WO2020178944A1 - Dispositif de bobine et procédé de fabrication - Google Patents
Dispositif de bobine et procédé de fabrication Download PDFInfo
- Publication number
- WO2020178944A1 WO2020178944A1 PCT/JP2019/008387 JP2019008387W WO2020178944A1 WO 2020178944 A1 WO2020178944 A1 WO 2020178944A1 JP 2019008387 W JP2019008387 W JP 2019008387W WO 2020178944 A1 WO2020178944 A1 WO 2020178944A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coil
- adhesive layer
- coil device
- support
- manufacturing
- Prior art date
Abstract
Priority Applications (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2020536702A JP6774699B1 (ja) | 2019-03-04 | 2019-03-04 | コイル装置及び製造方法 |
KR1020207029119A KR102389151B1 (ko) | 2019-03-04 | 2019-03-04 | 코일 장치 및 제조 방법 |
CN202210651017.8A CN114999764A (zh) | 2019-03-04 | 2019-03-04 | 线圈装置及制造方法 |
CN201980024372.9A CN113474852B (zh) | 2019-03-04 | 2019-03-04 | 线圈装置及制造方法 |
PCT/JP2019/008387 WO2020178944A1 (fr) | 2019-03-04 | 2019-03-04 | Dispositif de bobine et procédé de fabrication |
TW109106701A TWI767195B (zh) | 2019-03-04 | 2020-03-02 | 線圈裝置及製造方法 |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/JP2019/008387 WO2020178944A1 (fr) | 2019-03-04 | 2019-03-04 | Dispositif de bobine et procédé de fabrication |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2020178944A1 true WO2020178944A1 (fr) | 2020-09-10 |
Family
ID=72338260
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2019/008387 WO2020178944A1 (fr) | 2019-03-04 | 2019-03-04 | Dispositif de bobine et procédé de fabrication |
Country Status (5)
Country | Link |
---|---|
JP (1) | JP6774699B1 (fr) |
KR (1) | KR102389151B1 (fr) |
CN (2) | CN113474852B (fr) |
TW (1) | TWI767195B (fr) |
WO (1) | WO2020178944A1 (fr) |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR20220042663A (ko) | 2020-09-28 | 2022-04-05 | 주식회사 엘지에너지솔루션 | 양극 스크랩을 이용한 활물질 재사용 방법 |
KR20220130891A (ko) | 2021-03-19 | 2022-09-27 | 스템코 주식회사 | 코일 기판과 그 제조 방법 및 상기 코일 기판을 구비하는 전자 장치 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH02152295A (ja) * | 1988-12-05 | 1990-06-12 | Asahi Chem Ind Co Ltd | 精細な回路 |
JPH11274694A (ja) * | 1998-03-18 | 1999-10-08 | Dainippon Printing Co Ltd | 転写用部材の製造法及び転写用部材 |
JP2005150536A (ja) * | 2003-11-18 | 2005-06-09 | Furukawa Electric Co Ltd:The | 線材固着材の製造方法 |
JP2010205905A (ja) * | 2009-03-03 | 2010-09-16 | Fuji Electric Systems Co Ltd | 磁気部品および磁気部品の製造方法 |
WO2014068614A1 (fr) * | 2012-10-30 | 2014-05-08 | 株式会社Leap | Procédé de production d'un élément bobine en utilisant un substrat en résine et en utilisant l'électroformage |
Family Cites Families (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5531639B1 (fr) * | 1970-01-26 | 1980-08-19 | ||
DE2506930C2 (de) | 1975-02-19 | 1987-01-29 | W. Schlafhorst & Co, 4050 Mönchengladbach | Verfahren und Vorrichtung zum Bilden einer Fadenreserve aus dem Fadenende einer Textilspule |
JPH06310832A (ja) * | 1993-04-22 | 1994-11-04 | Asahi Chem Ind Co Ltd | プリント配線板の製造方法 |
JPH08181415A (ja) * | 1994-12-27 | 1996-07-12 | Tokai Rubber Ind Ltd | 窓開き回路基板の製法 |
JP2000294443A (ja) | 1999-04-01 | 2000-10-20 | Tdk Corp | 薄膜デバイスの製造方法及び薄膜デバイス |
JP4191506B2 (ja) | 2003-02-21 | 2008-12-03 | Tdk株式会社 | 高密度インダクタおよびその製造方法 |
JP2006294891A (ja) | 2005-04-12 | 2006-10-26 | Tdk Corp | 電子部品の製造方法 |
JP6102578B2 (ja) * | 2012-09-27 | 2017-03-29 | Tdk株式会社 | 異方性めっき方法 |
JP2015041693A (ja) * | 2013-08-21 | 2015-03-02 | 日立化成株式会社 | 多層配線基板およびその製造方法ならびに積層コイル部品 |
