WO2011062192A1 - 熱アシスト記録用磁気記録媒体に用いられるＡｇ合金熱拡散制御膜、及び熱アシスト記録用磁気記録媒体、スパッタリングターゲット - Google Patents

熱アシスト記録用磁気記録媒体に用いられるＡｇ合金熱拡散制御膜、及び熱アシスト記録用磁気記録媒体、スパッタリングターゲット Download PDF

Info

Publication number
WO2011062192A1
WO2011062192A1 PCT/JP2010/070486 JP2010070486W WO2011062192A1 WO 2011062192 A1 WO2011062192 A1 WO 2011062192A1 JP 2010070486 W JP2010070486 W JP 2010070486W WO 2011062192 A1 WO2011062192 A1 WO 2011062192A1
Authority
WO
WIPO (PCT)
Prior art keywords
alloy
diffusion control
atomic
control film
recording medium
Prior art date
Application number
PCT/JP2010/070486
Other languages
English (en)
French (fr)
Inventor
中井　淳一
田内　裕基
Original Assignee
株式会社神戸製鋼所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社神戸製鋼所 filed Critical 株式会社神戸製鋼所
Priority to CN2010800522891A priority Critical patent/CN102612713A/zh
Priority to EP10831586.2A priority patent/EP2503549A4/en
Priority to US13/509,196 priority patent/US20120225323A1/en
Publication of WO2011062192A1 publication Critical patent/WO2011062192A1/ja

Abstract

　熱アシスト記録用磁気媒体に用いられる熱拡散制御膜であって、高い熱伝導率を維持すると共に、高い熱拡散率、平滑な表面粗さ、および高い耐熱性の全てを兼ね備えたＡｇ合金熱拡散制御膜を提供する。本発明は、熱アシスト記録用磁気記録媒体に用いられる熱拡散制御膜であって、Ａｇを主成分とするＡｇ合金から構成されており、表面粗さＲａ１．０ｎｍ以下、熱伝導率１００Ｗ／（ｍ・Ｋ）以上、熱拡散率４．０×１０-５ｍ２／ｓｅｃ以上を満足するＡｇ合金熱拡散制御膜に関する。

Description

[規則37.2に基づきISAが決定した発明の名称]　熱アシスト記録用磁気記録媒体に用いられるＡｇ合金熱拡散制御膜、及び熱アシスト記録用磁気記録媒体、スパッタリングターゲット
　本発明は、記録過程でレーザー光または近接場光による局所的な加熱で磁気記録を補助する熱アシスト記録方式［ｈｅａｔ－ａｓｓｉｓｔｅｄ ｍａｇｎｅｔｉｃ ｒｅｃｏｒｄｉｎｇ（ＨＡＭＲ）］用のハードディスクドライブに用いられる磁気記録媒体において、基板と、記録膜または下地層との間に形成される熱拡散制御膜として有用なＡｇ合金薄膜、及びそれを用いて構成される磁気記録媒体に関するものである。
　磁気記録媒体は、近年、記録容量に対する要求が一層増しており、このため磁気記録媒体の面記録密度もさらに上昇している。一方、磁気記録媒体の記録密度上昇に伴って１ビット当たりの磁気記録媒体の体積は減少することから、熱擾乱により記録減磁の問題が顕在化している。
