WO2017038917A1 - 粘着シート - Google Patents

粘着シート Download PDF

Info

Publication number
WO2017038917A1
WO2017038917A1 PCT/JP2016/075604 JP2016075604W WO2017038917A1 WO 2017038917 A1 WO2017038917 A1 WO 2017038917A1 JP 2016075604 W JP2016075604 W JP 2016075604W WO 2017038917 A1 WO2017038917 A1 WO 2017038917A1
Authority
WO
WIPO (PCT)
Prior art keywords
pressure
sensitive adhesive
adhesive sheet
mass
layer
Prior art date
Application number
PCT/JP2016/075604
Other languages
English (en)
French (fr)
Japanese (ja)
Inventor
高野　健
和浩 菊池
貴志 杉野
Original Assignee
リンテック株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by リンテック株式会社 filed Critical リンテック株式会社
Priority to KR1020177034192A priority Critical patent/KR101930197B1/ko
Priority to JP2017518161A priority patent/JP6148805B1/ja
Priority to CN201680030959.7A priority patent/CN107636100B/zh
Priority to KR1020187035736A priority patent/KR102612643B1/ko
Publication of WO2017038917A1 publication Critical patent/WO2017038917A1/ja

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J7/00—Adhesives in the form of films or foils
    • C09J7/20—Adhesives in the form of films or foils characterised by their carriers
    • C09J7/29—Laminated material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/38—Layered products comprising a layer of synthetic resin comprising epoxy resins
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D163/00—Coating compositions based on epoxy resins; Coating compositions based on derivatives of epoxy resins
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
    • C09J133/04—Homopolymers or copolymers of esters
    • C09J133/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, the oxygen atom being present only as part of the carboxyl radical
    • C09J133/062—Copolymers with monomers not covered by C09J133/06
    • C09J133/066—Copolymers with monomers not covered by C09J133/06 containing -OH groups
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
    • C09J133/04—Homopolymers or copolymers of esters
    • C09J133/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, the oxygen atom being present only as part of the carboxyl radical
    • C09J133/08—Homopolymers or copolymers of acrylic acid esters
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J183/00—Adhesives based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Adhesives based on derivatives of such polymers
    • C09J183/04—Polysiloxanes
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J7/00—Adhesives in the form of films or foils
    • C09J7/20—Adhesives in the form of films or foils characterised by their carriers
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J7/00—Adhesives in the form of films or foils
    • C09J7/20—Adhesives in the form of films or foils characterised by their carriers
    • C09J7/22—Plastics; Metallised plastics
    • C09J7/25—Plastics; Metallised plastics based on macromolecular compounds obtained otherwise than by reactions involving only carbon-to-carbon unsaturated bonds
    • C09J7/255—Polyesters
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J7/00—Adhesives in the form of films or foils
    • C09J7/50—Adhesives in the form of films or foils characterised by a primer layer between the carrier and the adhesive
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/04—Manufacture or treatment of semiconductor devices or of parts thereof the devices having potential barriers, e.g. a PN junction, depletion layer or carrier concentration layer
    • H01L21/50—Assembly of semiconductor devices using processes or apparatus not provided for in a single one of the subgroups H01L21/06 - H01L21/326, e.g. sealing of a cap to a base of a container
    • H01L21/56—Encapsulations, e.g. encapsulation layers, coatings
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J2203/00—Applications of adhesives in processes or use of adhesives in the form of films or foils
    • C09J2203/326—Applications of adhesives in processes or use of adhesives in the form of films or foils for bonding electronic components such as wafers, chips or semiconductors
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J2301/00—Additional features of adhesives in the form of films or foils
    • C09J2301/10—Additional features of adhesives in the form of films or foils characterized by the structural features of the adhesive tape or sheet
    • C09J2301/12—Additional features of adhesives in the form of films or foils characterized by the structural features of the adhesive tape or sheet by the arrangement of layers
    • C09J2301/122—Additional features of adhesives in the form of films or foils characterized by the structural features of the adhesive tape or sheet by the arrangement of layers the adhesive layer being present only on one side of the carrier, e.g. single-sided adhesive tape
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J2463/00—Presence of epoxy resin
    • C09J2463/003—Presence of epoxy resin in the primer coating
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J2467/00—Presence of polyester
    • C09J2467/003—Presence of polyester in the primer coating
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J2467/00—Presence of polyester
    • C09J2467/006—Presence of polyester in the substrate

