WO2013073368A1 - 透明耐熱難燃フィルム - Google Patents
透明耐熱難燃フィルム Download PDFInfo
- Publication number
- WO2013073368A1 WO2013073368A1 PCT/JP2012/078137 JP2012078137W WO2013073368A1 WO 2013073368 A1 WO2013073368 A1 WO 2013073368A1 JP 2012078137 W JP2012078137 W JP 2012078137W WO 2013073368 A1 WO2013073368 A1 WO 2013073368A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- transparent heat
- film
- group
- protective layer
- resistant
- Prior art date
Abstract
Description
本発明において、熱可塑性樹脂フィルムとしては、熱変形温度が250℃以下で透明な非晶質性のものであれば特に限定されない。このような熱可塑性樹脂フィルムとしては、例えば、非晶性ポリエステルフィルム[非晶性ポリエチレンテレフタレート(PET)フィルム等]、非晶性ポリオレフィンフィルム[4-メチルペンテン(共)重合体フィルム等]、環状ポリオレフィンフィルム、ポリカーボネート(PC)フィルム、ポリ塩化ビニル(PVC)フィルム、スチレン系樹脂フィルム(ポリスチレンフィルム、ABS樹脂フィルム、AS樹脂フィルム等)、アクリル樹脂フィルムなどが挙げられる。熱可塑性樹脂フィルムは、単層フィルムであってもよく、積層フィルムであってもよい。前記熱可塑性樹脂フィルムとしては無延伸フィルムであるのが好ましい。
本発明において、透明耐熱保護層は、無機酸化物粒子が架橋剤として含有されたポリシロキサン樹脂により形成された層である。無機酸化物粒子とポリシロキサン樹脂とは化学結合により結合しているのが好ましい。
-OR3 (3)
で表される基を含有する。式(3)で表される基はケイ素原子に結合しており、分子末端に存在する。
-OR4 (4)
で表される基を含有する。式(4)で表される基はケイ素原子に結合しており、分子末端に存在する。
本発明において、無機酸化物粒子が架橋剤として含有されたポリシロキサン樹脂中の無機酸化物粒子の含有量(或いは、透明耐熱保護層中の無機酸化物粒子の含有量)は適宜選択できるが、上限は、例えば30重量%、好ましくは20重量%、さらに好ましくは15重量%であり、下限は、例えば1重量%、好ましくは2重量%、さらに好ましくは3重量%である。無機酸化物粒子の含有量が少なすぎると、透明耐熱保護層の機械的強度が低下しやすく、無機酸化物粒子の含有量が多すぎると、透明耐熱保護層が脆くなりやすい。いずれの場合も、最終的に得られる透明耐熱難燃フィルムの曲げ強度が低下しやすくなり、該フィルムの透明耐熱保護層にクラックが入りやすくなる。
本発明の透明耐熱難燃フィルムは、前記熱変形温度が250℃以下で透明な非晶質性の熱可塑性樹脂フィルムの少なくとも一方の面に、無機酸化物粒子が架橋剤として含有されたポリシロキサン樹脂を含むシリコーン樹脂組成物から形成された透明耐熱保護層を設けることにより製造できる。
撹拌機、還流冷却器及び窒素導入管を備えた容器に、平均粒子径8-11nmのコロイダルシリカ溶液(商品名:スノーテクスOS、日産化学社製、固形分濃度20%)30g、2-プロパノール30g、2-メトキシエタノール5gを加えた。濃硝酸を加えて液の酸性度(pH)を2~4の範囲内に調整した。次いで70℃に昇温したのち、分子末端に反応性のメトキシシリル基を有するポリシロキサン化合物(シルセスキオキサン化合物)(商品名:X-40-9225、信越化学社製、メトキシ含有量24%)80gを2-プロパノール80gに溶解した液を、滴下ロートを用いて2時間かけて滴下し、ポリシロキサン化合物(シルセスキオキサン化合物)とコロイダルシリカ粒子表面の反応を行った。