　このような問題に対し、例えば水平記録から垂直記録への記録方式の変更や、記録層の構成変更などにより対処する方法が提案されているが、これは、本質的な問題解決ではない。上述した熱擾乱による記録減磁は、磁気記録材料の有する結晶磁気異方性定数（Ｋｕ）と１ビット当たりの体積（ｖ）に対して、ｅｘｐ（－ｖＫｕ／ｋＴ）（ｋ：ボルツマン定数、Ｔ：絶対温度）で表される関数に依存して増加する。すなわち、記録密度増大のために１ビット当たりの体積（ｖ）を低減する場合に、それに見合ったＫｕの増加が必要となるが、Ｋｕは材料固有の値であり、軟磁性記録材料として汎用されているＣｏＣｒＰｔ系等のＫｕは低く、このような要請に充分応えることができない。
　そのため、より結晶磁気異方性の高い材料の提供を目指して、ＣｏＰｔ、ＦｅＰｔ等の規則化合金が検討されている。しかしながら、これら高結晶磁気異方性の材料は、現状の記録ヘッドの記録可能な磁界で記録できないという問題がある。
　そこで、記録材料の結晶磁気異方性が温度と共に減少することを利用して、記録時のみ対象領域をレーザー光、または近接場光を用いて加熱する熱アシスト記録方式が提案されている。熱アシスト記録方式は、磁気記録技術と光記録技術を融合した記録方式であり、通常の磁気記録では記録できないような高保持力媒体に対して、レーザー光の照射による熱で記録磁気部分の保持力を局所的に下げて記録した後、室温まで急冷して保持力を大きくして保存するというものである。
　熱アシスト記録方式では、記録時における加熱後は速やかに冷却されることが望ましいことから、熱拡散を促進するために、基板と下地層または記録膜との間に、高い熱伝導率を有する熱拡散制御膜が配置されている。図１に、熱拡散制御膜を有する熱アシスト磁気記録媒体の膜構成の一例を示す。
　このような熱アシスト記録方式の磁気記録媒体として、例えば特許文献１及び２が挙げられる。これらの文献には、熱拡散制御膜として、Ｃｕ，Ａｇ，Ａｕ，Ｗ，Ｓｉ，Ｍｏを含むヒートシンク層（特許文献１）；Ａｌ，Ｎｉ，Ａｕ，Ａｇ，Ｃｕ，Ｒｈ，Ｐｔ，Ｒｕを母元素として、これにＡｌ，Ｎｉ，Ａｕ，Ａｇ，Ｃｕ，Ｒｈ，Ｐｔ，Ｐｄ，Ｔｉ，Ｔａ，Ｎｂ，Ｃｒ，Ｚｒ，Ｖの元素を含む熱制御層（特許文献２）が開示されている。
日本国特開２００８－２１０４２６号公報 日本国特開２００８－３４０７８号公報
　これらのうち、Ａｕ、Ｃｕ、Ａｇの熱伝導率（バルクのデータ）は、理化学事典等によれば、Ａｕ：３１７Ｗ／（ｍ・Ｋ）、Ｃｕ：４０１Ｗ／（ｍ・Ｋ）、Ａｇ：４２９Ｗ／（ｍ・Ｋ）程度と高く、熱拡散制御膜として好適である。しかしながら、熱アシスト記録方式では、レーザー照射を行う書き込み時には急速に温度が上昇し、レーザーをオフにした時には急速に温度が下がることが必要であり、そのためには、高い熱伝導率に加えて、熱拡散率が高いことも重要である。上記元素の熱拡散率は、Ａｕ：１．３×１０－４ｍ２／ｓｅｃ、Ｃｕ：１．２×１０－４ｍ２／ｓｅｃ、Ａｇ：１．８×１０－４ｍ２／ｓｅｃであり、Ａｇが最も高い値を有している。Ａｇ以外の元素について検討すると、Ａｕは耐食性が非常に高いが非常に高価であり、工業的にはコストの観点で好適でない。またＣｕは、ＡｇやＡｕに比べて酸化し易く、耐食性の点で問題がある。これに対し、Ａｇは、上述したように熱拡散率が最も大きく良好な熱的特性を有していることに加え、貴金属に分類されることから明らかなように、酸化による腐食に強く、他の金属との反応性も低いため、熱拡散制御層に最も適している。
　しかしながら、Ａｇ薄膜は一般に、表面粗さＲａが数ｎｍ以上と大きく、加熱により容易に粒成長や粗面化などの膜構造変化を起こす。一方、磁気記録媒体では、磁気ヘッド－磁気記録媒体間の距離が非常に狭いため、磁気記録媒体のＲａは１．０ｎｍ以下程度の非常に平滑な表面が必要とされている。そのために、例えばＡｇ薄膜の膜厚を約２０ｎｍ程度以下と非常に薄くすることでＲａの増加を抑制することが検討されているが、これは、熱容量や熱拡散効果の低下を招き、その結果、熱拡散制御層としての機能が大幅に低下するようになる。また、熱アシスト記録方式では、１００℃を超える高温加熱に曝され、このような高温加熱と室温までの急激な冷却の繰返しサイクルを受けるため、高い耐熱性も要求される。
