WO2021040932A1 - Improved microgranulation methods and product particles therefrom - Google Patents

Improved microgranulation methods and product particles therefrom Download PDF

Info

Publication number
WO2021040932A1
WO2021040932A1 PCT/US2020/043621 US2020043621W WO2021040932A1 WO 2021040932 A1 WO2021040932 A1 WO 2021040932A1 US 2020043621 W US2020043621 W US 2020043621W WO 2021040932 A1 WO2021040932 A1 WO 2021040932A1
Authority
WO
WIPO (PCT)
Prior art keywords
particles
product
graphite
precursor
precursor particles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2020/043621
Other languages
English (en)
French (fr)
Inventor
Mark Obrovac
Lituo Zheng
Matthew GARAYT
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Novonix Battery Technology Solutions Inc
Original Assignee
Novonix Battery Testing Services Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to PL20757437.7T priority Critical patent/PL4021855T3/pl
Priority to JP2022510172A priority patent/JP2022546264A/ja
Priority to US17/638,646 priority patent/US12434978B2/en
Priority to CN202511790134.2A priority patent/CN121651451A/zh
Priority to CA3146930A priority patent/CA3146930A1/en
Priority to EP20757437.7A priority patent/EP4021855B1/en
Priority to CN202080060756.9A priority patent/CN114341061B/zh
Priority to KR1020227009567A priority patent/KR20220054822A/ko
Application filed by Novonix Battery Testing Services Inc filed Critical Novonix Battery Testing Services Inc
Publication of WO2021040932A1 publication Critical patent/WO2021040932A1/en
Anticipated expiration legal-status Critical
Priority to JP2025038649A priority patent/JP2025105606A/ja
Priority to US19/261,930 priority patent/US20250369147A1/en
Priority to US19/309,288 priority patent/US20250376387A1/en
Ceased legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G1/00—Methods of preparing compounds of metals not covered by subclasses C01B, C01C, C01D, or C01F, in general
    • C01G1/02—Oxides
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G53/00—Compounds of nickel
    • C01G53/80—Compounds containing nickel, with or without oxygen or hydrogen, and containing one or more other elements
    • C01G53/82—Compounds containing nickel, with or without oxygen or hydrogen, and containing two or more other elements
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G45/00—Compounds of manganese
    • C01G45/12—Complex oxides containing manganese and at least one other metal element
    • C01G45/1221—Manganates or manganites with trivalent manganese, tetravalent manganese or mixtures thereof
    • C01G45/1228—Manganates or manganites with trivalent manganese, tetravalent manganese or mixtures thereof of the type (MnO2)-, e.g. LiMnO2 or Li(MxMn1-x)O2
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G45/00—Compounds of manganese
    • C01G45/20—Compounds containing manganese, with or without oxygen or hydrogen, and containing one or more other elements
    • C01G45/22—Compounds containing manganese, with or without oxygen or hydrogen, and containing two or more other elements
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G51/00—Compounds of cobalt
    • C01G51/40—Complex oxides containing cobalt and at least one other metal element
    • C01G51/42—Complex oxides containing cobalt and at least one other metal element containing alkali metals, e.g. LiCoO2
    • C01G51/44—Complex oxides containing cobalt and at least one other metal element containing alkali metals, e.g. LiCoO2 containing manganese
    • C01G51/50—Complex oxides containing cobalt and at least one other metal element containing alkali metals, e.g. LiCoO2 containing manganese of the type (MnO2)n-, e.g. Li(CoxMn1-x)O2 or Li(MyCoxMn1-x-y)O2
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G51/00—Compounds of cobalt
    • C01G51/80—Compounds containing cobalt, with or without oxygen or hydrogen, and containing one or more other elements
    • C01G51/82—Compounds containing cobalt, with or without oxygen or hydrogen, and containing two or more other elements
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G53/00—Compounds of nickel
    • C01G53/40—Complex oxides containing nickel and at least one other metal element
    • C01G53/42—Complex oxides containing nickel and at least one other metal element containing alkali metals, e.g. LiNiO2
    • C01G53/44—Complex oxides containing nickel and at least one other metal element containing alkali metals, e.g. LiNiO2 containing manganese
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G53/00—Compounds of nickel
    • C01G53/40—Complex oxides containing nickel and at least one other metal element
    • C01G53/42—Complex oxides containing nickel and at least one other metal element containing alkali metals, e.g. LiNiO2
    • C01G53/44—Complex oxides containing nickel and at least one other metal element containing alkali metals, e.g. LiNiO2 containing manganese
    • C01G53/50—Complex oxides containing nickel and at least one other metal element containing alkali metals, e.g. LiNiO2 containing manganese of the type (MnO2)n-, e.g. Li(NixMn1-x)O2 or Li(MyNixMn1-x-y)O2
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B1/00—Single-crystal growth directly from the solid state
    • C30B1/12—Single-crystal growth directly from the solid state by pressure treatment during the growth
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B29/00—Single crystals or homogeneous polycrystalline material with defined structure characterised by the material or by their shape
    • C30B29/10—Inorganic compounds or compositions
    • C30B29/16—Oxides
    • C30B29/22—Complex oxides
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/50—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese
    • H01M4/505—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/52—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron
    • H01M4/525—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/20—Two-dimensional structures
    • C01P2002/22—Two-dimensional structures layered hydroxide-type, e.g. of the hydrotalcite-type
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/50—Solid solutions
    • C01P2002/52—Solid solutions containing elements as dopants
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
    • C01P2002/74—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by peak-intensities or a ratio thereof only
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
    • C01P2002/76—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by a space-group or by other symmetry indications
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
    • C01P2002/77—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by unit-cell parameters, atom positions or structure diagrams
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/80—Crystal-structural characteristics defined by measured data other than those specified in group C01P2002/70
    • C01P2002/85—Crystal-structural characteristics defined by measured data other than those specified in group C01P2002/70 by XPS, EDX or EDAX data
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/01—Particle morphology depicted by an image
    • C01P2004/03—Particle morphology depicted by an image obtained by SEM
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/30—Particle morphology extending in three dimensions
    • C01P2004/32—Spheres
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/51—Particles with a specific particle size distribution
    • C01P2004/52—Particles with a specific particle size distribution highly monodisperse size distribution
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/62—Submicrometer sized, i.e. from 0.1-1 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/64—Nanometer sized, i.e. from 1-100 nanometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/40—Electric properties
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries

Definitions

  • the present invention pertains to improved microgranulation methods for aggregating precursor particles into larger product particles with improved properties and, in some instances, novel structures.
  • the product particles are useful as electrode materials in lithium batteries and other applications.
  • the particles used in the manufacture of electrodes for rechargeable high energy density batteries such as Li-ion batteries
  • the particles used in the manufacture of electrodes for rechargeable high energy density batteries can be spherical in shape and of uniform size.
  • the cathode particles for Li- ion batteries e.g. lithium nickel manganese cobalt oxides or NMC
  • the cathode particles for Li- ion batteries are often made by a co precipitation process in a continuous flow tank reactor. This results in a broad particle size distribution because of the variable particle residence time of the particles in the reactor.
  • careful process control and various chemical additives are required (e.g.
  • the anode particles for Li-ion batteries are typically carbonaceous, e.g. graphite particles.
  • the natural graphite is first ground and classified in order to obtain a powder with the desired size distribution (-10-20 pm in diameter). The sized powders are then spheronized using a spheronizer.
  • the spheronizing process is typically only 50-60% efficient, producing a mixture of the desired spheronized particles and fine particles less than 5 pm in diameter.
  • the resulting mixture requires an additional classification step to separate the desired particles from the fine particles, which are typically disposed of as waste. Obviously then, a significant amount of the starting natural graphite is lost as a result.
  • Granulation is a method in which small particles may be aggregated into larger particles.
  • Granulation methods include both wet and dry methods.
  • Wet granulation methods include fluid bed, disc, drum, and mixer (e.g. via the use of pins, paddles and/or blades) methods. Such wet methods require the separation of the product particles from liquids and may require additional binders or dispersing agents.
  • Dry granulation methods include roll pressing, tableting, ram/piston extrusion, pelleting mills, radial extrusion, and axial exclusion.
  • both wet and dry methods of granulation have difficulty in making uniform product particles less than 100 pm in diameter and the resulting product particles can often contain internal voids.
  • a fluid comprising a liquid (typically water) and suspended particulates and/or dissolved species are sprayed through a nozzle to produce droplets.
  • the fluid can further contain additives, such as wetting agents and binders.
  • the droplets emitted from the spray nozzle are dried (e.g. by a flow of air) while still airborne and captured in a filter.
  • This method can be expensive and wasteful, as it is typically energy intensive to remove the liquid during the drying step and the liquid is often lost as waste.
  • the resulting powders are often porous and may need further processing (e.g. washing and filtering).
  • Prilling is a method in which a molten liquid spray is solidified in-flight. This method is only applicable for materials that can form a molten state.
  • MF mechanofiision
  • onion graphite refers to spherical or ovoid graphite particles where the graphite basal planes are arranged in nested ovoid or spherical smooth concentric layers centered around a common point in the core of the particle, and where the alignment of the edges of graphite sheets does not radiate from a central nucleus (to others, onion graphite refers to only to perfect nested buckyballs).
  • the graphene layers in onion graphite are randomly positioned on the surface of the concentric nested spheres or ovoids, excepting that they are oriented such that their basal planes are tangential to the concentric nested spheres or ovoids.
  • Onion graphite can be differentiated from graphite spheres in cast irons, which are known to have a micro structure in which the graphite basal planes are arranged concentrically, however the edges of the planes radiate from a central core (e.g. as shown in Figure 6-4 of "Mesomolecules: From Molecules to Materials" SEARCH Series, Volume 1, G. David Mendenhall, Arthur Greenberg, and Jeol F.
  • Nano-sized graphite onions have only been made previously in small quantities by synthetic means, for instance by the high electron irradiation of carbon particles, the annealing of nanodiamonds, an arc discharge between two graphite electrodes submerged in water, the carbon-ion implantation of silver or copper substrates (e.g. see V.D. Blank, B.A. Kulnitskiy and I.A.
  • product particles can desirably be made in narrow particle size distributions and in smooth, spherical or rounded shapes that are free from cavities. In some aspects, cavities can be included within the product particles.
  • the product particles are made using a microgranulation method involving the steps of: obtaining an amount of precursor particles having an average particle size less than 1000 pm, obtaining an amount of templating media having an average particle size less than 500 pm and a hardness greater than that of the precursor particles, and then preparing a mixture comprising the amounts of precursor particles and templating media. This mixture is then subjected to an appropriate high shear and high pressure field, such as that obtained via mechanofusion, such that the precursor particles are aggregated into desirable product particles. The product particles can then be separated from the templating media if desired for an intended application.
  • precursor particles having a wide range of properties.
  • Suitable types of precursor particles include powders intended for use (either directly or after subsequent processing) in battery electrodes, fertilizers, pharmaceuticals, toners, pigments, fillers, or catalysts.
  • suitable precursor particles include carbonaceous powders, mixed metal oxide powders or metal carbonate powders, e.g. a carbon, graphite flakes or LiNiiaMniaComCE powder.
  • mixed metal oxide powders used as precursor particles may be made by an all -solid-state method comprising ball milling an amount of metal oxide raw material powders to produce the precursor particles.
  • the precursor particles used in the following Examples were not suitable for use per se in battery electrodes but can be made suitable for such use by microgranulation processing and optionally by subsequent processing steps, e.g. by heating.
  • at least a portion of the amount of precursor particles may be processed in some suitable manner prior to preparing the mixture (including ball milling or heating). While the inventive method desirably produced spherical and/or rounded aggregate, the starting precursor particles can be quite irregularly shaped powders. In addition, while the inventive method desirably produces powders with a narrow particle size distribution, the particle size distribution of the starting precursor particles can be quite large.
  • the resulting characteristics of the product particles obtained are in part a function of those of the templating media employed.
  • the hardness of the templating media is greater than that of the precursor particles so as not to break down the former.
  • Suitable templating media may thus be selected from the group consisting of zirconium oxide, tungsten carbide, tungsten, silicon oxide, aluminum oxide, silicon nitride, hardened steel, stainless steel, and agate.
  • templating media whose average size is 100 pm or smaller may be employed.
  • the surface of the templating media may desirably be smooth and spherically shaped.
  • it is desirable for the size distribution of the templating media to be uniform, e.g.
  • the bulk volume of the amount of templating media employed can be greater than that of the bulk volume of the amount of precursor particles employed, and particularly greater than or about three times that of the bulk volume of the amount of precursor particles.
  • a mechanofusion system suitable for use in the inventive method can comprise a chamber, a rotating wall within the chamber, a scraper within the rotating wall, and a press-head within the rotating wall.
  • a representative gap between the scraper and the rotating wall may be about 0.5 mm.
  • a representative gap between the press-head and the rotating wall may be about 1.4 mm.
  • a representative speed for rotating the rotating wall is one that results in wall surface speeds of about 8 m/s.
  • mechanofusing times of greater than or about 12 hours have proved to be successful. Shorter processing times may be achieved if the templating media already coated with precursor from a previous synthesis are reused in a new synthesis. While the aforementioned system produces product in batch form, advantageously mechanofusion can also be performed in a continuous manner (for instance with suitable modifications to such a system).
  • product particles can be produced whose average size is between 10 and 100 pm. Further, the size distribution of exemplary product particles can be sufficiently uniform such that (D90-D10)/D50 ⁇ 2. Further still, the surface of the product particles may desirably be smooth. In some aspects of the invention the product particles comprise particles having a roughness (as defined below) less than 0.02, less than 0.01, less than 0.006 or even smaller. In some aspects of the invention all the product particles essentially have roughness values less than 0.02, less than 0.01, less than 0.006 or even smaller. In some aspects of the invention, the product particles comprise particles that are essentially free from cavities. In some aspects of the invention, all the product particles are essentially free from cavities And as demonstrated in the Examples below, product particles can be made that are spherically shaped or tetrahedrally shaped.
  • the complete preparation of product particles may additionally comprise an annealing step at an elevated temperature (for instance to recrystallize the particles following mechanofusion).
  • the product particles made according to the inventive method may be considered for use in numerous commercial applications including as a battery electrode, a fertilizer, a pharmaceutical, a toner, a pigment, a fdler, or a catalyst. They can be particularly suitable for use in anode or cathode electrodes in rechargeable lithium batteries, e.g. lithium ion batteries.
  • a novel graphite particulate comprises graphite particles in which the graphite particles are shaped as spheres or ovoids and they comprise concentric nested spheres or ovoids of graphene layers. These graphene layers are randomly positioned on the surface of the concentric nested spheres or ovoids, except that the graphene layers are oriented such that their basal planes are tangential to the concentric nested spheres or ovoids.
  • the graphite particles further have an average particle size greater than 2 pm and an average doo2 spacing of less than 3.400 A.
  • the graphite particles in the particulate comprise concentric layers of porosity with a void or hollow near its core. In some embodiments, the graphite particles have an average particle size between 5 pm and 50 pm and a size distribution of (D90-D10)/D50 ⁇ 2.
  • a novel lithium mixed metal oxide particulate comprises particles having a core of lithium nickel manganese cobalt oxide crystallites that are randomly oriented and have an average size of about 1 pm coated with smaller randomly oriented lithium nickel manganese cobalt oxide crystallites that have an average size of about 0.3 pm.
  • the preceding novel lithium transition metal oxide particulate comprises particles having at least two transition metals present from the group consisting of Mn, Ni, and Co. Further, the particles have an 03 structure, an average particle size ranging from 1 to 50 pm, and they comprise crystallites that vary randomly in shape and size throughout their interior. In certain embodiments, the crystallites have an average size greater than 0.5 pm and the average particle size of the particles is more than 5 times larger than the average crystallite size. In certain embodiments, the composition of one of the two transition metals can vary from the core of the particles to the shell of the particles by at least 5 atomic %.
  • the method can be used to make product particles of uniform composition but also can be used to make product particles having different compositions near their core than near their surface.
  • the precursor particles employed may be a single phase or they may consist of a mixture of particles having different characteristics.
  • the precursor particles may consist of a mixture of first particles of a first composition and second particles of a second composition in which the first and second compositions are different and/or in which the first and second particles have comprise crystallites with different average crystallite sizes (e.g. in which the average crystallite size of the first precursor particles differs from the average crystallite size of the second precursor particles by at least 10%).
  • Suitable precursor particles for the formation of graphite product particles include graphitizable carbons, such as natural graphite, coke, and soft carbons.
  • Suitable precursor particles for the formation of product particles useful as cathode materials in Li-ion batteries include hydroxides, oxides, sulfates, nitrates, and carbonates of lithium, aluminum, magnesium, transition metals, and mixtures thereof.
  • suitable precursor particles are lithium nickel manganese cobalt oxide particles.
  • suitable precursor particles are lithium transition metal oxide particles.
  • Figure 1 schematically shows a mechanofusion system suitable for use in the microgranulation method of the invention.
  • Figures 2a and 2b show SEM images of the ZrCh templating media used in the Examples at two different magnifications.
  • Figure 2c shows a cross section of a ZrCh particle with its perimeter and centroid shown.
  • Figure 2d shows a plot of the residuals of the interpolated radial segment values and the interpolated ftx) values a function of x.
  • Figure 3 shows the particle size distribution of the ZrCh templating media used in the Examples.
  • Figures 4a and 4b show SEM images of the graphite flake precursor particles used in the Examples at two different magnifications.
  • Figures 5a and 5b show SEM images at two different magnifications of the product obtained after mechanofusing the mixture of graphite flake precursor particles and ZrCE templating media.
  • Figures 6a and 6b show SEM images at two different magnifications of the graphite sphere product particles in Figures 5a and 5b after separating them from the ZrCE templating media.
  • Figures 7a, 7b, and 7c show the XRD patterns between 20° and 65° of the graphite flake precursor particles before mechanofusing, the graphite sphere product particles after mechanofusing and separation from the templating media, and the graphite sphere product particles after annealing respectively.
  • Figure 8 shows the particle size distribution of the graphite sphere product particles after annealing. For comparison, the particle size distribution of the ZrCh templating media is also shown (dashed line).
  • Figures 9a, 9b, and 9c show the electrochemical performance of a cell comprising inventive graphitic sphere product particles.
  • the voltage curve, the corresponding differential capacity curve, and the cycling performance are shown respectively.
  • Figures 10a, 10b, and 10c show various SEM images of cross-sectioned graphitic sphere product particles.
  • Figure 10a shows a complete section of a product particle while Figures 10b and 10c show different portions of a product particle at greater magnification.
  • Figure lOd shows a cross section of a graphitic sphere product particle with its perimeter and centroid shown.
  • Figure lOe shows a plot of the residuals of the interpolated radial segment values and the interpolated f(x) values a function of x of the product particle.
  • Figures 11a and lib show SEM images at two different magnifications of the NMC precursor particles used in the Examples and which had been synthesized using an all -solid-state method.
  • Figures 12a and 12b show SEM images at two different magnifications of the product obtained after mechanofusing the mixture of NMC precursor particles and ZrCh templating media.
  • Figures 13a and 13b show SEM images at two different magnifications of the tetrahedral shaped NMC product particles in Figures 12a and 12b after separating them from the ZrCE templating media.
  • Figures 14a, 14b, and 14c show the XRD patterns patterns between 10° and 80° of the NMC precursor particles before mechanofusing, the tetrahedral shaped NMC product particles after mechanofusing and separation from the templating media, and the NMC product particles after annealing respectively.
  • Figure 15 shows the particle size distribution of the NMC product particles after annealing. For comparison, the particle size distribution of the ZrC templating media is also shown (dashed line).
  • Figures 16a and 16b show the electrochemical performance of a cell comprising inventive NMC product particles. In these Figures, the voltage curve and the cycling performance are shown respectively.
  • Figures 17a, 17b, 17c, and 17d show various SEM images of cross-sectioned NMC product particles.
  • Figure 17a shows a complete section of a product particle while Figures 17b, 17c and 17d show different portions of a product particle at several greater magnifications.
  • Figure 17e shows a cross section of a NMC product particle with its perimeter and centroid shown.
  • Figure 17f shows a plot of the residuals of the interpolated radial segment values and the interpolated f(x) values a function of x of the product particle.
  • Figure 18a and 18b show SEM images of comparative NMC particles after being subjected to lengthy auto-grinding.
  • Figure 19 illustrates the various dimensions involved in characterizing particle surface cavities from particle cross-sections or projected areas.
  • Figure 20a and 20b show SEM images of cross-sectioned core-shell product particles of Inventive Example 3.
  • Figure 21 shows a cross section image of a core-shell product particle of Inventive Example 3 with the position of five points indicated as Spectrum 1-5, at which compositions were obtained by EDS.
  • Figure 22 shows an XRD pattern of the shell precursor particles of Inventive Example 4.
  • Figure 23 an SEM image of the shell precursor particles of Inventive Example 4.
  • Figure 24 shows an XRD pattern of Intermediate A of Inventive Example 4.
  • Figure 25 shows an SEM image of Intermediate A of Inventive Example 4.
  • Figure 26 shows an SEM image of core precursor particles of Inventive Example 4.
  • Figure 27 shows an XRD pattern of the core precursor particles of Inventive Example 4.
  • Figures 28a and 28b show SEM images of cross-sectioned core-shell product particles of Inventive Example 4.
  • Figure 29 shows a cross section image of a core-shell product particle of Inventive Example 4 with the position of five points indicated as Spectrum 1-5 (from right to left), at which compositions were obtained by EDS.
  • Figure 30a shows SEM images of cross-sectioned core-shell product particles of Inventive Example 4.
  • Figure 30b shows the EDS elemental mapping of Ni of cross-sectioned core-shell product particles of Inventive Example 4.
  • Figure 31 shows an XRD pattern of the product particles of Inventive Example 4.
  • Figure 32 shows an XRD pattern of the heated product particles of Inventive Example 4.
  • Figure 33 shows SEM images of cross-sections of heated product particles of Inventive Example 4.
  • Figure 34 shows a cross section image of a core-shell product particle after heating of Inventive Example 4 with the position of five points indicated as Spectrum 1-5 (from left to right), at which compositions were obtained by EDS.
  • Figure 35 shows the variation in the transition metal composition as a function of the distance from the surface of a heated product particle of Inventive Example 4.
  • Figure 36 shows SEM images of cross sections of heated product particles of Inventive Example 5.
  • high shear and high pressure field refers to shear and pressure conditions similar to those experienced during typical mechanofiision processes.
  • the term “irregularly shaped” is intended to refer to both individual particles of irregular shape but also mixtures of otherwise regularly shaped particles with no shape in common.
  • Dn diameter at which n% of the sample’s mass has a smaller particle size.
  • average size of a group of particles is thus defined as its D50 diameter.
  • projected area diameter of a particle is the diameter of a circle with the same area as the projected image of the particle (i.e. its silhouette) or the particle's cross section, where the cross section passes near the particle's centroid.
  • cavity or “cavities” is used to refer to depressions on particle surfaces having both a relative depth in the range of 0.02 and 0.1 and a relative aspect greater than 0.2.
  • the methods for quantifying relative depth and relative aspect are provided under Material Characterization in the following Examples.
  • smooth refers to a particle whose roughness is less than 0.02.
  • centroid is used to refer to a particle whose surface does not vary in distance from the particle centroid by more than 25%.
  • pill refers to a plurality of particles or aggregated particles.
  • the term “about” should be construed as being in the range up to plus 10% and down to minus 10%.
  • anode refers to the electrode at which oxidation occurs when a metal-ion cell is discharged.
  • the anode is the electrode that is delithiated during discharge and lithiated during charge.
  • cathode refers to the electrode at which reduction occurs when a metal-ion is discharged.
  • the cathode is the electrode that is lithiated during discharge and delithiated during charge.
  • metal-ion cell or “metal-ion battery” refers to alkali metal ion cells, including lithium ion cells and sodium ion cells.
  • half-cell refers to a cell that has a working electrode and a metal counter/reference electrode.
