WO2013100477A1 - 다이싱 다이본딩 필름 및 다이싱 다이본딩 필름에 홈을 형성하는 방법 - Google Patents

다이싱 다이본딩 필름 및 다이싱 다이본딩 필름에 홈을 형성하는 방법 Download PDF

Info

Publication number
WO2013100477A1
WO2013100477A1 PCT/KR2012/011108 KR2012011108W WO2013100477A1 WO 2013100477 A1 WO2013100477 A1 WO 2013100477A1 KR 2012011108 W KR2012011108 W KR 2012011108W WO 2013100477 A1 WO2013100477 A1 WO 2013100477A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive layer
point
dicing die
region
film
Prior art date
Application number
PCT/KR2012/011108
Other languages
English (en)
French (fr)
Inventor
박백성
최재원
김성민
김인환
이준우
임수미
Original Assignee
제일모직주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 제일모직주식회사 filed Critical 제일모직주식회사
Priority to CN201280065015.5A priority Critical patent/CN104024359B/zh
Publication of WO2013100477A1 publication Critical patent/WO2013100477A1/ko
Priority to US14/315,495 priority patent/US9287217B2/en

Abstract

본원 발명은 점착층과 링프레임간의 탈리를 방지하여 공정성을 높이는 다이싱 다이본딩 필름에 관한 것이다. 보다 구체적으로 본원 발명은 점착층 중 링프레임과의 부착 영역 내에 홈이 형성되어있어, 반도체 제조 공정상 투입되는 물 및/또는 공기를 상기 홈을 통하여 제거함으로써, 필름과 링프레임간의 부착력 약화 및 탈리를 방지하는 다이싱 다이본딩 필름에 관한 것이다.

Description

다이싱 다이본딩 필름 및 다이싱 다이본딩 필름에 홈을 형성하는 방법
본원 발명은 점착층과 링프레임간의 탈리를 방지하여 공정성을 높이는 다이싱 다이본딩 필름에 관한 것이다. 보다 구체적으로 본원 발명은 점착층 중 링프레임과의 부착 영역 내에 홈이 형성되어 있어, 반도체 제조 공정상 투입되는 물 및/또는 공기를 상기 홈을 통하여 제거함으로써, 필름과 링프레임간의 부착력 약화 및 탈리를 방지하는 비자외선형 다이싱 다이본딩 필름에 관한 것이다.
반도체 제조 공정에 사용되는 다이싱 다이본딩 필름은 자외선 노광이 필요한 자외선형(UV TYPE) 필름과 자외선 노광을 필요로 하지 않는 비자외선형(NON UV TYPE) 필름으로 분류된다.
자외선형 필름은 광경화 전 우수한 점착력을 나타내어 절삭 공정이 우수하다. 그러나, 자와선형 필름은 절삭 공정 후 픽업 공정을 실시하기 위하여 자외선을 조사하는 노광 공정을 추가로 실시해야 하므로 공정의 번거로움이 있다. 픽업 전 수행되는 자외선 노광 공정은 반도체 패키지 제조 과정 중에 많은 시간을 소요하는 공정으로, 반도체 패키지 생산성에 큰 영향을 미쳐 생산성 증대를 저해할 수 있다. 또한, 자외선 노광 과정 중에 자외선 조사기의 오작동이 발생할 경우, 랏(lot)에 정렬된 웨이퍼 중 충분한 자외선 에너지가 공급되지 못하는 부분이 생길 수 있고, 이에 따라 소잉(sawing)된 반도체 칩들이 픽업 과정에서 다이싱 필름층(점착층)으로부터 박리되지 못하는 픽업 공정 불량이 발생할 수 있다.
이와 같은 문제를 해결하고자, 픽업 공정 전에 도입되는 자외선 노광 과정을 생략할 수 있는 비자외선형 필름에 대한 필요성이 증대되고 있다.
그러나 비자외선형 필름의 경우, 점착력이 약하여 링프레임으로부터의 탈리가 쉽게 일어나는 문제가 있다.
본 발명자들은 상기의 문제점을 해결하기 위하여, 점착층 중 링프레임과의 부착 영역에 절삭수가 제거될 수 있는 홈을 내어 수침을 방지함으로써, 링프레임과의 탈리를 제어하는 비자외선형 다이싱 다이본딩 필름을 개발하기에 이르렀다.
