソシアネート化合物、シリコーン重合体およびワックスからなる群から選択される少なくとも1種以上を含むことを特徴とする、請求項1に記載の撥水剤組成物。
- 前記第1脂肪族ポリイソシアネート誘導体が、脂肪族ポリイソシアネートのイソシアヌレート誘導体を含むことを特徴とする、請求項1に記載の撥水剤組成物。
- 前記第1ポリウレタン樹脂化合物の前記カチオン性活性水素化合物において、
前記カチオン性基が、3級アミノ基であり、
前記活性水素基が、水酸基であり、
前記カチオン性活性水素化合物は、1分子あたり2つ以上の水酸基を有することを特徴とする、請求項1に記載の撥水剤組成物。 - 請求項3に記載の撥水剤組成物の製造方法であって、
前記ポリウレタン樹脂化合物と前記界面活性剤と前記液体媒体との存在下において、前記モノマー成分を重合することにより、前記非フッ素撥水性化合物を生成することを特徴とする、撥水剤組成物の製造方法。 - 請求項1に記載の撥水剤組成物による撥水処理物であることを特徴とする、繊維製品。