  • a lithium half-cell has a working electrode and a lithium metal counter/reference electrode.
  • active material refers to a material that can reversibly store metal ions in an anode or cathode.
  • anode active material or “anode material” refer to an active material that is used to reversibly store metal ions in an anode.
  • anode materials are lithiated during charge and delithiated during discharge at potentials less than 2 V vs. Li.
  • anode materials are delithiated during charge and lithiated during discharge at potentials less than 2 V vs. Li.
  • cathode active material or “cathode material” refer to an active material that is used to reversibly store metal ions in a cathode.
  • cathode materials are lithiated during discharge and delithiated during charge at potentials greater than 2 V vs. Li.
  • cathode materials are delithiated during charge and lithiated during discharge at potentials greater than 2 V vs. Li.
  • cross-section is understood to refer to a cross-section that passes near a particle's centroid.
  • average crystallite size refers to the grain size of a phase as determined by the Scherrer crystallite size determination method as described in more detail below. (Note that in principle the average crystallite size can be determined not only by X-ray diffraction techniques but also from SEM images. In the former, known as the Scherrer grain size determination method, the Scherrer equation is applied to the x-ray diffraction peak FWHM of any one of a phase's x-ray powder diffraction peaks between 20° and 60° 2-theta under incident Cu-Ka ⁇ radiation. A description of the Scherrer equation may be found in "X-ray Diffraction" by B.E. Warren, Dover Publications (1990). In the latter, average crystallite size is determined from the average of the crystallite sizes of a random sampling of crystallites observed by scanning electron microscopy.)
  • 03 phase refers to a phase having a a-NaFe0 2 type structure, as described in C. Delmas, C. Fouassier, and P. Hagenmuller, Physica, 99B (1980) 81-85.
  • L1C0O2 which is used extensively as an active positive electrode material in commercial Li-ion batteries has an 03 structure.
  • X-ray diffraction may be used to determine the structure of phases in a sample, including if a material comprises a phase having the 03 structure or a phase having the graphite structure.
  • MF mechanofusion
  • the product particles may be separated from the templating media by air classification, sieving, cyclone, elutriation, sedimentation, hydrocyclone or other wet or dry methods that are known to separate particles based on size, shape or density.
  • Figure 1 schematically shows a suitable MF system 1 for preparing particulate according to the method of the invention. It consists of rotating cylindrical chamber 2 in which fixed rounded press- head 3 and fixed scraper 4 are placed.
  • the radius of press-head 3 is smaller than that of chamber 2 and the clearance space between press-head 3 and chamber wall 5 generally ranges from 1 to 5 mm.
  • the clearance between scraper 4 and chamber wall 5 is smaller, usually around 0.5 mm.
  • these clearances are adjustable for optimization, depending on factors such as the chamber size, particle size, powder hardness, and so on.
  • MF system 1 Operation of MF system 1 is simple, but the mechanism by which powder is processed within the chamber is complex (see W. Chen, R. N. Dave, R. Pfeffer and O. Walton, Powder Technol, 2004, 146, 121-136).
  • powder mixture 6 (comprising suitable amounts of precursor particles and templating media) is placed into the chamber and chamber 2 is sealed.
  • powder mixture 6 is forced to chamber wall 5 by centrifugal action. This also forces the powder mixture to pass through the converging space between fixed press-head 3 and rotating chamber wall 5, establishing a high-shear and high pressure field. As the powder particles come out of the diverging space of the press-head region, they adhere to each other and to the chamber wall.
  • Scraper 4 serves to scrape off the powder attached to chamber wall 5.
  • the sheared powder mixture is then re -dispersed into the chamber and moves towards the press-head region again.
  • the powder continuously undergoes this process of compression, frictional shearing, and de -agglomeration while chamber 2 is rotating.
  • appropriate operating parameters for the MF system can be expected to vary according to the product particles desired and on the types and amounts of the precursor particles and templating media employed. It is expected that those of ordinary skill will readily be able to determine appropriate operating parameters for a given situation based on guidance provided in the Examples below.
  • the method of the invention may be used to aggregate a variety of types of precursor particles into larger, uniform product particles.
  • an amount of any precursor particles having an average particle size less than 1000 pm may be aggregrated.
  • precursor particles larger than the templating media may be employed.
  • Such particles can be ground to smaller size in-situ during the processing.
  • the method is particularly suitable for making product particles whose average size is less than 100 pm and even smaller (e.g. less than 50 pm or even less than 10 pm).
  • powders for use in battery electrodes may be aggregated via the inventive method.
  • Such precursor powders include both anode active and cathode active materials such as carbonaceous powders (e.g. graphite flakes) or conventional mixed metal oxide powders (e.g. NMC or LiNiiaMniaCoi ⁇ CE) powder.
  • Suitable precursor powders also include unconventionally prepared mixed metal oxide powders, such as those prepared using a novel all -solid-state method in which an appropriate mixture of metal oxide raw material powders is ball milled to produce the mixed metal oxide precursor particles.
  • a useful feature of the inventive method is that no special shape or particle size distribution is required of the starting precursor particles in order to obtain desirable end product.
  • the precursor particles may have a regular shape or alternatively be irregularly shaped powders and may have narrow, broad or multimodal size distributions.
  • the microgranulation method of the invention generally involves preparing a mixture of the chosen amount of precursor particles with an appropriate amount of templating media.
  • the templating media generally has an average particle size less than 500 pm and is selected so as to have a hardness greater than that of the precursor particles. In this way, the templating media is not broken up itself under the high shear and pressure conditions involved in the method. Suitable material choices for the templating media include zirconium oxide, tungsten carbide, tungsten, silicon oxide, aluminum oxide, silicon nitride, hardened steel, stainless steel, and agate. Further, the templating media is preferably regular, smooth, and spherical in shape because it otherwise would be more likely to break down, and particularly to break down into spheres anyway, during processing and thereby contaminate the end product.
  • the size, uniformity, and amount of the templating media employed can also be important with regards to the characteristics of the desired end product particulate. It is expected for the aggregate end product particles to be somewhat smaller but of order of the size of the templating media used. Thus, for smaller aggregates, it can be desirable for the average particle size of the templating media to be less than 100 pm. Further, it is expected that the uniformity of the end product particulate would roughly be analogous to that of the templating media used.
  • the size distribution of the templating media can be sufficiently uniform such that its (D90-D10)/D50 ⁇ 2, preferably (D90-D10)/D50 ⁇ 1, more preferably (D90-D10)/D50 ⁇ 0.7 or its (D90-D10)/D50 is even smaller.
  • a sufficient amount of templating media should be employed in the method in order to fully and successfully process all the precursor particles present.
  • the bulk volume of the amount of templating media is desirably greater than that of the bulk volume of the amount of precursor particles.
  • the relevant amounts in the mixture are preferably chosen such that the volume of precursor particles can fit into the void volume existing between randomly packed templating media spheres (which is about 1/3 of the bulk volume of the spheres).
  • a 1:3 bulk volume ratio of small precursor particles to templating media can be preferred (i.e. the bulk volume of the amount of templating media is preferably greater than or about three times that of the bulk volume of the amount of precursor particles).
  • the microgranulation processing itself involves subjecting the appropriate mixture comprising the amounts of precursor particles and templating media to mechanofusion or other equivalent high shear and high pressure fields. This step serves to aggregate the precursor particles into the product particles.
  • Mechanofusing can, for instance, be performed in the mechanofusion system of Figure 1. Representative settings for processing include gaps of about 0.5 mm between the scraper and the rotating wall and of about 1.4 mm between the press-head and the rotating wall. Representative rotation speeds are of order of 1000 rpm and higher, which result in wall surface speeds of about 8 m/s or higher. Mechanofusion processing times of greater than or about 12 hours have been shown to be sufficient. Less processing time may be achieved when different sample volumes, rotation speeds, powder ratios are used or if the templating media is recycled.
  • the precursor particles and template particles are in a vacuum or a fluid environment, typically a gas atmosphere.
  • the gas atmosphere is air.
  • the gas atmosphere may be an inert gas, such as argon or nitrogen.
  • the gas atmosphere may be reducing and may comprise hydrogen or ammonia, for instance a mixture of 5 % hydrogen gas and 95% nitrogen gas.
  • the gas atmosphere may be oxidizing and may comprise an oxidizing gas, such as oxygen or carbon dioxide.
  • mechanofusion system shown in Figure 1 and discussed above is used to prepare product particles in a batch process
  • preparation may be done continuously instead.
  • particles may be continuously drawn from the mechanofusion machine in a particle stream.
  • the desired product particles may then be separated from the particle stream by a continuous classification process and collected.
  • the remaining unprocessed precursor particles and templating media in the particle stream may then be returned to the mechanofusion machine.
  • Additional precursor particles may also be continuously added to the mechanofusion machine to replace the product particles removed by classification. In this way product particles may be continuously produced and collected.
  • the product particles are then separated from the templating media. This may be accomplished in a variety of conventional ways. For instance, if the product particles and templating media are sufficiently uniform yet different in size, adequate separation can simply be achieved by sieving. Alternatively, if the product particles and templating media are sufficiently different in density, density separation techniques may be employed (e.g. as demonstrated in the Examples in which dense, ZrCL microspheres were used as templating media and then readily separated from significantly less dense product particles using a density separation technique). Methods of separating the product particles from the templating media include air classification, sieving, cyclone, elutriation, sedimentation, hydrocyclone or other wet or dry methods that are known to separate particles based on size, shape or density.
  • the synthesis of precursor particles may include a step that reduces average particle size, for example by grinding, including ball milling or classifying. In some embodiments, the synthesis of precursor particles may include a step that reduces crystallite size, including ball milling. In some embodiments, the synthesis of precursor particles may include a step that increases crystallite size, including a heating step or a classifying step. In some embodiments, the synthesis of precursor particles may include a step of reacting more than one constituent together, including co -precipitation, heating, ball milling or other known methods. In some embodiments, the synthesis of precursor particles may include a step of combining particles with different average crystallite sizes and different compositions together.
  • applying the above microgranulation methods to template particles and precursor particles comprising a mixture of precursor particles having different crystallite sizes results in product particles having on average larger precursor particle crystallites near the product particle core and smaller precursor particle crystallites near the product particle surface.
  • product particles result in which the product particle core has a composition that more closely resembles the composition of the precursor particles with the larger crystallite size and the product particle surface has a composition that more closely resembles the composition of the precursor particles with the smaller crystallite size.
  • product particles having continuously varying composition can be made by applying the above methods to mixtures of template particles and precursor particles, the precursor particles comprising mixtures of precursor particle powders having different compositions and average crystallite sizes, such that the composition of the product particles varies from their surface to the core according to the order of increasing average crystallite size of each precursor particle powder.
  • the precursor particles may also comprise particles with different compositions, so that composite product particles comprising an aggregated mixture of precursor particles with different compositions are produced.
  • composite product particles may be heated so that the constituent precursor particles react with each other.
  • Product particles can be prepared in this manner whose average size is between 10 and 100 pm. Further, the product particles can be very uniform in size with narrow particle size distributions similar to that of the templating media employed. For instance, the size distribution of the product particles can be uniform such that (D90-D10)/D50 ⁇ 2, (D90-D10)/D50 ⁇ 1, (D90-D10)/D50 ⁇ 0.7 or even smaller. Further still, the product particles can desirably be smooth and formed into regular, rounded shapes such as spheres and rounded tetrahedrons. The product particles may further contain no features having both a relative depth in the range of 0.1 and 0.2 and a relative aspect greater than 0.2.
  • electrodes and electrochemical devices employing product particles may be prepared in numerous manners known to those in the art. For instance, there are numerous optional designs and methods for making electrodes for rechargeable lithium ion batteries as well as for making the batteries themselves and these have been documented extensively in the art.
  • Mechanofusing methods have been found to be effective in preparing uniform rounded aggregate in this manner, whereas other conventional granulation methods such as auto-grinding and ball milling process do not.
  • the precursor particles initially coat the templating media.
  • the precursor particles adhere poorly to the templating media. Therefore after a certain thickness is reached, the layer of precursor particles spalls off the templating media. This results in the formation of intermediate particles of relatively uniform volume. These intermediate particles are then spheronized to form the product particles.
  • This process therefore relies on the ability of the mechanofusion process to form dense coatings on particles. This is only possible in the high shear and high compression fields present during the mechanofusion process. Other processes, such as grinding, milling, and high shear mixing, were found not to have this property and therefore did not produce equivalent product particles.
  • graphite particulate can be prepared which comprises graphite particles shaped as spheres or ovoids and which comprise concentric nested spheres or ovoids of graphene layers. These graphene layers are randomly positioned on the surface of the concentric nested spheres or ovoids, except that the graphene layers are oriented such that their basal planes are tangential to the concentric nested spheres or ovoids.
  • the graphite particles further can have an average particle size greater than 2 pm and an average doo2 spacing of less than 3.400 A.
  • the graphite particles in the particulate comprise concentric layers of porosity with a void or hollow near its core.
  • the graphite particles have an average particle size between 5 pm and 50 pm and a size distribution of (D90- D10)/D50 ⁇ 2.
  • the aforementioned graphite particulate and also highly graphitic onion graphites are expected to be advantageous for use as an active negative electrode material in Li-ion batteries. It is well known that the basal planes of graphite are sites of high reactivity with Li-ion battery electrolyte. Therefore, natural graphites are typically spheronized to reduce the surface area of basal planes in contact with the electrolyte, as discussed in M. Yoshio et al., J. Mater. Chem. 14 (3005) 1754-1758. However, conventional spheronization methods result in the graphite planes to be curled in a spiral, with the same arrangement as a jellyroll or as described by M.
  • the spherical natural graphite particles look like clenched fists.
  • the graphite layers in conventionally spheronized natural graphite particles are arranged concentrically around a central axis (i.e. nested concentric cylinders) rather than concentrically around a point, as in the case of onion graphite (i.e. nested concentric spheres or ovoids).
  • the arrangement of the graphite basal planes in spherical natural graphite reduces the amount of graphite basal planes exposed to the electrolyte, graphite basal planes remain exposed at either end of the "jellyroll".
  • spherical natural graphites are typically carbon coated, as described by M. Yoshio et al.
  • the microstructure of onion graphite has no basal planes exposed to the electrolyte and is therefore expected to have improved performance as a negative electrode material in a Li-ion battery.
  • Onion graphite is also expected to be superior to the type of graphite spheres found in cast irons, which are known to have a microstructure in which the graphite basal planes are arranged concentrically, however the planes radiate from a central core (e.g. as shown in Figure 6-4 of "Mesomolecules: From Molecules to Materials" SEARCH Series, Volume 1, G.
  • the electrolyte is expected to have access to the graphite basal planes along radial lines separating the basal planes extending from the particle core to surface.
  • the size of the onion graphite should be greater than 5 pm or more advantageously between 10 pm and 50 pm in size.
  • the onion graphite should have a high level of graphitization, which is known to improve reversible capacity and reduce cell polarization.
  • a measure of the level of graphitization is the doo2 spacing of graphite, as measured by x-ray diffraction, where the lower the value of the doo2 spacing, the greater the degree of graphitization.
  • a preferred level of graphitization is indicated by a doo2 spacing of less than 3.400 A or more preferably less than 3.360 A or even more preferably less than 3.350 A.
  • lithium mixed metal oxide particulate can be prepared which comprises particles having a core of lithium nickel manganese cobalt oxide crystallites that are randomly oriented and have an average size of about 1 pm coated with smaller randomly oriented lithium nickel manganese cobalt oxide crystallites that have an average size of about 0.3 pm.
  • lithium mixed metal oxide product particles are in the form of smooth tetrahedra.
  • lithium transition metal oxide particulate can be prepared which comprises particles having at least two transition metals present from the group consisting of Mn, Ni, and Co. These particles have an 03 structure, an average particle size ranging from 1 to 50 pm, and they comprise crystallites that vary randomly in shape and size throughout their interior. In certain embodiments, the crystallites have an average size greater than 0.5 pm and the average particle size of the particles is more than 5 times larger than the average crystallite size. In certain embodiments, the composition of one of the two transition metals can vary from the core of the particles to the shell of the particles by at least 5 atomic %.
  • Exemplary particulates were prepared using mechanofusion to aggregate precursor particles in accordance with the invention. Other particulates were also prepared for comparison purposes. Various characteristics of these particulates were determined and presented below. In addition, electrodes and electrochemical cells were prepared using some of these particulates. The cell performance results obtained from the electrochemical cells are also presented below.
  • microgranulation was accomplished using an AM-15F Mechanofusion System (Hosokawa Micron Corporation, Osaka, Japan) schematically as depicted in Figure 1.
  • This equipment was modified by replacing the standard stainless steel chamber, scraper, and press head with identical hardened steel parts to reduce wear.
  • the chamber had a 15 cm inner diameter.
  • mechanofusion was conducted at high rpm with a 0.5 mm scraper/wall gap and a 1.4 mm press-head/wall gap. Samples were collected after a given process time from several different areas in the chamber. Unless otherwise indicated, the gas atmosphere used during mechanofusion processing was air.
  • Material characterization Particle size distributions of particulate samples were obtained using a Horiba Partica LA-950V2 laser scattering particle size distribution analyzer.
  • X-ray diffraction (XRD) patterns were collected using a Rigaku Ultima IV diffractometer equipped with a Cu Ka X-ray source, a diffracted beam graphite monochromator and a scintillation detector.
  • Average crystallite sizes of different phases were determined by applying the Scherrer equation to the largest XRD peak of the phase in question, unless otherwise specified.