US11083092B2 (en) * | 2015-03-13 | 2021-08-03 | Sumitomo Electric Printed Circuits, Inc. | Planar coil element and method for producing planar coil element |
TWI566309B (zh) * | 2016-01-08 | 2017-01-11 | 恆勁科技股份有限公司 | 封裝基板之製作方法 |
-
2019
- 2019-03-04 CN CN201980024372.9A patent/CN113474852B/zh active Active
- 2019-03-04 WO PCT/JP2019/008387 patent/WO2020178944A1/fr active Application Filing
- 2019-03-04 KR KR1020207029119A patent/KR102389151B1/ko active IP Right Grant
- 2019-03-04 CN CN202210651017.8A patent/CN114999764A/zh active Pending
- 2019-03-04 JP JP2020536702A patent/JP6774699B1/ja active Active
-
2020
- 2020-03-02 TW TW109106701A patent/TWI767195B/zh active
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH02152295A (ja) * | 1988-12-05 | 1990-06-12 | Asahi Chem Ind Co Ltd | 精細な回路 |
JPH11274694A (ja) * | 1998-03-18 | 1999-10-08 | Dainippon Printing Co Ltd | 転写用部材の製造法及び転写用部材 |
JP2005150536A (ja) * | 2003-11-18 | 2005-06-09 | Furukawa Electric Co Ltd:The | 線材固着材の製造方法 |
JP2010205905A (ja) * | 2009-03-03 | 2010-09-16 | Fuji Electric Systems Co Ltd | 磁気部品および磁気部品の製造方法 |
WO2014068614A1 (fr) * | 2012-10-30 | 2014-05-08 | 株式会社Leap | Procédé de production d'un élément bobine en utilisant un substrat en résine et en utilisant l'électroformage |
Also Published As
Publication number | Publication date |
---|---|
KR102389151B1 (ko) | 2022-04-20 |
TW202046351A (zh) | 2020-12-16 |
JP6774699B1 (ja) | 2020-10-28 |
TWI767195B (zh) | 2022-06-11 |
CN113474852A (zh) | 2021-10-01 |
CN113474852B (zh) | 2022-06-28 |
KR20200125730A (ko) | 2020-11-04 |
CN114999764A (zh) | 2022-09-02 |
JPWO2020178944A1 (ja) | 2021-03-11 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20090183901A1 (en) | Wiring Boards and Processes for Manufacturing the Same | |
US7487587B2 (en) | Methods of producing a composite substrate | |
JP6393619B2 (ja) | 多層プリント配線基板の製造方法及びベース基材 | |
WO2020178944A1 (fr) | Dispositif de bobine et procédé de fabrication | |
EP1675175A2 (fr) | Panneau à circuit | |
CN106463242A (zh) | 制造用于高频开关模式电源的微细加工的晶片级集成电感器或变压器的方法 | |
KR100952843B1 (ko) | 반도체 소자 테스트용 콘택터 및 그 제조방법 | |
JP5576546B2 (ja) | 配線基板の製造方法 | |
JP2017038044A (ja) | 配線基板及びその製造方法と電子部品装置 | |
US10440818B1 (en) | Flexible circuit board substrate and method of manufacturing the same | |
TW200913836A (en) | Method of forming solid blind vias through the dielectric coating on high density interconnect (HDI) substrate materials | |
KR20070047822A (ko) | 도전 리소그래픽 폴리머 및 이를 이용하여 소자를 만드는방법 | |
JP7498447B2 (ja) | コイル装置 | |
KR100970571B1 (ko) | 반도체 소자 테스트용 콘택터 및 그 제조방법 | |
JP3935558B2 (ja) | パターン形成方法 | |
JP2002368386A (ja) | 電着金属パターン転写用版およびこれを使用して作製した配線板 | |
JP2015109351A (ja) | 多層プリント配線基板の製造方法及びベース基材 | |
US9320142B2 (en) | Electrode structure | |
JPH08264941A (ja) | ビルドアップ多層プリント配線板及びその製造方法 | |
JP2004165321A (ja) | 配線基板およびその製造方法 | |
JPH07123178B2 (ja) | フレキシブル配線基板およびその製造方法 | |
JPH0495312A (ja) | 異方性導電膜 | |
JPH09260809A (ja) | プリント回路体及びその製造方法 | |
JP3953622B2 (ja) | 多層配線基板とその製造方法 | |
JPH0260233B2 (fr) |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
ENP | Entry into the national phase |
Ref document number: 2020536702 Country of ref document: JP Kind code of ref document: A |
|
ENP | Entry into the national phase |
Ref document number: 20207029119 Country of ref document: KR Kind code of ref document: A |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 19917547 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 19917547 Country of ref document: EP Kind code of ref document: A1 |