WO2017221802A1 - Composition d'encre pour éléments électroluminescents organiques, et procédé de production d'élément électroluminescent organique utilisant cette dernière - Google Patents

Composition d'encre pour éléments électroluminescents organiques, et procédé de production d'élément électroluminescent organique utilisant cette dernière Download PDF

Info

Publication number
WO2017221802A1
WO2017221802A1 PCT/JP2017/022077 JP2017022077W WO2017221802A1 WO 2017221802 A1 WO2017221802 A1 WO 2017221802A1 JP 2017022077 W JP2017022077 W JP 2017022077W WO 2017221802 A1 WO2017221802 A1 WO 2017221802A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
organic light
light emitting
solvent
ink composition
Prior art date
Application number
PCT/JP2017/022077
Other languages
English (en)
Japanese (ja)
Inventor
脇田全規
乙木栄志
Original Assignee
Dic株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dic株式会社 filed Critical Dic株式会社
Publication of WO2017221802A1 publication Critical patent/WO2017221802A1/fr

Abstract

Le but de la présente invention est de proposer une composition d'encre pour des éléments électroluminescents organiques, qui, lorsqu'un composé ayant un squelette de pyrène et/ou un composé ayant un squelette d'anthracène est utilisé en tant que matériau organique hôte, présente une excellente stabilité à la décharge de jet d'encre et qui est capable d'obtenir un rendement élevé d'émission. L'invention concerne une composition d'encre pour éléments électroluminescents organiques, qui comprend : un matériau hôte électroluminescent contenant un composé ayant un squelette de pyrène et/ou un composé ayant un squelette d'anthracène ; et un solvant ayant une pression de vapeur inférieure ou égale à 5 mm de Hg, la distance tridimensionnelle (Ra) représentée par la formule (a) étant inférieure ou égale à 8 (dans la formule, dDhôte, dPhôte et dHhôte représentent un terme de dispersion, un terme de polarisation et le terme de liaison hydrogène dans le paramètre de solubilité de Hansen du matériau hôte électroluminescent, respectivement ; et dDsolvant, dPsolvant et dHsolvant représentent un terme de dispersion, le terme de polarisation et le terme de liaison hydrogène dans le paramètre de solubilité de Hansen du solvant, respectivement.)
PCT/JP2017/022077 2016-06-21 2017-06-15 Composition d'encre pour éléments électroluminescents organiques, et procédé de production d'élément électroluminescent organique utilisant cette dernière WO2017221802A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016122623 2016-06-21
JP2016-122623 2016-06-21

Publications (1)

Publication Number Publication Date
WO2017221802A1 true WO2017221802A1 (fr) 2017-12-28

Family

ID=60784722

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/022077 WO2017221802A1 (fr) 2016-06-21 2017-06-15 Composition d'encre pour éléments électroluminescents organiques, et procédé de production d'élément électroluminescent organique utilisant cette dernière

Country Status (2)

Country Link
TW (1) TW201815997A (fr)
WO (1) WO2017221802A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018230548A1 (fr) * 2017-06-15 2018-12-20 Dic株式会社 Encre permettant de former une couche fonctionnelle
WO2019163625A1 (fr) * 2018-02-23 2019-08-29 コニカミノルタ株式会社 Composition pour dispositifs électroniques, encre pour dispositifs électroniques, et procédé de production de dispositif électronique
JP2019214659A (ja) * 2018-06-12 2019-12-19 Dic株式会社 機能層形成用インク
JP2021064467A (ja) * 2019-10-10 2021-04-22 東京応化工業株式会社 有機ｅｌパネル用基板の製造方法、有機ｅｌパネル用基板、及びネガ型感光性樹脂組成物
EP3971249A1 (fr) * 2020-09-22 2022-03-23 Samsung Display Co., Ltd. Encre contenant des éléments électroluminescents et procédé de fabrication d'un dispositif d'affichage l'utilisant

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013527980A (ja) * 2010-04-12 2013-07-04 メルク パテント ゲーエムベーハー 改良された性能を有する組成物
JP2013144675A (ja) * 2011-12-15 2013-07-25 Ricoh Co Ltd アントラセン誘導体、有機ｅｌ用材料およびその製造方法
JP2013533606A (ja) * 2010-05-27 2013-08-22 メルク パテント ゲゼルシャフト ミット ベシュレンクテル ハフツング 有機電子装置を調製するための配合物および方法
JP2013214496A (ja) * 2012-03-08 2013-10-17 Seiko Epson Corp 有機ｅｌ装置の製造方法、有機ｅｌ装置、電子機器
WO2015018480A1 (fr) * 2013-08-07 2015-02-12 Merck Patent Gmbh Formulation pour la préparation de dispositifs électroniques organiques (oe) comprenant un liant polymère
WO2016093111A1 (fr) * 2014-12-10 2016-06-16 Dic株式会社 Composition d'encre pour élément électroluminescent organique, et élément électroluminescent organique utilisant celle-ci