  • SEM and cross-sectional SEM were used to study sample morphology.
  • a TESCAN MIRA 3 LMU Variable Pressure Schottky Field Emission Scanning Electron Microscope (SEM) was used.
  • Cross-sections of sample were prepared with a JEOL Cross-Polisher (JEOL Ltd., Tokyo, Japan) which sections samples by shooting argon ions at them.
  • the relative depth and relative aspect of depressions on particle surfaces are measured from particle cross-sections or projected areas (i.e. silhouettes) as follows.
  • a line AB is made above a depression on the particle surface with both ends tangent to the particle surface.
  • the longest distance as measured perpendicularly from line AB to the particle surface (line GC) is referred to as the feature depth, d.
  • Two lines are drawn from the point C such that they contact the surface contact line AB and have the largest acute angle possible between them without passing into the particle volume (lines EC and CF in Figure a).
  • the relative depth of the particle is defined as d/D, where D is the projected area diameter.
  • the relative aspect is defined as ⁇ (EC+FC)/EF-1 ⁇ .
  • Surface cavities are those features having both relative depths in the range of 0.02 and 0.1 and relative aspects greater than 0.2.
  • a spline variation method is used to determine particle roughness.
  • the particle roughness is determined by quantifying the variation in the radius of the surface as measured from the centroid.
  • a scanning electron microscope (SEM) digital image of a cross-section or silhouette of the desired particle is obtained having a minimum image resolution such that at least 1000 image pixels reside on the perimeter of the particle.
  • the centroid of this outlined silhouette is found.
  • the distances from each point on the outlined silhouette to the centroid, "radial segment values" are measured.
  • the radial segment values are then plotted as a function of angle around the centroid between 0° and 360, and this plot is fit to a smoothing spline function -f- A j / ⁇ x ⁇ * dx where x, is the angle value, Yi are the radial segment values, ftx) is the cubic smoothing spline function (as described on pg. 17 of P.J. Green, Bernard. W. Silverman, Nonparametric Regression and Generalized Linear Models: A roughness penalty approach, copyright 1994 by P.J. Green and B.W. Silverman, CTC Press reprint 2000), and l is the smoothing parameter which is greater than or equal to zero in general but in this case is fixed to be 999.
  • the number of radial segment values is then reduced to 1000 by linear interpolation, such that each interpolated radial segment value associated with a particular angle x is calculated as the average of the maximum number of unique radial segment values that are closest that angle.
  • the number of f(x) values also reduced to 1000 by linear interpolation in the same way, such that for each interpolated radial segment value there is an interpolated f(x) value at the same value of x.
  • the coefficient of variation is then determined as the standard deviation divided by the mean radius of the interpolated radial segment values and the interpolated f(x) values a function of x.
  • the coefficient of variation is identified with the surface roughness, having a value is always greater than or equal to zero (i.e. zero being the roughness of a perfect circle). The larger the coefficient of variation, the rougher the particle.
  • Sample electrodes for laboratory testing were prepared from slurries prepared by mixing the prepared particulate, carbon black (Super C65, Imerys Graphite and Carbon) and lithium polyacrylate (LiPAA, the LiPAA was provided in a 10 weight% aqueous solution, made by neutralizing a polyacrylic acid solution (Sigma-Aldrich, average molecular weight ⁇ 250,000 g/mole, 35 wt% in FLO) with LiOH LO (Sigma Aldrich, 98%) in distilled water) in an active particle/carbon black/LiPAA volumetric ratio of 70/5/25 in distilled water, where volumes are determined based on bulk densities.
  • a polyacrylic acid solution Sigma-Aldrich, average molecular weight ⁇ 250,000 g/mole, 35 wt% in FLO
  • LiOH LO Sigma Aldrich, 98%) in distilled water
  • ZrCri Zirconium oxide
  • Figures 2a and 2b show SEM images of the ZrCh templating media at two different magnifications.
  • Figure 2c shows a cross section of a ZrCh particle with its perimeter and centroid shown.
  • Figure 2d shows a plot of the residuals of the interpolated radial segment values and the interpolated f(x) values a function of x. From this data the roughness was determined.
  • the ZrCh templating media is smooth, having a roughness of only 0.0022, and has no cavities.
  • Natural graphite flakes (230U, Asbury Graphite Mills Inc.) were used as graphite precursor particles.
  • Figures 4a and 4b show SEM images of these precursor particles at two different magnifications. As is evident from these images, the graphite flakes are irregularly shaped particles with a layered structure and the size of the particles differs dramatically. Many of the particles have jagged surface features, which are large cavities.
  • a mixture comprising ⁇ 225g of ZrCE microsphere templating media and ⁇ 25g of graphite precursor particles ( ⁇ 50 mL total powder volume) was prepared and then subjected to the high shear and high pressure field provided by the aforementioned mechanofusion system. The system was run at 1500 rpm (12 m/s wall speed) for 12 hours.
  • Figures 5a and 5b show SEM images at two different magnifications of the product obtained after this mechanofusing. In these images, the ZrCh microspheres are seen to be partially coated with a thin layer of graphite. Also evident are graphite spheres (the product particles) which have a slightly smaller diameter than the ZrCE microspheres.
  • the graphite sphere product particles were then separated from the ZrCE microspheres by density using diiodomethane (MI-GEE, GEO Liquids, Inc., Prospect Heights, IL), which has a density of 3.32 g/cm 3 (between that of Zr0 2 at 5.68 g/cm 3 and graphite at 2.23 g/cm 3 ).
  • Figures 6a and 6b show SEM images at two different magnifications of the graphite sphere product particles after separating with diiodomethane and drying. Almost all the Zr0 2 was removed and thus most of the remaining particles were graphite spheres. XRD patterns of the graphite were obtained before and after the mechanofusion process.
  • Figure 8 shows the particle size distribution of the graphite sphere product particles after annealing. For comparison, the particle size distribution of the ZrC templating media is also shown (dashed line). The graphite sphere product particles are seen to be very uniform in size with an average diameter of about 41 pm.
  • Electrodes were prepared using these graphite sphere product particles as anode active material and a lithium half-cell comprising such an electrode was made and tested. Cells were cycled between 0.005 V and 0.9 V. For the first cycle, cells were cycled at C/10 and at the lower potential, cells were held at constant potential until the current reduced to a value of C/20 prior to starting the next cycle. For subsequent cycles, cells were cycled at C/5 and held at each lower potential limit until the current was reduced to C/10 prior to starting the next cycle.
  • Figures 9a, 9b, and 9c show the electrochemical performance of this cell. In these Figures, the voltage curve, the corresponding differential capacity curve, and the cycling performance are shown respectively. The voltage curve is typical for graphite and the expected staging can be clearly observed in the differential capacity curve. A reversible capacity of -275 mAh/g is obtained with good cycling performance.
  • Figures 10a, 10b, and 10c show several of the SEM images obtained.
  • Figure 10a shows a complete section of a product particle while Figures 10b and 10c show different portions of a product particle at greater magnification.
  • Some of the product particles comprise a void space near the center of the particle (i.e. hollow core).
  • porosity arranged in concentric layers is observed throughout the particles.
  • the product particles thus appear to be characterized with a novel concentric structure.
  • the product particles comprise concentric layers of graphene sheets.
  • Figure lOd shows a cross section of a product particle with its perimeter and centroid shown.
  • Figure lOe shows a plot of the residuals of the interpolated radial segment values and the interpolated f(x) values a function of x of the product particle. From this data the roughness was determined.
  • the graphite product particles are smooth, having a roughness of only 0.0052, and have no cavities.
  • Zirconium oxide (ZrCh) microspheres similar to the preceding Example were used as templating media to aggregate submicron irregularly shaped precursor NMC particles into larger regularly shaped NMC product particles.
  • NMC precursor particles with the formula LiNiiaMniaCoi ⁇ CE were prepared using an all -solid-state method. Specifically, stoichiometric amounts of NiO (Sigma-Aldrich, 99%), MnO (Aldrich, 99%), C03O4 (Alfa Aesar, 99.7%), and L12CO3 (Alfa Aesar, 99%) with 10% excess L12CO3 were mixed together by high energy ball milling using a SPEX8000 mixer. A sample size of ⁇ 2.4 g was milled with 180 g of 1.6 mm stainless steel balls (Thomson Linear Motion) for 4 hours.
  • NiO Sigma-Aldrich, 99%
  • MnO Aldrich, 99%
  • C03O4 Alfa Aesar, 99.7%
  • L12CO3 Alfa Aesar, 99%
  • FIG. 12a and 12b show SEM images at two different magnifications of the product obtained after this mechanofiising. In these images, the ZrCh microspheres are seen to be partially coated with a thin layer of NMC. Also evident are NMC tetrahedra (the product particles) which are of slightly smaller size than the ZrCh microspheres, but much larger than the NMC precursor particles.
  • FIGS. 13a and 13b show SEM images at two different magnifications of the tetrahedral shaped NMC product particles after separating in this manner.
  • the product particles are smooth. Again, almost all the ZrCh was removed.
  • XRD patterns of the NMC product particles were obtained before and after the mechanofusion process. Again, it appeared that the mechanofusion process disrupted the crystal structure of the product particles somewhat and caused a loss of some crystallinity. This was evidenced by broadened peaks and amorphous features in the XRD patterns. The pattern also indicated the presence of a small amount of ZrCh impurity left in the sample.
  • NMC product particles were thus recrystallized by annealing at 900 °C in air.
  • a subsequent XRD pattern was obtained of the annealed product particles and all the peaks are now sharp, indicating good crystallinity.
  • a small amount of ZrCh was still present in the XRD pattern.
  • Figures 14a, 14b, and 14c show these various XRD patterns, namely of the NMC precursor particles before mechanofusing, the tetrahedral shaped NMC product particles after mechanofusing and separation from the templating media, and the NMC product particles after annealing respectively.
  • Figure 15 shows the particle size distribution of the NMC product particles after annealing.
  • the particle size distribution of the ZrC templating media is also shown (dashed line).
  • Electrodes were prepared using these NMC product particles as cathode active material and a lithium half-cell comprising such an electrode was made and tested. Cells were cycled at C/10 between 3.0 V and 4.2 V for the first cycle. For the rest of the cycles, cells were cycled at C/4 and held at the upper cut-off potential until the current reduced to C/10 prior to the next cycle.
  • Figures 16a and 16b show the electrochemical performance of this cell. In these Figures, the voltage curve and the cycling performance are shown respectively. The voltage curve is typical for NMC and a reversible capacity of ⁇ 90 mAh/g is obtained.
  • Figures 17a, 17b, 17c, and 17d show several of the SEM images obtained.
  • Figure 17a shows a complete section of a product particle while Figures 17b, 17c and 17d show different portions of a product particle at several greater magnifications.
  • the product particles are smooth and are seen to be tetrahedral in shape with rounded comers. They comprise a core of crystallites that are randomly oriented and have an average size of about 1 pm coated with smaller randomly oriented crystallites that have an average size of about 0.3 pm.
  • the aggregated NMC product particles thus appear to be characterized with a novel structure.
  • Figure 17e shows a cross section of a product particle with its perimeter and centroid shown.
  • Figure 17f shows a plot of the residuals of the interpolated radial segment values and the interpolated fix) values a function of x of the product particle. From this data the roughness was determined.
  • the NMC product particles are smooth, having a roughness of only 0.0094, and have no cavities. using an auto-respray
  • ZrCE Zirconium oxide
  • NMC precursor particles similar to the preceding Example were used.
  • a mixture comprising the same ratio of ZrCE and NMC was mixed in a Brinkmann Retsch auto-grinder.
  • the auto-grinder was set to run at -120 rpm for two weeks.
  • Figure 18a and 18b show the SEM images obtained for this sample subjected to auto-grinding.
  • the SEM images show that all the ZrCE microspheres are loosely coated with NMC but almost no granulation of NMC can be observed.
  • This comparative example shows that very lengthy auto-grinding does not provide the unique benefits of the mechanofusion process.
  • Example 3 microgranulation of a mixture of having different compositions and different average crystallite sizes.
  • ZrCE Zirconium oxide
  • a mixture comprising -180 g of ZrCE microsphere templating media, 6.94 g NiO (Sigma-Aldrich, 99%), 2.20 g MnO (Aldrich, 99%), 2.48 g C0 3 CE (Alfa Aesar, 99.7%), and 6.29 g LECCE (Alfa Aesar, 99%) was prepared.
  • the average crystallite size of the C0 3 CE was 0.3 pm and the average crystallite size of the NiO was 2 pm, as determined by observation of single crystalline crystallites by SEM.
  • the mixture was then subjected to mechanofusion as described above at 1000 rpm ( ⁇ 8 m/s wall speed) for 18 hours.
  • Figures 20a and 20b show SEM images at two different magnifications of cross sections of product particles.
  • the product particles are smooth with most of particles having a diameter of 5-10 pm.
  • the particles can be seen to have a core-shell structure.
  • the brightness is different for the particle core and for the particle shell, indicating a different elemental composition for the core and the shell.
  • Figure 21 shows a cross section image of a particle with the position of five data points indicated, labelled as Spectrum 1-5.
  • the elemental composition at each point, as determined by EDS is listed in Table 1 below.
  • the core is rich in Co, while the shell is rich in Mn and Ni.
  • a target composition of LiNiiaMniaCowC ⁇ (NMC111) was chosen as the Mn-rich particle shell.
  • Shell precursor powder was made by sealing 12.88 g NiO (Sigma-Aldrich, 99%), 12.24 g MnO (Aldrich, 99%), 13.85 g C03O4 (Alfa Aesar, 99.7%), 21.03 g L12CO3 (Alfa Aesar, 99%), corresponding to 10% excess L12CO3 according to the formula LiNiiaMniaCowC ⁇ and 10 kg of 0.5 inch stainless steel balls in a 5 L stainless-steel jar mill (US Stoneware) and milling for one week at 85 rpm.
  • An XRD pattern of the resulting shell precursor powder is shown in Figure 22. It comprises a mixture of L12CO3, C03O4, NiO, and MnO phases.
  • An SEM image of the resulting shell precursor powder is shown in Figure 23. It comprises crystallites that are less than 0.1 pm in size.
  • a target composition of LiNi0 . 6Mn0 . 2Co0 . 2O2 was chosen as the Ni-rich particle core.
  • Core precursor powder was made by sealing in air 41.61 g NiO (Sigma-Aldrich, 99%), 13.18 g MnO (Aldrich, 99%), 14.90 g C03O4 (Alfa Aesar, 99.7%), and 10 kg of 0.5 inch stainless steel balls in a 5 L stainless-steel jar mill (US Stoneware) and milling for one week at 85 rpm (denoted as Intermediate A).
  • Figure 24 shows an XRD pattern of Intermediate A, which corresponds to a single -phase rocksalt structure.
  • An SEM image of Intermediate A is shown in Figure 25.
  • Intermediate A consists of crystallites that are less than 0.1 pm in size.
  • 15 g of Intermediate A was mixed with 7.83 g of L12CO3 (Alfa Aesar, 99%), corresponding to 5% excess L12CO3 according to the formula LiNi 0.6 Mn 0.2 Co 0.2 O 2 , until a homogeneous mixture was obtained ( ⁇ 10 minutes).
  • the mixture was placed in an alumina crucible and heated in a box furnace in air for 3 hours at 900 °C, resulting in core precursor particles.
  • the purpose of this heating step is to increase the crystallite size of the core precursor particles such that they are more than 10% larger than the shell precursor particle crystallite size.
  • Figure 26 shows an SEM image of the resulting core precursor particles.
  • Figure 27 shows an XRD pattern of the core precursor particles, which corresponds to phase pure 03 -phase NMC622.
  • a mixture comprising -180 g of ZrC microsphere templating media, 13.33 g shell precursor particles, and 6.67 g core precursor particles was prepared. The mixture was then subjected to mechanofusion as described above at 1000 rpm ( ⁇ 8 m/s wall speed) for 20 hours. The product particles were then separated from the ZrCh microspheres using a 400 mesh sieve.
  • Figure 28a and 28b shows SEM images at two different magnifications of cross sections of product particles. Most of the product particles having a diameter of 5-20 pm. In cross section, the particles can be seen to have a core-shell structure. The brightness is different for the particle core and for the particle shell, indicating a different elemental composition for the core and the shell.
  • the core consists of randomly oriented crystallites that have the same average crystallite size as the core precursor particles and the shell consists of randomly oriented crystallites having the same average crystallite size as the shell precursor particles. Both core and shell contain porosity.
  • Figure 29 shows a cross section SEM image of a product particle with the position of five data points indicated, labelled as Spectrum 1-5. The elemental composition at each point, as determined by EDS is listed in Table 2 below.
  • the core is about 13% richer in Ni than the shell.
  • Figure 30a shows a cross section image of a product particle and Figure 30b shows an EDS Ni- mapping of the same product particle.
  • the intensity of the Ni signal from the core is stronger than the signal from the shell, confirming that the product particle consist a Ni-rich core and the shell is rich in Co and Mn.
  • Figure 31 shows an XRD pattern of the product particles. The XRD pattern corresponds to that of a mixture of product particles and core particles.
  • FIG. 32 shows an XRD pattern of the heated product particles.
  • Figure 33 shows SEM images of cross-sections of heated product particles. The size of the heated product particles was the same as the product particles before heating. The heated product particles contain randomly oriented crystallites that are also randomly shaped, having an average size of 2 pm. Some of the heated product particles contained voids, while others did not.
  • Figure 34 shows a cross section image of a heated product particle with the position of six data points indicated, labelled as Spectrum 1-6.
  • the elemental composition at each point, as determined by EDS is listed in Table 3 below.
  • the diffusion of transition metals during the high temperature heating process results in a concentration gradient, where the Ni content gradually increases from the shell to the core and the Mn content increases from the core to the shell.
  • the variation in the transition metal composition as a function of the distance from the heated product particle surface as determined from Spectrum 1 to Spectrum 6 in Figure 34 is shown in Figure 35.
  • the Ni concentration near the core is about 9% larger than in the shell.
  • Inventive Example 5 microgranulation of graphite flakes
  • Graphite product particles were made using the same method as Inventive Example 1, excepting the product particles were separated from the ZrCE templating media by passing the product particle/templating media mixture through a 38 pm sieve after mechanofusion processing. The product particles were then heated to 2840°C under argon gas for 90 minutes, producing graphite spheres. The annealed product particle spheres had the same shape and average particle size as those in Inventive Example 1, but less porosity, presumably because diiodomethane was not used during processing. It is believed that diiodomethane might intercalate between the graphite layers, producing concentric porosity and void spaces during heating.
  • Figure 36 shows SEM cross-section images of some annealed product particles of Inventive Example 5. Some of the annealed product particles contained little or no porosity, some contained concentric porosity and some contained central void spaces. All of the annealed product particles contained layers of graphite arranged concentrically in nested ovoid or spherical shells and with the basal plane edges not radiating from a central point to the outside of the particles.
  • the resulting product particles were separated from the ZrCE spheres using a 400 mesh sieve.
  • the resulting product particles had a nodular shape, but were rounded and smooth and having an average diameter of 20 pm.
  • the preceding examples demonstrate that mechanofusion can be used to simply and efficiently aggregate various precursor particles into larger product particles.
  • the product particles are uniform and may desirably be smooth and either spherical or rounded in shape.
  • the method can produce particulate with novel structures.
  • the invention can be used to manufacture particulate suitable for electrode materials in lithium batteries.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Battery Electrode And Active Subsutance (AREA)
  • Inorganic Compounds Of Heavy Metals (AREA)
  • Glanulating (AREA)
  • Carbon And Carbon Compounds (AREA)
  • Pigments, Carbon Blacks, Or Wood Stains (AREA)
PCT/US2020/043621 2019-08-29 2020-07-24 Improved microgranulation methods and product particles therefrom Ceased WO2021040932A1 (en)

