WO2018038160A1 - Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides, et élément d'affichage à cristaux liquides - Google Patents

Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides, et élément d'affichage à cristaux liquides Download PDF

Info

Publication number
WO2018038160A1
WO2018038160A1 PCT/JP2017/030130 JP2017030130W WO2018038160A1 WO 2018038160 A1 WO2018038160 A1 WO 2018038160A1 JP 2017030130 W JP2017030130 W JP 2017030130W WO 2018038160 A1 WO2018038160 A1 WO 2018038160A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid crystal
solvent
group
aligning agent
crystal aligning
Prior art date
Application number
PCT/JP2017/030130
Other languages
English (en)
Japanese (ja)
Inventor
大輝 山極
Original Assignee
日産化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日産化学工業株式会社 filed Critical 日産化学工業株式会社
Priority to CN201780051793.1A priority Critical patent/CN109643038B/zh
Priority to JP2018535735A priority patent/JP6974800B2/ja
Priority to KR1020197008452A priority patent/KR102430123B1/ko
Publication of WO2018038160A1 publication Critical patent/WO2018038160A1/fr

Abstract

Cet agent d'alignement de cristaux liquides est caractérisé en ce qu'il contient : au moins un type de polymère choisi dans le groupe constitué par les polyimides et les précurseurs de polyimide; et un solvant organique contenant des solvants spécifiés par le groupe (A) et le groupe (B). Groupe (A) : au moins un type de solvant choisi parmi la N-méthyl-2-pyrrolidone, la N-éthyl-2-pyrrolidone et la γ-butyrolactone. Groupe (B) : au moins un type de solvant choisi parmi la 4-méthoxy-4-méthyl-2-pentanone, la 4-hydroxy-2-butanone, et le 2-méthyl-2-hexanol.
PCT/JP2017/030130 2016-08-24 2017-08-23 Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides, et élément d'affichage à cristaux liquides WO2018038160A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN201780051793.1A CN109643038B (zh) 2016-08-24 2017-08-23 液晶取向剂、液晶取向膜和液晶表示元件
JP2018535735A JP6974800B2 (ja) 2016-08-24 2017-08-23 液晶配向剤、液晶配向膜及び液晶表示素子
KR1020197008452A KR102430123B1 (ko) 2016-08-24 2017-08-23 액정 배향제, 액정 배향막 및 액정 표시 소자

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016163463 2016-08-24
JP2016-163463 2016-08-24

Publications (1)

Publication Number Publication Date
WO2018038160A1 true WO2018038160A1 (fr) 2018-03-01

Family

ID=61245222

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/030130 WO2018038160A1 (fr) 2016-08-24 2017-08-23 Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides, et élément d'affichage à cristaux liquides

Country Status (5)

Country Link
JP (1) JP6974800B2 (fr)
KR (1) KR102430123B1 (fr)
CN (1) CN109643038B (fr)
TW (1) TWI735635B (fr)
WO (1) WO2018038160A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111566554A (zh) * 2018-03-07 2020-08-21 Jsr株式会社 液晶取向剂、液晶取向膜及液晶元件
WO2021106979A1 (fr) * 2019-11-26 2021-06-03 日産化学株式会社 Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102267591B1 (ko) * 2018-11-20 2021-06-18 주식회사 엘지화학 액정 배향제 조성물, 이를 이용한 액정 배향막의 제조 방법, 이를 이용한 액정 배향막 및 액정표시소자

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10338880A (ja) * 1997-06-09 1998-12-22 Jsr Corp 液晶配向剤
JP2001305549A (ja) * 2000-04-24 2001-10-31 Jsr Corp 液晶配向剤

