WO2013081113A1 - 耐火物及び鋳造用ノズル - Google Patents
耐火物及び鋳造用ノズル Download PDFInfo
- Publication number
- WO2013081113A1 WO2013081113A1 PCT/JP2012/081101 JP2012081101W WO2013081113A1 WO 2013081113 A1 WO2013081113 A1 WO 2013081113A1 JP 2012081101 W JP2012081101 W JP 2012081101W WO 2013081113 A1 WO2013081113 A1 WO 2013081113A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- refractory
- cao
- mass
- molten steel
- layer
- Prior art date
Abstract
Description
1000℃の非酸化雰囲気で加熱後の化学成分において、B2O3、TiO2、V2O5、P2O5、及びSiO2から選択する1種又は2種以上の金属酸化物を合計で0.1質量%以上5.0質量%以下、フリーの炭素を2質量%以上35質量%以下含有し、残部がCaOとMgOとを含み、その質量比(CaO/MgO)が0.1以上1.5以下であり、
かつ、1000℃の非酸化雰囲気で加熱後の試料について室温での顕微鏡観察で、前記CaO成分を含む耐火性粒子の少なくともCaO表面に、CaOと前記B2O3、TiO2、V2O5、P2O5及びSiO2から選択する1種又は2種以上の金属酸化物とからなる0.1μm以上25μm以下の厚さの無機質被膜が形成されている耐火物。(請求項1)
(2)炭酸カルシウムの分解温度以上の熱処理を受けていない状態において、CaCO3を0.1質量%以上2.5質量%未満含有する(1)に記載の耐火物。(請求項2)
(3)1000℃の非酸化雰囲気で加熱後の試料について室温での顕微鏡観察において、その顕微鏡観察視野中のCaO成分及びMgO成分のいずれか一方又は両方を含む耐火性粒子のうち最大径粒子の両側に存在する炭素質マトリックスとの界面における空隙の合計厚みが、当該粒子サイズの0.1%以上3.0%以下である(1)又は(2)に記載の耐火物。(請求項3)
(4)SiC、Si3N4、ZrO2及び金属Siから選択する1種又は複数種を更に含有し、
各含有量は、1000℃の非酸化雰囲気で加熱後の化学成分において、SiC、Si3N4についてはいずれか一方又は両方の合計で20質量%以下、ZrO2については5質量%以下、金属Siについては2質量%以下である、(1)から(3)のいずれかに記載の耐火物。(請求項4)
(5)(1)から(4)のいずれかに記載の耐火物が、溶鋼と接触する部位の一部又は全部の領域に、溶鋼と接触する面から背面側に単層として配置されている鋳造用ノズル。(請求項5)
(6)(1)から(4)のいずれかに記載の耐火物が溶鋼に接触する面の一部又は全部に配置され、その背面側には前記の溶鋼に接触する面の一部又は全部に配置された耐火物とは異なる組成の耐火物からなる層が配置された複数の層をなしており、前記複数の層が相互に直接接触した状態で一体構造とされている鋳造用ノズル。(請求項6)
(7)(1)から(4)のいずれかに記載の耐火物が溶鋼に接触する面の一部又は全部に配置され、その背面側には前記の溶鋼に接触する面の一部又は全部に配置された耐火物とは異なる組成の耐火物からなる層が配置された複数の層をなしており、
更に、前記の溶鋼に接触する面の一部又は全部に配置された耐火物の層とその背面側に配置された耐火物の層との間に、炭素含有量が90質量%以上で厚さが0.1mm以上3mm以下のシート状の層が配置されており、前記の溶鋼に接触する面に配置された耐火物の層とその背面側に配置された耐火物の層とが、相互に接触しない状態で一体構造とされている鋳造用ノズル。(請求項7)
