WO2011071006A1 - はんだペースト用フラックス及びはんだペースト - Google Patents
はんだペースト用フラックス及びはんだペースト Download PDFInfo
- Publication number
- WO2011071006A1 WO2011071006A1 PCT/JP2010/071808 JP2010071808W WO2011071006A1 WO 2011071006 A1 WO2011071006 A1 WO 2011071006A1 JP 2010071808 W JP2010071808 W JP 2010071808W WO 2011071006 A1 WO2011071006 A1 WO 2011071006A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- solder paste
- flux
- meth
- rosin
- solder
- Prior art date
Links
- 229910000679 solder Inorganic materials 0.000 title claims abstract description 172
- 230000004907 flux Effects 0.000 title claims abstract description 74
- RSWGJHLUYNHPMX-UHFFFAOYSA-N Abietic-Saeure Natural products C12CCC(C(C)C)=CC2=CCC2C1(C)CCCC2(C)C(O)=O RSWGJHLUYNHPMX-UHFFFAOYSA-N 0.000 claims abstract description 31
- KHPCPRHQVVSZAH-HUOMCSJISA-N Rosin Natural products O(C/C=C/c1ccccc1)[C@H]1[C@H](O)[C@@H](O)[C@@H](O)[C@@H](CO)O1 KHPCPRHQVVSZAH-HUOMCSJISA-N 0.000 claims abstract description 31
- KHPCPRHQVVSZAH-UHFFFAOYSA-N trans-cinnamyl beta-D-glucopyranoside Natural products OC1C(O)C(O)C(CO)OC1OCC=CC1=CC=CC=C1 KHPCPRHQVVSZAH-UHFFFAOYSA-N 0.000 claims abstract description 31
- 239000004925 Acrylic resin Substances 0.000 claims abstract description 23
- 229920000178 Acrylic resin Polymers 0.000 claims abstract description 23
- CERQOIWHTDAKMF-UHFFFAOYSA-N Methacrylic acid Chemical compound CC(=C)C(O)=O CERQOIWHTDAKMF-UHFFFAOYSA-N 0.000 claims abstract description 19
- 238000010008 shearing Methods 0.000 claims description 10
- 125000000217 alkyl group Chemical group 0.000 claims description 6
- 238000007334 copolymerization reaction Methods 0.000 claims description 5
- 238000000034 method Methods 0.000 abstract description 29
- 238000007650 screen-printing Methods 0.000 abstract description 16
- 125000006733 (C6-C15) alkyl group Chemical group 0.000 abstract 1
- -1 acrylic ester Chemical class 0.000 description 25
- NIXOWILDQLNWCW-UHFFFAOYSA-M Acrylate Chemical compound [O-]C(=O)C=C NIXOWILDQLNWCW-UHFFFAOYSA-M 0.000 description 21
- 229920001903 high density polyethylene Polymers 0.000 description 21
- 239000004700 high-density polyethylene Substances 0.000 description 20
- 239000004743 Polypropylene Substances 0.000 description 18
- 229920001155 polypropylene Polymers 0.000 description 18
- 230000000052 comparative effect Effects 0.000 description 17
- 238000004519 manufacturing process Methods 0.000 description 17
- 239000011135 tin Substances 0.000 description 17
- ATJFFYVFTNAWJD-UHFFFAOYSA-N Tin Chemical compound [Sn] ATJFFYVFTNAWJD-UHFFFAOYSA-N 0.000 description 16
- 239000000843 powder Substances 0.000 description 16
- 229910052751 metal Inorganic materials 0.000 description 15
- 239000002184 metal Substances 0.000 description 15
- 230000006866 deterioration Effects 0.000 description 14
- 239000000203 mixture Substances 0.000 description 14
- 230000008569 process Effects 0.000 description 14
- 239000002904 solvent Substances 0.000 description 14
- 239000002245 particle Substances 0.000 description 12
- 206010016256 fatigue Diseases 0.000 description 11
- 239000007787 solid Substances 0.000 description 10
- 238000010438 heat treatment Methods 0.000 description 9
- 239000011347 resin Substances 0.000 description 9
- 229920005989 resin Polymers 0.000 description 9
- 238000003860 storage Methods 0.000 description 9
- 239000000126 substance Substances 0.000 description 9
- 239000002253 acid Substances 0.000 description 8
- 238000002156 mixing Methods 0.000 description 8
- 230000009477 glass transition Effects 0.000 description 7
- 239000007788 liquid Substances 0.000 description 7
- 238000002844 melting Methods 0.000 description 7
- 230000008018 melting Effects 0.000 description 7
- 238000007639 printing Methods 0.000 description 7
- 229910001128 Sn alloy Inorganic materials 0.000 description 6
- 238000000576 coating method Methods 0.000 description 6
- 239000010949 copper Substances 0.000 description 6
- MTHSVFCYNBDYFN-UHFFFAOYSA-N diethylene glycol Chemical compound OCCOCCO MTHSVFCYNBDYFN-UHFFFAOYSA-N 0.000 description 6
- 230000001965 increasing effect Effects 0.000 description 6
- 238000005096 rolling process Methods 0.000 description 6
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 5
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 5
- BQCADISMDOOEFD-UHFFFAOYSA-N Silver Chemical compound [Ag] BQCADISMDOOEFD-UHFFFAOYSA-N 0.000 description 5
- 230000009471 action Effects 0.000 description 5
- JCXGWMGPZLAOME-UHFFFAOYSA-N bismuth atom Chemical compound [Bi] JCXGWMGPZLAOME-UHFFFAOYSA-N 0.000 description 5
- 229910052802 copper Inorganic materials 0.000 description 5
- 238000005259 measurement Methods 0.000 description 5
- 239000004332 silver Substances 0.000 description 5
- 239000000758 substrate Substances 0.000 description 5
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 description 4
- 238000010586 diagram Methods 0.000 description 4
- 238000004898 kneading Methods 0.000 description 4
- 230000003287 optical effect Effects 0.000 description 4
- 150000003254 radicals Chemical class 0.000 description 4
- 238000007665 sagging Methods 0.000 description 4
- 229910052709 silver Inorganic materials 0.000 description 4
- 238000005476 soldering Methods 0.000 description 4
- ZUHZGEOKBKGPSW-UHFFFAOYSA-N tetraglyme Chemical compound COCCOCCOCCOCCOC ZUHZGEOKBKGPSW-UHFFFAOYSA-N 0.000 description 4
- 239000011701 zinc Substances 0.000 description 4
- 229910001152 Bi alloy Inorganic materials 0.000 description 3
- LYCAIKOWRPUZTN-UHFFFAOYSA-N Ethylene glycol Chemical compound OCCO LYCAIKOWRPUZTN-UHFFFAOYSA-N 0.000 description 3
- 229910000846 In alloy Inorganic materials 0.000 description 3
- NIXOWILDQLNWCW-UHFFFAOYSA-N acrylic acid group Chemical group C(C=C)(=O)O NIXOWILDQLNWCW-UHFFFAOYSA-N 0.000 description 3
- 229910052797 bismuth Inorganic materials 0.000 description 3
- 230000008859 change Effects 0.000 description 3
- 238000009826 distribution Methods 0.000 description 3
- 230000003647 oxidation Effects 0.000 description 3
- 238000007254 oxidation reaction Methods 0.000 description 3
- 239000003381 stabilizer Substances 0.000 description 3
- 238000012360 testing method Methods 0.000 description 3
- 229910052725 zinc Inorganic materials 0.000 description 3
- DTGKSKDOIYIVQL-WEDXCCLWSA-N (+)-borneol Chemical group C1C[C@@]2(C)[C@@H](O)C[C@@H]1C2(C)C DTGKSKDOIYIVQL-WEDXCCLWSA-N 0.000 description 2
- HFDVRLIODXPAHB-UHFFFAOYSA-N 1-tetradecene Chemical compound CCCCCCCCCCCCC=C HFDVRLIODXPAHB-UHFFFAOYSA-N 0.000 description 2
- GZMAAYIALGURDQ-UHFFFAOYSA-N 2-(2-hexoxyethoxy)ethanol Chemical compound CCCCCCOCCOCCO GZMAAYIALGURDQ-UHFFFAOYSA-N 0.000 description 2
- SBASXUCJHJRPEV-UHFFFAOYSA-N 2-(2-methoxyethoxy)ethanol Chemical compound COCCOCCO SBASXUCJHJRPEV-UHFFFAOYSA-N 0.000 description 2
- SVTBMSDMJJWYQN-UHFFFAOYSA-N 2-methylpentane-2,4-diol Chemical compound CC(O)CC(C)(C)O SVTBMSDMJJWYQN-UHFFFAOYSA-N 0.000 description 2
- 229910001316 Ag alloy Inorganic materials 0.000 description 2
- 229910000838 Al alloy Inorganic materials 0.000 description 2
- 229910000881 Cu alloy Inorganic materials 0.000 description 2
- 229910001297 Zn alloy Inorganic materials 0.000 description 2
- 239000012190 activator Substances 0.000 description 2
