WO2012070582A1 - 共役系化合物、並びにこれを用いた有機薄膜及び有機薄膜素子 - Google Patents

共役系化合物、並びにこれを用いた有機薄膜及び有機薄膜素子 Download PDF

Info

Publication number
WO2012070582A1
WO2012070582A1 PCT/JP2011/076934 JP2011076934W WO2012070582A1 WO 2012070582 A1 WO2012070582 A1 WO 2012070582A1 JP 2011076934 W JP2011076934 W JP 2011076934W WO 2012070582 A1 WO2012070582 A1 WO 2012070582A1
Authority
WO
WIPO (PCT)
Prior art keywords
formula
group
group represented
organic thin
thin film
Prior art date
Application number
PCT/JP2011/076934
Other languages
English (en)
French (fr)
Inventor
家　裕隆
西田　和史
安蘇　芳雄
上田　将人
Original Assignee
住友化学株式会社
国立大学法人大阪大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社, 国立大学法人大阪大学 filed Critical 住友化学株式会社
Publication of WO2012070582A1 publication Critical patent/WO2012070582A1/ja

Abstract

　本発明は、電子輸送性に優れたｎ型半導体として利用でき、溶剤への溶解性にも優れる共役系化合物を提供することを課題とする。好適な実施形態の共役系化合物は、式（Ｉ）で表される。［Ｒ０１及びＲ０２はアルカン骨格を含む１価の基、Ｒ１１、Ｒ１２、Ｒ２１及びＲ２２は水素原子、ハロゲン原子又は１価の基、Ｘ１１、Ｘ１２、Ｘ２１及びＸ２２は酸素原子、硫黄原子又は式（ａ）で表される基を示すが、Ｘ１１、Ｘ１２、Ｘ２１及びＸ２２の１つは硫黄原子又は式（ａ）で表される基である。Ｚ１及びＺ２は式（ｉ）～（ｉｘ）のいずれかを示す。Ａｒ０、Ａｒ１及びＡｒ２は芳香族炭化水素基又は複素環基を示す。ｒは１～６の整数を示し、ｓ及びｔは０～６の整数を示す。Ａは、水素原子、ハロゲン原子又は１価の基を示すが、Ａの１つは電子吸引性の基である。Ｒ３、Ｒ４、Ｒ５及びＲ６は水素原子、ハロゲン原子又は１価の基を示す。］

Description

共役系化合物、並びにこれを用いた有機薄膜及び有機薄膜素子
本発明は、共役系化合物、これを含む有機薄膜、並びに係る有機薄膜を備える有機薄膜素子、有機薄膜トランジスタ及び有機薄膜太陽電池に関する。
電子輸送性又はホール輸送性を有する有機材料を含む薄膜は、有機薄膜トランジスタ、有機薄膜太陽電池、光センサ等の有機薄膜素子への応用が期待されている。ところが、これまでは、有機ｐ型半導体（ホール輸送性を示す）に比べると、有機ｎ型半導体（電子輸送性を示す）が得難かったことから、有機ｎ型半導体が種々検討されている。
近年、有機ｎ型半導体に適用できる電子輸送性材料として、π共役化合物の電子受容性を増加させるべく、チオフェン環にフルオロアルキル基を導入した化合物の研究が盛んに行われている（例えば、特許文献１参照）。
また、分子構造の平面性を高めて電子輸送性を向上させるために、架橋した構造を有するポリチオフェンが種々検討されている（特許文献２）。
米国特許出願公開第２００４／１８６２６６号明細書 特開２００４－３３９５１６号公報
しかしながら、上述したような従来の材料であっても、未だ有機ｎ型半導体として十分な性能を得ることは困難な傾向にあった。
また、フレキシブル基板上に有機薄膜素子を形成する場合、有機薄膜を印刷法により形成することができると有利である。そのためには有機溶剤への溶解性に優れた材料が求められる。しかし、十分な有機ｎ型半導体としての特性を有しながら、溶解性の点でも十分に優れた材料は、これまで得ることは極めて困難であった。
そこで、本発明はこのような事情に鑑みてなされたものであり、電子輸送性に優れたｎ型半導体として利用可能であり、しかも溶剤への溶解性にも優れる共役系化合物を提供することを目的とする。
また本発明は、かかる共役系化合物を含む有機薄膜、並びに係る有機薄膜を備える有機薄膜素子、有機薄膜トランジスタ及び有機薄膜太陽電池を提供することを目的とする。
上記目的を達成するために、本発明の共役系化合物は、式（Ｉ）で表されることを特徴とする。
Figure JPOXMLDOC01-appb-C000010
  
Figure JPOXMLDOC01-appb-C000011
  
Figure JPOXMLDOC01-appb-C000012
  
式（Ｉ）中、Ｒ０１及びＲ０２は、それぞれ独立に、アルカン骨格が含まれる１価の基を示し、Ｒ１１、Ｒ１２、Ｒ２１及びＲ２２は、それぞれ独立に、水素原子、ハロゲン原子又は１価の基を示す。Ｘ１１、Ｘ１２、Ｘ２１及びＸ２２は、それぞれ独立に、酸素原子、硫黄原子又は式（ａ）で表される基を示す。ただし、Ｘ１１、Ｘ１２、Ｘ２１及びＸ２２の少なくとも１つは、硫黄原子又は式（ａ）で表される基である。Ｚ１及びＺ２は、それぞれ独立に、式（ｉ）で表される基、式（ｉｉ）で表される基、式（ｉｉｉ）で表される基、式（ｉｖ）で表される基、式（ｖ）で表される基、式（ｖｉ）で表される基、式（ｖｉｉ）で表される基、式（ｖｉｉｉ）で表される基及び式（ｉｘ）で表される基（以下、同様の表記は、「式（ｉ）～（ｉｘ）で表される基」のように表記する。）からなる群より選ばれるいずれか１種の基を示す。Ａｒ０、Ａｒ１及びＡｒ２は、それぞれ独立に、炭素数６以上の２価の芳香族炭化水素基、又は炭素数４以上の２価の複素環基を示し、これらは置換基を有していてもよい。ｒは１～６の整数を示し、ｓ及びｔは、それぞれ独立に、０～６の整数を示す。
また、式（ａ）中、Ａは、水素原子、ハロゲン原子又は１価の基を示し、複数あるＡはそれぞれ同一でも異なっていてもよいが、少なくとも１つのＡは電子吸引性の基である。
さらに、式（ｖｉｉ）、式（ｖｉｉｉ）及び式（ｉｘ）中、Ｒ３、Ｒ４、Ｒ５及びＲ６は、それぞれ独立に、水素原子、ハロゲン原子又は１価の基を示し、Ｒ３とＲ４とは互いに結合して環を形成していてもよい。なお、式（ｖｉｉｉ）で表される基は左右反転していてもよい。
上記構成を有する本発明の共役系化合物は、環同士のπ共役平面性が良好であるとともに、特定の構造を有する末端基が両端に導入されていることで、十分に低いＬＵＭＯ（最低空軌道）を示すことができる。そのため、電子輸送性に優れた有機ｎ型半導体として利用可能である。また、共役系化合物は、π共役平面性が高いことに加えて、末端基がＲ０１及びＲ０２で表されるアルカン骨格が含まれる基を有していることから、化学的に安定で、しかも有機溶剤への溶解性が優れている。したがって、本発明の共役系化合物によれば、塗布法により有機薄膜を形成でき、性能の優れた有機薄膜素子を得ることが可能となる。
本発明の共役系化合物においては、式（Ｉ）におけるＸ１１及びＸ１２の少なくとも一方が式（ａ）で表される基であり、Ｘ２１及びＸ２２の少なくとも一方が式（ａ）で表される基であると好ましい。式（ａ）で表される基は電子吸引性を有することから、かかる基を有することにより、共役系化合物は一層低いＬＵＭＯを示すことができる。その結果、電子輸送性が更に向上する。
また、Ａｒ０は、アルカン骨格を含む置換基を有していない基であるとより好ましい。このような構成とすることで、優れた電子輸送性が得られる。また、Ａｒ０がアルカン骨格を有していなくても、上記のような特定の末端基を有していることから、共役系化合物は、一層優れた溶解性を有することができる。
共役系化合物としては、式（Ｉ）におけるＡｒ０が、式（ＩＩ）で表される基又は式（ＩＩＩ）で表される基であるとより好ましい。このような構成を有することで、電子輸送性が更に高められる傾向にある。
Figure JPOXMLDOC01-appb-C000013
Figure JPOXMLDOC01-appb-C000014
Figure JPOXMLDOC01-appb-C000015
式（ＩＩ）中、Ｚ３は、式（ｘｉ）～式（ｘｉｘ）で表される基からなる群より選ばれるいずれか１種の基を示す。なお、式（ｘｖｉｉｉ）で表される基は左右反転していてもよい。
式（ＩＩＩ）中、Ａｒ３及びＡｒ４は、それぞれ独立に、炭素数６以上の３価の芳香族炭化水素基又は炭素数４以上の３価の複素環基であって、アルカン骨格を含む置換基を有していない基を示し、Ｘ３は、酸素原子、硫黄原子又は式（ａ）で表される基を示す。
上記効果を得やすくなるので、式（ＩＩＩ）で表される基は、式（ＩＶ）で表される基であると好ましい。
Figure JPOXMLDOC01-appb-C000016
Figure JPOXMLDOC01-appb-C000017
 ［式（ＩＶ）中、Ｘ３は前記と同義であり、Ｙ１及びＹ２は、それぞれ独立に、炭素原子又は窒素原子を示し、Ｚ４及びＺ５は、それぞれ独立に、式（ｘｘｉ）～式（ｘｘｉｘ）で表される基からなる群より選ばれるいずれか１種の基を示す。なお、式（ｘｘｖｉｉｉ）で表される基は左右反転していてもよい。］
特に、本発明の共役系化合物は、Ｘ１１及びＸ１２のうちの一方が酸素原子であり、Ｘ１１及びＸ１２のうちの残りの一方が式（ａ１）で表される基であり、かつ、Ｘ２１及びＸ２２のうちの一方が酸素原子であり、Ｘ２１及びＸ２２のうちの残りの一方が式（ａ１）で表される基であると好ましい。また、Ｚ４及びＺ５が、式（ｘｘｉｉ）で表される基又は式（ｘｘｖｉｉ）で表される基であると好ましい。これらの構成を有することで、本発明の共役系化合物は、優れた電子輸送性及び溶解性が一層得られ易いものとなる。
Figure JPOXMLDOC01-appb-C000018
本発明はまた、上記本発明の共役系化合物を含有する有機薄膜、それを備える有機薄膜素子、有機薄膜トランジスタ及び有機薄膜太陽電池を提供する。このような有機薄膜、有機薄膜トランジスタ及び有機薄膜太陽電池は、上述のように優れた電子輸送性を示す本発明の共役系化合物を含む有機薄膜を備えることから、印刷法を用いることで素子の製造が容易であり、しかも優れた性能を発揮することができる。
本発明によれば、電子輸送性に優れたｎ型半導体として利用可能であり、しかも溶剤への溶解性にも優れる共役系化合物を提供することが可能となる。また、本発明によれば、かかる共役系化合物を含む有機薄膜、並びに係る有機薄膜を備える有機薄膜素子、有機薄膜トランジスタ及び有機薄膜太陽電池を提供することが可能となる。
