WO2013051288A1 - 複合構造体およびその製造方法、それを用いた包装材料および成形品、ならびにコーティング液 - Google Patents
複合構造体およびその製造方法、それを用いた包装材料および成形品、ならびにコーティング液 Download PDFInfo
- Publication number
- WO2013051288A1 WO2013051288A1 PCT/JP2012/006435 JP2012006435W WO2013051288A1 WO 2013051288 A1 WO2013051288 A1 WO 2013051288A1 JP 2012006435 W JP2012006435 W JP 2012006435W WO 2013051288 A1 WO2013051288 A1 WO 2013051288A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- acid
- composite structure
- coating liquid
- compound
- Prior art date
Abstract
Description
以下、本発明の複合構造体の製造方法及びそれに用いるコーティング液について説明する。この製造方法は、基材(X)と、基材(X)に積層された層(Y)とを含む複合構造体の製造方法である。この製造方法は、以下の工程(I)~(IV)を含む。工程(I)では、アルミニウム化合物(A)を含む分散液(S)を調製する。工程(II)では、分散液(S)と、アルミニウム化合物(A)と反応可能な部位を有するリン化合物(B)とを少なくとも混合することによってコーティング液(U)を調製する。工程(III)では、基材(X)上にコーティング液(U)を塗布することによって、基材(X)上に層(Y)の前駆体層を形成する。工程(IV)では、前駆体層を110℃以上の温度で熱処理することによって層(Y)を形成する。アルミニウム化合物(A)は、アルミン酸塩溶液に酸を添加することによって形成される化合物である。コーティング液(U)において、アルミニウム化合物(A)に由来するアルミニウム原子のモル数(NM)と、リン化合物(B)に由来するリン原子のモル数(NP)とが、0.8≦(NM)/(NP)≦4.5を満たす。
アルミン酸塩溶液はアルミン酸塩を含む溶液である。アルミン酸塩を構成する陰イオンは、たとえば[Al(OH)4]-、[Al(OH)6]3-等の形態をとると考えられている。アルミン酸塩溶液は、たとえば、水酸化アルミニウムを塩基に溶解することで得ることができる。アルミン酸塩溶液を、以下では、溶液(SA)という場合がある。工程(I)は、アルミン酸塩溶液に酸を添加することによってアルミニウム化合物(A)を含む水性懸濁液(D)を得る工程(I-a)と、水性懸濁液(D)の溶媒を除去した後に脱塩することによってアルミニウム化合物(A)を得る工程(I-b)とを含んでもよい。
溶液(SA)(アルミン酸塩溶液)は、水酸基を含有する有機化合物、前記重合体(C)あるいは水酸基を含有する重合体を含んでいてもよい。溶液(SA)が、水酸基など親水性の高い官能基を含有する有機化合物あるいは重合体を含むことによって、アルミニウム化合物(A)の溶媒への分散性が向上する。水酸基含有有機化合物は、好ましくは、水酸基を含有する水溶性の有機化合物である。水酸基を含有する水溶性の有機化合物の例としては、メタノール、エタノール、イソプロピルアルコール等のモノアルコール類やエチレングリコールやグリセリン等の多価アルコール類、ポリビニルアルコール等が挙げられる。前記重合体(C)の例は後述するが、これらのなかでも、水酸基を含有する重合体が好ましく、少量で効果が得られることからポリビニルアルコールが更に好ましい。
工程(II)では、分散液(S)と、アルミニウム化合物(A)と反応可能な部位を有するリン化合物(B)とを少なくとも混合することによってコーティング液(U)を調製する。なお、コーティング液(U)は、分散液(S)、リン化合物(B)および他の成分を混合することによって調製してもよい。コーティング液(U)は、分散液(S)と、リン化合物(B)を含む溶液(T)とを少なくとも混合することによって調製することが好ましい。
リン化合物(B)を含む溶液(T)は、リン化合物(B)を溶媒に溶解することによって調製できる。リン化合物(B)の溶解性が低い場合には、加熱処理や超音波処理を施すことによって溶解を促進してもよい。
