WO2020053949A1 - 粘着性フィルムおよび電子装置の製造方法 - Google Patents

粘着性フィルムおよび電子装置の製造方法 Download PDF

Info

Publication number
WO2020053949A1
WO2020053949A1 PCT/JP2018/033579 JP2018033579W WO2020053949A1 WO 2020053949 A1 WO2020053949 A1 WO 2020053949A1 JP 2018033579 W JP2018033579 W JP 2018033579W WO 2020053949 A1 WO2020053949 A1 WO 2020053949A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive
resin layer
adhesive resin
adhesive film
electronic component
Prior art date
Application number
PCT/JP2018/033579
Other languages
English (en)
French (fr)
Inventor
宏嘉 栗原
五十嵐　康二
Original Assignee
三井化学東セロ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三井化学東セロ株式会社 filed Critical 三井化学東セロ株式会社
Priority to CN201880097408.1A priority Critical patent/CN112673465A/zh
Priority to PCT/JP2018/033579 priority patent/WO2020053949A1/ja
Priority to KR1020217008545A priority patent/KR102436952B1/ko
Priority to EP18933150.7A priority patent/EP3852134A4/en
Priority to SG11202102426TA priority patent/SG11202102426TA/en
Publication of WO2020053949A1 publication Critical patent/WO2020053949A1/ja

Abstract

本発明の粘着性フィルム（５０）は、電子装置の製造工程において封止材により電子部品を封止する際に上記電子部品を仮固定するために用いられる粘着性フィルムであって、上記電子部品を仮固定するための粘着性樹脂層（Ａ）と、支持基板に貼り付けるために用いられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、粘着性樹脂層（Ａ）と粘着性樹脂層（Ｂ）との間に設けられた中間層（Ｃ）と、を備え、中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ'が１．０×１０５Ｐａ以上８．０×１０６Ｐａ以下であり、かつ、中間層（Ｃ）の１２０℃における損失正接（ｔａｎδ）が０．１以下である。

Description

粘着性フィルムおよび電子装置の製造方法
　本発明は、粘着性フィルムおよび電子装置の製造方法に関する。
　電子装置（例えば、半導体装置）の小型化・軽量化を図ることができる技術として、ファンアウト型ＷＬＰ（ウエハレベルパッケージ）が開発されている。
　ファンアウト型ＷＬＰの作製方法のひとつであるｅＷＬＢ（Embedded Wafer Level Ball Grid Array）では、支持基板に貼り付けた粘着性フィルム上に、半導体チップ等の複数の電子部品を離間させた状態で仮固定し、封止材により複数の電子部品を一括封止する手法が取られる。ここで、粘着性フィルムは、封止工程等においては電子部品および支持基板に固着させる必要があり、封止後は支持基板とともに封止された電子部品から除去する必要がある。
　このようなファンアウト型ＷＬＰの製造方法に関する技術としては、例えば、特許文献１（特開２０１１－１３４８１１号）に記載のものが挙げられる。
　特許文献１には、基板レス半導体チップを樹脂封止する際に、貼着して使用される半導体装置製造用耐熱性粘着シートであって、上記耐熱性粘着シートは基材層と粘着剤層とを有し、該粘着剤層は貼り合わせ後の対ＳＵＳ３０４粘着力が０．５Ｎ／２０ｍｍ以上であり、樹脂封止工程完了時点に至るまでに受ける刺激により硬化して、対パッケージ剥離力が２．０Ｎ／２０ｍｍ以下になる層であることを特徴とする半導体装置製造用耐熱性粘着シートが記載されている。
特開２０１１－１３４８１１号公報
　本発明者らの検討によれば、支持基板に貼り付けた粘着性フィルム上に電子部品を配置して封止材により電子部品を封止し、その後支持基板から粘着性フィルムを剥離する際に、支持基板側に粘着性フィルムの粘着性樹脂層の一部（以下、糊とも呼ぶ。）が残ってしまう場合がある（以下、糊残りとも呼ぶ。）ことが明らかになった。
　本発明は上記事情に鑑みてなされたものであり、支持基板から粘着性フィルムを剥離する際の支持基板側の糊残りを抑制することが可能な電子部品仮固定用粘着性フィルムを提供するものである。
　本発明者らは、上記課題を達成するために鋭意検討を重ねた。その結果、電子部品を仮固定するための粘着性樹脂層（Ａ）と、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）との間に、特定の弾性率および損失正接（ｔａｎδ）を有する中間層（Ｃ）を設けることにより、支持基板から粘着性フィルムを剥離する際の支持基板側の糊残りを抑制することができることを見出して、本発明を完成させた。
　本発明によれば、以下に示す粘着性フィルムおよび電子装置の製造方法が提供される。
［１］
　電子装置の製造工程において封止材により電子部品を封止する際に上記電子部品を仮固定するために用いられる粘着性フィルムであって、
　上記電子部品を仮固定するための粘着性樹脂層（Ａ）と、
　支持基板に貼り付けるために用いられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、
　上記粘着性樹脂層（Ａ）と上記粘着性樹脂層（Ｂ）との間に設けられた中間層（Ｃ）と、
を備え、
　上記中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’が１．０×１０５Ｐａ以上８．０×１０６Ｐａ以下であり、かつ、上記中間層（Ｃ）の１２０℃における損失正接（ｔａｎδ）が０．１以下である粘着性フィルム。
［２］
　上記［１］に記載の粘着性フィルムにおいて、
　上記粘着性樹脂層（Ｂ）は加熱により粘着力が低下する粘着性フィルム。
［３］
　上記［２］に記載の粘着性フィルムにおいて、
　上記粘着性樹脂層（Ｂ）が気体発生成分および熱膨張性の微小球から選択される少なくとも一種を含む粘着性フィルム。
［４］
　上記［１］乃至［３］のいずれか一つに記載の粘着性フィルムにおいて、
　上記粘着性樹脂層（Ａ）中の気体発生成分および熱膨張性の微小球から選択される少なくとも一種の含有量が、上記粘着性樹脂層（Ａ）の全体を１００質量％としたとき、０．１質量％以下である粘着性フィルム。
［５］
　上記［１］乃至［４］のいずれか一つに記載の粘着性フィルムにおいて、
　上記封止材がエポキシ樹脂系封止材である粘着性フィルム。
［６］
　上記［１］乃至［５］のいずれか一つに記載の粘着性フィルムにおいて、
　上記粘着性樹脂層（Ａ）は（メタ）アクリル系粘着性樹脂を含む粘着性フィルム。
