WO2013011770A1 - ガラスエッチング用保護シート - Google Patents
ガラスエッチング用保護シート Download PDFInfo
- Publication number
- WO2013011770A1 WO2013011770A1 PCT/JP2012/064837 JP2012064837W WO2013011770A1 WO 2013011770 A1 WO2013011770 A1 WO 2013011770A1 JP 2012064837 W JP2012064837 W JP 2012064837W WO 2013011770 A1 WO2013011770 A1 WO 2013011770A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- protective sheet
- pressure
- sensitive adhesive
- glass
- meth
- Prior art date
Abstract
Description
CH2=CR1COOR2
(式中、R1は水素原子またはメチル基、R2はアルキル基を示す)で表わされるモノマーを主モノマーとして含むモノマー原料を重合して合成されたものであり、前記主モノマーは、前記式のR2が炭素数6以上のアルキル基であるモノマーを主成分として含むことを特徴とする。
CH2=CR1COOR2 (1)
(式中、R1は水素原子またはメチル基、R2は炭素数6以上のアルキル基を示す)で表わされるモノマーを主モノマーとするアクリル系ポリマーであることが好ましい。
CH2=CR1COOR2 (1)
(式中、R1は水素原子またはメチル基、R2は炭素数6以上のアルキル基を示す)で表わされるモノマーを主モノマーとするアクリル系ポリマーであることを特徴とする。
CH2=CR1COOR2 (1)
(式中、R1は水素原子またはメチル基、R2は炭素数6以上のアルキル基を示す)で表わされる1種以上のモノマー、つまり(メタ)アクリル酸エステルに由来する側鎖を含んでいる。
CH2=CR1COOR2
(式中、R1は水素原子またはメチル基、R2はアルキル基を示す)で表わされるモノマーを含む。上記アルキル基は直鎖状または分岐状である。また、上記主モノマーは、上記式のR2が炭素数6以上のアルキル基であるモノマー(主モノマーA)を主成分として含む。主モノマーAのアルキル基(R2)の炭素数は、好ましくは7以上(典型的には8)である。かかるアルキル基の炭素数が増加するほど疎水性が上がり、エッチング液の浸入を防ぐ効果が期待できる。また、原料の入手しやすさ、製造しやすさ、耐エッチング液浸入性を考慮して、上記炭素数は凡そ30以下とすることが好ましい。なかでも、R2がヘキシル基、ヘプチル基、オクチル基、ノニル基、2-エチルヘキシル基、プロピルヘキシル基のアルキル(メタ)アクリレートが好ましい。R2が2-エチルヘキシル基であるアルキル(メタ)アクリレートがさらに好ましい。これらのモノマーは、1種を単独でまたは2種以上を組み合わせて用いることができる。
例えばアクリル酸、メタクリル酸、クロトン酸、カルボキシエチル(メタ)アクリレート、カルボキシペンチル(メタ)アクリレート等のエチレン性不飽和モノカルボン酸、イタコン酸、マレイン酸、フマル酸、シトラコン酸等のエチレン性不飽和ジカルボン酸等のカルボキシル基含有モノマー;
例えば無水マレイン酸、無水イタコン酸等の上記エチレン性不飽和ジカルボン酸等の酸無水物等の酸無水物基含有モノマー;
例えば2-ヒドロキシエチル(メタ)アクリレート、2-ヒドロキシプロピル(メタ)アクリレート、3-ヒドロキシプロピル(メタ)アクリレート、2-ヒドロキシブチル(メタ)アクリレート、4-ヒドロキシブチル(メタ)アクリレート、6-ヒドロキシヘキシル(メタ)アクリレート、8-ヒドロキシオクチル(メタ)アクリレート、10-ヒドロキシデシル(メタ)アクリレート、12-ヒドロキシラウリル(メタ)アクリレート、(4-ヒドロキシメチルシクロヘキシル)メチル(メタ)アクリレート等のヒドロキシアルキル(メタ)アクリレート類、N-メチロール(メタ)アクリルアミド、ビニルアルコール、アリルアルコール、2-ヒドロキシエチルビニルエーテル、4-ヒドロキシブチルビニルエーテル、ジエチレングリコールモノビニルエーテル等の不飽和アルコール類等のヒドロキシル基(水酸基)含有モノマー;
以下に述べるアミド基含有モノマー、アミノ基含有モノマーおよびシアノ基含有モノマー等の、窒素原子を官能基中に含む官能基含有モノマー、すなわち
例えば(メタ)アクリルアミド、N,N-ジメチル(メタ)アクリルアミド、N-ブチル(メタ)アクリルアミド、N-メチロール(メタ)アクリルアミド、N-メチロールプロパン(メタ)アクリルアミド、N-メトキシメチル(メタ)アクリルアミド、N-ブトキシメチル(メタ)アクリルアミド等のアミド基含有モノマー;
例えばアミノエチル(メタ)アクリレート、N,N-ジメチルアミノエチル(メタ)アクリレート、t-ブチルアミノエチル(メタ)アクリレート等のアミノ基含有モノマー;
例えばアクリロニトリル、メタクリロニトリル等のシアノ基含有モノマー;