リン化合物(B)は、アルミニウム化合物(A)と反応可能な部位を含有し、典型的には、そのような部位を複数含有する。好ましい一例では、リン化合物(B)は、そのような部位(原子団または官能基)を2~20個含有する。そのような部位の例には、アルミニウム化合物(A)の表面に存在する水酸基と反応可能な部位が含まれる。たとえば、そのような部位の例には、リン原子に直接結合したハロゲン原子や、リン原子に直接結合した酸素原子が含まれる。それらのハロゲン原子や酸素原子は、アルミニウム化合物(A)の表面に存在する水酸基と縮合反応(加水分解縮合反応)を起こすことができる。
重合体(C)は、水酸基、カルボキシル基、カルボン酸無水物基、およびカルボキシル基の塩からなる群より選ばれる少なくとも1種の官能基(f)を有する重合体である。複合構造体が有する層(Y)において重合体(C)は、それが有する官能基(f)によってアルミニウム化合物(A)の粒子およびリン化合物(B)に由来するリン原子の一方または両方と直接的にまたは間接的に結合していてもよい。また複合構造体が有する層(Y)において後述する反応生成物(R)は、重合体(C)がアルミニウム化合物(A)やリン化合物(B)と反応するなどして生じる重合体(C)部分を有していてもよい。なお、本明細書において、リン化合物(B)としての要件を満たす重合体であって官能基(f)を含む重合体は、重合体(C)には含めずにリン化合物(B)として扱う。
工程(III)では、基材(X)上にコーティング液(U)を塗布することによって、基材(X)上に層(Y)の前駆体層を形成する。コーティング液(U)は、基材(X)の少なくとも一方の面の上に直接塗布してもよい。また、コーティング液(U)を塗布する前に、基材(X)の表面を公知のアンカーコーティング剤で処理したり、基材(X)の表面に公知の接着剤を塗布したりするなどして、基材(X)の表面に接着層(H)を形成しておいてもよい。
工程(IV)では、工程(III)で形成された前駆体層(層(Y)の前駆体層)を、110℃以上の温度で熱処理することによって層(Y)を形成する。前駆体層を処理する方法としては、熱処理、紫外線等の電磁波照射などが挙げられる。工程(IV)で行われる処理は、アルミニウム化合物(A)とリン化合物(B)とを反応させる処理であってもよい。たとえば、工程(IV)で行われる処理は、アルミニウム化合物(A)とリン化合物(B)とを反応させることによって、リン化合物(B)に由来するリン原子を介してアルミニウム化合物(A)の粒子同士を結合させる処理であってもよい。なお、特に限定されるわけではないが、前記前駆体層の赤外線吸収スペクトルにおいては、800~1400cm-1の範囲における最大吸光度(A1’)と、2500~4000cm-1の範囲における水酸基の伸縮振動に基づく最大吸光度(A2’)とが、吸光度(A2’)/吸光度(A1’)>0.2の関係を満たす場合がある。
本発明のコーティング液は、上述したコーティング液(U)である。すなわち、本発明のコーティング液は、アルミニウム化合物(A)とリン化合物(B)と溶媒とを含む。上述したように、本発明のコーティング液は、重合体(C)および酸化合物(D)からなる群より選ばれる少なくとも1つをさらに含んでもよい。本発明のコーティング液(U)で形成された層を110℃以上の温度で熱処理することによって、層(Y)を形成できる。
本発明の複合構造体は、本発明の製造方法によって製造できる。なお、本発明の製造方法について説明した事項は、本発明の複合構造体に適用できるため、重複する説明を省略する場合がある。また、本発明の複合構造体に適用した事項は、本発明の製造方法に適用できる。