- 239000000654 additive Substances 0.000 description 2
- WNLRTRBMVRJNCN-UHFFFAOYSA-N adipic acid Chemical compound OC(=O)CCCCC(O)=O WNLRTRBMVRJNCN-UHFFFAOYSA-N 0.000 description 2
- 239000012298 atmosphere Substances 0.000 description 2
- 230000000740 bleeding effect Effects 0.000 description 2
- 238000009835 boiling Methods 0.000 description 2
- BNHZZINHLCTQKT-UHFFFAOYSA-N butyl acetate;2-(2-hydroxyethoxy)ethanol Chemical compound OCCOCCO.CCCCOC(C)=O BNHZZINHLCTQKT-UHFFFAOYSA-N 0.000 description 2
- XSIFPSYPOVKYCO-UHFFFAOYSA-N butyl benzoate Chemical compound CCCCOC(=O)C1=CC=CC=C1 XSIFPSYPOVKYCO-UHFFFAOYSA-N 0.000 description 2
- 230000015556 catabolic process Effects 0.000 description 2
- 238000006243 chemical reaction Methods 0.000 description 2
- 239000011248 coating agent Substances 0.000 description 2
- 238000006731 degradation reaction Methods 0.000 description 2
- FLKPEMZONWLCSK-UHFFFAOYSA-N diethyl phthalate Chemical compound CCOC(=O)C1=CC=CC=C1C(=O)OCC FLKPEMZONWLCSK-UHFFFAOYSA-N 0.000 description 2
- SZXQTJUDPRGNJN-UHFFFAOYSA-N dipropylene glycol Chemical compound OCCCOCCCO SZXQTJUDPRGNJN-UHFFFAOYSA-N 0.000 description 2
- SNRUBQQJIBEYMU-UHFFFAOYSA-N dodecane Chemical compound CCCCCCCCCCCC SNRUBQQJIBEYMU-UHFFFAOYSA-N 0.000 description 2
- 150000002148 esters Chemical class 0.000 description 2
- 239000010931 gold Substances 0.000 description 2
- 230000006872 improvement Effects 0.000 description 2
- APFVFJFRJDLVQX-UHFFFAOYSA-N indium atom Chemical compound [In] APFVFJFRJDLVQX-UHFFFAOYSA-N 0.000 description 2
- 238000009413 insulation Methods 0.000 description 2
- 239000000463 material Substances 0.000 description 2
- 238000006116 polymerization reaction Methods 0.000 description 2
- 238000002360 preparation method Methods 0.000 description 2
- 238000003756 stirring Methods 0.000 description 2
- YFNKIDBQEZZDLK-UHFFFAOYSA-N triglyme Chemical compound COCCOCCOCCOC YFNKIDBQEZZDLK-UHFFFAOYSA-N 0.000 description 2
- 239000003981 vehicle Substances 0.000 description 2
- 230000000007 visual effect Effects 0.000 description 2
- JHPBZFOKBAGZBL-UHFFFAOYSA-N (3-hydroxy-2,2,4-trimethylpentyl) 2-methylprop-2-enoate Chemical compound CC(C)C(O)C(C)(C)COC(=O)C(C)=C JHPBZFOKBAGZBL-UHFFFAOYSA-N 0.000 description 1
- WUOACPNHFRMFPN-SECBINFHSA-N (S)-(-)-alpha-terpineol Chemical compound CC1=CC[C@@H](C(C)(C)O)CC1 WUOACPNHFRMFPN-SECBINFHSA-N 0.000 description 1
- DSESGJJGBBAHNW-UHFFFAOYSA-N (e)-[amino(anilino)methylidene]-phenylazanium;bromide Chemical compound Br.C=1C=CC=CC=1N=C(N)NC1=CC=CC=C1 DSESGJJGBBAHNW-UHFFFAOYSA-N 0.000 description 1
- ALDZNWBBPCZXGH-UHFFFAOYSA-N 12-hydroxyoctadecanamide Chemical compound CCCCCCC(O)CCCCCCCCCCC(N)=O ALDZNWBBPCZXGH-UHFFFAOYSA-N 0.000 description 1
- QAOJBHRZQQDFHA-UHFFFAOYSA-N 2,3-dichlorobenzoic acid Chemical compound OC(=O)C1=CC=CC(Cl)=C1Cl QAOJBHRZQQDFHA-UHFFFAOYSA-N 0.000 description 1
- OAYXUHPQHDHDDZ-UHFFFAOYSA-N 2-(2-butoxyethoxy)ethanol Chemical compound CCCCOCCOCCO OAYXUHPQHDHDDZ-UHFFFAOYSA-N 0.000 description 1
- ZUAURMBNZUCEAF-UHFFFAOYSA-N 2-(2-phenoxyethoxy)ethanol Chemical compound OCCOCCOC1=CC=CC=C1 ZUAURMBNZUCEAF-UHFFFAOYSA-N 0.000 description 1
- OADIZUFHUPTFAG-UHFFFAOYSA-N 2-[2-(2-ethylhexoxy)ethoxy]ethanol Chemical compound CCCCC(CC)COCCOCCO OADIZUFHUPTFAG-UHFFFAOYSA-N 0.000 description 1
- SFPNZPQIIAJXGL-UHFFFAOYSA-N 2-ethoxyethyl 2-methylprop-2-enoate Chemical compound CCOCCOC(=O)C(C)=C SFPNZPQIIAJXGL-UHFFFAOYSA-N 0.000 description 1
- XULHFMYCBKQGEE-UHFFFAOYSA-N 2-hexyl-1-Decanol Chemical compound CCCCCCCCC(CO)CCCCCC XULHFMYCBKQGEE-UHFFFAOYSA-N 0.000 description 1
- KXGFMDJXCMQABM-UHFFFAOYSA-N 2-methoxy-6-methylphenol Chemical class [CH]OC1=CC=CC([CH])=C1O KXGFMDJXCMQABM-UHFFFAOYSA-N 0.000 description 1
- QCDWFXQBSFUVSP-UHFFFAOYSA-N 2-phenoxyethanol Chemical compound OCCOC1=CC=CC=C1 QCDWFXQBSFUVSP-UHFFFAOYSA-N 0.000 description 1
- CUXGDKOCSSIRKK-UHFFFAOYSA-N 7-methyloctyl prop-2-enoate Chemical compound CC(C)CCCCCCOC(=O)C=C CUXGDKOCSSIRKK-UHFFFAOYSA-N 0.000 description 1
- VIZORQUEIQEFRT-UHFFFAOYSA-N Diethyl adipate Chemical compound CCOC(=O)CCCCC(=O)OCC VIZORQUEIQEFRT-UHFFFAOYSA-N 0.000 description 1
- LFQSCWFLJHTTHZ-UHFFFAOYSA-N Ethanol Chemical compound CCO LFQSCWFLJHTTHZ-UHFFFAOYSA-N 0.000 description 1
- JOYRKODLDBILNP-UHFFFAOYSA-N Ethyl urethane Chemical compound CCOC(N)=O JOYRKODLDBILNP-UHFFFAOYSA-N 0.000 description 1
- 229910000990 Ni alloy Inorganic materials 0.000 description 1
- 229910000978 Pb alloy Inorganic materials 0.000 description 1
- ALQSHHUCVQOPAS-UHFFFAOYSA-N Pentane-1,5-diol Chemical compound OCCCCCO ALQSHHUCVQOPAS-UHFFFAOYSA-N 0.000 description 1
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 1
- MZVQCMJNVPIDEA-UHFFFAOYSA-N [CH2]CN(CC)CC Chemical group [CH2]CN(CC)CC MZVQCMJNVPIDEA-UHFFFAOYSA-N 0.000 description 1
- 238000010521 absorption reaction Methods 0.000 description 1
- 239000013543 active substance Substances 0.000 description 1
- 230000000996 additive effect Effects 0.000 description 1
- 235000011037 adipic acid Nutrition 0.000 description 1
- 239000001361 adipic acid Substances 0.000 description 1
- 230000002776 aggregation Effects 0.000 description 1
- 238000004220 aggregation Methods 0.000 description 1
- 229920000180 alkyd Polymers 0.000 description 1
- 229910045601 alloy Inorganic materials 0.000 description 1
- 239000000956 alloy Substances 0.000 description 1
- OVKDFILSBMEKLT-UHFFFAOYSA-N alpha-Terpineol Natural products CC(=C)C1(O)CCC(C)=CC1 OVKDFILSBMEKLT-UHFFFAOYSA-N 0.000 description 1
- 229940088601 alpha-terpineol Drugs 0.000 description 1
- 229910052782 aluminium Inorganic materials 0.000 description 1
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 1
- 239000002518 antifoaming agent Substances 0.000 description 1
- 229910052787 antimony Inorganic materials 0.000 description 1
- WATWJIUSRGPENY-UHFFFAOYSA-N antimony atom Chemical compound [Sb] WATWJIUSRGPENY-UHFFFAOYSA-N 0.000 description 1
- 239000003963 antioxidant agent Substances 0.000 description 1
- 230000003078 antioxidant effect Effects 0.000 description 1
- 238000012662 bulk polymerization Methods 0.000 description 1
- 125000006226 butoxyethyl group Chemical group 0.000 description 1
- 125000000484 butyl group Chemical group [H]C([*])([H])C([H])([H])C([H])([H])C([H])([H])[H] 0.000 description 1
- 239000003054 catalyst Substances 0.000 description 1
- 239000002738 chelating agent Substances 0.000 description 1
- 239000003086 colorant Substances 0.000 description 1
- 150000001875 compounds Chemical class 0.000 description 1
- 229920001577 copolymer Polymers 0.000 description 1
- 230000007797 corrosion Effects 0.000 description 1
- 238000005260 corrosion Methods 0.000 description 1
- 239000006071 cream Substances 0.000 description 1
- 125000000113 cyclohexyl group Chemical group [H]C1([H])C([H])([H])C([H])([H])C([H])(*)C([H])([H])C1([H])[H] 0.000 description 1
- 125000002704 decyl group Chemical group [H]C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])* 0.000 description 1
- 150000004985 diamines Chemical class 0.000 description 1
- 229940028356 diethylene glycol monobutyl ether Drugs 0.000 description 1
- 239000000539 dimer Substances 0.000 description 1
- 239000006185 dispersion Substances 0.000 description 1