例えばスチレンスルホン酸、アリルスルホン酸、2-(メタ)アクリルアミド-2-メチルプロパンスルホン酸、(メタ)アクリルアミドプロパンスルホン酸、スルホプロピル(メタ)アクリレート、(メタ)アクリロイルオキシナフタレンスルホン酸等のスルホン酸基含有モノマー;
例えば2-ヒドロキシエチルアクリロイルホスフェート等のリン酸基含有モノマー;
例えばグリシジル(メタ)アクリレート、メチルグリシジル(メタ)アクリレート、アリルグリシジルエーテル等のエポキシ基(グリシジル基)含有モノマー;
例えばジアセトン(メタ)アクリルアミド、ジアセトン(メタ)アクリレート、ビニルメチルケトン、ビニルエチルケトン、アリルアセトアセテート、ビニルアセトアセテート等のケト基含有モノマー;
例えば2-(メタ)アクリロイルオキシエチルイソシアネート等のイソシアネート基含有モノマー;
例えばメトキシエチル(メタ)アクリレート、エトキシエチル(メタ)アクリレート等のアルコキシ基含有モノマー;
例えば3-(メタ)アクリロキシプロピルトリメトキシシラン、3-(メタ)アクリロキシプロピルトリエトキシシラン、3-(メタ)アクリロキシプロピルメチルジメトキシシラン、3-(メタ)アクリロキシプロピルメチルジエトキシシラン等のアルコキシシリル基含有モノマー;
が挙げられる。これらは1種を単独でまたは2種以上を組み合わせて用いることができる。なかでも、アクリル系ポリマーに架橋点を好適に導入することができ、また、アクリル系ポリマーの凝集力をより高めることができることから、カルボキシル基、ヒドロキシル基、エポキシ基等の官能基含有モノマーが好ましい。カルボキシル基含有モノマーまたはヒドロキシル基含有モノマーがより好ましい。
例えば酢酸ビニル、プロピオン酸ビニル等のビニルエステル系モノマー;
例えばスチレン、置換スチレン(α-メチルスチレン等)、ビニルトルエン等の芳香族ビニル化合物;
例えばアリール(メタ)アクリレート(例えばフェニル(メタ)アクリレート)、アリールオキシアルキル(メタ)アクリレート(例えばフェノキシエチル(メタ)アクリレート)、アリールアルキル(メタ)アクリレート(例えばベンジル(メタ)アクリレート)等の芳香族性環含有(メタ)アクリレート;
例えばN-ビニル-2-ピロリドン、N-メチルビニルピロリドン、N-ビニルピリジン、N-ビニルピペリドン、N-ビニルピリミジン、N-ビニルピペラジン、N-ビニルピラジン、N-ビニルピロール、N-ビニルイミダゾール、N-ビニルオキサゾール、N-ビニルモルホリン、N-ビニルカプロラクタム、N-(メタ)アクリロイルモルホリン等の窒素原子含有環を有するモノマー;
例えばエチレン、プロピレン、イソプレン、ブタジエン、イソブチレン等のオレフィン系モノマー;
例えば塩化ビニル、塩化ビニリデン等の塩素含有モノマー;
例えばメチルビニルエーテル、エチルビニルエーテル等のビニルエーテル系モノマー;
例えばシクロペンチル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート等のシクロアルキル(メタ)アクリレート;が挙げられる。これらは1種を単独でまたは2種以上を組み合わせて用いることができる。なかでも、得られるアクリル系ポリマーの凝集力を向上する観点からビニルエステル系モノマーが好ましい。そのなかでも酢酸ビニルがより好ましい。
ゲル分率[%]=(Wc-Wa)/(Wb-Wa)×100
により求められる。
(1)保護シート表面からのエッチング液浸入の評価
ガラス基板上にpH試験紙を載置し、このpH試験紙を完全に被覆するように保護シートを貼り合わせ、pH試験紙を封止する。これを水平面に置いた後、保護シート上にエッチング液を2cc滴下して、pH試験紙の変色度合を目視で観察し、またその時間を記録する。封止されたpH試験紙の変色度合(pH低下)が少なく、また変色に要する時間が長いほど耐エッチング液浸入性に優れる。pH試験紙のサイズは9mm×15mm、保護シートのサイズは40mm×40mmとすることができる。また、使用するエッチング液としては、HF1mol%、H2SO42mol%、HNO33mol%およびHPO42mol%の混合物を含む水溶液(原液10倍希釈品)を使用することができる。
(2)保護シート側面からのエッチング液浸入の評価
上記(1)と同様にしてガラス基板上に保護シートを貼り合わせる。これを容器に収容し、エッチング液に埋没させて1時間浸漬させる。保護シートの貼付け面におけるガラス基板の浸食(変形)の有無を保護シートの表面から目視で観察する。エッチング液は、上記(1)と同様のものを使用することができる。
○:剥離の際に保護シートに変化はなく、また、ガラス基板にも変化はなかった。
×:剥離の際に保護シートが切れたり、ガラス基板に損傷が確認された。
DM25=EM25h3/12(1-V2);
により求められる値である。曲げ剛性値DT25についても、DM25の場合と同様にして、TDへの引張弾性率ET25を用いて求められる。なお、粘着剤層の曲げ剛性値は基材の曲げ剛性値に比べ非常に小さいため、保護シートの曲げ剛性値は基材の曲げ剛性値と略同等となり得る。したがって、保護シートの曲げ剛性値DM25,DT25は、保護シートを構成する基材の断面積当たりに換算した値をいうものとする。基材の断面積は基材の厚さに基づき算出される。基材の厚さhは、保護シートの厚さの実測値から粘着剤層の厚さを差し引いた値とする。ポアソン比Vは、基材の材質によって定まる値(無次元数)であって、該材質が樹脂である場合には、通常、Vの値として0.35を採用することができる。より具体的には、曲げ剛性値DM25,DT25は、例えば後述する実施例に記載した測定方法にしたがって得られる値を採用することができる。
