WO2013035589A1 - 変性共役ジエン系重合体の製造方法、変性共役ジエン系重合体、変性共役ジエン系重合体組成物、ゴム組成物及びタイヤ - Google Patents
変性共役ジエン系重合体の製造方法、変性共役ジエン系重合体、変性共役ジエン系重合体組成物、ゴム組成物及びタイヤ Download PDFInfo
- Publication number
- WO2013035589A1 WO2013035589A1 PCT/JP2012/071730 JP2012071730W WO2013035589A1 WO 2013035589 A1 WO2013035589 A1 WO 2013035589A1 JP 2012071730 W JP2012071730 W JP 2012071730W WO 2013035589 A1 WO2013035589 A1 WO 2013035589A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- conjugated diene
- diene polymer
- compound
- carbon atoms
- modified conjugated
- Prior art date
Abstract
Description
一方、安全性の観点からは、ウェットスキッド抵抗に優れ、実用上十分な耐摩耗性、破壊特性を有する材料の開発が求められている。
シリカを用いると、低ヒステリシスロス性及びウェットスキッド抵抗性の向上が図ることができるという利点を有している。しかし、カーボンブラックの表面が疎水性であるのに対し、シリカの表面は親水性であるため、共役ジエン系ゴムとの親和性が低く、カーボンブラックに比較して分散性が悪いという欠点を有していることから、分散性を改良させたり、シリカ-共役ジエン系ゴム間の結合付与を行ったりするため、別途シランカップリング剤等を含有させる必要がある。
特許文献2~4には、アミノ基を含有するアルコキシシラン類を重合体活性末端に反応させて得られる変性ジエン系ゴム、及びこれらとシリカとの組成物についての提案がなされている。
特許文献5には、環式アザシラサイクル化合物を重合体活性末端と反応させて官能化した変性ジエン系ゴムが提案されている。
また、特許文献6には重合体活性末端と多官能性シラン化合物とをカップリング反応させて得られる変性ジエン系ゴムが提案されている。
また、特許文献7の変性ジエン系ゴムは、両末端に官能基を導入したことにより、より一層のヒステリシスロスの低減効果が見られるものの、混練り中に変性ジエン系ゴムの分子鎖の末端の変性基とシリカ等の無機充填剤との反応が進行して粘度が上昇し、混練りが困難になったり、混練り後にシートに加工する際の肌荒れやシートの切れが生じやすくなったりするなど、加工性が悪化する傾向があるという問題を有している。
すなわち、本発明は以下の通りである。
すなわち、本発明は下記の通りである。
下記化学式(1)又は(2)で表される、分子内に少なくとも1つ窒素原子を有する化合物及び有機リチウム化合物を含む重合開始剤を用い、
共役ジエン化合物、又は共役ジエン化合物と芳香族ビニル化合物とを重合又は共重合することで、活性末端を有する共役ジエン系重合体を得る重合工程と、
前記共役ジエン系重合体の活性末端に、下記化学式(6)で表される変性剤を反応させる変性工程と、
を、有する、変性共役ジエン系重合体の製造方法。
R1及びR2は、結合して隣接した窒素原子とともに環状構造を形成していてもよく、その場合はR1及びR2は、合計の炭素数が5~12の炭化水素基であって、不飽和結合を有していても、分岐構造を有していてもよい。
前記重合工程で用いられる重合開始剤が、
前記分子内に少なくとも1つ窒素原子を有する化合物及び前記有機リチウム化合物を反応させることにより得られる、下記化学式(7)又は(8)で表される分子内に少なくとも1つ窒素原子を有する有機リチウム化合物を含む、前記〔1〕に記載の変性共役ジエン系重合体の製造方法。
R1及びR2は、結合して隣接した窒素原子とともに環状構造を形成していてもよく、その場合はR1及びR2は、合計の炭素数が5~12の炭化水素基であって、不飽和結合を有していても、分岐構造を有していてもよい。
前記重合工程が、
下記化学式(1)又は(2)で表される分子内に少なくとも1つ窒素原子を有する化合物と、
有機リチウム化合物と、
共役ジエン化合物、又は共役ジエン化合物と芳香族ビニル化合物と、
を同時に添加し、重合又は共重合することで、活性末端を有する共役ジエン系重合体を得る工程を含む、
前記〔1〕又は〔2〕に記載の変性共役ジエン系重合体の製造方法。
R1及びR2は、結合して隣接した窒素原子とともに環状構造を形成していてもよく、その場合はR1及びR2は、合計の炭素数が5~12の炭化水素基であって、不飽和結合を有していても、分岐構造を有していてもよい。
前記式(6)において、mが2であり、nが3である、前記〔1〕乃至〔3〕のいずれか一に記載の変性共役ジエン系重合体の製造方法。
〔5〕
前記〔1〕乃至〔4〕のいずれか一に記載の変性共役ジエン系重合体の製造方法によって得られる、変性共役ジエン系重合体。
〔6〕
前記〔5〕に記載の変性共役ジエン系重合体を20質量部以上含有するゴム成分100質量部と、
シリカ系無機充填剤0.5~300質量部と、
を、含む、変性共役ジエン系重合体組成物。
〔7〕
前記〔6〕に記載の変性共役ジエン系重合体組成物を架橋処理したゴム組成物。
〔8〕
前記〔7〕に記載のゴム組成物を含むタイヤ。
本実施形態の変性共役ジエン系重合体の製造方法は、
下記化学式(1)又は(2)で表される、分子内に少なくとも1つ窒素原子を有する化合物及び有機リチウム化合物を含む重合開始剤を用い、
共役ジエン化合物、又は共役ジエン化合物と芳香族ビニル化合物とを重合又は共重合することで、活性末端を有する共役ジエン系重合体を得る重合工程と、
前記共役ジエン系重合体の活性末端に、下記化学式(6)で表される変性剤を反応させる変性工程と、
を、有する。
R1及びR2は、結合して隣接した窒素原子とともに環状構造を形成していてもよく、その場合はR1及びR2は、合計の炭素数が5~12の炭化水素基であって、不飽和結合を有していても、分岐構造を有していてもよい。
重合工程においては、上記化学式(1)又は(2)で表される、分子内に少なくとも1つ窒素原子を有する化合物及び有機リチウム化合物を含む重合開始剤を用い、共役ジエン化合物、又は共役ジエン化合物と芳香族ビニル化合物とを重合又は共重合し、活性末端を有する共役ジエン系重合体を得る。
本実施形態では、分子内に少なくとも1つ窒素原子を有する化合物及び有機リチウム化合物を含む、所定の重合開始剤を用いる。
重合開始剤は、分子内に少なくとも1つ窒素原子を有する化合物と有機リチウム化合物とが反応することによって得られる、後述する式(7)又は(8)で表される、分子内に少なくとも1つ窒素原子を有する有機リチウム化合物を含んでおり、窒素を有さない有機リチウム化合物を含んでいてもよい。当該式(7)又は(8)で表される、分子内に少なくとも1つ窒素原子を有する有機リチウム化合物は、予め所定の反応器で調製しておいてもよいし、後述する重合又は共重合を行うための反応器中に供給し、重合又は共重合と同時、もしくはその前に、分子内に少なくとも1つ窒素原子を有する化合物と有機リチウムを反応させてもよい。
分子内に少なくとも1つ窒素原子を有する化合物としては、下記式(1)、(2)で表される化合物を用いる。
前記式(1)で表される化合物としては、以下に限定されるものではないが、例えば、ジメチルアミン、ジエチルアミン、ジブチルアミン、ジプロピルアミン、ジへプチルアミン、ジへキシルアミン、ジオクチルアミン、ジ-2-エチルへキシルアミン、ジデシルアミン、エチルプロピルアミン、エチルブチルアミン、エチルベンジルアミン、メチルフェネチルアミン等が挙げられ、上記式(1)の条件を満たせば、これらの類似物を含む。
後述する変性共役ジエン系重合体組成物のヒステリシスロス低減や、後述する変性共役ジエン系重合体の不快臭の低減の観点から、ジブチルアミン、ジへキシルアミンが好ましい。より好ましくはジブチルアミンである。