第１実施形態に係る有機薄膜トランジスタの模式断面図である。 第２実施形態に係る有機薄膜トランジスタの模式断面図である。 第３実施形態に係る有機薄膜トランジスタの模式断面図である。 第４実施形態に係る有機薄膜トランジスタの模式断面図である。 第５実施形態に係る有機薄膜トランジスタの模式断面図である。 第６実施形態に係る有機薄膜トランジスタの模式断面図である。 第７実施形態に係る有機薄膜トランジスタの模式断面図である。 実施形態に係る有機薄膜太陽電池の模式断面図である。 第１実施形態に係る光センサの模式断面図である。 第２実施形態に係る光センサの模式断面図である。 第３実施形態に係る光センサの模式断面図である。
以下、場合により図面を参照しつつ、本発明の好適な実施形態について詳細に説明する。なお、図面中、同一要素には同一符号を付すこととし、重複する説明は省略する。また、上下左右等の位置関係は、特に断らない限り、図面に示す位置関係に基づくものとする。更に、図面の寸法比率は図示の比率に限られるものではない。
［共役系化合物］
　好適な実施形態の共役系化合物は、上記の式（Ｉ）で表される構造を有している。ここで、本明細書において、共役系化合物とは、化合物の主骨格において、単結合と、不飽和結合、孤立電子対、ラジカル又は非結合性軌道とが交互に連なる構造を含み、π軌道又は非結合性軌道の相互作用による電子の非局在化が主骨格の一部又は全域に起こっているものをいう。主骨格とは、共役系化合物を構成している構造単位の連鎖のうち、最も長いものであり、芳香環同士が連続して結合している部分は、芳香環が連鎖した構造が主骨格となる。共役系化合物の中でもπ軌道の相互作用によるπ共役系化合物が好ましい。
式（Ｉ）において、Ｒ０１及びＲ０２は、それぞれ独立に、アルカン骨格が含まれる１価の基を示す。ここで、アルカン骨格とは、一般式ＣｎＨ２ｎ＋２（ここで、ｎは１以上の整数を表す。）で表される鎖式飽和炭化水素から１個又は２個の水素原子を取り除いた残りの原子団からなる骨格を表す。アルカン骨格が含まれる１価の基とは、このような鎖式飽和炭化水素からなる基、又は、鎖式飽和炭化水素を少なくとも一部に有する基を表す。アルカン骨格が含まれる１価の基としては、アルキル基、アルコキシ基、チオアルキル基、アルキルフェニル基、アルコキシフェニル基、アルキルチオフェニル基、アルコキシカルボニル基、アルキルシリル基及びアルキルアミノ基が例示される。
アルカン骨格が含まれる１価の基において、アルカン骨格が有している炭素数は、１～３０であると好ましく、３～２４であるとより好ましい。特に、有機溶媒への溶解性が高くなるので、アルカン骨格が有している炭素数は、６～２０であると更に好ましい。アルカン骨格は、直鎖状、分岐状のいずれでもよい。ただし、分子間の配列をよくするためには直鎖状のアルカン骨格が好ましい一方、有機溶媒への溶解性が高くなるので、分岐状のアルカン骨格が好ましく、所望とする特性に応じて選択することができる。
アルカン骨格が含まれる１価の基は、アルキル基であると好ましい。アルキル基としては、直鎖状、分岐状又は環状の炭素数１～３０のアルキル基が好ましく、直鎖状又は分岐状の炭素数３～２４のアルキル基がより好ましく、直鎖状又は分岐状の炭素数６～２０のアルキル基がより好ましい。アルキル基の具体例として、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、イソブチル基、ｔｅｒｔ－ブチル基、３－メチルブチル基、ペンチル基、ヘキシル基、２－エチルヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ラウリル基、３，７－ジメチルオクチル基、３，７，１１－トリメチルドデシル基が挙げられる。なお、アルキル基以外のアルカン骨格が含まれる１価の基が有しているアルカン骨格についても、同様のものが例示できる。
式（Ｉ）において、Ｘ１１、Ｘ１２、Ｘ２１及びＸ２２は、それぞれ独立に、酸素原子、硫黄原子又は式（ａ）で表される基を示す。ただし、Ｘ１１、Ｘ１２、Ｘ２１及びＸ２２の少なくとも１つは、硫黄原子又は式（ａ）で表される基であり、Ｘ１１及びＸ１２の少なくとも１つは、硫黄原子又は式（ａ）で表される基であり、かつ、Ｘ２１及びＸ２２の少なくとも１つは、硫黄原子又は式（ａ）で表される基であるとより好ましい。式（Ｉ）におけるＸ１１、Ｘ１２、Ｘ２１及びＸ２２が含まれる末端基の平面性が高くなるので、Ｘ１２又はＸ２２は、酸素原子又は硫黄原子であることがより好ましい。
式（Ｉ）においては、Ｘ１１及びＸ１２の少なくとも一方が式（ａ）で表される基であり、Ｘ２１及びＸ２２の少なくとも一方が式（ａ）で表される基であると好ましい。式（ａ）中、Ａは、水素原子、ハロゲン原子又は１価の基を示す。複数あるＡは、それぞれ同一でも異なっていてもよいが、少なくとも一つのＡは電子吸引性の基であり、両方が電子吸引性の基であると好ましい。このようにＡとして電子吸引基を有することで、共役系化合物のＬＵＭＯを低くすることができる。電子吸引性の基としては、シアノ基、ニトロ基、ホルミル基、アシル基、アルコキシカルボニル基、カルボキシル基、水酸基及びハロゲン原子が例示され、シアノ基、ニトロ基及びハロゲン原子が好ましく、シアノ基が特に好ましい。
式（Ｉ）において、Ｒ１１、Ｒ１２、Ｒ２１及びＲ２２は、それぞれ独立に、水素原子、ハロゲン原子又は１価の基を示す。ハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子が挙げられる。なお、本明細書で説明されるハロゲン原子としては、いずれも同様の原子が適用できる。１価の基としては、直鎖状若しくは分岐状の低分子鎖からなる基、１価の環状基（この環状基は、単環でも縮合環でも、炭化水素環でも複素環でも、飽和でも不飽和でもよく、置換基を有していてもいなくてもよい）が例示され、これらの基が有する水素原子の一部又は全部は所定の置換基、例えば、ハロゲン原子で置換されていてもよい。
共役系化合物のＬＵＭＯをより低くできるので、Ｒ１１、Ｒ１２、Ｒ２１及びＲ２２の少なくとも一つは電子吸引性の基であることが好ましく、Ｒ１１及びＲ１２の少なくとも一方又はＲ２１及びＲ２２の少なくとも一方が、電子吸引性の基であることがより好ましく、Ｒ１１、Ｒ１２、Ｒ２１及びＲ２２のすべてが電子吸引性の基であることがさらに好ましい。これらの電子吸引性の基としては、ハロゲン原子、及び、上述したような、水素原子の一部又は全部がハロゲン原子で置換された１価の基が好ましく、フッ素原子、及び、一部又は全部の水素原子がフッ素原子で置換されたアルキル基がさらに好ましく、フッ素原子が特に好ましい。
式（Ｉ）において、Ｚ１及びＺ２は、それぞれ独立に、上記の式（ｉ）～（ｉｘ）で表される基からなる群より選ばれるいずれか一種の基を示す。Ｒ３、Ｒ４、Ｒ５及びＲ６は、それぞれ独立に、水素原子、ハロゲン原子又は１価の基を示し、Ｒ３とＲ４とは互いに結合して環を形成していてもよい。なお、式（ｖｉｉｉ）で表される基は左右反転していてもよい。
式（Ｉ）中のＺ１及びＺ２としては、式（ｉ）、（ｉｉ）、（ｉｉｉ）、（ｖｉｉ）、（ｖｉｉｉ）及び（ｉｘ）のいずれかで表される基が好ましく、式（ｉｉ）及び（ｖｉｉ）のいずれかで表される基がより好ましく、式（ｉｉ）で表される基が特に好ましい。式（Ｉ）におけるＺ１及びＺ２を含む環が、チオフェン環、フラン環、ピロール環又はピリジン環、特にチオフェン環となる場合は、特徴的な電気的性質（例えば、電子輸送に適したＬＵＭＯレベル及び安定なキノイド構造をとりやすい性質）が得られ、種々の電気的特性（例えば、高い電子輸送性）が発揮される。
式（Ｉ）において、Ａｒ０は、炭素数６以上の２価の芳香族炭化水素基又は炭素数４以上の２価の複素環基を示す。Ａｒ０としては、上記のようなアルカン骨格を含む置換基を有していない炭素数６以上の２価の芳香族炭化水素基、又はアルカン骨格を含む置換基を有していない炭素数４以上の２価の複素環基が好ましい。このように、式（Ｉ）で表される共役系化合物の中央部分のＡｒ０が、アルカン骨格が含まれる置換基を有しないことにより、分子間のπスタックがし易く、それにより電荷の分子間移動が起こりやすくなるため、有機ｎ型半導体としての性能が向上する傾向にある。
式（Ｉ）中のｒは、Ａｒ０で表される基の繰り返し数を示し、１～６の整数であり、１～３の整数であると好ましい。ｒが２以上である場合、複数のＡｒ０は、それぞれ同一でも異なっていてもよい。
Ａｒ０としては、式（ＩＩ）で表される基が好ましい。式（ＩＩ）中、Ｚ３は、式（ｘｉ）～（ｘｉｘ）で表される基のいずれかを示し、式（ｘｖｉｉｉ）で表される基は左右反転していてもよい。
Figure JPOXMLDOC01-appb-C000019
式（ＩＩ）におけるＺ３としては、なかでも、式（ｘｉ）、（ｘｉｉ）、（ｘｉｉｉ）、（ｘｖｉｉ）、（ｘｖｉｉｉ）のいずれかで表される基が好ましく、式（ｘｉｉ）、（ｘｉｉｉ）、（ｘｖｉｉ）のいずれかで表される基がより好ましく、式（ｘｉｉ）、（ｘｖｉｉ）のいずれかで表される基がさらに好ましく、式（ｘｉｉ）で表される基が特に好ましい。式（ＩＩ）におけるＺ３を含む環が、チオフェン環、フラン環、ピロール環又はピリジン環、特にチオフェン環となる場合、特徴的な電気的性質（例えば、電子輸送に適したＬＵＭＯレベル及び安定なキノイド構造をとりやすい性質）が得られ、種々の電気的特性（例えば、高い電子輸送性）が発揮される。
また、式（Ｉ）におけるＡｒ０は、分子の平面性が高くなるので、式（ＩＩＩ）で表される基であっても好ましい。
Figure JPOXMLDOC01-appb-C000020
式（ＩＩＩ）中、Ａｒ３及びＡｒ４は、それぞれ独立に、炭素数６以上の３価の芳香族炭化水素基又は炭素数４以上の３価の複素環基を示し、これらは上記のようなアルカン骨格が含まれる置換基を有しない基である。Ｘ３は、酸素原子、硫黄原子又は式（ａ）で表される基を示す。
ここで、３価の芳香族炭化水素基とは、ベンゼン環又は縮合環から水素原子３個を除いた残りの原子団からなる基をいう。３価の芳香族炭化水素基の炭素数は、６～６０であることが好ましく、６～２０であることがより好ましい。縮合環としては、ナフタレン環、アントラセン環、テトラセン環、ペンタセン環、ピレン環、ペリレン環、フルオレン環が挙げられる。３価の芳香族炭化水素基としては、これらの中でも、ベンゼン環から水素原子３個を除いた残りの原子団からなる基が特に好ましい。なお、３価の芳香族炭化水素基は、アルカン骨格が含まれる置換基以外の置換基であれば有していてもよい。その場合、３価の芳香族炭化水素基の炭素数には、置換基の炭素数は含まれない。置換基としては、ハロゲン原子、アリール基、アリールオキシ基、１価の複素環基、アミノ基、ニトロ基、シアノ基等が挙げられる。