プロピレンのホモポリマー(すなわちホモポリプロピレン)。例えばアイソタクチックポリプロピレン、シンジオタクチックポリプロピレン、アタクチックポリプロピレン。
プロピレンと他のα-オレフィン(典型的には、エチレンおよび炭素数4~10のα-オレフィンから選択される1種または2種以上)とのランダム共重合体(ランダムポリプロピレン)。例えばプロピレン96~99.9モル%と他のα-オレフィン(好ましくはエチレンおよび/またはブテン)0.1モル%~4モル%とをランダム共重合したランダムポリプロピレン。
プロピレンに他のα-オレフィン(典型的には、エチレンおよび炭素数4~10のα-オレフィンから選択される1種または2種以上)をブロック共重合した共重合体(ブロックポリプロピレン)。かかるブロックポリプロピレンは、副生成物として、プロピレンおよび上記他のα-オレフィンのうち少なくとも1種を成分とするゴム成分をさらに含み得る。例えばプロピレン90モル%~99.9モル%に他のα-オレフィン(好ましくはエチレンおよび/またはブテン)0.1モル%~10モル%をブロック共重合したポリマーと、副生成物としてプロピレンおよび他のα-オレフィンのうち少なくとも1種を成分とするゴム成分をさらに含むブロックポリプロピレン。
CH2=CR1COOR2
で表わされる化合物を好適に用いることができる。
ここで、上記式中のR1は水素原子またはメチル基である。また、R2は炭素原子数1~20のアルキル基(以下、このような炭素原子数の範囲を「C1-20」と表すことがある。)である。粘着剤の貯蔵弾性率等の観点から、R2がC1-14(例えばC1-10)のアルキル基であるアルキル(メタ)アクリレートであってもよい。なお、上記アルキル基は、直鎖状または分岐状である。
例えばアクリル酸、メタクリル酸、クロトン酸、カルボキシエチル(メタ)アクリレート、カルボキシペンチル(メタ)アクリレート等のエチレン性不飽和モノカルボン酸、イタコン酸、マレイン酸、フマル酸、シトラコン酸等のエチレン性不飽和ジカルボン酸等のカルボキシル基含有モノマー;
例えば無水マレイン酸、無水イタコン酸等の上記エチレン性不飽和ジカルボン酸等の酸無水物等の酸無水物基含有モノマー;
例えば2-ヒドロキシエチル(メタ)アクリレート、2-ヒドロキシプロピル(メタ)アクリレート、3-ヒドロキシプロピル(メタ)アクリレート、2-ヒドロキシブチル(メタ)アクリレート、4-ヒドロキシブチル(メタ)アクリレート、6-ヒドロキシヘキシル(メタ)アクリレート、8-ヒドロキシオクチル(メタ)アクリレート、10-ヒドロキシデシル(メタ)アクリレート、12-ヒドロキシラウリル(メタ)アクリレート、(4-ヒドロキシメチルシクロヘキシル)メチル(メタ)アクリレート等のヒドロキシアルキル(メタ)アクリレート類、N-メチロール(メタ)アクリルアミド、ビニルアルコール、アリルアルコール、2-ヒドロキシエチルビニルエーテル、4-ヒドロキシブチルビニルエーテル、ジエチレングリコールモノビニルエーテル等の不飽和アルコール類等のヒドロキシル基(水酸基)含有モノマー;
以下に述べるアミド基含有モノマー、アミノ基含有モノマーおよびシアノ基含有モノマー等の窒素原子を官能基中に含む官能基含有モノマー、すなわち
例えば(メタ)アクリルアミド、N,N-ジメチル(メタ)アクリルアミド、N-ブチル(メタ)アクリルアミド、N-メチロール(メタ)アクリルアミド、N-メチロールプロパン(メタ)アクリルアミド、N-メトキシメチル(メタ)アクリルアミド、N-ブトキシメチル(メタ)アクリルアミド等のアミド基含有モノマー;
例えばアミノエチル(メタ)アクリレート、N,N-ジメチルアミノエチル(メタ)アクリレート、t-ブチルアミノエチル(メタ)アクリレート等のアミノ基含有モノマー;
例えばアクリロニトリル、メタクリロニトリル等のシアノ基含有モノマー;
例えばスチレンスルホン酸、アリルスルホン酸、2-(メタ)アクリルアミド-2-メチルプロパンスルホン酸、(メタ)アクリルアミドプロパンスルホン酸、スルホプロピル(メタ)アクリレート、(メタ)アクリロイルオキシナフタレンスルホン酸等のスルホン酸基含有モノマー;
例えば2-ヒドロキシエチルアクリロイルホスフェート等のリン酸基含有モノマー;
例えばグリシジル(メタ)アクリレート、メチルグリシジル(メタ)アクリレート、アリルグリシジルエーテル等のエポキシ基(グリシジル基)含有モノマー;
例えばジアセトン(メタ)アクリルアミド、ジアセトン(メタ)アクリレート、ビニルメチルケトン、ビニルエチルケトン、アリルアセトアセテート、ビニルアセトアセテート等のケト基含有モノマー;
例えば2-(メタ)アクリロイルオキシエチルイソシアネート等のイソシアネート基含有モノマー;
例えばメトキシエチル(メタ)アクリレート、エトキシエチル(メタ)アクリレート等のアルコキシ基含有モノマー;