- 125000003438 dodecyl group Chemical group [H]C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])* 0.000 description 1
- KWKXNDCHNDYVRT-UHFFFAOYSA-N dodecylbenzene Chemical compound CCCCCCCCCCCCC1=CC=CC=C1 KWKXNDCHNDYVRT-UHFFFAOYSA-N 0.000 description 1
- 230000000694 effects Effects 0.000 description 1
- 238000010556 emulsion polymerization method Methods 0.000 description 1
- 230000002708 enhancing effect Effects 0.000 description 1
- 125000006232 ethoxy propyl group Chemical group [H]C([H])([H])C([H])([H])OC([H])([H])C([H])([H])C([H])([H])* 0.000 description 1
- 125000001495 ethyl group Chemical group [H]C([H])([H])C([H])([H])* 0.000 description 1
- 238000011049 filling Methods 0.000 description 1
- 239000012530 fluid Substances 0.000 description 1
- 238000005243 fluidization Methods 0.000 description 1
- 229910052732 germanium Inorganic materials 0.000 description 1
- GNPVGFCGXDBREM-UHFFFAOYSA-N germanium atom Chemical compound [Ge] GNPVGFCGXDBREM-UHFFFAOYSA-N 0.000 description 1
- PCHJSUWPFVWCPO-UHFFFAOYSA-N gold Chemical compound [Au] PCHJSUWPFVWCPO-UHFFFAOYSA-N 0.000 description 1
- 229910052737 gold Inorganic materials 0.000 description 1
- 125000004051 hexyl group Chemical group [H]C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])* 0.000 description 1
- 229940051250 hexylene glycol Drugs 0.000 description 1
- 229910052738 indium Inorganic materials 0.000 description 1
- 125000000959 isobutyl group Chemical group [H]C([H])([H])C([H])(C([H])([H])[H])C([H])([H])* 0.000 description 1
- 125000001449 isopropyl group Chemical group [H]C([H])([H])C([H])(*)C([H])([H])[H] 0.000 description 1
- 239000006224 matting agent Substances 0.000 description 1
- 238000000691 measurement method Methods 0.000 description 1
- 239000002923 metal particle Substances 0.000 description 1
- 125000002496 methyl group Chemical group [H]C([H])([H])* 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- 125000001421 myristyl group Chemical group [H]C([*])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])[H] 0.000 description 1
- 125000004108 n-butyl group Chemical group [H]C([H])([H])C([H])([H])C([H])([H])C([H])([H])* 0.000 description 1
- 229910052759 nickel Inorganic materials 0.000 description 1
- 125000002347 octyl group Chemical group [H]C([*])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])[H] 0.000 description 1
- JCGNDDUYTRNOFT-UHFFFAOYSA-N oxolane-2,4-dione Chemical compound O=C1COC(=O)C1 JCGNDDUYTRNOFT-UHFFFAOYSA-N 0.000 description 1
- 150000002978 peroxides Chemical class 0.000 description 1
- 229960005323 phenoxyethanol Drugs 0.000 description 1
- 125000001997 phenyl group Chemical group [H]C1=C([H])C([H])=C(*)C([H])=C1[H] 0.000 description 1
- WVDDGKGOMKODPV-ZQBYOMGUSA-N phenyl(114C)methanol Chemical compound O[14CH2]C1=CC=CC=C1 WVDDGKGOMKODPV-ZQBYOMGUSA-N 0.000 description 1
- 230000000704 physical effect Effects 0.000 description 1
- 239000002798 polar solvent Substances 0.000 description 1
- 229920000642 polymer Polymers 0.000 description 1
- 229920000098 polyolefin Polymers 0.000 description 1
- 150000007519 polyprotic acids Polymers 0.000 description 1
- 229920003225 polyurethane elastomer Polymers 0.000 description 1
- 238000012545 processing Methods 0.000 description 1
- 125000006225 propoxyethyl group Chemical group [H]C([H])([H])C([H])([H])C([H])([H])OC([H])([H])C([H])([H])* 0.000 description 1
- 239000007870 radical polymerization initiator Substances 0.000 description 1
- 238000010526 radical polymerization reaction Methods 0.000 description 1
- 230000004044 response Effects 0.000 description 1
- 238000000926 separation method Methods 0.000 description 1
- 229910052710 silicon Inorganic materials 0.000 description 1
- 239000010703 silicon Substances 0.000 description 1
- 125000004079 stearyl group Chemical group [H]C([*])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])[H] 0.000 description 1
- 230000001629 suppression Effects 0.000 description 1
- 238000010558 suspension polymerization method Methods 0.000 description 1
- 238000010408 sweeping Methods 0.000 description 1
- 239000003784 tall oil Substances 0.000 description 1
- JBQYATWDVHIOAR-UHFFFAOYSA-N tellanylidenegermanium Chemical compound [Te]=[Ge] JBQYATWDVHIOAR-UHFFFAOYSA-N 0.000 description 1
- 125000000999 tert-butyl group Chemical group [H]C([H])([H])C(*)(C([H])([H])[H])C([H])([H])[H] 0.000 description 1
- 229940095068 tetradecene Drugs 0.000 description 1
- 230000008719 thickening Effects 0.000 description 1
- 239000010936 titanium Substances 0.000 description 1
- 229910052719 titanium Inorganic materials 0.000 description 1
- 125000001425 triazolyl group Chemical group 0.000 description 1
- ZIBGPFATKBEMQZ-UHFFFAOYSA-N triethylene glycol Chemical compound OCCOCCOCCO ZIBGPFATKBEMQZ-UHFFFAOYSA-N 0.000 description 1
- JLGLQAWTXXGVEM-UHFFFAOYSA-N triethylene glycol monomethyl ether Chemical compound COCCOCCOCCO JLGLQAWTXXGVEM-UHFFFAOYSA-N 0.000 description 1
- 235000021122 unsaturated fatty acids Nutrition 0.000 description 1
- 150000004670 unsaturated fatty acids Chemical class 0.000 description 1
- 239000003190 viscoelastic substance Substances 0.000 description 1
- 239000001993 wax Substances 0.000 description 1
- 238000009736 wetting Methods 0.000 description 1
- 239000002023 wood Substances 0.000 description 1
Images
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
- B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
- B23K35/36—Selection of non-metallic compositions, e.g. coatings, fluxes; Selection of soldering or welding materials, conjoint with selection of non-metallic compositions, both selections being of interest
- B23K35/362—Selection of compositions of fluxes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
- B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
- B23K35/0222—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape for use in soldering, brazing
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
- B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
- B23K35/0222—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape for use in soldering, brazing
- B23K35/0244—Powders, particles or spheres; Preforms made therefrom
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
- B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
- B23K35/0222—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape for use in soldering, brazing
- B23K35/0244—Powders, particles or spheres; Preforms made therefrom
- B23K35/025—Pastes, creams, slurries
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
- B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
- B23K35/24—Selection of soldering or welding materials proper
- B23K35/26—Selection of soldering or welding materials proper with the principal constituent melting at less than 400 degrees C
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
- B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
- B23K35/36—Selection of non-metallic compositions, e.g. coatings, fluxes; Selection of soldering or welding materials, conjoint with selection of non-metallic compositions, both selections being of interest
- B23K35/3612—Selection of non-metallic compositions, e.g. coatings, fluxes; Selection of soldering or welding materials, conjoint with selection of non-metallic compositions, both selections being of interest with organic compounds as principal constituents