また、３価の複素環基とは、複素環式化合物から水素原子３個を除いた残りの原子団からなる基をいう。ここで、複素環式化合物とは、環式構造をもつ有機化合物のうち、環を構成する元素が炭素原子だけでなく、酸素原子、硫黄原子、窒素原子、リン原子、ホウ素原子、ケイ素原子等のヘテロ原子を環内に含むものをいう。３価の複素環基の炭素数は、４～６０であることが好ましく、４～２０であることがより好ましい。３価の複素環基としては、チオフェン環、チエノチオフェン環、フラン環、ピロール環、ピリジン環、チアゾール環、オキサゾール環又はイミダゾール環から水素原子３個を除いた残りの原子団からなる基が例示される。特に、Ａｒ３やＡｒ４が、チオフェン環、チエノチオフェン環又はチアゾール環から水素原子３個を除いた残りの原子団からなる基であると、特徴的な電気的性質（例えば、電子輸送に適したＬＵＭＯレベル及び安定なキノイド構造をとりやすい性質）が得られ、従来にない新たな電気的特性が発現することも期待できる。
このような３価の複素環基としては、３価の芳香族複素環基が好ましい。３価の複素環基は、アルカン骨格が含まれる置換基以外の置換基であれば有していてもよい。その場合、３価の複素環基の炭素数には、置換基の炭素数は含まれない。置換基としては、ハロゲン原子、アリール基、アリールオキシ基、１価の複素環基、アミノ基、ニトロ基、シアノ基等が挙げられる。
式（ＩＩＩ）で表される基としては、式（ＩＶ）で表される基が好ましい。式（ＩＶ）中、Ｘ３は、上記と同義である。Ｙ１及びＹ２は、それぞれ独立に、炭素原子又は窒素原子を表す。Ｚ４及びＺ５は、それぞれ独立に、式（ｘｘｉ）～（ｘｘｉｘ）で表される基のいずれかを示し、式（ｘｘｖｉｉｉ）で表される基は左右反転していてもよい。
Figure JPOXMLDOC01-appb-C000021
式（ＩＶ）中のＺ４及びＺ５としては、なかでも、式（ｘｘｉ）、（ｘｘｉｉ）、（ｘｘｉｉｉ）、（ｘｘｖｉｉ）、（ｘｘｖｉｉｉ）のいずれかで表される基が好ましく、式（ｘｘｉｉ）、（ｘｘｉｉｉ）、（ｘｘｖｉｉ）のいずれかで表される基がより好ましく、式（ｘｘｉｉ）、（ｘｘｖｉｉ）のいずれかで表される基がさらに好ましく、式（ｘｘｉｉ）で表される基が特に好ましい。また、式（ＩＶ）中のＹ１及びＹ２の少なくとも一方は、ＬＵＭＯをより低くできるので、窒素原子が好ましく、Ｙ１及びＹ２の両方が窒素原子であるとより好ましい。
式（ＩＩＩ）又は（ＩＶ）中のＸ３としては、共役系化合物のＬＵＭＯをより低くできるので、酸素原子又は式（ａ）で表される基が好ましく、酸素原子又は式（ａ）において少なくとも一方のＡがシアノ基である基がより好ましく、酸素原子又は式（ａ）において両方のＡがシアノ基である基がさらに好ましい。
式（ＩＩＩ）又は（ＩＶ）で表される基としては、例えば、以下の化学式で表される基が挙げられる。
Figure JPOXMLDOC01-appb-C000022
Figure JPOXMLDOC01-appb-C000023
式（Ｉ）におけるＡｒ１及びＡｒ２は、それぞれ独立に、炭素数６以上の２価の芳香族炭化水素基又は炭素数４以上の２価の複素環基を示し、これらは置換基を有してもよい。式（Ｉ）におけるｓは、Ａｒ１で表される基の繰り返し数を示し、ｔは、Ａｒ２で表される基の繰り返し数を示す。ｓ及びｔは、それぞれ独立に、０～６の整数であり、０～２の整数であると好ましい。ｓ又はｔが２以上である場合、複数となるＡｒ１又は複数となるＡｒ２は、それぞれ同一でも異なっていてもよい。
ここで、２価の芳香族炭化水素基とは、ベンゼン環又は縮合環から水素原子２個を除いた残りの原子団からなる基をいう。２価の芳香族炭化水素基は、炭素数６～６０であると好ましく、６～２０であるとより好ましい。縮合環としては、例えば、ナフタレン環、アントラセン環、テトラセン環、ペンタセン環、ピレン環、ペリレン環、フルオレン環が挙げられる。
２価の芳香族炭化水素基としては、ベンゼン環、ペンタセン環、ピレン環又はフルオレン環から水素原子２個を除いた残りの原子団からなる基が好ましい。なお、２価の芳香族炭化水素基は、置換基を更に有していてもよい。その場合、２価の芳香族炭化水素基の炭素数には、置換基の炭素数は含まれない。置換基としては、ハロゲン原子、飽和若しくは不飽和炭化水素基、アリール基、アルコキシ基、アリールオキシ基、１価の複素環基、アミノ基、ニトロ基、シアノ基が挙げられる。
一方、２価の複素環基とは、複素環式化合物から水素原子２個を除いた残りの原子団からなる基をいう。２価の複素環基は、炭素数が３～６０であると好ましく、３～２０であるとより好ましい。２価の複素環基としては、例えば、チオフェン環、チエノチオフェン環、ジチエノチオフェン環等のチオフェン環が２～６個縮環した化合物、チアゾール環、ピロール環、ピリジン環、ピリミジン環、ピラジン環、トリアジン環から水素原子２個を除いた残りの原子団からなる基が挙げられる。好ましくは、チオフェン環、チエノチオフェン環、ジチエノチオフェン環等のチオフェン環が２～６個縮環した化合物から水素原子２個を除いた残りの原子団からなる基である。特に、チオフェン環、チエノチオフェン環から水素原子２個を除いた残りの原子団からなる基が好ましい。
２価の複素環基は、置換基を更に有していてもよい。その場合、２価の複素環基の炭素数には、置換基の炭素数は含まれない。置換基としては、ハロゲン原子、飽和若しくは不飽和炭化水素基、アリール基、アルコキシ基、アリールオキシ基、１価の複素環基、アミノ基、ニトロ基、シアノ基が挙げられる。
上述したような本実施形態の共役系化合物としては、以下の化学式で示される化合物が例示できる。
Figure JPOXMLDOC01-appb-C000024
Figure JPOXMLDOC01-appb-C000025
Figure JPOXMLDOC01-appb-C000026
Figure JPOXMLDOC01-appb-C000027
Figure JPOXMLDOC01-appb-C000028
Figure JPOXMLDOC01-appb-C000029
これらの化学式におけるＲ００は、上述したＲ０１又はＲ０２と同義である。Ｒ＊は、水素原子、炭素数３～２４のアルキル基、炭素数３～２４のフルオロアルキル基、炭素数３～２４のアルコキシ基、又は炭素数１～２０のフルオロアルコキシ基を示し、水素原子又は炭素数３～２４のアルキル基が好ましく、水素原子又は炭素数６～２０のアルキル基がより好ましい。なお、分子中に複数のＲ００やＲ＊が存在する場合、それらはそれぞれ同一でも異なっていてもよい。
［共役系化合物の製造方法］
　上述したような好適な実施形態の共役系化合物は、上記の構造が得られる限り、どのような方法により製造してもよい。好適な製造方法としては、以下の例が挙げられる。なお、以下の製造方法における反応条件や反応試薬等は、下記の例示以外にも選択することが可能である。
以下の例では、式（Ｉ）において、Ａｒ０が、Ｘ３として酸素原子を有する式（ＩＶ）で表される基であり、ｓ及びｔが０、すなわちＡｒ１及びＡｒ２が含まれず、且つ、Ｘ１１、Ｘ１２、Ｘ２１及びＸ２２として、いずれも両方のＡがシアノ基である式（ａ１）で表される基を有する共役系化合物を製造する方法の好適な実施形態について説明する。
共役系化合物の製造においては、まず、下記スキーム（Ｓ１）に示すように、式（ａａ）及び（ａ’）で表される出発原料を用い、それらを反応させて前駆体（ｂ）を製造し、得られた前駆体（ｂ）を、更にカルボニル架橋剤（ｃ）と反応させることによって、中間体（ｄ）を得る。
次いで、下記スキーム（Ｓ２）に示すように、化合物（ｆ）や（ｎ）の合成等を経由する反応を行って、化合物（ｏ）を得る。この反応では、まず、中間体（ｄ）を、アルコール（ｅ）と反応させて、中間体（ｄ）におけるカルボニル基が保護された化合物（ｆ）を形成する。なお、カルボニル基の保護は、例えば、アルコール（ｅ）に代え、２，２－ジブチル－１，３－プロペンジオール等を反応させてアセタール基を形成することによって行ってもよい。
それから、カルボニル基が保護された化合物（ｆ）に所定の反応活性基（Ｖ’’）を付与して化合物（ｈ）を得た後、これと末端基を形成するための原料化合物（ｎ）とを反応させて化合物（ｏ）を形成する。
Figure JPOXMLDOC01-appb-C000030
Figure JPOXMLDOC01-appb-C000031
スキーム（Ｓ１）及び（Ｓ２）中、Ｚ＊は、式（ＩＶ）中のＺ４又はＺ５を表し、Ｙ＊は、式（ＩＶ）中のＹ１又はＹ２を表す。Ｚ＊＊は、式（Ｉ）中のＺ１又はＺ２を表し、Ｒ＊は、式（Ｉ）中のＲ１１、Ｒ１２、Ｒ２１又はＲ２２を表し、Ｒ０＊は、式（Ｉ）中のＲ０１又はＲ０２を表す。
Ｖ、Ｖ’及びＶ”は、反応活性基を表し、それぞれ同一でも異なっていてもよい。反応活性基としては、例えば、ハロゲン原子、アルキルスルホネート基、アリールスルホネート基、アリールアルキルスルホネート基、アルキルスタニル基、アリールスタニル基、アリールアルキルスタニル基、ホウ酸エステル残基、スルホニウムメチル基、ホスホニウムメチル基、ホスホネートメチル基、モノハロゲン化メチル基、ホウ酸残基（－Ｂ（ＯＨ）２）、ホルミル基、ビニル基が挙げられる。ホウ酸エステル残基としては、下記の式で示される基が挙げられる。
Figure JPOXMLDOC01-appb-C000032
合成における反応性が良好になるので、Ｖ、Ｖ’及びＶ”はそれぞれ独立に、ハロゲン原子、アルキルスルホネート基、アリールスルホネート基、アリールアルキルスルホネート基、アルキルスタニル基、ホウ酸エステル残基又はホウ酸残基であることが好ましい。
また、Ｘ、Ｘ’、Ｘ”は、それぞれ独立にハロゲン原子を表し、Ｗ、Ｗ’及びＷ”は、それぞれ独立に脱離基を表す。脱離基としては、アミノ基、アルコキシ基が例示される。
そして、上記反応により得られた化合物（ｏ）から、カルボニル基の保護基を外してカルボニル化合物とすることにより、好適な実施形態に係る共役系化合物を得ることができる。なお、共役系化合物を用いて有機薄膜等を形成する場合は、必ずしもカルボニル基の保護基を外してから有機薄膜等の形成を行うのではなく、例えば、保護基を有した状態の化合物（化合物（ｏ）等）を用いて有機薄膜を形成した後に、有機薄膜となった状態で加熱等を行うことにより保護基を外し、これにより共役系化合物を含む有機薄膜中を形成してもよい。この場合、有機薄膜中には、特性に大きく影響しない限り、保護基が外れる前の状態の化合物又はその副生成物が残存していてもよい。
上記のような方法によって好適な実施形態の共役系化合物を得ることができるが、例えば、式（Ｉ）においてｓ及びｔが１以上である、すなわちＡｒ１及びＡｒ２を含む共役系化合物を形成する場合は、次のような製造方法を適用することができる。
この場合、まず、式（ｐ）（好ましくは、式（ｑ））で表される化合物と、式（ｒ）で表される化合物とを用いて、中間体である式（ｓ）（好ましくは、式（ｔ））で表される化合物（ｓ）又は化合物（ｔ）を生成する。そして、得られた化合物（ｓ）又は化合物（ｔ）と、上述したような末端基を形成するための原料化合物（ｎ）とを反応させることによって、式（ｒ）の化合物が有していたＡｒ＊＊に由来するＡｒ１及びＡｒ２で表される基を分子中に有する、すなわち、ｓ及びｔが１以上である、式（Ｉ）で表される共役系化合物を得ることができる。