例えば3-(メタ)アクリロキシプロピルトリメトキシシラン、3-(メタ)アクリロキシプロピルトリエトキシシラン、3-(メタ)アクリロキシプロピルメチルジメトキシシラン、3-(メタ)アクリロキシプロピルメチルジエトキシシラン等のアルコキシシリル基含有モノマー;
が挙げられる。これらは1種を単独でまたは2種以上を組み合わせて用いることができる。なかでも、アクリル系ポリマーに架橋点を好適に導入することができ、また、アクリル系ポリマーの凝集力をより高めることができることから、カルボキシル基、ヒドロキシル基、エポキシ基等の官能基含有モノマーが好ましく、カルボキシル基含有モノマーまたはヒドロキシル基含有モノマーがより好ましい。
例えば酢酸ビニル、プロピオン酸ビニル等のビニルエステル系モノマー;
例えばスチレン、置換スチレン(α-メチルスチレン等)、ビニルトルエン等の芳香族ビニル化合物;
例えばアリール(メタ)アクリレート(例えばフェニル(メタ)アクリレート)、アリールオキシアルキル(メタ)アクリレート(例えばフェノキシエチル(メタ)アクリレート)、アリールアルキル(メタ)アクリレート(例えばベンジル(メタ)アクリレート)等の芳香族性環含有(メタ)アクリレート;
例えばN-ビニル-2-ピロリドン、N-メチルビニルピロリドン、N-ビニルピリジン、N-ビニルピペリドン、N-ビニルピリミジン、N-ビニルピペラジン、N-ビニルピラジン、N-ビニルピロール、N-ビニルイミダゾール、N-ビニルオキサゾール、N-ビニルモルホリン、N-ビニルカプロラクタム、N-(メタ)アクリロイルモルホリン等の窒素原子含有環を有するモノマー;
例えばエチレン、プロピレン、イソプレン、ブタジエン、イソブチレン等のオレフィン系モノマー;
例えば塩化ビニル、塩化ビニリデン等の塩素含有モノマー;
例えばメチルビニルエーテル、エチルビニルエーテル等のビニルエーテル系モノマー;
例えばシクロペンチル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート等のシクロアルキル(メタ)アクリレート;が挙げられる。これらは1種を単独でまたは2種以上を組み合わせて用いることができる。なかでも、得られるアクリル系ポリマーの凝集力を向上する観点からビニルエステル系モノマーが好ましい。そのなかでも酢酸ビニルがより好ましい。
ゲル分率[%]=(Wc-Wa)/(Wb-Wa)×100
により求められる。
実施例1
基材としてPEフィルムを用いて保護シートを作製した。低密度ポリエチレン(東ソー(株)製、商品名「ペトロセン180」)をインフレーション成形機によりダイス温度160℃の条件で100μm厚に成膜し、片面にコロナ放電処理を施してPEフィルムを作製した。このフィルムのコロナ処理面にアクリル系粘着剤組成物aを塗付し、80℃で1分間乾燥させて、厚さ3μmの粘着剤層を形成した。さらにこの粘着剤層を同フィルムの非コロナ処理面を貼り合わせ、50℃条件下で2日間エージングして、保護シートを作製した。
架橋剤としてエポキシ系架橋剤(三菱瓦斬化学(株)製「TETRAD(登録商標)-C」)4部を加え(言い換えると、エポキシ系架橋剤の使用量を2部とし)、粘着剤層の厚さが10μmとなるように形成したこと以外は実施例1と同様に保護シートを作製した。
実施例1と同様の基材を150μm厚に製膜し(言い換えると、基材の厚さを150μmとした他は実施例1と同様にして基材を製膜し)、粘着剤層の厚さが10μmとなるようにアクリル系粘着剤組成物bを塗付して保護シートを作製した。アクリル系粘着剤組成物bとして、以下の方法で製造したものを使用した。冷却管、窒素導入管、温度計、撹拌装置を備えた反応容器に、2-エチルヘキシルアクリレート100部、酢酸ビニル80部、アクリル酸5部および重合開始剤としてベンゾイルパーオキサイド(BPO,日油(株)製「ナイパー(登録商標)BW」)0.3部を、所望の固形分になるよう配合したトルエン中で共重合させてアクリル系共重合ポリマーを得た。さらにこのアクリル系ポリマー100部に対し、キシレン樹脂(三菱瓦斬化学(株)製「ニカノール(登録商標)H-80」)20部、ブチル化メラミン架橋剤(DIC(株)製「スーパーベッカミン(登録商標)J-820-60N」)2部、アルキルリン酸エステル(東邦化学工業(株)製「フォスファノール(登録商標)RL-210」)0.7部、イソシアネート系架橋剤(日本ポリウレタン工業(株)製、「コロネート(登録商標)L」)5部を加え、所望の固形分になるようトルエンを加えてアクリル系粘着剤組成物bとした。
基材として、60μm厚に製膜したこと以外(言い換えると、基材の厚さを60μmとした他)は実施例1と同様に保護シートを作製した。
実施例1と同様の基材を55μm厚に製膜し(言い換えると、基材の厚さを55μmとした他は実施例1と同様にして基材を製膜し)、粘着剤層の厚さが5μmとなるようにアクリル系粘着剤組成物cを塗付して保護シートを作製した。アクリル系粘着剤組成物cとして、以下の方法で製造したものを使用した。冷却管、窒素導入管、温度計、撹拌装置を備えた反応容器に、ブチルアクリレート58部、n-ブチルメタクリレート40部およびアクリル酸2部からなる単量体混合物100部に対し、界面活性剤(第一工業製薬(株)製「アクアロン(登録商標)BC-2020」)1.65部、アルキルリン酸エステル(東邦化学工業(株)製「フォスファノールRE-410」0.6部、重合開始剤として過硫酸アンモニウム(キシダ化学(株)製「1級ペルオキソ二硫酸アンモニウム」)0.23部を、所望の固形分になるように配合して水中で乳化重合し、10%アンモニウム水によりpH8に調整して、ポリマーエマルションを得た。重合開始剤は所定量の水で希釈し、滴下しながら加えた。さらにこのポリマーエマルションの固形分100部に対し、オキサゾリン系架橋剤((株)日本触媒製「エポクロス(登録商標)WS-500」)2部を混合して、アクリル系粘着剤組成物cとした。