Definitions

  • the present invention relates to an adhesive sheet.
  • Patent Document 1 discloses a mask sheet for suppressing adhesive residue of an adhesive and stably producing a QFN (Quad Flat Non-lead) semiconductor package.
  • a mask sheet is prepared using a specific heat-resistant film and a silicone-based pressure-sensitive adhesive to withstand an environment of 150 to 180 ° C. for 1 to 6 hours in a die attach process and a resin sealing process. It is stated that you get.
  • pressure-sensitive adhesive sheets are also used in processes where high temperature conditions such as 180 ° C. or higher and 200 ° C. or lower are imposed.
  • high-temperature process for example, when an inexpensive film (for example, a film such as polyethylene terephthalate) having a low heat resistance compared to a polyimide film or the like is used as a base material, the adhesive sheet is removed from the adherend after the process is completed. It was found that the surface of the adherend was contaminated when peeled off. It is thought that the cause of such contamination is that a low molecular weight component (oligomer) contained in the resin film used as the base material is deposited on the surface of the adherend.
  • oligomer a low molecular weight component contained in the resin film used as the base material
  • An object of the present invention is to provide a pressure-sensitive adhesive sheet that can prevent contamination of the surface of an adherend even after undergoing a process in which high-temperature conditions are imposed.
  • a pressure-sensitive adhesive sheet used for sealing a semiconductor element on a pressure-sensitive adhesive sheet which includes a base material, a pressure-sensitive adhesive layer containing a pressure-sensitive adhesive, the base material, and the pressure-sensitive adhesive.
  • An pressure-sensitive adhesive sheet having an oligomer sealing layer provided between the layers is provided.
  • the oligomer sealing layer is a cured film obtained by curing a composition for an oligomer sealing layer containing an epoxy compound, a polyester compound, and a polyfunctional amino compound. Is preferred.
  • the composition for an oligomer sealing layer comprises (A) 50% by mass to 80% by mass of a bisphenol A type epoxy compound and (B) 5% by mass to 30% by mass. It is preferable to contain the following polyester compounds and (C) 10 to 40 mass% polyfunctional amino compounds.
  • the storage elastic modulus of the substrate at 100 ° C. is preferably 1 ⁇ 10 7 Pa or more.
  • the pressure-sensitive adhesive layer preferably contains an acrylic pressure-sensitive adhesive composition or a silicone-based pressure-sensitive adhesive composition.
  • the acrylic pressure-sensitive adhesive composition preferably includes an acrylic copolymer containing 2-ethylhexyl acrylate as a main monomer.
  • the silicone-based pressure-sensitive adhesive composition contains an addition polymerization type silicone resin.
  • the oligomer sealing layer is provided on both surfaces of the base material.
  • the base material preferably contains a polyester resin.
  • FIG. 1 shows a schematic cross-sectional view of the pressure-sensitive adhesive sheet 10 of the present embodiment.
  • the pressure-sensitive adhesive sheet 10 has a base material 11, a pressure-sensitive adhesive layer 12, and an oligomer sealing layer 13.
  • the base material 11 has a first base material surface 11a and a second base material surface 11b opposite to the first base material surface 11a.
  • An oligomer sealing layer 13 is provided between the substrate 11 and the pressure-sensitive adhesive layer 12.
  • the oligomer sealing layer 13 is preferably laminated on the first base material surface 11 a, and the first base material surface 11 a is preferably covered with the oligomer sealing layer 13.
  • the shape of the pressure-sensitive adhesive sheet 10 can take any shape such as a sheet shape, a tape shape, and a label shape.
  • the substrate 11 is a member that supports the pressure-sensitive adhesive layer 12 and the oligomer sealing layer 13.
  • a sheet material such as a synthetic resin film can be used.
  • synthetic resin films include polyethylene film, polypropylene film, polybutene film, polybutadiene film, polymethylpentene film, polyvinyl chloride film, vinyl chloride copolymer film, polyethylene terephthalate film, polyethylene naphthalate film, polybutylene terephthalate film.
  • examples of the substrate 11 include these cross-linked films and laminated films.
  • the base material 11 preferably includes a polyester-based resin, and more preferably includes a material having a polyester-based resin as a main component.
  • the material having a polyester-based resin as a main component means that the ratio of the mass of the polyester-based resin to the total mass of the material constituting the substrate is 50% by mass or more.
  • the polyester resin is, for example, any resin selected from the group consisting of polyethylene terephthalate resin, polybutylene terephthalate resin, polyethylene naphthalate resin, polybutylene naphthalate resin, and copolymer resins of these resins. Is preferred, and polyethylene terephthalate resin is more preferred.
  • a polyethylene terephthalate film or a polyethylene naphthalate film is preferable, and a polyethylene terephthalate film is more preferable.
  • the oligomers contained in the polyester film are derived from polyester-forming monomers, dimers, trimers, and the like.
  • the lower limit of the storage elastic modulus at 100 ° C. of the substrate 11 is preferably 1 ⁇ 10 7 Pa or more, and more preferably 1 ⁇ 10 8 Pa or more, from the viewpoint of dimensional stability during processing.
  • the upper limit of the storage elastic modulus at 100 ° C. of the substrate 11 is preferably 1 ⁇ 10 12 Pa or less from the viewpoint of workability.
  • the storage elastic modulus is a value measured at a frequency of 1 Hz by a torsional shear method using a dynamic viscoelasticity measuring apparatus.
  • the substrate to be measured is cut into a width of 5 mm and a length of 20 mm, and a viscoelasticity measuring device (manufactured by TA Instruments, DMAQ800) is used, and the storage viscoelasticity at 100 ° C. is measured at a frequency of 1 Hz and a tensile mode. taking measurement.
  • a viscoelasticity measuring device manufactured by TA Instruments, DMAQ800
  • the first substrate surface 11a may be subjected to at least one surface treatment such as a primer treatment, a corona treatment, and a plasma treatment in order to improve the adhesion with the oligomer sealing layer 13.
  • the first base material surface 11a of the base material 11 may be subjected to an adhesive treatment by applying an adhesive.
  • the pressure-sensitive adhesive used for the pressure-sensitive adhesive treatment of the substrate include acrylic, rubber-based, silicone-based, and urethane-based pressure-sensitive adhesives.
  • the thickness of the substrate 11 is preferably 10 ⁇ m or more and 500 ⁇ m or less, more preferably 15 ⁇ m or more and 300 ⁇ m or less, and further preferably 20 ⁇ m or more and 250 ⁇ m or less.
  • the pressure-sensitive adhesive layer 12 includes a pressure-sensitive adhesive composition.
  • the pressure-sensitive adhesive contained in this pressure-sensitive adhesive composition is not particularly limited, and various types of pressure-sensitive adhesives can be applied to the pressure-sensitive adhesive layer 12.
  • Examples of the adhesive contained in the adhesive layer 12 include rubber-based, acrylic-based, silicone-based, polyester-based, and urethane-based.
  • the kind of adhesive is selected in consideration of the use and the kind of adherend to be attached.
  • the pressure-sensitive adhesive layer 12 preferably contains an acrylic pressure-sensitive adhesive composition or a silicone-based pressure-sensitive adhesive composition.
  • the acrylic pressure-sensitive adhesive composition preferably contains an acrylic copolymer containing 2-ethylhexyl acrylate as a main monomer. . Moreover, when the adhesive layer 12 contains an acrylic adhesive composition, it is preferable that the acrylic copolymer and the adhesion promoter are included.
  • the acrylic copolymer is preferably a copolymer having 2-ethylhexyl acrylate as a main monomer.
  • the adhesive aid preferably contains a rubber-based material having a reactive group as a main component.
  • 2-ethylhexyl acrylate is the main monomer, and the ratio of the mass of the copolymer component derived from 2-ethylhexyl acrylate to the total mass of the acrylic copolymer is 50% by mass or more. Means.
  • the proportion of the copolymer component derived from 2-ethylhexyl acrylate in the acrylic copolymer is preferably 50% by mass or more and 95% by mass or less, and 60% by mass or more and 95% by mass or less. It is more preferable that it is 80 mass% or more and 95 mass% or less, and it is still more preferable that it is 85 mass% or more and 93 mass% or less.
  • the proportion of the copolymer component derived from 2-ethylhexyl acrylate is 50% by mass or more, the adhesive strength does not become too high after heating, and the adhesive sheet is more easily peeled off from the adherend, and 80% by mass or more. If it is, it will become still easier to peel. If the proportion of the copolymer component derived from 2-ethylhexyl acrylate is 95% by mass or less, the initial adhesive force is insufficient and the substrate is deformed during heating, or the adhesive sheet is peeled off from the adherend due to the deformation. Can be prevented.
  • the type and number of copolymer components other than 2-ethylhexyl acrylate in the acrylic copolymer are not particularly limited.
  • a functional group-containing monomer having a reactive functional group is preferable.
  • a reactive functional group of a 2nd copolymer component when using the crosslinking agent mentioned later, it is preferable that it is a functional group which can react with the said crosslinking agent.
  • This reactive functional group is preferably at least one substituent selected from the group consisting of, for example, a carboxyl group, a hydroxyl group, an amino group, a substituted amino group, and an epoxy group. These substituents are more preferable, and a carboxyl group is still more preferable.
  • Examples of the monomer having a carboxyl group include ethylenically unsaturated carboxylic acids such as acrylic acid, methacrylic acid, crotonic acid, maleic acid, itaconic acid, and citraconic acid.
  • carboxyl group-containing monomers acrylic acid is preferable from the viewpoint of reactivity and copolymerization.
  • a carboxyl group-containing monomer may be used independently and may be used in combination of 2 or more type.
  • Examples of the monomer having a hydroxyl group include, for example, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 3-hydroxypropyl (meth) acrylate, (meth) acrylic acid 2 And (meth) acrylic acid hydroxyalkyl esters such as hydroxybutyl, 3-hydroxybutyl (meth) acrylate, and 4-hydroxybutyl (meth) acrylate.
  • 2-hydroxyethyl (meth) acrylate is preferred from the viewpoint of hydroxyl reactivity and copolymerization.
  • a hydroxyl-containing monomer may be used independently and may be used in combination of 2 or more type.
  • “(meth) acrylic acid” is a notation used to represent both “acrylic acid” and “methacrylic acid”, and the same applies to other similar terms.
  • Examples of the acrylate ester having an epoxy group include glycidyl acrylate and glycidyl methacrylate.
  • Examples of other copolymer components in the acrylic copolymer include (meth) acrylic acid alkyl esters having an alkyl group with 2 to 20 carbon atoms.
  • Examples of the (meth) acrylic acid alkyl ester include, for example, ethyl (meth) acrylate, propyl (meth) acrylate, n-butyl (meth) acrylate, n-pentyl (meth) acrylate, and (meth) acrylic acid n.
  • Examples of other copolymer components in the acrylic copolymer include, for example, alkoxyalkyl group-containing (meth) acrylic acid ester, (meth) acrylic acid ester having an aliphatic ring, and (meth) acrylic acid having an aromatic ring.
  • alkoxyalkyl group-containing (meth) acrylic acid ester examples include methoxymethyl (meth) acrylate, methoxyethyl (meth) acrylate, ethoxymethyl (meth) acrylate, and ethoxyethyl (meth) acrylate.
  • examples of the (meth) acrylic acid ester having an aliphatic ring include cyclohexyl (meth) acrylate.
  • examples of the (meth) acrylic acid ester having an aromatic ring examples include phenyl (meth) acrylate.
  • non-crosslinkable acrylamides examples include acrylamide and methacrylamide.
  • Examples of the (meth) acrylic acid ester having a non-crosslinkable tertiary amino group include (meth) acrylic acid (N, N-dimethylamino) ethyl and (meth) acrylic acid (N, N-dimethylamino). Propyl.