　上述したように熱アシスト記録用磁気記録媒体に用いられる熱拡散制御膜は、高い熱伝導率に加えて、高い熱拡散率、高い表面平滑性、高い耐熱性の全ての特性を兼ね備えていることが要求されるが、Ａｇ単体薄膜は、このような要求特性を満足することができない。
　本発明は上記事情に鑑みてなされたものであり、その目的は、熱アシスト記録用磁気媒体に用いられるＡｇ合金熱拡散制御膜であって、高い熱伝導率を維持すると共に、高い熱拡散率、平滑な表面粗さ、および高い耐熱性の全てを兼ね備えたＡｇ合金熱拡散制御膜、及びそれを用いた磁気記録媒体、並びに当該Ａｇ合金熱拡散制御膜の作製に有用なスパッタリングターゲットを提供することにある。
　本発明は以下の態様を含む。
（１）熱アシスト記録用磁気記録媒体に用いられる熱拡散制御膜であって、Ａｇを主成分とするＡｇ合金から構成されており、表面粗さＲａ１．０ｎｍ以下、熱伝導率１００Ｗ／（ｍ・Ｋ）以上、熱拡散率４．０×１０-５ｍ２／ｓｅｃ以上を満足するＡｇ合金熱拡散制御膜。
（２）前記Ａｇ合金は、ＮｄおよびＹのうち少なくとも一つを０．０５～０．８原子％、並びにＢｉを０．０５～０．５原子％含有する（１）に記載のＡｇ合金熱拡散制御膜。
（３）前記Ａｇ合金は、更にＣｕを０．２～１．０原子％含有する（２）に記載のＡｇ合金熱拡散制御膜。
（４）（１）～（３）のいずれか一つに記載のＡｇ合金熱拡散制御膜を備えた熱アシスト記録用磁気記録媒体。
（５）（１）～（３）のいずれか一つに記載のＡｇ合金熱拡散制御膜の作製に用いられるスパッタリングターゲットであって、ＮｄおよびＹのうち少なくとも一つを０．０５～０．８原子％、並びにＢｉを０．０５～０．５原子％含有するＡｇ合金であるスパッタリングターゲット。
（６）前記Ａｇ合金が、更にＣｕを０．２～１．０原子％含有する（５）に記載のスパッタリングターゲット。
　本発明によれば、Ａｇ合金の組成が適切に制御されているため、Ａｇによる高い熱伝導率を維持すると共に、熱拡散率、表面平滑性、耐熱性がすべて高められたＡｇ合金熱拡散制御膜を提供することができた。よって、上記の熱拡散制御膜は、熱アシスト記録用磁気記録媒体に好適に用いられる。
図１は、熱アシスト記録用磁気記録媒体の膜構成の一例を示す説明図である。 図２（ａ）～図２（ｃ）は、実施例２における純Ａｇ薄膜の表面性状を示すＳＥＭ写真であり、図２（ａ）は、成膜後（ａｓ－ｄｅｐｏｓｉｔｉｏｎ）のＳＥＭ写真（倍率３００００倍）であり、図２（ｂ）は、大気雰囲気中で４００℃、１時間の熱処理を１回行った後のＳＥＭ写真（倍率６０００倍）であり、図２（ｃ）は図２（ｂ）の拡大図である（倍率３００００倍）。 図３（ａ）～図３（ｃ）は、実施例２におけるＡｇ合金薄膜（Ａｇ－０．２５Ｎｄ合金）の表面性状を示すＳＥＭ写真であり、図３（ａ）は、成膜後（ａｓ－ｄｅｐｏｓｉｔｉｏｎ）のＳＥＭ写真（倍率３００００倍）であり、図３（ｂ）は、大気雰囲気中で４００℃、１時間の熱処理を１回行った後のＳＥＭ写真（倍率６０００倍）であり、図３（ｃ）は図３（ｂ）の拡大図である（倍率３００００倍）。 図４（ａ）～図４（ｂ）は、実施例２におけるＡｇ合金薄膜（Ａｇ－０．０７Ｂｉ－０．１８Ｎｄ合金）の表面性状を示すＳＥＭ写真であり、図４（ａ）は、成膜後（ａｓ－ｄｅｐｏｓｉｔｉｏｎ）のＳＥＭ写真（倍率３００００倍）であり、図４（ｂ）は、大気雰囲気中で４００℃、１時間の熱処理を１回行った後のＳＥＭ写真（倍率３００００倍）である。 図５は、実施例３において、成膜時のＡｒガス圧がＡｇ合金薄膜の表面粗さＲａに及ぼす影響を示すグラフである。 図６は、実施例３において、Ａｇ合金薄膜の膜厚が表面粗さＲａに及ぼす影響を示すグラフである。