R1及びR2基が、結合している場合に、前記式(1)で表される化合物としては、例えば、ピペリジン、ヘキサメチレンイミン、アザシクロオクタン、1,3,3-トリメチル-6-アザビシクロ[3.2.1]オクタン、1,2,3,6-テトラヒドロピリジン等が挙げられ、これらに限定されるものではなく、上記条件を満たせば、これらの類似物を含む。
後述する変性共役ジエン系重合体組成物のヒステリシスロス低減や、後述する変性共役ジエン系重合体の不快臭の低減の観点から、ピペリジン、ヘキサメチレンイミン、アザシクロオクタン、1,3,3-トリメチル-6-アザビシクロ[3.2.1]オクタンが好ましい。より好ましくはピペリジン、ヘキサメチレンイミンである。
この場合に前記式(2)で表される化合物としては、以下に限定されるものではないが、例えば、3-クロロ-ジメチルプロパン-1-アミン、3-クロロ-ジエチルプロパン-1-アミン、3-クロロ-ジブチルプロパン-1-アミン、3-クロロ-ジプロピルプロパン-1-アミン、3-クロロ-ジヘプチルプロパン-1-アミン、3-クロロ-ジヘキシルプロパン-1-アミン、3-クロロロプロピル-エチルヘキサン-1-アミン、3-クロロ-ジデシルプロパン-1-アミン、3-クロロ-エチルプロパン-1-アミン、3-クロロ-エチルブタン-1-アミン、3-クロロ-エチルプロパン-1-アミン、ベンジル-3-クロロ-エチルプロパン-1-アミン、3-クロロ-エチルフェネチルプロパン-1-アミン、3-クロロ-メチルフェネチルプロパン-1-アミン、1-(3-クロロプロピル)ピペリジン、1-(3-クロロプロピル)ヘキサメチレンイミン、1-(3-クロロプロピル)アザシクロオクタン、6-(3-クロロプロピル)-1,3,3-トリメチル-6-アザビシクロ[3.2.1]オクタン、1-(3-クロロプロピル)-1,2,3,6-テトラヒドロピリジン、1-(3-ブロモプロピル)ヘキサメチレンイミン、1-(3-ヨードプロピル)ヘキサメチレンイミン、1-(3-クロロブチル)ヘキサメチレンイミン、1-(3-クロロペンチル)ヘキサメチレンイミン、1-(3-クロロヘキシル)ヘキサメチレンイミン、1-(3-クロロデシル)ヘキサメチレンイミン等が挙げられ、上記条件を満たせば、これらの類似物を含む。
カーボンブラック、シリカ等の無機充填剤との反応性及び相互作用性の観点から、3-クロロ-ジブチルプロパン-1-アミン、1-(3-クロロプロピル)ヘキサメチレンイミンが好ましく、より好ましくは1-(3-クロロプロピル)ピペリジン、1-(3-クロロプロピル)ヘキサメチレンイミンである。
後述する変性共役ジエン系重合体組成物のヒステリシスロス低減の観点から、N,N-ジブチル-2-ブテニル1-アミン、1-(2-ブテニル)ヘキサメチレンイミンが好ましく、より好ましくは1-(2-ブテニル)ピペリジン、1-(2-ブテニル)ヘキサメチレンイミンである。
有機リチウム化合物としては、以下に限定されるものではないが、例えば、n-ブチルリチウム、sec-ブチルリチウム、tert-ブチルリチウム、n-プロピルリチウム、iso-プロピルリチウム等が挙げられる。
上述した分子内に少なくとも1つ窒素原子を有する化合物及び前記有機リチウム化合物が反応することにより得られる、分子内に少なくとも1つ窒素原子を有する有機リチウム化合物としては、アニオン重合可能なものであり、下記式(7)、(8)で表される化合物を用いることができる。
前記式(7)で表される化合物としては、以下に限定されるものではないが、例えば、ジメチルアミノリチウム、ジエチルアミノリチウム、ジブチルアミノリチウム、ジプロピルアミノリチウム、ジへプチルアミノリチウム、ジへキシルアミノリチウム、ジオクチルアミノリチウム、ジ-2-エチルへキシルアミノリチウム、ジデシルアミノリチウム、エチルプロピルアミノリチウム、エチルブチルアミノリチウム、エチルベンジルアミノリチウム、メチルフェネチルアミノリチウムが挙げられ、上記条件を満たせば、これらの類似物を含む。
溶媒への可溶性や、後述する変性共役ジエン系重合体組成物のヒステリシスロス低減の観点から、ジブチルアミノリチウム、ジへキシルアミノリチウムが好ましい。より好ましくはジブチルアミンである。
R1及びR2基が結合している場合に、前記式(7)で表される化合物としては、以下に限定されるものではないが、例えば、ピペリジノリチウム、ヘキサメチレンイミノリチウム、リチウムアザシクロオクタン、リチウム-1,3,3-トリメチル-6-アザビシクロ[3.2.1]オクタン、1,2,3,6-テトラヒドロピリジノリチウム等が挙げられ、上記条件を満たせば、これらの類似物を含む。
重合開始剤の溶媒への可溶性や、後述する変性共役ジエン系重合体の不快臭の低減の観点から、ピペリジノリチウム、ヘキサメチレンイミノリチウム、リチウムアザシクロオクタン、リチウム-1,3,3-トリメチル-6-アザビシクロ[3.2.1]オクタンが好ましい。より好ましくはピペリジノリチウム、ヘキサメチレンイミノリチウムである。
R3は炭素数1~20のアルキレン基、又は下記式(3)~(5)のいずれかで表される。
カーボン、シリカ等の無機充填剤との反応性及び相互作用性の観点から、(3-(ジブチルアミノ)-プロピル)リチウムがより好ましい。
重合開始剤としての反応性の観点から、4-(ジメチルアミノ)-2-ブテニル)リチウム、(4-(ジエチルアミノ)-2-ブテニル)リチウム、(4-(ジブチルアミノ)-2-ブテニル)リチウムが好ましく、より好ましくは(4-(ジブチルアミノ)-2-ブテニル)リチウムである。
R1及びR2基が結合している場合、式(8)で表される化合物としては、以下に限定されるものではないが、例えば、(3-(ピペリジニル)プロピル)リチウム、(3-(ヘキサメチンレンイミニル)プロピル)リチウム、(3-(ヘプタメチレンイミニル)プロピル)リチウム、(3-(オクタメチレンイミニル)プロピル)リチウム、(3-(1,3,3-トリメチル-6-アザビシクロ[3.2.1]オクタニル)プロピル)リチウム、(3-(1,2,3,6-テトラヒドロピリジニル)プロピル)リチウム、(2-(ヘキサメチンレンイミニル)エチル)リチウム、(4-(ヘキサメチンレンイミニル)ブチル)リチウム、(5-(ヘキサメチンレンイミニル)ペンチル)リチウム、(6-(ヘキサメチンレンイミニル)ヘキシル)リチウム、(10-(ヘキサメチンレンイミニル)デシル)リチウム、(4-(ピペリジニル)-2-ブテニル)リチウム、(4-(ヘキサメチンレンイミニル)-2-ブテニル)リチウム、(4-(ヘプタメチレンイミニル)-2-ブテニル)リチウム、(4-(オクタメチレンイミニル)-2-ブテニル)リチウム、(4-(1,3,3-トリメチル-6-アザビシクロ[3.2.1]オクタニル)-2-ブテニル)リチウム、(4-(1,2,3,6-テトラヒドロピリジニル)-2-ブテニル)リチウム、(4-(ヘキサメチンレンイミニル)-2-メチル-2-ブテニル)リチウム、(4-(ヘキサメチンレンイミニル)-3-メチル-2-ブテニル)リチウムが挙げられ、上記条件を満たせば、これらの類似物を含む。
式(7)又は(8)で表される、分子内に少なくとも1つ窒素原子を有する有機リチウム化合物は、上述した重合工程の前に予め調製しておいてもよく、調製方法は、従来公知の方法を適用できる。
R1及びR2は、結合して隣接した窒素原子とともに環状構造を形成していてもよく、その場合はR1及びR2は、合計で炭素数5~12の炭化水素基であって、不飽和結合を有していても、分岐構造を有していてもよい。
反応温度は0~80℃が好ましく、生産性の観点から10~70℃が好ましい。
X1、X2が、互いに異なるハロゲン原子であることにより、反応性に差をもたせることができ、当該反応性の差を利用して、先ず反応性が高い方のハロゲンとリチウムアミド化合物とを反応させ、次に、残った方のハロゲンと有機リチウム化合物とを反応させることにより、前記式(8)のような化合物が得られる。
R3aは、炭素数1~20のアルキレン基であり、好ましくは炭素数2~16のアルキレン基であり、より好ましくは炭素数3~10のアルキレン基である。
反応性や安全性の観点から、1-ブロモ-3-クロロプロパン、1-ブロモ-4-クロロブタン、1-ブロモ-5-クロロペンタン、1-ブロモ-6-クロロヘキサン、1-ブロモ-10-クロロデカンが好ましく、より好ましくは1-ブロモ-3-クロロプロパン、1-ブロモ-4-クロロブタン、1-ブロモ-6-クロロヘキサンである。