Priority Applications (11)

Application Number Priority Date Filing Date Title
CN202080060756.9A CN114341061B (zh) 2019-08-29 2020-07-24 改进的微造粒方法及其制得的产品粒子
US17/638,646 US12434978B2 (en) 2019-08-29 2020-07-24 Microgranulation methods and product particles therefrom
CN202511790134.2A CN121651451A (zh) 2019-08-29 2020-07-24 改进的微造粒方法及其制得的产品粒子
CA3146930A CA3146930A1 (en) 2019-08-29 2020-07-24 Improved microgranulation methods and product particles therefrom
EP20757437.7A EP4021855B1 (en) 2019-08-29 2020-07-24 Improved microgranulation methods and product particles therefrom
PL20757437.7T PL4021855T3 (pl) 2019-08-29 2020-07-24 Ulepszone sposoby mikrogranulacji i uzyskiwane nimi cząstki produktowe
JP2022510172A JP2022546264A (ja) 2019-08-29 2020-07-24 改善されたミクロ粒状化法及びその製品粒子
KR1020227009567A KR20220054822A (ko) 2019-08-29 2020-07-24 개선된 미세과립화 방법 및 이로부터의 생성물 입자
JP2025038649A JP2025105606A (ja) 2019-08-29 2025-03-11 改善されたミクロ粒状化法及びその製品粒子
US19/261,930 US20250369147A1 (en) 2019-08-29 2025-07-07 Microgranulation methods and product particles therefrom
US19/309,288 US20250376387A1 (en) 2019-08-29 2025-08-25 Microgranulation methods and product particles therefrom

