WO2012033369A2 - 리튬 이차 전지용 양극 활물질 및 이의 제조방법 - Google Patents

리튬 이차 전지용 양극 활물질 및 이의 제조방법 Download PDF

Info

Publication number
WO2012033369A2
WO2012033369A2 PCT/KR2011/006672 KR2011006672W WO2012033369A2 WO 2012033369 A2 WO2012033369 A2 WO 2012033369A2 KR 2011006672 W KR2011006672 W KR 2011006672W WO 2012033369 A2 WO2012033369 A2 WO 2012033369A2
Authority
WO
WIPO (PCT)
Prior art keywords
active material
lithium secondary
secondary battery
source
positive electrode
Prior art date
Application number
PCT/KR2011/006672
Other languages
English (en)
French (fr)
Other versions
WO2012033369A3 (ko
Inventor
오성우
선희영
도유림
이형복
Original Assignee
에스케이이노베이션 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 에스케이이노베이션 주식회사 filed Critical 에스케이이노베이션 주식회사
Priority to JP2013528128A priority Critical patent/JP5678191B2/ja
Priority to CN201180043417.0A priority patent/CN103098271B/zh
Priority to EP11823802.1A priority patent/EP2615672A4/en
Priority to US13/821,615 priority patent/US9825294B2/en
Publication of WO2012033369A2 publication Critical patent/WO2012033369A2/ko
Publication of WO2012033369A3 publication Critical patent/WO2012033369A3/ko

Abstract

본 발명은 리튬 이차 전지용 양극 활물질의 제조방법에 관한 것으로, 상세하게, 본 발명에 따른 제조방법은 니켈 소스, 코발트 소스, 알루미늄 소스, 암모니아수, 슈크로스 및 pH조절제를 혼합 반응시켜 혼합 용액을 제조하는 단계; 상기 혼합 용액을 건조, 산화시켜 활물질 전구체를 제조하는 단계; 및 상기 활물질 전구체에 리튬소스를 넣고 소성하여 리튬 이차 전지용 양극 활물질을 제조하는 단계;를 포함는 특징이 있다.

Description

리튬 이차 전지용 양극 활물질 및 이의 제조방법
본 발명은 리튬 이차 전지용 양극 활물질 및 이의 제조방법에 관한 것으로, 상세하게 극히 높은 용량을 가지며 전기화학적 특성이 향상된 양극 활물질 및 이의 제조방법에 관한 것이다.
전지는 크게 1차 전지와 2차 전지로 구분될 수 있는데, 1차 전지란 비가역적인 반응을 이용하여 전기를 생산하므로 한 번 사용된 후에는 재사용이 불가능한 전지로서 일반적으로 많이 사용하는 건전지, 수은 전지, 볼타 전지 등이 이에 속하며, 2차 전지는 이와는 달리 가역적인 반응을 이용하므로 사용 후 충전하여 재사용이 가능한 전지로서 납 축전지, 리튬 이온 전지, 니카드(Ni-Cd) 전지 등이 이에 속한다.
2차 전지 중 하나인 리튬 이온 전지는 일반적으로 탄소로 이루어지는 음극 및 일반적으로 리튬 화합물로 이루어지는 양극, 두 극 사이에 위치하는 전해질, 그리고 음극 및 양극을 연결하는 전선을 포함하여 구성된다. 전해질 내의 리튬 이온은 충전(charge) 시에는 음극 쪽으로, 방전(discharge) 시에는 양극 쪽으로 이동하며, 각 극에서 잉여의 전자를 방출하거나 또는 흡수하면서 화학 반응을 일으키게 된다. 이러한 과정에서 상기 전선에 전자가 흐르게 되며, 이에 따라 전기 에너지가 발생하게 된다. 여기에서 리튬 이온 전지를 사용하여 설명하였으나, 다른 2차 전지의 경우도 전극 또는 전해질로 사용되는 물질이 달라질 뿐 기본 원리 및 구조는 이와 동일하다. 즉, 일반적으로 2차 전지는 상술한 바와 같이 음극, 양극, 전해질 및 전선을 포함하여 이루어지는 것이다.
