WO2016017778A1 - Composition de peinture - Google Patents

Composition de peinture Download PDF

Info

Publication number
WO2016017778A1
WO2016017778A1 PCT/JP2015/071710 JP2015071710W WO2016017778A1 WO 2016017778 A1 WO2016017778 A1 WO 2016017778A1 JP 2015071710 W JP2015071710 W JP 2015071710W WO 2016017778 A1 WO2016017778 A1 WO 2016017778A1
Authority
WO
WIPO (PCT)
Prior art keywords
acid
coating
coating composition
meth
compound
Prior art date
Application number
PCT/JP2015/071710
Other languages
English (en)
Japanese (ja)
Inventor
千尋 長野
達也 東
誠 安原
直人 松島
Original Assignee
関西ペイント株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 関西ペイント株式会社 filed Critical 関西ペイント株式会社
Priority to CN201580036978.6A priority Critical patent/CN106536652B/zh
Priority to JP2016538450A priority patent/JP6524090B2/ja
Publication of WO2016017778A1 publication Critical patent/WO2016017778A1/fr

Abstract

L'invention a pour objet de fournir un film de revêtement matant excellant en termes de stabilité d'éclat, de résistance aux alcalins, de stabilité au stockage et de résistance au choc. Plus précisément, l'invention concerne une composition de peinture qui est caractéristique en ce qu'elle contient une résine pour formation de film (A) et un agent de matité (B), et qui contient également une dispersion de polymère non aqueuse (C) constituée d'un composant peau et d'un composant noyau et/ou un composé polyisocyanate séquencé (D). La dispersion de polymère non aqueuse (C) comprend : un produit d'autocondensation d'acides gras possédant un groupe hydroxyalkyl de 10 à 25 atomes de carbone de polymère acrylique et/ou de chaîne alkyl ; et un macromonomère possédant en moyenne un groupe insaturé polymérisable ou plus par molécule, en tant qu'au moins une partie de composant peau. Enfin, le composé polyisocyanate séquencé (D) consiste en un composé polyisocyanate séquencé à base de méthylène actif dans lequel un composé de désorption lors d'une réaction de réticulation soumet un alcool monofonctionnel de 3 à 12 atomes de carbone à une désorption.
PCT/JP2015/071710 2014-07-30 2015-07-30 Composition de peinture WO2016017778A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201580036978.6A CN106536652B (zh) 2014-07-30 2015-07-30 涂料组合物
JP2016538450A JP6524090B2 (ja) 2014-07-30 2015-07-30 塗料組成物

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014-154437 2014-07-30
JP2014154437 2014-07-30

Publications (1)

Publication Number Publication Date
WO2016017778A1 true WO2016017778A1 (fr) 2016-02-04

Family

ID=55217674

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/071710 WO2016017778A1 (fr) 2014-07-30 2015-07-30 Composition de peinture

Country Status (3)

Country Link
JP (1) JP6524090B2 (fr)
CN (1) CN106536652B (fr)
WO (1) WO2016017778A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2020059763A (ja) * 2018-10-04 2020-04-16 旭化成株式会社 ポリイソシアネート組成物、塗料組成物及び塗膜
WO2020115984A1 (fr) 2018-12-07 2020-06-11 関西ペイント株式会社 Composition de revêtement
WO2020137161A1 (fr) * 2018-12-25 2020-07-02 日本ペイント・オートモーティブコーティングス株式会社 Composition de revêtement transparente et procédé de formation d'un film de revêtement transparent
JP2021091764A (ja) * 2019-12-09 2021-06-17 荒川化学工業株式会社 コーティング剤、硬化物及びフィルム
WO2022124372A1 (fr) * 2020-12-11 2022-06-16 日本ペイント・オートモーティブコーティングス株式会社 Composition de revêtement mat, article revêtu et procédé de production d'un article revêtu

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6869184B2 (ja) * 2015-10-01 2021-05-12 関西ペイント株式会社 塗料組成物
CN116144256B (zh) * 2023-01-10 2024-07-05 东风汽车集团股份有限公司 一种适用于水性三涂一烘生产线的亚光清漆及其涂装方法

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5525401A (en) * 1978-08-10 1980-02-23 Kansai Paint Co Ltd High solid coating composition
JPH04261473A (ja) * 1991-02-14 1992-09-17 Kansai Paint Co Ltd 防汚塗料組成物
JPH05117548A (ja) * 1991-10-24 1993-05-14 Kansai Paint Co Ltd 艶消し塗料組成物
JPH0641496A (ja) * 1992-07-21 1994-02-15 Kansai Paint Co Ltd 塗料組成物、塗膜形成方法及び塗装物品
JPH08295839A (ja) * 1995-04-26 1996-11-12 Dainippon Ink & Chem Inc 塗料用樹脂組成物
JP2001226411A (ja) * 2000-02-16 2001-08-21 Kansai Paint Co Ltd 非水重合体分散液及びこの重合体を含有する塗料組成物
JP2004256582A (ja) * 2003-02-24 2004-09-16 Nippon Steel Corp プレコート金属板用水系塗料、プレコート塗装金属板およびその製造方法
JP2004535474A (ja) * 2000-12-14 2004-11-25 バイエル アクチェンゲゼルシャフト Ｈｄｉ系ブロックポリイソシアネート
JP2007501297A (ja) * 2003-08-02 2007-01-25 ビーエーエスエフ　コーティングス　アクチェンゲゼルシャフト 透明な熱硬化性被覆材料、その製法およびその使用
WO2012063756A1 (fr) * 2010-11-08 2012-05-18 関西ペイント株式会社 Composition de revêtement antitache ayant une excellente durabilité

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS53231A (en) * 1976-06-23 1978-01-05 Kansai Paint Co Ltd Thermosetting, high-solid coating composition
JP2000290493A (ja) * 1999-04-09 2000-10-17 Asahi Chem Ind Co Ltd ブロックポリイソシアネート組成物
EP2695902B1 (fr) * 2011-04-08 2023-08-02 Kansai Paint Co., Ltd Composé polyisocyanate bloqué

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5525401A (en) * 1978-08-10 1980-02-23 Kansai Paint Co Ltd High solid coating composition
JPH04261473A (ja) * 1991-02-14 1992-09-17 Kansai Paint Co Ltd 防汚塗料組成物
JPH05117548A (ja) * 1991-10-24 1993-05-14 Kansai Paint Co Ltd 艶消し塗料組成物
JPH0641496A (ja) * 1992-07-21 1994-02-15 Kansai Paint Co Ltd 塗料組成物、塗膜形成方法及び塗装物品
JPH08295839A (ja) * 1995-04-26 1996-11-12 Dainippon Ink & Chem Inc 塗料用樹脂組成物
JP2001226411A (ja) * 2000-02-16 2001-08-21 Kansai Paint Co Ltd 非水重合体分散液及びこの重合体を含有する塗料組成物
JP2004535474A (ja) * 2000-12-14 2004-11-25 バイエル アクチェンゲゼルシャフト Ｈｄｉ系ブロックポリイソシアネート
JP2004256582A (ja) * 2003-02-24 2004-09-16 Nippon Steel Corp プレコート金属板用水系塗料、プレコート塗装金属板およびその製造方法
JP2007501297A (ja) * 2003-08-02 2007-01-25 ビーエーエスエフ　コーティングス　アクチェンゲゼルシャフト 透明な熱硬化性被覆材料、その製法およびその使用
WO2012063756A1 (fr) * 2010-11-08 2012-05-18 関西ペイント株式会社 Composition de revêtement antitache ayant une excellente durabilité

