WO2016051503A1 - 表面疵の発生し難い熱間圧延用チタン鋳片およびその製造方法 - Google Patents

表面疵の発生し難い熱間圧延用チタン鋳片およびその製造方法 Download PDF

Info

Publication number
WO2016051503A1
WO2016051503A1 PCT/JP2014/076084 JP2014076084W WO2016051503A1 WO 2016051503 A1 WO2016051503 A1 WO 2016051503A1 JP 2014076084 W JP2014076084 W JP 2014076084W WO 2016051503 A1 WO2016051503 A1 WO 2016051503A1
Authority
WO
WIPO (PCT)
Prior art keywords
titanium
hot rolling
ingot
layer
cast
Prior art date
Application number
PCT/JP2014/076084
Other languages
English (en)
French (fr)
Inventor
知徳 國枝
吉紹 立澤
藤井　秀樹
Original Assignee
新日鐵住金株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 新日鐵住金株式会社 filed Critical 新日鐵住金株式会社
Priority to PCT/JP2014/076084 priority Critical patent/WO2016051503A1/ja
Priority to JP2014549253A priority patent/JP6075386B2/ja
Priority to EP14903122.1A priority patent/EP3202952B1/en
Priority to CN201480082158.6A priority patent/CN106715756B/zh
Priority to UAA201702701A priority patent/UA115854C2/uk
Priority to US15/513,355 priority patent/US11504765B2/en
Priority to EA201790409A priority patent/EA031176B1/ru
Priority to KR1020177007577A priority patent/KR101953487B1/ko
Publication of WO2016051503A1 publication Critical patent/WO2016051503A1/ja

Abstract

　工業用純チタンからなるチタン鋳片であって、圧延面となる表面に、α相安定化元素、中性元素の何れか一方、もしくは、両方のうち一種または二種類以上の元素を添加して溶融させ再凝固させた溶融再凝固層を深さ１ｍｍ以上の範囲に有し、深さ１ｍｍまでの範囲におけるα相安定化元素と中性元素の合計の濃度の平均値が、母材中のα相安定化元素と中性元素の合計の濃度に比較して、質量％で、０．１％以上、２．０％未満高くなっている。

Description

表面疵の発生し難い熱間圧延用チタン鋳片およびその製造方法
　本発明は、熱間圧延用チタン鋳片およびその製造方法に関するものであり、特に、分塊圧延工程や精整工程を省略しても熱間圧延後の表面性状を良好に保つことができる熱間圧延用チタン鋳片およびその製造方法に関する。