본원 발명은 점착층 중 링프레임과의 부착 영역에 홈이 형성되어있어 절삭수에 의한 수침을 방지하여 링프레임과의 탈리를 제어하는 다이싱 다이본딩 필름을 제공하는 것을 목적으로 한다.
본원 발명의 일 양태는,
a) 기재 필름;
b) 상기 기재 필름에 적층된 점착층; 및
c) 상기 점착층에 적층된 접착층을 포함하는 다이싱 다이본딩 필름으로서,
상기 점착층은 상기 접착층과 중첩되는 제1 영역과, 상기 접착층과 비중첩되는 제2 영역을 포함하고,
상기 제2 영역은 상기 제1 영역과 인접하는 제3 영역과, 상기 제3 영역과 인접하고 홈이 형성된 제4 영역을 포함하는, 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면, 상기 제4 영역에 링프레임이 부착되는 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면, 상기 홈의 최고점이 상기 제3 영역과 상기 제4 영역의 경계에 위치하는 점착층의 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면,
a) 기재 필름;
b) 상기 기재 필름에 적층된 점착층;
c) 상기 점착층에 적층된 접착층; 및
d) 상기 접착층 또는 점착층에 적층된 이형 필름;
을 포함하는 다이싱 다이본딩 필름으로서,
상기 점착층은 상기 접착층과 중첩되는 제1 영역 및 상기 제1 영역을 둘러싸고 상기 접착층과 비중첩되는 제2 영역을 포함하고,
상기 기재 필름, 및 상기 제2 영역을 관통하는 하나 이상의 홈이 형성된, 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면, 상기 홈이 이형 필름은 관통하지 않는 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면, 상기 제2 영역 내에 링프레임이 부착되는 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면, 상기 홈과 홈 사이의 간격이 1 mm 내지 15 mm인, 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면, 상기 홈은 점착층 내의 서로 다른 지점에 위치하는 제1점(點), 제2점 및 제3점을, 제1점-제3점-제2점; 또는 제2점-제3점-제1점 순으로 연결한 선을 따라 절개하여 형성된 것으로서,
상기 제1점, 제2점 및 상기 점착층의 중심점은 세 점이 동시에 일 직선상에 위치하지 아니하고;
상기 점착층의 중심점으로부터 제1점까지의 거리(a), 상기 점착층의 중심점으로부터 제2점까지의 거리(b) 및 상기 점착층의 중심점으로부터 제3점까지의 거리(c)의 관계가 c〈 a 이고, c〈 b 인, 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면, 상기 a = b 인, 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면, 상기 제1점 및 제2점 사이의 거리가 1 mm 내지 15 mm인, 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면, 상기 제1점 및 제2점을 잇는 직선으로부터 상기 제3점까지의 수직 거리가 1 내지 10 mm인, 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면, 상기 홈의 모양은,
Figure PCTKR2012011108-appb-I000001
및
Figure PCTKR2012011108-appb-I000002
로 이루어진 군에서 선택되는, 다이싱 다이본딩 필름을 제공한다.
본원 발명의 또 다른 일 양태에 따르면,
a) 기재 필름;
b) 상기 기재 필름에 적층된 점착층;
c) 상기 점착층의 중심부에 적층된 접착층; 및
d) 상기 접착층 또는 점착층에 적층된 이형 필름;
을 포함하는 다이싱 다이본딩 필름에 있어서,
상기 기재 필름, 및 상기 접착층이 적층되지 않은 영역의 점착층을 관통하되, 상기 이형 필름은 관통하지 않는 높이까지 칼날을 삽입하여 다이싱 다이본딩 필름에 홈을 형성하는 방법을 제공한다.
본원 발명의 다이싱 다이본딩 필름은 비자외선형 필름에 있어서 반도체 제조 공정시 링프레임으로부터의 탈리를 방지하는 효과를 갖는다.
구체적으로, 본원 발명은 점착층 중 링프레임과의 부착 영역 내에 홈이 형성된 다이싱 다이본딩 필름으로서, 소잉 공정시 투입되는 절삭수를 상기 홈을 통하여 제거함으로써 점착층과 링프레임의 부착 영역의 수침을 방지하여 점착층과 링프레임과의 부착력이 약화되는 것을 방지하는 효과를 갖는다.