［７］
　上記［１］乃至［６］のいずれか一つに記載の粘着性フィルムと、上記粘着性フィルムの上記粘着性樹脂層（Ａ）に貼り付けられた電子部品と、上記粘着性フィルムの上記粘着性樹脂層（Ｂ）に貼り付けられた支持基板と、を備える構造体を準備する工程（１）と、
　封止材により上記電子部品を封止する工程（２）と、
　外部刺激を与えることにより上記粘着性樹脂層（Ｂ）の粘着力を低下させて上記構造体から上記支持基板を剥離する工程（３）と、
　上記電子部品から上記粘着性フィルムを剥離する工程（４）と、
を少なくとも備える電子装置の製造方法。
［８］
　上記［７］に記載の電子装置の製造方法において、
　上記封止材がエポキシ樹脂系封止材である電子装置の製造方法。
　本発明によれば、支持基板から粘着性フィルムを剥離する際の支持基板側の糊残りを抑制することが可能な電子部品仮固定用粘着性フィルムを提供することができる。
　上述した目的、およびその他の目的、特徴および利点は、以下に述べる好適な実施の形態、およびそれに付随する以下の図面によってさらに明らかになる。
本発明に係る実施形態の粘着性フィルムの構造の一例を模式的に示した断面図である。 本発明に係る実施形態の粘着性フィルムの構造の一例を模式的に示した断面図である。 本発明に係る実施形態の電子装置の製造方法の一例を模式的に示した断面図である。 本発明に係る実施形態の電子装置の製造方法の一例を模式的に示した断面図である。
　以下、本発明の実施形態について、図面を用いて説明する。なお、すべての図面において、同様な構成要素には共通の符号を付し、適宜説明を省略する。また、図は概略図であり、実際の寸法比率とは一致していない。また、数値範囲の「Ａ～Ｂ」は特に断りがなければ、Ａ以上Ｂ以下を表す。また、本実施形態において、「（メタ）アクリル」とはアクリル、メタクリルまたはアクリルおよびメタクリルの両方を意味する。
１．電子部品仮固定用粘着性フィルム
　以下、本実施形態に係る粘着性フィルム５０について説明する。
　図１および図２は、本発明に係る実施形態の粘着性フィルム５０の構造の一例を模式的に示した断面図である。
　図１に示すように、本実施形態に係る粘着性フィルム５０は、電子装置の製造工程において封止材により電子部品を封止する際に上記電子部品を仮固定するために用いられる粘着性フィルムであって、上記電子部品を仮固定するための粘着性樹脂層（Ａ）と、支持基板に貼り付けるために用いられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、粘着性樹脂層（Ａ）と粘着性樹脂層（Ｂ）との間に設けられた中間層（Ｃ）と、を備える。そして、中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’が１．０×１０５Ｐａ以上８．０×１０６Ｐａ以下であり、かつ、中間層（Ｃ）の１２０℃における損失正接（ｔａｎδ）が０．１以下である。
　上述したように、本発明者らの検討によれば、支持基板に貼り付けた粘着性フィルム上に電子部品を配置して封止材により電子部品を封止し、その後支持基板から粘着性フィルムを剥離する際に、支持基板側に糊残りが生じてしまう場合があることが明らかになった。
　この理由は明らかではないが、以下の理由が考えられる。まず、封止材により電子部品を封止する際に金枠（金型の外周部）が粘着性フィルムに接触し、その接触部位において粘着性フィルムおよび支持基板に応力が加わる。この応力が加わる部位において、支持基板と粘着性樹脂層との粘着力が高まり、支持基板から粘着性フィルムを剥離する際に、支持基板側に粘着性フィルムの粘着性樹脂層の一部が残る現象が起きてしまうと考えられる。
　本発明者らは、電子装置の製造工程において封止材により電子部品を封止する際に、支持基板側に生じる糊残りを抑制することが可能な電子部品仮固定用粘着性フィルムを実現するために、鋭意検討を重ねた。その結果、電子部品を仮固定するための粘着性樹脂層（Ａ）と、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、を備える粘着性フィルムにおいて、粘着性樹脂層（Ａ）と粘着性樹脂層（Ｂ）との間に特定の弾性率および損失正接（ｔａｎδ）を有する中間層（Ｃ）を設けることが有効という知見を得た。
　そして、本発明者らは上記知見を基にさらに鋭意検討した結果、中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’および損失正接（ｔａｎδ）を上記範囲とすることにより、支持基板から粘着性フィルムを剥離する際の支持基板側の糊残りを効果的に抑制することができることを初めて見出した。
　すなわち、本実施形態に係る粘着性フィルム５０は、粘着性樹脂層（Ａ）と粘着性樹脂層（Ｂ）との間に中間層（Ｃ）を設け、その中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’および損失正接（ｔａｎδ）を上記範囲とすることで、支持基板から粘着性フィルムを剥離する際の支持基板側の糊残りを効果的に抑制することが可能となる。
　本実施形態に係る粘着性フィルム５０を用いると支持基板から粘着性フィルムを剥離する際の支持基板側の糊残りを効果的に抑制することができる理由は明らかではないが、以下の理由が考えられる。
　まず、前述したように、封止材により電子部品を封止する際に金枠（金型の外周部）が粘着性フィルムに接触し、その接触部位において粘着性フィルムおよび支持基板に応力が加わる。この応力が加わる部位において、支持基板と粘着性樹脂層との粘着力が高まり、支持基板から粘着性フィルムを剥離する際に、支持基板側に粘着性フィルムの粘着性樹脂層の一部が残る現象が起きてしまうと考えられる。
　一方で、本実施形態に係る粘着性フィルム５０は、粘着性樹脂層（Ａ）と粘着性樹脂層（Ｂ）との間に１２０℃における貯蔵弾性率Ｅ’および損失正接（ｔａｎδ）が上記範囲内である中間層（Ｃ）が設けられている。この中間層（Ｃ）によって、金枠からの応力が緩和され、支持基板と粘着性樹脂層との粘着力の上昇を抑制でき、その結果、支持基板から粘着性フィルムを剥離する際の支持基板側の糊残りを効果的に抑制することができると考えられる。
　本実施形態に係る粘着性フィルム５０全体の厚さは、機械的特性と取扱い性のバランスの観点から、好ましくは１０μｍ以上１０００μｍ以下であり、より好ましくは２０μｍ以上５００μｍ以下である。
　本実施形態に係る粘着性フィルム５０は、電子装置の製造工程において電子部品を仮固定するためのフィルム等に用いることができ、特に、ファンアウト型ＷＬＰやファンアウト型ＰＬＰの製造工程において電子部品を仮固定するためのフィルムとして好適に用いることができる。
　次に、本実施形態に係る粘着性フィルム５０を構成する各層について説明する。
＜粘着性樹脂層（Ａ）＞
　粘着性樹脂層（Ａ）は、電子装置の製造工程において封止材により電子部品を封止する際に、電子部品の表面に接触して電子部品を仮固定するための層である。
　粘着性樹脂層（Ａ）は、粘着性樹脂を含む。
　粘着性樹脂としては、例えば、（メタ）アクリル系粘着性樹脂、シリコーン系粘着性樹脂、ウレタン系粘着性樹脂、オレフィン系粘着性樹脂、スチレン系粘着性樹脂等が挙げられる。
　これらの中でも粘着力の調整を容易にする観点等から、（メタ）アクリル系粘着性樹脂が好ましい。
　粘着性樹脂層（Ａ）としては、放射線により粘着力を低下させる放射線架橋型粘着性樹脂層を用いることもできる。放射線架橋型粘着性樹脂層は、放射線の照射により架橋して粘着力が著しく減少するため、電子部品から粘着性フィルム５０を剥離し易くなる。放射線としては、紫外線、電子線、赤外線等が挙げられる。