Figure JPOXMLDOC01-appb-C000033
Figure JPOXMLDOC01-appb-C000034
上記の式中、Ａｒ＊は、式（Ｉ）におけるＡｒ０を示し、Ａｒ＊＊は、式（Ｉ）におけるＡｒ１又はＡｒ２を示す。また、Ｖ、Ｖ’及びＺ３は、それぞれ上記と同義である。式（ｐ）で表される化合物として式（ｑ）で表される化合物を用いる場合、この化合物は、例えば、Ｚ３を含む複素環に対応する複素環式化合物に、Ｖ及びＶ’で表される反応活性基を付与することによって得ることができる。式（ｐ）で表される化合物としては、上記の化合物（ｈ）も用いることができ、その場合は、上記と同様の方法により化合物（ｈ）を合成することができる。
上述したような共役系化合物の製造方法においては、例えば途中で化合物（ｆ）を合成するなどしてカルボニル基を保護したが、同様に、反応性の高い官能基に対しては、不要な反応を生じることを避けるために、その後の反応において不活性な官能基（保護基）に変換し、目的の反応の終了後に保護基を外す工程を行ってもよい。保護基は、保護する官能基や用いる反応に応じて選択することができる。例えば、活性水素の保護にはトリメチルシリル（ＴＭＳ）、トリエチルシリル（ＴＥＳ）、ｔｅｒｔ－ブチルジメチルシリル（ＴＢＳ又はＴＢＤＭＳ）、トリイソプロピルシリル（ＴＩＰＳ）、ｔｅｒｔ－ブチルジフェニルシリル（ＴＢＤＰＳ）を用いることが好ましい。
上述したような共役系化合物を合成するための各反応では、溶媒を用いてもよい。用いられる溶媒としては、なるべく目的の反応を阻害しないものが好ましい。例えば、ヘキサン等の脂肪族炭化水素、ベンゼン、トルエン等の芳香族炭化水素、アセトニトリル等のニトリル、ジエチルエーテル、テトラヒドロフラン、１，２－ジメトキシエタン等のエーテル、ジクロロメタン、１，２－ジクロロエタン、四塩化炭素等のハロゲン化溶媒等が挙げられる。これらは、単独で用いてもよく、２種類以上併用してもよい。好適な溶媒としては、例えばジクロロメタンが挙げられる。
そして、得られた共役系化合物を有機薄膜素子用の材料として用いる場合は、その純度が素子特性に影響を与えることもあるため、共役系化合物の合成後、得られた生成物を、蒸留、昇華精製、再結晶等の方法で純化処理することが好ましい。
［有機薄膜］
　次に好適な実施形態に係る有機薄膜について説明する。本実施形態の有機薄膜は、上述した好適な実施形態の共役系化合物を含むものである。
有機薄膜の厚さは、１ｎｍ～１００μｍであると好ましく、２ｎｍ～１０００ｎｍであるとより好ましく、５ｎｍ～５００ｎｍであると更に好ましく、２０ｎｍ～２００ｎｍであると一層好ましい。
有機薄膜は、好適な実施形態の共役系化合物の１種類を単独で含むものであってもよく、また共役系化合物の２種類以上を含むものであってもよい。また、有機薄膜は、その電子輸送性又はホール輸送性を高めるために、共役系化合物以外に、電子輸送性若しくはホール輸送性を有する低分子化合物又は高分子化合物（これらの低分子化合物及び高分子化合物を総称して、「電子輸送性材料」、「ホール輸送性材料」という。）を混合して用いることもできる。
ホール輸送性材料としては、公知のものが使用できる。例えば、ピラゾリン誘導体、アリールアミン誘導体、スチルベン誘導体、トリアリールジアミン誘導体、オリゴチオフェン及びその誘導体、ポリビニルカルバゾール及びその誘導体、ポリシラン及びその誘導体、側鎖若しくは主鎖に芳香族アミンを有するポリシロキサン誘導体、ポリアニリン及びその誘導体、ポリチオフェン及びその誘導体、ポリピロール及びその誘導体、ポリアリーレンビニレン及びその誘導体、ポリチエニレンビニレン及びその誘導体が挙げられる。
電子輸送性材料としては、公知のものが使用できる。例えば、オキサジアゾール誘導体、アントラキノジメタン及びその誘導体、ベンゾキノン及びその誘導体、ナフトキノン及びその誘導体、アントラキノン及びその誘導体、テトラシアノアンスラキノジメタン及びその誘導体、フルオレノン誘導体、ジフェニルジシアノエチレン及びその誘導体、ジフェノキノン誘導体、又は８－ヒドロキシキノリン及びその誘導体の金属錯体、ポリキノリン及びその誘導体、ポリキノキサリン及びその誘導体、ポリフルオレン及びその誘導体、Ｃ６０等のフラーレン類及びその誘導体が挙げられる。
また、有機薄膜は、有機薄膜中で吸収した光により電荷を発生させるために、電荷発生材料を含んでいてもよい。電荷発生材料としては、公知のものが使用できる。例えば、アゾ化合物及びその誘導体、ジアゾ化合物及びその誘導体、無金属フタロシアニン化合物及びその誘導体、金属フタロシアニン化合物及びその誘導体、ペリレン化合物及びその誘導体、多環キノン系化合物及びその誘導体、スクアリリウム化合物及びその誘導体、アズレニウム化合物及びその誘導体、チアピリリウム化合物及びその誘導体、Ｃ６０等のフラーレン類及びその誘導体が挙げられる。
さらに、有機薄膜は、種々の機能を発現させるために必要な材料を含んでいてもよい。このような材料としては、例えば、吸収した光により電荷を発生させる機能を増感するためのため増感剤、安定性を増すための安定化剤、紫外（ＵＶ）光を吸収するためのＵＶ吸収剤が挙げられる。
また、有機薄膜は、機械的特性を高めるため、上述した実施形態の共役系化合物以外の高分子化合物材料を高分子バインダーとして含んでいてもよい。高分子バインダーとしては、電子輸送性又はホール輸送性を極度に阻害しないものが好ましく、また可視光に対する吸収が強くないものが好ましく用いられる。
このような高分子バインダーとして、ポリ（Ｎ－ビニルカルバゾール）、ポリアニリン及びその誘導体、ポリチオフェン及びその誘導体、ポリ（ｐ－フェニレンビニレン）及びその誘導体、ポリ（２，５－チエニレンビニレン）及びその誘導体、ポリカーボネート、ポリアクリレート、ポリメチルアクリレート、ポリメチルメタクリレート、ポリスチレン、ポリ塩化ビニル、ポリシロキサンが例示される。
有機薄膜の製造方法としては、例えば、共役系化合物、必要に応じて混合する電子輸送性材料又はホール輸送性材料、高分子バインダーを含む溶液を用いた成膜による方法が挙げられる。また、共役系化合物が昇華性を有する場合は、真空蒸着法により薄膜を形成することもできる。
溶液を用いた成膜に用いる溶媒としては、共役系化合物やその他混合する電子輸送性材料又はホール輸送性材料、高分子バインダーを溶解させるものであればよい。溶媒としては、トルエン、キシレン、メシチレン、テトラリン、デカリン、ビシクロヘキシル、ｎ－ブチルベンゼン、ｓｅｃ－ブチルベンゼン、ｔｅｒｔ－ブチルベンゼン等の不飽和炭化水素系溶媒、四塩化炭素、クロロホルム、ジクロロメタン、ジクロロエタン、クロロブタン、ブロモブタン、クロロペンタン、ブロモペンタン、クロロヘキサン、ブロモヘキサン、クロロシクロヘキサン、ブロモシクロヘキサン等のハロゲン化飽和炭化水素系溶媒、クロロベンゼン、ジクロロベンゼン、トリクロロベンゼン等のハロゲン化不飽和炭化水素系溶媒、テトラヒドロフラン、テトラヒドロピラン等のエーテル類系溶媒が例示される。共役系化合物は、その構造や分子量にもよるが、例えば、これらの溶媒に０．１質量％以上溶解させることができる。
溶液を用いた成膜方法としては、スピンコート法、キャスティング法、マイクログラビアコート法、グラビアコート法、バーコート法、ロールコート法、ワイアーバーコート法、ディップコート法、スプレーコート法、スクリーン印刷法、フレキソ印刷法、オフセット印刷法、インクジェット印刷法、ディスペンサー印刷法、ノズルコート法及びキャピラリーコート法等の塗布法を用いることができる。なかでも、スピンコート法、フレキソ印刷法、インクジェット印刷法、ディスペンサー印刷法、ノズルコート法及びキャピラリーコート法が好ましい。
有機薄膜を製造する工程には、共役系化合物を配向させる工程が含まれていてもよい。このような工程を行うことで、有機薄膜においては、共役系化合物の主鎖又は側鎖が一方向に並ぶので、電荷移動度が更に向上する傾向にある。
共役系化合物を配向させる方法としては、液晶の配向手法として知られている方法を用いることができる。中でもラビング法、光配向法、シェアリング法（ずり応力印加法）や引き上げ塗布法が配向手法として簡便かつ有用で利用しやすく、ラビング法、シェアリング法が好ましい。
また、有機薄膜を製造する工程には、成膜後にアニール処理をする工程が含まれていてもよい。この工程により、共役系化合物間の相互作用が促進される等、有機薄膜の膜質が改善され、電荷移動度が向上する。アニール処理の処理温度としては、５０℃から共役系化合物のガラス転移温度（Ｔｇ）付近の間の温度が好ましく、（Ｔｇ－３０℃）からＴｇの間の温度がより好ましい。アニール処理する時間としては、１分から１０時間が好ましく、１０分から１時間がより好ましい。アニール処理する雰囲気としては、真空中又は不活性ガス雰囲気中が好ましい。
好適な実施形態の共役系化合物を含む有機薄膜は、優れた電子輸送性を有することから、電極から注入された電子や、光吸収により発生した電荷を輸送制御することができ、その特性により、有機薄膜トランジスタ、有機薄膜太陽電池、光センサ等、種々の有機薄膜素子に用いることができる。有機薄膜をこれらの有機薄膜素子に用いる場合は、配向処理により配向させて用いることが電子輸送性より向上するため好ましい。
［有機薄膜素子］
　上述した有機薄膜は、上述したような好適な実施形態の共役系化合物を含むことから、優れた電荷（特に電子）輸送性を有するものとなる。したがって、この有機薄膜は、各種の電気素子（有機薄膜素子）に応用することができる。また、上記の共役系化合物は、環境安定性に優れているため、これらを用いて薄膜を形成することで、通常の大気中においても性能が安定している有機薄膜素子を製造することが可能となる。以下、有機薄膜素子の例についてそれぞれ説明する。
（有機薄膜トランジスタ）
　まず、好適な実施形態の有機薄膜トランジスタは、上述した好適な実施形態の共役化合物を備えるものである。以下、好適な実施形態に係る有機薄膜トランジスタについて説明する。好適な実施形態に係る有機薄膜トランジスタは、ソース電極及びドレイン電極、これらの間の電流経路となり好適な実施形態の共役系化合物を含む活性層（有機薄膜層）、電流経路を通る電流量を制御するゲート電極を備えた構造であればよく、電界効果型、静電誘導型が例示される。
電界効果型有機薄膜トランジスタは、ソース電極及びドレイン電極、これらの間の電流経路となり好適な実施形態の共役系化合物を含む活性層、電流経路を通る電流量を制御するゲート電極、並びに、活性層とゲート電極との間に配置される絶縁層を備えることが好ましい。特に、ソース電極及びドレイン電極が、好適な実施形態の共役系化合物を含む活性層に接して設けられており、さらに活性層に接した絶縁層を挟んでゲート電極が設けられていることが好ましい。