또한, 본원 발명은 소잉 공정 후 건조 공정 시 투입되는 공기를 상기 홈을 통해 제거함으로써 점착층과 링프레임의 부착 계면에 공기가 유입되는 것을 방지하는 효과를 갖는다.
또한, 본원 발명은 반도체 제조 공정 중 다이싱 다이본딩 필름이 링프레임으로부터 탈리되는 것을 방지함으로써, 픽업 공정성을 향상시키는 효과를 갖는다.
도 1은 본원 발명의 홈의 절개부 상의 양 말단에 위치한 점(제1점 및 제2점)과, 절개부 상의 임의의 한 점(제3점)을 나타낸 것이다.
도 2는 다이싱 다이본딩 필름상에서의 도 1의 3 개 점의 위치 관계를 대략적으로 도시한 것이다.
도 3a 및 3b는 홈이 형성된 다이싱 다이본딩 필름의 일 양태를 대략적으로 도시한 것이다.
도 4는 비교예 2에 따른 다이싱 다이본딩 필름을 대략적으로 도시한 것이다.
도 5a, 5b 및 5c는 다이싱 다이본딩 필름에 홈을 형성하는 방법을 대략적으로 도시한 것이다.
이하, 본원 발명에 대하여 보다 상세히 설명한다. 본원 명세서에 기재되지 아니한 사항은 본원 발명의 기술 분야에서 숙련된 자이면 충분히 인식하고 유추할 수 있는 것이므로 그 설명을 생략한다.
본원 발명의 일 양태는,
a) 기재 필름;
b) 상기 기재 필름에 적층된 점착층; 및
c) 상기 점착층에 적층된 접착층을 포함하는 다이싱 다이본딩 필름으로서,
상기 점착층은 상기 접착층이 적층된 제1 영역과, 상기 접착층이 적층되지 않은 제2 영역을 포함하고,
상기 제2 영역은 상기 제1 영역과 인접하는 제3 영역과, 상기 제3 영역과 인접하고 홈이 형성된 제4 영역을 포함하는, 다이싱 다이본딩 필름을 제공한다.
상기 기재 필름, 점착층, 접착층 및 이형 필름은 특별히 제한되지 아니하며, 반도체 패키지 분야에서 일반적인 제품으로 제공되는 것을 사용할 수 있다.
상기 홈은 임의의 개(開)곡선을 따라 형성된 절개부를 말한다. 개곡선이란 폐(閉)곡선의 반대 개념으로, 선의 시작점과 끝점이 서로 이어지지 아니하고 끊어져 있는 선을 의미한다.
상기 홈은, 상기 점착층 중 제4 영역 내의 서로 다른 지점에 위치하는 제1점(點), 제2점 및 제3점을, 제1점-제3점-제2점; 또는 제2점-제3점-제1점 순으로 연결한 선을 따라 절개하여 형성된 것일 수 있다. 상기 제1점, 제2점 및 상기 점착층의 중심점은 세 점이 동시에 일 직선상에 위치하지 아니하고, 상기 점착층의 중심점으로부터 각각 제1점까지의 거리(a), 제2점까지의 거리(b) 및 제3점까지의 거리(c)의 관계가 c〈 a이고, c〈 b 일 수 있다.
상기 홈은 도 1에 나타낸 바와 같이, 제1점, 제2점 및 제3점에 있어서 제1점-제3점-제2점, 또는 제2점-제3점-제1점 순으로 연결한 임의의 선을 따라 절개된 홈일 수 있다. 상기 세 점을 연결함에 있어서 상기 제1점과 제2점은 제3점을 거치지 아니하고는 서로 직접 연결되지 아니한다. 상기 점들을 연결한 임의의 선의 모양은 특별히 한정되지 아니하며 그 비제한적인 예로는 직선, 곡선, 물결선, 요철 모양의 선 등을 들 수 있다.
도 1의 제1 내지 제3점은 모두 점착층 중 제4 영역 내에 존재하여야 한다.