　チタン材は、一般に、溶解工程から得られるインゴットを分塊工程でスラブまたはビレット形状にして、表面を手入れした後、熱間圧延し、さらに焼鈍や冷間加工を施して製造される。溶解工程には、広く用いられている真空アーク溶解（ＶＡＲ：Ｖａｃｕｕｍ　Ａｒｃ　Ｒｅｍｅｌｔｉｎｇ）法のほか、鋳型とは別の場所で溶解を行い鋳型に流し込む電子ビーム溶解（ＥＢＲ：Ｅｌｅｃｔｒｏｎ　Ｂｅａｍ　Ｒｅｍｅｌｔｉｎｇ）法やプラズマ溶解法等がある。前者では、鋳型が円筒型に限定されるため板材の製造には分塊もしくは鍛造工程が必須である。後者は、鋳型形状の自由度が高く、円筒型の他、角型の鋳型を使用できる。従って、前記電子ビーム溶解法やプラズマ溶解法を用いれば、角型インゴットや円柱型インゴットを直接鋳込むことができる。そのため、角型インゴットから板材を製造する場合や、円柱型インゴットから棒材や線材を製造する場合には、インゴット形状の点からは分塊工程を省略することができる。この場合、分塊工程にかかるコストと時間が省略できるため、生産効率が著しく向上することが期待される。
　しかし、工業的に用いられる大型インゴットの鋳造まま組織は、結晶粒径が数十ｍｍにもおよぶ粗大粒が形成される。このようなインゴットを、分塊工程を経ないで直接熱間圧延する場合には、粗大な結晶粒に起因して粒内および結晶粒間の変形異方性の影響により表面に凹凸が生じて表面疵となる。従って、前記電子ビーム溶解や、プラズマ溶解法で、角型インゴットや円柱型インゴットを直接製造し、分塊工程を省略した場合、その後の熱間圧延において、表面疵が発生してしまう。熱間圧延で発生した表面疵を除去するためには、酸洗工程で熱延板表面の溶削量を増やす必要があり、コストや歩留を悪化させる問題が生じる。即ち、表面疵を落とすための精整工程を新たに導入する必要がある。従って、分塊工程を省略することによって期待される生産効率の向上は、このような精整工程の新たな導入によって相殺されてしまう懸念があった。このような問題に対し、熱間圧延用素材の製造方法や製造後に加工や熱処理を施すことによって表面疵を低減する方法が提案されている。
　特許文献１では、チタン材のインゴットを、分塊工程を省略して直接熱延加工する場合に、表層付近の結晶粒を微細化するために、表面層にひずみを付与した後、再結晶温度以上に加熱して表面から深さ２ｍｍ以上を再結晶させる方法が提案されている。ひずみを付与する手段としては、鍛造、ロール圧下、ショットブラスト等が挙げられている。
　特許文献２では、チタン材のインゴットを、Ｔβ＋５０℃以上に加熱後、Ｔβ―５０℃以下に冷却した後に熱間圧延することで、粗大な結晶粒の変形異方性によって圧延中に形成される表面の波打ちやシワを低減し、表面疵を低減する方法が提案されている。
　特許文献３では、チタン材において、分塊工程を経る場合の圧延製品の表面疵低減方法として、分塊工程終了時の温度をα域にする、あるいは、さらに熱間圧延前の加熱をα域で行うことにより、表面から６０μｍ以上を等軸晶とする方法が提案されている。これにより、酸素リッチ層が部分的に深くなることを避けることができ、脱スケール工程で酸素リッチ層を除去できるようになり、硬度・延性の不均一な部分が無くなるため、冷間加工後の表面性状が改善するとしている。
　特許文献４では、チタン材のインゴットを、熱間加工工程を省略して直接熱間圧延を行う場合に、インゴットの圧延面にあたる面の表層を高周波誘導加熱、アーク加熱、プラズマ加熱、電子ビーム加熱及びレーザー加熱などで溶融再凝固させることで、表層から深さ１ｍｍ以上を細粒化し、熱間圧延後の表層組織を改善する方法が挙げられている。これは、表層部を急冷凝固により微細で不規則な方位を有する凝固組織を形成することで、表面疵の発生を防止している。チタンスラブの表層組織を溶融させる方法として、高周波誘導加熱、アーク加熱、プラズマ加熱、電子ビーム加熱、及びレーザー加熱が挙げられている。
特開平０１－１５６４５６号公報 特開平０８－０６０３１７号公報 特開平０７－１０２３５１号公報 特開２００７－３３２４２０号公報
　しかしながら特許文献１に記載の方法では、ひずみを付与する手段にショットブラストが挙げられているが、一般的なショットブラストで付与されるひずみの深さは３００～５００μｍ程度以下であり、品質を改善するために必要としている深さ２ｍｍ以上の再結晶層を形成するには不十分である。従って、実質的には、鍛造もしくはロール圧下により深い位置まで歪を与えることが必要であるが、鍛造もしくはロール圧下を、熱間圧延用の大型インゴットに対して行うには大きな設備が必要で、通常の分塊工程と比較してコスト低下になるものではない。