(8)(1)から(4)のいずれかに記載の耐火物が溶鋼に接触する面の一部又は全部に配置され、その背面側には前記の溶鋼に接触する面の一部又は全部に配置された耐火物とは異なる組成の耐火物からなる層が配置された複数の層をなしており、
更に、前記の溶鋼に接触する面の一部又は全部に配置された耐火物の層とその背面側に配置された耐火物の層とが、溶鋼温度にて溶融による流下を生じない成分からなるモルタルにて接着されており、前記の溶鋼に接触する面に配置された耐火物の層とその背面側に配置された耐火物の層とが、前記のモルタル層により相互に接触しない状態で保持された構造とされている鋳造用ノズル。(請求項8)
(9)内孔部の一部にガス吹き込み用の耐火物からなる層を備えた、請求項5から8のいずれかに記載の鋳造用ノズル。(請求項9)
CaO+H2O=Ca(OH)2
この反応において標準生成自由エネルギーΔG゜は、-57.8kJ/mol(T=298K)である。
3CaO・2TiO2(+12.4kJ/mol)、4CaO・3TiO2(+16.8kJ/mol)、CaO・TiO2(+24.4kJ/mol)
3CaO・V2O5(+52.9kJ/mol)、2CaO・V2O5(+74.6kJ/mol)、CaO・V2O5(+88.2kJ/mol)
3CaO・P2O5(+236kJ/mol)、2CaO・P2O5(+280.7kJ/mol)
3CaO・SiO3(-17.5kJ/mol)、2CaO・SiO2(+3.3kJ/mol)、CaO・SiO2(+33.9kJ/mol)
MS=L/D×100(%)
(2)CaO成分を含む(MgO成分を含まない)耐火性粒子と、MgO成分を含む耐火性粒子との組み合わせ
(3)MgO成分を含む(CaO成分を含まない)耐火性粒子と、CaO成分を含む耐火性粒子との組み合わせ
この実施例では、耐火物の化学成分のうち、金属酸化物量の影響を調査した。
実施例Bは、本発明の金属酸化物として酸化バナジウム(V2O5)及び酸化チタニウム(TiO2)、五酸化二リン(P2O5)、酸化珪素(SiO2)、ほう珪酸ガラスについて、耐消化性その他の特性を調査した例である。また、酸化硼素(B2O3)も含め、これら金属酸化物を併存する場合の効果も調査した。試料は、実施例Aと同じ要領で製造し、同じ方法で評価を行った。
実施例Cは、耐火物の化学成分のうち、炭素含有量及びCaOとMgOとの合量の影響を調査した例である。前記実施例Aと同じ要領で耐火物を製造し、その評価を行った。耐火物の評価としては、溶鋼中回転試験及び耐消化性の試験に加え、耐割れ性の試験を行った。
この実施例では、耐火物の化学成分のうち、(CaO/MgO)質量比の影響を調査した。ここでは炭素量を21.6質量%に固定し、CaO/MgO比を変化させた。前記実施例Aと同じ要領で耐火物を製造し、その評価を行った。
この実施例Eでは、耐火物の化学成分のうち、CaCO3量の影響を調査した。耐火物の製造方法は前記実施例Aと同様であるが、本実施例では炭酸化処理の時間を変えることにより耐火物中のCaCO3量を変化させた。炭酸化処理により得られた耐火物の評価は、溶鋼中回転試験及び耐消化性の試験に加え、脱ガス性の試験を行った。
この実施例Fは、焼成ドロマイトクリンカー粒子と炭素質マトリックスとの間に空隙層が存在する場合の効果を確認した例である。
この実施例GはSiC、Si3N4、ZrO2及び金属Siから選択する1又は複数種を含み、残部が前記[課題を解決するための手段](1)(請求項1)に記載の耐火物からなる耐火物につき、これら成分の効果を調査した例である。
2 熱処理前の炭素質マトリックス
3 焼成ドロマイトクリンカー粒子
4 熱処理後の炭素質マトリックス
5 熱処理後に生成した空隙層
6 熱処理後に生成したB2O3系被膜
10 試験片
10a 端面
11 ホルダー
12 坩堝
13 溶鋼
14 高周波誘導炉
20 本発明の耐火物
21 パウダーライン材質(背面側の耐火物)
22 本体材質(背面側の耐火物)
22G 本体材質(通気性の耐火物)