本発明の複合構造体が有する層(Y)の厚さ(複合構造体が2層以上の層(Y)を有する場合には各層(Y)の厚さの合計)は、4.0μm以下であることが好ましく、2.0μm以下であることがより好ましく、1.0μm以下であることがさらに好ましく、0.9μm以下であることが特に好ましい。層(Y)を薄くすることによって、印刷、ラミネート等の加工時における複合構造体の寸法変化を低く抑えることができ、さらに複合構造体の柔軟性が増し、その力学的特性を、基材自体の力学的特性に近づけることができる。本発明の複合構造体では、層(Y)の厚さの合計が1.0μm以下(例えば0.9μm以下)の場合でも、40℃、90/0%RH(相対湿度)の条件下における透湿度を5g/(m2・day)以下とし、且つ、20℃、85%RH(相対湿度)の条件下における酸素透過度を1ml/(m2・day・atm)以下とすることが可能である。ここで「90/0%RH」とは複合構造体に対して一方の側の相対湿度が90%で他方の側の相対湿度が0%であることを意味する。また、層(Y)の厚さ(複合構造体が2層以上の層(Y)を有する場合には各層(Y)の厚さの合計)は、0.1μm以上(例えば0.2μm以上)であることが好ましい。なお、層(Y)1層当たりの厚さは、本発明の複合構造体のバリア性がより良好になる観点から、0.05μm以上(例えば0.15μm以上)であることが好ましい。層(Y)の厚さは、層(Y)の形成に用いられる後述するコーティング液(U)の濃度や、その塗布方法によって制御することができる。
本発明の複合構造体が有する基材(X)の材質に特に制限はなく、様々な材質からなる基材を用いることができる。基材(X)の材質としては、例えば、熱可塑性樹脂、熱硬化性樹脂等の樹脂;布帛、紙類等の繊維集合体;木材;ガラス;金属;金属酸化物などが挙げられる。なお、基材は複数の材質からなる複合構成または多層構成のものであってもよい。
本発明の複合構造体において、層(Y)は、基材(X)と直接接触するように積層されていてもよいが、基材(X)と層(Y)との間に配置された接着層(H)を介して層(Y)が基材(X)に積層されていてもよい。この構成によれば、基材(X)と層(Y)との接着性を高めることができる場合がある。接着層(H)は、接着性樹脂で形成してもよい。接着性樹脂からなる接着層(H)は、基材(X)の表面を公知のアンカーコーティング剤で処理するか、基材(X)の表面に公知の接着剤を塗布することによって形成できる。当該接着剤としては、ポリイソシアネート成分とポリオール成分とを混合し反応させる二液反応型ポリウレタン系接着剤が好ましい。また、アンカーコーティング剤や接着剤に、公知のシランカップリング剤などの少量の添加剤を加えることによって、さらに接着性を高めることができる場合がある。シランカップリング剤の好適な例としては、イソシアネート基、エポキシ基、アミノ基、ウレイド基、メルカプト基などの反応性基を有するシランカップリング剤を挙げることができる。基材(X)と層(Y)とを接着層(H)を介して強く接着することによって、本発明の複合構造体に対して印刷やラミネートなどの加工を施す際に、バリア性や外観の悪化をより効果的に抑制することができる。
本発明の複合構造体(積層体)は、基材(X)および層(Y)のみによって構成されてもよいし、基材(X)、層(Y)および接着層(H)のみによって構成されていてもよい。本発明の複合構造体は、複数の層(Y)を含んでもよい。また、本発明の複合構造体は、基材(X)、層(Y)および接着層(H)以外の他の部材(例えば熱可塑性樹脂フィルム層、紙層、無機蒸着層等の他の層など)をさらに含んでもよい。そのような他の部材(他の層など)を有する本発明の複合構造体は、基材(X)に直接または接着層(H)を介して層(Y)を積層させた後に、さらに当該他の部材(他の層など)を直接または接着層を介して接着または形成することによって製造できる。このような他の部材(他の層など)を複合構造体に含ませることによって、複合構造体の特性を向上させたり、新たな特性を付与したりすることができる。例えば、本発明の複合構造体にヒートシール性を付与したり、バリア性や力学的物性をさらに向上させたりすることができる。
(1)層(Y)/ポリエステル層、
(2)層(Y)/ポリエステル層/層(Y)、
(3)層(Y)/ポリアミド層、
(4)層(Y)/ポリアミド層/層(Y)、
(5)層(Y)/ポリオレフィン層、
(6)層(Y)/ポリオレフィン層/層(Y)、
(7)層(Y)/水酸基含有ポリマー層、
(8)層(Y)/水酸基含有ポリマー層/層(Y)、
(9)層(Y)/紙層、
(10)層(Y)/紙層/層(Y)、
(11)層(Y)/無機蒸着フィルム層/ポリエステル層、
(12)層(Y)/無機蒸着フィルム層/ポリアミド層、
(13)層(Y)/無機蒸着フィルム層/ポリオレフィン層、
(14)層(Y)/無機蒸着フィルム層/水酸基含有ポリマー層、
(15)層(Y)/ポリエステル層/ポリアミド層/ポリオレフィン層、