リチウムアミド化合物に前記式(9)で表される化合物を反応させる際の反応温度は好ましくは-78~70℃であり、より好ましくは-50~50℃である。その後得られた化合物に有機リチウム化合物を反応させる際の反応温度は、好ましくは-78~70℃であり、より好ましくは-50~50℃である。
(II) 炭化水素溶媒中、得られたリチウムアミド化合物とブタジエン、あるいはイソプレンを反応させる。
(III) アルコールを加えてリチウムを失活させ、得られた生成物を減圧蒸留する。
(IV) 蒸留して得られた生成物と有機リチウム化合物を炭化水素溶媒中で反応させる。
アルコールは、公知の材料を使用できるが、低分子量のものが好ましく、例えばメタノール、エタノール、イソプロパノール等が好ましく、より好ましくはエタノールである。
工程(IV)の反応温度は0~80℃が好ましく、より好ましくは10~70℃である。
極性化合物としては、3級モノアミン、3級ジアミン、鎖状又は環状エーテル等が挙げられる。
前記極性化合物は、1種のみを単独で用いてもよく、2種以上を組み合わせて用いてもよい。
反応促進や溶媒への可溶化の効果を十分に発現するためには30ppm以上の添加が好ましく、後の重合工程でのミクロ構造調整の自由度を確保することや重合後の溶媒を回収し、精製する工程における重合溶媒との分離を考慮すると50,000ppm以下で添加することが好ましい。
変性前の共役ジエン系重合体は、上述した式(1)又は(2)で表される分子内に少なくとも1つ窒素原子を有する化合物及び有機リチウム化合物を含む重合開始剤を用いて、共役ジエン化合物を重合し、又は共役ジエン化合物と芳香族ビニル化合物とを共重合することによって得られる。なお、上記重合開始剤には、窒素を有さない有機リチウム化合物を含んでいてもよい。
また、共役ジエン系重合体の重合は、回分式、又は1個の反応器若しくは2個以上の連結された反応器での連続式等の重合様式により行ってもよい。
共役ジエン化合物としては、重合可能な単量体であればよく、特に限定されず、例えば1,3-ブタジエン、イソプレン、2,3-ジメチル-1,3-ブタジエン、1,3-ペンタジエン、3-メチル-1,3-ペンタジエン、1,3-ヘプタジエン、1,3-ヘキサジエン等が挙げられる。
これらの中でも、工業的入手の容易さの観点から、1,3-ブタジエン、イソプレンが好ましい。これらは1種のみならず2種以上を併用してもよい。
芳香族ビニル化合物としては、共役ジエン化合物と共重合可能な単量体であればよく、特に限定されず、例えば、スチレン、p-メチルスチレン、α-メチルスチレン、ビニルエチルベンゼン、ビニルキシレン、ビニルナフタレン、ジフェニルエチレン等が挙げられる。
これらの中でも、工業的入手の容易さの観点から、スチレンが好ましい。これらは1種のみならず2種以上を併用してもよい。
変性前の共役ジエン系重合体の重合工程において、共役ジエン化合物、芳香族ビニル化合物と同時、もしくは重合途中に、多官能芳香族ビニル化合物を用いてもよい。これにより、分子鎖の分岐をコントロールし、コールドフローを防止することができる。
多官能芳香族ビニル化合物としては、ジビニルベンゼン等が挙げられる。
共役ジエン系重合体の重合反応は、溶媒中で行うことが好ましい。
溶媒としては、以下に限定されるものではないが、例えば、飽和炭化水素、芳香族炭化水素等の炭化水素系溶媒が挙げられる。具体的には、ブタン、ペンタン、ヘキサン、ヘプタン等の脂肪族炭化水素;シクロペンタン、シクロヘキサン、メチルシクロペンタン、メチルシクロヘキサン等の脂環族炭化水素;ベンゼン、トルエン、キシレン等の芳香族炭化水素及びそれらの混合物からなる炭化水素等が挙げられる。
上述した共役ジエン化合物、芳香族ビニル化合物、及び重合溶媒は、それぞれ単独で、あるいはこれらの混合液を、予め重合反応に供する前に、不純物であるアレン類やアセチレン類を、有機金属化合物を反応させ処理しておくこともできる。これにより、前記不純物による重合の阻害が防止でき、重合体の活性末端量が高濃度となり、よりシャープな分子量分布を達成でき、さらには高い変性率が達成される傾向にあるため好ましい。
共役ジエン系重合体の重合反応においては、極性化合物を添加してもよい。
芳香族ビニル化合物を共役ジエン化合物とランダムに共重合させることができ、共役ジエン部のミクロ構造を制御するためのビニル化剤としても用いることができる。また、重合速度の改善等にも効果がある。
これらの極性化合物は、それぞれ単独で用いてもよく2種以上を組み合わせて用いてもよい。
このような極性化合物(ビニル化剤)は、重合体共役ジエン部分のミクロ構造の調節剤として、所望のビニル結合量に応じて、適量用いることができる。多くの極性化合物は、同時に共役ジエン化合物と芳香族ビニル化合物との共重合において有効なランダム化効果を有し、芳香族ビニル化合物の分布の調整やスチレンブロック量の調整剤として用いることができる。共役ジエン化合物と芳香族ビニル化合物とをランダム化する方法としては、例えば特開昭59-140211号公報に記載されているような、共重合の途中に1,3-ブタジエンの一部を断続的に添加する方法を用いてもよい。
重合温度はリビングアニオン重合が進行する温度であれば、特に限定されないが、生産性の観点から、0℃以上であることが好ましく、重合終了後の活性末端に対する変性剤の反応量を充分に確保する観点から、120℃以下であることが好ましい。
本実施形態において、共役ジエン系重合体は、上述した式(7)又は(8)で表される分子内に少なくとも1つ窒素原子を有する有機リチウム化合物を重合開始剤とし、アニオン重合反応により成長して得られることが好ましい。特に、共役ジエン系重合体は、リビングアニオン重合による成長反応によって得られる活性末端を有する重合体であることがより好ましい。これにより、高変性率の変性共役ジエン系重合体を得ることができる。
上述した重合工程により得られる共役ジエン系重合体を、不活性溶剤中で更に水素化することによって、二重結合の全部又は一部を飽和炭化水素に変換することができる。その場合、耐熱性、耐候性が向上し、高温で加工する場合の製品の劣化を防止することができる。その結果、自動車用途等種々の用途で一層優れた性能を発揮する。
より具体的には、共役ジエン化合物に基づく不飽和二重結合の水素化率(すなわち「水添率」)は、目的に応じて任意に選択でき、特に限定されない。
加硫ゴムとして用いる場合には、共役ジエン部の二重結合が部分的に残存していることが好ましい。かかる観点から、重合体中の共役ジエン部の水添率は3~70%であることが好ましく、5~65%であることがより好ましく、10~60%であることがさらに好ましい。
特に好適な水素化の方法としては、触媒の存在下、重合体溶液に気体状水素を吹き込む方法で水素化する方法が挙げられる。
触媒としては、貴金属を多孔質無機物質に担持させた触媒等の不均一系触媒;ニッケル、コバルト等の塩を可溶化し有機アルミニウム等と反応させた触媒、チタノセン等のメタロセンを用いた触媒等の均一系触媒等が挙げられる。これら中でも、特にマイルドな水素化条件を選択できる観点から、チタノセン触媒が好ましい。また、芳香族基の水素化は、貴金属の担持触媒を用いることによって行うことができる。
水素化触媒の具体例としては、(1)Ni,Pt,Pd,Ru等の金属をカーボン、シリカ、アルミナ、ケイソウ土等に担持させた担持型不均一系水添触媒、(2)Ni,Co,Fe,Cr等の有機酸塩又はアセチルアセトン塩等の遷移金属塩と有機アルミニウム等の還元剤とを用いる、いわゆるチーグラー型水添触媒、(3)Ti,Ru,Rh,Zr等の有機金属化合物等のいわゆる有機金属錯体等が挙げられる。例えば水素化触媒として特公昭42-8704号公報、特公昭43-6636号公報、特公昭63-4841号公報、特公平1-37970号公報、特公平1-53851号公報、特公平2-9041号公報、特開平8-109219号公報に記載された水素化触媒を使用することができる。好ましい水素化触媒としてはチタノセン化合物と還元性有機金属化合物との反応混合物が挙げられる。
[結合共役ジエン量]
重合工程により得られる共役ジエン系重合体中の結合共役ジエン量は、特に限定されないが、50~100質量%であることが好ましく、60~80質量%であることがより好ましい。
また、重合工程により得られる共役ジエン系重合体中の結合芳香族ビニル量は、特に限定されないが、0~50質量%であることが好ましく、20~40質量%であることがより好ましい。