이 때, 2차 전지는 음극, 양극, 전해질 및 전선이 각각 단일 개 구비되어 형성될 수도 있지만, 보다 일반적으로는 단일 개의 음극, 양극, 전해질 및 전선으로 이루어지는 단위 셀이 다수 개 연결되어 이루어진다. 즉, 2차 전지 팩의 내부에는 상기 설명한 바와 같은 단위 셀이 다수 개 들어 있게 된다. 물론 각 단위 셀은 전기적으로 서로 연결된다.
일반적으로 2차 전지는 그 내부에 다수 개의 단위 셀을 포함하고 있으며, 또한 일반적으로 각 셀의 전극들과 연결된 한 쌍의 외부 단자 탭(즉 각 단위 셀의 음극들이 연결된 하나의 음극, 각 셀의 양극들이 연결된 하나의 양극으로서, 전지 하나당 한 쌍이 구비되어 전극으로서 기능하는 탭)이 외부로 노출되어 있는 형태로 구성된다. 이와 같은 2차 전지들은 일반적으로 단일한 양극 및 음극이 사용되기보다는 다수 개의 양극 및 음극이 연결되어 하나의 팩으로서의 배터리를 형성하게 된다.
대한민국 공개특허 제2009-0020288호, 대한민국 공개특허 제2009-0006898호와 같이, 리튬 이차전지의 양극 활물질로, Li-M-P계(M은 Fe, Mn, Co, Ni로 구성된 군에서 선택된 1종 이상), Li-Mn-Ni계, Li-Ni-Mn-Co계와 같은 리튬 활물질 전구체가 사용되고 있다.
그러나, 리튬이차전지의 양극 활물질로 널리 사용되고 있는 LiNi1/3Co1/3Mn1/3O2물질은 단락 전압(cut-off voltage)이 3.0-4.3V의 경우 반쪽전지(Half Cell)로 테스트 할 때 약 150mAh/g의 용량을 가질 뿐이며, EV용 배터리와 같은 고용량 배터리를 제조하기 위해서는 고용량 양극 활물질 개발이 시급한 실정이다.
본 발명은 고용량 리튬 이차 전지용 양극 활물질 및 이의 제조방법을 제공하는데 목적이 있다. 본 발명은 리튬이온이 본 발명에 따른 리튬 이차 전지용 양극 활물질의 구조 내에서 탈·삽입이 원활하게 되어, 리튬이온의 확산속도가 증가함에 따라 전기 화학적 특성이 향상될 뿐 아니라 고율특성이 향상된 리튬 이차 전지용 양극 활물질 및 이의 제조방법을 제조하는 방법을 제공하는데 목적이 있다.
본 발명에 따른 양극 활물질의 제조방법은 다공성 구조를 가져 높은 비표면적 및 기공 부피를 가지며, 높은 용량을 갖는 리튬 이차 전지용 양극 활물질을 제조하는 방법으로, 본 발명에 따른 다공성 양극 활물질의 제조방법은 니켈 소스와 코발트 소스 및 알루미늄 소스를 함유하는 금속 수용액, 암모니아수, 슈크로스 및 pH조절제를 포함하는 원료를 혼합 반응시켜 활물질 전구체를 제조하는 단계; 및 상기 활물질 전구체에 리튬 소스를 넣고 소성하여 하기 화학식1의 리튬 이차 전지용 양극 활물질을 제조하는 단계;를 포함하여 제조된다.