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013527980A (ja) * 2010-04-12 2013-07-04 メルク パテント ゲーエムベーハー 改良された性能を有する組成物
JP2013533606A (ja) * 2010-05-27 2013-08-22 メルク パテント ゲゼルシャフト ミット ベシュレンクテル ハフツング 有機電子装置を調製するための配合物および方法
JP2013144675A (ja) * 2011-12-15 2013-07-25 Ricoh Co Ltd アントラセン誘導体、有機ｅｌ用材料およびその製造方法
JP2013214496A (ja) * 2012-03-08 2013-10-17 Seiko Epson Corp 有機ｅｌ装置の製造方法、有機ｅｌ装置、電子機器
WO2015018480A1 (fr) * 2013-08-07 2015-02-12 Merck Patent Gmbh Formulation pour la préparation de dispositifs électroniques organiques (oe) comprenant un liant polymère
WO2016093111A1 (fr) * 2014-12-10 2016-06-16 Dic株式会社 Composition d'encre pour élément électroluminescent organique, et élément électroluminescent organique utilisant celle-ci

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018230548A1 (fr) * 2017-06-15 2018-12-20 Dic株式会社 Encre permettant de former une couche fonctionnelle
WO2019163625A1 (fr) * 2018-02-23 2019-08-29 コニカミノルタ株式会社 Composition pour dispositifs électroniques, encre pour dispositifs électroniques, et procédé de production de dispositif électronique
JPWO2019163625A1 (ja) * 2018-02-23 2021-02-04 コニカミノルタ株式会社 電子デバイス用組成物、電子デバイス用インク及び電子デバイスの製造方法
JP7156357B2 (ja) 2018-02-23 2022-10-19 コニカミノルタ株式会社 電子デバイス用組成物、電子デバイス用インク及び電子デバイスの製造方法
JP2019214659A (ja) * 2018-06-12 2019-12-19 Dic株式会社 機能層形成用インク
JP2021064467A (ja) * 2019-10-10 2021-04-22 東京応化工業株式会社 有機ｅｌパネル用基板の製造方法、有機ｅｌパネル用基板、及びネガ型感光性樹脂組成物
EP3971249A1 (fr) * 2020-09-22 2022-03-23 Samsung Display Co., Ltd. Encre contenant des éléments électroluminescents et procédé de fabrication d'un dispositif d'affichage l'utilisant

Also Published As

Publication number Publication date
TW201815997A (zh) 2018-05-01

Similar Documents

Publication Publication Date Title
WO2017221802A1 (fr) Composition d'encre pour éléments électroluminescents organiques, et procédé de production d'élément électroluminescent organique utilisant cette dernière
JP2018009078A (ja) 有機発光素子用インキ組成物、並びにこれを用いた有機発光素子およびその製造方法
TWI396703B (zh) 成膜用組成物及有機電場發光元件
JP5401791B2 (ja) スプレー又はインクジェット塗布用電荷輸送性ワニス
JP5617640B2 (ja) 正孔または電子輸送性薄膜形成用ワニス
CN102106017B (zh) 有机电致发光元件、有机电致发光显示装置以及有机电致发光光源
JP4723555B2 (ja) 電子デバイスの製造方法及びその製造方法に適した塗布液
CN104365180B (zh) 导电性薄膜积层体的制造方法
TWI710608B (zh) 適合於在有機電子中使用的非水性組成物
JP5259139B2 (ja) 有機電界発光素子用組成物、有機電界発光素子および有機電界発光素子の製造方法
KR101314704B1 (ko) 유기 발광 소자 및 이의 제조 방법
JP7183177B2 (ja) 半導体の有機層を形成するためのインク組成物
KR20140110927A (ko) 코팅용 조성물, 다공질막, 광 산란막 및 유기 전계 발광 소자
JPWO2008032616A1 (ja) オリゴアニリン化合物
JP6607606B2 (ja) トリアジン置換インドロカルバゾール誘導体、それからなる有機電子デバイス形成用アルコール不溶性塗膜、及びそれを用いた有機電子デバイス
KR102285565B1 (ko) 잉크 조성물 및 유기 발광 소자 제조방법
CN102986052A (zh) 有机电致发光元件、有机电致发光器件、有机el显示装置和有机el照明
CN102860130B (zh) 有机电致发光元件用组合物的制造方法、有机电致发光元件用组合物、有机电致发光元件的制造方法、有机电致发光元件、有机el显示设备及有机el照明
CN103931009A (zh) 有机电致发光元件和有机电致发光器件
JP2011151097A (ja) 有機発光層材料，有機発光層材料を用いた有機発光層形成用塗布液，有機発光層形成用塗布液を用いた有機発光素子および有機発光素子を用いた光源装置
CN107532022A (zh) 适用于有机电子器件的非水性组合物
WO2018230548A1 (fr) Encre permettant de former une couche fonctionnelle
WO2010104183A1 (fr) Composition pour élément organique électroluminescent, élément organique électroluminescent, écran organique el, et éclairage organique el
JP5145652B2 (ja) 有機化合物、電荷輸送材料、有機電界発光素子用組成物および有機電界発光素子
Cole et al. Inkjet‐printed self‐hosted tadf polymer light‐emitting diodes

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17815270

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17815270

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP