WO2015041286A1 - Membrane à fibre creuse poreuse et son procédé de fabrication - Google Patents
Membrane à fibre creuse poreuse et son procédé de fabrication Download PDFInfo
- Publication number
- WO2015041286A1 WO2015041286A1 PCT/JP2014/074680 JP2014074680W WO2015041286A1 WO 2015041286 A1 WO2015041286 A1 WO 2015041286A1 JP 2014074680 W JP2014074680 W JP 2014074680W WO 2015041286 A1 WO2015041286 A1 WO 2015041286A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- hollow fiber
- fiber membrane
- porous
- porous hollow
- film
- Prior art date
Abstract
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2014548799A JP6020592B2 (ja) | 2013-09-18 | 2014-09-18 | 多孔質中空糸膜及びその製造方法 |
KR1020167007460A KR101826451B1 (ko) | 2013-09-18 | 2014-09-18 | 다공질 중공사막 및 그의 제조 방법 |
CN201480061790.2A CN105722585A (zh) | 2013-09-18 | 2014-09-18 | 多孔质中空纤维膜及其制造方法 |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2013193213 | 2013-09-18 | ||
JP2013193214 | 2013-09-18 | ||
JP2013-193213 | 2013-09-18 | ||
JP2013-193214 | 2013-09-18 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2015041286A1 true WO2015041286A1 (fr) | 2015-03-26 |
Family
ID=52688933
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2014/074680 WO2015041286A1 (fr) | 2013-09-18 | 2014-09-18 | Membrane à fibre creuse poreuse et son procédé de fabrication |
Country Status (4)
Country | Link |
---|---|
JP (2) | JP6020592B2 (fr) |
KR (1) | KR101826451B1 (fr) |
CN (1) | CN105722585A (fr) |
WO (1) | WO2015041286A1 (fr) |
Cited By (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP3056261A4 (fr) * | 2013-10-11 | 2016-09-28 | Mitsubishi Rayon Co | Membrane poreuse creuse |
JP2017056387A (ja) * | 2015-09-15 | 2017-03-23 | 三菱レイヨン株式会社 | 多孔質中空糸膜の製造方法 |
WO2017131209A1 (fr) * | 2016-01-29 | 2017-08-03 | 東レ株式会社 | Membrane de séparation |
JP2017170319A (ja) * | 2016-03-23 | 2017-09-28 | 旭化成株式会社 | ポリフッ化ビニリデン製多孔膜とその製造方法 |
JP2018012058A (ja) * | 2016-07-20 | 2018-01-25 | 三菱ケミカル株式会社 | 多孔質膜 |
WO2018021545A1 (fr) * | 2016-07-29 | 2018-02-01 | 東レ株式会社 | Membrane de séparation et son procédé de fabrication |
WO2020059344A1 (fr) * | 2018-09-20 | 2020-03-26 | 住友電気工業株式会社 | Membranes à fibres creuses |
EP3574987A4 (fr) * | 2017-02-28 | 2020-12-09 | Toray Industries, Inc. | Membrane composite à fibres creuses et son procédé de fabrication |
US10974204B2 (en) | 2016-06-17 | 2021-04-13 | Asahi Kasei Kabushiki Kaisha | Porous membrane and process for producing porous membrane |
KR20220057247A (ko) * | 2020-10-29 | 2022-05-09 | 서울대학교산학협력단 | 성장체의 제조방법 및 이에 의해 제조된 성장체 |
WO2023276614A1 (fr) * | 2021-06-28 | 2023-01-05 | 旭化成株式会社 | Membrane d'osmose directe et module de membrane d'osmose directe comprenant celle-ci |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP7204382B2 (ja) * | 2017-09-07 | 2023-01-16 | 旭化成株式会社 | 多孔質膜を用いた醤油の製造方法 |
JP7182960B2 (ja) * | 2017-09-07 | 2022-12-05 | 旭化成株式会社 | 多孔質膜を用いた醤油の製造方法 |
WO2021153486A1 (fr) | 2020-01-28 | 2021-08-05 | 東レ株式会社 | Procédé de filtrage d'huile |
KR102316399B1 (ko) * | 2021-05-27 | 2021-10-22 | 김기영 | 샌드코어 조립 자동화 시스템 |
WO2023074670A1 (fr) * | 2021-10-29 | 2023-05-04 | 株式会社クラレ | Membrane poreuse et procédé de fabrication de membrane poreuse |
Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS61502902A (ja) * | 1984-06-13 | 1986-12-11 | エンスチチユ ナシヨナル ド リシエルシユ シミク アプリケ | 中空繊維、その製造法および特に膜型分離の分野でのその応用 |
WO1995033549A1 (fr) * | 1994-06-07 | 1995-12-14 | Mitsubishi Rayon Co., Ltd. | Membrane poreuse a base de polysulfone et procede de production de cette membrane |
JP2000117070A (ja) * | 1998-10-16 | 2000-04-25 | Nitto Denko Corp | 限外濾過膜及びその製造方法 |
JP2004025067A (ja) * | 2002-06-26 | 2004-01-29 | Mitsubishi Rayon Co Ltd | 多孔質中空糸膜の製造方法及び製造装置 |
WO2007043553A1 (fr) * | 2005-10-13 | 2007-04-19 | Asahi Kasei Chemicals Corporation | Membrane en fibres creuses multicouche poreuse et processus de production correspondant |
JP2008126199A (ja) * | 2006-11-24 | 2008-06-05 | Mitsubishi Rayon Co Ltd | 中空状多孔質膜およびその製造方法 |
WO2009142279A1 (fr) * | 2008-05-21 | 2009-11-26 | 三菱レイヨン株式会社 | Membrane poreuse creuse et son procédé de fabrication |
JP2012110856A (ja) * | 2010-11-26 | 2012-06-14 | Mitsubishi Rayon Co Ltd | 中空状多孔質膜の製造装置 |
WO2013137379A1 (fr) * | 2012-03-14 | 2013-09-19 | 三菱レイヨン株式会社 | Dispositif de production d'un film poreux creux et procédé associé |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS59160506A (ja) * | 1983-02-28 | 1984-09-11 | Kuraray Co Ltd | 複合中空糸分離膜およびその製造法 |
-
2014
- 2014-09-18 CN CN201480061790.2A patent/CN105722585A/zh active Pending
- 2014-09-18 JP JP2014548799A patent/JP6020592B2/ja active Active
- 2014-09-18 WO PCT/JP2014/074680 patent/WO2015041286A1/fr active Application Filing
- 2014-09-18 KR KR1020167007460A patent/KR101826451B1/ko not_active Application Discontinuation
-
2016
- 2016-08-08 JP JP2016155863A patent/JP2016196004A/ja active Pending
Patent Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS61502902A (ja) * | 1984-06-13 | 1986-12-11 | エンスチチユ ナシヨナル ド リシエルシユ シミク アプリケ | 中空繊維、その製造法および特に膜型分離の分野でのその応用 |
WO1995033549A1 (fr) * | 1994-06-07 | 1995-12-14 | Mitsubishi Rayon Co., Ltd. | Membrane poreuse a base de polysulfone et procede de production de cette membrane |
JP2000117070A (ja) * | 1998-10-16 | 2000-04-25 | Nitto Denko Corp | 限外濾過膜及びその製造方法 |
JP2004025067A (ja) * | 2002-06-26 | 2004-01-29 | Mitsubishi Rayon Co Ltd | 多孔質中空糸膜の製造方法及び製造装置 |
WO2007043553A1 (fr) * | 2005-10-13 | 2007-04-19 | Asahi Kasei Chemicals Corporation | Membrane en fibres creuses multicouche poreuse et processus de production correspondant |
JP2008126199A (ja) * | 2006-11-24 | 2008-06-05 | Mitsubishi Rayon Co Ltd | 中空状多孔質膜およびその製造方法 |
WO2009142279A1 (fr) * | 2008-05-21 | 2009-11-26 | 三菱レイヨン株式会社 | Membrane poreuse creuse et son procédé de fabrication |
JP2012110856A (ja) * | 2010-11-26 | 2012-06-14 | Mitsubishi Rayon Co Ltd | 中空状多孔質膜の製造装置 |
WO2013137379A1 (fr) * | 2012-03-14 | 2013-09-19 | 三菱レイヨン株式会社 | Dispositif de production d'un film poreux creux et procédé associé |
Cited By (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP3056261A4 (fr) * | 2013-10-11 | 2016-09-28 | Mitsubishi Rayon Co | Membrane poreuse creuse |
JP2017056387A (ja) * | 2015-09-15 | 2017-03-23 | 三菱レイヨン株式会社 | 多孔質中空糸膜の製造方法 |
JPWO2017131209A1 (ja) * | 2016-01-29 | 2018-11-29 | 東レ株式会社 | 分離膜 |
WO2017131209A1 (fr) * | 2016-01-29 | 2017-08-03 | 東レ株式会社 | Membrane de séparation |
US10799837B2 (en) | 2016-01-29 | 2020-10-13 | Toray Industries, Inc. | Separation membrane |
JP2017170319A (ja) * | 2016-03-23 | 2017-09-28 | 旭化成株式会社 | ポリフッ化ビニリデン製多孔膜とその製造方法 |
US10974204B2 (en) | 2016-06-17 | 2021-04-13 | Asahi Kasei Kabushiki Kaisha | Porous membrane and process for producing porous membrane |
JP2018012058A (ja) * | 2016-07-20 | 2018-01-25 | 三菱ケミカル株式会社 | 多孔質膜 |
WO2018021545A1 (fr) * | 2016-07-29 | 2018-02-01 | 東レ株式会社 | Membrane de séparation et son procédé de fabrication |
EP3574987A4 (fr) * | 2017-02-28 | 2020-12-09 | Toray Industries, Inc. | Membrane composite à fibres creuses et son procédé de fabrication |
US11369925B2 (en) | 2017-02-28 | 2022-06-28 | Toray Industries, Inc. | Composite hollow-fiber membrane and production method therefor |
WO2020059344A1 (fr) * | 2018-09-20 | 2020-03-26 | 住友電気工業株式会社 | Membranes à fibres creuses |
KR20220057247A (ko) * | 2020-10-29 | 2022-05-09 | 서울대학교산학협력단 | 성장체의 제조방법 및 이에 의해 제조된 성장체 |
KR102412426B1 (ko) | 2020-10-29 | 2022-06-23 | 서울대학교산학협력단 | 성장체의 제조방법 및 이에 의해 제조된 성장체 |
WO2023276614A1 (fr) * | 2021-06-28 | 2023-01-05 | 旭化成株式会社 | Membrane d'osmose directe et module de membrane d'osmose directe comprenant celle-ci |
Also Published As
Publication number | Publication date |
---|---|
CN105722585A (zh) | 2016-06-29 |
KR20160044582A (ko) | 2016-04-25 |
JP2016196004A (ja) | 2016-11-24 |
JPWO2015041286A1 (ja) | 2017-03-02 |
JP6020592B2 (ja) | 2016-11-02 |
KR101826451B1 (ko) | 2018-02-06 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP6020592B2 (ja) | 多孔質中空糸膜及びその製造方法 | |
JP4050977B2 (ja) | 編物により補強された複合中空糸膜 | |
KR102031395B1 (ko) | 상용성 브레이드화 지지체 필라멘트를 갖는 복합 중공 섬유 막 | |
JP5433921B2 (ja) | 高分子多孔質中空糸膜 | |
JP6694326B2 (ja) | 複合膜 | |
JP5798680B2 (ja) | 加圧式中空糸膜モジュール | |
Moattari et al. | Reinforced hollow fiber membranes: A comprehensive review | |
JP5609116B2 (ja) | 耐ファウリング性に優れる中空糸型限外ろ過膜 | |
JP2019022893A (ja) | 中空状多孔質膜及びその製造方法 | |
CN111107926A (zh) | 多孔中空丝膜和其制造方法 | |
JP2007313491A (ja) | 低汚染性フッ化ビニリデン系樹脂多孔水処理膜およびその製造方法 | |
US10413869B2 (en) | Composite hollow fiber membrane and manufacturing method thereof | |
JP6221949B2 (ja) | 多孔質中空糸膜膜の製造方法及び孔質中空糸膜膜 | |
CN109070011B (zh) | 中空丝膜 | |
WO2014003140A1 (fr) | Membrane composite semi-perméable et élément de membrane composite semi-perméable | |
Rahman et al. | Effect of the addition of the surfactant Tetronic 1307 on poly (ether sulfone) porous hollow‐fiber membrane formation | |
WO2013180272A1 (fr) | Film poreux creux | |
KR101050591B1 (ko) | 관형 편직물 및 이를 이용한 복합 중공사막 | |
KR20130047226A (ko) | 막의 물성이 개선된 수처리용 pvdf 분리막 및 이의 제조방법 | |
JP2017144390A (ja) | 複合膜 | |
KR20100078481A (ko) | 거대기공이 없는 중공사 분리막 및 그 제조방법 | |
WO2023276614A1 (fr) | Membrane d'osmose directe et module de membrane d'osmose directe comprenant celle-ci | |
JP2005058906A (ja) | 高分子多孔質膜、血液浄化器および高分子多孔質膜の製造方法 | |
KR101226400B1 (ko) | 관형 편직물 및 이를 이용하는 복합 중공사막 | |
JP2005211784A (ja) | 多孔質膜およびその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
ENP | Entry into the national phase |
Ref document number: 2014548799 Country of ref document: JP Kind code of ref document: A |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 14846105 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: 20167007460 Country of ref document: KR Kind code of ref document: A |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 14846105 Country of ref document: EP Kind code of ref document: A1 |