結合共役ジエン量及び結合芳香族ビニル量が上記範囲であると、低ヒステリシスロス性とウェットスキッド抵抗性のバランスが更に優れ、耐摩耗性や破壊強度も満足する加硫物を得ることができる。
ここで、結合芳香族ビニル量は、フェニル基の紫外吸光によって測定でき、ここから結合共役ジエン量も求めることができる。具体的には、後述する実施例に従った方法により測定することができる。
また、共役ジエン結合単位中のビニル結合量は、特に限定されないが、10~75モル%であることが好ましく、25~65モル%であることがより好ましい。
ビニル結合量が上記範囲であると、低ヒステリシスロス性とウェットスキッド抵抗性のバランスが更に優れ、耐摩耗性や破壊強度も満足する加硫物を得ることができる。
ここで、変性共役ジエン系重合体がブタジエンとスチレンの共重合体である場合には、ハンプトンの方法(R.R.Hampton,Analytical Chemistry,21,923(1949))により、ブタジエン結合単位中のビニル結合量(1,2-結合量)を求めることができる。
共役ジエン系重合体は、ランダム共重合体であってもブロック共重合体であってもよい。 ランダム共重合体としては、例えば、ブタジエン-イソプレンランダム共重合体、ブタジエン-スチレンランダム共重合体、イソプレン-スチレンランダム共重合体、ブタジエン-イソプレン-スチレンランダム共重合体等が挙げられる。
共重合体鎖中の各単量体の組成分布としては、特に限定されず、例えば統計的ランダムな組成に近い完全ランダム共重合体、組成がテーパー状に分布しているテーパー(勾配)ランダム共重合体等が挙げられる。共役ジエンの結合様式、すなわち1,4-結合や1,2-結合等の組成は、均一であってもよいし、分布があってもよい。
ミクロ構造(上記変性共役ジエン系共重合体中の各結合量)が上記範囲にあり、さらに共重合体のガラス転移温度が-45℃~-15℃の範囲にあるときに、低ヒステリシスロス性とウェットスキッド抵抗性とのバランスにより一層優れた加硫物を得ることができる。ガラス転移温度については、ISO22768:2006に従い、所定の温度範囲で昇温しながらDSC曲線を記録し、DSC微分曲線のピークトップ(Inflection point)をガラス転移温度とする。
本実施形態の共役ジエン系重合体が共役ジエン-芳香族ビニル共重合体である場合、芳香族ビニル単位が30以上連鎖しているブロックの数が少ないか又は無いものであることが好ましい。具体的には、共重合体がブタジエン-スチレン共重合体の場合、Kolthoffの方法(I.M.KOLTHOFF,et al.,J.Polym.Sci.1,429(1946)に記載の方法)により重合体を分解し、メタノールに不溶なポリスチレン量を分析する公知の方法において、芳香族ビニル単位が30以上連鎖しているブロックが、重合体の総量に対して好ましくは5質量%以下、より好ましくは3質量%以下である。
変性工程においては、上述した重合工程により得られる共役ジエン系重合体の活性末端に、下記式(6)で表される化合物(変性剤)を反応させ、変性共役ジエン系重合体を得る。
これらの中でも、変性剤の官能基とシリカ等の無機充填剤との反応性及び相互作用性の観点や、加工性の観点から、mが2、nが3であるものが好ましい。具体的には、2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタン、2,2-ジエトキシ-1-(3-トリエトキシシリルプロピル)-1-アザ-2-シラシクロペンタンが好ましい。
変性共役ジエン系重合体において十分な変性率を得る観点から0.6倍以上とすることが好ましく、加工性改良のために重合体末端同士をカップリングさせ分岐状重合体成分を得ることが好ましいことに加え、変性剤コストの観点から3倍以下とすることが好ましい。
失活剤としては、特に限定されず、例えば、水、メタノール、エタノール、イソプロパノール等のアルコール等が挙げられる。
中和剤としては、特に限定されず、例えば、ステアリン酸、オレイン酸、バーサチック酸等のカルボン酸;無機酸の水溶液、炭酸ガス等が挙げられる。
本実施形態の変性共役ジエン系重合体を、重合体溶液から取得する方法としては、公知の方法を用いることができる。
例えば、スチームストリッピング等で溶媒を分離した後、変性共役ジエン系重合体を濾別し、さらにそれを脱水及び乾燥して変性共役ジエン系重合体を取得する方法、フラッシングタンクで濃縮し、さらにベント押し出し機等で脱揮する方法、ドラムドライヤー等で直接脱揮する方法等が挙げられる。
(構造)
上述した変性工程では、重合工程により得られた共役ジエン系共重合体の活性末端と、上記式(6)で表される変性剤とが反応することによって、変性共役ジエン系重合体が得られればよく、その作用については以下のように推測される。
例えば、変性剤として、2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタン等の環状構造を有するアザシラン化合物を用いた場合、共役ジエン系重合体の活性末端が、変性剤のアルコキシシリル基又はSi-N結合部分と反応することで、共役ジエン系重合体末端とSiとの結合が形成される(下記式(10)参照)。
例えば、変性剤1モルに対して4モルの共役ジエン系重合体活性末端が反応する場合、下記式(10)で示されるような4個の分子鎖がカップリングした形態の変性共役ジエン系重合体が得られる。
さらにアルコールや水等との反応により、第2級アミノ基が形成される。
かかる第2級アミノ基とアルコキシシリル基を有する変性共役ジエン系重合体を用いることで、加硫物としたときの低ヒステリシスロス性とウェットスキッド抵抗性のバランス性に優れ、かつ実用上十分な耐摩耗性や破壊強度を付与できるとともに、かつ優れた加工性も発現させることができるものと考えられる。
なお、本実施形態の作用は、上述した例に限定されない。
また、上述した変性工程において得られる変性共役ジエン系重合体が、1個の第2級アミノ基及び少なくとも1個のアルコキシシリル基を有しているとき、当該変性共役ジエン系重合体を用いることにより、加硫物としたときの低ヒステリシスロス性とウェットスキッド抵抗性のバランス性に優れ、かつ実用上十分な耐摩耗性や破壊強度を付与できるとともに、かつ優れた加工性も発現させることができる。
さらに、上述した変性工程において得られる変性共役ジエン系重合体が、1~6分岐の構造を有しているとき、当該変性共役ジエン系重合体及び当該重合体組成物は加工性が優れ、かかる観点から、1~4分岐の構造を有していることがより好ましい。
変性工程においては、加硫物としたときに、低ヒステリシスロス性とウェットスキッド抵抗性のバランスに優れ、実用上十分な耐摩耗性や破壊強度を有するものにする観点から、官能基成分を有する重合体(少なくとも片方の末端を変性した重合体)の割合(変性率)は、好ましくは50質量%以上、より好ましくは80質量%以上、さらに好ましくは90質量%以上、さらにより好ましくは95質量%含有する重合体となるように、変性共役ジエン系重合体を製造することが好ましい。
本実施形態の変性共役ジエン系重合体の製造方法により得られる変性共役ジエン系重合体における変性率とは、シリカ粒子充填カラムを用いたゲル浸透クロマトグラフィー(GPC)測定のカラムへの吸着量によって求められる、すなわち官能基成分を有する重合体の割合のことである。変性率を測定するタイミングは、変性工程後に活性末端を失活させた後である。
官能基成分を有する重合体の定量方法としては、官能基含有の変性成分と非変性成分を分離できるクロマトグラフィーによって測定する方法が適用できる。このクロマトグラフィーを用いた方法としては、官能基成分を吸着するシリカ等の極性物質を充填剤としたGPCカラムを使用し、非吸着成分の内部標準を比較に用いて定量する方法が挙げられる。
本実施形態の変性共役ジエン系重合体の分子量は、(重量平均分子量:ポリスチレン換算)は、加工性や後述する変性共役ジエン系重合体組成物の引張特性等の性能の観点から、3万から200万が好ましい。より好ましくは5万~150万である。
また分子量分布(重量平均分子量/数平均分子量)は、加工性や後述する変性共役ジエン系重合体組成物のヒステリシスロス低減の観点から、1.0~3.0が好ましく、より好ましくは1.1~2.0である。