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2020059763A (ja) * 2018-10-04 2020-04-16 旭化成株式会社 ポリイソシアネート組成物、塗料組成物及び塗膜
JP7206089B2 (ja) 2018-10-04 2023-01-17 旭化成株式会社 ポリイソシアネート組成物、塗料組成物及び塗膜
WO2020115984A1 (fr) 2018-12-07 2020-06-11 関西ペイント株式会社 Composition de revêtement
WO2020137161A1 (fr) * 2018-12-25 2020-07-02 日本ペイント・オートモーティブコーティングス株式会社 Composition de revêtement transparente et procédé de formation d'un film de revêtement transparent
JP2020100783A (ja) * 2018-12-25 2020-07-02 日本ペイント・オートモーティブコーティングス株式会社 クリヤー塗料組成物及びクリヤー塗膜の形成方法
JP2021091764A (ja) * 2019-12-09 2021-06-17 荒川化学工業株式会社 コーティング剤、硬化物及びフィルム
KR20210072718A (ko) * 2019-12-09 2021-06-17 아라까와 가가꾸 고교 가부시끼가이샤 코팅제, 경화물 및 필름
JP7047831B2 (ja) 2019-12-09 2022-04-05 荒川化学工業株式会社 コーティング剤、硬化物及びフィルム
KR102577871B1 (ko) 2019-12-09 2023-09-12 아라까와 가가꾸 고교 가부시끼가이샤 코팅제, 경화물 및 필름
WO2022124372A1 (fr) * 2020-12-11 2022-06-16 日本ペイント・オートモーティブコーティングス株式会社 Composition de revêtement mat, article revêtu et procédé de production d'un article revêtu
JP2022092772A (ja) * 2020-12-11 2022-06-23 日本ペイント・オートモーティブコーティングス株式会社 艶消し塗料組成物および塗装物品、ならびに塗装物品の製造方法
JP7453132B2 (ja) 2020-12-11 2024-03-19 日本ペイント・オートモーティブコーティングス株式会社 艶消し塗料組成物および塗装物品、ならびに塗装物品の製造方法

Also Published As

Publication number Publication date
CN106536652B (zh) 2019-08-16
CN106536652A (zh) 2017-03-22
JPWO2016017778A1 (ja) 2017-05-25
JP6524090B2 (ja) 2019-06-05

Similar Documents

Publication Publication Date Title
JP6524090B2 (ja) 塗料組成物
JP6275447B2 (ja) 塗料組成物及び複層塗膜形成方法
JP7043621B2 (ja) 複層塗膜形成方法
CA2869137C (fr) Composition aqueuse de peinture et procede de fabrication d'un article peint
JP5451207B2 (ja) 水性塗料組成物及び複層塗膜形成方法
JP5630833B2 (ja) 塗料組成物および該塗料組成物を用いた塗膜形成方法
JP7187483B2 (ja) 塗料組成物
JP6392801B2 (ja) 複層塗膜形成方法
JP2009530425A (ja) 塗料組成物及び塗膜形成方法
JPWO2010047195A1 (ja) 塗料組成物及び塗膜形成方法
JP6732913B2 (ja) 塗料組成物
JP2014177598A (ja) 艶消し塗料組成物
WO2022107847A1 (fr) Composition de matériau de revêtement à haut extrait sec, et procédé de formation de film de revêtement multicouche
JP6230473B2 (ja) 塗料組成物及び複層塗膜形成方法
WO2022107848A1 (fr) Composition de matériau de revêtement à haut extrait sec, et procédé de formation de film de revêtement multicouche
JP5015884B2 (ja) 複層塗膜形成方法
JP2021138819A (ja) 塗料組成物及び複層塗膜形成方法
WO2020166197A1 (fr) Modificateur de viscosité et composition de peinture
JP7200444B1 (ja) 高固形分塗料組成物及び複層塗膜形成方法
JP5416385B2 (ja) 塗料組成物及び塗膜形成方法
CN113166578B (zh) 涂料组合物
JP7355968B1 (ja) 水性塗料組成物、塗膜形成方法及び複層塗膜形成方法
JP7352766B1 (ja) 複層塗膜形成方法
JP7389538B2 (ja) 有機ケイ素化合物の加水分解縮合物分散液の製造方法
WO2024018708A1 (fr) Composition de matériau de revêtement aqueux, procédé de formation de film de revêtement, et procédé de formation de film de revêtement multicouche

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15827574

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2016538450

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15827574

Country of ref document: EP

Kind code of ref document: A1