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4156445B2 (ja) 2003-06-04 2008-09-24 株式会社 日立ディスプレイズ 液晶表示装置の製造方法
CN101405349A (zh) * 2006-03-20 2009-04-08 三菱化学株式会社 酞菁结晶、使用该酞菁结晶的电子照相感光体、电子照相感光体盒以及图像形成装置
JP4869892B2 (ja) 2006-12-06 2012-02-08 株式会社 日立ディスプレイズ 液晶表示装置
JP5532195B2 (ja) * 2008-06-10 2014-06-25 Ｊｓｒ株式会社 液晶配向剤および液晶表示素子
JP5553531B2 (ja) 2009-06-03 2014-07-16 株式会社ジャパンディスプレイ 液晶表示装置
KR101620675B1 (ko) * 2011-03-25 2016-05-12 가부시키가이샤 아이.에스.티 폴리이미드 전구체 용액, 폴리이미드 전구체, 폴리이미드 수지, 합제 슬러리, 전극, 합제 슬러리 제조 방법, 및 전극 형성 방법
KR20190095556A (ko) * 2012-09-19 2019-08-14 혼슈우 카가쿠고교 가부시키가이샤 폴리이미드 및 그의 성형체
KR102234876B1 (ko) * 2013-09-03 2021-03-31 닛산 가가쿠 가부시키가이샤 액정 배향 처리제, 액정 배향막 및 액정 표시 소자
WO2015053394A1 (fr) * 2013-10-10 2015-04-16 日産化学工業株式会社 Composition, agent de traitement pour l'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides
KR102437798B1 (ko) * 2014-09-25 2022-08-29 닛산 가가쿠 가부시키가이샤 액정 표시 소자

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10338880A (ja) * 1997-06-09 1998-12-22 Jsr Corp 液晶配向剤
JP2001305549A (ja) * 2000-04-24 2001-10-31 Jsr Corp 液晶配向剤

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111566554A (zh) * 2018-03-07 2020-08-21 Jsr株式会社 液晶取向剂、液晶取向膜及液晶元件
TWI800603B (zh) * 2018-03-07 2023-05-01 日商Ｊｓｒ股份有限公司 液晶配向劑、液晶配向膜、液晶元件及其製造方法
WO2021106979A1 (fr) * 2019-11-26 2021-06-03 日産化学株式会社 Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides

Also Published As

Publication number Publication date
JP6974800B2 (ja) 2021-12-01
TW201825658A (zh) 2018-07-16
TWI735635B (zh) 2021-08-11
JPWO2018038160A1 (ja) 2019-06-24
CN109643038A (zh) 2019-04-16
KR102430123B1 (ko) 2022-08-05
KR20190044642A (ko) 2019-04-30
CN109643038B (zh) 2022-01-25

Similar Documents

Publication Publication Date Title
JP5870487B2 (ja) 液晶配向剤、液晶配向膜及び液晶表示素子
JP5771948B2 (ja) 液晶配向剤、液晶配向膜、及び液晶表示素子
JP6187457B2 (ja) 光配向法用の液晶配向剤、液晶配向膜、及び液晶表示素子
JP6064900B2 (ja) 液晶配向剤、及びそれを用いた液晶配向膜
JP6372009B2 (ja) 液晶配向剤、液晶配向膜及び液晶表示素子
JP6202006B2 (ja) 液晶配向膜の製造方法、液晶配向膜、及び液晶表示素子
WO2012133829A1 (fr) Agent d'alignement de cristaux liquides et film d'alignement de cristaux liquides fabriqué avec ledit agent
JP6597645B2 (ja) 液晶配向剤
WO2020040089A1 (fr) Agent d'alignement de cristaux liquides et son procédé de production, film d'alignement de cristaux liquides, et élément d'affichage à cristaux liquides
JP7239872B2 (ja) 液晶配向剤、液晶配向膜、及び液晶表示素子
JP6974800B2 (ja) 液晶配向剤、液晶配向膜及び液晶表示素子
TWI839328B (zh) 聚合物及使用該聚合物之液晶配向劑
JP5630625B2 (ja) 液晶配向剤、液晶配向膜及び液晶表示素子
JP6460342B2 (ja) 液晶配向剤及びそれを用いた液晶表示素子
CN111263913B (zh) 液晶取向剂、液晶取向膜及液晶表示元件
WO2018051923A1 (fr) Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides
CN114479077B (zh) 一种聚酰胺酸酯及其在液晶取向剂、液晶取向膜和液晶单元中的应用
TWI744574B (zh) 液晶配向劑、液晶配向膜及液晶顯示元件
JP2018040979A (ja) 液晶配向膜の製造方法、液晶配向膜、及び液晶表示素子

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17843638

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2018535735

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20197008452

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 17843638

Country of ref document: EP

Kind code of ref document: A1