　放射線架橋型粘着性樹脂層としては、紫外線架橋型粘着性樹脂層が好ましい。
　粘着性樹脂層（Ａ）に使用される（メタ）アクリル系粘着性樹脂としては、例えば、（メタ）アクリル酸アルキルエステルモノマー単位（Ａ）および架橋剤と反応し得る官能基を有するモノマー単位（Ｂ）を含む共重合体が挙げられる。
　本実施形態において、（メタ）アクリル酸アルキルエステルとは、アクリル酸アルキルエステル、メタクリル酸アルキルエステル、またはこれらの混合物を意味する。
　本実施形態に係る（メタ）アクリル系粘着性樹脂は、例えば、（メタ）アクリル酸アルキルエステルモノマー（Ａ）および架橋剤と反応し得る官能基を有するモノマー（Ｂ）を含むモノマー混合物を共重合することにより得ることができる。
　（メタ）アクリル酸アルキルエステルモノマー単位（Ａ）を形成するモノマー（Ａ）としては、炭素数１～１２程度のアルキル基を有する（メタ）アクリル酸アルキルエステルが挙げられる。好ましくは炭素数１～８のアルキル基を有する（メタ）アクリル酸アルキルエステルである。具体的には、アクリル酸メチル、メタクリル酸メチル、アクリル酸エチル、メタクリル酸エチル、アクリル酸ブチル、メタクリル酸ブチル、アクリル酸－２－エチルヘキシル、メタクリル酸－２－エチルヘキシル等が挙げられる。これらは単独で使用してもよいし、２種以上を使用してもよい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂において、（メタ）アクリル酸アルキルエステルモノマー単位（Ａ）の含有量は、（メタ）アクリル系粘着性樹脂中の全モノマー単位の合計を１００質量％としたとき、１０質量％以上９８．９質量％以下であることが好ましく、８５質量％以上９５質量％以下であることがより好ましい。
　架橋剤と反応し得る官能基を有するモノマー（Ｂ）を形成するモノマー（Ｂ）としては、アクリル酸、メタクリル酸、イタコン酸、メサコン酸、シトラコン酸、フマル酸、マレイン酸、イタコン酸モノアルキルエステル、メサコン酸モノアルキルエステル、シトラコン酸モノアルキルエステル、フマル酸モノアルキルエステル、マレイン酸モノアルキルエステル、アクリル酸グリシジル、メタクリル酸グリシジル、アクリル酸－２－ヒドロキシエチル、メタクリル酸－２－ヒドロキシエチル、アクリルアミド、メタクリルアミド、ターシャル－ブチルアミノエチルアクリレート、ターシャル－ブチルアミノエチルメタクリレート等が挙げられる。好ましくは、アクリル酸、メタクリル酸、アクリル酸－２－ヒドロキシエチル、メタクリル酸－２－ヒドロキシエチル、アクリルアミド、メタクリルアミド等である。これらは単独で使用してもよいし、２種以上を使用してもよい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂において、モノマー単位（Ｂ）の含有量は、（メタ）アクリル系粘着性樹脂中の全モノマー単位の合計を１００質量％としたとき、１質量％以上４０質量％以下であることが好ましく、１質量％以上２０質量％以下であることがより好ましく、１質量％以上１０質量％以下であることがさらに好ましい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂は、モノマー単位（Ａ）およびモノマー単位（Ｂ）以外に、２官能性モノマー（Ｃ）や界面活性剤としての性質を有する特定のコモノマー（以下、重合性界面活性剤と称する）単位をさらに含んでもよい。
　重合性界面活性剤は、モノマー（Ａ）、モノマー（Ｂ）およびモノマー（Ｃ）と共重合する性質を有すると共に、乳化重合する場合には乳化剤としての作用を有する。
　２官能性モノマー単位（Ｃ）を形成するモノマー（Ｃ）としては、メタクリル酸アリル、アクリル酸アリル、ジビニルベンゼン、メタクリル酸ビニル、アクリル酸ビニル、トリメチロールプロパントリ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、テトラエチレングリコールジ（メタ）アクリレートや、例えば、両末端がジアクリレートまたはジメタクリレートで主鎖の構造がプロピレングリコール型（例えば、日本油脂（株）製、商品名；ＰＤＰ－２００、同ＰＤＰ－４００、同ＡＤＰ－２００、同ＡＤＰ－４００）、テトラメチレングリコール型（例えば、日本油脂（株）製、商品名；ＡＤＴ－２５０、同ＡＤＴ－８５０）およびこれらの混合型（例えば、日本油脂（株）製、商品名：ＡＤＥＴ－１８００、同ＡＤＰＴ－４０００）であるもの等が挙げられる。
　本実施形態に係る（メタ）アクリル系粘着性樹脂において、モノマー単位（Ｃ）の含有量は、（メタ）アクリル系粘着性樹脂中の全モノマー単位の合計を１００質量％としたとき、０．１質量％以上３０質量％以下であることが好ましく、０．１質量％以上５質量％以下であることがより好ましい。
　重合性界面活性剤の例としては、例えば、ポリオキシエチレンノニルフェニルエーテルのベンゼン環に重合性の１－プロペニル基を導入したもの（第一工業製薬（株）製；商品名：アクアロンＲＮ－１０、同ＲＮ－２０、同ＲＮ－３０、同ＲＮ－５０等）、ポリオキシエチレンノニルフェニルエーテルの硫酸エステルのアンモニウム塩のベンゼン環に重合性の１－プロペニル基を導入したもの（第一工業製薬（株）製；商品名：アクアロンＨＳ－１０、同ＨＳ－２０、同ＨＳ－１０２５等）、および分子内に重合性二重結合を持つ、スルホコハク酸ジエステル系（花王（株）製；商品名：ラテムルＳ－１２０Ａ、同Ｓ－１８０Ａ等）等が挙げられる。
　本実施形態に係る（メタ）アクリル系粘着性樹脂は、さらに必要に応じて、酢酸ビニル、アクリロニトリル、スチレン等の重合性２重結合を有するモノマーにより形成されたモノマー単位をさらに含有してもよい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂の重合反応機構としては、ラジカル重合、アニオン重合、カチオン重合等が挙げられる。（メタ）アクリル系粘着性樹脂の製造コスト、モノマーの官能基の影響および電子部品表面へのイオンの影響等を考慮すればラジカル重合によって重合することが好ましい。
　ラジカル重合反応によって重合する際、ラジカル重合開始剤として、ベンゾイルパーオキサイド、ジ－ｔ－ブチルパーオキサイド、ジクミルパーオキサイド、３，３，５－トリメチルヘキサノイルパーオキサイド、ジ－２－エチルヘキシルパーオキシジカーボネート、メチルエチルケトンパーオキサイド、ｔ－ブチルパーオキシフタレート、ｔ－ブチルパーオキシベンゾエート、ジ－ｔ－ブチルパーオキシアセテート、ｔ－ブチルパーオキシイソブチレート、ｔ－ブチルパーオキシ－２－ヘキサノエート、ｔ－ブチルパーオキシ－２－エチルヘキサノエート、ｔ－ブチルパーオキシ－３，５，５－トリメチルヘキサノエート、アセチルパーオキサイド、イソブチリルパーオキサイド、オクタノイルパーオキサイド、ｔ－ブチルパーオキサイド、ジ－ｔ－アミルパーオキサイド等の有機過酸化物；過硫酸アンモニウム、過硫酸カリウム、過硫酸ナトリウム等の無機過酸化物；２，２'－アゾビスイソブチロニトリル、２，２'－アゾビス－２－メチルブチロニトリル、４，４'－アゾビス－４－シアノバレリックアシッド等のアゾ化合物が挙げられる。
　乳化重合法により重合する場合には、これらのラジカル重合開始剤の中で、水溶性の過硫酸アンモニウム、過硫酸カリウム、過硫酸ナトリウム等の無機過酸化物、同じく水溶性の４，４'－アゾビス－４－シアノバレリックアシッド等の分子内にカルボキシル基を持ったアゾ化合物が好ましい。電子部品表面へのイオンの影響を考慮すれば、過硫酸アンモニウム、４，４'－アゾビス－４－シアノバレリックアシッド等の分子内にカルボキシル基を有するアゾ化合物がさらに好ましく、４，４'－アゾビス－４－シアノバレリックアシッド等の分子内にカルボキシル基を有するアゾ化合物が特に好ましい。