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US201962893787P 2019-08-29 2019-08-29
US62/893,787 2019-08-29
US201962946938P 2019-12-11 2019-12-11
US62/946,938 2019-12-11
US202063020526P 2020-05-05 2020-05-05
US63/020,526 2020-05-05

Related Child Applications (3)

Application Number Title Priority Date Filing Date
US17/638,646 A-371-Of-International US12434978B2 (en) 2019-08-29 2020-07-24 Microgranulation methods and product particles therefrom
US19/261,930 Continuation US20250369147A1 (en) 2019-08-29 2025-07-07 Microgranulation methods and product particles therefrom
US19/309,288 Division US20250376387A1 (en) 2019-08-29 2025-08-25 Microgranulation methods and product particles therefrom

Publications (1)

Publication Number Publication Date
WO2021040932A1 true WO2021040932A1 (en) 2021-03-04

Family

ID=72087174

Family Applications (3)

Application Number Title Priority Date Filing Date
PCT/US2020/043621 Ceased WO2021040932A1 (en) 2019-08-29 2020-07-24 Improved microgranulation methods and product particles therefrom
PCT/US2020/043599 Ceased WO2021040931A1 (en) 2019-08-29 2020-07-24 Lithium transition metal oxide and precursor particulates and methods
PCT/US2020/047597 Ceased WO2021041296A1 (en) 2019-08-29 2020-08-24 Lithium transition metal oxide and precursor particulates and methods

Family Applications After (2)

Application Number Title Priority Date Filing Date
PCT/US2020/043599 Ceased WO2021040931A1 (en) 2019-08-29 2020-07-24 Lithium transition metal oxide and precursor particulates and methods
PCT/US2020/047597 Ceased WO2021041296A1 (en) 2019-08-29 2020-08-24 Lithium transition metal oxide and precursor particulates and methods

Country Status (9)

Country Link
US (5) US12434978B2 (https=)
EP (2) EP4021855B1 (https=)
JP (3) JP2022546264A (https=)
KR (2) KR20220054822A (https=)
CN (3) CN121651451A (https=)
CA (2) CA3146930A1 (https=)
HU (1) HUE073378T2 (https=)
PL (1) PL4021855T3 (https=)
WO (3) WO2021040932A1 (https=)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022200766A1 (en) * 2021-03-24 2022-09-29 Ev Metals Uk Limited Process for producing an electrochemically active oxide material
WO2023106734A1 (ko) * 2021-12-06 2023-06-15 오씨아이 주식회사 이차전지용 음극재 및 그 제조 방법
WO2023121089A1 (ko) * 2021-12-22 2023-06-29 오씨아이 주식회사 이차전지용 음극재 및 그 제조 방법
US12378132B2 (en) 2019-08-29 2025-08-05 Novonix Battery Technology Solutions Inc. Lithium transition metal oxide and precursor particulates and methods
WO2026075874A1 (en) 2024-10-03 2026-04-09 Novonix Battery Technology Solutions Inc. Recycling of used cathode materials

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP4095102A1 (en) * 2021-05-28 2022-11-30 Basf Se Process for making a particulate electrode active material, and electrode active material
CN114146643B (zh) * 2021-12-23 2023-09-15 成都瑞德琅科技有限公司 一种粉末涂料加工装置
CA3251808A1 (en) * 2022-05-20 2025-07-09 Lg Chem, Ltd. Positive electrode active material precursor, method for preparing positive electrode active material using same, and positive electrode active material
CN119585208A (zh) 2022-05-27 2025-03-07 诺沃尼克斯电池技术解决方案公司 用于制备锂镍锰钴氧化物颗粒的方法
CN119894829A (zh) 2022-08-19 2025-04-25 诺沃尼克斯电池技术解决方案公司 从元素金属原料制备锂过渡金属氧化物的方法及其产物
JP2025536429A (ja) * 2022-11-07 2025-11-05 ノヴォニクス・バッテリー・テクノロジー・ソリューションズ・インコーポレイテッド 遊離粒子及び電気化学セルにおける使用のための作製方法
JP7707217B2 (ja) * 2023-01-20 2025-07-14 プライムプラネットエナジー＆ソリューションズ株式会社 正極用ｎｃｍ系活物質、正極および電池
JP7704785B2 (ja) * 2023-01-20 2025-07-08 プライムプラネットエナジー＆ソリューションズ株式会社 正極用ｎｃｍ系活物質、正極および電池
KR102684130B1 (ko) * 2023-08-03 2024-07-11 권호진 전이금속 전구체의 사용이 배제된 신규 공정을 통한 고성능 리튬 이차전지용 양극 활물질의 제조 방법과 이를 이용한 리튬 이차전지
WO2025211064A1 (ja) * 2024-04-05 2025-10-09 株式会社村田製作所 正極活物質、正極、および固体電池