静電誘導型有機薄膜トランジスタは、ソース電極及びドレイン電極、これらの間の電流経路となり好適な実施形態の共役系化合物を含有する活性層、並びに電流経路を通る電流量を制御するゲート電極を有し、該ゲート電極が活性層中に設けられていることが好ましい。特に、ソース電極、ドレイン電極及び有機薄膜層中に設けられたゲート電極が、好適な実施形態の共役系化合物を含有する活性層に接して設けられていることが好ましい。ゲート電極の構造としては、ソース電極からドレイン電極へ流れる電流経路が形成され、かつゲート電極に印加した電圧で電流経路を流れる電流量が制御できる構造であればよく、例えば、くし形電極が挙げられる。
図１は第１実施形態に係る有機薄膜トランジスタ（電界効果型有機薄膜トランジスタ）の模式断面図である。図１に示す有機薄膜トランジスタ１００は、基板１と、基板１上に所定の間隔を持って形成されたソース電極５及びドレイン電極６と、ソース電極５及びドレイン電極６を覆うようにして基板１上に形成された活性層２と、活性層２上に形成された絶縁層３と、ソース電極５とドレイン電極６との間の絶縁層３の領域を覆うように絶縁層３上に形成されたゲート電極４と、を備えるものである。
図２は第２実施形態に係る有機薄膜トランジスタ（電界効果型有機薄膜トランジスタ）の模式断面図である。図２に示す有機薄膜トランジスタ１１０は、基板１と、基板１上に形成されたソース電極５と、ソース電極５を覆うようにして基板１上に形成された活性層２と、ソース電極５と所定の間隔を持って活性層２上に形成されたドレイン電極６と、活性層２及びドレイン電極６上に形成された絶縁層３と、ソース電極５とドレイン電極６との間の絶縁層３の領域を覆うように絶縁層３上に形成されたゲート電極４と、を備えるものである。
図３は、第３の実施形態に係る有機薄膜トランジスタ（電界効果型有機薄膜トランジスタ）の模式断面図である。図３に示す有機薄膜トランジスタ１２０は、基板１と、基板１上に形成された活性層２と、活性層２上に所定の間隔を持って形成されたソース電極５及びドレイン電極６と、ソース電極５及びドレイン電極６を一部覆うようにして活性層２上に形成された絶縁層３と、ソース電極５が下部に形成されている絶縁層３の領域とドレイン電極６が下部に形成されている絶縁層３の領域とをそれぞれ一部覆うように、絶縁層３上に形成されたゲート電極４と、を備えるものである。
図４は第４実施形態に係る有機薄膜トランジスタ（電界効果型有機薄膜トランジスタ）の模式断面図である。図４に示す有機薄膜トランジスタ１３０は、基板１と、基板１上に形成されたゲート電極４と、ゲート電極４を覆うようにして基板１上に形成された絶縁層３と、ゲート電極４が下部に形成されている絶縁層３の領域を一部覆うように、絶縁層３上に所定の間隔を持って形成されたソース電極５及びドレイン電極６と、ソース電極５及びドレイン電極６を一部覆うように絶縁層３上に形成された活性層２と、を備えるものである。
図５は第５実施形態に係る有機薄膜トランジスタ（電界効果型有機薄膜トランジスタ）の模式断面図である。図５に示す有機薄膜トランジスタ１４０は、基板１と、基板１上に形成されたゲート電極４と、ゲート電極４を覆うようにして基板１上に形成された絶縁層３と、ゲート電極４が下部に形成されている絶縁層３の領域を一部覆うように絶縁層３上に形成されたソース電極５と、ソース電極５を一部覆うようにして絶縁層３上に形成された活性層２と、ゲート電極４が下部に形成されている活性層２の領域を一部覆うように、ソース電極５と所定の間隔を持って絶縁層３上に形成されたドレイン電極６と、を備えるものである。
図６は第６実施形態に係る有機薄膜トランジスタ（電界効果型有機薄膜トランジスタ）の模式断面図である。図６に示す有機薄膜トランジスタ１５０は、基板１と、基板１上に形成されたゲート電極４と、ゲート電極４を覆うようにして基板１上に形成された絶縁層３と、ゲート電極４が下部に形成されている絶縁層３の領域を覆うように形成された活性層２と、ゲート電極４が下部に形成されている活性層２の領域を一部覆うように絶縁層３上に形成されたソース電極５と、ゲート電極４が下部に形成されている活性層２の領域を一部覆うように、ソース電極５と所定の間隔を持って絶縁層３上に形成されたドレイン電極６と、を備えるものである。
図７は第７実施形態に係る有機薄膜トランジスタ（静電誘導型有機薄膜トランジスタ）の模式断面図である。図７に示す有機薄膜トランジスタ１６０は、基板１と、基板１上に形成されたソース電極５と、ソース電極５上に形成された活性層２と、活性層２上に所定の間隔を持って複数形成されたゲート電極４と、ゲート電極４の全てを覆うようにして活性層２上に形成された活性層２ａ（活性層２ａを構成する材料は、活性層２と同一でも異なっていてもよい）と、活性層２ａ上に形成されたドレイン電極６と、を備えるものである。
第１～第７実施形態に係る有機薄膜トランジスタにおいては、活性層２及び／又は活性層２ａは、好適な実施形態の共役系化合物を含有しており、ソース電極５とドレイン電極６の間の電流通路（チャネル）となる。また、ゲート電極４は、電圧を印加することにより活性層２及び／又は活性層２ａにおける電流通路（チャネル）を通る電流量を制御する。
このような電界効果型有機薄膜トランジスタは、公知の方法、例えば特開平５－１１００６９号公報記載の方法により製造することができる。また、静電誘導型有機薄膜トランジスタは、公知の方法、例えば特開２００４－００６４７６号公報記載の方法により製造することができる。
基板１としては有機薄膜トランジスタとしての特性を阻害しない材質のものであればよく、ガラス基板やフレキシブルなフィルム基板やプラスチック基板を用いることができる。
活性層２を形成する際に、有機溶媒可溶性の化合物を用いることが製造上非常に有利であり好ましいことから、上記で説明した有機薄膜の製造方法を用いて、活性層２となる有機薄膜を形成することができる。
活性層２に接した絶縁層３としては、電気の絶縁性が高い材料であればよく、公知のものを用いることができる。例えば、ＳｉＯｘ，ＳｉＮｘ、Ｔａ２Ｏ５、ポリイミド、ポリビニルアルコール、ポリビニルフェノール、有機ガラス及びフォトレジストが挙げられる。低電圧化できるので、誘電率の高い材料の方が好ましい。
絶縁層３の上に活性層２を形成する場合は、絶縁層３と活性層２の界面特性を改善するため、シランカップリング剤等の表面処理剤で絶縁層３の表面を処理して表面改質した後に活性層２を形成することも可能である。表面処理剤としては、例えば、長鎖アルキルクロロシラン類、長鎖アルキルアルコキシシラン類、フッ素化アルキルクロロシラン類、フッ素化アルキルアルコキシシラン類、ヘキサメチルジシラザン等のシリルアミン化合物が挙げられる。表面処理剤で処理する前に、絶縁層表面をオゾンＵＶ、Ｏ２プラズマで処理をしておくことも可能である。
また、有機薄膜トランジスタを作製後、素子を保護するために有機薄膜トランジスタ上に保護膜を形成することが好ましい。これにより、有機薄膜トランジスタが、大気から遮断され、有機薄膜トランジスタの特性の低下を抑えることができる。また、保護膜により有機薄膜トランジスタの上に駆動する表示デバイスを形成する工程からの影響を低減することができる。
保護膜を形成する方法としては、例えば、ＵＶ硬化樹脂、熱硬化樹脂又は無機のＳｉＯＮｘ膜でカバーする方法が挙げられる。大気との遮断を効果的に行うため、有機薄膜トランジスタを作製後、保護膜を形成するまでの工程を大気に曝すことなく（例えば、乾燥した窒素雰囲気中、真空中）行うことが好ましい。
（有機薄膜太陽電池）
　次に、有機薄膜太陽電池への応用を説明する。図８は、実施形態に係る有機薄膜太陽電池の模式断面図である。図８に示す有機薄膜太陽電池２００は、基板１と、基板１上に形成された第１の電極７ａと、第１の電極７ａ上に形成された好適な実施形態の共役系化合物を含有する有機薄膜からなる活性層２と、活性層２上に形成された第２の電極７ｂと、を備えるものである。
本実施形態に係る有機薄膜太陽電池においては、第１の電極７ａ及び第２の電極７ｂの一方に透明又は半透明の電極を用いる。電極材料としては、アルミニウム、金、銀、銅、アルカリ金属、アルカリ土類金属等の金属又はそれらの半透明膜、透明導電膜を用いることができる。高い開放電圧を得るためには、それぞれの電極として、仕事関数の差が大きくなるように選ばれることが好ましい。活性層２中には光感度を高めるために電荷発生剤、増感剤等を添加して用いることができる。基材１としては、シリコン基板、ガラス基板、プラスチック基板等を用いることができる。
（光センサ）
　次に、有機薄膜の光センサへの応用を説明する。図９は、第１実施形態に係る光センサの模式断面図である。図９に示す光センサ３００は、基板１と、基板１上に形成された第１の電極７ａと、第１の電極７ａ上に形成された好適な実施形態の共役系化合物を含有する有機薄膜からなる活性層２と、活性層２上に形成された電荷発生層８と、電荷発生層８上に形成された第２の電極７ｂと、を備えるものである。
図１０は、第２実施形態に係る光センサの模式断面図である。図１０に示す光センサ３１０は、基板１と、基板１上に形成された第１の電極７ａと、第１の電極７ａ上に形成された電荷発生層８と、電荷発生層８上に形成された好適な実施形態の共役系化合物を含有する有機薄膜からなる活性層２と、活性層２上に形成された第２の電極７ｂと、を備えるものである。
図１１は、第３実施形態に係る光センサの模式断面図である。図１１に示す光センサ３２０は、基板１と、基板１上に形成された第１の電極７ａと、第１の電極７ａ上に形成された好適な実施形態の共役系化合物を含有する有機薄膜からなる活性層２と、活性層２上に形成された第２の電極７ｂと、を備えるものである。
第１～第３実施形態に係る光センサにおいては、第１の電極７ａ及び第２の電極７ｂの一方に透明又は半透明の電極を用いる。電荷発生層８は光を吸収して電荷を発生する層である。電極材料としては、アルミニウム、金、銀、銅、アルカリ金属、アルカリ土類金属等の金属又はそれらの半透明膜、透明導電膜を用いることができる。活性層２中には光感度を高めるためにキャリア発生剤、増感剤等を添加して用いることができる。また基材１としては、シリコン基板、ガラス基板、プラスチック基板等を用いることができる。
以上、本発明をその実施形態に基づいて詳細に説明した。しかし、本発明は上記実施形態に限定されるものではない。本発明は、その要旨を逸脱しない範囲で様々な変形が可能である。
以下、実施例及び比較例に基づいて本発明をさらに詳細に説明するが、本発明は以下の実施例に何ら限定されるものではない。
（測定条件等）
　まず、以下の実施例及び比較例で行った測定の条件について説明する。核磁気共鳴（ＮＭＲ）スペクトルは、ＪＥＯＬ（日本電子株式会社）製の商品名ＪＭＮ－２７０（１Ｈ測定時４００ＭＨｚ）、又は同社製の商品名ＪＭＮＬＡ－６００（１９Ｆ測定時６００ＭＨｚ）を用いて測定した。その結果において、ケミカルシフトは百万分率（ｐｐｍ）で表している。内部標準０ｐｐｍには、テトラメチルシラン（ＴＭＳ）を用いた。結合定数（Ｊ）は、ヘルツで示しており、略号ｓ、ｄ、ｔ、ｑ、ｍ及びｂｒは、それぞれ、一重線（ｓｉｎｇｌｅｔ）、二重線（ｄｏｕｂｌｅｔ）、三重線（ｔｒｉｐｌｅｔ）、四重線（ｑｕａｒｔｅｔ）、多重線（ｍｕｌｔｉｐｌｅｔ）及び広幅線（ｂｒｏａｄ）を表す。