- B23K35/3613—Polymers, e.g. resins
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C13/00—Alloys based on tin
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K3/00—Apparatus or processes for manufacturing printed circuits
- H05K3/30—Assembling printed circuits with electric components, e.g. with resistor
- H05K3/32—Assembling printed circuits with electric components, e.g. with resistor electrically connecting electric components or wires to printed circuits
- H05K3/34—Assembling printed circuits with electric components, e.g. with resistor electrically connecting electric components or wires to printed circuits by soldering
- H05K3/3489—Composition of fluxes; Methods of application thereof; Other methods of activating the contact surfaces
Definitions
- the present invention relates to a solder paste flux and a solder paste.
- a screen printing process in a soldering process in which a solder paste is used is mainly classified into four processes shown in FIGS. 1A to 1D.
- First, an appropriate amount of solder paste 16 is applied onto a so-called stencil mask plate 14 made of metal that opens above the electrode 12 disposed on the substrate 10 to be soldered.
- the solder paste 16 is imprinted into the aforementioned opening by a urethane or metal spatula jig called a squeegee 20 (FIG. 1A).
- the solder paste 16 is transferred and applied onto the electrode 12 (FIG. 1B).
- various electronic components 30 are mounted (FIG. 1C).
- the solder metal is melted through a heating temperature raising process called reflow, whereby the electronic component 30 and the electrode 12 on the substrate 10 are joined (FIG. 1D).
- a solder paste is a viscoelastic material having both solid and liquid properties.
- the solder paste exhibits solid properties when left on a stencil mask.
- the solder paste is fluidized by expressing the liquid property in a state where the shearing force is applied by the squeegee.
- the solder paste can be filled in the opening of the mask.
- the solder paste is brought into a stationary state without a load of a shearing force, so that a solid property is expressed again, so that the transferred shape can be maintained.
- solder paste since the solder paste has a solid property and a liquid property as basic physical properties, both properties are required to be appropriately expressed in the screen printing process. If the solder paste is too fluid, bleeding due to printing occurs. On the other hand, if the solder paste is solid and too hard, there may be a problem that a predetermined amount cannot be imprinted in the opening.
- the above process is repeated for a large number of substrates. Specifically, the process of leaving the solder paste after being subjected to a shearing force load by a squeegee is repeated.
- the viscoelastic properties of the solder paste deteriorate due to fatigue and its fluidity increases.
- there have been problems such as bleeding during screen printing, progress of “sag” due to heating, or separation of solder metal and flux. Further, since the screen printing process is usually performed in the atmosphere, the solder metal is repeatedly exposed to the atmosphere.
- solder paste needs to have sufficient resistance to these problems.
- improvement in mass productivity of component mounting has been demanded, and there is an increasing demand for continuous use of solder paste, in other words, realization of solder paste that can withstand long-time printing.
- Patent Document 1 a method using a compound having a triazole structure as a stabilizer
- Patent Document 2 a method using a polyhemiacetal ester resin
- Patent Document 3 a method of coating the solder metal surface with an oxide film
- Patent Document 4 a method of applying a polymer solution containing silicon to the solder metal powder
- Patent Document 5 a soldering flux using a rosin resin as a main component and using a methacrylic ester or an acrylic ester as a solvent has been proposed.
- a solder paste composition for circuit board soldering which does not cause cracks in the flux residue film even when used in an environment where the temperature difference is severe, it does not cause short circuit or corrosion of the circuit of the narrow pitch printed circuit board.
- a solder paste composition for soldering a circuit board using a solder paste flux containing a resin and a rosin resin has been proposed (Patent Document 6).
- a flux for cream solder (Patent Document 7) characterized by containing a copolymer having a rosin structure has been proposed.
- the solderability is deteriorated because the melting of the solder metal is inhibited in the subsequent reflow process.
- an effective measure for improving the fatigue deterioration of the solder paste due to the shear force load repeatedly applied during screen printing has not been confirmed.
- flux and solder paste for solder paste that have moderate fluidity even when repeated shearing force is applied by a screen printing method and suppress fatigue deterioration of viscoelastic properties and various performance deteriorations associated therewith. Providing a strong response to market demands.
- the present invention greatly contributes to the practical application of flux and solder paste that can be sufficiently applied to the mass production of electronic circuit parts, which have been remarkably advanced in recent years, by solving the above technical problems.
- the inventors of the present invention have made extensive studies in order to obtain a solder paste flux and a solder paste that achieve good printability. As a result, it has been found that the printability can be improved by focusing on the mixing ratio of the acrylic resin and the rosin contained in the flux and the solder paste, and giving a specific environment or condition to the solder paste.
- the present invention was created from such a viewpoint.
- One solder paste flux of the present invention is obtained by radical copolymerization of a (meth) acrylate ester having an alkyl group of C 6 or more and C 15 or less and a (meth) acrylate ester other than the (meth) acrylate ester.
- the obtained acrylic resin and rosins are included, and the weight ratio of the above-mentioned acrylic resin when the rosins are 1 is 0.5 or more and 1.2 or less, and the shearing force is 10 Pa or more and 150 Pa or less. Fluidize by giving
- This flux for solder paste contributes to continuous solder paste printability improvement in mass production because fatigue deterioration of viscoelastic properties is suppressed. Moreover, since the solder paste using this flux is fluidized under a specific shear force load environment during screen printing, fatigue deterioration of its viscoelastic characteristics can be suppressed. Therefore, an excellent solder paste can be obtained in that performance degradation can be suppressed even during continuous printing over a long period of time. As a result, it is possible to obtain a flux and a solder paste that can be sufficiently applied to mass production of electronic circuit components that have made remarkable progress in miniaturization.