　また、特許文献２に記載の方法は、β域への加熱により粗大な結晶粒が再結晶して微細化する効果がある。しかし、分塊工程を経ない場合には加工歪が与えられていないため再結晶核が少ないことや、インゴット全体を加熱するため加熱後の冷却速度が遅く結晶粒が粗大化することにより、再結晶による微細化効果は限定され、変形異方性の低減は十分ではない。また、再結晶しても元の粗大粒の結晶方位の影響を受けることも、変形異方性の解消に至らない要因である。逆に、中程度の細粒化によって表面の凹凸の元となる粒界は増加する結果となり、表面疵の発生が増加する結果になる。
　また、特許文献３に記載の方法は、分塊工程を経ることによって鋳造組織が壊されて細粒化および等軸化することを前提としており、分塊工程を省略する場合には意味をなさない。仮に分塊工程を省略して熱処理のみによって、表面から６０μｍ以上の等軸粒を形成しても、単なる再結晶でありその結晶方位は元の結晶方位の影響を受ける。従って、鋳造まま組織の粗大粒による変形異方性に起因する凹凸を防止するには不十分であり、表面疵による問題が生じることは明らかである。
　また、特許文献４に記載の方法は、インゴット表層部の組織改質を行っており、熱延後の表面性状を良くする効果がある。
　そこで、本発明では、分塊工程や精整工程を省略しても熱間圧延後の表面性状を良好に保つことのできる、工業用純チタンインゴット及びその製造方法を提供することを目的とするものである。
　本発明者らは、上記目的を達成するために鋭意検討した結果、インゴットから分塊工程や精整工程を省略して熱間圧延を行って工業用純チタン製品を製造するに際し、熱間圧延の前工程として、鋳造ままチタン材の圧延面表層にα安定化元素もしくは中性元素を含有する素材（粉末、チップ、ワイヤー、薄膜等）を据えるもしくは散布し、素材ごとスラブ表層を再溶融することで、スラブ表層にα安定化元素もしくは中性元素を含有させることで、熱間圧延加熱時においてもスラブ表層部の組織を微細に保つことができ、その結果、元の粗大な凝固組織の変形異方性の影響による表面疵が低減し、分塊工程や精整工程を経る場合と同等な表面性状を得ることができることを見出した。
本発明の要旨とするところは、以下のとおりである。
（１）
　工業用純チタンからなるチタン鋳片であって、
　圧延面となる表面に、α相安定化元素、中性元素の何れか一方もしくは両方のうち一種または二種類以上の元素を添加して溶融させ再凝固させた溶融再凝固層を深さ１ｍｍ以上の範囲に有し、
　深さ１ｍｍまでの範囲におけるα相安定化元素と中性元素の合計の濃度が、母材中のα相安定化元素と中性元素の合計の濃度に比較して、質量％で、０．１％以上、２．０％未満高いことを特徴とする、熱間圧延用チタン鋳片。
（２）
　α相安定化元素、中性元素がＡｌ，Ｓｎ，Ｚｒである、（１）に記載の熱間圧延用チタン鋳片。
（３）
　さらに、溶融再凝固相にβ相安定化元素の一種もしくは二種類以上を質量％で１．５％以下含有する、（１）に記載の熱間圧延用チタン鋳片。
（４）
　前記再溶融凝固層よりも内側は、鋳造ままの組織もしくは鋳造後にβ域に加熱され、その後冷却された組織である、（１）に記載の熱間圧延用チタン鋳片。
（５）
　チタン鋳片の圧延面となる表面を、α相安定化元素、中性元素の何れか一方もしくは両方のうち一種または二種類以上の元素を含有する素材とともに溶融させた後、凝固させる、熱間圧延用チタン鋳片の製造方法。
（６）
　前記α相安定化元素、中性元素の何れか一方もしくは両方のうち一種または二種類以上の元素を含有する素材が、粉末、チップ、ワイヤー、薄膜、切り粉のうちの一種または二種以上である、（５）に記載の熱間圧延用チタン鋳片の製造方法。
（７）
　チタン鋳片の表面を、電子ビーム加熱、アーク加熱、レーザー加熱、プラズマ加熱、および誘導加熱のうちの一種または二種以上を用いて溶融させる、（５）に記載の熱間圧延用チタン鋳片の製造方法。