　本発明者らは、熱アシスト記録用磁気記録媒体の熱拡散制御膜として好適に用いられるＡｇ合金薄膜を提供するため、検討を重ねてきた。その結果、Ｎｄおよび／またはＹ、並びにＢｉを所定量含むＡｇ合金、好ましくは更にＣｕを所定量含むＡｇ合金を用いれば所期の目的が達成されることを見出し、本発明を完成した。
　すなわち、本発明の熱拡散制御膜は、Ａｇを主成分とするＡｇ合金から構成されており、表面粗さＲａ１．０ｎｍ以下、熱伝導率１００Ｗ／（ｍ・Ｋ）以上、熱拡散率４．０×１０-５ｍ２／ｓｅｃ以上を満足するところに特徴がある。前述したように、熱アシスト記録用磁気記録媒体に用いられる熱拡散制御膜は、熱伝導率、熱拡散率、表面平滑性、耐熱性の全ての特性に優れていることが要求されるが、本発明によれば、このような要求特性を全て兼ね備えたＡｇ合金膜を提供できる。
　なお、「Ａｇを主成分とするＡｇ合金」とは、合金中にＡｇを最も多く含む合金を意味し、通常、Ａｇを５０原子％以上（好ましくは７０原子％以上）、１００原子％未満含む合金を意味する。
　ここで、上記特性のうち、熱伝導率および熱拡散率の数値設定理由について説明する。
　一般に、熱伝導率および熱拡散率は、合金元素の添加量が増える程、低下する。例えば前述した図１の熱アシスト記録用磁気記録媒体において、軟磁性層として用いられるＣｏＦｅ合金膜の上記特性は詳細には検討されていないが、上記の傾向に鑑み、純Ｃｏの数値を考慮してＣｏＦｅの熱伝導率および熱拡散率を計算すると、純Ａｇ比で、熱伝導率は約０．２３倍程度、熱拡散率は約０．１５倍程度となり、純Ａｇに比べて非常に低かった（表１を参照）。なお、熱拡散率は、熱拡散率＝熱伝導率／（比熱×密度）と定義され、一般に、合金化により比熱と密度は変化しないため、熱拡散率は熱伝導率から一意的に決まる。
　上記数値の算出は、以下のようにして行なった。まず、純Ｃｏの熱伝導率、比熱、および密度は、理化学辞典などの文献から引用した値である。また、純Ａｇ及びＡｇ合金薄膜の熱伝導率の実測は困難なため、理論式に従って電気伝導率より算出した。一般にインゴットの熱伝導率に対し、薄膜の熱伝導率は欠陥や粒界のため低くなり、純Ａｇの場合、インゴットでは４２９Ｗ／（ｍ・Ｋ）であるのに対し、薄膜では３１４Ｗ／（ｍ・Ｋ）と低下した（後記する表２のＮｏ．１を参照）。純Ａｇの密度および比熱は、薄膜とインゴットで同等とした。参考のため、表１に、Ａｌ、Ｃｕ、Ｃｏ、ＡｕおよびＡｇの熱伝導率および熱拡散率を示す。
Figure JPOXMLDOC01-appb-T000001
　熱アシスト記録方式用の熱拡散制御膜として用いるには、汎用のＣｏＦｅ膜よりも高い熱伝導率と高い熱拡散率を有している必要がある。そのため、本発明では上記の数値を考慮して、Ａｇ薄膜合金では、純Ａｇ薄膜比で、熱伝導率および熱拡散率のいずれにおいても約０．５程度以上であれば効果を奏すると考え、熱伝導率１００Ｗ／（ｍ・Ｋ）以上、熱拡散率４．０×１０-５ｍ２／ｓｅｃ以上と定めた。好ましくは、純Ａｇ薄膜比で、熱伝導率および熱拡散率のいずれにおいても約０．６程度以上であり、その場合の熱伝導率は２００Ｗ／（ｍ・Ｋ）以上、熱拡散率８．２×１０-５ｍ２／ｓｅｃ以上である。
　また、本発明における表面粗さＲａは１．０ｎｍ以下とする。表面粗さＲａは小さい程良く、好ましくは０．８ｎｍ以下である。
　具体的には、本発明に用いられるＡｇ合金としては、Ｎｄおよび／またはＹを０．０５～０．８原子％、並びにＢｉを０．０５～０．５原子％含有しており、好ましくは、更にＣｕを０．２～１．０原子％含有しているＡｇ合金が挙げられる。
（Ｎｄおよび／またはＹ：０．０５～０．８原子％）
　ＮｄおよびＹは、表面平滑性向上に寄与すると共に、耐熱性向上作用も有している。これらの元素は単独で添加しても良いし、併用しても良い。これらのうち好ましいのはＮｄである。