구체적으로 도 3a 및 도 3b를 참조하여 살펴보면, 다이싱 다이본딩 필름의 점착층은 크게 접착층이 적층된 제1 영역(130)과 접착층이 적층되지 않으며 링프레임과 부착되지 않는 제2 영역으로 구분되며, 상기 제2 영역은 다시 상기 제1 영역(130)과 인접하는 제3 영역(120)과, 상기 제3 영역(120)과 인접하고 홈이 형성되어 있는 제4 영역(110)으로 구분된다. 상기 제4 영역(110)은 일반적으로 다이싱 다이본딩 필름의 점착층의 최외곽 부분에 위치하게 되며 상기 제4 영역(110)에 부착되는 링프레임 면의 두께는 예를 들어 20 mm 내외일 수 있다. 따라서 상기 제4 영역(110)은 다이싱 다이본딩 필름의 점착층의 최외곽으로부터 20 mm 내외에 해당하는 영역일 수 있다.
상기 제1 내지 제3점 중 어느 한 점이 점착층의 제4 영역(110) 외에 존재하는 경우에는, 홈(300)이 점착층 중 제4 영역 외의 부분에 형성(도 4 참조)되어 반도체 제조 공정 중 점착층이 링프레임으로부터 탈리되는 현상이 일어나 공정 불량을 야기할 우려가 있으며, 공정 중 점착층이 찢어지거나 손상될 위험이 있다.
상기 제1점 및 제2점 사이의 거리는, 두 점이 모두 점착층 중 제4 영역(110) 내에 존재하는 경우라면 특별히 제한되지 아니하나, 1 mm 내지 15 mm인 것이 바람직하다. 상기 범위 내에서 적절한 크기의 홈이 형성되어 절삭수 및/또는 공기의 제거가 효과적으로 이루어지게 되며, 제3점과의 관계를 고려할 때, 점착층 중 제4 영역(110)을 벗어나지 않는 범위 내에서 홈(300)이 형성될 수 있도록 한다.
도 1을 참조할 때, A 점과 제3점 사이의 거리는, 제1점, 제2점 및 제3점이 모두 점착층의 제4 영역(110) 내에 존재하는 경우라면 특별히 제한되지 아니하나, 1 내지 10 mm인 것이 바람직하다. 상기 두 점 사이의 거리가 1 mm 미만일 경우에는 홈의 모양이 도형이 아닌 선에 가까운 형상으로 형성되어 홈의 역할을 수행하지 못할 우려가 있으며, 10 mm를 초과하는 경우에는 상기 제1점, 제2점 및 제3점이 모두 점착층의 제4 영역(110) 내에 존재하지 못할 우려가 있다.
도 2를 참조할 때,
점착층의 중심점으로부터 제1점까지의 거리(a);
점착층의 중심점으로부터 제2점까지의 거리(b); 및
점착층의 중심점으로부터 제3점까지의 거리(c)에 있어서,
상기 c 〈 a 이고, c〈 b 이다.
상기 a 및 b는 상기 제1점 및 제2점이 모두 점착층의 제4 영역(110) 내에 존재하는 경우라면 특별히 제한되지 아니하며 서로 상이할 수 있으나, 바람직하게는 a = b 일 수 있다.
상기 홈(300)의 모양은 특별히 한정되지 아니하며, 무정형일 수 있다. 상기 홈(300)의 모양의 비제한적인 예로는, 도 1의 제1점 및 제2점을 지나는 가상의 직선을 밑변으로 할 때, 반원형, U자형, 타원형, 삼각형, 사각형, 오각형, 기타 다각형 등을 들 수 있다(예컨대,
Figure PCTKR2012011108-appb-I000003
).
상기 홈(300)의 모양은 바람직하게는 반원형, 삼각형, 사각형, 오각형일 수 있다.
상기 홈(300)과 홈(300) 사이의 간격은, 형성된 모든 홈(300)이 점착층의 제4 영역(110) 내에 존재하는 경우라면 특별히 제한되지 아니하나, 바람직하게는 1 내지 15 mm일 수 있다. 상기 범위 내에서, 반도체 제조 공정 중 서로 이웃한 홈(300)이 연결되어 점착층이 찢어지는 문제를 방지할 수 있으며, 적절한 개수의 홈(300)이 형성됨으로써 절삭수 및/또는 공기가 효과적으로 제거될 수 있도록 하는 이점이 있다.
상기 점착층 중 제4 영역(110) 내에 형성된 홈(300)의 개수는 특별히 제한되지 아니한다.