（８）
　真空もしくは不活性ガス雰囲気でチタン鋳片の表面を溶融させる、（５）に記載の熱間圧延用チタン鋳片の製造方法。
　本発明の熱間圧延用チタン鋳片およびその製造方法は、チタン材の製造に際し従来必要であった分塊や鍛造などの熱間加工工程やその後の精整工程を省略しても、分塊工程や精整工程を経る場合と同等以上の表面性状を有するチタン材の製造を可能にするものであり、熱間加工工程の省略による加熱時間の低減、スラブ表面平滑化に伴う切削手入れの低減、表面品質向上による酸洗量の低減等によって歩留まりの向上が図られることから、製造コストの削減のみならず、エネルギー効率の向上にも大きな効果があり、産業上の効果は計り知れない。
溶融再凝固層の濃度変化の模式図を示す。
　以下、本発明について詳しく説明する。
[溶融再凝固層の厚み]
　本発明では、工業用純チタンからなるチタン材の圧延面にあたる面に深さ１ｍｍ以上の溶融再凝固層を有している。熱延後の表面疵の発生は、上述したように、粗大な結晶粒を有する組織に起因して発生するチタン材表面の凹凸が原因である。そのため、インゴット表層部のみの結晶粒径をなるべく細かくすればよい。下記のα安定化元素や中性元素を添加することで熱延加熱時の結晶粒成長を抑制し、かつ、それにより表面疵の発生を抑制するには、下記のα安定化元素や中性元素を含有した溶融再凝固層の厚みを１ｍｍとする必要である。溶融再凝固層の厚みが１ｍｍ未満だと、下部組織の鋳造組織の影響を受け表面疵が発生してしまい、表面性状が良化しない。なお、最大深さについて特に規定しないが、溶融深さが深くなりすぎると、熱延後のショット酸洗工程後にも合金元素を含有した層が残存する懸念があるので、好ましくは、溶融深さは５ｍｍ程度までが望ましい。なお、熱間圧延されるチタン材としては、インゴット、スラブ及びビレットなどがある。
　溶融再凝固層は、チタン鋳片の表面を溶融させ、この溶融後に急冷再凝固されて形成される。溶融ビードの走査方向と垂直方向の断面で見ると、溶融再凝固層の形状は、チタン鋳片表層の再溶融時の溶融ビード中央で一番深くなる傾向があり、溶融ビードを重ねた際、隣接した溶融ビード同士の中間で一番浅くなり、最深部と最浅部が周期的に繰り返される形態をとる。この際、最深部と最浅部の差が大きいと、熱間圧延時にこの差により変形抵抗に差異が生じ、これに起因した疵が生じることがある。そのため、上記の差異は２ｍｍ未満であることが望ましい。なお、本発明では溶融再凝固層の深さを１ｍｍ以上としているが、この深さとは、溶融ビードの走査方向と垂直方向の断面で見た際の最浅部の深さを指すものとする。
　ここで工業用純チタンとは、ＪＩＳ規格の１種～４種、およびそれに対応するＡＳＴＭ規格のＧｒａｄｅ１～４、ＤＩＮ規格の３・７０２５で規定される工業用純チタンを含むものとする。すなわち、本発明で対象とする工業用純チタンは、質量％で、Ｃ：０．１％以下、Ｈ：０．０１５％以下、Ｏ：０．４％以下、Ｎ：０．０７％以下、Ｆｅ：０．５％以下、残部Ｔｉからなるもの、と言うことができる。
[α安定化元素もしくは中性元素の含有量]
　本発明では、溶融再凝固層がα安定化元素もしくは中性元素の内一種類以上を母材部に比べある一定以上多く含有していることを特徴としている。これらの元素は、チタン中にある程度含有すると、α単相域で結晶粒成長を抑制することができる。そのため、通常、工業用純チタンを熱延する際の加熱温度域であるα相高温域に加熱しても、結晶粒を微細に保つことができる。本発明では後述するようにα安定化元素もしくは中性元素の内一種類以上を濃化させる手法として、これら元素の内一種類以上からなる素材とともにインゴット表層部を溶融させることとしている。このように、これら元素を含む素材と共に表層を溶融させると、凝固偏析などの影響により溶融部の中でも特に表層部に元素を濃化させることができる。そのため、添加元素量以上を表層に濃化させることで、より組織微細化への効果を発現させることができる。