　これら元素の含有量（単独の場合は単独量であり、併用するときは合計量である。）が０．０５原子％未満では上記作用が有効に発揮されないおそれがあり、一方、０．８原子％を超えると、熱伝導率および熱拡散率が大きく低下するおそれがある。好ましい含有量は、０．１原子％以上０．６原子％以下であり、より好ましくは０．１原子％以上０．５原子％以下である。なお、上記元素の含有量の上限と下限を任意に組み合わせて上記元素の含有量の範囲とすることもできる。
（Ｂｉ：０．０５～０．５原子％）
　ＢｉもＮｄと同様、表面平滑性向上作用および耐熱性向上作用を有している。詳細には、Ｂｉは、ＮｄやＹに比べて表面平滑性向上効果は少ないが、耐熱性向上効果が大きい元素である。Ｂｉが０．０５原子％未満では、上記作用が有効に発揮されないおそれがあり、一方、０．５原子％を超えると、熱伝導率および熱拡散率が大きく低下するおそれがある。Ｂｉの好ましい含有量は、０．０５原子％以上０．４原子％以下であり、より好ましくは０．０５原子％以上０．３原子％以下である。なお、上記元素の含有量の上限と下限を任意に組み合わせて上記元素の含有量の範囲とすることもできる。
　本発明に用いられるＡｇ合金の態様として、Ｎｄおよび／またはＹ、並びにＢｉを含有し、残部：Ａｇおよび不可避的不純物であるＡｇ合金が挙げられる。また、Ｎｄおよび／またはＹ、並びにＢｉを含有し、更なる特性向上を目的として、後述のＣｕを０．２～１．０原子％含有し、残部：Ａｇおよび不可避的不純物であるＡｇ合金も挙げられる。
　なお、不可避不純物としては、例えば、Ｎ、Ｏ、Ｃ、Ｆｅ、Ｓｉなどが挙げられ、その含有量は、通常０．０１重量％以下である。
（Ｃｕ：０．２～１．０原子％）
　Ｃｕは、Ａｇ合金薄膜の結晶粒径を微細化し、表面平滑性向上作用を有する。Ｃｕ量が０．２原子％未満では、上記作用が有効に発揮されないおそれがあり、一方、Ｃｕ量が１．０原子％を超えると、熱伝導率および熱拡散率が大きく低下するおそれがある。Ｃｕの好ましい含有量は、０．４原子％以上１．０原子％以下であり、より好ましくは０．５原子％以上０．８原子％以下である。なお、上記元素の含有量の上限と下限を任意に組み合わせて上記元素の含有量の範囲とすることもできる。
　更に本発明に用いられる上記元素と、表面粗さ（Ｒａ１．０ｎｍ以下）との関係について、詳しく説明する。
　一般に薄膜の表面平滑性は、その結晶粒径にほぼ対応しており、結晶粒径を細かくする程、表面は平滑になる。本発明に用いられるＡｇ合金において、例えばＮｄを含むＡｇ－Ｎｄ合金について検討すると、ＮｄはＡｇと比較して約１．３倍の原子半径を有しているため、スパッタ成膜時に形成される過飽和固溶体には、非常に大きな格子歪みが生じる。前述したように純Ａｇ膜では、スパッタ成膜時に結晶粒が粗大化し易いが、Ａｇ－Ｎｄ合金では、この格子歪みによりＡｇ－Ｎｄ合金薄膜の結晶粒が微細化することによって、高い表面平滑性が得られるようになる。また、格子歪みが大きいために加熱時の結晶粒成長が抑制され、その結果、熱処理後も表面平滑性が維持されるようになる。
　一方、Ａｇ薄膜加熱時における表面粗さの増大（表面粗面化）は、結晶粒径の増大だけでなく、表面張力の低減により薄膜表面のＡｇの拡散も招く。Ａｇは貴金属に分類されるように非常に酸化され難い元素であるから、薄膜表面には酸化被膜が形成されず、その結果、Ａｇの表面拡散は抑制され難いという性質を有している。
　そして本発明で添加されるＮｄは、Ａｇ結晶粒中に分散して粒成長を抑制するという効果は有しているが、Ａｇの表面拡散を抑制する効果はない。Ｙも同様である。
　一方、Ａｇの表面拡散の抑制にはＢｉが非常に有効である。ＢｉはＡｇに固溶せず、また、拡散が非常に速いためにスパッタ成膜中にＡｇ膜表面に拡散し、Ｂｉ酸化物のバリア層を形成する。このＢｉ酸化物バリア層がＡｇの表面拡散を抑制するために、加熱時でも高い表面平滑性を維持すると考えられる。ただし、ＢｉはＮｄやＹと異なり、Ａｇ結晶粒の内部に歪みを生じ、結晶粒成長の抑制効果は殆どない。