(화학식1)
Li1+zNi1-x-yCoxAlyO2
상기 z는 0 이상 내지 0.3 이하의 실수이고, 상기 x는 0.05 이상 내지 0.3이하의 실수이며, 상기 y는 0 초과 내지 0.3이하의 실수이며, 1-x-y는 0.4 이상 내지 0.95 미만의 실수이며, 바람직하게, 상기 y는 0.01 이상 내지 0.3 이하의 실수이며, 상기 1-x-y는 0.4 이상 내지 0.94이하인 실수이다.
상술한 바와 같이, 본 발명에 따른 제조방법은 니켈 소스, 코발트 소스, 알루미늄 소스, 킬레이트제인 암모니아수, pH조절제 및 슈크로스를 원료로 활물질 전구체를 제조한 후, 상기 활물질 전구체에 리튬 소스를 투입한 후 이를 열처리하여 양극 활물질을 제조하는 특징이 있다.
본 발명에 따라 제조된 리튬이차 전지용 양극 활물질은 총 기공 부피가 6.5~8.0x10-2cc/g이며, 비표면적이 0.7~1.0m2/g인 것을 특징으로 하며, 다공 구조를 갖는 구형의 입자형태를 가질 수 있다.
본 발명에 따라 제조된 리튬이차 전지용 양극 활물질은 고율특성이 놀랍게 향상되는 효과를 가져 반쪽전지 테스트를 할 경우 200mAh/g이상의 고용량을 나타낼 수 있으며, 보다 구체적으로는 200~215mAh/g의 용량을 나타낼 수 있다.
상세하게, 본 발명에 따른 양극 활물질의 제조방법은 pH조절제로 반응기에 공급된 혼합액의 pH를 일정하게 유지하며, 니켈 소스와 코발트 소스 및 알루미늄 소스를 함유하는 금속 수용액, 바람직하게는 니켈 소스, 코발트 소스, 알루미늄 소스 및 슈크로스를 함유하는 금속 수용액과 암모니아수를 반응기에 공급 및 반응시켜 반응물을 제조하고, 제조된 반응물을 건조 및 자연산화시켜 활물질 전구체를 제조한 후, 제조된 활물질 전구체와 리튬 소스를 혼합하고 이를 소성하여 상기 화학식1의 리튬 이차 전지용 양극 활물질을 제조하는 특징이 있다.
상기 니켈 소스는 황산니켈, 질산니켈, 탄산니켈, 니켈아세테이트, 염화니켈 및 수산화니켈로부터 하나 또는 둘 이상 선택하여 사용할 수 있으며, 바람직하게는 황산니켈을 사용하는 것이 좋다.
상기 코발트 소스는 황산코발트, 질산코발트, 탄산코발트, 염화코발트 및 수산화 코발트로부터 하나 또는 둘 이상 선택하여 사용될 수 있으며, 바람직하게는 황산니켈을 사용하는 것이 좋다.
상기 알루미늄 소스는 Al2O3, Al(ClO4)3, AlPO4, AlK(SO4)2, Al2(SO4)3, Al2S3, Al2O3·TiO2, AlF3 및 이들의 수화물로부터 하나 또는 둘 이상 선택하여 사용할 수 있으며, 바람직하게는 황산알루미늄을 사용하는 것이 좋다.
상기 니켈 소스, 코발트 소스 및 알루미늄 소스는 수용액 상태로 반응기에 공급되는데, 상기 니켈 소스, 코발트 소스 및 알루미늄 소스를 함유하는 금속 수용액은 금속의 몰 농도가 1 내지 3M인 것이 바람직하다. 이때, 상기 금속은 니켈, 코발트 및 알루미늄을 의미한다.
상기 몰 농도가 1M보다 작게 되면 구형의 입자를 형성하는데 반응시간이 오래 걸리는 단점이 있고, 3M을 초과하면 반응 초기에 반응성이 크게 되어 탭밀도가 떨어지는 입자가 형성되는 단점이 있다.
상기 금속 수용액은 0.2~0.5L/hr의 속도로 반응기에 공급하여 반응시키는 것이 반응성에 있어 좋다.
상기 금속 수용액에 함유된 니켈 소스, 코발트 소스 및 알루미늄 소스의 몰 비는 상기 화학식 1에 따른 니켈, 코발트 및 알루미늄의 원소비를 만족하도록 정량 투입되는 것이 바람직하다.
상세하게, 상기 금속 수용액은 니켈 : 코발트 : 알루미늄의 몰비가 0.4 내지 0.94 : 0.05 내지 0.3: 0.01 내지 0.3인 것이 바람직하다. 보다 상세하게, 니켈 소스, 코발트 소스 및 알루미늄 소스의 각 금속 원소의 몰을 기준으로, 금속 원소(니켈, 코발트 및 알루미늄)의 총 몰수에 대한 코발트 몰수의 비가 0.05 내지 0.3이 되도록 코발트 소스를 함유하며, 상기 금속 원소의 총 몰수에 대한 알루미늄 몰수의 비가 0 초과 내지 0.3, 바람직하게 0.01 내지 0.3가 되도록 알루미늄 소스를 함유하며, 상기 금속 원소의 총 몰수에 대한 니켈 몰수의 비가 0.4 이상 내지 0.95 미만, 바람직하게 0.4 내지 0.94가 되도록 니켈 소스를 함유한다.
Co와 Al의 몰비가 상기 한정범위를 넘을 경우 즉, Co가 0.05몰 미만의 경우는 Ni 함량이 너무 많아져서 안정성에 문제가 생기며, 0.3몰 초과의 경우 전체적인 양극 활물질 용량이 감소하는 문제점이 발생할 수 있다. 또한 Al의 경우 0.01몰 미만의 경우 구조적 안정성의 특성이 나타나지 않으며, Al이 0.2몰 초과의 경우 용량 감소의 원인이 되는 문제점이 발생할 수 있다.
상기 슈크로스는 5~30 중량%로 상기 금속 수용액에 함유되는 특징이 있다. 상기 슈크로스는 원료의 혼합 반응에 의해 Ni-Co-Al-(OH)2의 내부에 존재하게 되고, 소성시 슈크로스가 탄화하게 되면서, 제조된 리튬이차 전지용 양극 활물질의 입자 내부에 기공을 형성하게 된다. 상기 기공으로 인하여 전해액이 입자 내부까지 침투가 가능하기 때문에 리튬이온이 구조 내에서 탈, 삽입이 원활하게 되며, 고율특성이 향상될 수 있다.
상술한 상기 슈크로스를 함유하는 금속 수용액, 암모니아수 및 pH조절제를 반응기에 첨가하고 교반하여 활물질 전구체를 제조하는데, 상기 pH 조절제에 의해, 상기 반응기 내 혼합 용액의 pH가 11~13로 조절되며, 반응기 내 혼합 용액의 평균체류시간이 5~7시간이 되도록 원료의 공급 속도를 조절하는 것이 좋다. 상기 반응기의 반응온도는 40~60℃인 것이 바람직하다. 상기 pH를 조절하기 위한 pH 조절제로는 크게 제한 받는 것은 아니나 수산화나트륨을 사용하는 것이 바람직하다.
상기 암모니아수는 상기 금속 수용액의 금속 몰농도에 대하여 0.1 내지 0.25배의 농도인 것이 바람직하며, 상기 암모니아수는 0.02~0.05L/hr의 속도로 반응기에 공급 혼합하는 것이 좋다. 암모니아는 킬레이트제(chealating agent)로써 금속이온(Metalion)들을 균일한 조성으로 잡아주기 위해 사용된다. 상기 암모니아 농도가 상기 범위를 벗어날 경우 NaOH에 의해 불균일한 조성으로 침전이 되어 최적 조건의 전구체를 얻을 수 없다.
상기 활물질 전구체는 상기 반응기에서 수득된 반응물을 건조 및 자연산화시켜 제조된 것이 바람직하다. 크게 제한 받는 것은 아니나 바람직하게는 90~120℃에서 10~20 시간 건조시키고, 동일 온도에서 10~15시간 동안 공기중 자연산화시키는 것이 좋다.