実施例1と同様の基材を60μm厚に製膜し(言い換えると、基材の厚さを60μmとした他は実施例1と同様にして基材を製膜し)、粘着剤層の厚さが3μmとなるようにアクリル系粘着剤組成物dを塗付して保護シートを作製した。アクリル系粘着剤組成物dとして、以下の方法で製造したものを使用した。冷却管、窒素導入管、温度計、撹拌装置を備えた反応容器に、2-エチルヘキシルアクリレート95部、アクリル酸5部および重合開始剤としてベンゾイルパーオキサイド(BPO,日油(株)製「ナイパー(登録商標)BW」)0.15部を、所望の固形分になるように配合してトルエン中で共重合させてアクリル系共重合ポリマーを得た。さらにこのアクリル系ポリマー100部に対し、イソシアネート系架橋剤(日本ポリウレタン工業(株)製「コロネート(登録商標)L」)3部を加え、所望の固形分になるようにトルエンを加えてアクリル系粘着剤組成物dを作製した。
粘着剤組成物の約0.1g(W1)をテフロン(登録商標)膜に包み、秤量した。これを溶媒(トルエン)に浸漬し、室温で1週間放置した。試料を乾燥した後、不溶解分の質量(W2)を測定し、ゲル分率(%)=100×W2/W1により求めた。
(1)保護シート表面からのエッチング液浸入
ガラス基板上にpH試験紙を載置し、このpH試験紙を完全に被覆するように、保護シートを貼り合わせた。この保護シートの上にエッチング液を2cc滴下し、pH試験紙が変色するか否かを観察した。変色しなかった場合は○、変色した場合は×とした。エッチング液は、HF:1%、H2SO4:2%、HNO3:3%およびHPO4:2%の混合物を含む水溶液(原液10倍希釈品)を使用した。
pH試験紙のサイズ:9mm×15mm
テープのサイズ:40mm×40mm
(2)保護シート側面からのエッチング液浸入
ガラス基板上に保護シートを貼り合わせ、エッチング液に1時間浸漬させ、保護シートの表面から観察し、浸食の有無を確認した。
上記(1)および(2)のエッチング液浸入の評価を行い、保護シート表面からのエッチング液浸入および保護シート側面からの液浸入が起こらなかったものをAとした。保護シート側面からの液浸入は起こらなかったが、保護シート表面からのエッチング液浸入が一部見られたものをBとした。保護シート表面からのエッチング液浸入は起こらなかったが、保護シート側面からの液浸入が一部見られたものをCとした。保護シート表面からのエッチング液浸入および保護シート側面からの液浸入が共に見られたものは×とした。
ガラス基板上に保護シートを貼り合わせ、エッチング液に1時間浸漬させた後で、保護シートを剥離する際の作業性を評価した。重剥離により被着体が破壊した場合は×、被着体に影響がなかった場合は○とした。
測定温度:25℃
試験片の幅:20mm
引張速度:300mm/min
引き剥がし方向:180°
保護シートのサイズ:20mm×60mm(MD方向を長手方向として切断した)
ガラス:松浪硝子工業(株)製「MICROSLIDE GLASS」1.3mm×65mm×165mm
貼合せ方法:2kgローラーで1往復させて貼り合わせた。
粘着剤組成物として、アクリル系粘着剤組成物dを使用した。
架橋剤として、エポキシ系架橋剤(三菱瓦斬化学(株)製「TETRAD(登録商標)-C」)0.6部を加えたこと以外(言い換えると、イソシアネート系架橋剤3部に代えてエポキシ系架橋剤(三菱瓦斬化学(株)製「TETRAD(登録商標)-C」)0.6部を用いたこと以外)は、参考例1と同様にしてアクリル系粘着剤組成物eを作製した。
架橋剤として、エポキシ系架橋剤(三菱瓦斬化学(株)製「TETRAD(登録商標)-C」)1.2部を加えたこと以外(言い換えると、イソシアネート系架橋剤3部に代えてエポキシ系架橋剤(三菱瓦斬化学(株)製「TETRAD(登録商標)-C」)1.2部を用いたこと以外)は、参考例1と同様にしてアクリル系粘着剤組成物fを作製した。
ガラス基板上にpH試験紙を載置し、このpH試験紙を完全に被覆するように、粘着剤組成物を100μmの膜厚で積層した。この粘着剤組成物の上にエッチング液を2cc滴下し、pH試験紙が変色するまでの時間を観察した。エッチング液は、HF:1%、H2SO4:2%、HNO3:3%およびHPO4:2%の混合物を含む水溶液(原液10倍希釈品)を使用した。
pH試験紙のサイズ:9mm×15mm
テープ(粘着剤層)のサイズ:40mm×40mm
[粘着剤組成物の調製]
<調製例1>