　本発明の好ましい態様では、Ｎｄおよび／またはＹと、Ｂｉを併用しているが、これにより、Ｎｄおよび／またはＹの粒成長抑制効果と、Ｂｉの表面拡散抑制効果とが複合的に作用し、その結果、Ａｇ合金膜の熱処理時における表面平滑性の劣化を抑制すると考えられる。
　一方、本発明において好ましい選択成分として用いられるＣｕは、Ａｇ結晶粒に歪みを生じることもないし、Ａｇ薄膜表面に偏在することもない。しかしながら、Ｃｕは、Ａｇより融点が高いためにスパッタ成膜初期の核生成サイトとなり、Ａｇ結晶粒のサイズを低減する効果がある。なお、Ｃｕは、耐熱性向上作用を有していないが、添加量に対する熱伝導率の低下作用や熱拡散率の低下作用が少ないため、初期結晶粒微細化の目的で、Ｎｄおよび／またはＹと、Ｂｉに好ましく添加することができる。このような作用を有する元素としては、Ｃｕの他にＰｄ、Ａｕが挙げられるが、これらはＣｕに比べて熱伝導率の低下が大きく、また高価であるため、本発明では、Ｃｕを好ましい選択成分として採用した。
　本発明のＡｇ合金熱拡散制御膜の厚さとしては、Ｒａを１．０ｎｍ以下に制御できる厚さであればよく、具体的には、約２７０ｎｍ以下とすることが好ましく、より好ましくは２００ｎｍ以下、また、好ましくは１０ｎｍ以上、より好ましくは５０ｎｍ以上である。
　上記Ａｇ合金膜は、スパッタリング法にてスパッタリングターゲット（以下「ターゲット」ということがある）を用いて形成することがより好ましい。スパッタリング法によれば、イオンプレーティング法や電子ビーム蒸着法で形成された薄膜よりも、成分や膜厚の膜面内均一性に優れた薄膜を容易に形成できるからである。
　上記スパッタリング法で上記Ａｇ合金膜を形成するには、上記ターゲットとして、前述した元素（Ｎｄおよび／またはＹと、Ｂｉ、好ましくは更にＣｕ）を含むものであって、所望のＡｇ合金膜と同一組成のＡｇ合金スパッタリングターゲットを用いれば、組成ズレの恐れがなく、所望の成分組成のＡｇ合金膜を形成することができるのでよい。
　従って、本発明には、前述したＡｇ合金膜と同じ組成のスパッタリングターゲットも本発明の範囲内に包含される。詳細には、上記ターゲットとしては、Ｎｄおよび／またはＹを０．０５～０．８原子％、並びにＢｉを０．０５～０．５原子％含有し、残部Ａｇおよび不可避不純物であるターゲットが挙げられる。また、好ましいターゲットとしては、Ｎｄおよび／またはＹを０．０５～０．８原子％、並びにＢｉを０．０５～０．５原子％含有し、更にＣｕを０．２～１．０原子％含有し、残部Ａｇおよび不可避不純物であるターゲットが挙げられる。
　上記ターゲットの形状は、スパッタリング装置の形状や構造に応じて任意の形状（角型プレート状、円形プレート状、ドーナツプレート状など）に加工したものが含まれる。
　上記ターゲットの製造方法としては、溶解鋳造法や粉末焼結法、スプレイフォーミング法が挙げられる。
　スパッタリングを行うにあたってのＡｒガス圧としては、Ｒａを１．０ｎｍ以下に制御できる範囲であればよく、具体的には、概ね６ｍＴｏｒｒ以下に制御することが好ましく、より好ましくは５ｍＴｏｒｒ以下、また、好ましくは０．５ｍＴｏｒｒ以上、より好ましくは１ｍＴｏｒｒ以上である。
　本発明のＡｇ合金熱拡散制御膜は、熱アシスト記録用磁気記録媒体に好適に用いられる。熱アシスト記録用磁気記録媒体の膜構成は、通常用いられるものであれば限定されず、代表的には、基板の上に、上記の熱拡散制御膜と、少なくとも一層の下地層と、少なくとも一層の磁気記録層と、少なくとも一層の保護層を有する積層構造である。上記の熱拡散制御膜は、例えば基板と、下地層または磁気記録層との間に設けられる。前述した図１は、本発明のＡｇ合金熱拡散制御膜を適応し得る熱アシスト記録用磁気記録媒体の一例であり、本発明はこれに限定する趣旨ではない。