상기 활물질 전구체에 리튬 소스를 넣어 소성시켜 본 발명에 따른 양극 활물질을 제조할 수 있다.
상세하게, 상기 건조 및 자연산화에 의해 수득된 활물질 전구체와 상기 리튬 소스를 믹서를 포함한 통상의 교반 장치를 이용하여 혼합 한 후, 리튬 소스와 활물질 전구체의 혼합물을 열처리하여 본 발명에 따른 양극 활물질을 제조한다.
상기 활물질 전구체와 상기 리튬 소스의 혼합시, 상기 리튬 소스는 화학식 1에 따른 리튬의 원소비를 만족하도록 정량 투입되는 것이 바람직하다.
상세하게, 상기 활물질 전구체를 제조하는 혼합용액에 함유된 니켈 소스의 니켈, 코발트 소스의 코발트 및 알루미늄 소스의 알루미늄의 몰수의 합을 전체금속몰수로 하여, 상기 전체금속몰수 1몰에 대해 1 내지 1.3몰의 리튬에 해당하는 리튬 소스와 상기 활물질 전구체가 혼합되는 것이 바람직하다.
상기 리튬 소스는 리튬염을 포함하며, 상기 리튬염은 LiOH를 포함한다.
상기 소성시 승온은 0.5~1℃/min로 400~500℃까지 승온시키는 1단계; 및 1~2 ℃/min로 800~900℃까지 승온시키는 2단계;를 포함하여 수행되는 특징이 있으며, 상기 소성은 상기 1단계 승온 시점을 기준으로 15~20시간 수행되는 특징이 있다.
상세하게, 상기 소성은 0.5~1℃/min의 속도로 400~500℃까지 승온시킨 후, 400~500℃에서 열처리가 이루어지고, 1~2 ℃/min의 속도로 800~900℃까지 승온시킨 후, 800~900℃에서 다시 열처리가 이루어지는 다단 열처리인 것이 바람직하다. 이때, 상기 400~500℃의 열처리는 4 내지 6 시간 동안 수행되는 것이 바람직하다.
상기 소성시 승온속도가 상기 범위를 벗어날 경우 슈크로스가 빠르게 분해되어 제조되는 리튬 이차 전지용 양극 활물질 입자가 깨지는 현상이 나타날 수 있으며, 보다 효과적인 기공형성을 위하여 상기 소성은 상기의 조건(열처리 프로화일)에 부합되도록 수행하는 것이 바람직하다.
본 발명에 의해 제조된 리튬 이차 전지용 양극 활물질은 5~15㎛의 균일한 크기의 다공성 입자인 특징이 있으며, 화학식1의 구조를 가지며, 기공이 형성된 리튬 이차 전지용 양극 활물질인 특징이 있다.
(화학식1)
Li1+zNi1-x-yCoxAlyO2
상기 z는 0 이상 내지 0.3 이하의 실수이고, 상기 x는 0.05 이상 내지 0.3이하의 실수이며, 상기 y는 0 초과 내지 0.3이하의 실수이며, 1-x-y는 0.4 이상 내지 0.95 미만의 실수이며, 바람직하게, 상기 y는 0.01 이상 내지 0.3 이하의 실수이며, 상기 1-x-y는 0.4 이상 내지 0.94 이하인 실수이다.
본 발명에 따른 리튬 이차 전지용 양극 활물질 제조방법은 슈크로스를 넣어줌으로써 제조된 리튬 이차 전지용 양극 활물질의 입자 내부에 기공이 형성되어, 상기 기공으로 인하여 전해액이 입자 내부까지 침투가 가능하기 때문에 리튬이온이 양극 활물질 구조 내에서 탈, 삽입이 원활하게 되어 고율특성이 향상되는 효과가 있다. 또한 본 발명에 따른 리튬 이차 전지용 양극 활물질의 기공부피가 넓어 본 발명에 의해 제조된 양극 활물질의 구조 내의 리튬이온의 확산속도가 증가하게 되어, 전기화학적 특성이 향상되는 효과가 있다.