重量平均分子量は、例えば、ポリスチレン系ゲルを充填剤としたカラム3本を連結して用いたGPCを使用してクロマトグラムを測定し、標準ポリスチレンを使用した検量線により分子量を計算して求めることができる。
具体的には、溶離液にテトラヒドロフラン(THF)を使用し、カラムとして、ガードカラム:東ソー TSKguardcolumn HHR-H、カラム:東ソー TSKgel G6000HHR、TSKgel G5000HHR、TSKgel G4000HHRを使用し、オーブン温度40℃、THF流量1.0mL/分の条件で東ソー製 HLC8020(検出器:RI)を用いて測定を行うことができる。
試料は20mLのTHFに対して分子量分布の狭い重合体(1以上1.8未満)の場合には10mgを、広い重合体(1.8以上)の場合には20mgを溶解し、20μL注入して測定するのが好適である。
<ゴム用安定剤>
また、本実施形態の変性共役ジエン系重合体は、重合後のゲル生成を防止する観点や、加工時の安定性を向上させる観点から、ゴム用安定剤を添加することが好ましい。
ゴム用安定剤は、特に限定されず、公知のものを用いることができるが、例えば、2,6-ジ-tert-ブチル-4-ヒドロキシトルエン(BHT)、n-オクタデシル-3-(4’-ヒドロキシ-3’,5’-ジ-tert-ブチルフェノール)プロピネート、2-メチル-4,6-ビス[(オクチルチオ)メチル]フェノール等の酸化防止剤が好ましい。
また、本実施形態の変性共役ジエン系重合体の加工性を更に改善するために、必要に応じて伸展油を変性共役ジエン系共重合体に添加することができる。
伸展油を変性共役ジエン系重合体に添加する方法としては、特に限定されないが、伸展油を重合体溶液に加え、混合して、油展共重合体溶液としたものを脱溶媒する方法が好ましい。
伸展油としては、以下に限定されるものではないが、例えば、アロマ油、ナフテン油、パラフィン油等が挙げられる。これらの中でも、環境安全上の観点や、オイルブリード防止及びウェットグリップ特性の観点から、IP346法による多環芳香族(PCA)成分が3質量%以下であるアロマ代替油が好ましい。
アロマ代替油としては、Kautschuk Gummi Kunststoffe 52(12)799(1999)に示されるTDAE(Treated Distillate Aromatic Extracts)、MES(Mild Extraction Solvate)等の他、RAE(Residual Aromatic Extracts)等が挙げられる。
伸展油の添加量は、特に限定されないが、通常は、変性共役ジエン系重合体100質量部に対し、10~60質量部であり、20~37.5質量部が好ましい。
本実施形態の変性共役ジエン系重合体組成物は、上述した本実施形態の変性共役ジエン系重合体20質量部以上含有するゴム成分100質量部と、シリカ系無機充填剤0.5~300質量部とを含有する。
前記ゴム成分としては、本実施形態の変性共役ジエン系重合体以外のゴム状重合体を、本実施形態の変性共役ジエン系重合体と組み合わせて使用できる。
本実施形態の変性共役ジエン系重合体以外のゴム状重合体としては、特に限定されず、例えば、共役ジエン系重合体又はその水素添加物、共役ジエン系化合物とビニル芳香族化合物とのランダム共重合体又はその水素添加物、共役ジエン系化合物とビニル芳香族化合物とのブロック共重合体又はその水素添加物、非ジエン系重合体、天然ゴム等が挙げられる。
具体的には、ブタジエンゴム又はその水素添加物、イソプレンゴム又はその水素添加物、スチレン-ブタジエンゴム又はその水素添加物、スチレン-ブタジエンブロック共重合体又はその水素添加物、スチレン-イソプレンブロック共重合体又はその水素添加物等のスチレン系エラストマー、アクリロニトリル-ブタジエンゴム又はその水素添加物等が挙げられる。
また、非ジエン系重合体としては、エチレン-プロピレンゴム、エチレン-プロピレン-ジエンゴム、エチレン-ブテン-ジエンゴム、エチレン-ブテンゴム、エチレン-ヘキセンゴム、エチレン-オクテンゴム等のオレフィン系エラストマー、ブチルゴム、臭素化ブチルゴム、アクリルゴム、フッ素ゴム、シリコーンゴム、塩素化ポリエチレンゴム、エピクロルヒドリンゴム、α、β-不飽和ニトリル-アクリル酸エステル-共役ジエン共重合ゴム、ウレタンゴム、多硫化ゴム等が挙げられる。
上述した各種ゴム状重合体は、水酸基やアミノ基等の極性を有する官能基を付与した変性ゴムであってもよい。またその重量平均分子量は、性能と加工特性のバランスの観点から、2,000~2,000,000であることが好ましく、5,000~1,500,000であることがより好ましい。また、低分子量のいわゆる液状ゴムを用いることもできる。これらのゴム状重合体は、単独で用いてもよく2種以上を組み合わせて用いてもよい。
本実施形態の変性共役ジエン系重合体に、シリカ系無機充填剤を分散させることで、加硫物としたときに、低ヒステリシスロス性とウェットスキッド抵抗性とのバランスに優れ、かつ実用上十分な耐摩耗性や破壊強度を有し、優れた加工性を付与できる。
ここで、主成分とは、シリカ系無機充填剤中に50質量%以上、好ましくは70質量%以上、より好ましくは80質量%以上含有される成分をいう。
また、表面を疎水化したシリカ系無機充填剤や、シリカ系無機充填剤とシリカ系以外の無機充填剤との混合物も用いることができる。
これらの中でも、強度や耐摩耗性等の観点から、シリカ及びガラス繊維が好ましく、シリカがより好ましい。
シリカとしては、乾式シリカ、湿式シリカ、合成ケイ酸塩シリカ等が挙げられる。これらの中でも、破壊特性の改良効果及びウェットスキッド抵抗性のバランスに優れる観点から、湿式シリカが好ましく、変性共役ジエン系重合体組成物において、実用上良好な耐摩耗性や破壊特性を得る観点から、シリカ系無機充填剤のBET吸着法で求められる窒素吸着比表面積は、100~300m2/gであることが好ましく、170~250m2/gであることがより好ましい。
また必要に応じて、比較的比表面積が小さい(例えば比表面積が200m2/g以下の)シリカ系無機充填剤と、比較的比表面積の大きい(例えば200m2/g以上の)シリカ系無機充填剤と、を組み合わせて用いることができる。これにより、良好な耐摩耗性や破壊特性と低ヒステリシスロス性を高度にバランスさせることができる。
シリカ系無機充填剤の含有量は、無機充填剤の添加効果が発現する観点から、0.5質量部以上とし、一方、無機充填剤を十分に分散させ、組成物の加工性や機械強度を実用的に十分なものとする観点から、300質量部以下とする。
本実施形態の変性共役ジエン系重合体組成物には、カーボンブラックを含有させてもよい。
カーボンブラックとしては、特に限定されず、例えば、SRF、FEF、HAF、ISAF、SAF等の各クラスのカーボンブラックが使用できる。これらの中でも、窒素吸着比表面積が50m2/g以上、ジブチルフタレート(DBP)吸油量が80mL/100gのカーボンブラックが好ましい。
本実施形態の変性共役ジエン系重合体組成物には、上述したシリカ系無機充填剤やカーボンブラック以外に、金属酸化物や金属水酸化物を含有させてもよい。
金属酸化物とは、化学式MxOy(Mは金属原子を表し、x及びyは各々1~6の整数を表す。)を構成単位の主成分とする固体粒子のことをいい、特に限定されるものではないが、例えば、アルミナ、酸化チタン、酸化マグネシウム、酸化亜鉛等を用いることができる。また金属酸化物と金属酸化物以外の無機充填剤の混合物も用いることができる。
金属水酸化物としては、特に限定されるものではないが、例えば、水酸化アルミニウム、水酸化マグネシウム、水酸化ジルコニウム等が挙げられる。
本実施形態の変性共役ジエン系重合体組成物には、シランカップリング剤を含有させてもよい。
シランカップリング剤は、ゴム成分とシリカ系無機充填剤との相互作用を緊密にする機能を有しており、ゴム成分及びシリカ系無機充填剤のそれぞれに対する親和性又は結合性の基を有しており、一般的には、硫黄結合部分とアルコキシシリル基、シラノール基部分を一分子中に有する化合物が用いられる。具体的には、ビス-[3-(トリエトキシシリル)-プロピル]-テトラスルフィド、ビス-[3-(トリエトキシシリル)-プロピル]-ジスルフィド、ビス-[2-(トリエトキシシリル)-エチル]-テトラスルフィド等が挙げられる。
本実施形態の変性共役ジエン系重合体組成物には、加工性の改良を図るために、ゴム用軟化剤を含有させてもよい。