(16)層(Y)/ポリエステル層/層(Y)/ポリアミド層/ポリオレフィン層、
(17)ポリエステル層/層(Y)/ポリアミド層/ポリオレフィン層、
(18)層(Y)/ポリアミド層/ポリエステル層/ポリオレフィン層、
(19)層(Y)/ポリアミド層/層(Y)/ポリエステル層/ポリオレフィン層、
(20)ポリアミド層/層(Y)/ポリエステル層/ポリオレフィン層、
(21)層(Y)/ポリオレフィン層/ポリアミド層/ポリオレフィン層、
(22)層(Y)/ポリオレフィン層/層(Y)/ポリアミド層/ポリオレフィン層、
(23)ポリオレフィン層/層(Y)/ポリアミド層/ポリオレフィン層、
(24)層(Y)/ポリオレフィン層/ポリオレフィン層、
(25)層(Y)/ポリオレフィン層/層(Y)/ポリオレフィン層、
(26)ポリオレフィン層/層(Y)/ポリオレフィン層、
(27)層(Y)/ポリエステル層/ポリオレフィン層、
(28)層(Y)/ポリエステル層/層(Y)/ポリオレフィン層、
(29)ポリエステル層/層(Y)/ポリオレフィン層、
(30)層(Y)/ポリアミド層/ポリオレフィン層、
(31)層(Y)/ポリアミド層/層(Y)/ポリオレフィン層、
(32)ポリアミド層/層(Y)/ポリオレフィン層、
(33)層(Y)/ポリエステル層/紙層、
(34)層(Y)/ポリアミド層/紙層、
(35)層(Y)/ポリオレフィン層/紙層、
(36)ポリオレフィン層/紙層/ポリオレフィン層/層(Y)/ポリエステル層/ポリオレフィン層、
(37)ポリオレフィン層/紙層/ポリオレフィン層/層(Y)/ポリアミド層/ポリオレフィン層、
(38)ポリオレフィン層/紙層/ポリオレフィン層/層(Y)/ポリオレフィン層、
(39)紙層/ポリオレフィン層/層(Y)/ポリエステル層/ポリオレフィン層、
(40)ポリオレフィン層/紙層/層(Y)/ポリオレフィン層、
(41)紙層/層(Y)/ポリエステル層/ポリオレフィン層、
(42)紙層/層(Y)/ポリオレフィン層、
(43)層(Y)/紙層/ポリオレフィン層、
(44)層(Y)/ポリエステル層/紙層/ポリオレフィン層、
(45)ポリオレフィン層/紙層/ポリオレフィン層/層(Y)/ポリオレフィン層/水酸基含有ポリマー層、
(46)ポリオレフィン層/紙層/ポリオレフィン層/層(Y)/ポリオレフィン層/ポリアミド層、
(47)ポリオレフィン層/紙層/ポリオレフィン層/層(Y)/ポリオレフィン層/ポリエステル層。
(性能1)40℃、90/0%RHの条件下における透湿度が5g/(m2・day)以下である。
(性能2)20℃、85%RHの条件下における酸素透過度が、1ml/(m2・day・atm)以下である。
(性能3)120℃の熱水中に30分間浸漬した後の40℃、90/0%RHの条件下における透湿度が、浸漬前の40℃、90/0%RHの条件下における透湿度の2倍以下である。
(性能4)120℃の熱水中に30分間浸漬した後の20℃、85%RHの条件下における酸素透過度が、浸漬前の20℃、85%RHの条件下における酸素透過度の2倍以下である。
本発明の複合構造体は、ガスバリア性および水蒸気バリア性のいずれにも優れ、屈曲処理後においても、両バリア性を高いレベルで維持できる。また、本発明によれば、外観に優れる複合構造体を得ることができる。そのため、本発明の複合構造体は、様々な用途に適用できる。本発明の複合構造体は、包装材料として特に好ましく用いられる。包装材料以外の用途の例には、LCD用基板フィルム、有機EL用基板フィルム、電子ペーパー用基板フィルム、電子デバイス用封止フィルム、PDP用フィルム、LED用フィルム、ICタグ用フィルム、太陽電池用バックシート、太陽電池用保護フィルムなどの電子デバイス関連フィルム、光通信用部材、電子機器用フレキシブルフィルム、燃料電池用隔膜、燃料電池用封止フィルム、各種機能性フィルムの基板フィルムが含まれる。
(1)バリア層/基材/バリア層
(2)基材/バリア層/接着層/表面保護層
(3)バリア層/基材/バリア層/接着層/表面保護層
実施例で形成される層(Y)の赤外線吸収スペクトル、および比較例で形成される層(Y’)の赤外線吸収スペクトルは、以下の方法で測定した。
得られた複合構造体の外観を、目視によって下記のように評価した。
S:無色透明で均一な外観であり、きわめて良好であった。
A:わずかにくもりまたはムラが見られたが良好であった。
B:コーティング液のはじきなどによって、連続した層が得られなかった。