- solder paste flux of the present invention and one solder paste of the present invention the printability of continuous solder paste during mass production is improved.
- the solder paste flux of the present invention and the solder paste of the present invention can be sufficiently applied to the mass production of electronic circuit components that have made remarkable progress in miniaturization.
- the solder paste flux of the present embodiment is a radical of a (meth) acrylic acid ester having a C 6 or more and C 15 or less alkyl group and a (meth) acrylic acid ester other than the (meth) acrylic acid ester.
- An acrylic resin obtained by copolymerization and rosins are included.
- the weight ratio of the acrylic resin described above when the rosin is 1 is 0.5 or more and 1.2 or less. If it is less than 0.5, the solid property as the solder paste becomes dominant, and there is a risk of fatigue deterioration.
- solder paste flux of this embodiment is fluidized by applying a shearing force of 10 Pa to 150 Pa.
- this acrylic resin is obtained by radical copolymerization of a (meth) acrylic acid ester having an alkyl group of C 6 or more and C 15 or less and a (meth) acrylic acid ester other than the (meth) acrylic acid ester. .
- (meth) acrylic acid ester having an alkyl group of C 6 or more and C 15 or less are hexyl (meth) acrylate, octyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, (meth ) Isononyl acrylate, isobornyl (meth) acrylate, decyl (meth) acrylate, lauryl (meth) acrylate, myristyl (meth) acrylate, cyclohexyl (meth) acrylate, and the like.
- (meth) acrylic acid esters other than the above (meth) acrylic acid esters are methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, and (meth) acrylic acid n.
- typical radical polymerization is a bulk polymerization method, a liquid polymerization method, a suspension polymerization method or an emulsion polymerization method using a radical polymerization initiator such as peroxide as a catalyst, but other known polymerization methods. Can also be applied.
- the weight average molecular weight of the acrylic resin is 6000 or more and 12000 or less and the number average molecular weight is 4000 or more and 6000 or less, from the viewpoint of obtaining excellent crack resistance and excellent viscoelastic properties. It is an aspect. Moreover, it is preferable from the viewpoint of improving the crack resistance and solderability of the flux residue that the content of the acrylic resin contained in the solder paste flux of the present embodiment is 15 wt% or more and 30 wt% or less.
- typical examples of the above-mentioned rosin are ordinary gum rosin, tall oil rosin, or wood rosin.
- Representative examples of the derivatives include resins obtained by heat-treating rosin, disproportionated rosin, polymerized rosin, hydrogenated rosin, formylated rosin, rosin ester, rosin-modified maleic resin, rosin-modified phenolic resin, acrylic acid-added rosin, Or a rosin modified alkyd resin. These rosins and derivatives thereof can be dominant components that affect the viscoelastic properties of the flux and the solder paste using the flux as a base resin of the flux.
- the above-mentioned rosins are at least one selected from the group consisting of acrylic acid-added rosins, disproportionated rosins, polymerized rosins, and hydrogenated rosins, combined with the specific acrylic resin described above.
- This is another preferred embodiment from the viewpoint of controlling the viscoelastic characteristics of the flux and the solder paste using the flux, and suppressing fatigue deterioration under repeated shear load application.
- the solder paste is used for screen printing, it is possible to provide appropriate hardness and deformability and ensure good solderability, so that the content of the rosin is 15% by weight or more. It is another preferred embodiment that it is 30% by weight or less.
- the well-known component which can be used at the time of flux preparation other than each above-mentioned component can be added to the flux of this embodiment.
- known activators, polyolefins, waxes, solvents and the like can be applied as additives.
- the flux of this embodiment is obtained, for example, by radical copolymerization of a (meth) acrylic acid ester having an alkyl group of C 6 or more and C 15 or less and a (meth) acrylic acid ester other than the (meth) acrylic acid ester.
- Acrylic resin (Arakawa Chemical Industries, Ltd .: weight average molecular weight of about 9000, acid value of 0, glass transition temperature of ⁇ 60 ° C.) and rosins (acrylic acid-added rosin, disproportionated rosin, polymerized rosin mixture: Arakawa Chemical Industry Co., Ltd.), diethylene glycol monohexyl ether (manufactured by Nippon Emulsifier Co., Ltd.), adipic acid (manufactured by Tokyo Chemical Industry Co., Ltd.), dichlorobenzoic acid (manufactured by Tokyo Chemical Industry Co., Ltd.), unsaturated Fatty acid dimer (manufactured by Harima Kasei Co., Ltd.), diphenylguanidine hydrobromide (manufactured by Nakao Pharmaceutical Co., Ltd.), high density polyethylene (manufactured by Mitsui Chemicals, Inc.) Ethylenebis 12-hydroxystearic acid amide (manufactured by N
- each component described above is heated and dissolved and / or mixed at one time or sequentially, and then cooled.
- a known apparatus such as a kneading apparatus, a vacuum stirring apparatus, a homodisper, a three-one motor, or a planetary mixer can be applied as an apparatus for dissolving or mixing the above-described components.
- the mixing temperature of each above-mentioned component is not specifically limited. However, it is a preferable embodiment to dissolve the above-mentioned components by heating at a temperature lower than the boiling point of the solvent used for mixing. Other known flux manufacturing processes can also be applied to this embodiment.
- solder paste of this embodiment a solder powder having a composition ratio in which tin is 96.5% by weight, silver is 3.0% by weight, and copper is 0.5% by weight.
- each above-mentioned numerical value shows the weight ratio of each metal.
- the solder paste of this embodiment is kneaded and blended with one or a plurality of types of solder paste fluxes of this embodiment including the preferred mode disclosed in the first embodiment and the above-described solder powder by a known means.
- a known means such as a vacuum stirring device, a kneading device, or a planetary mixer can be applied as a device for kneading and blending the above-described components.
- the manufacturing method of this embodiment is not specifically limited. However, the treatment is preferably performed at 5 ° C. or more and 50 ° C.
- the manufacturing method of this embodiment is not specifically limited. However, from the viewpoint of printing workability and paste stability, it is preferable that the weight ratio of the solder powder is 80 or more and 95 or less with respect to the weight ratio of 5 or more and 20 or less.
- solder paste of the present embodiment is an antioxidant, a matting agent, a colorant, an antifoaming agent, a dispersion stabilizer, a chelating agent, etc.
- the composition of the solder powder used in the solder paste of the present embodiment is not particularly limited to the above-described solder powder.
- solder powder tin (Sn), copper (Cu), zinc (Zn), silver (Ag), antimony (Sb), lead (Pb), indium (In), bismuth (Bi), nickel (Ni),
- solder powder containing one or more selected from the group consisting of aluminum (Al), gold (Au), and germanium (Ge).
- tin / lead alloys tin / silver alloys, tin / silver / copper alloys, tin / silver / bismuth / indium, tin / copper alloys, tin / copper / nickel, tin / zinc alloys, tin / zinc / bismuth.
- One or two selected from the group consisting of alloys, tin / zinc / aluminum alloys, tin / zinc / bismuth / aluminum alloys, tin / zinc / bismuth / indium alloys, tin / bismuth alloys, and tin / indium alloys Solder powder containing more than a seed is another example.
- the shape of the solder powder is preferably a perfect sphere or a substantially true sphere. Moreover, if the particle size of the solder powder is normal, it can be mixed with the flux disclosed in the first embodiment. For example, when true spherical solder powder is employed, it is preferable that solder powder having a diameter of 5 ⁇ m or more and 60 ⁇ m or less is employed in terms of achieving high precision in mounting of minute electronic components. Further, the composition ratio of the composition constituting the solder powder is not particularly limited. For example, Sn63 / Pb37, Sn96.5 / Ag3.5, Sn96 / Ag3.5 / Cu0.5, Sn96.6 / Ag2.9 / Cu0.5, Sn96.5 / Ag3.0 / Cu0.5, etc. An example of a suitable solder powder is mentioned. In addition, each above-mentioned numerical value shows the weight ratio of each metal.
- the solder paste of this embodiment manufactured by the above-described method is very excellent in the printability of the continuous solder paste at the time of mass production.