冷却管、窒素導入管、温度計、滴下ロートおよび撹拌装置を備えた反応容器に、重合溶媒としてトルエン100部、主モノマーとして2-エチルヘキシルアクリレート100部、副モノマーとしてアクリル酸5部、酢酸ビニル80部、過酸化物系重合開始剤としてベンゾイルパーオキサイド(BPO,日油(株)製「ナイパー(登録商標)BW」)0.3部を入れ、窒素還流を室温にて1時間行った。次に、容器内容物の温度を63℃に昇温し、窒素気流中で重合を4時間行った。その後、さらに容器内容物の温度を80℃に昇温して2時間熟成し、アクリル系ポリマーAの溶液を得た。このアクリル系ポリマーAの重合率は99.5重量%であった。このようにして得たアクリル系ポリマーA100部(固形分)に対し、架橋剤としてエポキシ系架橋剤(三菱瓦斬化学(株)製「TETRAD(登録商標)-C」)2部(固形分)を配合して、粘着剤組成物Aとした。
冷却管、窒素導入管、温度計、滴下ロートおよび撹拌装置を備えた反応容器に、重合溶媒として酢酸エチル100部、主モノマーとしてn-ブチルメタクリレート95部、副モノマーとしてアクリル酸5部、アゾ系重合開始剤として2,2′-アゾビス-2-メチルブチロニトリル(AMBN)0.1部を入れ、窒素還流を室温にて1時間行った。次に、容器内容物の温度を63℃に昇温し、窒素気流中で重合を4時間行った。その後、さらに容器内容物の温度を80℃に昇温して2時間熟成し、アクリル系ポリマーBの溶液を得た。このアクリル系ポリマーBの重合率は99.5重量%であった。このようにして得たアクリル系ポリマーB100部(固形分)に対し、架橋剤としてイソシアネート系架橋剤(トリメチロールプロパンのトリレンジイソシアネート付加物(日本ポリウレタン工業(株)製「コロネート(登録商標)L」))2部(固形分)を配合して、粘着剤組成物Bとした。
冷却管、窒素導入管、温度計、滴下ロートおよび撹拌装置を備えた反応容器に、重合溶媒として酢酸エチル100部、主モノマーとして2-エチルヘキシルアクリレート95部、副モノマーとしてアクリル酸5部、アゾ系重合開始剤として2,2’-アゾビスイソブチロニトリル(AIBN)0.1部を入れ、窒素還流を室温にて1時間行った。次に、容器内容物の温度を60℃に昇温し、窒素気流中で重合を4時間行った。その後、さらに容器内容物の温度を75℃に昇温して2時間熟成し、アクリル系ポリマーCの溶液を得た。このアクリル系ポリマーCの重合率は99.9重量%であった。このようにして得たアクリル系ポリマーC100部(固形分)に対し、架橋剤としてイソシアネート系架橋剤(商品名:コロネート(登録商標)L)3部(固形分)を配合して、粘着剤組成物Cとした。
冷却管、窒素導入管、温度計、滴下ロートおよび撹拌装置を備えた反応容器に、重合溶媒としてトルエン65部、主モノマーとして2-エチルヘキシルアクリレート100部、副モノマーとして2-ヒドロキシエチルアクリレート9.3部、過酸化物系重合開始剤としてBPO0.2部を入れ、窒素気流中で61℃にて6時間重合処理をし、質量平均分子量約58万のアクリル系ポリマーDを得た。このアクリル系ポリマーDに2-メタクリロイルオキシエチルイソシアネート(MOI)10.0部(2-ヒドロキシエチルアクリレートに対して80mol%)を加え、空気気流中で50℃にて48時間、付加反応処理をし、アクリル系ポリマーの溶液を得た。次に、得られたアクリル系ポリマー100部(固形分)に対し、イソシアネート系架橋剤(商品名:コロネート(登録商標)L)8部と光重合開始剤(BASF社製、商品名「イルガキュア250」)5部を加えて、粘着剤組成物Dを得た。
冷却管、窒素導入管、温度計、滴下ロートおよび撹拌装置を備えた反応容器に、重合溶媒として酢酸エチル100部、主モノマーとして2-エチルヘキシルアクリレート50部およびエチルアクリレート50部、副モノマーとして2-ヒドロキシエチルアクリレート5部、アゾ系重合開始剤としてAMBN0.1部を入れ、窒素還流を室温にて1時間行った。次に、容器内容物の温度を63℃に昇温し、窒素気流中で重合を4時間行った。その後、さらに容器内容物の温度を80℃に昇温して2時間熟成し、アクリル系ポリマーEの溶液を得た。このアクリル系ポリマーEの重合率は99.5重量%であった。このようにして得たアクリル系ポリマーE100部(固形分)に対して、イソシアネート系架橋剤(商品名:コロネート(登録商標)L)2部と、アルキルフェノール樹脂(荒川化学工業(株)製「タマノル100S」)10部と、熱膨張性微小球(松本油脂製薬(株)「マツモトマイクロスフェアーF50D」、発泡開始温度:120℃、平均粒子径:14μm):40部を加えて粘着剤組成物Eを得た。
冷却管、窒素導入管、温度計、滴下ロートおよび撹拌装置を備えた反応容器に、重合溶媒としてトルエン100部、主モノマーとして2-エチルヘキシルアクリレート100部、副モノマーとしてアクリル酸5部、酢酸ビニル80部、過酸化物系重合開始剤としてベンゾイルパーオキサイド(BPO,日油(株)製「ナイパー(登録商標)BW」)0.3部を入れ、窒素還流を室温にて1時間行った。次に、容器内容物の温度を63℃に昇温し、窒素気流中で重合を4時間行った。その後、さらに容器内容物の温度を80℃に昇温して2時間熟成し、アクリル系ポリマーFの溶液を得た。このアクリル系ポリマーFの重合率は99.5重量%であった。このようにして得たアクリル系ポリマーA100部(固形分)に対し、架橋剤としてエポキシ系架橋剤(三菱瓦斬化学(株)製「TETRAD(登録商標)-C」)1.5部(固形分)を配合して、粘着剤組成物Fとした。
<製造例1>