次いで、分子末端に反応性のメトキシシリル基を有する別のポリシロキサン化合物(3官能アルコキシシラン及び2官能アルコキシシランから誘導されるポリシロキサン化合物)(商品名:X-40-9246、信越化学社製、メトキシ含有量12%)40gを2-プロパノール40gに溶解した液を1時間かけて滴下して、前記コロイダルシリカ上のシルセスキオキサン化合物と反応を行った。80℃で1時間加熱撹拌を行った後、ロータリーエバポレーターにて溶媒を留去し、次いでトルエンを80g加えて、90℃で1時間加熱撹拌を行った。室温に冷却し、溶媒を留去して粘度調整を行い、透明耐熱保護層形成用樹脂溶液Aを得た。
上記透明耐熱保護層形成用樹脂溶液Aを、剥離処理を施したポリエチレンテレフタレート(PET)フィルム(商品名「MRF38」、三菱樹脂社製)に、乾燥後の膜厚が100μmになるように塗工し、130℃で10分間加熱してフィルムを作製した。このフィルムの屈折率は1.41であった。
合成例1と同様の実験装置を用い、コロイダルシリカ溶液の量を60g、初期の2-プロパノールの量を60gに変えた以外は合成例1と同様の処理を行い、透明耐熱保護層形成用樹脂溶液Bを得た。
上記透明耐熱保護層形成用樹脂溶液Bを、剥離処理を施したポリエチレンテレフタレート(PET)フィルム(商品名「MRF38」、三菱樹脂社製)に、乾燥後の膜厚が100μmになるように塗工し、130℃で10分間加熱してフィルムを作製した。このフィルムの屈折率は1.42であった。
合成例1と同様の実験装置を用い、X-40-9225の量を80g、これを溶解するための2-プロパノールの量を80g、X-40-9246の量を30g、これを溶解するための2-プロパノールの量を30gに変えるとともに、X-40-9246を含む溶液の滴下終了後、さらに別の反応性のシラノール基を有するポリシロキサン化合物(商品名:X-21-3153、信越化学社製、シラノール基含有量1~14%)10gを2-プロパノール10gに溶解した液を1時間かけて滴下し、その後、80℃で1時間加熱撹拌を行ったこと以外は、合成例1と同様の処理を行い、透明耐熱保護層形成用樹脂溶液Cを得た。
上記透明耐熱保護層形成用樹脂溶液Cを、剥離処理を施したポリエチレンテレフタレート(PET)フィルム(商品名「MRF38」、三菱樹脂社製)に、乾燥後の膜厚が100μmになるように塗工し、130℃で10分間加熱してフィルムを作製した。このフィルムの屈折率は1.42であった。
無機酸化物粒子として、平均粒子サイズが約7nmで、且つその粒子表面をヘキサメチルジシラザンで表面処理されたシリカ(商品名:AEROSIL R816、日本アエロジル社製)30gを用い、これを水30gに超音波ホモジナイザーを用いて分散して水分散液を得た。合成例1において、平均粒子径8-11nmのコロイダルシリカ溶液(商品名:スノーテクスOS、日産化学社製、固形分濃度20%)の代わりに、前記水分散液を用いたこと以外は、合成例1と同様の処理を行い、保護層形成用樹脂溶液Dを得た。
上記透明耐熱保護層形成用樹脂溶液Dを、剥離処理を施したポリエチレンテレフタレート(PET)フィルム(商品名「MRF38」、三菱樹脂社製)に、乾燥後の膜厚が100μmになるように塗工し、130℃で10分間加熱してフィルムを作製した。このフィルムは透明性が低く、正確な屈折率は測定できなかった。
合成例1で得られた透明耐熱保護層形成用樹脂溶液Aを、乾燥後の膜厚が10μmになるように、ポリエチレンテレフタレート(PET)フィルム(商品名「ルミラーS10」、東レ社製、膜厚25μm、屈折率1.57)の両面に塗工し、130℃で10分間加熱乾燥して、透明耐熱保護層を形成し、透明耐熱難燃フィルムA1を得た。
実施例1において、ポリエチレンテレフタレート(PET)フィルムの代わりに、ポリカーボネートフィルム(商品名「ラクロンR」、インターナショナルケミカル社製、膜厚30μm、屈折率1.59)の両面に塗工した以外は、実施例1と同様の処理を行い、透明耐熱難燃フィルムA2を得た。
実施例1において、ポリエチレンテレフタレート(PET)フィルムの代わりに、シクロオレフィン系フィルム(商品名「アートンF5023」、JSR社製、膜厚30μm、屈折率1.51)の両面に塗工した以外は、実施例1と同様の処理を行い、透明耐熱難燃フィルムA3を得た。
実施例1において、ポリエチレンテレフタレート(PET)フィルムの代わりに、シクロオレフィン系フィルム(商品名「ゼオノア1060R」、日本ゼオン社製、膜厚30μm、屈折率1.53)の両面に塗工した以外は、実施例1と同様の処理を行い、透明耐熱難燃フィルムA4を得た。