상기 홈(300)의 위치는 점착층의 제4 영역(110) 내에 존재하는 경우라면 특별히 제한되지 아니하나, 제4 영역(110) 중 안쪽(점착층의 중심부 쪽)에 위치할수록 바람직하다. 절삭수 또는 공기의 제거에 보다 유리하기 때문이다. 가장 바람직하게는 상기 홈(300)은, 상기 홈의 최고점이 상기 제3 영역과 제4 영역의 경계에 위치할 수 있다. 상기 '홈의 최고점'이란 홈의 외곽선 중 상기 점착층의 중심에 가장 가깝게 형성된 지점을 말한다.
상기 홈(300)을 형성하는 방법은 기재 필름에 도포된 점착층과 접착제를 합지하고 규격화된 모양과 크기로 잘라주는 컷팅 공정 시 상기 홈이 형성된 피나클로 홈을 만들어 주는 방법에 의할 수 있다.
상기 다이싱 다이본딩 필름은 비자외선형(NON UV TYPE)일 수 있다.
상기 다이싱 다이본딩 필름은 광경화성 점착 조성물로 제조된 점착층에 미리 UV를 조사하는 공정을 거쳐 제작된 점착층을 포함하는, 선경화형 비자외선형 필름일 수 있다.
상기 다이싱 다이본딩 필름은 비광경화성 점착 조성물로 제조된 점착층을 포함하는, 비광경화형 비자외선형 필름일 수 있다.
도 3a 및 3b는 본원 발명의 실시예에 따른 다이싱 다이본딩 필름을 나타낸 것이다.
도 3a에서는
Figure PCTKR2012011108-appb-I000004
모양의 홈을, 도 3b에서는
Figure PCTKR2012011108-appb-I000005
모양의 홈을 형성하였으나, 홈의 모양은 특별히 제한되니 아니하므로 예컨대
Figure PCTKR2012011108-appb-I000006
등과 같이 여러 다양한 형태일 수 있다.
도 3a 및 3b에 나타난 점착층 및 접착층의 면적, 상기 홈(300)의 모양, 크기, 개수, 및 점착층 중 제4 영역(110) 내에서의 위치 등은 수치적으로 계산된 것이 아니며, 본원 발명의 일 양태의 전반적인 형상만을 간략히 나타낸 것임을 밝힌다. 따라서 본원 발명의 내용이 도 3a 및 3b에 의해 제한되는 것으로 해석되어서는 아니된다.
본원 발명의 또 다른 일 양태에 따르면,
a) 기재 필름;
b) 상기 기재 필름에 적층된 점착층;
c) 상기 점착층에 적층된 접착층; 및
d) 상기 접착층 또는 점착층에 적층된 이형 필름;
을 포함하는 다이싱 다이본딩 필름으로서,
상기 점착층은 상기 접착층과 중첩되는 제1 영역 및 상기 제1 영역을 들러싸고 상기 접착층과 비중첩되는 제2 영역을 포함하고,
상기 기재 필름, 및 상기 제2 영역을 관통하는 하나 이상의 홈이 형성된, 다이싱 다이본딩 필름을 제공한다.
상기 기재 필름, 점착층, 접착층 및 이형 필름은 특별히 한정되지 아니하며, 반도체 패키지 분야에서 일반적인 제품으로 제공되는 것을 사용할 수 있다.
상기 접착층은 점착층보다 크기가 작으며, 점착층의 중심부에 적층되어 있다(도 5a 참조).
상기에서 "관통"한다는 것은, 해당 층(또는 필름)을 완전히 뚫고 지나가는 것을 의미한다.
상기 홈은, 상기 기재 필름의 바깥쪽 표면에서부터 상기 점착층을 관통하되, 상기 점착층에 적층된 이형 필름은 완전히 관통하지 않도록 형성된다. 즉, 상기 기재 필름의 바깥쪽 표면에서부터 상기 점착층 및 상기 점착층과 이형 필름간의 경계면까지 관통하고, 나아가 이형 필름의 내부 일부까지 뚫리도록 홈을 형성할 수 있으나(도 5a), 이형 필름의 바깥쪽 표면까지 뚫려 이형 필름을 완전히 관통하는 홈은 형성되지 않도록 한다(도 5c).
상기 홈이 상기 이형 필름의 바깥쪽 표면까지 완전히 관통하는 경우에는 마운팅 공정에서 이형 필름을 벗겨낼 때 점착층의 홈의 열려진 절개면 부위가 따라 올라가면서 상기 열려진 절개면 부위가 안쪽으로 접혀 붙으면서 공정 불량을 야기할 우려가 있다.