- mode that the elasticity modulus in the normal temperature of the solder paste of this embodiment is 1000 Pa or more and 100000 Pa or less. It is.
- a solvent may be used as necessary.
- the kind of solvent is not specifically limited. However, it is preferable that a solvent having a boiling point of 150 ° C. or higher is used because it is difficult to evaporate during the manufacture of the solder paste.
- triethylene glycol monomethyl ether triethylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, diethylene glycol monomethyl ether, diethylene glycol monobutyl ether, diethylene glycol monohexyl ether, ethylene glycol monophenyl ether, diethylene glycol monophenyl ether, diethylene glycol monobutyl acetate, Dipropylene glycol, diethylene glycol-2-ethylhexyl ether, ⁇ -terpineol, benzyl alcohol, 2-hexyldecanol, butyl benzoate, diethyl adipate, diethyl phthalate, dodecane, tetradecene, dodecylbenzene, ethylene glycol, diethylene glycol, dipropylene Glycol, triethylene glycol, hexylene glycol, 1,5-pentanediol, methyl carbitol, butyl carbitol.
- a preferred example of the solvent used in the present embodiment is a polar solvent that can be easily made into a solution by dissolving components such as an activator and a resin.
- an alcohol type is used, and particularly, diethylene glycol monoethers are excellent in volatility and solubility of the active agent.
- the usage-amount of the solvent is not restrict
- the solvent is 15 parts by weight or more and 40 parts by weight or less with respect to 100 parts by weight of the flux.
- the total amount of these solvents is preferably within the above-mentioned range. Further, from the above viewpoint, it is more preferable that the solvent is 20 parts by weight or more and 35 parts by weight or less.
- solder paste flux prepared using each component listed in Table 1, and solder powder (tin: 96.5% by weight, silver: 3.0) whose particle size distribution corresponds to Type 4 in the IPC standard
- a solder paste was prepared by mixing 89 parts by weight of copper (0.5% by weight, copper: 0.5% by weight) with a planetary mixer.
- the average particle diameter of the high-density polyethylene used for the preparation of the solder paste flux was about 20 ⁇ m
- the viscosity molecular weight was about 3000
- the melting point was 120 ° C.
- the acid value was 0,
- glass transition temperature was ⁇ 50 ° C.
- the acrylic resin had a weight average molecular weight of about 9000, an acid value of 0, and a glass transition temperature of ⁇ 60 ° C.
- Example 1 the point at which the dynamic storage elastic modulus and the dynamic loss elastic modulus measured as described above become equal is that the solid substance changes to a liquid substance when an extremely low shear stress is applied. Evaluate to be the fluidization point.
- Example 2 solder paste (sample) of Example 1 for 4 hours. Specifically, using a polyurethane rubber squeegee (hardness 90), squeezing was continuously performed for 4 hours under the conditions of a squeegee angle of 60 °, a printing tact time of 30 seconds, and a stroke of 300 mm. Note that the amount of sample input was 500 g. The dynamic viscoelasticity measurement similar to that described above was performed on the sample after continuous rolling obtained in this manner.
- Example 2 The solder paste of Example 2 is manufactured in the same manner as Example 1.
- the solder paste of Example 2 is the same as Example 1 except that the composition ratio of the acrylic resin and the rosins in the solder paste flux is different from that of Example 1. Therefore, the overlapping description is omitted.
- Example 3 The solder paste of Example 3 is manufactured in the same manner as Example 1.
- the solder paste of Example 3 is the same as Example 1 except that the composition ratio of the acrylic resin and the rosins in the solder paste flux is different from that of Example 1. Therefore, the overlapping description is omitted.
- Example 4 The solder paste of Example 4 is manufactured in the same manner as Example 1.
- the solder paste of Example 4 is the same as Example 1 except that the composition ratio of acrylic resin and rosins in the solder paste flux is different from that of Example 1. Therefore, the overlapping description is omitted.
- Comparative Example 1 The solder paste of Comparative Example 1 is manufactured in the same manner as in Example 1.
- the solder paste of Comparative Example 1 is the same as Example 1 except that the composition ratio of the acrylic resin and the rosin of the solder paste flux is different from those of Example 1. Therefore, the overlapping description is omitted.
- Comparative Example 2 The solder paste of Comparative Example 2 is manufactured in the same manner as in Example 1.
- the solder paste of Comparative Example 2 is the same as Example 1 except that the composition ratio of the acrylic resin and the rosin in the solder paste flux is different from that of Example 1. Therefore, the overlapping description is omitted.
- FIG. 2 is a graph showing the dynamic viscoelasticity measurement results of the solder paste (hereinafter also referred to as sample 1A) in Example 1.
- Table 2 is a table that simply shows the results of measurement of the solder paste dynamic viscoelasticity of Examples 1 to 4, Comparative Example 1, and Comparative Example 2.
- Table 3 is a table that briefly shows each performance of Examples 1 to 4, Comparative Example 1, and Comparative Example 2.
- the dynamic storage elastic modulus when a shear stress of 9.9 Pa was applied was 4950 Pa. It was. Moreover, since the dynamic storage elastic modulus at that time is larger than the dynamic loss elastic modulus, it can be determined that the sample 1A is a solid substance. However, when a shearing stress of 59.6 Pa is applied to the sample 1A, the dynamic storage elastic modulus and the dynamic loss elastic modulus are the same value (1176 Pa), so this shear stress value is determined as the flow start point. it can.
- the above-mentioned continuous rolling (squeezing) test was performed on the sample 1A for 4 hours.
- the dynamic storage elastic modulus when a shear stress of 9.9 Pa was applied was 7570 Pa.
- the dynamic storage elastic modulus at that time is larger than the dynamic loss elastic modulus, it can be determined that the sample 1B is a solid substance.
- the dynamic storage elastic modulus and the dynamic loss elastic modulus are the same value (1228 Pa), so this shear stress value is determined as the flow start point. it can.
- the flow start point is slightly shifted to the high shear stress side, but the shift amount (hereinafter also referred to as S value) is only 100 Pa or less. That is, it can be seen that the solder paste of Example 1 contains a flux with a very small change in viscoelastic properties, that is, fatigue suppression. Therefore, it has been clarified that the use of the solder flux of Example 1 greatly suppresses deterioration of printability and solderability of the continuous solder paste.
- Example 1 the dynamic viscoelasticity of the solder pastes of Examples 2 to 4 was measured.
- each of the solder pastes of Example 2 to Example 4 contains a flux having a very small amount of change in viscoelastic characteristics, that is, a fatigue deterioration-suppressed, like the solder paste of Example 1. I understood that. Therefore, even when any solder flux of Example 2 to Example 4 was used, it became clear that deterioration of printability and solderability of continuous solder paste was greatly suppressed. .
- the solder paste of Comparative Example 1 had an S value of 100 Pa or more.
- the solder paste of Comparative Example 1 has a large amount of change in viscoelastic properties, that is, contains a flux that causes fatigue deterioration, and therefore has poor printability and solderability of continuous solder paste during mass production.
- the storage elastic modulus was already smaller than the loss elastic modulus in the initial state before continuous rolling, in other words, there was no S value.
- the solder paste of Comparative Example 2 had a liquid high fluidity, and maintained high fluidity even after 4 hours of continuous rolling. Therefore, such a material having high fluidity is not preferable as a solder paste used for screen printing because the paste transferred onto the substrate cannot maintain its form.
- high density polyethylene is contained in the flux or solder paste as a resin additive.
- the particle size, particle size distribution, or shape of the particulate high density polyethylene satisfy at least one of the following conditions a) to d): It is. a) The average particle diameter of the longest diameter of the high density polyethylene is 0.001 ⁇ m or more and 50 ⁇ m or less.
- the number of solder paste fluxes selected at random is 3.1 mm ⁇ 2.3 mm when observed with an optical microscope at a magnification of 100 times.
- the number of high-density polyethylene having a longest particle diameter in the field of view of 100 ⁇ m or more is 1% or less of the total number of the high-density polyethylene.