また、質量分析（ＭＳ）は、株式会社島津製作所製のＧＣＭＳ－ＱＰ５０５０Ａ（商品名）を用い、電子イオン化（ＥＩ）法、直接試料導入（ＤＩ）法により行った。カラムクロマトグラフィー分離におけるシリカゲルは、関東化学株式会社製の商品名Ｓｉｌｉｃａｇｅｌ　６０Ｎ（４０～５０μｍ）を用いた。全ての化学物質は、試薬級であり、和光純薬工業株式会社、東京化成工業株式会社、関東化学株式会社、ナカライテスク株式会社、シグマアルドリッチジャパン株式会社、又はダイキン化成品株式会社より購入した。
さらに、マイクロウェーブ照射下での反応は、Ｂｉｏｔａｇｅ　ＡＢ社製のＩｎｉｔｉａｔｏｒＴＭ　Ｖｅｒ．２．５を用い、出力４００Ｗ、２．４５ＧＨｚで行った。サイクリックボルタンメトリー（ＣＶ）は、測定装置としてビー・エー・エス株式会社（ＢＡＳ社）製の商品名「ＣＶ－５０Ｗ」を使用し、作用電極としてＢＡＳ社製Ｐｔ電極、対電極としてＰｔ線、参照電極としてＡｇ線を用いて測定した。この測定時の掃引速度は１００ｍＶ／ｓ、走査電位領域は－２．８Ｖ～１．６Ｖであった。還元電位及び酸化電位の測定は、化合物及び重合体を１×１０－３ｍｏｌ／Ｌ、支持電解質としてテトラブチルアンモニウムヘキサフルオロフォスフェート（ＴＢＡＰＦ６）０．１ｍｏｌ／Ｌをモノフルオロベンゼン溶媒に完全に溶解し測定した。
［実施例１：共役系化合物（Ｅ）の合成］
　以下に示す各種の中間体の合成を経て、共役系化合物（Ｅ）を合成した。
（化合物（Ｂ）の合成）
　まず、以下の反応を行って、末端基を形成するための原料化合物である化合物（Ｂ）を合成した。
すなわち、Ｊ．　Ｏｒｇ．　Ｃｈｅｍ．　２００６，　７１，　９４７５－９４８３に記載された方法で合成した化合物（Ａ－１）を原料にして、下記のスキームにしたがった反応を行い、中間体である化合物（Ａ－３）を合成した。
Figure JPOXMLDOC01-appb-C000035
ここで、化合物（Ａ－３）の合成では、まず、５０ｍＬの３つ口フラスコに化合物（Ａ－１）（１ｇ，３．４３ｍｍｏｌ）及び塩化チオニル（ＳＯＣｌ２）（１ｍＬ，１３．７４ｍｍｏｌ）を加え、１時間還流させた後、ＳＯＣｌ２を留去した。室温で、ニトロベンゼン（ＰｈＮＯ２）を４０ｍＬ加え、さらにマロニルクロライド（５３２ｍｇ，３．７８ｍｍｏｌ）、及び、塩化アルミニウム（１．３７ｇ，１３．７２ｍｍｏｌ）を加えて８０℃に昇温し、それらを４時間攪拌した。それから、１０重量％シュウ酸溶液を加えて反応を停止させた後、反応液を水洗し、酢酸エチルで抽出した。得られた有機層を硫酸ナトリウムで乾燥させて、溶媒を留去した後、真空乾燥した。得られた生成物を、シリカゲルカラム（ヘキサン／酢酸エチル＝１０／１（容積比））で精製を行い、中間体である白色固体の化合物（Ａ－２）（６０６ｍｇ，収率５６％）を得た。
１００ｍｌのナスフラスコに、化合物（Ａ－２）（６０６ｍｇ，１．９２ｍｍｏｌ）、及びフッ素化剤「ＳｅｌｅｃｔｆｌｕｏｒＴＭ（登録商標）」（１．６３ｇ，４．６１ｍｍｏｌ）を入れ、これにテトラヒドロフラン（ＴＨＦ）（３０ｍＬ）を加えて溶かした。そこに、テトラブチルアンモニウムハイドロオキサイド（ＴＢＡＨ）（１０重量％メタノール溶液）（１９．９４ｇ，４．６１ｍｍｏｌ）を加えて、０℃で２時間攪拌した後に、室温まで昇温した。攪拌後の溶液を水洗した後、酢酸エチルを用いて抽出した。得られた有機層を硫酸ナトリウムで乾燥させ、溶媒を留去した後、真空乾燥した。得られた生成物を、シリカゲルカラム（ヘキサン／酢酸エチル＝１０／１（容積比））により精製し、中間体である白色固体の化合物（Ａ－３）（５２７ｍｇ，収率７８％）を得た。
このようにして化合物（Ａ－３）を合成した後、１００ｍＬナスフラスコに、得られた化合物（Ａ－３）（１．０９ｇ，３．１０ｍｍｏｌ）、マロノニトリル（４０９ｍｇ，６．２０ｍｍｏｌ）、酢酸アンモニウム（３５８ｍｇ，４．６４ｍｍｏｌ）、トルエン（４０ｍＬ）、及び、酢酸（４ｍＬ）を加え、４時間還流させた。還流後の溶液を水洗した後、酢酸エチルを用いて抽出した。得られた有機層を硫酸ナトリウムで乾燥させ、溶媒を留去した後、真空乾燥した。そして、得られた生成物を、シリカゲルカラム（ヘキサン／酢酸エチル＝１０／１（容積比））により精製して、目的物である緑色固体の化合物（Ｂ）（６２７ｍｇ，収率５０％）を得た。化合物（Ｂ）の分析結果及び化学式は以下の通りである。
　ＴＬＣ　Ｒｆ＝０．５（ヘキサン／酢酸エチル＝１０／１（容積比））
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝０．９０（ｍ，３Ｈ），１．３４（ｍ，６Ｈ），１．６２（ｍ，２Ｈ），２．８９（ｍ，２Ｈ）
　ＧＣ－ＭＳ（ＤＩ）：ｍ／ｚ＝３９８（Ｍ＋）
Figure JPOXMLDOC01-appb-C000036
（化合物（Ｄ）の合成）
　まず、共役系化合物の中央部分を構成するための原料となる化合物（Ｃ）を、Ｐｈｉｌｉｐｐｅ　Ｌｕｃａｓ　ｅｔ　ａｌ．　Ｓｙｎｔｈｅｓｉｓ，　２０００　Ｎｏ．９　ｐ．１２５３．及びＭｙｕｎｇ－Ｈａｎ　Ｙｏｏｎ　ｅｔ　ａｌ．，　Ｃｈｅｍｉｓｔｒｙ　Ｍａｔｅｒｉａｌｓ　ｖｏｌ．１９　（２００７）　ｐ．４８６４．に記載された方法にしたがって合成した。
Figure JPOXMLDOC01-appb-C000037
次いで、５ｍＬの試験管に、上記で得られた化合物（Ｂ）（２１５ｍｇ，０．５４ｍｍｏｌ）、化合物（Ｃ）（２００ｍｇ，０．２５ｍｍｏｌ）、トリス（ジベンジリデンアセトン）ジパラジウム（０）（Ｐｄ２（ｄｂａ）３）（１２ｍｇ，０．０１３ｍｍｏｌ）、トリ－ｏ－トリルホスフィン（８ｍｇ，０．０２６ｍｍｏｌ）、及び、クロロベンゼン（３ｍＬ）を入れ、マイクロウェーブ照射下でそれらを反応させた（１８０℃，５分）。反応後の生成物を、シリカゲルカラム（クロロホルム）及びゲルパーミエーションクロマトグラフ（ＧＰＣ）を用いて精製して、目的物である濃青黒色固体の化合物（Ｄ）（１４２ｍｇ，収率６６％）を得た。化合物（Ｄ）の分析結果及び化学式は以下の通りである。
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝０．９７（ｍ，６Ｈ），１．３５（ｍ），１．４７（ｍ），１．６７（ｍ），３．１１（ｍ，４Ｈ），４．４２（ｓ，４Ｈ），７．３９（ｓ，２Ｈ）
　ＭＡＬＤＩ　ＴＯＦＭＳ：ｍ／ｚ＝８７２
Figure JPOXMLDOC01-appb-C000038
（共役系化合物（Ｅ）の合成）
　ふた付き試験管に、上記で得られた化合物（Ｄ）（１４２ｍｇ，０．１６ｍｍｏｌ）、塩酸（０．５ｍＬ）、及び、酢酸（４ｍＬ）を入れ、１００℃で一晩攪拌した。攪拌後の溶液を水洗した後、ジクロロメタンを用いて抽出した。得られた有機層を硫酸ナトリウムで乾燥させ、溶媒を留去した後、真空乾燥した。得られた生成物を、シリカゲルカラム（クロロホルム）及びＧＰＣにより精製して、目的物である濃青黒色固体の共役系化合物（Ｅ）（１１８ｍｇ，収率８８％）を得た。共役系化合物（Ｅ）の分析結果及び化学式は以下の通りである。
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝０．９１（ｍ，６Ｈ），０．９７（ｍ），１．３５（ｍ），１．４７（ｍ），１．６７（ｍ），３．０８（ｍ，４Ｈ），７．４４（ｓ，２Ｈ）
　ＭＡＬＤＩ　ＴＯＦＭＳ：ｍ／ｚ＝８２８
Figure JPOXMLDOC01-appb-C000039
得られた共役系化合物（Ｅ）について、ＣＶ測定を行ったところ、－０．８２Ｖ及び＋１．０４Ｖにそれぞれ可逆な還元波及び酸化波が観測された。還元波よりＬＵＭＯレベルが低くなっていることが確認できた。
［実施例２：共役系化合物（Ｇ）の合成］
　上記で得た化合物（Ｂ）を用いて、共役系化合物（Ｇ）を合成した。
（共役系化合物（Ｇ）の合成）
　まず、原料となる５，５’－ビス（トリ－ｎ－ブチルスタニル）－２，２’－ジチオフェン（化合物（Ｆ））をＪｉａ　Ｈｕａｎｇ　ｅｔ　ａｌ．，　Ｊ．　Ａｍ．　Ｃｈｅｍ．　Ｓｏｃ．，　ｖｏｌ．１２９　（２００７）　ｐ．９３６６．に記載された方法にしたがって合成した。
次に、５ｍＬの試験管に、上記で得られた化合物（Ｂ）（１４８ｍｇ，０．３７ｍｍｏｌ）、化合物（Ｆ）（１２４ｍｇ，０．１７ｍｍｏｌ）、Ｐｄ２（ｄｂａ）３（７ｍｇ，０．００８ｍｍｏｌ）、トリ－ｏ－トリルホスフィン（５ｍｇ，０．０１６ｍｍｏｌ）、及び、クロロベンゼン（３ｍＬ）を入れ、マイクロウェーブ照射下でそれらを反応させた（１８０℃，５分）。得られた生成物を、シリカゲルカラム（クロロホルム）及びＧＰＣにより精製して、目的物である濃青黒色固体の共役系化合物（Ｇ）（９３ｍｇ，収率７０％）を得た。共役系化合物（Ｇ）の分析結果及び化学式は以下の通りである。
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝０．９１（ｍ，６Ｈ），１．３５（ｍ），１．４７（ｍ），１．６９（ｍ），３．１２（ｍ，４Ｈ），７．３９（ｍ，２Ｈ），７．４９（ｍ，２Ｈ）
　ＭＡＬＤＩ　ＴＯＦＭＳ：ｍ／ｚ＝８０２
Figure JPOXMLDOC01-appb-C000040
共役系化合物（Ｇ）について、ＣＶ測定を行ったところ、－０．８６Ｖ及び＋１．０６Ｖにそれぞれ可逆な還元波及び酸化波が観測された。還元波から見積もったＬＵＭＯエネルギーは－３．９４ｅＶであり、ＬＵＭＯレベルが低くなっていることが確認できた。
［実施例３：共役系化合物（Ｊ）の合成］
　以下に示す各種の中間体の合成を経て、共役系化合物（Ｊ）を合成する。
（化合物Ｉの合成）
　まず、共役系化合物の中央部分を構成するための原料となる化合物（Ｈ）をＹｕｔａｋａ　Ｉｅ　ｅｔ　ａｌ．，　Ａｄｖａｎｃｅｄ　Ｆｕｎｃｔｉｏｎａｌ　Ｍａｔｅｒｉａｌｓ，　ｖｏｌ．２０　（２０１０）　ｐ．９０７．に記載の方法にしたがって合成する。
Figure JPOXMLDOC01-appb-C000041
次いで、５ｍＬの試験管に上記で得られた化合物（Ｂ）、化合物（Ｈ）、Ｐｄ２（ｄｂａ）３、トリ－ｏ－トリルホスフィン、及び、クロロベンゼンを入れ、それらをマイクロウェーブ照射下で反応させる。そして、得られた生成物を、シリカゲルカラム（クロロホルム）及びＧＰＣにより精製して、目的物である化合物（Ｉ）を得る。
Figure JPOXMLDOC01-appb-C000042
（共役系化合物（Ｊ）の合成）
　ふた付き試験管に、塩酸と酢酸を入れ１００℃で一晩攪拌する。攪拌後の溶液を水洗した後、ジクロロメタンを用いた抽出を行う。得られた有機層を硫酸ナトリウムで乾燥させ、溶媒を留去した後、真空乾燥する。得られた生成物を、シリカゲルカラム（クロロホルム）及びＧＰＣにより精製して、目的物である共役系化合物（Ｊ）を得る。