さらに、溶融再凝固相の表層部のみに濃化させることにより、熱延加熱等の熱処理時に、表層部に含有した合金元素の内部への拡散を軽減でき、製品の材質の劣化を抑制することができる。α安定化元素もしくは中性元素の溶融再凝固層の平均濃度が、母材部に比べ合計で０．１％以上高くなるように添加すれば、表層部近傍で元素がより濃化し結晶粒成長が十分に抑制できることから、これを下限とした。一方、溶融再凝固層の平均濃度が２．０％以上母材部より高くなると、合金元素を含有した表層部と内部で熱間加工性の差を生じたり、表層部でより元素が濃化することで熱間圧延時に割れが生じたり、さらには、表層部に元素が濃化していても添加量が多いため、熱延加熱等の熱処理時に、表層部に含有した合金元素が多量に内部に拡散し、製品の材質を劣化させる懸念があることから、これを上限とした。α安定化元素や中性元素は複数の元素を組み合わせて添加しても良く、その場合のα安定化元素と中性元素の濃度は、各元素の合計の濃度である。
[α安定化元素および中性元素の種類]
　本発明では、α安定化元素および中性元素として、Ａｌ、Ｓｎ、Ｚｒを用いることができる。これら元素はα相中に固溶し、熱延する際の加熱温度域において結晶粒成長を抑制する。
[β安定化元素]
　本発明では、α安定元素や中性元素とともに、β安定化元素を含有しても良い。β安定化元素を含有することで、上記の結晶粒成長だけでなく、熱延する際の加熱温度域において第２相であるβ相が生成しやすくなることで、さらに結晶粒成長が抑制されるため、更なる組織微細化が期待できる。さらに、これら合金元素を含有するチタン合金スクラップを添加素材とすることで、コスト低減も期待できる。
［溶融再凝固層の厚みの測定方法］
　本発明では、α安定化元素もしくは中性元素の合金元素が濃化した溶融再凝固層が深さ１ｍｍ以上であることを規定している。この溶融再凝固層の厚みの測定方法について説明する。この濃化層は断面の埋め込み研磨試料をＳＥＭ（Ｓｃａｎｉｎｇ　Ｅｌｅｃｔｒｏｎ　Ｍｉｃｒｏｓｃｏｐｙ）／ＥＰＭＡ（Ｅｌｅｃｔｒｏｎ　Ｐｒｏｂｅ　ＭｉｃｒｏＡｎａｌｙｓｅｒ）により容易に判別できる。図１に融再凝固層の濃度変化の模式図を示す。α安定化元素や中性元素を添加しているため、溶融再凝固層では母層部に比べてα安定化元素や中性元素の濃度が高くなっており、この厚みを溶融再凝固層の厚みとした。なお、溶融再凝固層がＳＥＭ／ＥＰＭＡの測定範囲より大きい場合は、厚み方向を何回かに分けて測定し、それら結果を付け合わせることで溶湯再凝固層厚を測定した。
［溶融部および母材部の元素濃度の測定方法］
　溶融再凝固層および母材部の濃度については、上記の濃度が上昇した部位および素材の中心部より分析用の試験片を切りだし、ＩＣＰ発光分光分析を行うことで求めた。濃度の測定は、チタン鋳片の圧延面の任意の複数箇所（例えば１０箇所）の表層１ｍｍ以内から分析サンプルを採取し、ＩＣＰ発光分光分析を行い、それらの平均値を溶融再凝固層の濃度とすることができる。また、比較として、チタン鋳片の表層を再溶融する前にチタン鋳片の圧延面の任意の複数箇所（例えば３箇所）の表層２０ｍｍ以内から分析サンプルを採取して、同様にＩＣＰ発光分光分析を行い、その平均値を母材部の濃度とすることができる。
[添加方法]
　本発明では、インゴットの表層部にα安定化元素もしくは中性元素の内一種類以上を濃化させる手法として、これら元素の内一種類以上からなる素材とともにインゴット表層部を溶融させることとしている。こうすることで、インゴットの表層部のこれら元素の濃度を高めることができる。さらに、これら元素を含有するチタン合金を使用してもよい。そうすることで、これら元素とともにβ安定化元素も簡単に添加することができる。素材としては、粉末、チップ、ワイヤー、薄膜、切り粉のうちの一種または二種以上を組み合わせて用いることができる。
［表層溶融の方法］