　以下、実施例を挙げて本発明をより具体的に説明するが、本発明は以下の実施例によって制限されず、上記・下記の趣旨に適合し得る範囲で変更を加えて実施することも可能であり、それらはいずれも本発明の技術的範囲に包含される。
実施例１
　本実施例では、Ａｇ合金薄膜の組成が、熱伝導率、熱拡散率、および表面平滑性（Ｒａ）に及ぼす影響を調べた。
　具体的には、ＤＣマグネトロンスパッタを用い、ガラス基板（コーニング＃１７３７，基板サイズ：直径５０ｍｍ、厚さ１ｍｍ）上に、表２に記載の種々のＡｇ合金薄膜を２００ｎｍ作製した。成膜条件は、基板温度：２２℃、Ａｒガス圧：２ｍＴｏｒｒ、投入電力密度：０．０２５Ｗ／ｃｍ２、背圧：＜５×１０-６Ｔｏｒｒとした。
　なお、上記Ａｇ合金における各元素の含有量は、ガラス基板上に膜厚１００ｎｍで作製した試料からＩＣＰ発光分析（誘導結合プラズマ発光分析）法によって求めた。
　このようにして得られたＡｇ合金薄膜を用い、熱伝導率、熱拡散率、および表面平滑性（Ｒａ）を以下のようにして調べた。
（熱伝導率および熱拡散率の測定）
　熱伝導率は、４端子法を用いて測定した薄膜の電気抵抗率から換算した。
　また、熱拡散率は、熱拡散率＝熱伝導率／（比熱×密度）に基づき、算出した。前述したように、純Ａｇ及びＡｇ合金膜の密度および比熱は、一般にインゴットの純Ａｇの各値と変わらないため、それぞれ文献値［密度８９００ｋｇ／ｍ３、比熱２３４Ｊ／（ｋｇ・Ｋ）］を用いた。
（表面粗さＲａの測定）
　Ｒａは、原子間力顕微鏡（Ａｔｏｍｉｃ Ｆｏｒｃｅ Ｍｉｃｒｏｓｃｏｐｅ、ＡＦＭ）を用い、３μｍ×３μｍのエリアの測定値から算出した。測定は、成膜直後の薄膜、および２００℃×１０分の真空熱処理後の薄膜のそれぞれについて行った。
　総合評価として、熱伝導率２００Ｗ／（ｍ・Ｋ）以上、熱拡散率８．２×１０－５ｍ２／ｓｅｃ以上、かつ、表面粗さＲａが１．０ｎｍ以下であるものを「Ａ」、熱伝導率１００Ｗ／（ｍ・Ｋ）以上、熱拡散率４．０×１０－５ｍ２／ｓｅｃ以上、かつ、表面粗さＲａが１．０ｎｍ以下であるものを「Ｂ」、その他のものを「Ｃ」とした。
　これらの結果を表２に併記する。
Figure JPOXMLDOC01-appb-T000002
  
　表２より、Ｎｄ並びにＢｉ、更にはＣｕを本発明の範囲で含有するＡｇ合金（Ｎｏ．２～８）は、純Ａｇ（Ｎｏ．１）と同様に高い熱伝導率を有しており、且つ、純Ａｇに比べ、熱拡散率および表面平滑性も大幅に向上した。表面平滑性については、成膜直後だけでなく、加熱後も高い表面平滑性が維持されたことから、これらは高い耐熱性を有していることが確認された。
　一方、Ｎｏ．９～１２は、本発明で規定しない元素を含むＡｇ合金を用いた例であり、熱拡散率、またはＲａのいずれか一方が低下した。
実施例２
　本実施例では、ガラス基板上に種々のＡｇ合金薄膜を作製し、成膜後及び熱処理後の表面形状を走査型反射電子顕微鏡（ＳＥＭ）で観察した。
　詳細には、前述した実施例１と同様にして図３（ａ）～図３（ｃ）及び図４（ａ）～図４（ｂ）に示す種々のＡｇ合金薄膜を２００ｎｍ作製した。Ａｇ合金薄膜の含有量も、実施例１と同様にして算出した。なお、比較のため、純Ａｇ（図２（ａ）～図２（ｃ））についても同様に作製した。
　熱処理は、大気雰囲気中で４００℃、１時間行った。なお、熱アシスト記録方式では、実際の記録時の加熱温度は１００～３００℃程度と推定されるが、本実施例では、加速試験として４００℃を設定した。
　これらの結果を図２（ａ）～図２（ｃ）、図３（ａ）～図３（ｃ）及び図４（ａ）～図４（ｂ）に示す。
　図２（ａ）～図２（ｃ）、図３（ａ）～図３（ｃ）及び図４（ａ）～図４（ｂ）より、純Ａｇ薄膜では、Ａｇが凝集するまでに膜構造が変化しており、ドーム状のＡｇ結晶粒以外の部分ではガラス基板が露出している。