低密度ポリエチレン(東ソー(株)製「ペトロセン(登録商標)186R」)をTダイ押出機を用いて成形することによって、厚さ150μmのフィルム状基材Aを得た。基材Aの片面にはコロナ放電処理を施した。
エチレン-酢酸ビニル共重合体(EVA)(東ソー(株)製「ウルトラセン(登録商標)635」)30部、多段重合エチレン/プロピレン共重合体(サンアロマー(株)製「キャタロイQ-200F」)70部、アミノシランカップリング処理焼成カオリン(BASF社製「TRANSLINK445」)35部、フェノール系酸化防止剤((株)ADEKA製「アデカスタブ(登録商標)AO-60」0.5部をドライブレンドし、加圧ニーダーにて180℃で混練してペレット化した。このペレットを、カレンダー押出機を用いて成形することによって、厚さ150μmのフィルム状基材Bを得た。基材Bの片面にはコロナ放電処理を施した。
エチレン酢酸ビニル共重合体(EVA)(三井・デュポン・ポリケミカル(株)製「エバフレックス(登録商標)EV270」)をTダイ押出機を用いて成形することによって、厚さ115μmのフィルム状基材Cを得た。基材Cの片面にはコロナ放電処理を施した。
厚さ75μmのポリエチレンテレフタレート(東レ(株)製「ルミラー(登録商標)S-10」を基材Dとして用いた。
た。
フィルムの厚さを100μmに変更した他は、製造例1と同様にして基材Eを作製した。基材Eの片面にはコロナ放電処理を施した。
得られた粘着剤組成物A~Fを、アプリケータを用いて、シリコーン処理が施された厚さが38μmのポリエチレンテレフタレート(PET)フィルムの片面に付与し、温度120℃で3分間乾燥することによって表4に示す厚さの粘着剤層を形成した。粘着剤組成物A~Fから形成された粘着剤と基材A~Eとが表4に示す組合せとなるように、粘着剤層のPETフィルム側とは反対側の表面に基材のコロナ放電処理面を貼り合わせて、例1~例10に係る保護シートを作製した。各例で作製した保護シートにつき、下記の評価試験を行った。
各保護シートにつき、以下の方法で10%延伸時強度を測定した。すなわち、粘着剤層上に剥離ライナーが配置された形態(剥離ライナー付き保護シートの形態)で、基材のMD方向に沿って幅10mm×長さ150mmの短冊状に保護シートを切り出し、剥離ライナーを除去したものを試験片として用いた。JIS K7127に準拠して、上記試験片をMDへ10%延伸したときの強度TM25(N/cm)を以下の条件で測定した。
10%延伸時強度の測定条件:
測定温度 25℃(当該温度に試験片を30分以上保持した後に測定を開始した。);
引張速度 300mm/分;
チャック間距離 100mm;
各保護シートにつき、TDを長手方向として幅10mmの短冊状に切り出した試験片を用い、上記と同様にしてTDへ10%延伸したときの強度(引張張力)を測定し、TDへの10%延伸時の強度TT25(N/cm)を求めた。
また、測定されたTM25,TT25から、これらの合計値TS25を求めた。
各保護シートを、MDを長手方向として幅10mmの短冊状にカットして試験片を作製した。この試験片を、JIS K7161に準拠して、下記条件で延伸することにより応力-ひずみ曲線を得た。
延伸条件:
測定温度 25℃;
引張速度 300mm/分;
チャック間距離 50mm;
MD引張弾性率EM25は、規定された2点のひずみε1=1およびε2=2の間の曲線の線形回帰によって求めた。異なる箇所から切り出した3つの試験片を用いて上記測定を行い、それらの平均値を25℃におけるMDへの引張弾性率EM25(MPa)とした。また、各保護シートを、TDを長手方向として幅10mmの短冊状にカットして試験片を作製した。この試験片を用い、上記と同様にして、25℃におけるTDへの引張弾性率ET25(MPa)を求めた。測定されたEM25,ET25から、これらの合計値ES25(MPa)を求めた。なお、EM25,ET25は、各保護シートの厚さの実測値から粘着剤層の厚さを差し引いた厚さの値、または基材そのものの厚さを測定して得た値に基づいて、基材の断面積当たりの値に換算して求めた。
上記で測定したEM25,ET25、各基材の厚さh、および式:
D=Eh3/12(1-V2);
から、曲げ剛性値DM25,DT25(Pa・m3)を各々算出し、それらの合計値DS25を求めた。ここで、上記式におけるポアソン比Vの値としては0.35を採用した。
図3に示すように、100mm×50mmにカットした各例の保護シート10を用意し、側面から見たときに、保護シート10の長手方向の60mmの部分が水平上面を有する試験台40上に乗り、かつ該長手方向の残りの40mmの部分が試験台40の端面から側方に突出するように保護シート10を試験台40に固定した。この保護シート10の試験台40から側方に突出した部分の鉛直方向に対する角度A°を測定した。この角度A°をたわみ角度として記録した。