　本発明では、α安定化元素もしくは中性元素の内一種類以上からなる素材とともにチタン材表層部を加熱し、溶融再凝固させることを特徴としている。表層部の加熱方法としては、電子ビーム加熱、誘導加熱、アーク加熱、プラズマ加熱およびレーザー加熱のうち一種または二種以上を組み合わせて用いることができる。上記の方法を組み合わせて用いる場合、例えば、誘導加熱で予熱した後の、レーザー加熱によって表層溶融することができる。コスト、チタン材のサイズ、処理時間などの条件を考慮し、これらの中から採用すればよい。本発明は、真空もしくは不活性ガス雰囲気でチタン材表層部を加熱すると好ましい。チタンは非常に活性な金属であるため、大気中で処理をした場合、溶融再凝固部に酸素や窒素が多量に混入してしまい品質が変化してしまう。そのため、真空あるいは不活性雰囲気とした容器内で行うと良好な結果を得ることができる。なお、本発明における不活性ガスはアルゴンおよびヘリウムを指し、チタンと反応する窒素は含まない。真空容器内で行う場合の真空度は、５×１０-5Ｔｏｒｒ程度か、より高い真空度であることが望ましい。
　本発明では、表層に深さ１ｍｍ以上の上記範囲でα安定化元素もしくは中性元素の内一種類以上が濃化した溶融再凝固層を有し、その他の部分が鋳造ままもしくは鋳造後β変態点以上に加熱後急冷した組織である熱間圧延用チタン材を特徴としている。この素材を用いることで、分塊工程を省略した場合でも、通常の分塊工程を経る場合と同等の表面品質を有するチタン材を得ることができる。
　以下、実施例により本発明を詳しく説明する。表１のＮｏ．１～１９は板材を対象にした例、Ｎｏ．２０～２６は線材を対象にした例である。
Figure JPOXMLDOC01-appb-T000001
　表１のＮｏ．１から１９に示す参考例、実施例および比較例において、チタン鋳片の製造は、電子ビーム溶解法で行い、角型鋳型にて鋳造した。その後、鋳肌の切削手入れのある場合においては、切削によりチタン鋳片の表層の手入れを行い、切削手入れが無い場合は、切削による表層の手入れを行わずに、表層溶融を行った。その後、厚さ２５０ｍｍ×幅１０００ｍｍ×長さ４５００ｍｍのインゴットから、鉄鋼材料の熱間圧延設備を用いて、熱間圧延を行い、厚さ４ｍｍの帯状コイルとした。なお、表面疵の評価は、酸洗後の板表層を目視にて行った。
　Ｎｏ．１から６の参考例、実施例および比較例は、インゴット製造後にインゴット（鋳片）の鋳肌を切削除去している。一方、Ｎｏ．６から３１の実施例は、インゴット製造後の鋳肌に溶融再凝固処理を施している。
　表１の「溶融方法」に「ＥＢ」と記載したものは電子ビームによって表層の溶融再凝固を行い、「ＴＩＧ」と記載したものはＴＩＧ溶接によって表層の溶融再凝固を行い、「レーザー」と記載したものは、レーザー溶接によって表層の溶融再凝固を行っている。電子ビームによる表層溶融は、規定出力３０ｋＷの電子ビーム溶接装置を用いた。ＴＩＧ溶接による表層溶融は、２００Ａで溶加材を用いないで行った。レーザー溶接による表層溶融は、ＣＯ２レーザーを用いた。
　Ｎｏ．１に記載の参考例は工業用純チタンインゴットを用いて、従来の分塊工程をたどる方法で製造した場合である。分塊工程を経るため、製造された板材の表面疵は、軽微である。
　Ｎｏ．２に記載の比較例は、インゴットを切削手入れ後、α相安定化元素や中性元素を添加せずにインゴット表面を、ＥＢにより表層溶融処理を施している。そのため、再溶融凝固層の厚みは１ｍｍ以上と深く、疵は軽微な傾向にあるものの一部で発生しており悪化傾向にある。
　Ｎｏ．３に記載の比較例は、インゴットを切削手入れ後、Ａｌ粉末と共にインゴット表面を、ＥＢにより表層溶融処理を施しているが、再溶融凝固部のＡｌの含有量が母材部に比べ０．１％以上と十分多いが、厚みが０．５ｍｍと浅いため、部分的にやや粗大な表面疵が観察された。