  • a copolymer component derived from a monomer having a nitrogen atom-containing ring is also preferable from the viewpoint of improving the polarity of the pressure-sensitive adhesive and improving adhesion and adhesive strength. .
  • Monomers having a nitrogen atom-containing ring include N-vinyl-2-pyrrolidone, N-methylvinylpyrrolidone, N-vinylpiperidone, N-vinylpiperazine, N-vinylpyrazine, N-vinylpyrrole, N-vinylimidazole, N- Examples include vinyl morpholine, N-vinyl caprolactam, and N- (meth) acryloyl morpholine.
  • N- (meth) acryloylmorpholine is preferable. These monomers may be used independently and may be used in combination of 2 or more type.
  • a carboxyl group-containing monomer or a hydroxyl group-containing monomer is preferable as the second copolymer component, and acrylic acid is more preferable.
  • the acrylic copolymer includes a copolymer component derived from 2-ethylhexyl acrylate and a copolymer component derived from acrylic acid
  • the copolymer component derived from acrylic acid occupies the total mass of the acrylic copolymer.
  • the mass ratio is preferably 1% by mass or less, and more preferably 0.1% by mass or more and 0.5% by mass or less. If the ratio of acrylic acid is 1 mass% or less, when an adhesive composition contains a crosslinking agent, crosslinking of the acrylic copolymer can be prevented from proceeding too quickly.
  • the acrylic copolymer may contain a copolymer component derived from two or more kinds of functional group-containing monomers.
  • the acrylic copolymer may be a ternary copolymer.
  • an acrylic copolymer obtained by copolymerizing 2-ethylhexyl acrylate, a carboxyl group-containing monomer and a hydroxyl group-containing monomer is preferred, and this carboxyl group-containing monomer is preferred.
  • the hydroxyl group-containing monomer is preferably 2-hydroxyethyl acrylate.
  • the ratio of the copolymer component derived from 2-ethylhexyl acrylate in the acrylic copolymer is 80% by mass or more and 95% by mass or less, and the ratio of the mass of the copolymer component derived from acrylic acid is 1% by mass or less.
  • the balance is preferably a copolymer component derived from 2-hydroxyethyl acrylate.
  • the weight average molecular weight (Mw) of the acrylic copolymer is preferably from 300,000 to 2,000,000, more preferably from 600,000 to 1,500,000, and even more preferably from 800,000 to 1,200,000. preferable. If the weight average molecular weight Mw of the acrylic copolymer is 300,000 or more, the acrylic copolymer can be peeled without a residue of the adhesive on the adherend. When the weight average molecular weight Mw of the acrylic copolymer is 2 million or less, it can be reliably attached to the adherend.
  • the weight average molecular weight Mw of the acrylic copolymer is a standard polystyrene equivalent value measured by a gel permeation chromatography (GPC) method.
  • the acrylic copolymer can be produced according to a conventionally known method using the above-mentioned various raw material monomers.
  • the form of copolymerization of the acrylic copolymer is not particularly limited, and any of a block copolymer, a random copolymer, and a graft copolymer may be used.
  • the content of the acrylic copolymer in the pressure-sensitive adhesive composition is preferably 40% by mass or more and 90% by mass or less, and more preferably 50% by mass or more and 90% by mass or less.
  • the adhesive aid preferably contains a rubber-based material having a reactive group as a main component.
  • the pressure-sensitive adhesive composition contains a reactive pressure-sensitive adhesive aid, the adhesive residue can be reduced.
  • the content of the adhesion assistant in the pressure-sensitive adhesive composition is preferably 3% by mass or more and 50% by mass or less, and more preferably 5% by mass or more and 30% by mass or less. If the content rate of the adhesion promoter in an adhesive composition is 3 mass% or more, generation
  • including a rubber-based material having a reactive group as a main component means that the proportion of the mass of the rubber-based material having a reactive group in the total mass of the adhesive aid exceeds 50% by mass.
  • the ratio of the rubber-based material having a reactive group in the adhesion assistant is preferably more than 50% by mass, and more preferably 80% by mass or more. It is also preferable that the adhesion assistant is made of a rubber-based material having a substantially reactive group.
  • the reactive group is preferably one or more functional groups selected from the group consisting of a hydroxyl group, an isocyanate group, an amino group, an oxirane group, an acid anhydride group, an alkoxy group, an acryloyl group, and a methacryloyl group. More preferably.
  • the reactive group possessed by the rubber material may be one type or two or more types.
  • the rubber-based material having a hydroxyl group may further have the aforementioned reactive group.
  • the number of reactive groups may be one per molecule constituting the rubber-based material, or two or more.
  • the rubber-based material is not particularly limited, but a polybutadiene-based resin and a hydrogenated product of a polybutadiene-based resin are preferable, and a hydrogenated product of a polybutadiene-based resin is more preferable.
  • the polybutadiene-based resin include resins having 1,4-repeating units, resins having 1,2-repeating units, and resins having both 1,4-repeating units and 1,2-repeating units.
  • the hydrogenated product of the polybutadiene resin of the present embodiment includes a hydride of a resin having these repeating units.
  • the polybutadiene resin and the hydrogenated product of the polybutadiene resin preferably have reactive groups at both ends.
  • the reactive groups at both ends may be the same or different.
  • the reactive groups at both ends are preferably one or more functional groups selected from the group consisting of a hydroxyl group, an isocyanate group, an amino group, an oxirane group, an acid anhydride group, an alkoxy group, an acryloyl group, and a methacryloyl group. More preferred is a hydroxyl group.
  • both ends are hydroxyl groups.
  • the pressure-sensitive adhesive composition according to the present embodiment preferably contains a cross-linked product obtained by cross-linking a composition containing a cross-linking agent in addition to the acrylic copolymer and the pressure-sensitive adhesive aid.
  • the solid content of the pressure-sensitive adhesive composition substantially consists of a cross-linked product obtained by cross-linking the above-mentioned acrylic copolymer, the pressure-sensitive adhesive aid, and the cross-linking agent as described above.
  • “substantially” means that the solid content of the pressure-sensitive adhesive composition is composed only of the cross-linked product, excluding trace amounts of impurities that are inevitably mixed in the pressure-sensitive adhesive.
  • examples of the crosslinking agent include an isocyanate crosslinking agent, an epoxy crosslinking agent, an aziridine crosslinking agent, a metal chelate crosslinking agent, an amine crosslinking agent, and an amino resin crosslinking agent.
  • These cross-linking agents may be used alone or in combination of two or more.
  • a crosslinking agent (isocyanate-based crosslinking agent) containing a compound having an isocyanate group as a main component is preferable.
  • isocyanate crosslinking agent examples include 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 1,3-xylylene diisocyanate, 1,4-xylylene diisocyanate, diphenylmethane-4,4′-diisocyanate, Polyvalent isocyanates such as diphenylmethane-2,4'-diisocyanate, 3-methyldiphenylmethane diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, dicyclohexylmethane-4,4'-diisocyanate, dicyclohexylmethane-2,4'-diisocyanate, and lysine isocyanate Compounds.
  • Polyvalent isocyanates such as diphenylmethane-2,4'-diisocyanate, 3-methyldiphenylmethane diisocyanate, hexamethylene diisocyanate,
  • the polyisocyanate compound may be a trimethylolpropane adduct-type modified product of the above-described compound, a burette-type modified product reacted with water, or an isocyanurate-type modified product having an isocyanurate ring.
  • crosslinking agent mainly comprising a compound having an isocyanate group means that the ratio of the mass of the compound having an isocyanate group to the total mass of the components constituting the crosslinking agent is 50% by mass or more. To do.
  • the content of the crosslinking agent in the pressure-sensitive adhesive composition is preferably 0.1 parts by mass or more and 20 parts by mass or less, more preferably 1 part by mass or more with respect to 100 parts by mass of the acrylic copolymer. 15 parts by mass or less, more preferably 5 parts by mass or more and 10 parts by mass or less. If content of the crosslinking agent in an adhesive composition is in such a range, the adhesiveness of the layer (adhesive layer) containing an adhesive composition and a to-be-adhered body (for example, base material) will be improved. It is possible to shorten the curing period for stabilizing the adhesive property after the production of the adhesive sheet.
  • the isocyanate-based crosslinking agent is more preferably a compound having an isocyanurate ring (isocyanurate-type modified product).
  • the compound having an isocyanurate ring is preferably blended in an amount of 0.7 to 1.5 equivalents with respect to the hydroxyl equivalent of the acrylic copolymer. If the compounding quantity of the compound which has an isocyanurate ring is 0.7 equivalent or more, the adhesive strength will not become too high after heating, the adhesive sheet will be easily peeled off, and the adhesive residue can be reduced. If the compounding quantity of the compound which has an isocyanurate ring is 1.5 equivalent or less, it can prevent that an initial stage adhesive force becomes low too much, or can prevent a sticking fall.
  • the pressure-sensitive adhesive composition in this embodiment contains a crosslinking agent
  • the pressure-sensitive adhesive composition preferably further contains a crosslinking accelerator.
  • the crosslinking accelerator is preferably selected and used as appropriate according to the type of the crosslinking agent.
  • the pressure-sensitive adhesive composition contains a polyisocyanate compound as a crosslinking agent
  • a silicone-type adhesive composition contains an addition polymerization type silicone resin.
  • a silicone pressure-sensitive adhesive composition containing an addition polymerization type silicone resin is referred to as an addition reaction type silicone pressure-sensitive adhesive composition.
  • the addition reaction type silicone pressure-sensitive adhesive composition contains a main agent and a crosslinking agent.
  • the addition reaction type silicone pressure-sensitive adhesive composition has an advantage that it can be used only by primary curing at a low temperature and does not require secondary curing at a high temperature.
  • the conventional peroxide-curing silicone pressure-sensitive adhesive requires secondary curing at a high temperature such as 150 ° C. or higher. Therefore, by using the addition reaction type silicone pressure-sensitive adhesive composition, it is possible to produce a pressure-sensitive adhesive sheet at a relatively low temperature, use the base material 11 having excellent energy economy and relatively low heat resistance. Thus, the pressure-sensitive adhesive sheet 10 can be manufactured. Further, since no by-product is produced during curing unlike the peroxide-curing silicone pressure-sensitive adhesive, there are no problems such as odor and corrosion.
  • the addition reaction type silicone pressure-sensitive adhesive composition is usually composed of a main agent composed of a mixture of a silicone resin component and a silicone rubber component, a hydrosilyl group (SiH group) -containing crosslinking agent, and a curing catalyst used as necessary.
  • the silicone resin component is an organopolysiloxane having a network structure obtained by hydrolyzing organochlorosilane or organoalkoxysilane and then performing a dehydration condensation reaction.
  • the silicone rubber component is a diorganopolysiloxane having a linear structure.
  • both the silicone resin component and the silicone rubber component are a methyl group, an ethyl group, a propyl group, a butyl group, a phenyl group, and the like.
  • the aforementioned organo groups are partially vinyl, hexenyl, allyl, butenyl, pentenyl, octenyl, (meth) acryloyl, (meth) acryloylmethyl, (meth) acryloylpropyl, and cyclohexenyl.
  • Substituting with an unsaturated group such as a group.
  • An organo group having a vinyl group that is easily available industrially is preferred.
  • crosslinking proceeds by an addition reaction between an unsaturated group and a hydrosilyl group to form a network structure, thereby exhibiting adhesiveness.