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130189178A1 (en) 2011-06-06 2013-07-25 Shinko Seiki Company, Limited Method of Manufacturing Onion-like Carbon
US9132482B2 (en) 2010-12-10 2015-09-15 Commissariat A L'energie Atomique Et Aux Energies Alternatives Method for the dry granulation of nanometric particles
US9142832B2 (en) 2010-08-11 2015-09-22 Jx Nippon Oil & Energy Corporation Graphite material for negative electrodes of lithium ion secondary battery, manufacturing method for said material, and lithium ion secondary battery using same
CN105861961A (zh) * 2016-04-12 2016-08-17 苏州赛福德备贸易有限公司 碳纳米管增强铝合金及其制备方法
CN106328887A (zh) * 2015-06-19 2017-01-11 宁德时代新能源科技股份有限公司 锂离子电池阳极材料及其制备方法
US20170050182A1 (en) * 2009-01-29 2017-02-23 Basf Corporation Mechanically fused materials for pollution abatement in mobile and stationary sources
CN106531980A (zh) * 2015-11-17 2017-03-22 宁波杉杉新材料科技有限公司 一种锂离子电池负极材料及其制备方法和应用
CN107785560A (zh) * 2017-11-15 2018-03-09 国联汽车动力电池研究院有限责任公司 一种高性能硅碳负极材料及其制备方法
CN108172826A (zh) * 2017-12-30 2018-06-15 国联汽车动力电池研究院有限责任公司 一种磷酸铁锂纳米颗粒包覆高镍三元材料的方法

Family Cites Families (79)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE69010045T2 (de) 1989-03-30 1995-01-26 Matsushita Electric Ind Co Ltd Sekundärzelle mit nichtwässerigem Elektrolyten.
JP2001163700A (ja) 1999-12-08 2001-06-19 Tohoku Techno Arch Co Ltd リチウム系複合金属酸化物およびその製造方法
US7468223B2 (en) 2000-06-22 2008-12-23 Uchicago Argonne, Llc Lithium metal oxide electrodes for lithium cells and batteries
CN1287474C (zh) 2001-03-22 2006-11-29 松下电器产业株式会社 正极活性物质及含该活性物质的非水电解质二次电池
US20030108793A1 (en) 2001-08-07 2003-06-12 3M Innovative Properties Company Cathode compositions for lithium ion batteries
JP4301875B2 (ja) 2003-06-30 2009-07-22 三菱化学株式会社 リチウム二次電池正極材料用リチウムニッケルマンガンコバルト系複合酸化物及びそれを用いたリチウム二次電池用正極、並びにリチウム二次電池
US7211237B2 (en) 2003-11-26 2007-05-01 3M Innovative Properties Company Solid state synthesis of lithium ion battery cathode material
DE602005023607D1 (de) 2004-05-17 2010-10-28 Osmose Inc Holzbehandlung mit injizierbarer holzkonservierungsmittelsuspension mit bioziden partikeln
JP2005336004A (ja) 2004-05-26 2005-12-08 Mitsubishi Chemicals Corp ニッケルマンガンコバルト系複合酸化物、層状リチウムニッケルマンガンコバルト系複合酸化物及びリチウム二次電池正極材料とそれを用いたリチウム二次電池用正極、並びにリチウム二次電池
JP2006127923A (ja) * 2004-10-29 2006-05-18 Shin Kobe Electric Mach Co Ltd リチウム二次電池用の正極活物質及びリチウム二次電池
JP2007184145A (ja) 2006-01-06 2007-07-19 Hitachi Vehicle Energy Ltd リチウム二次電池
JP2007317585A (ja) 2006-05-29 2007-12-06 Hitachi Vehicle Energy Ltd リチウム二次電池用正極活物質及びこれを用いたリチウム二次電池
JP4788579B2 (ja) 2006-11-30 2011-10-05 東ソー株式会社 リチウム−ニッケル−マンガン複合酸化物、及びその製造方法、並びにその用途
US9608266B2 (en) 2007-01-29 2017-03-28 Umicore Cathode material for lithium-ion rechargeable batteries
CN100497180C (zh) 2007-04-25 2009-06-10 北京理工大学 一种纳米晶锂钛复合氧化物的制备方法
US8088699B2 (en) 2008-02-13 2012-01-03 Saint-Gobain Centre De Recherches Et D'etudes Europeen BSAS powder
CN102171865A (zh) 2008-12-24 2011-08-31 日本碍子株式会社 锂二次电池的正极活性物质用的板状粒子以及锂二次电池
CN102239588B (zh) 2008-12-24 2014-09-24 日本碍子株式会社 正极活性物质用板状粒子或膜、其制造方法及锂二次电池
US8287772B2 (en) 2009-05-14 2012-10-16 3M Innovative Properties Company Low energy milling method, low crystallinity alloy, and negative electrode composition
EP2355214B1 (fr) 2010-01-28 2013-12-25 Prayon Accumulateurs au lithium à base de phosphate de fer lithié et de carbone
PL2399869T3 (pl) * 2010-06-25 2015-11-30 Evonik Degussa Gmbh Proszek tlenku mieszanego zawierający pierwiastki lit, mangan, nikiel i kobalt i sposoby otrzymywania
CN101916843A (zh) 2010-08-02 2010-12-15 中国科学院宁波材料技术与工程研究所 一种锂离子电池正极材料锂过渡金属复合氧化物的制备方法
US8557438B2 (en) * 2010-08-25 2013-10-15 Uchicago Argonne, Llc Electrode materials for rechargeable battery
JP5880928B2 (ja) 2011-03-14 2016-03-09 国立研究開発法人産業技術総合研究所 リチウムマンガンチタンニッケル複合酸化物及びその製造方法、並びにそれを部材として使用したリチウム二次電池
WO2012163660A1 (en) * 2011-05-30 2012-12-06 Umicore Positive electrode material having a size dependent composition
CN102683669B (zh) 2011-12-19 2016-03-30 中国科学院宁波材料技术与工程研究所 锂离子电池正极材料及其制备方法
CN102569780B (zh) 2012-02-28 2014-04-09 南京航空航天大学 锂离子电池层状结构正极材料的制备方法
KR101443359B1 (ko) 2012-07-20 2014-09-23 주식회사 포스코이에스엠 니켈 함량이 높은 리튬-니켈-코발트-망간계 복합 산화물의 제조 방법, 이에 의하여 제조된 니켈 함량이 높은 리튬-니켈-코발트-망간계 복합 산화물, 및 이를 포함하는 리튬 이차 전지
CN102881874B (zh) 2012-10-15 2015-02-18 福建师范大学 一种通过还原过程制备富锂固溶体正极材料的方法
CN103855372B (zh) 2012-11-29 2017-02-22 国联汽车动力电池研究院有限责任公司 一种高锰复合正极材料及其制备方法
JP6007867B2 (ja) 2013-06-20 2016-10-12 信越化学工業株式会社 非水電解質二次電池活物質用粉砕助剤及び粉砕方法
CN103682287B (zh) * 2013-12-19 2016-09-14 深圳市贝特瑞新能源材料股份有限公司 一种锂离子电池硅基复合负极材料、制备方法及电池
CN104201366B (zh) * 2014-01-10 2017-01-04 兰州金里能源科技有限公司 一种高安全性高压实密度镍钴锰酸锂ncm523三元材料的制备方法
CN103811744B (zh) * 2014-02-13 2016-09-21 北大先行科技产业有限公司 一种锂离子电池三元正极材料的制备方法
ES2927109T3 (es) 2014-05-27 2022-11-02 Jiangsu Hengtron Nanotech Co Ltd Materiales de cátodo de óxido de litio y metal mejorados y método para fabricarlos
TWI633062B (zh) 2014-06-12 2018-08-21 烏明克公司 用於可充電電池的鋰過渡金屬氧化物陰極材料之先質
JP6471025B2 (ja) 2014-06-27 2019-02-13 住友化学株式会社 リチウム含有複合酸化物およびその製造方法
EP3204972B1 (en) * 2014-10-08 2021-05-12 Umicore Carbonate precursors for lithium nickel manganese cobalt oxide cathode material and the method of making same
KR102591083B1 (ko) * 2014-12-23 2023-10-18 퀀텀스케이프 배터리, 인코포레이티드 리튬이 풍부한 니켈 망간 코발트 산화물
EP3248232B1 (en) 2015-01-23 2019-07-03 Umicore Lithium nickel-manganese-cobalt oxide cathode powders for high voltage lithium-ion batteries
CN104953199B (zh) 2015-05-13 2018-03-13 中国科学院过程工程研究所 利用锂离子电池正极废料合成的金属掺杂镍钴锰酸锂及其制备方法和用途
CN105345012B (zh) 2015-07-20 2017-11-03 昆明贵金属研究所 一种高导电性片状银粉的制备方法及应用
US10651467B2 (en) 2015-08-27 2020-05-12 Haldor Topsøe A/S High tap density lithium positive electrode active material, intermediate and process of preparation
KR20200021564A (ko) 2015-09-08 2020-02-28 유미코아 충전식 배터리용 Li 전이 금속 산화물 캐소드의 제조를 위한 전구체 및 방법
CN107482172B (zh) 2016-06-07 2021-02-09 江苏当升材料科技有限公司 一种高倍率型层状富锂锰基正极材料及其制备方法
EP3447108B1 (en) 2016-08-11 2020-07-15 Avantama AG Luminescent crystals and manufacturing thereof
JP2018063777A (ja) * 2016-10-11 2018-04-19 株式会社東芝 活物質、非水電解質電池、電池パック及び車両
US10892488B2 (en) * 2017-01-17 2021-01-12 Samsung Electronics Co., Ltd. Electrode active material, lithium secondary battery containing the electrode active material, and method of preparing the electrode active material
CN106654227B (zh) 2017-01-18 2019-07-26 新乡天力锂能股份有限公司 一种镍钴锰酸锂正极材料的制备方法
CN107910526A (zh) 2017-11-15 2018-04-13 何本科 一种高倍率高安全性镍钴锰酸锂三元材料的制备方法
WO2019117282A1 (ja) 2017-12-15 2019-06-20 株式会社Ｇｓユアサ 非水電解質二次電池用正極活物質、非水電解質二次電池用正極活物質の製造方法、非水電解質二次電池用正極、及び非水電解質二次電池
PL3728129T3 (pl) 2017-12-22 2022-01-17 Umicore Materiał elektrody dodatniej do akumulatorów litowo-jonowych
CN108172836B (zh) 2017-12-29 2020-03-24 山东华夏神舟新材料有限公司 聚偏氟乙烯改性复合导电粘结剂的制备方法
CN112004779B (zh) 2018-03-29 2023-02-07 尤米科尔公司 用于制备可再充电锂离子蓄电池的正极材料的方法
US11316157B1 (en) 2018-05-26 2022-04-26 Ge Solartech, LLC Methods for the production of cathode materials for lithium ion batteries
CN108682840B (zh) * 2018-06-08 2021-06-15 四川大学 纳米(Mg0.2Co0.2Ni0.2Cu0.2Zn0.2)O的制备方法及应用
CN109279659B (zh) 2018-08-22 2021-04-27 中伟新材料股份有限公司 一种单晶三元正极材料制备方法
KR102771682B1 (ko) 2018-10-26 2025-02-25 주식회사 엘지에너지솔루션 이차전지용 양극 활물질, 그 제조방법 및 이를 포함하는 리튬 이차전지
CN109802133B (zh) 2019-01-16 2021-09-21 宁德新能源科技有限公司 钴酸锂前驱体及其制备方法与由该钴酸锂前驱体所制备的钴酸锂复合物
CN109888207B (zh) 2019-01-25 2022-05-17 高点(深圳)科技有限公司 高镍低游离锂的锂离子三元正极材料及其制法和应用
CN110336007A (zh) 2019-07-08 2019-10-15 苏州拉瓦锂能源科技有限公司 一种单晶型电池材料及其制备方法
WO2021040932A1 (en) 2019-08-29 2021-03-04 Novonix Battery Testing Services Inc. Improved microgranulation methods and product particles therefrom
CN110581272B (zh) 2019-09-30 2022-05-10 昆明云大新能源有限公司 一种高性能锂离子电池三元正极材料及其制备方法
EP4030505A4 (en) 2019-10-23 2022-11-30 Lg Chem, Ltd. Cathode active material, and cathode and lithium secondary battery which comprise same
CN110776021B (zh) 2019-11-27 2022-05-13 桑顿新能源科技有限公司 镍钴锰酸锂正极材料及其制备方法、锂离子电池正极浆料、锂离子电池正极和锂离子电池
GB201918699D0 (en) 2019-12-18 2020-01-29 Johnson Matthey Plc Process
US20210359300A1 (en) 2020-05-14 2021-11-18 Nano One Materials Corp. Alternative Method for Making Lithium Battery Cathode Materials
CN111661880B (zh) 2020-06-16 2022-08-09 中国科学院宁波材料技术与工程研究所 一种正极材料及其制备方法
GB202012628D0 (en) 2020-08-13 2020-09-30 Johnson Matthey Plc Cathode materials
US12381213B2 (en) 2020-09-21 2025-08-05 Lg Chem, Ltd. Positive electrode active material by solid phase synthesis and method for manufacturing the same
CN112614991A (zh) 2020-12-15 2021-04-06 广东邦普循环科技有限公司 一种高镍三元正极材料及其制备方法和应用
EP4095102A1 (en) 2021-05-28 2022-11-30 Basf Se Process for making a particulate electrode active material, and electrode active material
CN113782715A (zh) 2021-08-12 2021-12-10 西安交通大学 一种磷酸锂改性高镍系镍钴锰酸锂正极材料制备方法及其应用
EP4441823A1 (en) 2021-12-03 2024-10-09 Sylvatex, Inc. Method for the manufacture of cathode materials
CN114388758B (zh) 2022-01-06 2023-12-19 中国科学院宁波材料技术与工程研究所 一种具有新型复合相结构的锂金属氧化物正极材料及其制备方法和应用
CN119585208A (zh) 2022-05-27 2025-03-07 诺沃尼克斯电池技术解决方案公司 用于制备锂镍锰钴氧化物颗粒的方法
CN119894829A (zh) 2022-08-19 2025-04-25 诺沃尼克斯电池技术解决方案公司 从元素金属原料制备锂过渡金属氧化物的方法及其产物
CN115557544A (zh) 2022-10-28 2023-01-03 安徽格派新能源有限公司 一种高容量镍锰酸锂的制备方法
CN116417592A (zh) 2023-03-29 2023-07-11 宜春国轩电池有限公司 一种疏水复合镍钴锰酸锂材料及其制备方法