22S 空間(ガスの通過経路、蓄圧室)
23 シート状の層又はモルタル層
A:上部ノズル
B:スライディングノズルプレート
C:下部ノズル
D:ロングノズル
E:ロングストッパー
F:浸漬ノズル
G:内張り用耐火物
Claims (9)
- CaO成分を含む耐火性粒子とMgO成分を含む耐火性粒子とを含む耐火物であって、
1000℃の非酸化雰囲気で加熱後の化学成分において、B2O3、TiO2、V2O5、P2O5、及びSiO2から選択する1種又は2種以上の金属酸化物を合計で0.1質量%以上5.0質量%以下、フリーの炭素を2質量%以上35質量%以下含有し、残部がCaOとMgOとを含み、その質量比(CaO/MgO)が0.1以上1.5以下であり、
かつ、1000℃の非酸化雰囲気で加熱後の試料について室温での顕微鏡観察で、前記CaO成分を含む耐火性粒子の少なくともCaO表面に、CaOと前記B2O3、TiO2、V2O5、P2O5及びSiO2から選択する1種又は2種以上の金属酸化物とからなる0.1μm以上25μm以下の厚さの無機質被膜が形成されている耐火物。 - 炭酸カルシウムの分解温度以上の熱処理を受けていない状態において、CaCO3を0.1質量%以上2.5質量%未満含有する請求項1に記載の耐火物。
- 1000℃の非酸化雰囲気で加熱後の試料について室温での顕微鏡観察において、その顕微鏡観察視野中のCaO成分及びMgO成分のいずれか一方又は両方を含む耐火性粒子のうち最大径粒子の両側に存在する炭素質マトリックスとの界面における空隙の合計厚みが、当該粒子サイズの0.1%以上3.0%以下である請求項1又は2に記載の耐火物。
- SiC、Si3N4、ZrO2及び金属Siから選択する1種又は複数種を更に含有し、
各含有量は、1000℃の非酸化雰囲気で加熱後の化学成分において、SiC、Si3N4についてはいずれか一方又は両方の合計で20質量%以下、ZrO2については5質量%以下、金属Siについては2質量%以下である、請求項1から請求項3のいずれかに記載の耐火物。 - 請求項1から4のいずれかに記載の耐火物が、溶鋼と接触する部位の一部又は全部の領域に、溶鋼と接触する面から背面側に単層として配置されている鋳造用ノズル。
- 請求項1から4のいずれかに記載の耐火物が溶鋼に接触する面の一部又は全部に配置され、その背面側には前記の溶鋼に接触する面の一部又は全部に配置された耐火物とは異なる組成の耐火物からなる層が配置された複数の層をなしており、前記複数の層が相互に直接接触した状態で一体構造とされている鋳造用ノズル。
- 請求項1から4のいずれかに記載の耐火物が溶鋼に接触する面の一部又は全部に配置され、その背面側には前記の溶鋼に接触する面の一部又は全部に配置された耐火物とは異なる組成の耐火物からなる層が配置された複数の層をなしており、
更に、前記の溶鋼に接触する面の一部又は全部に配置された耐火物の層とその背面側に配置された耐火物の層との間に、炭素含有量が90質量%以上で厚さが0.1mm以上3mm以下のシート状の層が配置されており、前記の溶鋼に接触する面に配置された耐火物の層とその背面側に配置された耐火物の層とが、相互に接触しない状態で一体構造とされている鋳造用ノズル。 - 請求項1から4のいずれかに記載の耐火物が溶鋼に接触する面の一部又は全部に配置され、その背面側には前記の溶鋼に接触する面の一部又は全部に配置された耐火物とは異なる組成の耐火物からなる層が配置された複数の層をなしており、
更に、前記の溶鋼に接触する面の一部又は全部に配置された耐火物の層とその背面側に配置された耐火物の層とが、溶鋼温度にて溶融による流下を生じない成分からなるモルタルにて接着されており、前記の溶鋼に接触する面に配置された耐火物の層とその背面側に配置された耐火物の層とが、前記のモルタル層により相互に接触しない状態で保持された構造とされている鋳造用ノズル。 - 内孔部の一部にガス吹き込み用の耐火物からなる層を備えた、請求項5から8のいずれかに記載の鋳造用ノズル。