　Ｎｏ．４に記載の実施例は、インゴットを切削手入れ後、Ａｌチップと共にインゴット表面を、ＥＢにより表層溶融処理を施しており、再溶融凝固層のＡｌの含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．５に記載の実施例は、インゴットを切削手入れ後、Ａｌ箔と共にインゴット表面を、レーザーにより表層溶融処理を施しており、再溶融凝固層のＡｌの含有量が母材部に比べ０．１％以上と十分多く、Ａｌ濃化層の厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．６に記載の実施例は、インゴットを切削手入れ後、Ａｌ箔と共にインゴット表面を、ＴＩＧより表層溶融処理を施しており、再溶融凝固層のＡｌの含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．７に記載の実施例は、インゴットを切削せず、Ａｌ粉末と共にインゴット表面を、ＥＢにより表層溶融処理を施しており、再溶融凝固層のＡｌの含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．８に記載の実施例は、インゴットを切削せず、Ｓｎ粉末と共にインゴット表面を、ＥＢにより表層溶融処理を施しており、再溶融凝固層のＳｎの含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．９に記載の実施例は、インゴットを切削せず、Ｚｒ切り粉と共にインゴット表面を、ＥＢにより表層溶融処理を施しており、再溶融凝固層のＺｒの含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．１０に記載の実施例は、インゴットを切削せず、Ａｌ及びＺｒの切り粉と共にインゴット表面を、ＴＩＧにより表層溶融処理を施しており、再溶融凝固層のＡｌとＺｒの合計含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．１１に記載の実施例は、インゴットを切削せず、ＡｌとＳｎを含有するチタン合金の切り粉と共にインゴット表面を、ＴＩＧにより表層溶融処理を施しており、再溶融凝固層のＡｌとＳｎの含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．１２から１５に記載の実施例は、インゴットを切削せず、Ａｌ及びβ相安定化元素を含有するチタン合金の切り粉と共にインゴット表面を、ＴＩＧにより表層溶融処理を施しており、再溶融凝固層のＡｌの含有量が母材部に比べ０．１％以上と十分多く、β相安定化元素の含有量も１．５％以下と少ない。さらに、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．１６に記載の実施例は、インゴットを切削せず、Ａｌチップと共にインゴット表面を、ＥＢにより表層溶融処理を施しており、再溶融凝固層のＡｌの含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．１７に記載の実施例は、インゴットを切削せず、Ｓｎ粉末と共にインゴット表面を、ＴＩＧにより表層溶融処理を施しており、再溶融凝固層のＳｎの含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．１８およびＮｏ．１９に記載の実施例は純チタン３種および４種からなるインゴットを切削せず、Ａｌ粉末と共にインゴット表面を、ＥＢにより表層溶融処理を施しており、再溶融凝固層のＡｌの含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　表１のＮｏ．２０からＮｏ．２６に示す参考例、比較例および実施例において、工業用純チタン２種材を用い、チタンインゴットの製造は真空アーク溶解法もしくは電子ビーム溶解法で行った。直径１７０ｍｍ×１２ｍ長のインゴットから、熱間圧延により直径１３ｍｍの線材を製造した。なお、表面疵の評価は、酸洗後の板表層を目視にて行った。
　Ｎｏ．２０から２４の参考例、比較例および実施例は、インゴット製造後にインゴットの鋳肌を切削除去している。一方、Ｎｏ．２５、２６の実施例は、インゴット製造後の鋳肌に溶融再凝固処理を施している。
　Ｎｏ．２０に記載の参考例は、従来の分塊工程をたどる方法で製造した場合である。