상기 이형 필름은, 그 바깥 표면까지 완전히 관통되지 않는 경우라면, 점착층과의 경계면에서부터 임의의 높이까지 관통하는 홈이 형성될 수 있으나, 바람직하게는 상기 기재 필름에서부터 점착층과 이형 필름의 계면에 이르는 높이까지만 관통하는 홈이 형성될 수 있다(도 5b).
도 5a는 기재 필름, 점착층, 접착층 및 이형 필름 순으로 적층된 4층 구조의 다이싱 다이본딩 필름에 있어서, 기재 필름에서부터 이형 필름의 내부 일부에 이르는 높이까지 칼날을 삽입하여 홈을 형성하는 방법을 나타낸 것이다.
도 5b는 기재 필름, 점착층, 접착층 및 이형 필름 순으로 적층된 4층 구조의 다이싱 다이본딩 필름에 있어서, 기재 필름에서부터 점착층과 이형 필름의 계면에 이르는 높이까지 칼날을 삽입하여 홈을 형성하는 방법을 나타낸 것이다.
상기 홈의 모양, 크기, 개수는 특별히 한정되지 않는다.
상기 홈은 점착층 중 제4 영역(110) 내에 존재하도록 형성되는 것이 바람직하다.
본원 발명의 또 다른 일 양태에 따르면,
a) 기재 필름;
b) 상기 기재 필름에 적층된 점착층;
c) 상기 점착층의 중심부에 적층된 접착층; 및
d) 상기 접착층 또는 점착층에 적층된 이형 필름;
을 포함하는 다이싱 다이본딩 필름에 있어서,
상기 기재 필름, 및 상기 접착층이 적층되지 않은 영역의 점착층을 관통하되, 상기 이형 필름은 관통하지 않는 높이까지 칼날을 삽입하여 다이싱 다이본딩 필름에 홈을 형성하는 방법을 제공한다.
상기 홈을 형성함에 있어서, 기재 필름에서부터 이형 필름의 내부 일부에 이르는 높이까지 칼날을 삽입하여 홈을 형성할 수 있으며(도 5a), 보다 바람직하게는 기재 필름에서부터 점착층과 이형 필름의 계면에 이르는 높이까지 칼날을 삽입하여 홈을 형성할 수 있다(도 5b).
이하, 실시예, 비교예 및 실험예를 기술함으로써 본원 발명을 보다 상세히 설명한다. 다만, 하기의 실시예, 비교예 및 실험예는 본원 발명의 일 예시에 불과하며, 본원 발명의 내용이 이에 한정되는 것으로 해석되어서는 아니된다.
실시예 1
점착층 중 링프레임과의 부착 영역 내에 홈을 형성하는 방법
광경화성 점착층을 갖는 시중의 다이싱 다이본딩 필름(제일모직 제조) 및 비광경화성 점착층을 갖는 시중의 다이싱 다이본딩 필름(제일모직 제조)을 입수하여, 상기 각각의 필름의 점착층 중 링프레임과의 부착 영역에 도 3a와 같은 형상으로 홈을 형성하였다.
상기 홈을 형성하는 방법은, 기재 필름에 도포된 점착층과 접착제를 합지하고 웨이퍼 형상의 규격화된 모양과 크기로 잘라주는 컷팅 공정 시 상기 홈이 형성된 피나클로 홈을 만들어 주었다.
실시예 1에서는 8 인치(inch) 크기의 웨이퍼에 적용되는 내경 250 mm의 링프레임에 사용되는 다이싱 다이본딩 필름(제일모직 제조)을 이용하여 중심점에서 제3점까지의 거리를 128 mm로 하고, 제1점과 제2점 간의 거리는 5 mm, 중심점에서 제1점까지 및 중심점에서 제2점까지의 거리는 132 mm로 하며, 홈과 홈간의 간격을 5 mm로 하여, 상기 다이싱 다이본딩 필름(제일모직 제조)의 링프레임 부착 영역 내에 홈이 위치하게 제조하였다.
실시예 2
점착층 중 링프레임과의 부착 영역 내에 홈을 형성하는 방법
실시예 1에 있어서, 12 인치 크기의 웨이퍼에 적용되는 내경 350 mm의 링프레임에 사용되는 다이싱 다이본딩 필름(제일모직 제조)을 이용하고, 중심점에서 제3점까지의 거리를 178 mm로 하며, 중심점에서 제1점까지 및 중심점에서 제2점까지의 거리를 182 mm로 한 것을 제외하고는, 상기 실시예 1과 동일한 방법으로 수행하였다.