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20170050182A1 (en) * 2009-01-29 2017-02-23 Basf Corporation Mechanically fused materials for pollution abatement in mobile and stationary sources
US9142832B2 (en) 2010-08-11 2015-09-22 Jx Nippon Oil & Energy Corporation Graphite material for negative electrodes of lithium ion secondary battery, manufacturing method for said material, and lithium ion secondary battery using same
US9132482B2 (en) 2010-12-10 2015-09-15 Commissariat A L'energie Atomique Et Aux Energies Alternatives Method for the dry granulation of nanometric particles
US20130189178A1 (en) 2011-06-06 2013-07-25 Shinko Seiki Company, Limited Method of Manufacturing Onion-like Carbon
CN106328887A (zh) * 2015-06-19 2017-01-11 宁德时代新能源科技股份有限公司 锂离子电池阳极材料及其制备方法
CN106531980A (zh) * 2015-11-17 2017-03-22 宁波杉杉新材料科技有限公司 一种锂离子电池负极材料及其制备方法和应用
CN105861961A (zh) * 2016-04-12 2016-08-17 苏州赛福德备贸易有限公司 碳纳米管增强铝合金及其制备方法
CN107785560A (zh) * 2017-11-15 2018-03-09 国联汽车动力电池研究院有限责任公司 一种高性能硅碳负极材料及其制备方法
CN108172826A (zh) * 2017-12-30 2018-06-15 国联汽车动力电池研究院有限责任公司 一种磷酸铁锂纳米颗粒包覆高镍三元材料的方法

Non-Patent Citations (15)

* Cited by examiner, † Cited by third party
Title
"SEARCH Series", vol. 1, 1995, CHAPMAN & HALL, article "Mesomolecules: From Molecules to Materials"
B.E. WARREN: "X-ray Diffraction", 1990, DOVER PUBLICATIONS
C. DELMASC. FOUASSIERP. HAGENMULLER, PHYSICA, vol. 99B, 1980, pages 81 - 85
C.-S. CHOUC.-H. TSOUC.-I. WANG, ADV. POWDER TECHNOL., vol. 19, 2008, pages 383 - 396
M. ALONSOM. SATOHK. MIYANAMI, POWDER TECHNOL., vol. 59, 1989, pages 45 - 52
M. NAITOA. KONDOT. YOKOYAMA, ISIJLNT., vol. 33, 1993, pages 915 - 924
M. NAITOM. YOSHIKAWAT. TANAKAA. KONDO, KONA POWDER PART. J., vol. 11, 1993, pages 229 - 234
M. YOSHIO ET AL., J. MATER. CHEM., vol. 14, no. 3005, pages 1754 - 1758
M. YOSHIO ET AL., THE SPHERICAL NATURAL GRAPHITE PARTICLES LOOK LIKE CLENCHED FISTS
N. PRODUCT AND M. FEATURES, vol. 17, 1999, pages 244 - 250
P.J. GREENBERNARD. W. SILVERMAN: "Nonparametric Regression and Generalized Linear Models: A roughness penalty approach", 1994, CTC PRESS, pages: 17
R. PFEFFERR. N. DAVED. WEIM. RAMLAKHAN, POWDER TECHNOL., vol. 117, 2001, pages 40 - 67
T. YOKOYANIAK. URAYAMAT. YOKOYAMA, KONA POWDER PART. J., vol. 1, 1983, pages 53 - 63
V.D. BLANKB.A. KULNITSKIYI.A. PEREZHOGIN, SCRIPTA MATERIALIA, vol. 60, 2009, pages 407 - 410
W. CHENR. N. DAVER. PFEFFERO. WALTON, POWDER TECHNOL., vol. 146, 2004, pages 121 - 136

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US12378132B2 (en) 2019-08-29 2025-08-05 Novonix Battery Technology Solutions Inc. Lithium transition metal oxide and precursor particulates and methods
US12434978B2 (en) 2019-08-29 2025-10-07 Novonix Battery Technology Solutions Inc. Microgranulation methods and product particles therefrom
WO2022200766A1 (en) * 2021-03-24 2022-09-29 Ev Metals Uk Limited Process for producing an electrochemically active oxide material
WO2023106734A1 (ko) * 2021-12-06 2023-06-15 오씨아이 주식회사 이차전지용 음극재 및 그 제조 방법
WO2023121089A1 (ko) * 2021-12-22 2023-06-29 오씨아이 주식회사 이차전지용 음극재 및 그 제조 방법
WO2026075874A1 (en) 2024-10-03 2026-04-09 Novonix Battery Technology Solutions Inc. Recycling of used cathode materials

Also Published As

Publication number Publication date
EP4021855C0 (en) 2025-10-15
EP4021854B9 (en) 2025-12-24
WO2021040931A1 (en) 2021-03-04
EP4021854C0 (en) 2025-09-17
JP7504195B2 (ja) 2024-06-21
KR20220054816A (ko) 2022-05-03
US20250368527A1 (en) 2025-12-04
CN114341061A (zh) 2022-04-12
CN114341061B (zh) 2025-12-19
US20250369147A1 (en) 2025-12-04
US20220298023A1 (en) 2022-09-22
KR20220054822A (ko) 2022-05-03
CA3146934A1 (en) 2021-03-04
JP2025105606A (ja) 2025-07-10
EP4021854B1 (en) 2025-09-17
CN121651451A (zh) 2026-03-13
CN114302862A (zh) 2022-04-08
HUE073378T2 (hu) 2026-01-28
EP4021855A1 (en) 2022-07-06
EP4021854A1 (en) 2022-07-06
JP2022546934A (ja) 2022-11-10
JP2022546264A (ja) 2022-11-04
US20250376387A1 (en) 2025-12-11
US20220336805A1 (en) 2022-10-20
US12378132B2 (en) 2025-08-05
EP4021855B1 (en) 2025-10-15
US12434978B2 (en) 2025-10-07
CA3146930A1 (en) 2021-03-04
WO2021041296A1 (en) 2021-03-04
PL4021855T3 (pl) 2026-01-19

Similar Documents

Publication Publication Date Title
US20250376387A1 (en) Microgranulation methods and product particles therefrom
TWI323524B (https=)
KR101842823B1 (ko) 니켈 복합 수산화물과 그의 제조 방법, 비수계 전해질 이차 전지용 정극 활물질과 그의 제조 방법, 및 비수계 전해질 이차 전지
US20120256337A1 (en) Cathode active material precursor particle, method for producing thereof and method for producing cathode active material for lithium secondary battery
US20120258369A1 (en) Lithium secondary battery and cathode active material therefor
US20120258365A1 (en) Cathode active material precursor particle, cathode active material particle for lithium secondary battery and lithium secondary battery
JP5162388B2 (ja) リチウムイオン二次電池に適したリチウム含有複合酸化物の製造方法。
US20100196761A1 (en) Granular powder of transition metal compound as raw material for cathode active material for lithium secondary battery, and method for its production
JP4299065B2 (ja) リチウム二次電池用正極材およびその製造方法
Cao et al. Mechanofusion-derived Si-alloy/graphite composite electrode materials for Li-ion batteries
JP2004220897A (ja) リチウム二次電池用正極活物質粉末
JP7520006B2 (ja) 充電式電池のアノード用の電気化学的活性分散物及び複合材料
JP6808959B2 (ja) リチウムイオン二次電池用複合活物質およびその製造方法
EP4184614A1 (en) Positive electrode active material for lithium ion secondary battery, and lithium ion secondary battery in which same is used
Ren et al. Preparation-microstructure-performance relationship of Li-rich transition metal oxides microspheres as cathode materials for lithium ion batteries
JP7532880B2 (ja) リチウムイオン二次電池用正極活物質、及びその製造方法、並びにリチウムイオン二次電池
KR100752058B1 (ko) 비수계 리튬이온전지용 음극 활물질
EP4616457A2 (en) Free particles and methods for making for use in electrochemical cells
CA3069168A1 (en) Polycrystalline particulates for rechargeable battery electrodes
JP2024145933A (ja) ナトリウムイオン二次電池
JP2012051744A (ja) スピネル型リチウム・マンガン系複合酸化物およびその製造方法ならびに用途

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 3146930

Country of ref document: CA

ENP Entry into the national phase

Ref document number: 2022510172

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20227009567

Country of ref document: KR

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2020757437

Country of ref document: EP

Effective date: 20220329

WWE Wipo information: entry into national phase

Ref document number: 523441363

Country of ref document: SA

WWE Wipo information: entry into national phase

Ref document number: 522431795

Country of ref document: SA

WWG Wipo information: grant in national office

Ref document number: 17638646

Country of ref document: US

WWG Wipo information: grant in national office

Ref document number: 2020757437

Country of ref document: EP

WWR Wipo information: refused in national office

Ref document number: 522431795

Country of ref document: SA

WWE Wipo information: entry into national phase

Ref document number: 523441363

Country of ref document: SA