ゴム用軟化剤としては、鉱物油、又は液状若しくは低分子量の合成軟化剤が好適である。
鉱物油系ゴム用軟化剤は、ゴムの軟化、増容、加工性の向上を図るために使用されているプロセスオイル又はエクステンダーオイルと呼ばれるオイルを含み、これらのうち、芳香族環、ナフテン環、及びパラフィン鎖の混合物であり、パラフィン鎖の炭素数が全炭素中50%以上を占めるものがパラフィン系と呼ばれ、ナフテン環炭素数が30~45%のものがナフテン系、芳香族炭素数が30%を超えるものがアロマ系と呼ばれている。
本実施形態の変性共役ジエン系重合体組成物に用いられるゴム用軟化剤としては、環境安全上の観点や、オイルブリード防止、及びウェットグリップ特性の観点から、IP346法による多環芳香族(PCA)成分が3質量%以下であるアロマ代替油が好ましい。
本実施形態の変性共役ジエン系重合体組成物には、本実施形態の目的を損なわない範囲内で、上述した以外のその他の軟化剤や充填剤、さらに、耐熱安定剤、帯電防止剤、耐候安定剤、老化防止剤、着色剤、滑剤等の各種添加剤を用いてもよい。その他の軟化剤としては、公知の軟化剤を用いることができる。
その他の充填剤としては、具体的には、炭酸カルシウム、炭酸マグネシウム、硫酸アルミニウム、硫酸バリウム等が挙げられる。
上記の耐熱安定剤、帯電防止剤、耐候安定剤、老化防止剤、着色剤、潤滑剤としては、それぞれ公知の材料を用いることができる。
本実施形態の変性共役ジエン系重合体組成物の製造方法については、特に限定されるものではない。例えば、上述したゴム成分と、シリカ系無機充填材、その他必要に応じて上述した各種材料を、例えば、オープンロール、バンバリーミキサー、ニーダー、単軸スクリュー押出機、2軸スクリュー押出機、多軸スクリュー押出機等の一般的な混和機を用いた溶融混練する方法、各成分を溶解混合後、溶剤を加熱除去する方法等が挙げられる。
これらのうち、ロール、バンバリーミキサー、ニーダー、押出機による溶融混練法が生産性、良混練性の観点から好ましい。
また、変性共役ジエン系重合体と各種材料とを一度に混練する方法、複数の回数に分けて混合する方法のいずれも適用可能である。
本実施形態の変性共役ジエン系重合体組成物は、加硫物として好適に用いられる。
加硫物は、変性共役ジエン系重合体を、シリカ系無機充填剤や、必要に応じてカーボンブラック等の無機充填剤、変性共役ジエン系重合体以外のゴム状重合体、シランカップリング剤、ゴム用軟化剤、加硫剤、加硫促進剤・助剤等と混合し、加熱して加硫することにより得ることができる。
加硫剤としては、例えば、有機過酸化物及びアゾ化合物等のラジカル発生剤、オキシム化合物、ニトロソ化合物、ポリアミン化合物、硫黄、硫黄化合物が使用できる。硫黄化合物には、一塩化硫黄、二塩化硫黄、ジスルフィド化合物、高分子多硫化合物等が含まれる。
加硫剤の含有量は、通常は、本実施形態の変性共役ジエン系重合体を含むゴム成分100質量部に対して0.01~20質量部であり、0.1~15質量部が好ましい。加硫方法としては、従来公知の方法を適用でき、加硫温度は、通常120~200℃、であり、好ましくは140~180℃である。
加硫促進剤としては、従来公知の材料を用いることができ、例えば、スルフェンアミド系、グアニジン系、チウラム系、アルデヒド-アミン系、アルデヒド-アンモニア系、チアゾール系、チオ尿素系、ジチオカルバメート系等の加硫促進剤が挙げられる。
加硫促進剤の含有量は、通常、本実施形態の変性共役ジエン系重合体を含有するゴム成分100質量部に対して0.01~20質量部であり、0.1~15質量部が好ましい。
また、加硫助剤としては、亜鉛華、ステアリン酸等を使用できる。
上述した変性共役ジエン系重合体組成物は、加硫剤、各種配合剤等を加えて架橋し、ゴム組成物として所望のゴム製品の製造に用いることができる。
上述した変性共役ジエン系重合体組成物を架橋処理したゴム組成物は、タイヤ、防振ゴム、各種工業用品に用いることができる。
後述する実施例及び比較例で得られた変性共役ジエン系重合体の試料100mgをクロロホルムで100mLにメスアップし、溶解して測定サンプルとした。
島津製作所製:UV-2450を用い、スチレンのフェニル基によるUV254nmの吸収により結合スチレン量(質量%)を測定した。
後述する実施例及び比較例で得られた変性共役ジエン系重合体の試料50mgを10mLの二硫化炭素に溶解して測定サンプルとした。
溶液セルを用いて、測定装置として、日本分光(株)製:FT-IR230を用い、赤外線スペクトルを600~1000cm-1の範囲で測定して、所定の波数における吸光度によりハンプトンの方法の計算式に従いブタジエン部分のミクロ構造(1,2-ビニル結合量(mol%))を求めた。
後述する実施例及び比較例で得られた変性共役ジエン系重合体のムーニー粘度を下記のようにして測定した。
ムーニー粘度計(上島製作所社製、「VR1132」)を用い、JIS K6300(ISO289-1)に準拠し、ムーニー粘度を測定した。測定温度は100℃とした。まず、試料を1分間予熱した後、2rpmでローターを回転させ、4分後のトルクを測定してムーニー粘度(ML1+4)とした。
後述する実施例及び比較例で得られた変性共役ジエン系重合体の変性率を、シリカ系ゲルを充填剤としたGPCカラムに変性した成分が吸着する特性を応用することにより測定した。
ここで変性率とは、少なくとも片方の末端が変性された重合体の割合である。
後述する実施例及び比較例で得られた変性共役ジエン系重合体の試料及び低分子量内部標準ポリスチレンを含む試料溶液を、ポリスチレン系ゲルカラムで測定したクロマトグラムと、シリカ系カラムで測定したクロマトグラムとの差分よりシリカカラムへの吸着量を測定し、変性率を求めた。
試料10mg及び標準ポリスチレン5mgを20mLのテトラヒドロフラン(THF)に溶解させた。
THFを溶離液として用い、試料200μLを装置に注入して測定した。カラムは、ガードカラム:東ソー TSKguardcolumn HHR-H、カラム:東ソー TSKgel G6000HHR、TSKgel G5000HHR、TSKgel G4000HHRを使用した。カラムオーブン温度40℃、THF流量1.0mL/分の条件で、東ソー製 HLC8020のRI検出器を用いて測定しクロマトグラムを得た。
THFを溶離液として用い、試料200μLを装置に注入して測定した。カラムは、デュポン社製:Zorbaxを使用した。カラムオーブン温度40℃、THF流量0.5mL/分の条件で、東ソー製 HLC8020のRI検出器を用いて測定しクロマトグラムを得た。
ポリスチレン系カラムを用いたクロマトグラムのピーク面積の全体を100として、試料のピーク面積をP1、標準ポリスチレンのピーク面積をP2、シリカ系カラムを用いたクロマトグラムのピーク面積の全体を100として、試料の面積をP3、標準ポリスチレンのピーク面積をP4として、下記式より変性率(%)を求めた。
変性率(%)=[1-(P2×P3)/(P1×P4)]×100
(なお、P1+P2=P3+P4=100)
内容積10Lで、撹拌機及びジャケットを具備する温度制御が可能なオートクレーブを反応器として使用し、予め不純物を除去した、1,3-ブタジエン762g、スチレン268g、シクロヘキサン4710g、極性物質として2,2-ビス(2-オキソラニル)プロパン1.3gを反応器へ入れ、反応器内温を42℃に保持した。
重合開始剤として、ジブチルアミン(13.0mmol)とn-ブチルリチウム(13.0mmol)を、予めトラヒドロフラン(26.0mmol)の存在下で反応させた、ジブチルアミノリチウム13.0mmolのシクロヘキサン溶液を反応器に供給した。
重合反応開始後、重合による発熱で反応器内の温度は上昇を始め、最終的な反応器内の温度は80℃に達した。
反応温度のピーク到達2分後、反応器に2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを3.25mmol添加し、5分間変性反応を実施した。
内容積10Lで、撹拌機及びジャケットを具備する温度制御が可能なオートクレーブを反応器として使用し、予め不純物を除去した、1,3-ブタジエン762g、スチレン268g、シクロヘキサン4710g、極性物質として2,2-ビス(2-オキソラニル)プロパン1.45gを反応器へ入れ、反応器内温を42℃に保持した。