  • the number of unsaturated groups such as vinyl groups is usually from 0.05 to 3.0, preferably from 0.1 to 2.5, per 100 organo groups.
  • organopolysiloxane described above examples include KS-3703 manufactured by Shin-Etsu Chemical Co., Ltd. (the number of vinyl groups is 0.6 per 100 methyl groups), Toray Dow Corning BY23-753 manufactured by the company (the number of vinyl groups is 0.1 per 100 methyl groups) and BY24-162 (the number of vinyl groups is 1.4 per 100 methyl groups) Things).
  • SD4560PSA, SD4570PSA, SD4580PSA, SD4584PSA, SD4585PSA, SD4587L, and SD4592PSA manufactured by Toray Dow Corning can also be used.
  • organopolysiloxane which is a silicone resin component
  • silicone rubber component KS-3800 (manufactured by Shin-Etsu Chemical Co., Ltd.) 7.6 for 100 methyl groups), BY24-162 made by Toray Dow Corning (number of vinyl groups is 1.4 for 100 methyl groups), BY24- 843 (having no unsaturated group) and SD-7292 (the number of vinyl groups is 5.0 with respect to 100 methyl groups).
  • Specific examples of the addition reaction type silicone as described above are described in, for example, JP-A-10-219229.
  • the crosslinking agent is usually 0.5 to 10 hydrogen atoms bonded to silicon atoms, preferably 1 or more to one unsaturated group such as a vinyl group of the silicone resin component and the silicone rubber component. It mix
  • the number By setting the number to 0.5 or more, the reaction between the unsaturated group such as a vinyl group and the hydrosilyl group does not proceed completely, thereby preventing poor curing.
  • the addition reaction type silicone pressure-sensitive adhesive composition preferably contains a curing catalyst together with the aforementioned addition reaction type silicone component (main agent comprising a silicone resin component and a silicone rubber component) and a crosslinking agent.
  • This curing catalyst is used to accelerate the hydrosilylation reaction between the unsaturated group in the silicone resin component and the silicone rubber component and the Si—H group in the crosslinking agent.
  • the curing catalyst is a platinum-based catalyst, that is, chloroplatinic acid, an alcohol solution of chloroplatinic acid, a reaction product of chloroplatinic acid and an alcohol solution, a reaction product of chloroplatinic acid and an olefin compound, chloroplatinic acid and vinyl Examples thereof include a reaction product with a group-containing siloxane compound, a platinum-olefin complex, a platinum-vinyl group-containing siloxane complex, and a platinum-phosphorus complex.
  • Specific examples of the curing catalyst as described above are described in, for example, JP-A-2006-28311 and JP-A-10-147758. More specifically, commercially available products include SRX-212 manufactured by Toray Dow Corning and PL-50T manufactured by Shin-Etsu Chemical Co., Ltd.
  • the blending amount of the curing catalyst is usually 5 mass ppm or more and 2000 mass ppm or less, preferably 10 mass ppm or more and 500 mass ppm or less with respect to the total amount of the silicone resin component and the silicone rubber component as platinum content.
  • curability is lowered and the crosslinking density is reduced, that is, the adhesive force and the cohesive force (holding force) are prevented from being reduced. While preventing, the stability of an adhesive layer can be hold
  • addition reaction type silicone pressure-sensitive adhesive composition adhesive force is exhibited even at room temperature by blending the above-mentioned components, but the addition reaction type silicone pressure-sensitive adhesive composition is applied to the substrate 11 or a release sheet described later. From the standpoint of stability of adhesive strength, the base material 11 and the release sheet are bonded together, and then a heating or active energy ray is irradiated to promote the crosslinking reaction of the silicone resin component and the silicone rubber component by the crosslinking agent. preferable.
  • the heating temperature is usually 60 ° C. or higher and 140 ° C. or lower, preferably 80 ° C. or higher and 130 ° C. or lower.
  • an active energy ray having energy quanta in an electromagnetic wave or a charged particle beam that is, an active light such as an ultraviolet ray or an electron beam
  • an active light such as an ultraviolet ray or an electron beam
  • a photopolymerization initiator is not required.
  • a photopolymerization initiator is present.
  • the photopolymerization initiator in the case of irradiation with ultraviolet rays is not particularly limited, and any photopolymerization initiator that has been conventionally used in ultraviolet curable resins can be appropriately selected and used. it can.
  • photopolymerization initiator examples include benzoins, benzophenones, acetophenones, ⁇ -hydroxy ketones, ⁇ -amino ketones, ⁇ -diketones, ⁇ -diketone dialkyl acetals, anthraquinones, thioxanthones, and other compounds. Etc. These photopolymerization initiators may be used alone or in combination of two or more. Further, the amount used is usually 0.01 parts by mass or more and 30 parts by mass or less, preferably 0.05 parts by mass with respect to 100 parts by mass of the total amount of the addition reaction type silicone component and the crosslinking agent used as the main agent. It is selected in the range of 20 parts by mass or less.
  • a pressure-sensitive adhesive sheet having a stable adhesive force can be obtained by crosslinking by irradiation with heat or active energy rays.
  • the acceleration voltage of the electron beam is generally 130 kV or more and 300 kV or less, preferably 150 kV or more and 250 kV or less. Irradiation at an acceleration voltage of 130 kV or more can prevent the silicone resin component and the silicone rubber component from being insufficiently crosslinked and prevent the adhesive force from becoming insufficient. By irradiation at an acceleration voltage of 300 kV or less, the adhesive It can prevent that a layer and a base material sheet deteriorate or discolor. A preferable range of the beam current is 1 mA or more and 100 mA or less.
  • the dose of the irradiated electron beam is preferably 1 Mrad to 70 Mrad, and more preferably 2 Mrad to 20 Mrad.
  • the irradiation amount in the case of ultraviolet irradiation is appropriately selected.
  • the light amount is from 100 mJ / cm 2 to 500 mJ / cm 2 and the illuminance is from 10 mW / cm 2 to 500 mW / cm 2 .
  • Heating and irradiation with active energy rays are preferably performed in a nitrogen atmosphere in order to prevent reaction inhibition by oxygen.
  • the thickness of the pressure-sensitive adhesive layer 12 is appropriately determined according to the use of the pressure-sensitive adhesive sheet 10.
  • the thickness of the pressure-sensitive adhesive layer 12 is preferably 5 ⁇ m or more and 60 ⁇ m or less, and more preferably 10 ⁇ m or more and 50 ⁇ m or less. If the thickness of the pressure-sensitive adhesive layer 12 is too thin, the pressure-sensitive adhesive layer 12 may not follow the irregularities on the circuit surface of the semiconductor chip, and a gap may be generated. For example, an interlayer insulating material and a sealing resin may enter the gap, and the wiring connection electrode pad on the chip circuit surface may be blocked.
  • the pressure-sensitive adhesive layer 12 When the thickness of the pressure-sensitive adhesive layer 12 is 5 ⁇ m or more, the pressure-sensitive adhesive layer 12 easily follows the unevenness of the chip circuit surface, and the generation of a gap can be prevented. If the thickness of the pressure-sensitive adhesive layer 12 is too thick, the semiconductor chip sinks into the pressure-sensitive adhesive layer, and there is a risk that a step between the semiconductor chip portion and the resin portion that seals the semiconductor chip occurs. If such a step occurs, the wiring may be disconnected during rewiring. If the thickness of the pressure-sensitive adhesive layer 12 is 60 ⁇ m or less, a step is hardly generated.
  • the pressure-sensitive adhesive composition may contain other components as long as the effects of the present invention are not impaired.
  • other components that can be included in the pressure-sensitive adhesive composition include organic solvents, flame retardants, tackifiers, ultraviolet absorbers, light stabilizers, antioxidants, antistatic agents, antiseptics, antifungal agents, and plastics. Agents, antifoaming agents, colorants, fillers, wettability adjusting agents and the like.
  • the addition reaction type silicone pressure-sensitive adhesive composition may contain non-reactive polyorganosiloxanes such as polydimethylsiloxane and polymethylphenylsiloxane as additives.
  • the oligomer sealing layer 13 is a layer for preventing the low molecular weight component (oligomer) from entering the pressure-sensitive adhesive layer 12.
  • oligomer low molecular weight component
  • the oligomer sealing layer 13 preferably prevents the oligomer from entering the pressure-sensitive adhesive layer 12 even under a high temperature condition of 180 ° C. or higher and 200 ° C. or lower.
  • the material of the oligomer sealing layer 13 is not particularly limited as long as the oligomer can be prevented from entering the pressure-sensitive adhesive layer 12.
  • the oligomer sealing layer 13 is a cured film obtained by curing a composition for an oligomer sealing layer containing (A) an epoxy compound, (B) a polyester compound, and (C) a polyfunctional amino compound. Is preferred.
  • the composition for oligomer sealing layer may further contain (D) an acidic catalyst.
  • the epoxy compound is preferably a bisphenol A type epoxy compound.
  • the bisphenol A type epoxy compound include bisphenol A diglycidyl ether.
  • the weight average molecular weight (Mw) of the bisphenol A type epoxy compound is preferably 1 ⁇ 10 4 or more and 5 ⁇ 10 4 or less. If the weight average molecular weight (Mw) of the bisphenol A type epoxy compound is 1 ⁇ 10 4 or more, the crosslink density required for the film can be obtained, and the precipitation of the oligomer can be easily prevented. If the weight average molecular weight (Mw) is 5 ⁇ 10 4 or less, it is possible to prevent the film from becoming too hard.
  • the weight average molecular weight Mw is a standard polystyrene conversion value measured by a gel permeation chromatography (GPC) method.
  • polyester compound (B) It does not specifically limit as a polyester compound, It can select from a well-known polyester compound suitably, and can be used.
  • the polyester compound is a resin obtained by a condensation reaction of a polyhydric alcohol and a polybasic acid, and is a compound modified with a condensate of a dibasic acid and a dihydric alcohol or a non-drying oil fatty acid or the like
  • a convertible polyester compound that is a condensate of a dibasic acid and a trivalent or higher alcohol.
  • any of these polyester compounds can be used.
  • Examples of the polyhydric alcohol used as a raw material for the polyester compound include dihydric alcohols, trihydric alcohols, and tetrahydric or higher polyhydric alcohols.
  • Examples of the dihydric alcohol include ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, trimethylene glycol, tetramethylene glycol, and neopentyl glycol.
  • Examples of the trihydric alcohol include glycerin, trimethylolethane, and trimethylolpropane.
  • Examples of the tetrahydric or higher polyhydric alcohol include diglycerin, triglycerin, pentaerythritol, dipentaerythritol, mannitol, and sorbit.
  • a polyhydric alcohol may be used individually by 1 type, and may be used in combination of 2 or more type.
  • polybasic acid examples include aromatic polybasic acids, aliphatic saturated polybasic acids, aliphatic unsaturated polybasic acids, and polybasic acids by Diels-Alder reaction.
  • aromatic polybasic acid examples include phthalic anhydride, terephthalic acid, isophthalic acid, and trimetic anhydride.
  • aliphatic saturated polybasic acid examples include succinic acid, adipic acid, and sebacic acid.
  • aliphatic unsaturated polybasic acid examples include maleic acid, maleic anhydride, fumaric acid, itaconic acid, and citraconic anhydride.
  • Examples of the polybasic acid by Diels-Alder reaction include cyclopentadiene-maleic anhydride adduct, terpene-maleic anhydride adduct, and rosin-maleic anhydride adduct.
  • a polybasic acid may be used individually by 1 type, and may be used in combination of 2 or more type.
  • non-drying oil fatty acid that is a modifier
  • examples of the non-drying oil fatty acid that is a modifier include octylic acid, lauric acid, palmitic acid, stearic acid, oleic acid, linoleic acid, linolenic acid, eleostearic acid, ricinoleic acid, dehydrated ricinoleic acid, or coconut oil. Linseed oil, tung oil, castor oil, dehydrated castor oil, soybean oil, safflower oil, and fatty acids thereof.
  • 1 type may be used independently and 2 or more types may be used in combination.
  • the polyester compound preferably has an active hydrogen group that serves as a base point for the crosslinking reaction.
  • the active hydrogen group include a hydroxyl group, a carboxyl group, and an amino group.
  • the polyester compound particularly preferably has a hydroxyl group.
  • the hydroxyl value of the polyester compound is preferably 5 mgKOH / g or more and 500 mgKOH / g or less, and more preferably 10 mgKOH / g or more and 300 mgKOH / g or less.
  • the number average molecular weight (Mn) of the polyester compound is preferably 500 or more and 10,000 or less, and more preferably 1000 or more and 5000 or less.
  • the aforementioned number average molecular weight is a value in terms of standard polystyrene measured by a gel permeation chromatography (GPC) method.
  • the glass transition temperature Tg of a polyester compound is 0 degreeC or more and 50 degrees C or less.
  • Mn number average molecular weight
  • Tg glass transition temperature
  • a polyfunctional amino compound As a polyfunctional amino compound, a melamine compound, a urea compound, a benzoguanamine compound, and diamine can be used, for example.
  • melamine compounds include hexamethoxymethyl melamine, methylated melamine compounds, and butylated melamine compounds.
  • urea compounds include methylated urea compounds and butylated urea compounds.
  • the benzoguanamine compound include a methylated benzoguanamine compound and a butylated benzoguanamine compound.
  • diamines examples include ethylenediamine, tetramethylenediamine, hexamethylenediamine, N, N′-diphenylethylenediamine, and p-xylylenediamine. From the viewpoint of curability, hexamethoxymethyl melamine is preferred as the (C) polyfunctional amino compound.
  • Acidic catalyst examples include hydrochloric acid and p-toluenesulfonic acid.
  • the oligomer sealing layer 13 contains (A) bisphenol A type epoxy compound, (B) polyester compound, and (C) polyfunctional amino compound, respectively (A) 50 mass% or more 80 It may be a cured film obtained by curing a composition for an oligomer sealing layer containing at a blending ratio of 5% by mass or less, (B) 5% by mass to 30% by mass, and (C) 10% by mass or more and 40% by mass or less. preferable.
  • the effect of preventing the oligomer sealing layer 13 from entering the pressure-sensitive adhesive layer 12 by the oligomer sealing layer 13 can be improved.
  • composition for an oligomer sealing layer As a more specific example of the composition for an oligomer sealing layer according to the present embodiment, for example, the following examples of the composition for an oligomer sealing layer may be mentioned. It is not limited.
  • composition for an oligomer sealing layer As an example of the composition for an oligomer sealing layer according to this embodiment, (A) an epoxy compound, (B) a polyester compound, (C) a polyfunctional amino compound, and (D) an acidic catalyst, A) an epoxy compound is a bisphenol A type epoxy compound, and (C) a polyfunctional amino compound includes a composition for an oligomer sealing layer, which is a melamine compound.
  • composition for an oligomer sealing layer As an example of the composition for an oligomer sealing layer according to this embodiment, (A) an epoxy compound, (B) a polyester compound, (C) a polyfunctional amino compound, and (D) an acidic catalyst,
  • the A) epoxy compound is a bisphenol A type epoxy compound, the weight average molecular weight (Mw) of the (A) epoxy compound is 1 ⁇ 10 4 or more and 5 ⁇ 10 4 or less, and (C) the polyfunctional amino compound is melamine
  • Mw weight average molecular weight of the (A) epoxy compound is 1 ⁇ 10 4 or more and 5 ⁇ 10 4 or less
  • the polyfunctional amino compound is melamine
  • composition for an oligomer sealing layer As an example of the composition for an oligomer sealing layer according to this embodiment, (A) an epoxy compound, (B) a polyester compound, (C) a polyfunctional amino compound, and (D) an acidic catalyst, A)
  • the epoxy compound is a bisphenol A type epoxy compound, the number average molecular weight (Mn) of the (B) polyester compound is 500 or more and 10,000 or less, and the glass transition temperature Tg of the (B) polyester compound is 0 ° C. or more.
  • the composition for oligomer sealing layers which is 50 degrees C or less and (C) polyfunctional amino compound is a melamine compound is mentioned.
  • composition for an oligomer sealing layer As an example of the composition for an oligomer sealing layer according to this embodiment, (A) an epoxy compound, (B) a polyester compound, (C) a polyfunctional amino compound, and (D) an acidic catalyst,
  • the A) epoxy compound is a bisphenol A type epoxy compound, the weight average molecular weight (Mw) of the (A) epoxy compound is 1 ⁇ 10 4 or more and 5 ⁇ 10 4 or less, and (B) the number average molecular weight of the polyester compound ( Mn) is 500 or more and 10,000 or less, (B)
  • the glass transition temperature Tg of the polyester compound is 0 ° C. or more and 50 ° C. or less, and
  • the polyfunctional amino compound is a melamine compound for the oligomer sealing layer.
  • the thickness of the oligomer sealing layer 13 is preferably 50 nm or more and 500 nm or less, and more preferably 80 nm or more and 300 nm or less. If the thickness of the oligomer sealing layer 13 is 50 nm or more, the penetration of the oligomer into the pressure-sensitive adhesive layer 12 can be effectively prevented. If the thickness of the oligomer sealing layer 13 is 500 nm or less, it will become easy to wind up when the adhesive sheet 10 is wound around a core material in roll shape. Examples of the material of the core material include paper, plastic, and metal.
  • the pressure-sensitive adhesive sheet 10 preferably exhibits the following adhesive strength after heating.
  • the pressure-sensitive adhesive sheet 10 is adhered to an adherend (copper foil or polyimide film), heated at 100 ° C. and 30 minutes, subsequently heated at 180 ° C. and 30 minutes, and further at 190 ° C. and 1 ° C.
  • the adhesive strength of the adhesive layer 12 to the copper foil at room temperature and the adhesive strength of the adhesive layer 12 to the polyimide film at room temperature are 0.7 N / 25 mm or more and 2.0 N / 25 mm, respectively. The following is preferable.
  • the adhesive sheet 10 can be prevented from peeling off from the adherend when the substrate or adherend is deformed by heating. Moreover, if the adhesive force after a heating is 2.0 N / 25mm or less, peeling force will not become high too much and it will be easy to peel the adhesive sheet 10 from a to-be-adhered body.
  • room temperature is a temperature of 22 ° C. or higher and 24 ° C. or lower.
  • the adhesive strength is a value measured by a 180 ° peeling method at a pulling speed of 300 mm / min and a width of 25 mm of the adhesive sheet.
  • pressure-sensitive adhesive composition includes the following pressure-sensitive adhesive compositions, but the present invention is not limited to such examples.
  • An example of the pressure-sensitive adhesive composition according to this embodiment includes an acrylic copolymer, a pressure-sensitive adhesive aid, and a crosslinking agent, and the acrylic copolymer contains at least 2-ethylhexyl acrylate and a carboxyl group.
  • An example of the pressure-sensitive adhesive composition according to this embodiment includes an acrylic copolymer, a pressure-sensitive adhesive aid, and a crosslinking agent, and the acrylic copolymer contains at least 2-ethylhexyl acrylate and a carboxyl group.
  • a pressure-sensitive adhesive composition which is an acrylic copolymer obtained by copolymerizing a monomer and a hydroxyl group-containing monomer, wherein the adhesion assistant is a hydroxylated hydrogenated polybutadiene at both terminals, and the crosslinking agent is an isocyanate crosslinking agent Things.
  • an acrylic copolymer, an adhesion assistant, and a crosslinking agent are included, and the acrylic copolymer includes at least 2-ethylhexyl acrylate, acrylic acid, And an acrylic copolymer obtained by copolymerizing 2-hydroxyethyl acrylate, wherein the adhesion assistant contains a rubber-based material having a reactive group as a main component, and the crosslinking agent is an isocyanate-based crosslinking.
  • a pressure-sensitive adhesive composition which is an agent is mentioned.
  • an acrylic copolymer, an adhesion assistant, and a crosslinking agent are included, and the acrylic copolymer includes at least 2-ethylhexyl acrylate, acrylic acid, and A pressure-sensitive adhesive composition which is an acrylic copolymer obtained by copolymerizing 2-hydroxyethyl acrylate, wherein the pressure-sensitive adhesive aid is a hydroxylated hydrogenated polybutadiene at both ends, and the cross-linking agent is an isocyanate-based cross-linking agent Things.
  • the acrylic copolymer includes at least 2-ethylhexyl acrylate, a carboxyl group-containing monomer, a hydroxyl group-containing monomer, and a monomer having a nitrogen atom-containing ring.
  • An acrylic copolymer obtained by polymerization is also preferred.
  • the acrylic copolymer contains at least 2-ethylhexyl acrylate, acrylic acid, 2-hydroxyethyl acrylate, and N- (meth) acryloylmorpholine.
  • An acrylic copolymer obtained by copolymerization is also preferred.
  • the proportion of the copolymer component derived from 2-ethylhexyl acrylate in the acrylic copolymer is 80% by mass or more and 95% by mass or less.
  • the proportion of the mass of the copolymer component derived from the group-containing monomer is preferably 1% by mass or less, and the remainder is preferably another copolymer component.
  • the other copolymer component is a copolymer derived from a hydroxyl group-containing monomer. It preferably contains a polymer component.
  • the manufacturing method of the adhesive sheet 10 is not particularly limited.
  • the adhesive sheet 10 is manufactured through the following processes. First, the composition for oligomer sealing layers is apply
  • the composition for oligomer sealing layer When the composition for oligomer sealing layer is applied to form the oligomer sealing layer 13, and when the pressure-sensitive adhesive composition is applied to form the pressure-sensitive adhesive layer 12, the composition for oligomer sealing layer and the pressure-sensitive adhesive composition It is preferable to prepare a coating solution by diluting the product with an organic solvent.
  • organic solvent include aromatic solvents, aliphatic solvents, ester solvents, ketone solvents, and alcohol solvents.
  • the aromatic solvent include benzene, toluene, and xylene.
  • the aliphatic solvent include normal hexane and normal heptane.
  • Examples of the ester solvent include ethyl acetate and butyl acetate.
  • Examples of the ketone solvent include methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, and cyclopentanone.
  • Examples of the alcohol solvent include isopropyl alcohol and methanol.
  • Examples of the coating method include spin coating, spray coating, bar coating, knife coating, roll knife coating, roll coating, blade coating, die coating, and gravure coating.
  • a crosslinking agent is blended in the pressure-sensitive adhesive composition, it is preferable to heat the coating film in order to promote the crosslinking reaction and improve the cohesive force.
  • the pressure-sensitive adhesive sheet 10 is used when sealing a semiconductor element.
  • the pressure-sensitive adhesive sheet 10 is not mounted on a metal lead frame, and is preferably used when sealing a semiconductor element that is stuck on the pressure-sensitive adhesive sheet 10.
  • the pressure-sensitive adhesive sheet 10 is not used when sealing a semiconductor element mounted on a metal lead frame, but seals a semiconductor element that is stuck to the pressure-sensitive adhesive layer 12.
  • a panel scale package Panel Scale Package
  • WLP wafer Level Package
  • the pressure-sensitive adhesive sheet 10 includes a step of attaching a frame member in which a plurality of openings are formed to the pressure-sensitive adhesive sheet 10; a step of attaching a semiconductor chip to the pressure-sensitive adhesive layer 12 exposed at the openings of the frame member; It is preferably used in a process having a step of covering the semiconductor chip with a sealing resin and a step of thermosetting the sealing resin.
  • FIGS. 2A to 2E are schematic views illustrating the method for manufacturing the semiconductor device according to the present embodiment.
  • the manufacturing method of the semiconductor device according to the present embodiment includes a step of attaching the frame member 20 in which a plurality of openings 21 are formed on the adhesive sheet 10 (adhesive sheet attaching step), and an opening 21 of the frame member 20.
  • a step of bonding the semiconductor chip CP to the exposed adhesive layer 12 (bonding step), a step of covering the semiconductor chip CP with the sealing resin 30 (sealing step), and a step of thermosetting the sealing resin 30 ( A thermosetting step) and a step of peeling the pressure-sensitive adhesive sheet 10 (peeling step) are carried out after thermosetting.
  • bonding step a step of bonding the semiconductor chip CP to the exposed adhesive layer 12
  • sealing step a step of covering the semiconductor chip CP with the sealing resin 30
  • a step of thermosetting the sealing resin 30 A thermosetting step
  • peeling the pressure-sensitive adhesive sheet 10 peeling step
  • the frame member 20 is formed in a lattice shape and has a plurality of openings 21.
  • the frame member 20 is preferably formed of a material having heat resistance. Examples of the material of the frame member 20 include metals such as copper and stainless steel, and heat resistant resins such as polyimide resin and glass epoxy resin.
  • the opening 21 is a hole that penetrates the front and back surfaces of the frame member 20.
  • the shape of the opening 21 is not particularly limited as long as the semiconductor chip CP can be accommodated in the frame.
  • the depth of the hole of the opening 21 is not particularly limited as long as the semiconductor chip CP can be accommodated.
  • FIG. 2B shows a schematic diagram for explaining a step of attaching the semiconductor chip CP to the adhesive layer 12.
  • the semiconductor chip CP is manufactured, for example, by performing a back grinding process for grinding the back surface of the semiconductor wafer on which the circuit is formed and a dicing process for dividing the semiconductor wafer into individual pieces.
  • a semiconductor chip CP semiconductor element
  • the dicing apparatus is not particularly limited, and a known dicing apparatus can be used.
  • the dicing conditions are not particularly limited. Note that a laser dicing method or a stealth dicing method may be used instead of the dicing method using a dicing blade.
  • an expanding process may be performed in which the dicing sheet is extended to widen the interval between the plurality of semiconductor chips CP.
  • the semiconductor chip CP can be picked up using a conveying means such as a collet. Further, by performing the expanding process, the adhesive force of the adhesive layer of the dicing sheet is reduced, and the semiconductor chip CP can be easily picked up.
  • the energy ray polymerizable compound is blended in the adhesive composition of the dicing sheet or the adhesive layer, the energy ray polymerizable compound is applied to the adhesive layer by irradiating the adhesive layer from the substrate side of the dicing sheet. Harden.
  • the energy ray polymerizable compound When the energy ray polymerizable compound is cured, the cohesive force of the adhesive layer is increased, and the adhesive force of the adhesive layer can be reduced.
  • the energy rays include ultraviolet rays (UV) and electron beams (EB), and ultraviolet rays are preferable.
  • UV ultraviolet rays
  • EB electron beams
  • the energy beam irradiation may be performed at any stage after the semiconductor wafer is pasted and before the semiconductor chip is peeled off (pickup). For example, the energy beam may be irradiated before or after dicing, or the energy beam may be irradiated after the expanding step.
  • the material of the sealing resin 30 is a thermosetting resin, and examples thereof include an epoxy resin.
  • the epoxy resin used as the sealing resin 30 may include, for example, a phenol resin, an elastomer, an inorganic filler, a curing accelerator, and the like.
  • the method for covering the semiconductor chip CP and the frame member 20 with the sealing resin 30 is not particularly limited. In the present embodiment, an embodiment using a sheet-like sealing resin 30 will be described as an example.
  • the sheet-shaped sealing resin 30 is placed so as to cover the semiconductor chip CP and the frame member 20, and the sealing resin 30 is heated and cured to form the sealing resin layer 30A. In this way, the semiconductor chip CP and the frame member 20 are embedded in the sealing resin layer 30A.
  • the sheet-shaped sealing resin 30 it is preferable to seal the semiconductor chip CP and the frame member 20 by a vacuum laminating method. By this vacuum laminating method, it is possible to prevent a gap from being generated between the semiconductor chip CP and the frame member 20.
  • the temperature condition range for heating by the vacuum laminating method is, for example, 80 ° C. or more and 120 ° C. or less.
  • a laminated sheet in which the sheet-shaped sealing resin 30 is supported by a resin sheet such as polyethylene terephthalate may be used.
  • the resin sheet may be peeled off from the sealing resin 30 and the sealing resin 30 may be heated and cured.
  • Examples of such a laminated sheet include an ABF film (manufactured by Ajinomoto Fine Techno Co., Ltd.).
  • a transfer molding method may be employed.
  • the semiconductor chip CP and the frame member 20 adhered to the pressure-sensitive adhesive sheet 10 are accommodated inside the mold of the sealing device.
  • a fluid resin material is injected into the mold to cure the resin material.
  • the heating and pressure conditions are not particularly limited.
  • a temperature of 150 ° C. or higher and a pressure of 4 MPa to 15 MPa are maintained for 30 seconds to 300 seconds.
  • the pressure is released, the cured product is taken out from the sealing device, and left in an oven, and a temperature of 150 ° C. or higher is maintained for 2 hours to 15 hours. In this way, the semiconductor chip CP and the frame member 20 are sealed.
  • the first heat pressing process may be performed before the process of thermosetting the sealing resin 30 (thermosetting process).
  • the semiconductor chip CP and the pressure-sensitive adhesive sheet 10 with the frame member 20 covered with the sealing resin 30 are sandwiched by plate members from both sides, and pressed under conditions of a predetermined temperature, time, and pressure. .
  • the sealing resin 30 is easily filled into the gap between the semiconductor chip CP and the frame member 20.
  • corrugation of 30 A of sealing resin layers comprised with the sealing resin 30 can also be planarized by implementing a heat press process.
  • the sealing body 50 When the pressure-sensitive adhesive sheet 10 is peeled after the thermosetting step, the semiconductor chip CP and the frame member 20 sealed with the sealing resin 30 are obtained. Hereinafter, this may be referred to as a sealing body 50.
  • FIG. 2D The schematic diagram explaining the process of sticking the reinforcing member 40 to the sealing body 50 is shown by FIG. 2D.
  • a rewiring process and a bumping process for forming a rewiring layer on the exposed circuit surface of the semiconductor chip CP are performed.
  • a process (reinforcing member attaching process) of attaching the reinforcing member 40 to the sealing body 50 is performed as necessary. May be.
  • FIG. As illustrated in FIG. 2D, the sealing body 50 is supported in a state of being sandwiched between the adhesive sheet 10 and the reinforcing member 40.
  • the reinforcing member 40 includes a heat-resistant reinforcing plate 41 and a heat-resistant adhesive layer 42.
  • the reinforcing plate 41 include a plate-like member containing a heat resistant resin such as a glass epoxy resin.
  • the adhesive layer 42 adheres the reinforcing plate 41 and the sealing body 50.
  • the adhesive layer 42 is appropriately selected according to the material of the reinforcing plate 41 and the sealing resin layer 30A.
  • the adhesive layer 42 is sandwiched between the sealing resin layer 30A of the sealing body 50 and the reinforcing plate 41, and is further sandwiched between the reinforcing plate 41 side and the adhesive sheet 10 side by plate members, respectively. It is preferable to carry out the second hot pressing step of pressing under the conditions of temperature, time and pressure.
  • the sealing body 50 and the reinforcing member 40 are temporarily fixed by the second heating press process. In order to cure the adhesive layer 42 after the second heat pressing step, it is preferable to heat the temporarily fixed sealing body 50 and the reinforcing member 40 under conditions of a predetermined temperature and time.
  • the conditions for heat curing are appropriately set according to the material of the adhesive layer 42, and are, for example, 185 ° C., 80 minutes, and 2.4 MPa.
  • a metal plate such as stainless steel can be used as the plate-like member.
  • FIG. 2E The schematic explaining the process of peeling the adhesive sheet 10 is shown by FIG. 2E.
  • the adhesive sheet 10 when the base material 11 of the adhesive sheet 10 is bendable, the adhesive sheet 10 can be easily peeled from the frame member 20, the semiconductor chip CP, and the sealing resin layer 30A while being bent.
  • peeling angle (theta) is not specifically limited, It is preferable to peel the adhesive sheet 10 with peeling angle (theta) of 90 degree
  • the peeling angle ⁇ is 90 degrees or more, the pressure-sensitive adhesive sheet 10 can be easily peeled from the frame member 20, the semiconductor chip CP, and the sealing resin layer 30A.
  • the peeling angle ⁇ is preferably 90 degrees or more and 180 degrees or less, and more preferably 135 degrees or more and 180 degrees or less.
  • the reinforcing member 40 When the reinforcing member 40 is attached, the reinforcing member 40 is peeled off from the sealing body 50 at the stage where the support by the reinforcing member 40 becomes unnecessary after the rewiring process and the bumping process are performed. Thereafter, the sealing body 50 is separated into individual semiconductor chips CP (individualization step).
  • a method for dividing the sealing body 50 into individual pieces is not particularly limited.
  • the semiconductor wafer can be separated into pieces by the same method as that used when dicing the semiconductor wafer.
  • the step of dividing the sealing body 50 into pieces may be performed in a state where the sealing body 50 is adhered to a dicing sheet or the like.
  • the pressure-sensitive adhesive sheet 10 that can prevent the surface of the adherend from being contaminated even after a process in which high temperature conditions are imposed.
  • Examples of the adherend to which the adhesive layer 12 is in contact include the semiconductor chip CP and the frame member 20.
  • the semiconductor chip CP and the frame member 20 are exposed to high temperature conditions while being in contact with the pressure-sensitive adhesive layer 12. Since the pressure-sensitive adhesive sheet 10 includes the oligomer sealing layer 13 between the base material 11 and the pressure-sensitive adhesive layer 12, the pressure-sensitive adhesive layer of the oligomer in the base material 11 even when the pressure-sensitive adhesive sheet 10 is exposed to high temperature conditions. Intrusion into 12 is prevented. Therefore, according to the pressure-sensitive adhesive sheet 10, it is possible to prevent contamination of the surfaces of the semiconductor chip CP and the frame member 20.
  • 2nd embodiment is different from 1st embodiment by the point which has an oligomer sealing layer on both surfaces of the base material of an adhesive sheet. Since the second embodiment is the same as the first embodiment in other points, the description is omitted or simplified.
  • FIG. 10 A of adhesive sheets The cross-sectional schematic of 10 A of adhesive sheets which concern on 2nd embodiment is shown by FIG. 10 A of adhesive sheets have the base material 11, the adhesive layer 12, the oligomer sealing layer 13 (1st oligomer sealing layer), and the oligomer sealing layer 14 (2nd oligomer sealing layer).
  • 10 A of adhesive sheets have the oligomer sealing layers 13 and 14 on both surfaces (the 1st base material surface 11a and the 2nd base material surface 11b) of the base material 11, respectively.
  • the oligomer sealing layer 13 is laminated on the first base material surface 11a
  • the oligomer sealing layer 14 is laminated on the second base material surface 11b.
  • the first base material surface 11 a is covered with the oligomer sealing layer 13 and the second base material surface 11 b is covered with the oligomer sealing layer 14. Similar to the first embodiment, an oligomer sealing layer 13 is provided between the base material 11 and the pressure-sensitive adhesive layer 12.
  • the shape of the pressure-sensitive adhesive sheet 10A can take any shape such as a sheet shape, a tape shape, and a label shape.
  • the oligomer sealing layer 13 (first oligomer sealing layer) is the same as in the first embodiment.
  • the oligomer sealing layer 14 (second oligomer sealing layer) is a layer for preventing oligomers that are heated and deposited on the second base material surface 11b of the base material 11 from adhering to and contaminating other members. is there.
  • the oligomer sealing layer 14 is preferably formed of the same material as the oligomer sealing layer 13.
  • the thickness of the oligomer sealing layer 14 is not particularly limited, and is preferably in the same range as the oligomer sealing layer 13 described in the first embodiment. As the thickness of the oligomer sealing layer is increased, the effect of the oligomer sealing is improved. For example, from the viewpoint of productivity and cost of the pressure-sensitive adhesive sheet, the thickness of the oligomer sealing layer 13 and the oligomer sealing layer 14 is 100 nm or more and 200 nm or less, or about 150 nm.
  • the manufacturing method of the pressure-sensitive adhesive sheet 10A is not particularly limited.
  • the adhesive sheet 10A is manufactured through the following steps. First, the composition for oligomer sealing layers is apply
  • the adhesive sheet 10A can also be used in the same manner as the adhesive sheet 10 according to the first embodiment, and can be used in the method for manufacturing a semiconductor device in the same manner as the adhesive sheet 10.
  • the pressure-sensitive adhesive sheet 10A As in the case of the pressure-sensitive adhesive sheet 10, it is possible to prevent the surface of the adherend from being contaminated even after a process in which high temperature conditions are imposed. Furthermore, according to the pressure-sensitive adhesive sheet 10A, the oligomer sealing layer 14 is also formed on the second base material surface 11b, so that the oligomer deposited on the second base material surface 11b adheres to members and devices other than the adherend. To prevent contamination. For example, in the method for manufacturing a semiconductor device, contamination of the plate-like member that comes into contact with the pressure-sensitive adhesive sheet 10A in the hot press process can be prevented.
  • the pressure-sensitive adhesive sheet may be a single sheet or may be provided in a state where a plurality of pressure-sensitive adhesive sheets are laminated.
  • the pressure-sensitive adhesive layer may be covered with a base material of another pressure-sensitive adhesive sheet to be laminated.
  • a long sheet may be sufficient as an adhesive sheet, and it may be provided in the state wound up by roll shape.
  • the pressure-sensitive adhesive sheet wound up in a roll shape can be used by being unwound from a roll and cut into a desired size.
  • the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet may be covered with a release sheet.
  • the release sheet is not particularly limited.
  • the release sheet preferably includes a release substrate and a release agent layer formed by applying a release agent on the release substrate.
  • the release sheet may be provided with a release agent layer only on one side of the release substrate, or may be provided with a release agent layer on both sides of the release substrate.
  • the release substrate include a paper substrate, a laminated paper obtained by laminating a thermoplastic resin such as polyethylene on the paper substrate, and a plastic film.
  • the paper substrate include glassine paper, coated paper, and cast coated paper.
  • plastic film examples include polyester films such as polyethylene terephthalate, polybutylene terephthalate, and polyethylene naphthalate, and polyolefin films such as polypropylene and polyethylene.
  • release agent examples include olefin resins, rubber elastomers (eg, butadiene resins, isoprene resins, etc.), long chain alkyl resins, alkyd resins, fluorine resins, and silicone resins.
  • the thickness of the release sheet is not particularly limited.
  • the thickness of the release sheet is usually from 20 ⁇ m to 200 ⁇ m, and preferably from 25 ⁇ m to 150 ⁇ m.
  • the thickness of the release agent layer is not particularly limited.
  • the thickness of the release agent layer is preferably 0.01 ⁇ m or more and 2.0 ⁇ m or less, and preferably 0.03 ⁇ m or more and 1.0 ⁇ m or less. More preferred.
  • the thickness of the plastic film is preferably 3 ⁇ m or more and 50 ⁇ m or less, and more preferably 5 ⁇ m or more and 40 ⁇ m or less.
  • the pressure-sensitive adhesive sheet having a release sheet is manufactured through the following steps, for example. First, a pressure-sensitive adhesive composition is applied on a release sheet to form a coating film. Next, the coating film is dried to form the pressure-sensitive adhesive layer 12. Moreover, the oligomer sealing layer 13 is formed on the first base material surface 11a of the base material 11 as described in the above embodiment. The pressure-sensitive adhesive layer 12 on the release sheet and the oligomer sealing layer 13 on the substrate 11 are bonded together. In the case of the embodiment having the oligomer sealing layer 14, the pressure-sensitive adhesive layer 12 and the oligomer sealing layer 13 are bonded together after the oligomer sealing layers 13 and 14 are formed on both surfaces of the substrate 11.
  • the sealing resin 30 is a thermosetting resin
  • the present invention is not limited to such a mode.
  • the sealing resin 30 may be an energy ray curable resin that is cured by energy rays such as ultraviolet rays.
  • the adhesive sheet 10 may be used in a method for manufacturing a semiconductor device that seals a semiconductor element without using a frame member.
  • a semiconductor chip was attached to the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet to obtain a pressure-sensitive adhesive sheet with a semiconductor chip.
  • This adhesive sheet with a semiconductor chip was heated under the conditions of 190 ° C. and 1 hour. After heating, the adhesive sheet was peeled off.
  • the adherend surface of the semiconductor chip after peeling was observed with a digital microscope (manufactured by Keyence Co., Ltd., digital microscope; VHX-1000) to confirm the presence or absence of residues. The observation magnification was 500 times. The case where a residue was not confirmed was determined as “A”, and the case where a residue was confirmed was determined as “B”.
  • coating oligomer sealing agent liquid The following (A) bisphenol A type epoxy compound, (B) polyester compound, (C) polyfunctional amino compound and (D) acidic catalyst are blended and stirred sufficiently.
  • the oligomer sealing agent liquid for coating which concerns on Example 1 (composition for oligomer sealing layers) was prepared.
  • oligomer sealing layer The prepared oligomer sealing agent liquid for coating was applied to a biaxially stretched polyethylene terephthalate film ("Diafoil T-100" (trade name) manufactured by Mitsubishi Plastics, Inc., thickness 50 ⁇ m, at 100 ° C. It was uniformly coated on one surface of storage elastic modulus 3.2 ⁇ 10 9 Pa) by the Mayer bar coating method so that the thickness after drying was 150 nm. The coated film was passed through the oven, and the coating film was cured by heating to obtain an oligomer sealing layer. As conditions for blowing hot air in the oven, the temperature was set to 150 ° C., the wind speed was set to 8 m / min, and the processing speed in the oven was adjusted so that the coated film passed through the oven in 20 seconds.
  • a biaxially stretched polyethylene terephthalate film (“Diafoil T-100" (trade name) manufactured by Mitsubishi Plastics, Inc., thickness 50 ⁇ m, at 100 ° C. It was uniformly coated on one surface of storage elastic
  • Acrylic ester copolymer 40 parts by mass (solid content)
  • the acrylic ester copolymer was prepared by copolymerizing 92.8% by mass of 2-ethylhexyl acrylate, 7.0% by mass of 2-hydroxyethyl acrylate, and 0.2% by mass of acrylic acid.
  • -Adhesion aid hydroxylated hydrogenated polybutadiene at both ends (manufactured by Nippon Soda Co., Ltd .; GI-1000), 5 parts by mass (solid content)
  • Crosslinking agent Aliphatic isocyanate having hexamethylene diisocyanate (isocyanurate-type modified product of hexamethylene diisocyanate; manufactured by Nippon Polyurethane Industry Co., Ltd .; Coronate HX), 3.5 parts by mass (solid content)
  • Diluting solvent Methyl ethyl ketone was used, and the solid content concentration of the coating adhesive solution was adjusted to 30% by mass.
  • Example 2 The pressure-sensitive adhesive sheet according to Example 2 was produced in the same manner as in Example 1 except that the polymer contained in the pressure-sensitive adhesive layer was different from that in Example 1.
  • the polymer used in Example 2 was composed of 80.8% by mass of 2-ethylhexyl acrylate, 7% by mass of 2-hydroxyethyl acrylate, 12% by mass of 4-acryloylmorpholine, and 0.2% by mass of acrylic acid. Prepared by copolymerization.
  • the pressure-sensitive adhesive sheet according to Comparative Example 1 is the same as Example 1 except that the pressure-sensitive adhesive aid contained in the pressure-sensitive adhesive layer is different from that in Example 1, the base material is different, and the oligomer sealing layer is not provided. It was prepared.
  • the adhesion promoter used in Comparative Example 1 is tributyl acetyl citrate [manufactured by Taoka Chemical Industry Co., Ltd.]. Note that tributyl acetylcitrate does not have the aforementioned reactive group.
  • the base material used in Comparative Example 1 is a polyethylene terephthalate film [manufactured by Mitsubishi Plastics; PET 50T-100, thickness 50 ⁇ m, storage elastic modulus at 100 ° C. 3.2 ⁇ 10 9 Pa].
  • the pressure-sensitive adhesive layer prepared on the surface of the release film was bonded to the base material to obtain a pressure-sensitive adhesive sheet according to Comparative Example 1.
  • Comparative Example 2 The pressure-sensitive adhesive sheet according to Comparative Example 2 was prepared in the same manner as in Comparative Example 1 except that the pressure-sensitive adhesive aid contained in the pressure-sensitive adhesive layer was different from that in Comparative Example 1.
  • the tackifier used in Comparative Example 2 is a hydroxylated hydrogenated polybutadiene at both ends (manufactured by Nippon Soda Co., Ltd .; GI-1000).
  • Comparative Example 3 The pressure-sensitive adhesive sheet according to Comparative Example 3 is different from Example 1 in that the pressure-sensitive adhesive contained in the pressure-sensitive adhesive layer is different, the thickness of the pressure-sensitive adhesive layer is different, the base material is different, and there is no oligomer sealing layer. Other than that, it was produced in the same manner as in Example 1. In Comparative Example 3, a silicone adhesive was used.
  • Silicone-based adhesive Ad1 (SD4580PSA) 18 parts by mass (solid content), Silicone-based adhesive Ad2 (SD4587L) 40 parts by mass (solid content), Catalyst Cat1 (NC-25 CAT) 0.3 part by mass (solid content), The catalyst Cat2 (CAT-SRX-212) 0.65 parts by mass (solid content) and the primer (BY24-712) 5 parts by mass (solid content) were blended and stirred thoroughly to give an adhesive solution for application (adhesion) Agent composition) was prepared.
  • the materials used for the pressure-sensitive adhesive composition of Comparative Example 3 are all manufactured by Toray Dow Corning Co., Ltd.
  • the pressure-sensitive adhesive liquid for coating according to Comparative Example 3 was applied to the release layer surface side of the release film and dried so that the thickness after drying was 30 ⁇ m, thereby preparing a pressure-sensitive adhesive layer. Drying conditions were 130 ° C. and 2 minutes.
  • the base material used in Comparative Example 3 was a polyethylene terephthalate film [Mitsubishi Resin Co., Ltd .; Diafoil PET50 T-100, thickness 50 ⁇ m, storage elastic modulus at 100 ° C. 3.2 ⁇ 10 9 Pa].
  • the pressure-sensitive adhesive layer prepared on the surface of the release film was bonded to the base material to obtain a pressure-sensitive adhesive sheet according to Comparative Example 3.
  • Table 1 shows the evaluation results of the pressure-sensitive adhesive sheets according to Example 1, Example 2, and Comparative Examples 1 to 3.
  • 10, 10A adhesive sheet, 11: base material, 12: adhesive layer, 13, 14: oligomer sealing layer.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Computer Hardware Design (AREA)
  • Materials Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • General Physics & Mathematics (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Power Engineering (AREA)
  • Adhesives Or Adhesive Processes (AREA)
  • Adhesive Tapes (AREA)
  • Encapsulation Of And Coatings For Semiconductor Or Solid State Devices (AREA)
  • Laminated Bodies (AREA)
  • Die Bonding (AREA)
  • Sealing Material Composition (AREA)
PCT/JP2016/075604 2015-09-01 2016-09-01 粘着シート WO2017038917A1 (ja)