　本実施形態に係る粘着性樹脂層（Ａ）は、（メタ）アクリル系粘着性樹脂に加えて、架橋性の官能基を１分子中に２個以上有する架橋剤をさらに含むことが好ましい。
　架橋性の官能基を１分子中に２個以上有する架橋剤は、（メタ）アクリル系粘着性樹脂が有する官能基と反応させ、粘着力および凝集力を調整するために用いる。
　このような架橋剤としては、ソルビトールポリグリシジルエーテル、ポリグリセロールポリグリシジルエーテル、ペンタエリスリトールポリグリシジルエーテル、ジグリセロールポリグリシジルエーテル、グリセロールポリグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、レソルシンジグリシジルエーテル等のエポキシ系化合物；テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、トリメチロールプロパンのトルエンジイソシアネート３付加物、ポリイソシアネート、ジフェニルメタンジイソシアネート、トリレンジイソシアネート等のイソシアネート系化合物；トリメチロールプロパン－トリ－β－アジリジニルプロピオネート、テトラメチロールメタン－トリ－β－アジリジニルプロピオネート、Ｎ，Ｎ'－ジフェニルメタン－４，４'－ビス（１－アジリジンカルボキシアミド）、Ｎ，Ｎ'－ヘキサメチレン－１，６－ビス（１－アジリジンカルボキシアミド）、Ｎ，Ｎ'－トルエン－２，４－ビス（１－アジリジンカルボキシアミド）、トリメチロールプロパン－トリ－β－（２－メチルアジリジン）プロピオネート等のアジリジン系化合物；Ｎ，Ｎ，Ｎ'，Ｎ'－テトラグリシジル－ｍ－キシレンジアミン、１，３－ビス（Ｎ，Ｎ'－ジグリシジルアミノメチル）シクロヘキサン等の４官能性エポキシ系化合物；ヘキサメトキシメチロールメラミン等のメラミン系化合物等が挙げられる。これらは単独で使用してもよいし、２種以上を併用してもよい。
　これらの中でも、エポキシ系化合物（上記４官能性エポキシ系化合物を含む）、イソシアネート系化合物およびアジリジン系化合物から選択される一種または二種以上を含むことが好ましい。
　架橋剤の含有量は、通常、架橋剤中の官能基数が（メタ）アクリル系粘着性樹脂中の官能基数よりも多くならない程度の範囲が好ましい。しかし、架橋反応で新たに官能基が生じる場合や、架橋反応が遅い場合等、必要に応じて過剰に含有してもよい。
　粘着性樹脂層（Ａ）中の架橋剤の含有量は、粘着性樹脂層（Ａ）の耐熱性や密着力とのバランスを向上させる観点から、（メタ）アクリル系粘着性樹脂１００質量部に対し、０．１質量部以上３０質量部以下であることが好ましく、０．１質量部以上２０質量部以下であることがより好ましく、０．１質量部以上１５質量部以下であることがさらに好ましい。
　粘着性樹脂層（Ａ）の厚さは特に制限されないが、例えば、１μｍ以上１００μｍ以下であることが好ましく、３μｍ以上５０μｍ以下であることがより好ましい。
　粘着性樹脂層（Ａ）は、例えば、中間層（Ｃ）あるいは後述の基材層１０上に粘着剤を塗布することにより形成することができる。粘着剤は溶剤に溶解して塗布液として塗布してもよいし、水系エマルジョンとして塗布してもよいし、液状の粘着剤を直に塗布してもよい。
　水系エマルジョン塗布液としては、例えば、（メタ）アクリル系粘着性樹脂（ａ）、シリコーン系粘着性樹脂、ウレタン系粘着性樹脂、オレフィン系粘着性樹脂、スチレン系粘着性樹脂等を水に分散させた塗布液が挙げられる。
　有機溶剤に溶解した粘着剤塗布液を用いてもよい。有機溶剤は特に限定されず、溶解性や乾燥時間を鑑みて公知の中から適宜選択すればよい。有機溶剤としては、酢酸エチル、酢酸メチルなどのエステル系；アセトン、ＭＥＫ等のケトン系；ベンゼン、トルエン、エチルベンゼン等の芳香族系；ヘプタン、ヘキサン、シクロヘキサン等の直鎖ないし環状脂肪族系；イソプロパノール、ブタノール等のアルコール系を例示することができる。有機溶剤として酢酸エチル、トルエンが好ましい。これらの溶剤は、１種単独で用いてもよいし、２種以上を混合して用いてもよい。
　粘着剤塗布液を塗布する方法としては、従来公知の塗布方法、例えば、ロールコーター法、リバースロールコーター法、グラビアロール法、バーコート法、コンマコーター法、ダイコーター法等が採用できる。塗布された粘着剤の乾燥条件には特に制限はないが、一般的には、８０～２００℃の温度範囲において、１０秒～１０分間乾燥することが好ましい。さらに好ましくは、８０～１７０℃において、１５秒～５分間乾燥する。架橋剤と粘着剤との架橋反応を十分に促進させるために、粘着剤塗布液の乾燥が終了した後、４０～８０℃において５～３００時間程度加熱してもよい。
　また、中間層（Ｃ）あるいは基材層１０と粘着性樹脂層（Ａ）とは共押出成形によって形成してもよいし、フィルム状の中間層（Ｃ）あるいは基材層１０とフィルム状の粘着性樹脂層（Ａ）とをラミネート（積層）して形成してもよい。
＜粘着性樹脂層（Ｂ）＞
　本実施形態に係る粘着性フィルム５０は、支持基板に貼り付けるために用いられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）を備える。
　これにより、外部刺激を与えることで支持基板から粘着性フィルム５０を容易に剥離することができる。
　ここで、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）としては、例えば、加熱により粘着力が低下する加熱剥離型の粘着性樹脂層や、放射線により粘着力が低下する放射線剥離型の粘着性樹脂層等が挙げられる。これらの中でも加熱により粘着力が低下する加熱剥離型の粘着性樹脂層が好ましい。
　加熱剥離型の粘着性樹脂層としては、例えば、気体発生成分を含む加熱膨張型粘着剤、膨張して粘着力を低減できる熱膨張性の微小球を含む加熱膨張型粘着剤、熱により接着剤成分が架橋反応することで接着力が低下する加熱膨張型粘着剤等により構成された粘着性樹脂層が挙げられる。
　本実施形態において、粘着性樹脂層（Ｂ）に使用される加熱膨張型粘着剤は、熱を与えることで接着力が低下または喪失する粘着剤である。例えば、１５０℃以下では剥離せず、１５０℃を超える温度で剥離する材料を選択することができ、電子装置の製造工程中に粘着性フィルム５０が支持基板から剥離しない程度の接着力を有していることが好ましい。
　加熱膨張型粘着剤に使用される気体発生成分としては、例えば、アゾ化合物、アジド化合物、メルドラム酸誘導体等を用いることができる。また、炭酸アンモニウム、炭酸水素アンモニウム、炭酸水素ナトリウム、亜硝酸アンモニウム、水酸化ホウ素ナトリウム、各種アジド類等の無機系発泡剤や、水；トリクロロモノフルオロメタン、ジクロロモノフルオロメタンなどの塩フッ化アルカン系化合物；アゾビスイソブチロニトリル、アゾジカルボンアミド、バリウムアゾジカルボキシレートなどのアゾ系化合物；パラトルエンスルホニルヒドラジド、ジフェニルスルホン－３，３’－ジスルホニルヒドラジド、４，４’－オキシビス（ベンゼンスルホニルヒドラジド）、アリルビス（スルホニルヒドラジド）などのヒドラジン系化合物；ｐ－トルイレンスルホニルセミカルバジド、４，４’－オキシビス（ベンゼンスルホニルセミカルバジド）などのセミカルバジド系化合物；５－モルホリル－１，２，３，４－チアトリアゾールなどのトリアゾール系化合物；Ｎ，Ｎ’－ジニトロソペンタメチレンテトラミン、Ｎ，Ｎ’－ジメチル－Ｎ，Ｎ’－ジニトロソテレフタルアミドなどのＮ－ニトロソ系化合物等の有機系発泡剤等も用いることができる。気体発生成分は粘着性樹脂に添加されていてもよく、粘着性樹脂に直接結合されていてもよい。
　加熱膨張型粘着剤に使用される熱膨張性の微小球としては、例えば、マイクロカプセル化されている発泡剤を用いることができる。このような熱膨張性の微小球としては、例えば、イソブタン、プロパン、ペンタンなどの加熱により容易にガス化して膨張する物質を、弾性を有する殻内に内包させた微小球などが挙げられる。上記殻を構成する材料として、例えば、塩化ビニリデン－アクリロニトリル共重合体、ポリビニルアルコール、ポリビニルブチラール、ポリメチルメタクリレート、ポリアクリロニトリル、ポリ塩化ビニリデン、ポリスルホンなどが挙げられる。熱膨張性の微小球は、例えば、コアセルベーション法や、界面重合法などにより製造することができる。
　熱膨張性の微小球は粘着性樹脂に添加することができる。
　気体発生成分および熱膨張性の微小球から選択される少なくとも一種の含有量は、加熱剥離型の粘着性樹脂層（Ｂ）の膨張倍率や接着力の低下性などに応じて適宜設定することができ、特に限定されないが、例えば、加熱剥離型の粘着性樹脂層（Ｂ）中の粘着性樹脂１００質量部に対して、例えば１質量部以上１５０質量部以下、好ましくは５質量部以上１３０質量部以下、さらに好ましくは１０質量部以上１００質量部以下である。
　気体が発生する温度や熱膨張性の微小球が熱膨張する温度が、１５０℃を超える温度になるように設計することが好ましい。
　加熱膨張型粘着剤を構成する粘着性樹脂としては、例えば、（メタ）アクリル系樹脂、ウレタン系樹脂、シリコーン系樹脂、ポリオレフィン系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、フッ素系樹脂、スチレン－ジエンブロック共重合体系樹脂等を挙げることができる。これらの中でも（メタ）アクリル系樹脂が好ましい。
　粘着性樹脂層（Ｂ）に使用される（メタ）アクリル系樹脂としては、例えば、前述した粘着性樹脂層（Ａ）に使用される（メタ）アクリル系粘着性樹脂と同様のものを用いることができる。
　また、本実施形態に係る粘着性フィルム５０において、外部刺激を与えることにより粘着性樹脂層（Ｂ）の粘着力を低下させて粘着性樹脂層（Ｂ）から支持基板を剥離する際に電子部品を粘着性樹脂層（Ａ）上に安定的に保持する観点から、粘着性樹脂層（Ａ）中の気体発生成分および熱膨張性の微小球から選択される少なくとも一種の含有量は、粘着性樹脂層（Ａ）の全体を１００質量％としたとき、０．１質量％以下であることが好ましく、０．０５質量％以下であることがより好ましく、０．０１質量％以下であることがさらに好ましく、粘着性樹脂層（Ａ）中に気体発生成分および熱膨張性の微小球から選択される少なくとも一種が含まれないことが特に好ましい。
　粘着性樹脂層（Ｂ）の厚さは特に制限されないが、例えば、５μｍ以上３００μｍ以下であることが好ましく、１０μｍ以上１５０μｍ以下であることがより好ましい。
　粘着性樹脂層（Ｂ）は、例えば、中間層（Ｃ）あるいは後述の基材層１０上に粘着剤塗布液を塗布することにより形成することができる。
　粘着剤塗布液を塗布する方法としては、従来公知の塗布方法、例えば、ロールコーター法、リバースロールコーター法、グラビアロール法、バーコート法、コンマコーター法、ダイコーター法等が採用できる。塗布された粘着剤の乾燥条件には特に制限はないが、一般的には、８０～２００℃の温度範囲において、１０秒～１０分間乾燥することが好ましい。さらに好ましくは、８０～１７０℃において、１５秒～５分間乾燥する。架橋剤と粘着剤との架橋反応を十分に促進させるために、粘着剤塗布液の乾燥が終了した後、４０～８０℃において５～３００時間程度加熱してもよい。
　また、中間層（Ｃ）あるいは基材層１０と粘着性樹脂層（Ｂ）とは共押出成形によって形成してもよいし、フィルム状の中間層（Ｃ）あるいは基材層１０とフィルム状の粘着性樹脂層（Ｂ）とをラミネート（積層）して形成してもよい。
＜中間層（Ｃ）＞
　本実施形態に係る粘着性フィルム５０は粘着性樹脂層（Ａ）と粘着性樹脂層（Ｂ）との間に特定の弾性率および損失正接（ｔａｎδ）を有する中間層（Ｃ）を備えている。これにより粘着性フィルム５０全体の応力吸収性が向上し、封止材により電子部品を封止する際の金枠からの応力を緩和することができ、その結果、支持基板と粘着性樹脂層（Ｂ）との粘着力の上昇を抑制でき、その結果、支持基板から粘着性フィルム５０を剥離する際の支持基板側の糊残りを効果的に抑制することができる。
　本実施形態に係る粘着性フィルム５０において、支持基板から粘着性フィルム５０を剥離する際の支持基板側の糊残りを効果的に抑制する観点から、中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’は１．０×１０５Ｐａ以上、好ましくは１．５×１０５Ｐａ以上、そして、８．０×１０６Ｐａ以下、好ましくは５．０×１０６Ｐａ以下、より好ましくは３．０×１０６Ｐａ以下である。
　中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’は、例えば、中間層（Ｃ）を構成する各成分の種類や配合割合を制御することにより上記範囲内に制御することができる。
　また、本実施形態に係る粘着性フィルム５０において、支持基板から粘着性フィルムを剥離する際の支持基板側の糊残りを効果的に抑制する観点から、１２０℃における損失正接（ｔａｎδ）が０．１以下である。１２０℃における損失正接（ｔａｎδ）の下限値は特に限定されないが、例えば、０．０００１以上、好ましくは０．００１以上、より好ましくは０．０１以上である。
　中間層（Ｃ）の１２０℃における損失正接（ｔａｎδ）は、例えば、中間層（Ｃ）を構成する各成分の種類や配合割合を制御することにより上記範囲内に制御することができる。
　中間層（Ｃ）を構成する樹脂は、１２０℃における貯蔵弾性率Ｅ’が上記範囲内であるものであれば特に限定されないが、例えば、熱可塑性樹脂を用いることができる。
　より具体的には、（メタ）アクリル系樹脂、ウレタン系樹脂、シリコーン系樹脂、ポリオレフィン系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、フッ素系樹脂、スチレン－ジエンブロック共重合体系樹脂等を挙げることができる。
　これらの中でも、１２０℃における貯蔵弾性率Ｅ’の調整が容易である点から、（メタ）アクリル系樹脂が好ましい。
　中間層（Ｃ）を構成する樹脂は単独で用いてもよいし、二種以上をブレンドして用いてもよい。
　中間層（Ｃ）に使用される（メタ）アクリル系樹脂としては、例えば、前述した粘着性樹脂層（Ａ）に使用される（メタ）アクリル系粘着性樹脂と同様のものを用いることができる。
　本実施形態に係る中間層（Ｃ）は（メタ）アクリル系樹脂を使用する場合、（メタ）アクリル系樹脂に加えて、架橋性の官能基を１分子中に２個以上有する架橋剤をさらに含むことが好ましい。
　架橋性の官能基を１分子中に２個以上有する架橋剤は、（メタ）アクリル系樹脂が有する官能基と反応させ、粘着力および凝集力を調整するために用いる。