이하, 실시예를 통하여 본 발명을 더욱 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 예시하기 위한 것으로, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지 않는 것은 당업계에서 통상의 지식을 가진 자에게 있어서 자명할 것이다.
(실시예1)
4L 크기의 반응기에 황산니켈(NiSO36H2O), 황산코발트(CoSO47H2O) 및 황산알루미늄(Al2(SO4)318H2O)이 2M로 용해되고, 20 중량%의 슈크로스를 함유하는 금속 수용액을 0.3L/hr의 속도로 공급하였다. 이때, 상기 금속 수용액은 니켈 : 코발트 : 알루미늄이 0.7 : 0.1 : 0.2의 몰비가 되도록 상기 황산니켈(NiSO36H2O), 황산코발트(CoSO47H2O) 및 황산알루미늄(Al2(SO4)318H2O)을 함유하였다.
0.2몰 농도의 암모니아수를 0.03L/hr의 속도로 반응기에 공급하였으며, pH가 11이 되도록 수산화나트륨 추가하고 반응기를 교반하면서 반응시켜 혼합 용액을 제조하였다. 이때, 상기 반응시 평균온도는 40℃가 되도록 유지하였다.
상기 반응기의 회전날개는 상하 균일 혼합을 위해 두 개의 역날개식으로 설계되었으며, 회전모터의 출력은 2.4kw였다. 회전수는 1500rpm이었다.
상기 반응기에서 수득된 반응물을 110℃에 15시간 정도 건조시키고 12시간 동안 공기중 자연 산화 시켜 활물질 전구체를 제조하였다.
제조된 활물질 전구체와 수산화리튬(LiOH)을 1:1.05의 몰비로 혼합 한 후, 공기중 1℃/min 의 속도로 500℃까지 승온하고 5시간 동안 열처리한 후, 2℃/min의 속도로 900℃까지 승온시켜 소성시키되, 총 소성시간이 20시간이 되도록 소성시켜 리튬 이차 전지용 양극 활물질 Li1.05Ni0.7Co0.1Al0.2O2을 제조하였다. 상기 제조된 리튬 이차 전지용 양극 활물질은 평균지름이 10㎛이며 기공이 형성된 균일 입자를 얻을 수 있었다.
(실시예 2)
상기 금속 수용액이 니켈 : 코발트 : 알루미늄의 몰비가 0.6 : 0.1 : 0.3이 되도록 상기 황산니켈(NiSO36H2O), 황산코발트(CoSO47H2O) 및 황산알루미늄(Al2(SO4)318H2O)을 함유한 것을 제외하고, 실시예 1과 동일하게 실시하여, 리튬 이차 전지용 양극 활물질 Li1.05Ni0.6Co0.1Al0.3O2을 제조하였다.
(비교예1)
상기 실시예1과 동일하게 실시하되 슈크로스를 포함하지 않은 것에 차이가 있으며, 나머지는 상기 실시예1과 동일하게 실시하였다.
실시예1과 비교예1에서 제조된 입자의 평균 비표면적과 평균기공부피를 측정하여 하기 표1에 나타내었다.
(표 1)
Figure PCTKR2011006672-appb-I000001
상기 표 1에서 알 수 있듯이, 본 발명에 따른 양극활물질의 경우, 매우 큰 기공 부피를 갖는 다공 구조의 입자가 제조됨을 알 수 있으며, 매우 높은 비표면적을 가짐을 알 수 있다.