100mm×100mmのガラス板に、テープ総厚53μmで70mm×70mmのポリエステル粘着テープ(日東電工(株)製「No.31B」)を前記ガラス板の中央に貼り付け、ガラス面に段差を設けた。このポリエステル粘着テープを完全に覆い、かつ前記ガラス板に重なるように、例1~例10で作製した保護シートを100mm×100mmにカットしたものをハンドローラーで貼り付け、これを試験サンプルとした。各試験サンプルを水中に24時間放置した後、取り出し、保護シートをガラス板から剥がし、保護シートの貼付け部分への水の浸入状況を目視で確認した。保護シート内への水の浸入が全く認められなかったものを◎、保護シート内への水の浸入がわずかに認められたものを○、水の浸入が認められたものを×とした。なお、シール性と次に説明する剥離性について、紫外線硬化型粘着剤を用いた例5の保護シートは、粘着剤層に紫外線を照射(照射積算光量:50~500mJ/cm2)した後に評価を行った。また、粘着剤に熱膨張性微小球を含有させた例6の保護シートは、粘着剤層に120℃で5分間の加熱処理を行った後に評価を行った。
上記シール性の評価において、保護シートをガラス板から剥がす際の作業性を評価した。スムーズに剥離することができ、保護シートの伸び、切れ、ポリエステル粘着テープの剥がれがなかったものを○、剥離が重く、保護シートの伸びが認められたものを×とした。
2 粘着剤層
3 剥離ライナー
10 保護シート
20 ガラス基板
30 ITO膜
40 試験台
Claims (13)
- 基材と該基材の片面に設けられた粘着剤層とを備え、ガラスをエッチングする際に非エッチング部分に貼り付けて該非エッチング部分をエッチング液から保護するガラスエッチング用保護シートであって、
前記粘着剤層を構成する粘着剤のゲル分率が60%以上であり、
前記粘着剤が、アクリル系ポリマーを主成分とするアクリル系粘着剤であり、
前記アクリル系ポリマーは、式:
CH2=CR1COOR2
(式中、R1は水素原子またはメチル基、R2はアルキル基を示す)
で表わされるモノマーを主モノマーとして含むモノマー原料を重合して合成されたものであり、
前記主モノマーは、前記式のR2が炭素数6以上のアルキル基であるモノマーを主成分として含むことを特徴とする、ガラスエッチング用保護シート。 - 基材と該基材の片面に設けられた粘着剤層とを備え、ガラスをエッチングする際に非エッチング部分に貼り付けて該非エッチング部分をエッチング液から保護するガラスエッチング用保護シートであって、
前記粘着剤層のゲル分率が60%以上であり、
前記粘着剤層は、式(1):
CH2=CR1COOR2 (1)
(式中、R1は水素原子またはメチル基、R2は炭素数6以上のアルキル基を示す)
で表わされるモノマーを主モノマーとするアクリル系ポリマーである、請求項1に記載のガラスエッチング用保護シート。 - 前記粘着剤層が、カルボキシル基または水酸基を有するモノマーを含有する、請求項1または2に記載のガラスエッチング用保護シート。
- 前記基材の厚さが80μm以上である、請求項1から3のいずれかに記載のガラスエッチング用保護シート。
- 前記基材の粘着剤層側表面および/または背面の算術平均表面粗さが0.05~1μmである、請求項1から4のいずれかに記載のガラスエッチング用保護シート。
- ガラスに対する粘着力が、0.05N/20mm~3.00N/20mmである、請求項1から5のいずれかに記載のガラスエッチング用保護シート。
- 前記基材が、ポリプロピレン(PP)、ポリエチレン(PE)、ポリエチレンテレフタレート(PET)、ポリ塩化ビニル(PVC)、ポリイミド(PI)、ポリブチレンテレフタレート(PBT)、ポリフェニレンサルファイド(PPS)、エチレン酢酸ビニル(EVA)またはポリテトラフルオロエチレン(PTFE)からなる層を含む、請求項1から6のいずれかに記載のガラスエッチング用保護シート。
- 前記粘着剤が架橋剤を含有し、該架橋剤がエポキシ系架橋剤またはイソシアネート系架橋剤である、請求項1から7のいずれかに記載のガラスエッチング用保護シート。
- ガラス基板の表面をエッチング処理する前に、前記ガラスエッチング用保護シートの粘着剤層側を該ガラス基板の一方の表面の非エッチング部分に貼り付けることで、該非エッチング部分をエッチング液から保護するガラス基板の表面保護シートとして用いられる、請求項1から8のいずれかに記載のガラスエッチング用保護シート。
- 基材と該基材の少なくとも一方の表面に設けられた粘着剤層とを備えるガラスエッチング用保護シートであって、
前記保護シートの温度25℃におけるMD(Machine Direction)への10%延伸時の強度TM25および同温度における前記MDに直交するTD(Transverse Direction)への10%延伸時の強度TT25の少なくとも一方が、1N/cm~25N/cmであることを特徴とする、ガラスエッチング用保護シート。 - 前記保護シートの温度25℃における前記MDへの曲げ剛性値DM25および同温度における前記TDへの曲げ剛性値DT25の少なくとも一方が、1.5×10-5~10×10-5Pa・m3である、請求項10に記載のガラスエッチング用保護シート。
- 前記粘着剤層の前記基材側とは反対側の面に配置される剥離ライナーの算術平均表面粗さが0.05μm~0.75μmである、請求項10または11に記載のガラスエッチング用保護シート。
- ガラス基板の切断面である側面をエッチング処理する前に、少なくとも2枚の前記ガラスエッチング用保護シートの各々の粘着剤層側を該ガラス基板の両表面に貼り付けることで、該ガラス基板の両表面をエッチング液から保護するガラス基板の両表面保護シートとして用いられる、請求項10から12のいずれかに記載のガラスエッチング用保護シート。