酸素透過度(OTR)は、酸素透過量測定装置(モダンコントロール社製「MOCON OX-TRAN2/20」)を用いて測定した。具体的には、酸素供給側に層(Y)(または層(Y’))が向き、キャリアガス側に後述するCPPの層が向くように複合構造体をセットし、温度が20℃、酸素供給側の湿度が85%RH、キャリアガス側の湿度が85%RH、酸素圧が1気圧、キャリアガス圧力が1気圧の条件下で酸素透過度(単位:ml/(m2・day・atm))を測定した。キャリアガスとしては2体積%の水素ガスを含む窒素ガスを使用した。
12cm×12cmの大きさの複合構造体を2枚作製した。そして、その2枚を、後述するCPPの層が内側になるように重ね合わせたのち、その3辺をその端から5mmまでヒートシールした。ヒートシールされた2枚の複合構造体の間に蒸留水80gを注入したのち、残された第4辺を同様にヒートシールした。このようにして、蒸留水が中に入ったパウチを作製した。
透湿度(水蒸気透過度;WVTR)は、水蒸気透過量測定装置(モダンコントロール社製「MOCON PERMATRAN3/33」)を用いて測定した。具体的には、水蒸気供給側に層(Y)(または層(Y’))が向き、キャリアガス側に後述するCPPの層が向くように複合構造体をセットし、温度が40℃、水蒸気供給側の湿度が90%RH、キャリアガス側の湿度が0%RHの条件下で透湿度(単位:g/(m2・day))を測定した。
レトルト処理後のサンプルは、レトルト処理後の酸素バリア性の項で述べた方法と同様によって得た。得られたサンプルの透湿度(水蒸気透過度;WVTR)を、水蒸気透過量測定装置(モダンコントロール社製「MOCON PERMATRAN3/33」)を用いて測定した。具体的には、水蒸気供給側に層(Y)(または層(Y’))が向き、キャリアガス側に後述するCPPの層が向くように複合構造体をセットし、温度が40℃、水蒸気供給側の湿度が90%RH、キャリアガス側の湿度が0%RHの条件下で透湿度(単位:g/(m2・day))を測定した。
実施例で作製されたコーティング液(U)中の粒子の粒子サイズは、以下の方法で測定した。
260.00質量部の20質量%水酸化ナトリウム溶液に28.53質量部の水酸化アルミニウムを添加し、95℃に昇温して溶解させた。この溶液を40℃まで冷却した後、79.60質量部の酢酸を滴下し、水性懸濁液(D1)を得た。続いて、水性懸濁液(D1)を濾過した後、得られた固体を300質量部の蒸留水中で洗浄、乾燥することにより脱塩しアルミニウム化合物(A1)を得た。741.86質量部の蒸留水、178.02質量部のメタノール及び10.00質量部の60%硝酸を含む溶液をホモミキサー(プライミクス株式会社製、TKホモミキサー2.5型)(周速19.8m/s:13500rpm)で攪拌しながら、アルミニウム化合物(A1)を添加した。続いて、液温度20~30℃で60分攪拌し、分散液(S1)を得た。
アルミン酸塩溶液に添加する酸として1.0N塩酸を使用したこと以外は実施例1と同様の方法によって、実施例2の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
260.00質量部の20質量%水酸化ナトリウム溶液に28.53質量部の水酸化アルミニウムを添加し、95℃に昇温して溶解させた。得られた溶液を、80℃に昇温した780.00質量部の20質量%エタノール水溶液(624.00質量部の蒸留水と156.00質量部のエタノールとの混合液)に攪拌しながら滴下した。得られた溶液を40℃に冷却した後、79.40質量部の酢酸を滴下し、水性懸濁液(D3)を得た。この懸濁液(D3)を得る操作以降は実施例1と同様の方法によって、実施例3の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
エタノール水溶液の濃度を20質量%から70質量%に変更したこと以外は実施例3と同様の方法によって、実施例4の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
エタノール水溶液をメタノール水溶液に変更したこと以外は実施例3と同様の方法によって、実施例5の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