重合開始剤として、ヘキサメチレンイミン(13.0mmol)とn-ブチルリチウム(13.0mmol)をあらかじめ反応させた、ヘキサメチレンイミノリチウム13.0mmolのシクロヘキサン溶液を反応器に供給した。
重合反応開始後、重合による発熱で反応器内の温度は上昇を始め、最終的な反応器内の温度は78℃に達した。反応温度のピーク到達2分後、反応器に2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを3.25mmol添加し、5分間変性反応を実施した。
ジブチルアミン(13.3mmol)とテトラヒドロフラン(26.6mmol)とヘキサンの混合物中に、室温でn-ブチルリチウム(13.3mmol)を加え、ジブチルアミノリチウムを調製した。このリチウムアミドのヘキサン溶液を-25℃まで冷却し、1-クロロ-3-ブロモプロパン(13.3mmol)を加えた。撹拌しながら1時間かけて0℃まで昇温し、再び-25℃まで冷却した後、t-ブチルリチウム(26.6mmol)のペンタン溶液を加え、(3-(ジブチルアミノ)-プロピル)リチウムの混合物を得た。そのまま撹拌して室温にし、一晩撹拌した。
この混合物を用いて、変性共役ジエン系重合体(試料C)の重合を行った。
重合開始剤として(3-(ジブチルアミノ)-プロピル)リチウム13.3mmolのヘキサン溶液を反応器に供給した。重合反応開始後、重合による発熱で反応器内の温度は上昇を始め、最終的な反応器内の温度は83℃に達した。反応温度のピーク到達2分後、反応器に2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを3.33mmol添加し、5分間変性反応を実施した。
ヘキサメチレンイミン(13.2mmol)とテトラヒドロフラン(26.4mmol)とヘキサンの混合物中に、室温でn-ブチルリチウム(13.2mmol)を加え、ヘキサメチレンイミノリチウムを調製した。このリチウムアミドのヘキサン溶液を-25℃まで冷却し、1-クロロ-3-ブロモプロパン(13.2mmol)を加えた。撹拌しながら1時間かけて0℃まで昇温し、再び-25℃まで冷却した後、t-ブチルリチウム(26.4mmol)のペンタン溶液を加え、(3-(ヘキサメチレンイミニル)プロピル)リチウムの混合物を得た。そのまま撹拌して室温にし、一晩撹拌した。
この混合物を用いて、変性共役ジエン系重合体(試料D)の重合を行った。
ジブチルアミン(0.5mol)とシクロヘキサンとn-ブチルリチウム(0.25mol)から成る混合物を密封容器内で4時間、室温で撹拌した。次に、この混合物に1,3-ブタジエン(0.34mol)を加え、50℃で一晩撹拌した。このボトルの内容物を10mLのエタノールで処理した後、蒸留を行うことによってそれの濃縮を行った。133Paで真空蒸留を行った時の最後の2つの溜分、すなわち125~145℃および135~155℃の成分を集めた。
重合開始剤として(4-(ジブチルアミノ)-2-ブテニル)リチウム13.4mmolのシクロヘキサン溶液を反応器に供給した。重合反応開始後、重合による発熱で反応器内の温度は上昇を始め、最終的な反応器内の温度は84℃に達した。反応温度のピーク到達2分後、反応器に2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを3.35mmol添加し、5分間変性反応を実施した。
ヘキサメチレンイミン(0.5mol)とシクロヘキサンとn-ブチルリチウム(0.25mol)から成る混合物を密封容器内で4時間、室温で撹拌した。次に、この混合物に1,3-ブタジエン(0.34mol)を加え、50℃で一晩撹拌した。このボトルの内容物を10mLのエタノールで処理した後、蒸留を行うことによってそれの濃縮を行った。133Paで真空蒸留を行った時の最後の2つの留分、すなわち110~130℃及び120~140℃の成分を集めた。
重合開始剤として(4-(ヘキサメチンレンイミニル)-2-ブテニル)リチウム13.3mmolのシクロヘキサン溶液を反応器に供給した。重合反応開始後、重合による発熱で反応器内の温度は上昇を始め、最終的な反応器内の温度は85℃に達した。反応温度のピーク到達2分後、反応器に2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを3.33mmol添加し、5分間変性反応を実施した。
内容積10Lで、撹拌機及びジャケットを具備する温度制御が可能なオートクレーブを反応器として使用し、予め不純物を除去した、1,3-ブタジエン762g、スチレン268g、シクロヘキサン4710g、極性物質として2,2-ビス(2-オキソラニル)プロパン1.30gを反応器へ入れ、反応器内温を42℃に保持した。
重合開始剤として、ピペリジン(13.0mmol)とn-ブチルリチウム(13.0mmol)をテトラヒドロフラン(26.0mmol)の存在下であらかじめ反応させた、ピペリジノリチウム13.0mmolのシクロヘキサン溶液を反応器に供給した。
重合反応開始後、重合による発熱で反応器内の温度は上昇を始め、最終的な反応器内の温度は79℃に達した。反応温度のピーク到達2分後、反応器に2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを3.25mmol添加し、5分間変性反応を実施した。
内容積10Lで、撹拌機及びジャケットを具備する温度制御が可能なオートクレーブを反応器として使用し、予め不純物を除去した、1,3-ブタジエン762g、スチレン268g、シクロヘキサン4710g、極性物質として2,2-ビス(2-オキソラニル)プロパン1.30gを反応器へ入れ、反応器内温を42℃に保持した。
重合開始剤として、1,2,3,6-テトラヒドロピリジン(13.0mmol)と、n-ブチルリチウム(13.0mmol)をテトラヒドロフラン(26.0mmol)の存在下であらかじめ反応させた、1,2,3,6-テトラヒドロピペリジノリチウム13.0mmolのシクロヘキサン溶液を反応器に供給した。
重合反応開始後、重合による発熱で反応器内の温度は上昇を始め、最終的な反応器内の温度は79℃に達した。反応温度のピーク到達2分後、反応器に2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを3.25mmol添加し、5分間変性反応を実施した。
2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを2-メトキシ-2-メチル-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンに変え、添加量を変えた以外は実施例2と同様にして、試料Iを作成した。
試料Iを分析した結果、結合スチレン量は26質量%、結合ブタジエン量は74質量%であった。100℃でのムーニー粘度は57であった。赤外分光光度計を用いた測定結果よりハンプトン法に準じて計算して求めたブタジエン部分のミクロ構造のビニル結合量(1,2-結合量)は56%であった。また、変性率は99%であった。試料Iの分析結果を表1に示した。
内容積10Lで、撹拌機及びジャケットを具備する温度制御が可能なオートクレーブを反応器として使用し、予め不純物を除去した、1,3-ブタジエン762g、スチレン268g、シクロヘキサン4710g、ヘキサメチレンイミン(HMI、13.0mol)、極性物質として2,2-ビス(2-オキソラニル)プロパン1.45gを反応器へ入れ、反応器内温を42℃に保持した。
重合開始剤として、n-ブチルリチウム(13.0mmol)を前記反応器に供給した。
前記n-ブチルリチウムは、前記ヘキサメチレンイミンと反応し、反応器中でヘキサメチレンイミノリチウムが生成した。
重合反応開始後、重合による発熱で反応器内の温度は上昇を始め、最終的な反応器内の温度は80℃に達した。反応温度のピーク到達2分後、反応器に2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを3.25mmol添加し、5分間変性反応を実施した。
2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを表1に示した変性剤とし、重合開始剤の添加量、極性化合物の添加量、反応温度、変性剤の添加量を表1のようにした以外は実施例2と同様にして、試料K~Oを製造した。