　このような架橋剤としては、ソルビトールポリグリシジルエーテル、ポリグリセロールポリグリシジルエーテル、ペンタエリスリトールポリグリシジルエーテル、ジグリセロールポリグリシジルエーテル、グリセロールポリグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、レソルシンジグリシジルエーテル等のエポキシ系化合物；テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、トリメチロールプロパンのトルエンジイソシアネート３付加物、ポリイソシアネート、ジフェニルメタンジイソシアネート、トリレンジイソシアネート等のイソシアネート系化合物；トリメチロールプロパン－トリ－β－アジリジニルプロピオネート、テトラメチロールメタン－トリ－β－アジリジニルプロピオネート、Ｎ，Ｎ'－ジフェニルメタン－４，４'－ビス（１－アジリジンカルボキシアミド）、Ｎ，Ｎ'－ヘキサメチレン－１，６－ビス（１－アジリジンカルボキシアミド）、Ｎ，Ｎ'－トルエン－２，４－ビス（１－アジリジンカルボキシアミド）、トリメチロールプロパン－トリ－β－（２－メチルアジリジン）プロピオネート等のアジリジン系化合物；Ｎ，Ｎ，Ｎ'，Ｎ'－テトラグリシジル－ｍ－キシレンジアミン、１，３－ビス（Ｎ，Ｎ'－ジグリシジルアミノメチル）シクロヘキサン等の４官能性エポキシ系化合物；ヘキサメトキシメチロールメラミン等のメラミン系化合物等が挙げられる。これらは単独で使用してもよいし、２種以上を併用してもよい。
　これらの中でも、エポキシ系化合物、イソシアネート系化合物およびアジリジン系化合物から選択される一種または二種以上を含むことが好ましい。
　中間層（Ｃ）中の架橋剤の含有量は、中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’および１２０℃における損失正接（ｔａｎδ）を所望の値に調整する観点から、（メタ）アクリル系樹脂１００質量部に対し、０．５質量部以上１０質量部以下であることが好ましく、０．７質量部以上５質量部以下であることがより好ましい。
　また、本実施形態に係る粘着性フィルム５０において、外部刺激を与えることにより粘着性樹脂層（Ｂ）の粘着力を低下させて粘着性樹脂層（Ｂ）から支持基板を剥離する際に中間層（Ｃ）と粘着性樹脂層（Ｂ）との間の接着性を良好に保つ観点から、中間層（Ｃ）中の気体発生成分および熱膨張性の微小球から選択される少なくとも一種の含有量は、中間層（Ｃ）の全体を１００質量％としたとき、０．１質量％以下であることが好ましく、０．０５質量％以下であることがより好ましく、０．０１質量％以下であることがさらに好ましく、中間層（Ｃ）中に気体発生成分および熱膨張性の微小球から選択される少なくとも一種が含まれないことが特に好ましい。
　中間層（Ｃ）の厚さは特に制限されないが、例えば、５μｍ以上３００μｍ以下であることが好ましく、１０μｍ以上１５０μｍ以下であることがより好ましい。
　中間層（Ｃ）は、例えば、粘着性樹脂層（Ａ）、粘着性樹脂層（Ｂ）あるいは後述の基材層１０上に塗布液を塗布することにより形成することができる。
　塗布液を塗布する方法としては、従来公知の塗布方法、例えば、ロールコーター法、リバースロールコーター法、グラビアロール法、バーコート法、コンマコーター法、ダイコーター法等が採用できる。塗布された粘着剤の乾燥条件には特に制限はないが、一般的には、８０～２００℃の温度範囲において、１０秒～１０分間乾燥することが好ましい。さらに好ましくは、８０～１７０℃において、１５秒～５分間乾燥する。架橋剤と粘着剤との架橋反応を十分に促進させるために、塗布液の乾燥が終了した後、４０～８０℃において５～３００時間程度加熱してもよい。
　また、粘着性樹脂層（Ａ）、粘着性樹脂層（Ｂ）あるいは基材層１０と中間層（Ｃ）とは共押出成形によって形成してもよいし、フィルム状の粘着性樹脂層（Ａ）、粘着性樹脂層（Ｂ）あるいは基材層１０とフィルム状の中間層（Ｃ）とをラミネート（積層）して形成してもよい。
＜基材層＞
　本実施形態に係る粘着性フィルム５０は、図２に示すように、粘着性フィルム５０の取り扱い性や機械的特性、耐熱性等の特性をより良好にすることを目的として粘着性樹脂層（Ａ）と粘着性樹脂層（Ｂ）との間に基材層１０をさらに設けることができる。基材層１０は、例えば、図２に示すように粘着性樹脂層（Ａ）と中間層（Ｃ）との間に設けてもよいし、粘着性樹脂層（Ｂ）と中間層（Ｃ）との間に設けてもよい。
　基材層１０は特に限定されないが、例えば、樹脂フィルムが挙げられる。
　上記樹脂フィルムを構成する樹脂としては、公知の熱可塑性樹脂を用いることができる。例えば、ポリエチレン、ポリプロピレン、ポリ（４－メチル－１－ペンテン）、ポリ（１－ブテン）等のポリオレフィン；ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート等のポリエステル；ナイロン－６、ナイロン－６６、ポリメタキシレンアジパミド等のポリアミド；ポリアクリレート；ポリメタアクリレート；ポリ塩化ビニル；ポリ塩化ビニリデン；ポリイミド；ポリエーテルイミド；エチレン・酢酸ビニル共重合体；ポリアクリロニトリル；ポリカーボネート；ポリスチレン；アイオノマー；ポリスルホン；ポリエーテルスルホン；ポリフェニレンエーテル等から選択される一種または二種以上を挙げることができる。
　これらの中でも、透明性や機械的強度、価格等のバランスに優れる観点から、ポリプロピレン、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリアミド、ポリイミドから選択される一種または二種以上が好ましく、ポリエチレンテレフタレート、ポリエチレンナフタレートから選択される少なくとも一種がより好ましい。
　基材層１０は、単層であっても、二種以上の層であってもよい。
　また、基材層１０を形成するために使用する樹脂フィルムの形態としては、延伸フィルムであってもよいし、一軸方向または二軸方向に延伸したフィルムであってもよいが、基材層１０の機械的強度を向上させる観点から、一軸方向または二軸方向に延伸したフィルムであることが好ましい。
　基材層１０の厚さは、良好なフィルム特性を得る観点から、好ましくは１μｍ以上５００μｍ以下、より好ましくは５μｍ以上３００μｍ以下、さらに好ましくは１０μｍ以上２５０μｍ以下である。
　基材層１０は、他の層との接着性を改良するために、表面処理を行ってもよい。具体的には、コロナ処理、プラズマ処理、アンダーコート処理、プライマーコート処理等を行ってもよい。
＜その他の層＞
　本実施形態に係る粘着性フィルム５０は、本実施形態の効果を損なわない範囲で、基材層１０と粘着性樹脂層（Ａ）との間あるいは基材層１０と粘着性樹脂層（Ｂ）との間に、例えば接着層等がさらに設けられていてもよい。
２．電子装置の製造方法
　次に、本実施形態に係る電子装置の製造方法について説明する。図３および４は、本発明に係る実施形態の電子装置の製造方法の一例を模式的に示した断面図である。
　本実施形態に係る電子装置の製造方法は、以下の４つの工程を少なくとも備えている。
　（１）本実施形態に係る粘着性フィルム５０と、粘着性フィルム５０の粘着性樹脂層（Ａ）に貼り付けられた電子部品７０と、粘着性フィルム５０の粘着性樹脂層（Ｂ）に貼り付けられた支持基板８０と、を備える構造体１００を準備する工程
　（２）封止材６０により電子部品７０を封止する工程
　（３）外部刺激を与えることにより粘着性樹脂層（Ｂ）の粘着力を低下させて構造体１００から支持基板８０を剥離する工程
　（４）電子部品７０から粘着性フィルム５０を剥離する工程
　そして、本実施形態に係る電子装置の製造方法では、電子部品７０を仮固定する粘着性フィルムとして、前述した本実施形態に係る粘着性フィルム５０を使用する。
　以下、本実施形態に係る電子装置の製造方法の各工程について説明する。
（工程（１））
　はじめに、粘着性フィルム５０と、粘着性フィルム５０の粘着性樹脂層（Ａ）に貼り付けられた電子部品７０と、粘着性フィルム５０の粘着性樹脂層（Ｂ）に貼り付けられた支持基板８０と、を備える構造体１００を準備する。
　このような構造体１００は、例えば、以下の手順で作製することができる。