Figure JPOXMLDOC01-appb-C000043
［実施例４：有機トランジスタ素子１の作製及びトランジスタ特性の評価］
　ゲート電極となる高濃度にドープされたｐ型シリコン基板の表面に、絶縁層となるシリコン酸化膜を熱酸化により３００ｎｍ形成したものを準備した。この基板の上に、リフトオフ法によりチャネル幅３８ｍｍ、チャネル長５μｍの櫛形ソース電極及びドレイン電極を形成した。得られた電極付き基板を、アセトンで１０分間、次いでイソプロピルアルコールで１０分間超音波洗浄した後、オゾンＵＶを３０分間照射し表面を洗浄した。
ここで、実施例１で合成した共役系化合物（Ｅ）をクロロホルムに溶解させ、１重量％の濃度となるように溶液を調製したところ、完全に溶解できたことから、共役系化合物（Ｅ）は、有機溶媒に溶解可能であることを確認できた。
得られた共役系化合物（Ｅ）のクロロホルム溶液を塗布液として用い、上記の洗浄後の基板上に、スピンコート法により共役系化合物（Ｅ）の有機薄膜を堆積させて、有機トランジスタ素子１を作製した。
得られた有機トランジスタ素子１について、半導体パラメータアナライザー（ｋｅｉｔｈｌｅｙ社製、商品名「４２００－ＳＣＳ」）を用い、真空中でゲート電圧Ｖｇ及びソース－ドレイン間電圧Ｖｓｄを０～８０Ｖの範囲で変化させる条件でトランジスタ特性を測定したところ、良好なｎ型半導体のドレイン電流（Ｉｄ）－ゲート電圧（Ｖｇ）特性が得られた。
このときの移動度は１．２×１０－３ｃｍ２／Ｖｓであり、しきい値電圧は３２Ｖであり、オン／オフ比は１０５であり、いずれも良好な値となった。このことから、共役系化合物（Ｅ）を用いた有機トランジスタ素子１は、ｎ型有機トランジスタとして有効に機能することが確認された。そして、共役系化合物（Ｅ）は、電子輸送性に優れた有機ｎ型半導体として利用可能であることが確認された。
［実施例５：有機トランジスタ素子２の作製及びトランジスタ特性の評価］
　実施例２で合成した共役系化合物（Ｇ）をクロロホルムに溶解させ、１重量％の濃度となるように溶液を調製したところ、完全に溶解できたことから、共役系化合物（Ｇ）は、有機溶媒に溶解可能であることを確認できた。
このようにして調製した共役系化合物（Ｇ）のクロロホルム溶液を塗布液として用いたこと以外は、実施例４と同様にして、共役系化合物（Ｅ）の代わりに共役系化合物（Ｇ）を含む有機薄膜を備える有機トランジスタ素子２を作製した。
得られた有機トランジスタ素子２について、実施例４と同様にして、トランジスタ特性を測定したところ、良好なｎ型半導体のＩｄ－Ｖｇ特性が得られた。このときの移動度は０．０１６ｃｍ２／Ｖｓであり、しきい値電圧１１Ｖであり、オン／オフ比１０５と良好であった。このことから、共役系化合物（Ｇ）を用いた有機トランジスタ素子２は、ｎ型有機トランジスタとして有効に機能することが確認された。また、共役系化合物（Ｇ）は、電子輸送性に優れた有機ｎ型半導体として利用可能であることが確認された。
［比較例１：共役系化合物（Ｌ）の合成］
　以下に示す中間体の合成を経て、共役系化合物（Ｌ）を合成した。
（化合物（Ｋ）の合成）
　まず、以下の反応を行って、末端基を形成するための原料化合物である化合物（Ｋ）を合成した。すなわち、化合物（Ｋ－１）を原料にして、下記のスキームにしたがった反応を行い、化合物（Ｋ）を茶色固体として得た。
Figure JPOXMLDOC01-appb-C000044
＜化合物（Ｋ－１）の合成＞
　以下、上述した化合物（Ｋ）を合成する工程を詳細に説明する。化合物（Ｋ）の合成では、まず、化合物（Ｋ－１）を、文献（Ｊ．Ｃｈｅｍ．Ｓｏｃ．Ｐｅｒｋｉｎ　Ｔｒａｎｓ　１．Ｏｒｇａｎｉｃ　ａｎｄ　Ｂｉｏ－Ｏｒｇａｎｉｃ　Ｃｈｅｍｉｓｔｒｙ　１９９２，２１，２９８５－２９８８）に記載の方法にしたがって合成した。
＜化合物（Ｋ－２）の合成＞
　次いで、３００ｍＬの三口フラスコに、化合物（Ｋ－１）（１．００ｇ，６．５８ｍｏｌ）、及びフッ素化剤「ＳｅｌｅｃｔｆｌｕｏｒＴＭ（登録商標）」（５．６０ｇ，１５．８ｍｏｌ）を入れ、ＴＨＦ（６５ｍＬ）を加えて溶かした。そこに、テトラブチルアンモニウムハイドロオキサイド（ＴＢＡＨ）（１０重量％メタノール溶液）（３．７６ｇ，１４．５ｍｏｌ）を加え、０℃で１２時間撹拌した。攪拌後の溶液から溶媒を減圧留去して、水を加え、水相を酢酸エチルで抽出した後、有機相を硫酸マグネシウムで乾燥させて、減圧濃縮した。得られた濃縮物をシリカゲルカラムクロマトグラフィー（ヘキサン／酢酸エチル＝３／１（容積比））で精製して、化合物（Ｋ－２）（０．９３４ｇ，収率７５％）を淡黄色固体として得た。化合物（Ｋ－２）の分析結果は以下の通りである。
　ｍｐ：１５６－１５８℃
　ＴＬＣ　Ｒｆ＝０．２９（２：１＝ヘキサン：酢酸エチル（容積比））
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝７．６０（ｄ，１Ｈ，Ｊ＝４．８Ｈｚ），８．２８（ｄ，１Ｈ，Ｊ＝４．８Ｈｚ）
　ＭＳ（ＥＩ）ｍ／ｚ＝１８８（Ｍ＋）
＜化合物（Ｋ－３）の合成＞
　２００ｍＬの三口フラスコに、化合物（Ｋ－２）（１．９７ｇ，１０．４８ｍｍｏｌ）を入れ、Ｎ，Ｎ’－ジメチルホルムアミド（ＤＭＦ）（５０ｍＬ）を加えて溶かし、さらに２－クロロメタノール（３．３７ｇ，４１．９１ｍｍｏｌ）を加えた。そこへＤＭＦ（５０ｍＬ）に溶かしたカリウムｔｅｒｔ－ブトキシドを－６０℃で滴下した。滴下終了後、室温で４時間撹拌し、水を加えて反応を停止した。次に、水層を酢酸エチルで抽出し、水で洗ってから有機層を硫酸マグネシウムで乾燥させ、ろ別し、減圧濃縮した。得られた濃縮物をシリカゲルカラムクロマトグラフィー（ヘキサン／酢酸エチル＝３／１（容積比））で精製して、化合物（Ｋ－３）（１．５８ｇ、収率５５％）を白色固体として得た。化合物（Ｋ－３）の分析結果は以下の通りである。
　ｍｐ：１１７－１２２℃
　ＴＬＣ　Ｒｆ＝０．３４（２：１＝ヘキサン：酢酸エチル（容積比））
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝４．２６（ｓ，８Ｈ），７．０２（ｄ，１Ｈ，Ｊ＝４．８Ｈｚ），７．５１（ｄ，１Ｈ，Ｊ＝５．１Ｈｚ）
　ＭＳ（ＥＩ）ｍ／ｚ＝２７６（Ｍ＋）
＜化合物（Ｋ）の合成＞
　１００ｍＬの三口フラスコに、化合物（Ｋ－３）（１．００ｇ，３．６２ｍｍｏｌ）を入れ、ＴＨＦ（３０ｍＬ）を加えて溶かした。そこへｎ－ブチルリチウム（１．５８Ｍ，２．７５ｍＬ，４．３４ｍｍｏｌ）を－７８℃で加えた。０．５時間撹拌した後、臭素（０．２９ｍＬ，５．４３ｍｍｏｌ）を加え、徐々に室温まで昇温した。１時間後、水を加えて反応を停止した。水層を酢酸エチルで抽出し、飽和チオ硫酸ナトリウム水溶液で洗い、水で洗ってから有機層を硫酸マグネシウムで乾燥させた。溶媒を減圧留去し、粗生成物をシリカゲルカラムクロマトグラフィー（ヘキサン／酢酸エチル＝３／１（容積比））に通して、中間化合物（Ｋ－４）の粗生成物を得た。
得られた中間化合物（Ｋ－４）を１００ｍＬナスフラスコに入れ、ＴＨＦ（３０ｍＬ）に溶かした。そこに濃硫酸（３０ｍＬ）を加え、室温で１２時間撹拌した。反応混合物を氷に注ぎ、水で抽出した。有機層を飽和炭酸水素ナトリウム水溶液、水の順で洗浄し、硫酸マグネシウムで乾燥させた後、ろ別し、減圧濃縮した。得られた濃縮物をシリカゲルカラムクロマトグラフィー（酢酸エチル）で精製して、化合物（Ｋ）（８７７ｍｇ、収率９１％　ｉｎ　２ｓｔｅｐｓ）を茶色固体として得た。化合物（Ｋ）の分析結果は以下の通りである。
　ＴＬＣ：Ｒｆ＝０．２１（３：１＝ヘキサン：酢酸エチル（容積比））
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝７．６０（ｓ，１Ｈ）；ＭＳ（ＥＩ）ｍ／ｚ＝２６６（Ｍ＋）
（共役系化合物（Ｌ）の合成）
　上記で得られた化合物（Ｋ）（３２６ｍｇ，１．２２ｍｍｏｌ）、５，５’－ビス（トリブチルスタニル）－２，２’－ビチオフェン（４１３ｍｇ，０．５５５ｍｍｏｌ）、及び、テトラキス（トリフェニルホスフィン）パラジウム（０）（６４ｍｇ，０．０５６ｍｍｏｌ）を試験管に入れ、トルエン（６ｍＬ）を加えて溶かした。これを１２０℃で１２時間撹拌した後、室温で放冷した。反応溶液をセライトろ過し溶媒を減圧留去した後、得られた固体をヘキサンで洗い、共役系化合物（Ｌ）（３５ｍｇ，収率７４％）を暗紫色固体として得た。共役系化合物（Ｌ）の分析結果及び化学式は以下の通りである。
　ｍｐ：＞３００℃
　ＭＳ（ＥＩ）：ｍ／ｚ＝５３８（Ｍ＋）
Figure JPOXMLDOC01-appb-C000045
このようにして得られた共役系化合物（Ｌ）をクロロホルムに溶解させたところ、１×１０－４ｍｏｌ／Ｌより高い濃度では完全に溶解せず、有機溶媒に難溶であることが判明した。
［比較例２］
（共役系化合物（Ｎ）の合成）
　以下に示す化合物（Ｍ）の合成を経て、共役系化合物（Ｎ）を合成した。まず、２０ｍＬの三口フラスコに、５，５’－ジブロモ－４，４’－ジヘキシル－２，２’－ビチオフェン（４９２ｍｇ，１．００ｍｍｏｌ）を入れ、ＴＨＦ（１０ｍＬ）を加えて溶かした。そこにｎ－ブチルリチウム（１．５８Ｍ，１．３９ｍＬ，２．２０ｍｍｏｌ）を－７８℃で加えた。１時間撹拌した後、塩化トリブチルスズ（０．５４３ｍｌ，２．００ｍｍｏｌ）を加え、徐々に室温まで昇温した。２時間後、水と微量の塩酸を加えて反応を停止した。水層をジエチルエーテルで抽出し、水で洗ってから有機層を硫酸マグネシウムで乾燥させた。溶媒を減圧留去した後、得られた液体をＧＰＣ（クロロホルム（ＣＨＣｌ３））で精製することにより、化合物（Ｍ）（６３０ｍｇ，収率６９％）を黄色液体として得た。化合物（Ｍ）の分析結果及び化学式は以下の通りである。
　ＴＬＣ：Ｒｆ＝１．０（ヘキサン）
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝０．８４－０．９４（ｍ，２４Ｈ），１．０２－１．２０（ｍ，１２Ｈ），１．２６－１．３９（ｍ，２４Ｈ），１．４６－１．６１（ｍ，１６－Ｈ），２．５１（ｔ，４Ｈ，８．０Ｈｚ），７．１３（ｓ，２Ｈ）
　ＭＳ（ＥＩ）：ｍ／ｚ＝９１２（Ｍ＋）．
Figure JPOXMLDOC01-appb-C000046
次に、上記で得た化合物（Ｍ）（５０ｍｇ，０．０５５ｍｍｏｌ）、比較例１で合成した化合物（Ｋ）（３２ｍｇ，０．１２ｍｍｏｌ）、及び、テトラキス（トリフェニルホスフィン）パラジウム（０）（６ｍｇ，０．００５ｍｍｏｌ）を蓋付き試験管に入れ、トルエン（１ｍＬ）を加えて溶かした。これを１２０℃で１２時間撹拌した後、室温で放冷した。次に溶媒を減圧留去し、粗生成物をシリカゲルカラムクロマトグラフィー（クロロホルム）に通してからＧＰＣ（クロロホルム）で精製して、共役系化合物（Ｎ）（１９ｍｇ，収率４９％）を橙色固体として得た。共役系化合物（Ｎ）の分析結果及び化学式は以下の通りである。