- the high-density polyethylene is polyhedral. Satisfaction with heating is improved by satisfying the above-mentioned conditions.
- the probability that the high-density polyethylene in the flux or solder paste is arranged on the miniaturized electrode or the like is increased, the applicability to miniaturization of electronic circuit components and the like is further increased.
- Many high density polyethylenes are polyhedral. It is more preferable to satisfy two or more of the above conditions a) to d) at the same time, and it is more preferable to satisfy all the conditions at the same time.
- the viscosity molecular weight of the high-density polyethylene is 1500 or more and 4500 or less. If this viscosity molecular weight range is satisfied, the “sagging” suppressing action during heating is further improved.
- the melting point of the high-density polyethylene is 110 ° C. or higher and 130 ° C. or lower. If this melting point range is satisfied, the “sagging” suppressing action during heating is further improved.
- the acid value of the high-density polyethylene is 1 or less. If this acid value range is satisfied, it is possible to prevent a decrease in insulation reliability due to the addition of high-density polyethylene.
- the glass transition temperature of the high-density polyethylene is ⁇ 50 ° C. or lower. If the range of this glass transition temperature is satisfied, it is possible to suppress the deterioration of the crack resistance of the flux residue, which is particularly required for pastes for in-vehicle electronic components.
- the particle size, particle size distribution, or shape of the particulate polypropylene satisfies at least one of the following conditions a) to d). a) The average particle diameter of the longest diameter of the polypropylene is 0.001 ⁇ m or more and 50 ⁇ m or less.
- the viscosity molecular weight of polypropylene is 5000 or more and 20000 or less. If this viscosity molecular weight range is satisfied, the “sagging” suppressing action during heating is further improved.
- the melting point of polypropylene is 130 ° C. or higher and 160 ° C. or lower. If this melting point range is satisfied, the “sagging” suppressing action during heating is further improved.
- the acid value of polypropylene is 1 or less. If this acid value range is satisfied, a decrease in insulation reliability due to the addition of polypropylene can be prevented.
- the glass transition temperature of polypropylene is 0 ° C. or lower. If the range of this glass transition temperature is satisfied, it is possible to suppress the deterioration of the crack resistance of the flux residue, which is particularly required for pastes for in-vehicle electronic components.
- solder paste containing the above-mentioned high-density polyethylene and / or the above-mentioned polypropylene has a melting point of 100 ° C. or higher obtained by dehydrating higher aliphatic monocarboxylic acid, polybasic acid, and diamine. It is another preferred embodiment to further include a waxy product. This waxy product can assist the action of the high density polyethylene or polypropylene described above.
- solder paste flux and solder paste of the present invention are extremely useful for solder connection for various uses such as electronic circuit components.
Landscapes
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Chemical & Material Sciences (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Manufacturing & Machinery (AREA)
- Microelectronics & Electronic Packaging (AREA)
- Electric Connection Of Electric Components To Printed Circuits (AREA)
- Macromonomer-Based Addition Polymer (AREA)
Priority Applications (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020127016875A KR101414296B1 (ko) | 2009-12-08 | 2010-12-06 | 땜납 페이스트용 플럭스 및 땜납 페이스트 |
US13/513,880 US20120291921A1 (en) | 2009-12-08 | 2010-12-06 | Flux for solder paste, and solder paste |
CN201080055183.7A CN102770232B (zh) | 2009-12-08 | 2010-12-06 | 焊膏用助焊剂及焊膏 |
CA2781958A CA2781958C (en) | 2009-12-08 | 2010-12-06 | Flux for solder paste and solder paste |
EP10835926.6A EP2511043B1 (de) | 2009-12-08 | 2010-12-06 | Flussmittel für eine lötpaste und lötpaste |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2009278210A JP5486282B2 (ja) | 2009-12-08 | 2009-12-08 | はんだペースト用フラックス及びはんだペースト |
JP2009-278210 | 2009-12-08 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2011071006A1 true WO2011071006A1 (ja) | 2011-06-16 |
Family
ID=44145550
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2010/071808 WO2011071006A1 (ja) | 2009-12-08 | 2010-12-06 | はんだペースト用フラックス及びはんだペースト |
Country Status (9)
Country | Link |
---|---|
US (1) | US20120291921A1 (de) |
EP (1) | EP2511043B1 (de) |
JP (1) | JP5486282B2 (de) |
KR (1) | KR101414296B1 (de) |
CN (1) | CN102770232B (de) |
CA (1) | CA2781958C (de) |
MY (1) | MY156299A (de) |
TW (1) | TWI488705B (de) |
WO (1) | WO2011071006A1 (de) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2022270282A1 (ja) * | 2021-06-25 | 2022-12-29 | 千住金属工業株式会社 | ソルダペーストおよび電子装置の製造方法 |
Families Citing this family (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP6196036B2 (ja) * | 2012-12-26 | 2017-09-13 | ハリマ化成株式会社 | フラックスおよびはんだペースト |
JP6259623B2 (ja) * | 2013-09-30 | 2018-01-10 | 株式会社タムラ製作所 | 低酸価アクリル樹脂含有はんだ付け用フラックスおよびはんだペースト組成物 |
JP6215633B2 (ja) | 2013-09-30 | 2017-10-18 | 株式会社タムラ製作所 | ロジン含有量を低減させたはんだ付け用フラックスおよびはんだペースト組成物 |
US9764430B2 (en) * | 2014-02-24 | 2017-09-19 | Koki Company Limited | Lead-free solder alloy, solder material and joined structure |
CN106736010A (zh) * | 2016-11-30 | 2017-05-31 | 安徽华众焊业有限公司 | 铜锌钎焊膏 |
CN107052614A (zh) * | 2016-11-30 | 2017-08-18 | 安徽华众焊业有限公司 | 无银黄铜焊料 |
JP6560283B2 (ja) * | 2017-03-17 | 2019-08-14 | 株式会社タムラ製作所 | フラックス組成物及びソルダペースト |
WO2019142826A1 (ja) * | 2018-01-16 | 2019-07-25 | 千住金属工業株式会社 | フラックス及びソルダペースト |
EP3950983A4 (de) * | 2019-03-29 | 2023-04-19 | Senju Metal Industry Co., Ltd. | Harzzusammensetzung zum löten, lötzusammensetzung, lot mit flussmittelkern, flussmittel und lötpaste |
HUE061641T2 (hu) * | 2019-12-10 | 2023-07-28 | Heraeus Deutschland Gmbh & Co Kg | Forrasztópaszta |
CN111940946A (zh) * | 2020-08-17 | 2020-11-17 | 惠州市源德智科技有限公司 | 一种快速固化的无铅锡膏及其制备方法 |