エタノール水溶液をイソプロピルアルコール水溶液に変更したこと以外は実施例3と同様の方法によって、実施例6の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
260.00質量部の20質量%水酸化ナトリウム溶液に28.53質量部の水酸化アルミニウムを添加し、95℃に昇温して溶解させた。この溶液を、95℃に昇温した5.00×10-3質量%PVA水溶液780.00質量部に攪拌しながら滴下した。この溶液を40℃に冷却した後、80.10質量部の酢酸を滴下し、水性懸濁液(D7)を得た。この懸濁液(D7)を70℃の熱風乾燥機で24時間乾燥した後、得られた固体を、25℃の蒸留水300.00質量部により洗浄、乾燥することにより脱塩し、アルミニウム化合物(A7)を得た。このアルミニウム化合物(A7)を得る操作以降は実施例1と同様の方法によって、実施例7の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
60%硝酸を添加しないこと以外は実施例1と同様の方法によって、実施例8の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
5質量%PVA水溶液を添加しないこと以外は実施例1と同様の方法によって、実施例9の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
5.00質量部の5質量%PVA水溶液の代わりに、5.00質量部の5質量%PAA水溶液を使用したこと以外は実施例1と同様の方法によって、実施例10の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
36.58質量部の85質量%リン酸水溶液の代わりに、44.45質量部のリン酸トリメチルを使用したこと以外は実施例1と同様の方法によって、実施例11の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
ホモミキサーの攪拌速度を周速19.8m/s(13500rpm)から16.1m/s(11000rpm)に変更したこと以外は実施例1と同様の方法によって、実施例12の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
ホモミキサーの攪拌速度を周速19.8m/s(13500rpm)から11.7m/s(8000rpm)に変更したこと以外は実施例1と同様の方法によって、実施例13の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
ホモミキサーのかわりに周速1.3m/s(500rpm)のスリーワンモータ(新東科学株式会社製、BL600、攪拌翼:ディスパー型、攪拌翼径:φ=50mm)を使用したこと以外は実施例1と同様の方法によって、複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
60質量%の硝酸を添加しなかったこと以外は実施例14と同様の方法によって、実施例15の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
(モル数(NM))/(モル数(NP))の比率を表1に従って変更したこと以外は実施例1と同様の方法によって、実施例16~19の複合構造体を製造し、コーティング液およびそれらの複合構造体について測定および評価を行った。
基材を延伸ナイロンフィルム(ユニチカ株式会社製 「エンブレム ONBC」(商品名)、厚さ15μm、「ONy」と略記することがある)としたこと以外は実施例1と同様の方法によって、実施例20の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
熱処理の温度を表1に従って変更したこと以外は実施例1と同様の方法によって、実施例21および22の複合構造体を製造し、コーティング液およびそれらの複合構造体について測定および評価を行った。
741.86質量部の蒸留水及び188.02質量部のメタノールを含む溶液をホモミキサー(周速19.8m/s:13500rpm)で攪拌しながら、28.53質量部の水酸化アルミニウムを添加した。続いて、液温度20~30℃で60分攪拌し、分散液(SC1)を得た。この分散液(SC1)を得る操作以降は実施例1と同様の方法によって、比較例1の複合構造体の製造を行った。しかし、粒子の分散性が悪く均一な層が得られなかった。コーティング液について測定を行った。