　ＴＬＣ：Ｒｆ＝０．４３（５：１＝ヘキサン：酢酸エチル（容積比））
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝０．８８－０．９６（ｍ，６Ｈ），１．２８－１．４９（ｍ，１２Ｈ），１．６５－１．７６（ｍ，４Ｈ），２．８５（ｔ，４Ｈ，Ｊ＝７．９Ｈｚ），７．１９（ｓ，２Ｈ），７．５１（ｓ，２Ｈ）
　ＭＳ（ＥＩ）ｍ／ｚ＝７０６（Ｍ＋）
Figure JPOXMLDOC01-appb-C000047
（有機トランジスタ素子３の作製及びトランジスタ特性の評価）
　共役系化合物（Ｎ）をクロロホルムに溶解させ、１重量％の濃度となるように溶液を調製したところ、完全に溶解できたことから、有機溶媒に溶解可能であることを確認できた。
このようにして調製した共役系化合物（Ｎ）のクロロホルム溶液を塗布液として用いたこと以外は、実施例４と同様にして、共役系化合物（Ｅ）の代わりに共役系化合物（Ｎ）を含む有機薄膜を備える有機トランジスタ素子３を作製した。
得られた有機トランジスタ素子３について、実施例４と同様にして、トランジスタ特性を測定したところ、ｎ型半導体のＩｄ－Ｖｇ特性が得られたが、このときの移動度は１．８×１０－５ｃｍ２／Ｖｓであり、実施例と比較して低かった。
［実施例５：共役系化合物（Ｐ）の合成］
　以下に示す各種の中間体の合成を経て、共役系化合物（Ｐ）を合成した。
（化合物（Ｏ）の合成）
　３０ｍＬの２口ナスフラスコに化合物（Ａ－３）（１００ｍｇ，０．２８ｍｍｏｌ）、マロノニトリル（７５ｍｇ，１．１２ｍｍｏｌ）、ピリジン（１８０ｍｇ，２．２４ｍｍｏｌ）、四塩化チタン（２１０ｍｇ，１．１２ｍｍｏｌ）、及び、クロロホルム（１０ｍＬ）を加え、８時間還流させた後、水洗しクロロホルムで抽出した。有機層を硫酸ナトリウムで乾燥させ溶媒を留去して、真空乾燥させた。得られた固形物を、シリカゲルカラム（ヘキサン／酢酸エチル＝１０／１（容積比））で精製して、目的物である黄色固体の化合物（Ｏ）（８８ｍｇ，収率６９％）を得た。得られた化合物（Ｏ）の分析結果及び化学式は以下の通りである。
　ＴＬＣ　Ｒｆ＝０．５（ヘキサン／酢酸エチル＝１０／１（容積比））
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝０．９０（ｍ，３Ｈ），１．３４（ｍ，４Ｈ），１．４３（ｍ，２Ｈ），１．５８（ｍ，２Ｈ），３．１４（ｍ，２Ｈ）
　ＧＣ－ＭＳ（ＤＩ）：ｍ／ｚ＝４４６（Ｍ＋）
Figure JPOXMLDOC01-appb-C000048
（共役系化合物（Ｐ）の合成）
　２ｍＬの試験管に、化合物（Ｏ）（１００ｍｇ，０．２２ｍｍｏｌ）、化合物（Ｆ）（７５ｍｇ，０．１６ｍｍｏｌ）、Ｐｄ２（ｄｂａ）３（２ｍｇ，０．００２ｍｍｏｌ）、トリ－ｏ－トリルホスフィン（３ｍｇ，０．００８ｍｍｏｌ）、及び、クロロベンゼン（１ｍＬ）を入れ、マイクロウェーブ照射下でそれらを反応させた（１８０℃，５分）。シリカゲルカラム（クロロホルム）及びＧＰＣで精製を行い、目的物である濃青黒色固体の共役系化合物（Ｐ）（１５ｍｇ，収率１７％）を得た。共役系化合物（Ｐ）の分析結果及び化学式は以下の通りである。
　１Ｈ－ＮＭＲ（４００ＭＨｚ，ＣＤＣｌ３）：δ（ｐｐｍ）＝０．８９（ｍ，６Ｈ），１．３２（ｍ），１．４６（ｍ），１．６４（ｍ），３．３４（ｍ，４Ｈ），７．４０（ｍ，２Ｈ），７．４６（ｍ，２Ｈ）
　ＭＡＬＤＩ　ＴＯＦＭＳ：ｍ／ｚ＝８９８．１
Figure JPOXMLDOC01-appb-C000049
共役系化合物（Ｐ）について、ＣＶ測定を行ったところ、－０．６２Ｖに可逆な還元波が観測された。還元波から見積もったＬＵＭＯエネルギーは－４．１８ｅＶであり、ＬＵＭＯが低くなっていることが確認できた。
［実施例６：共役系化合物（Ｑ）の合成］
（共役系化合物（Ｑ）の合成）
　試験管に、化合物（Ｏ）、２，２’－ビス（トリブチルスタニル）チエノチオフェン、Ｐｄ２（ｄｂａ）３、及びトリ－ｏ－トリルホスフィン及びクロロベンゼンを入れ、マイクロウェーブ照射下でそれらを反応させる。反応物を、シリカゲルカラム（クロロホルム）、及びＧＰＣで精製して、目的物である共役系化合物（Ｑ）を得る。
Figure JPOXMLDOC01-appb-C000050
［実施例７：有機トランジスタ素子４の作製及びトランジスタ特性の評価］
　共役系化合物（Ｐ）をクロロホルムに溶解させ、１重量％の濃度となるように溶液を調製したところ、完全に溶解できたことから、共役系化合物（Ｐ）は、有機溶媒に溶解可能であることを確認できた。
共役系化合物（Ｅ）のクロロホルム溶液に代えて、共役系化合物（Ｐ）のクロロホルム溶液を塗布液として用いたこと以外は、実施例４と同様にして、共役系化合物（Ｐ）を含む有機薄膜を備える有機トランジスタ素子４を作製した。
得られた有機トランジスタ素子４について、実施例４と同様にして、トランジスタ特性を真空中で測定したところ、良好なｎ型半導体のＩｄ－Ｖｇ特性が得られた。このときの移動度は４．９×１０－３ｃｍ２／Ｖｓであり、しきい値電圧２５Ｖであり、オン／オフ比１０６と良好であった。さらに有機トランジスタ素子４について、トランジスタ特性を大気中で測定したところ、移動度は２．８×１０－３ｃｍ２／Ｖｓであり、しきい値電圧２３Ｖであり、オン／オフ比１０６と真空中での特性とほぼ同等であった。このことから、共役系化合物（Ｐ）を用いた有機トランジスタ素子４は、ｎ型有機トランジスタとして有効に機能し、大気中でも安定に動作することが確認された。また、共役系化合物（Ｐ）は、電子輸送性に優れた有機ｎ型半導体として利用可能であることが確認された。

Claims (11)

  1. 式（Ｉ）で表される共役系化合物。
    Figure JPOXMLDOC01-appb-C000001
    Figure JPOXMLDOC01-appb-C000002
    Figure JPOXMLDOC01-appb-C000003
    ［式（Ｉ）中、Ｒ０１及びＲ０２は、それぞれ独立に、アルカン骨格が含まれる１価の基を示し、Ｒ１１、Ｒ１２、Ｒ２１及びＲ２２は、それぞれ独立に、水素原子、ハロゲン原子又は１価の基を示す。Ｘ１１、Ｘ１２、Ｘ２１及びＸ２２は、それぞれ独立に、酸素原子、硫黄原子又は式（ａ）で表される基を示す。ただし、Ｘ１１、Ｘ１２、Ｘ２１及びＸ２２の少なくとも１つは、硫黄原子又は式（ａ）で表される基である。Ｚ１及びＺ２は、それぞれ独立に、式（ｉ）で表される基、式（ｉｉ）で表される基、式（ｉｉｉ）で表される基、式（ｉｖ）で表される基、式（ｖ）で表される基、式（ｖｉ）で表される基、式（ｖｉｉ）で表される基、式（ｖｉｉｉ）で表される基及び式（ｉｘ）で表される基からなる群より選ばれるいずれか１種の基を示す。Ａｒ０、Ａｒ１及びＡｒ２は、それぞれ独立に、炭素数６以上の２価の芳香族炭化水素基、又は炭素数４以上の２価の複素環基を示し、これらは置換基を有していてもよい。ｒは１～６の整数を示し、ｓ及びｔは、それぞれ独立に、０～６の整数を示す。
    　式（ａ）中、Ａは、水素原子、ハロゲン原子又は１価の基を示し、複数あるＡはそれぞれ同一でも異なっていてもよいが、少なくとも１つのＡは電子吸引性の基である。
    　式（ｖｉｉ）、式（ｖｉｉｉ）及び式（ｉｘ）中、Ｒ３、Ｒ４、Ｒ５及びＲ６は、それぞれ独立に、水素原子、ハロゲン原子又は１価の基を示し、Ｒ３とＲ４とは互いに結合して環を形成していてもよい。なお、式（ｖｉｉｉ）で表される基は左右反転していてもよい。］
  2. 前記Ｘ１１及び前記Ｘ１２の少なくとも一方が式（ａ）で表される基であり、前記Ｘ２１及び前記Ｘ２２の少なくとも一方が式（ａ）で表される基である、請求項１記載の共役系化合物。
  3. 前記Ａｒ０が、アルカン骨格を含む置換基を有していない基である、請求項１又は２記載の共役系化合物。
  4. 前記Ａｒ０が、式（ＩＩ）で表される基又は式（ＩＩＩ）で表される基である、請求項１～３のいずれか一項に記載の共役系化合物。
    Figure JPOXMLDOC01-appb-C000004
    Figure JPOXMLDOC01-appb-C000005
    Figure JPOXMLDOC01-appb-C000006
     ［式（ＩＩ）中、Ｚ３は、式（ｘｉ）で表される基、式（ｘｉｉ）で表される基、式（ｘｉｉｉ）で表される基、式（ｘｉｖ）で表される基、式（ｘｖ）で表される基、式（ｘｖｉ）で表される基、式（ｘｖｉｉ）で表される基、式（ｘｖｉｉｉ）で表される基及び式（ｘｉｘ）で表される基からなる群より選ばれるいずれか１種の基を示す。なお、式（ｘｖｉｉｉ）で表される基は左右反転していてもよい。
    　式（ＩＩＩ）中、Ａｒ３及びＡｒ４は、それぞれ独立に、炭素数６以上の３価の芳香族炭化水素基又は炭素数４以上の３価の複素環基であって、アルカン骨格を含む置換基を有していない基を示し、Ｘ３は、酸素原子、硫黄原子又は式（ａ）で表される基を示す。］
  5. 式（ＩＩＩ）で表される基が、式（ＩＶ）で表される基である、請求項４記載の共役系化合物。
    Figure JPOXMLDOC01-appb-C000007
    Figure JPOXMLDOC01-appb-C000008
    ［式（ＩＶ）中、Ｘ３は前記と同義であり、Ｙ１及びＹ２は、それぞれ独立に、炭素原子又は窒素原子を示し、Ｚ４及びＺ５は、それぞれ独立に、式（ｘｘｉ）で表される基、式（ｘｘｉｉ）で表される基、式（ｘｘｉｉｉ）で表される基、式（ｘｘｉｖ）で表される基、式（ｘｘｖ）で表される基、式（ｘｘｖｉ）で表される基、式（ｘｘｖｉｉ）で表される基、式（ｘｘｖｉｉｉ）で表される基及び式（ｘｘｉｘ）で表される基からなる群より選ばれるいずれか１種の基を示す。なお、式（ｘｘｖｉｉｉ）で表される基は左右反転していてもよい。］
  6. 前記Ｘ１１及び前記Ｘ１２のうちの一方が酸素原子であり、前記Ｘ１１及び前記Ｘ１２のうちの残りの一方が式（ａ１）で表される基であり、かつ、前記Ｘ２１及び前記Ｘ２２のうちの一方が酸素原子であり、前記Ｘ２１及び前記Ｘ２２のうちの残りの一方が式（ａ１）で表される基である、請求項１～５のいずれか一項に記載の共役系化合物。
    Figure JPOXMLDOC01-appb-C000009
  7. 前記Ｚ４及びＺ５が、式（ｘｘｉｉ）で表される基又は式（ｘｘｖｉｉ）で表される基である、請求項５又は６記載の共役系化合物。
  8. 請求項１～７のいずれか一項に記載の共役系化合物を含む有機薄膜。
  9. 請求項８記載の有機薄膜を備える有機薄膜素子。
  10. 請求項８記載の有機薄膜を備える有機薄膜トランジスタ。
  11. 請求項８記載の有機薄膜を備える有機薄膜太陽電池。
PCT/JP2011/076934 2010-11-24 2011-11-22 共役系化合物、並びにこれを用いた有機薄膜及び有機薄膜素子 WO2012070582A1 (ja)