実施例1において、ポリエチレンテレフタレート(PET)フィルムの代わりに、透明ポリオレフィン系フィルム[ポリ(メチルペンテン)共重合体フィルム](商品名「オピュランX-44B」、三井化学東セロ社製、膜厚25μm、屈折率1.46)の両面に塗工した以外は、実施例1と同様の処理を行い、透明耐熱難燃フィルムA5を得た。
実施例1において、合成例1で得られた透明耐熱保護層形成用樹脂溶液Aの代わりに、合成例2で得られた透明耐熱保護層形成用樹脂溶液Bを用いた以外は、実施例1と同様の処理を行い、透明耐熱難燃フィルムB1を得た。
実施例1において、合成例1で得られた透明耐熱保護層形成用樹脂溶液Aの代わりに、合成例3で得られた透明耐熱保護層形成用樹脂溶液Cを用いた以外は、実施例1と同様の処理を行い、透明耐熱難燃フィルムC1を得た。
実施例1において、合成例1で得られた透明耐熱保護層形成用樹脂溶液Aの代わりに、比較合成例1で得られた保護層形成用樹脂溶液Dを用いた以外は、実施例1と同様の処理を行い、フィルムD1を得た。
実施例及び比較例で得られた各透明耐熱難燃フィルム(比較例1はフィルムD1)について、以下の評価を行った。結果を表1に示す。なお、耐熱性等の評価項目については、透明耐熱保護層を設ける前の熱可塑性樹脂フィルムについても同様の評価を行った。表1の括弧内の数値等は、透明耐熱保護層を設ける前の熱可塑性樹脂フィルムの評価結果を示すものである。
株式会社村上色彩技術研究所製のヘイズメーター(商品名「HR-100」)を用いて、全光線透過率(%)(厚み:100μmのサンプル)を測定した。
各フィルムを10cm・2cmの大きさにカットし、長手方向の端に5gのおもりをつけ、250℃の乾燥機内で1時間つるし、フィルムの変化の有無を目視観察した。表1中、「切断」とは、フィルムが切れたことを意味する。
各フィルムを縦5cm、幅1cmにカットして、オートグラフ(SHIMAZU社製)のチャック部に長さ2cmになるようにセットして、300mm/minの速度で引張試験を行い、引張り強度(MPa)、引張り伸び(%)を測定した。
UL94に基づいて、難燃性を評価した。
ASTEM D696に準じて、線膨張係数を測定した。
JIS K5401に準じて、フィルム表面の鉛筆硬度を測定した。
各フィルムを縦5cm、幅1cmにカットし、長手方向の中央部において、180度に折り曲げた状態で1分間保持し、フィルム上の透明耐熱保護層(保護層)の状態を目視観察した。
2 透明耐熱保護層
3 透明耐熱難燃フィルム
Claims (8)
- 熱変形温度が250℃以下で透明な非晶質性の熱可塑性樹脂フィルムの少なくとも一方の面に、無機酸化物粒子が架橋剤として含有されたポリシロキサン樹脂により形成された透明耐熱保護層を有する透明耐熱難燃フィルム。
- 前記透明耐熱保護層の屈折率が1.40~1.43の範囲にある請求項1記載の透明耐熱難燃フィルム。
- 前記透明耐熱保護層の厚みが1~100μmの範囲にある請求項1又は2記載の透明耐熱難燃フィルム。
- 前記無機酸化物粒子が、その一次粒子径が1~100nmの範囲にあり、その表面電位がpH2~5の範囲にあるコロイダルシリカであり、該コロイダルシリカ表面のシラノール基が前記ポリシロキサン樹脂と化学結合して該ポリシロキサン樹脂を架橋している請求項1~3のいずれか1項に記載の透明耐熱難燃フィルム。
- 前記ポリシロキサン樹脂が、分子内にアルコキシシリル基及びシラノール基から選択された少なくとも1種の反応性基を有しており、該反応性基の総含有量が8~48重量%であるポリシロキサン樹脂であり、該ポリシロキサン樹脂が前記無機酸化物粒子と化学結合により架橋されている請求項1~4のいずれか1項に記載の透明耐熱難燃フィルム。
- 請求項1~5のいずれか1項に記載の透明耐熱難燃フィルムを用いた燃焼防止フィルム。
- 請求項1~5のいずれか1項に記載の透明耐熱難燃フィルムを用いた光学用フィルム。
- 熱変形温度が250℃以下で透明な非晶質性の熱可塑性樹脂フィルムの少なくとも一方の面に、無機酸化物粒子が架橋剤として含有されたポリシロキサン樹脂を含むシリコーン樹脂組成物から形成された透明耐熱保護層を設けることを特徴とする透明耐熱難燃フィルムの製造方法。