　まず、支持基板８０上に、粘着性フィルム５０を、粘着性樹脂層（Ｂ）が支持基板８０側となるように貼着する。粘着性樹脂層（Ｂ）上には保護フィルムが貼付けられていてもよく、当該保護フィルムを剥がし、粘着性樹脂層（Ｂ）の露出面を支持基板８０表面に貼着することができる。
　支持基板８０としては、例えば、石英基板、ガラス基板、ＳＵＳ基板等を使用することができる。
　次いで、支持基板８０上に貼着された粘着性フィルム５０の粘着性樹脂層（Ａ）上に電子部品７０を配置することにより構造体１００を得ることができる。
　電子部品７０としては、例えば、ＩＣ、ＬＳＩ、ディスクリート、発光ダイオード、受光素子等の半導体チップや半導体パネル、半導体パッケージ等を挙げることができる。
（工程（２））
　次いで、封止材６０により電子部品７０を封止する。
　封止材６０により電子部品７０を覆い、例えば１５０℃以下の温度で封止材６０を硬化させて、電子部品７０を封止する。
　また、封止材６０の形態としては特に限定されないが、例えば、顆粒状、シート状または液状である。
　封止材６０としては特に限定されないが、例えば、エポキシ樹脂を用いたエポキシ樹脂系封止材を用いることができる。
　特に、粘着性フィルム５０への封止材６０の親和性がより良好になり、電子部品７０をより一層ムラなく封止することが可能となる点から、液状のエポキシ樹脂系封止材が好ましい。
　このようなエポキシ樹脂系封止材としては、例えば、ナガセケムテックス社製のＴ６９３／Ｒ４０００シリーズやＴ６９３／Ｒ１０００シリーズ、Ｔ６９３／Ｒ５０００シリーズ等を用いることができる。
　封止方法としては、例えば、トランスファー成形、射出成形、圧縮成形、注型成形等が挙げられる。封止材６０で電子部品７０を封止後、例えば１５０℃以下の温度で加熱することによって封止材６０を硬化させ、電子部品７０が封止された構造体１００が得られる。
（工程（３））
　次いで、外部刺激を与えることにより粘着性樹脂層（Ｂ）の粘着力を低下させて構造体１００から支持基板８０を剥離する。
　支持基板８０は、例えば、電子部品７０を封止した後、１５０℃を超える温度に加熱して、粘着性樹脂層（Ｂ）の接着力を低下させることにより、粘着性フィルム５０から容易に除去することができる。
（工程（４））
　次いで、電子部品７０から粘着性フィルム５０を除去し、電子装置２００を得る。
　電子部品７０から粘着性フィルム５０を除去する方法としては、例えば、機械的に剥離する方法や、粘着性フィルム５０表面の粘着力を低下させてから剥離する方法等が挙げられる。
（工程（５））
　本実施形態に係る電子装置の製造方法において、図４に示すように、得られた電子装置２００の露出面に、配線層３１０およびバンプ３２０を形成し、電子装置３００を得る工程（５）をさらに備えてもよい。
　配線層３１０は、最外面に形成された外部接続端子であるパッド（不図示）と、露出した電子部品７０と該パッドとを電気的に接続する配線（不図示）と、を備える。配線層３１０は、従来公知の方法によって形成することができ、多層構造であってもよい。
　そして、配線層３１０のパッド上にバンプ３２０を形成し、電子装置３００を得ることができる。バンプ３２０としては、はんだバンプや金バンプ等を挙げることができる。はんだバンプは、例えば、配線層３１０の外部接続端子であるパッド上にはんだボールを配置し、加熱してはんだを溶融させる（リフローする）ことにより形成することができる。金バンプは、ボールボンディング法、めっき法、Ａｕボール転写法等の方法により形成することができる。
（工程（６））
　本実施形態に係る電子装置の製造方法において、図４に示すように、電子装置３００をダイシングし、複数の電子装置４００を得る工程（６）をさらに備えてもよい。
　電子装置３００のダイシングは、公知の方法で行うことができる。
　以上、本発明の実施形態について述べたが、これらは本発明の例示であり、上記以外の様々な構成を採用することもできる。
　なお、本発明は前述の実施形態に限定されるものではなく、本発明の目的を達成できる範囲での変形、改良等は本発明に含まれるものである。
　以下、実施例により本発明を具体的に説明するが本発明はこれに限定されるものではない。
　実施例および比較例における粘着性フィルムの作製に用いた材料の詳細は以下の通りである。
＜粘着性樹脂層（Ａ）形成用の粘着剤塗布液Ａ＞
（粘着性樹脂溶液Ａ１の調製）
　脱イオンを行った純水中に、重合開始剤として４，４’－アゾビス－４－シアノバレリックアシッド（大塚化学（株）製、商品名：ＡＣＶＡ）を０．５質量部、モノマー（Ａ）としてアクリル酸－ｎ－ブチルを７４．３質量部およびメタクリル酸メチルを１３．７質量部、モノマー（Ｂ）としてメタクリル酸－２－ヒドロキシエチルを９質量部、重合性界面活性剤としてポリオキシエチレンノニルフェニルエーテルの硫酸エステルのアンモニウム塩のベンゼン環に重合性の１－プロペニル基を導入したもの（第一工業製薬社製；商品名：アクアロンＨＳ－１０２５）を３質量部それぞれ投入した。次いで、攪拌下で７０～７２℃において８時間乳化重合を実施し、アクリル系樹脂エマルションを得た。これをアンモニア水で中和（ｐＨ＝７．０）し、固形分濃度４２．５％の粘着性樹脂溶液Ａ１を得た。
（粘着性樹脂溶液Ａ２の調製）
　脱イオンを行った純水中に、重合開始剤として過硫酸アンモニウムを０．５質量部、モノマー（Ａ）としてアクリル酸－２－エチルヘキシルを６３質量部、アクリル酸－ｎ－ブチルを２１質量部およびメタクリル酸メチルを９質量部、モノマー（Ｂ）としてメタクリル酸－２－ヒドロキシエチルを３質量部、モノマー（Ｃ）としポリテトラメチレングリコールジアクリレート（日本油脂（株）製、商品名；ＡＤＴ－２５０）を１質量部、重合性界面活性剤としてポリオキシエチレンノニルフェニルエーテルの硫酸エステルのアンモニウム塩のベンゼン環に重合性の１－プロペニル基を導入したもの（第一工業製薬（株）製；商品名：アクアロンＨＳ－１０２５）を２質量部それぞれ投入し、攪拌下で７０～７２℃において８時間乳化重合を実施し、アクリル系樹脂エマルションを得た。これをアンモニア水で中和（ｐＨ＝７．０）し、固形分濃度５６．５％の粘着性樹脂溶液Ａ２を得た。
（粘着剤塗布液Ａの調製）
　粘着性樹脂溶液Ａ１を５０質量部、粘着性樹脂溶液Ａ２を５０質量部、ジメチルエタノールアミンを０．３質量部、架橋剤であるエポキシ系化合物（ナガセケムテックス社製、Ｅｘ－１６１０）を６質量部、それぞれ混合して粘着剤塗布液Ａを得た。
＜粘着性樹脂層（Ｂ）形成用の粘着剤塗布液Ｂ＞
（ポリマーＡ溶液の調製）
　アクリル酸－ｎ－ブチル：７４質量部、メタクリル酸メチル：１６質量部、メタクリル酸－２－ヒドロキシエチル：７質量部、アクリル酸：３質量部をトルエンおよび酢酸エチル混合溶媒中で共重合し、濃度４５質量％、分子量２５万のポリマーＡ溶液を得た。
（粘着剤塗布液Ｂの調製）
　ポリマーＡ溶液、架橋剤であるイソシアネート系化合物（三井化学社製、オレスターＰ４９－７５Ｓ）、膨張開始温度１６０℃の熱膨張性の微小球、粘着付与剤（荒川化学製、ペンセルＤ１２５）を１００：２：１５：５の割合（固形分質量比）で混合して粘着剤塗布液Ｂを得た。
＜中間層（Ｃ）形成用の塗布液Ｃ＞
（ポリマーＡ溶液の調製）
　アクリル酸－ｎ－ブチル：７４質量部、メタクリル酸メチル：１６質量部、メタクリル酸－２－ヒドロキシエチル：７質量部、アクリル酸：３質量部をトルエンおよび酢酸エチル混合溶媒中で共重合し、濃度４５質量％、分子量２５万のポリマーＡ溶液を得た。
（ポリマーＢ溶液の調製）
　アクリル酸－２－エチルヘキシル：３５質量部、アクリル酸－ｎ－ブチル：４１量部、アクリル酸エチル：１５質量部、メタクリル酸－２－ヒドロキシエチル：９質量部を窒素雰囲気下、トルエンおよび酢酸エチル混合溶媒中で共重合し、分子量３０万のポリマーＢ溶液を得た。