상기 실시예 1, 실시예 2 및 비교예1에서 제조된 입자의 용량을 측정하여 하기 표 2에 도시하였다
(표 2)
Figure PCTKR2011006672-appb-I000002

Claims (12)

  1. 리튬 이차 전지용 양극 활물질의 제조방법에 있어서,니켈 소스, 코발트 소스 및 알루미늄 소스를 함유하는 금속 수용액, 암모니아수, 슈크로스 및 pH조절제를 포함하는 원료를 혼합 반응시켜 활물질 전구체를 제조하는 단계; 및상기 활물질 전구체와 리튬 소스를 혼합하고 소성하여 하기 화학식1의 리튬 이차 전지용 양극 활물질을 제조하는 단계;를 포함하여 제조되는 다공성 리튬 이차 전지용 양극 활물질 제조방법.
    (화학식1)
    Li1+zNi1-x-yCoxAlyO2
    (상기 z는 0 이상 내지 0.3 이하의 실수이고, 상기 x는 0.05 이상 내지 0.3이하의 실수이며, 상기 y는 0 초과 내지 0.3이하의 실수이며, 1-x-y는 0.4 이상 내지 0.95 미만의 실수이다.)
  2. 제1항에 있어서, 상기 슈크로스는 5~30 중량%로 상기 금속 수용액에 함유된 것을 특징으로 하는 리튬 이차 전지용 양극 활물질 제조방법.
  3. 제2항에 있어서,상기 소성은 0.5~1℃/min로 400~500℃까지 승온시키는 1단계; 및 1~2 ℃/min로 800~900℃까지 승온시키는 2단계;로 15~20시간 수행하는 것을 특징으로 하는 리튬 이차 전지용 양극 활물질 제조방법.
  4. 제2항에 있어서, 상기 금속 수용액의 금속 몰농도는 1 내지 3M인 리튬 이차 전지용 양극 활물질 제조방법.
  5. 제4항에 있어서, 상기 금속 수용액은 니켈 : 코발트 : 알루미늄의 몰비가 0.5 내지 0.94 : 0.05 내지 0.3: 0.01 내지 0.3인 리튬 이차 전지용 양극 활물질 제조방법.
  6. 제4항에 있어서,상기 금속 수용액이 0.2~0.5L/hr의 속도로 반응기에 공급되는 리튬 이차 전지용 양극 활물질 제조방법.
  7. 제1항에 있어서,상기 혼합 반응시의 pH는 11~13인 리튬 이차 전지용 양극 활물질 제조방법.
  8. 제1항에 있어서,상기 암모니아수는 상기 금속 수용액의 금속 몰농도에 대하여 0.1 내지 0.25배의 몰농도를 갖는 리튬 이차 전지용 양극 활물질 제조방법.
  9. 제8항에 있어서,상기 암모니아수는 0.02~0.05L/hr의 속도로 공급되는 것을 특징으로 하는 리튬 이차 전지용 양극 활물질 제조방법.
  10. 제1항에 있어서,상기 리튬 소스는 LiOH인 리튬 이차 전지용 양극 활물질 제조방법.
  11. 제1항 내지 제10항에서 선택된 어느 한 항의 제조방법에 의해 제조되며, 총 기공부피가 6.5~8.0x10-2cc/g이며, 비표면적이 0.7~1.0m2/g 이고, 용량이 200~215mAh/g인 리튬 이차 전지용 양극 활물질.
  12. 리튬 이차 전지용 양극 활물질에 있어서,화학식1의 구조를 가지는 다공성 리튬 이차 전지용 양극 활물질.
    (화학식1)
    Li1+zNi1-x-yCoxAlyO2
    (상기 z는 0 이상 내지 0.3 이하의 실수이고, 상기 x는 0.05 이상 내지 0.3이하의 실수이며, 상기 y는 0 초과 내지 0.3이하의 실수이며, 1-x-y는 0.4 이상 내지 0.95 미만의 실수이다.)
PCT/KR2011/006672 2010-09-08 2011-09-08 리튬 이차 전지용 양극 활물질 및 이의 제조방법 WO2012033369A2 (ko)