　Ｎｏ．２１に記載の比較例は、インゴットを切削手入れ後、α相安定化元素や中性元素を添加せずにインゴット表面を、ＥＢにより表層溶融処理を施している。そのため、再溶融凝固部の厚みは１ｍｍ以上と深く、疵は軽微な傾向にあるものの一部で発生しており悪化傾向にある。
　Ｎｏ．２２に記載の比較例は、インゴットを切削手入れ後、Ａｌ箔と共にインゴット表面を、ＥＢにより表層溶融処理を施しているが、再溶融凝固部のＡｌの含有量が母材部に比べ０．１％以上と十分多いが、厚みが０．５ｍｍと浅いため、部分的にやや粗大な表面疵が観察された。
　Ｎｏ．２３に記載の実施例は、インゴットを切削手入れ後、Ａｌ箔と共にインゴット表面を、ＥＢにより表層溶融処理を施しており、再溶融凝固層のＡｌの含有量が母材部に比べ０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．２４に記載の実施例は、インゴットを切削手入れ後、Ａｌ箔と共にインゴット表面を、ＴＩＧにより表層溶融処理を施しており、再溶融凝固層のＡｌの含有量が０．１％以上と十分多く、厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．２５に記載の実施例は、インゴットを切削手入れ後、Ｓｎ粉末と共にインゴット表面を、レーザーにより表層溶融処理を施しており、再溶融凝固層のＳｎの含有量が母材部に比べ０．１％以上と十分多く、Ａｌ濃化層の厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。
　Ｎｏ．２６に記載の実施例は、インゴットを切削手入れ後、Ａｌ箔と共にインゴット表面を、ＥＢにより表層溶融処理を施しており、再溶融凝固層のＡｌの含有量が母材部に比べ０．１％以上と十分多く、Ａｌ濃化層の厚みが１ｍｍ以上と深いため、表面疵は軽微であり、分塊工程をたどる場合と同等レベルであった。

Claims (8)

  1. 　工業用純チタンからなるチタン鋳片であって、
    　圧延面となる表面に、α相安定化元素、中性元素の何れか一方もしくは両方のうち一種または二種類以上の元素を添加して溶融させ再凝固させた溶融再凝固層を深さ１ｍｍ以上の範囲に有し、
    　深さ１ｍｍまでの範囲におけるα相安定化元素と中性元素の合計の濃度が、母材中のα相安定化元素と中性元素の合計の濃度に比較して、質量％で、０．１％以上、２．０％未満高いことを特徴とする、熱間圧延用チタン鋳片。
  2. 　α相安定化元素、中性元素がＡｌ，Ｓｎ，Ｚｒである、請求項１に記載の熱間圧延用チタン鋳片。
  3. 　さらに、溶融再凝固相にβ相安定化元素の一種もしくは二種類以上を質量％で１．５％以下含有する、請求項１に記載の熱間圧延用チタン鋳片。
  4. 　前記再溶融凝固層よりも内側は、鋳造ままの組織もしくは鋳造後にβ域に加熱され、その後冷却された組織である、請求項１に記載の熱間圧延用チタン鋳片。
  5. 　チタン鋳片の圧延面となる表面を、α相安定化元素、中性元素の何れか一方もしくは両方のうち一種または二種類以上の元素を含有する素材とともに溶融させた後、凝固させる、熱間圧延用チタン鋳片の製造方法。
  6. 　前記α相安定化元素、中性元素の何れか一方もしくは両方のうち一種または二種類以上の元素を含有する素材が、粉末、チップ、ワイヤー、薄膜、切り粉のうちの一種または二種以上である、請求項５に記載の熱間圧延用チタン鋳片の製造方法。
  7. 　チタン鋳片の表面を、電子ビーム加熱、アーク加熱、レーザー加熱、プラズマ加熱、および誘導加熱のうちの一種または二種以上を用いて溶融させる、請求項５に記載の熱間圧延用チタン鋳片の製造方法。
  8. 　真空もしくは不活性ガス雰囲気でチタン鋳片の表面を溶融させる、請求項５に記載の熱間圧延用チタン鋳片の製造方法。
PCT/JP2014/076084 2014-09-30 2014-09-30 表面疵の発生し難い熱間圧延用チタン鋳片およびその製造方法 WO2016051503A1 (ja)