Priority Applications (4)

Application Number Priority Date Filing Date Title
KR1020177034192A KR101930197B1 (ko) 2015-09-01 2016-09-01 점착 시트
JP2017518161A JP6148805B1 (ja) 2015-09-01 2016-09-01 粘着シート
CN201680030959.7A CN107636100B (zh) 2015-09-01 2016-09-01 粘合片
KR1020187035736A KR102612643B1 (ko) 2015-09-01 2016-09-01 점착 시트

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015-172397 2015-09-01
JP2015172397 2015-09-01

Publications (1)

Publication Number Publication Date
WO2017038917A1 true WO2017038917A1 (ja) 2017-03-09

Family

ID=58187756

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/075604 WO2017038917A1 (ja) 2015-09-01 2016-09-01 粘着シート

Country Status (5)

Country Link
JP (2) JP6148805B1 (zh)
KR (2) KR102612643B1 (zh)
CN (2) CN107636100B (zh)
TW (2) TWI621684B (zh)
WO (1) WO2017038917A1 (zh)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2019029423A (ja) * 2017-07-26 2019-02-21 リンテック株式会社 剥離フィルム
WO2020031543A1 (ja) * 2018-08-10 2020-02-13 リンテック株式会社 粘着シート用基材及び電子部品加工用粘着シート
WO2020053949A1 (ja) * 2018-09-11 2020-03-19 三井化学東セロ株式会社 粘着性フィルムおよび電子装置の製造方法
WO2021132486A1 (ja) * 2019-12-25 2021-07-01 日東電工株式会社 積層体

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019163568A1 (ja) * 2018-02-22 2019-08-29 リンテック株式会社 フィルム状焼成材料、及び支持シート付フィルム状焼成材料
SG11202009374YA (en) * 2018-03-30 2020-10-29 Mitsui Chemicals Tohcello Inc Method for manufacturing electronic device
CN112352027A (zh) * 2018-06-13 2021-02-09 琳得科株式会社 粘合片
JP7084671B2 (ja) * 2018-07-30 2022-06-15 フジコピアン株式会社 手裂き可能な吸着テープ
JP7223586B2 (ja) * 2019-01-31 2023-02-16 日東電工株式会社 透明導電性フィルム積層体
JP7458374B2 (ja) * 2019-03-26 2024-03-29 リンテック株式会社 剥離シート
JP7285612B2 (ja) * 2019-06-12 2023-06-02 フジコピアン株式会社 耐熱保護用貼着フィルム

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008045091A (ja) * 2006-08-21 2008-02-28 Nitto Denko Corp 加工用粘着シート
JP2013038098A (ja) * 2011-08-03 2013-02-21 Nitto Denko Corp ダイシング・ダイボンドフィルム
JP2014239151A (ja) * 2013-06-07 2014-12-18 日東電工株式会社 アンダーフィル材、積層シート及び半導体装置の製造方法

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10214801A (ja) * 1997-01-31 1998-08-11 Teijin Ltd ダイシングテープ
JP4002736B2 (ja) 2001-03-21 2007-11-07 株式会社巴川製紙所 半導体装置組立用マスクシートおよび半導体装置の組み立て方法
JP4837490B2 (ja) * 2006-08-22 2011-12-14 日東電工株式会社 加工用粘着シート
KR101387706B1 (ko) * 2007-08-17 2014-04-23 삼성전자주식회사 반도체 칩 패키지, 그 제조 방법 및 이를 포함하는 전자소자
KR20090121254A (ko) * 2008-05-20 2009-11-25 주식회사 엘지화학 점착 필름, 다이싱 다이본딩 필름 및 반도체 웨이퍼
JP5632695B2 (ja) * 2009-11-26 2014-11-26 日東電工株式会社 ダイシングフィルム付き接着フィルム、及び、該ダイシングフィルム付き接着フィルムを用いた半導体装置の製造方法
JP5144634B2 (ja) * 2009-12-22 2013-02-13 日東電工株式会社 基板レス半導体パッケージ製造用耐熱性粘着シート、及びその粘着シートを用いる基板レス半導体パッケージ製造方法
KR20150001804A (ko) * 2010-03-31 2015-01-06 후루카와 덴키 고교 가부시키가이샤 다이싱 시트
JP5612403B2 (ja) * 2010-09-09 2014-10-22 日東電工株式会社 樹脂封止用粘着テープ及び樹脂封止型半導体装置の製造方法
TW201305306A (zh) * 2011-07-25 2013-02-01 Nitto Denko Corp 接著片及其用途
JP5824402B2 (ja) * 2012-04-02 2015-11-25 株式会社巴川製紙所 半導体装置製造用マスクシート及びそれを用いた半導体装置の製造方法
JP5877122B2 (ja) * 2012-05-21 2016-03-02 藤森工業株式会社 表面処理フィルム、表面保護フィルム及びそれが貼り合わされた精密電気・電子部品
JP6042251B2 (ja) * 2013-03-28 2016-12-14 リンテック株式会社 粘着シート
US9822284B2 (en) * 2013-08-29 2017-11-21 Mitsui Chemicals Tohcello, Inc. Adhesive film and method for manufacturing semiconductor device

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008045091A (ja) * 2006-08-21 2008-02-28 Nitto Denko Corp 加工用粘着シート
JP2013038098A (ja) * 2011-08-03 2013-02-21 Nitto Denko Corp ダイシング・ダイボンドフィルム
JP2014239151A (ja) * 2013-06-07 2014-12-18 日東電工株式会社 アンダーフィル材、積層シート及び半導体装置の製造方法

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2019029423A (ja) * 2017-07-26 2019-02-21 リンテック株式会社 剥離フィルム
WO2020031543A1 (ja) * 2018-08-10 2020-02-13 リンテック株式会社 粘着シート用基材及び電子部品加工用粘着シート
JPWO2020031543A1 (ja) * 2018-08-10 2020-08-20 リンテック株式会社 粘着シート用基材及び電子部品加工用粘着シート
CN112585733A (zh) * 2018-08-10 2021-03-30 琳得科株式会社 粘合片用基材及电子部件加工用粘合片
KR20210043557A (ko) 2018-08-10 2021-04-21 린텍 가부시키가이샤 점착 시트용 기재 및 전자 부품 가공용 점착 시트
WO2020053949A1 (ja) * 2018-09-11 2020-03-19 三井化学東セロ株式会社 粘着性フィルムおよび電子装置の製造方法
WO2021132486A1 (ja) * 2019-12-25 2021-07-01 日東電工株式会社 積層体
EP4082779A4 (en) * 2019-12-25 2024-01-03 Nitto Denko Corp LAYER BODY

Also Published As

Publication number Publication date
KR102612643B1 (ko) 2023-12-11
CN107636100B (zh) 2019-11-22
TWI621684B (zh) 2018-04-21
JPWO2017038917A1 (ja) 2017-09-21
CN110628349A (zh) 2019-12-31
KR101930197B1 (ko) 2018-12-17
TW201723119A (zh) 2017-07-01
KR20170136644A (ko) 2017-12-11
TWI734893B (zh) 2021-08-01
CN107636100A (zh) 2018-01-26
JP6853731B2 (ja) 2021-03-31
KR20180133949A (ko) 2018-12-17
JP2017197749A (ja) 2017-11-02
TW201821570A (zh) 2018-06-16
JP6148805B1 (ja) 2017-06-14

Similar Documents

Publication Publication Date Title
JP6148805B1 (ja) 粘着シート
JP6270736B2 (ja) 保護膜形成用フィルム
JP6268329B2 (ja) 粘着剤組成物及び粘着シート
JP6787900B2 (ja) 粘着シート
JP6220488B1 (ja) 粘着シート
JP6220487B1 (ja) 粘着シート
JPWO2016113998A1 (ja) 樹脂膜形成用シート、樹脂膜形成用複合シート、及びシリコンウエハの再生方法
TWI819016B (zh) 黏著薄片用基材及電子零件加工用黏著薄片
JP6713471B2 (ja) 粘着シート
WO2017038919A1 (ja) 粘着シート
JP6220481B2 (ja) 粘着シート
JP2019135753A (ja) 粘着シート及び半導体装置の製造方法

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2017518161

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16841946

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20177034192

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16841946

Country of ref document: EP

Kind code of ref document: A1