CN116529021B (zh) * | 2020-11-18 | 2024-03-08 | 千住金属工业株式会社 | 助焊剂及焊膏 |
US11986910B2 (en) | 2020-11-18 | 2024-05-21 | Senju Metal Industry Co., Ltd. | Flux and solder paste |
CN115401358B (zh) * | 2022-09-13 | 2023-12-19 | 苏州优诺电子材料科技有限公司 | 一种光固化焊锡膏及其制备方法 |
Citations (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS61199598A (ja) | 1985-02-28 | 1986-09-04 | Sony Corp | はんだ付用フラツクス及びクリ−ムはんだ |
JP2001150184A (ja) | 1999-12-01 | 2001-06-05 | Tamura Kaken Co Ltd | リフローはんだ付用ソルダーペースト組成物及び回路基板 |
JP2003164992A (ja) | 2001-11-29 | 2003-06-10 | Nippon Handa Kk | はんだ付け用フラックスおよびクリームはんだ |
JP2004209494A (ja) | 2002-12-27 | 2004-07-29 | Mitsui Mining & Smelting Co Ltd | はんだペースト用はんだ粉 |
JP2006088205A (ja) | 2004-09-24 | 2006-04-06 | Toshiba Corp | 接合材の製造方法及びその製造方法により得られた接合材 |
JP2006205203A (ja) | 2005-01-27 | 2006-08-10 | Nof Corp | はんだ付け用フラックス組成物およびはんだペースト |
JP2007222932A (ja) * | 2006-02-27 | 2007-09-06 | Arakawa Chem Ind Co Ltd | プリコート用鉛フリーソルダーペースト、プリコート用鉛フリーソルダーペーストに用いるフラックス |
JP2008062242A (ja) * | 2006-09-04 | 2008-03-21 | Harima Chem Inc | はんだ付け用フラックスおよびはんだペースト組成物 |
JP2008110370A (ja) * | 2006-10-30 | 2008-05-15 | Arakawa Chem Ind Co Ltd | クリームはんだ用フラックスおよびクリームはんだ |
JP2008110369A (ja) * | 2006-10-30 | 2008-05-15 | Arakawa Chem Ind Co Ltd | クリームはんだ用フラックスおよびクリームはんだ |
JP2008110365A (ja) | 2006-10-30 | 2008-05-15 | Arakawa Chem Ind Co Ltd | クリームはんだ用フラックスおよびクリームはんだ |
Family Cites Families (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3378139B2 (ja) * | 1996-03-19 | 2003-02-17 | 株式会社デンソー | はんだ付け用のフラックス |
JP4485652B2 (ja) * | 2000-06-07 | 2010-06-23 | 昭和電工株式会社 | ハンダペースト用フラックスの製造方法 |
JP2002336992A (ja) * | 2001-05-14 | 2002-11-26 | Nec Corp | 回路基板はんだ付用はんだ加工物及び回路基板 |
JP2008062253A (ja) * | 2006-09-05 | 2008-03-21 | Denso Corp | はんだ付け用フラックスおよびはんだペースト組成物 |
CN100479975C (zh) * | 2007-07-17 | 2009-04-22 | 西安理工大学 | 一种用于锡铅焊膏的低松香免清洗助焊剂及其制备方法 |
CN100528462C (zh) * | 2007-07-17 | 2009-08-19 | 西安理工大学 | 用于SnAgCu系无铅焊膏的低松香免清洗助焊剂及其制备方法 |
KR101142815B1 (ko) * | 2008-02-22 | 2012-05-08 | 하리마 카세이 가부시키가이샤 | 땜납 접합 구조 및 납땜용 플럭스 |
CN101486095B (zh) * | 2009-02-27 | 2012-08-15 | 北京工业大学 | 焊粉抗氧化有机包覆方法 |
-
2009
- 2009-12-08 JP JP2009278210A patent/JP5486282B2/ja active Active
-
2010
- 2010-12-06 CN CN201080055183.7A patent/CN102770232B/zh active Active
- 2010-12-06 KR KR1020127016875A patent/KR101414296B1/ko active IP Right Grant
- 2010-12-06 WO PCT/JP2010/071808 patent/WO2011071006A1/ja active Application Filing
- 2010-12-06 EP EP10835926.6A patent/EP2511043B1/de active Active
- 2010-12-06 US US13/513,880 patent/US20120291921A1/en not_active Abandoned
- 2010-12-06 MY MYPI2012002437A patent/MY156299A/en unknown
- 2010-12-06 CA CA2781958A patent/CA2781958C/en active Active
- 2010-12-07 TW TW099142666A patent/TWI488705B/zh active
Patent Citations (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS61199598A (ja) | 1985-02-28 | 1986-09-04 | Sony Corp | はんだ付用フラツクス及びクリ−ムはんだ |
JP2001150184A (ja) | 1999-12-01 | 2001-06-05 | Tamura Kaken Co Ltd | リフローはんだ付用ソルダーペースト組成物及び回路基板 |
JP2003164992A (ja) | 2001-11-29 | 2003-06-10 | Nippon Handa Kk | はんだ付け用フラックスおよびクリームはんだ |
JP2004209494A (ja) | 2002-12-27 | 2004-07-29 | Mitsui Mining & Smelting Co Ltd | はんだペースト用はんだ粉 |
JP2006088205A (ja) | 2004-09-24 | 2006-04-06 | Toshiba Corp | 接合材の製造方法及びその製造方法により得られた接合材 |
JP2006205203A (ja) | 2005-01-27 | 2006-08-10 | Nof Corp | はんだ付け用フラックス組成物およびはんだペースト |
JP2007222932A (ja) * | 2006-02-27 | 2007-09-06 | Arakawa Chem Ind Co Ltd | プリコート用鉛フリーソルダーペースト、プリコート用鉛フリーソルダーペーストに用いるフラックス |
JP2008062242A (ja) * | 2006-09-04 | 2008-03-21 | Harima Chem Inc | はんだ付け用フラックスおよびはんだペースト組成物 |
JP2008110370A (ja) * | 2006-10-30 | 2008-05-15 | Arakawa Chem Ind Co Ltd | クリームはんだ用フラックスおよびクリームはんだ |
JP2008110369A (ja) * | 2006-10-30 | 2008-05-15 | Arakawa Chem Ind Co Ltd | クリームはんだ用フラックスおよびクリームはんだ |
JP2008110365A (ja) | 2006-10-30 | 2008-05-15 | Arakawa Chem Ind Co Ltd | クリームはんだ用フラックスおよびクリームはんだ |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2022270282A1 (ja) * | 2021-06-25 | 2022-12-29 | 千住金属工業株式会社 | ソルダペーストおよび電子装置の製造方法 |
Also Published As
Publication number | Publication date |
---|---|
JP5486282B2 (ja) | 2014-05-07 |
US20120291921A1 (en) | 2012-11-22 |
CA2781958A1 (en) | 2011-06-16 |
CA2781958C (en) | 2015-04-07 |
EP2511043A1 (de) | 2012-10-17 |
KR101414296B1 (ko) | 2014-07-02 |
MY156299A (en) | 2016-01-29 |
JP2011121059A (ja) | 2011-06-23 |
EP2511043B1 (de) | 2018-07-11 |
CN102770232A (zh) | 2012-11-07 |
KR20120092683A (ko) | 2012-08-21 |
EP2511043A4 (de) | 2016-06-29 |
TW201124226A (en) | 2011-07-16 |
TWI488705B (zh) | 2015-06-21 |
CN102770232B (zh) | 2015-05-27 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP5486282B2 (ja) | はんだペースト用フラックス及びはんだペースト | |
JP6310894B2 (ja) | はんだ組成物および電子基板の製造方法 | |
TWI517929B (zh) | Solder paste | |
JP5324007B1 (ja) | はんだ合金、ソルダペーストおよび電子回路基板 | |
JP5238088B1 (ja) | はんだ合金、ソルダペーストおよび電子回路基板 | |
US10099321B2 (en) | Flux and solder paste | |
JP5856747B2 (ja) | はんだ付け用フラックスおよびはんだペースト組成物 | |
WO2012056753A1 (ja) | 低銀はんだ合金およびはんだペースト組成物 | |
JP2012004347A (ja) | はんだバンプ形成方法 | |
US20060043157A1 (en) | Flux for soldering, soldering method, and printed circuit board | |
JP5481753B2 (ja) | フラックス組成物及びはんだペースト組成物 | |
JP2020006402A (ja) | 低残渣ソルダペースト | |
JP6383587B2 (ja) | フラックス組成物、はんだ組成物、および電子基板の製造方法 | |
JP2017185541A (ja) | はんだペースト | |
JP7324024B2 (ja) | フラックス及びソルダペースト | |
JP7220694B2 (ja) | フラックス組成物、およびはんだ組成物、並びに、電子基板の製造方法 | |
JP2024046430A (ja) | フラックス組成物、はんだ組成物、および電子基板 | |
EP4144477A1 (de) | Lotzusammensetzung und verfahren zur herstellung elektronischer platte | |
JP2024052526A (ja) | フラックス組成物、はんだ組成物、および電子基板 | |
JP2024046403A (ja) | フラックス組成物、はんだ組成物、および電子基板 | |
JP2004058104A (ja) | はんだ付け用フラックス及びはんだペースト |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 201080055183.7 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 10835926 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2781958 Country of ref document: CA |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1201002676 Country of ref document: TH |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2010835926 Country of ref document: EP |
|
ENP | Entry into the national phase |
Ref document number: 20127016875 Country of ref document: KR Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 13513880 Country of ref document: US |