実施例2と同様に試料の分析を行い、試料K~Oの分析結果を表1に示した。
内容積10Lで、撹拌機及びジャケットを具備する温度制御が可能なオートクレーブを反応器として使用し、予め不純物を除去した、1,3-ブタジエン762g、スチレン268g、シクロヘキサン4710g、極性物質として2,2-ビス(2-オキソラニル)プロパン1.44gを反応器へ入れ、反応器内温を42℃に保持した。
重合開始剤としてn-ブチルリチウム(13.0mmol)を反応器に供給した。重合反応開始後、重合による発熱で反応器内の温度は上昇を始め、最終的な反応器内の温度は80℃に達した。
反応温度のピーク到達2分後、反応器に2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを3.25mmol添加し、5分間変性反応を実施した。
内容積10Lで、撹拌機及びジャケットを具備する温度制御が可能なオートクレーブを反応器として使用し、予め不純物を除去した、1,3-ブタジエン762g、スチレン268g、シクロヘキサン4710g、極性物質として2,2-ビス(2-オキソラニル)プロパン1.30gを反応器へ入れ、反応器内温を42℃に保持した。
重合開始剤として、ピロリジン(13.2mmol)と、n-ブチルリチウム(13.2mmol)をテトラヒドロフラン(26.4mmol)の存在下であらかじめ反応させた、ピロリジノリチウム13.2mmolのシクロヘキサン溶液を反応器に供給した。
重合反応開始後、重合による発熱で反応器内の温度は上昇を始め、最終的な反応器内の温度は75℃に達した。反応温度のピーク到達2分後、反応器に2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタンを3.30mmol添加し、5分間変性反応を実施した。
(重合開始剤*1)
DBA-Li : ジブチルアミノリチウム
HMI-Li : ヘキサメチレンイミノリチウム
DBA-Pr-Li : (3-(ジブチルアミノ)-プロピル)リチウム
HMI-Pr-Li : (3-(ヘキサメチレンイミニル)プロピル)リチウム
DBA-Bt-Li : (4-(ジブチルアミノ)-2-ブテニル)リチウム
HMI-Bt-Li : (4-(ヘキサメチンレンイミニル)-2-ブテニル)リチウム
Pp-Li : ピペリジノリチウム
THP-Li : 1,2,3,6-テトラヒドロピペリジノリチウム
NBL : ノルマルブチルリチウム
HMI : ヘキサメチレンイミン
Pr-Li : ピロリジノリチウム
(極性化合物 *2)
2,2-ビス-(2-オキソラニル)プロパン
(変性剤 *3)
AS-1 : 2,2-ジメトキシ-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタン
AS-2 : 2-メトキシ,2-メチル-1-(3-トリメトキシシリルプロピル)-1-アザ-2-シラシクロペンタン
HCDS : ヘキサクロロジシラン
BTESE : 1,2-ビス(3-トリエトキシシリル)エタン
BTESO : 1,2-ビス(3-トリエトキシシリル)オクタン
BTMSA : ビス(3-トリメトキシシリルプロピル)-N-メチルアミン
DMAPTES : 3-(ジメチルアミノ)プロピルトリエトキシシラン
表1に示す試料(試料A~Q)を原料ゴムとして、以下に示す配合に従い、それぞれの原料ゴムを含有する変性共役ジエン系重合体組成物を得た。
シリカ(エボニック デグサ社製、Ultrasil 7000GR):75.0質量部
カーボンブラック(東海カーボン社製、シーストKH(N339)):5.0質量部
シランカップリング剤(エボニック デグサ社製、Si75):6.0質量部
S-RAEオイル(ジャパンエナジー社製、JOMOプロセスNC140):30.0
質量部
ワックス(大内新興化学社製、サンノックN):1.5質量部
亜鉛華:2.5質量部
ステアリン酸:2.0質量部
老化防止剤(N-イソプロピル-N’-フェニル-p-フェニレンジアミン):2.0
質量部
硫黄:1.8質量部
加硫促進剤(N-シクロヘキシル-2-ベンゾチアジルスルフィンアミド):1.7質
量部
加硫促進剤(ジフェニルグアニジン):2.0質量部
合計:229.5質量部
上記した材料を下記の方法により混練して変性共役ジエン系重合体組成物を得た。
加硫後、変性共役ジエン系重合体組成物の物性を測定した。物性測定結果を表2及び表3に示した。
(1)組成物ムーニー粘度
ムーニー粘度計を使用し、JIS K6300-1に準じて、130℃、1分間の予熱を行った後に、ローターを毎分2回転で4分間回転させた後の粘度を測定し、比較例12の結果を100として指数化した。値が小さいほど加工性に優れることを示す。
JIS K6251の引張試験法に準じて測定し、比較例12の結果を100として指数化した。
レオメトリックス・サイエンティフィック社製の粘弾性試験機(ARES)を使用し、ねじりモードで粘弾性パラメータを測定した。
各々の測定値は比較例12を100として指数化した。
0℃において周波数10Hz、ひずみ1%で測定したtanδをウェットスキッド性能の指標とした。
値が大きいほどウェットスキッド性能が良好であることを示す。
また、50℃において周波数10Hz、ひずみ3%で測定したtanδを省燃費特性の指標とした。値が小さいほど省燃費性能が良好であることを示す。
アクロン摩耗試験機(安田精機製作所製)を使用し、JIS K6264-2に準じて、荷重44.1N、1000回転の摩耗量を測定し、比較例12を100として指数化した。指数が大きいほど耐摩耗性が優れることを示す。
更に実用上十分な加工性(配合物ムーニー粘度)、耐摩耗性、300%モジュラス、伸びを有していることが確認された。
Claims (8)
- 下記化学式(1)又は(2)で表される、分子内に少なくとも1つ窒素原子を有する化合物及び有機リチウム化合物を含む重合開始剤を用い、
共役ジエン化合物、又は共役ジエン化合物と芳香族ビニル化合物とを重合又は共重合することで、活性末端を有する共役ジエン系重合体を得る重合工程と、
前記共役ジエン系重合体の活性末端に、下記化学式(6)で表される変性剤を反応させる変性工程と、
を、有する、変性共役ジエン系重合体の製造方法。
R1及びR2は、結合して隣接した窒素原子とともに環状構造を形成していてもよく、その場合はR1及びR2は、合計の炭素数が5~12の炭化水素基であって、不飽和結合を有していても、分岐構造を有していてもよい。)
- 前記重合工程で用いられる重合開始剤が、
前記分子内に少なくとも1つ窒素原子を有する化合物及び前記有機リチウム化合物を反応させることにより得られる、下記化学式(7)又は(8)で表される分子内に少なくとも1つ窒素原子を有する有機リチウム化合物を含む、請求項1に記載の変性共役ジエン系重合体の製造方法。
R1及びR2は、結合して隣接した窒素原子とともに環状構造を形成していてもよく、その場合はR1及びR2は、合計の炭素数が5~12の炭化水素基であって、不飽和結合を有していても、分岐構造を有していてもよい。)
- 前記重合工程が、
下記化学式(1)又は(2)で表される分子内に少なくとも1つ窒素原子を有する化合物と、
有機リチウム化合物と、
共役ジエン化合物、又は共役ジエン化合物と芳香族ビニル化合物と、
を同時に添加し、重合又は共重合することで、活性末端を有する共役ジエン系重合体を得る工程を含む、
請求項1又は2に記載の変性共役ジエン系重合体の製造方法。
R1及びR2は、結合して隣接した窒素原子とともに環状構造を形成していてもよく、その場合はR1及びR2は、合計の炭素数が5~12の炭化水素基であって、不飽和結合を有していても、分岐構造を有していてもよい。)
- 前記式(6)において、mが2であり、nが3である、請求項1乃至3のいずれか一項に記載の変性共役ジエン系重合体の製造方法。
- 請求項1乃至4のいずれか一項に記載の変性共役ジエン系重合体の製造方法によって得られる、変性共役ジエン系重合体。
- 請求項5に記載の変性共役ジエン系重合体を20質量部以上含有するゴム成分100質量部と、
シリカ系無機充填剤0.5~300質量部と、
を、含む、変性共役ジエン系重合体組成物。 - 請求項6に記載の変性共役ジエン系重合体組成物を架橋処理したゴム組成物。
- 請求項7に記載のゴム組成物を含むタイヤ。