비교예 1
점착층에 홈이 형성되지 않은 다이싱 다이본딩 필름
비광경화성 점착층을 갖는 시중의 다이싱 다이본딩 필름(실시예 1에서 사용한 것과 동일한 것으로, 홈이 형성되어 있지 않은 상태의 필름)을 준비하였다.
비교예 2
점착층 중 링프레임 부착 영역이 아닌 부분에 홈이 형성된 다이싱 다이본딩 필름
실시예 1과 동일한 방법으로 점착층에 홈을 형성시키되, 중심점에서 제3점까지의 거리를 115 mm로 하고, 중심점에서 제1점까지 및 중심점에서 제2점까지의 거리는 119 mm로 하여, 점착층 중 링프레임 부착 영역이 아니면서 접착층이 적층되어 있지 않은 영역에 홈이 형성된 다이싱 다이본딩 필름을 제조하였다(도 4).
실험예 1
소잉 공정 시 절삭수에 의한 수침 및 링프레임 탈리 여부 평가
상기 실시예 1, 2 및 비교예 1, 2에 따른 다이싱 다이본딩 필름을 링프레임에 부착시키고 소잉 공정을 수행하여 수침 및 링프레임 탈리 여부를 평가하였다.
소잉 공정은 DISCO DFD-6361 설비를 이용하여 평가하며, 소잉 속도(Sawing speed): 10mm/sec, rpm: 50000, 수압: 1.6 Mpa, 수량: 1.5 L/min의 조건으로 소잉 공정을 진행한 후, 링프레임 영역의 수침 및 탈리 현상을 육안으로 관찰하였다. 구체적으로, 링프레임과 접착된 점착층 영역의 전체 면적을 12 등분하여 이중 2 개 이상의 부위에서 수침 및 탈리 현상이 발생한 경우에 "불량"으로 평가하였고, 0 개 또는 1 개 부위에서 발생한 경우에는 "양호"로 평가하였다
실험예 2
픽업(Pick up) 성공률 측정
칩 픽업 공정은 웨이퍼의 절삭 공정 후 칩화된 웨이퍼를 PCB 기판 또는 쌓여진 칩 위에 실장하는 공정을 말한다.
상기 실험예 1의 방법에 따라 웨이퍼를 소잉한 후, 절삭된 웨이퍼 중앙부의 칩 100 개에 대하여 다이본더 장치(SDB-1000M, 세크론)를 이용하여 픽업 시험을 실시하고, 그 성공률(%)을 측정하였다.
하기 표 1은 상기 실험예 1 및 2에 대한 측정 결과를 나타낸 것이다.
표 1
실시예 1 실시예 2 비교예 1 비교예 2
수침 및 링프레임 탈리 여부 양호 양호 불량 불량
픽업 성공률(%) 100 100 0(평가불가) 0(평가불가)
상기 표 1을 살펴보면, 실시예 1 및 실시예 2와 점착력 및 점착성은 동일하나 홈이 형성되어 있지 않은 비교예 1, 및 홈이 형성되어 있기는 하나 링프레임 부착 영역 외에 홈이 형성된 비교예 2는, 절삭수에 의한 수침이 심화되어 점착층이 링프레임으로부터 쉽게 탈리되어 불량으로 평가되었으며, 따라서 픽업이 되지 않아 픽업 성공률을 평가할 수 없었다.
반면, 비교예 1 및 비교예 2와 동일한 점착력 및 점착성을 가지나, 점착층 중 링프레임 부착 영역에 홈이 형성되어 있는 실시예 1 및 실시예 2의 경우, 상기 홈을 통하여 절삭수가 제거되어 수침이 거의 없고 따라서 링프레임 탈리가 일어나지 않아 양호로 평가되었다. 또한 픽업 성공률 역시 100%로 확인되었다.