741.86質量部の蒸留水、178.02質量部のメタノール及び10.00質量部の60%硝酸を含む溶液をホモミキサー(周速19.8m/s:13500rpm)で攪拌しながら、28.53質量部の水酸化アルミニウムを添加した。続いて、液温度20~30℃で60分攪拌し、分散液(SC2)を得た。この分散液(SC2)を得る操作以降は実施例1と同様の方法によって、比較例2の複合構造体の製造を行った。しかし、粒子の分散性が悪く均一な層が得られなかった。コーティング液について測定を行った。
(モル数(NM))/(モル数(NP))の比率を表1に従って変更したこと以外は実施例1と同様の方法によって、比較例3および4の複合構造体を製造し、コーティング液およびそれらの複合構造体について測定および評価を行った。
熱処理の温度を表1に従って変更したこと以外は実施例1と同様の方法によって、比較例5の複合構造体を製造し、コーティング液およびその複合構造体について測定および評価を行った。
Claims (32)
- アルミニウム化合物(A)を含む分散液(S)を調製する工程(I)と、
前記分散液(S)と、前記アルミニウム化合物(A)と反応可能な部位を有するリン化合物(B)とを少なくとも混合する工程(II)とを含む製造方法によって製造されるコーティング液であって、
前記アルミニウム化合物(A)は、アルミン酸塩溶液に酸を添加することによって形成される化合物であり、
前記アルミニウム化合物(A)に由来するアルミニウム原子のモル数(NM)と、前記リン化合物(B)に由来するリン原子のモル数(NP)とが、0.8≦(NM)/(NP)≦4.5を満たし、
該コーティング液中の粒子の粒子サイズが2000nm以下であるコーティング液。 - 前記工程(I)が、
前記アルミン酸塩溶液に前記酸を添加することによって前記アルミニウム化合物(A)を含む水性懸濁液(D)を得る工程(I-a)と、
前記水性懸濁液(D)の溶媒を除去した後に脱塩することによって前記アルミニウム化合物(A)を得る工程(I-b)とを含む、請求項1に記載のコーティング液。 - 前記アルミン酸塩溶液が、水酸基を含有する有機化合物を含む、請求項1または2に記載のコーティング液。
- 前記アルミン酸塩溶液が、水酸基、カルボキシル基、カルボン酸無水物基、およびカルボキシル基の塩からなる群より選ばれる少なくとも1種の官能基(f)を含有する重合体(C)を含む、請求項1または2に記載のコーティング液。
- 前記アルミン酸塩溶液が、水酸基を含有する重合体を含む、請求項3または4に記載のコーティング液。
- 前記工程(I)は、
前記工程(I-b)で得られた前記アルミニウム化合物(A)を高せん断攪拌によって液体中に分散させて分散液(S)を調製する工程(I-c)を含む、請求項2に記載のコーティング液。 - 前記リン化合物(B)が、リン酸、ポリリン酸、亜リン酸、ホスホン酸、およびそれらの誘導体からなる群より選ばれる少なくとも1種の化合物である、請求項1~6のいずれか1項に記載のコーティング液。
- 前記重合体(C)を含む、請求項4に記載のコーティング液。
- 前記重合体(C)が、ポリビニルアルコール、エチレン-ビニルアルコール共重合体、多糖類、ポリアクリル酸、ポリアクリル酸の塩、ポリメタクリル酸、およびポリメタクリル酸の塩からなる群より選ばれる少なくとも1種の重合体である、請求項8に記載のコーティング液。
- 酢酸、塩酸、硝酸、トリフルオロ酢酸およびトリクロロ酢酸からなる群より選ばれる少なくとも1種の酸化合物(D)をさらに含む、請求項1~9のいずれか1項に記載のコーティング液。
- 基材(X)と、前記基材(X)に積層された層(Y)とを含む複合構造体の製造方法であって、
アルミニウム化合物(A)を含む分散液(S)を調製する工程(I)と、
前記分散液(S)と、前記アルミニウム化合物(A)と反応可能な部位を有するリン化合物(B)とを少なくとも混合することによってコーティング液(U)を調製する工程(II)と、
前記基材(X)上に前記コーティング液(U)を塗布することによって、前記基材(X)上に前記層(Y)の前駆体層を形成する工程(III)と、
前記前駆体層を110℃以上の温度で熱処理することによって前記層(Y)を形成する工程(IV)とを含み、