（塗布液Ｃの調製）
　ポリマーＡ溶液と架橋剤であるエポキシ系化合物（テトラッドＣ、三菱ガス化学社製）を１００：１の割合（固形分質量比）で混合して塗布液Ｃ１を得た。
　また、ポリマー溶液の種類、架橋剤の種類および配合量を表１に記載の値に変更した以外は塗布液Ｃ１と同様にして、塗布液Ｃ１～Ｃ９をそれぞれ調製した。
　なお、表１中のエポキシ系化合物はテトラッドＣ（三菱ガス化学社製）であり、イソシアネート系化合物はオレスターＰ４９－７５Ｓ（三井化学社製）である。
［実施例１］
　基材層であるポリエチレンテレフタレート（ＰＥＴ）フィルム（厚さ３８μｍ）上に、粘着剤塗布液Ａを塗布した後、乾燥させて、厚さ１３μｍの粘着性樹脂層（Ａ）を形成した。次いで、ＰＥＴフィルムの粘着性樹脂層（Ａ）とは反対側の表面に、塗布液Ｃ１を塗布した後、乾燥させて、厚さ２０μｍの中間層（Ｃ）を形成した。次いで、中間層（Ｃ）上に粘着剤塗布液Ｂを塗布した後、乾燥させて、厚さ２５μｍの粘着性樹脂層（Ｂ）を形成し、粘着性フィルムを得た。
　得られた粘着性フィルムについて以下の評価をおこなった。得られた結果を表１に示す。
［実施例２～６および比較例１～３］
　塗布液Ｃ１の代わりに塗布液Ｃ２～Ｃ９をそれぞれ用いた以外は実施例１と同様にして粘着性フィルムをそれぞれ作製した。
　得られた粘着性フィルムについて以下の評価をそれぞれおこなった。得られた結果を表１にそれぞれ示す。
［比較例４］
　中間層（Ｃ）を形成しない以外は実施例１と同様にして粘着性フィルムを作製した。
　得られた粘着性フィルムについて以下の評価をそれぞれおこなった。得られた結果を表１にそれぞれ示す。
＜評価＞
（１）中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’および損失正接（ｔａｎδ）の測定
　塗布液Ｃ１～Ｃ９を離型フィルム上に乾燥厚みが２０μｍとなるようにそれぞれ塗布した後、１１０℃オーブン中で３分間乾燥させた。次いで、サンプル厚みが１ｍｍとなるまでそれぞれ重ね合わせて粘弾性測定用サンプルをそれぞれ得た。
　次いで、固体粘弾性測定装置（ＲＳＡ－３、ＴＡインスツルメント社製）を用いて、周波数１Ｈｚ、昇温速度５℃／ｍｉｎ、ひずみ０．０５％、チャック間距離２０ｍｍ、サンプル幅１０ｍｍの条件で中間層（Ｃ）の固体粘弾性を測定し、中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’および損失正接（ｔａｎδ）をそれぞれ算出した。
（２）支持基板上の糊残り
　実施例および比較例で得られた粘着性フィルムの粘着性樹脂層（Ｂ）を支持基板上に貼付け、次いで粘着性樹脂層（Ａ）上にシリコンチップを複数個配置した。
　次いで、２３℃で１分間放置後、圧縮成形機（アピックヤマダ社製、ＷＣＭ－３００ＭＣ）を用いて、粘着性樹脂層（Ａ）上に複数個配置したシリコンチップを、液状のエポキシ樹脂系封止材（ナガセケムテックス社製、Ｔ６９３／Ｒ４２１２）を用いて温度１２０℃で３分間封止した。
　次いで、支持基板／粘着性フィルム／シリコンチップ／封止材の構造体を圧縮成形機から取り出し、オーブンで１５０℃、３０分間加熱した後、１８５℃で粘着性樹脂層（Ｂ）を発泡させて支持基板を粘着性フィルム／シリコンチップ／封止材の構造体から脱離させた。
　次いで、脱離後の支持基板表面を目視で観察し、支持基板表面の粘着性フィルムの糊残りを確認し、下記の基準で粘着性フィルムの糊残りを評価した。
　〇：目視により、支持基板表面に糊残りが観察されなかった
　×：目視により、支持基板表面に糊残りが観察された
Figure JPOXMLDOC01-appb-T000001
　中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’が１．０×１０５Ｐａ以上８．０×１０６Ｐａ以下であり、かつ、中間層（Ｃ）の１２０℃における損失正接（ｔａｎδ）が０．１以下である粘着性フィルムを用いた実施例１～６では、支持基板上に糊残りは観察されなかった。よって、実施例１～６の粘着性フィルムでは、支持基板から粘着性フィルムを剥離する際の支持基板側の糊残りを抑制できることが理解できる。
　これに対し、中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’が１．０×１０５Ｐａ未満であり、かつ、損失正接（ｔａｎδ）が０．１を超える粘着性フィルムを用いた比較例２および３、あるいは中間層（Ｃ）の１２０℃における損失正接（ｔａｎδ）が０．１を超える粘着性フィルムを用いた比較例１、あるいは中間層（Ｃ）を設けない粘着性フィルムを用いた比較例４では、支持基板上に糊残りが観察された。よって、比較例１～４の粘着性フィルムでは、支持基板から粘着性フィルムを剥離する際に支持基板側に糊残りが発生してしまうことが理解できる。

Claims (8)

  1. 　電子装置の製造工程において封止材により電子部品を封止する際に前記電子部品を仮固定するために用いられる粘着性フィルムであって、
    　前記電子部品を仮固定するための粘着性樹脂層（Ａ）と、
    　支持基板に貼り付けるために用いられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、
    　前記粘着性樹脂層（Ａ）と前記粘着性樹脂層（Ｂ）との間に設けられた中間層（Ｃ）と、
    を備え、
    　前記中間層（Ｃ）の１２０℃における貯蔵弾性率Ｅ’が１．０×１０５Ｐａ以上８．０×１０６Ｐａ以下であり、かつ、前記中間層（Ｃ）の１２０℃における損失正接（ｔａｎδ）が０．１以下である粘着性フィルム。
  2. 　請求項１に記載の粘着性フィルムにおいて、
    　前記粘着性樹脂層（Ｂ）は加熱により粘着力が低下する粘着性フィルム。
  3. 　請求項２に記載の粘着性フィルムにおいて、
    　前記粘着性樹脂層（Ｂ）が気体発生成分および熱膨張性の微小球から選択される少なくとも一種を含む粘着性フィルム。
  4. 　請求項１乃至３のいずれか一項に記載の粘着性フィルムにおいて、
    　前記粘着性樹脂層（Ａ）中の気体発生成分および熱膨張性の微小球から選択される少なくとも一種の含有量が、前記粘着性樹脂層（Ａ）の全体を１００質量％としたとき、０．１質量％以下である粘着性フィルム。
  5. 　請求項１乃至４のいずれか一項に記載の粘着性フィルムにおいて、
    　前記封止材がエポキシ樹脂系封止材である粘着性フィルム。
  6. 　請求項１乃至５のいずれか一項に記載の粘着性フィルムにおいて、
    　前記粘着性樹脂層（Ａ）は（メタ）アクリル系粘着性樹脂を含む粘着性フィルム。
  7. 　請求項１乃至６のいずれか一項に記載の粘着性フィルムと、前記粘着性フィルムの前記粘着性樹脂層（Ａ）に貼り付けられた電子部品と、前記粘着性フィルムの前記粘着性樹脂層（Ｂ）に貼り付けられた支持基板と、を備える構造体を準備する工程（１）と、
    　封止材により前記電子部品を封止する工程（２）と、
    　外部刺激を与えることにより前記粘着性樹脂層（Ｂ）の粘着力を低下させて前記構造体から前記支持基板を剥離する工程（３）と、
    　前記電子部品から前記粘着性フィルムを剥離する工程（４）と、
    を少なくとも備える電子装置の製造方法。
  8. 　請求項７に記載の電子装置の製造方法において、
    　前記封止材がエポキシ樹脂系封止材である電子装置の製造方法。
PCT/JP2018/033579 2018-09-11 2018-09-11 粘着性フィルムおよび電子装置の製造方法 WO2020053949A1 (ja)