[부호의 설명]
110 점착층 중 접착층 비적층 및 링프레임 부착 영역
120 점착층 중 접착층 비적층 및 링프레임 비부착 영역
130 점착층 중 접착층 적층 영역
300 홈

Claims (13)

  1. a) 기재 필름;
    b) 상기 기재 필름에 적층된 점착층; 및
    c) 상기 점착층에 적층된 접착층을 포함하는 다이싱 다이본딩 필름으로서,
    상기 점착층은 상기 접착층과 중첩되는 제1 영역과, 상기 접착층과 비중첩되는 제2 영역을 포함하고,
    상기 제2 영역은 상기 제1 영역과 인접하는 제3 영역과, 상기 제3 영역과 인접하고 홈이 형성된 제4 영역을 포함하는, 다이싱 다이본딩 필름.
  2. 제1항에 있어서, 상기 제4 영역에 링프레임이 부착되는 다이싱 다이본딩 필름.
  3. 제1항에 있어서, 상기 홈의 최고점이 상기 제3 영역과 상기 제4 영역의 경계에 위치하는 점착층의 다이싱 다이본딩 필름.
  4. a) 기재 필름;
    b) 상기 기재 필름에 적층된 점착층;
    c) 상기 점착층에 적층된 접착층; 및
    d) 상기 접착층 또는 점착층에 적층된 이형 필름;
    을 포함하는 다이싱 다이본딩 필름으로서,
    상기 점착층은 상기 접착층과 중첩되는 제1 영역 및 상기 제1 영역을 둘러싸고 상기 접착층과 비중첩되는 제2 영역을 포함하고,
    상기 기재 필름, 및 상기 제2 영역을 관통하는 하나 이상의 홈이 형성된, 다이싱 다이본딩 필름.
  5. 제4항에 있어서, 상기 홈이 이형 필름은 관통하지 않는 다이싱 다이본딩 필름.
  6. 제4항에 있어서, 상기 제2 영역 내에 링프레임이 부착되는 다이싱 다이본딩 필름.
  7. 제1항 내지 제6항 중 어느 하나의 항에 있어서, 상기 홈과 홈 사이의 간격이 1 mm 내지 15 mm인, 다이싱 다이본딩 필름.
  8. 제1항 내지 제6항 중 어느 하나의 항에 있어서, 상기 홈은 점착층 내의 서로 다른 지점에 위치하는 제1점(點), 제2점 및 제3점을, 제1점-제3점-제2점; 또는 제2점-제3점-제1점 순으로 연결한 선을 따라 절개하여 형성된 것으로서,
    상기 제1점, 제2점 및 상기 점착층의 중심점은 세 점이 동시에 일 직선상에 위치하지 아니하고;
    상기 점착층의 중심점으로부터 제1점까지의 거리(a), 상기 점착층의 중심점으로부터 제2점까지의 거리(b) 및 상기 점착층의 중심점으로부터 제3점까지의 거리(c)의 관계가 c〈 a 이고, c〈 b 인, 다이싱 다이본딩 필름.
  9. 제8항에 있어서, 상기 a = b 인, 다이싱 다이본딩 필름.
  10. 제8항에 있어서, 상기 제1점 및 제2점 사이의 거리가 1 mm 내지 15 mm인, 다이싱 다이본딩 필름.
  11. 제8항에 있어서, 상기 제1점 및 제2점을 잇는 직선으로부터 상기 제3점까지의 수직 거리가 1 내지 10 mm인, 다이싱 다이본딩 필름.
  12. 제1항 내지 제4항 중 어느 하나의 항에 있어서, 상기 홈의 모양은,
    Figure PCTKR2012011108-appb-I000007
    및
    Figure PCTKR2012011108-appb-I000008
    로 이루어진 군에서 선택되는, 다이싱 다이본딩 필름.
  13. a) 기재 필름;
    b) 상기 기재 필름에 적층된 점착층;
    c) 상기 점착층의 중심부에 적층된 접착층; 및
    d) 상기 접착층 또는 점착층에 적층된 이형 필름;
    을 포함하는 다이싱 다이본딩 필름에 있어서,
    상기 기재 필름, 및 상기 접착층이 적층되지 않은 영역의 점착층을 관통하되, 상기 이형 필름은 관통하지 않는 높이까지 칼날을 삽입하여 다이싱 다이본딩 필름에 홈을 형성하는 방법.
PCT/KR2012/011108 2011-12-27 2012-12-18 다이싱 다이본딩 필름 및 다이싱 다이본딩 필름에 홈을 형성하는 방법 WO2013100477A1 (ko)