前記アルミニウム化合物(A)は、アルミン酸塩溶液に酸を添加することによって形成される化合物であり、
前記コーティング液(U)において、前記アルミニウム化合物(A)に由来するアルミニウム原子のモル数(NM)と、前記リン化合物(B)に由来するリン原子のモル数(NP)とが、0.8≦(NM)/(NP)≦4.5を満たす、製造方法。 - 前記工程(I)は、
アルミン酸塩溶液に前記酸を添加することによって前記アルミニウム化合物(A)を含む水性懸濁液(D)を得る工程(I-a)と、
前記水性懸濁液(D)の溶媒を除去した後に脱塩することによって前記アルミニウム化合物(A)を得る工程(I-b)とを含み、
前記工程(II)は、前記分散液(S)と、前記リン化合物(B)を含む溶液(T)とを混合することによって前記コーティング液(U)を調製する工程である、請求項11に記載の製造方法。 - 前記アルミン酸塩溶液が、水酸基を含有する有機化合物を含む、請求項12に記載の製造方法。
- 前記アルミン酸塩溶液が、水酸基、カルボキシル基、カルボン酸無水物基、およびカルボキシル基の塩からなる群より選ばれる少なくとも1種の官能基(f)を含有する重合体(C)を含む、請求項11または12に記載の製造方法。
- 前記アルミン酸塩溶液が、水酸基を含有する重合体を含む、請求項11または12に記載の製造方法。
- 前記工程(I)は、
前記工程(I-b)で得られた前記アルミニウム化合物(A)を高せん断攪拌によって液体中に分散させて分散液(S)を調製する工程(I-c)を含む、請求項12または13に記載の製造方法。 - 前記リン化合物(B)が、リン酸、ポリリン酸、亜リン酸、ホスホン酸、およびそれらの誘導体からなる群より選ばれる少なくとも1種の化合物である、請求項11~16のいずれか1項に記載の製造方法。
- 前記コーティング液(U)が、水酸基、カルボキシル基、カルボン酸無水物基、およびカルボキシル基の塩からなる群より選ばれる少なくとも1種の官能基(f)を含有する重合体(C)を含む、請求項11~17のいずれか1項に記載の製造方法。
- 前記重合体(C)が、ポリビニルアルコール、エチレン-ビニルアルコール共重合体、多糖類、ポリアクリル酸、ポリアクリル酸の塩、ポリメタクリル酸、およびポリメタクリル酸の塩からなる群より選ばれる少なくとも1種の重合体である、請求項18に記載の製造方法。
- 前記コーティング液(U)が、酢酸、塩酸、硝酸、トリフルオロ酢酸およびトリクロロ酢酸からなる群より選ばれる少なくとも1種の酸化合物(D)をさらに含む、請求項11~19のいずれか1項に記載の製造方法。
- 請求項11~20のいずれか1項に記載の製造方法によって得られる複合構造体。
- 800~1400cm-1の範囲における前記層(Y)の赤外線吸収スペクトルにおいて、赤外線吸収が最大となる波数(n1)が1080~1130cm-1の範囲にある、請求項21に記載の複合構造体。
- 前記基材(X)が層状である、請求項21または22に記載の複合構造体。
- 前記基材(X)が、熱可塑性樹脂フィルム層、紙層、および無機蒸着層からなる群より選ばれる少なくとも1種の層を含む、請求項23に記載の複合構造体。
- 40℃、90/0%RHの条件下における透湿度が5g/(m2・day)以下である、請求項21~24のいずれか1項に記載の複合構造体。
- 20℃、85%RHの条件下における酸素透過度が1ml/(m2・day・atm)以下である、請求項21~25のいずれか1項に記載の複合構造体。
- 120℃の熱水中に30分間浸漬した後の40℃、90/0%RHの条件下における透湿度が、浸漬前の40℃、90/0%RHの条件下における透湿度の2倍以下である、請求項21~25のいずれか1項に記載の複合構造体。
- 120℃の熱水中に30分間浸漬した後の20℃、85%RHの条件下における酸素透過度が、浸漬前の20℃、85%RHの条件下における酸素透過度の2倍以下である、請求項21~26のいずれか1項に記載の複合構造体。
- 請求項21~28のいずれか1項に記載の複合構造体を含む包装材料。
- レトルト食品用の包装材料である、請求項29に記載の包装材料。
- 請求項29に記載の包装材料を用いて形成される成形品。
- 縦製袋充填シール袋、真空包装袋、スパウト付パウチ、ラミネートチューブ容器、輸液バッグ、容器用蓋材、紙容器または真空断熱体である、請求項31に記載の成形品。