　一方、Ｎｄを添加したＡｇ－０．２５原子％Ｎｄ合金薄膜（比較例）では、ドーム状のＡｇ結晶粒の頻度は純Ａｇ薄膜に比べて著しく低減されており、ドーム状以外の部分では当該Ａｇ－Ｎｄ薄膜の平滑性は保たれている。しかしながら、Ａｇの表面拡散に起因するドーム状の結晶粒成長は充分に抑制されず、結晶粒成長が一旦始まった部位では上記の純Ａｇ薄膜と同程度の成長が見られた。
　これに対し、Ｎｄ並びにＢｉの両方を添加したＡｇ－０．０７原子％Ｂｉ－０．１８原子Ｎｄ合金薄膜（本発明例）では、熱処理後も全面に渡って平滑な表面が維持されており、ドーム状の結晶粒成長を飛躍的に抑制でき、耐熱性に極めて優れていることが分かった。
実施例３
　本実施例では、本発明の要件を満足するＡｇ－０．１４原子％Ｂｉ－０．２原子％Ｎｄ薄膜を用い、成膜時のＡｒガス圧および膜厚が表面粗度（Ｒａ）に及ぼす影響を調べた。
（Ａｇガス圧について）
　前述した実施例１において、Ａｒガス圧を図５に示すように２～１０ｍＴｏｒｒの範囲で変化させた（Ａｇ合金薄膜の膜厚＝２００ｎｍ）ときの表面粗さＲａを、前述した実施例１と同様にして測定した。これらの結果を図５に示す。
　図５より、Ａｇ合金薄膜の表面粗さＲａは、Ａｒガス圧が５ｍＴｏｒｒを超えると急激に増加した。これは、ターゲットよりスパッタされた金属粒子がＡｒによって散乱されるためと推定される。従って、Ｒａを本発明で規定する１．０ｎｍ以下に低減するためには、成膜時のＡｒガス圧を、概ね６ｍＴｏｒｒ以下に制御することが好ましい。
（膜厚について）
　前述した実施例１において、スパッタ時間を変えることによってＡｇ合金薄膜の膜厚を図６に示すように１０～１５０ｎｍの間で変化させた（Ａｒガス圧＝２ｍＴｏｒｒ）ときの表面粗さＲａを、前述した実施例１と同様にして測定した。これらの結果を図６に示す。
　図６より、表面Ｒａは、Ａｇ合金薄膜の膜厚が増加するにつれ、緩やかに上昇することが分かる。熱拡散制御の観点からはＡｇ合金薄膜の膜厚を一定以上厚くすることが望ましいが、本発明で規定するＲａを１．０ｎｍ以下に維持するためには、膜厚を約２７０ｎｍ以下に制御することが好ましいことが分かる。
　本出願を詳細にまた特定の実施態様を参照して説明したが、本発明の精神と範囲を逸脱することなく様々な変更や修正を加えることができることは当業者にとって明らかである。
　本出願は、2009年11月18日出願の日本特許出願（特願2009－262908）に基づくものであり、その内容はここに参照として取り込まれる。
　本発明によれば、Ａｇ合金の組成が適切に制御されているため、Ａｇによる高い熱伝導率を維持すると共に、熱拡散率、表面平滑性、耐熱性がすべて高められたＡｇ合金熱拡散制御膜を提供することができた。よって、上記の熱拡散制御膜は、熱アシスト記録用磁気記録媒体に好適に用いられる。

Claims (6)

  1. 　熱アシスト記録用磁気記録媒体に用いられる熱拡散制御膜であって、Ａｇを主成分とするＡｇ合金から構成されており、表面粗さＲａ１．０ｎｍ以下、熱伝導率１００Ｗ／（ｍ・Ｋ）以上、熱拡散率４．０×１０-５ｍ２／ｓｅｃ以上を満足するＡｇ合金熱拡散制御膜。
  2. 　前記Ａｇ合金は、ＮｄおよびＹのうち少なくとも一つを０．０５～０．８原子％、並びにＢｉを０．０５～０．５原子％含有する請求項１に記載のＡｇ合金熱拡散制御膜。
  3. 　前記Ａｇ合金は、更にＣｕを０．２～１．０原子％含有する請求項２に記載のＡｇ合金熱拡散制御膜。
  4. 　請求項１～３のいずれか一項に記載のＡｇ合金熱拡散制御膜を備えた熱アシスト記録用磁気記録媒体。
  5. 　請求項１～３のいずれか一項に記載のＡｇ合金熱拡散制御膜の作製に用いられるスパッタリングターゲットであって、ＮｄおよびＹのうち少なくとも一つを０．０５～０．８原子％、並びにＢｉを０．０５～０．５原子％含有するＡｇ合金であるスパッタリングターゲット。
  6. 　前記Ａｇ合金が、更にＣｕを０．２～１．０原子％含有する請求項５に記載のスパッタリングターゲット。
PCT/JP2010/070486 2009-11-18 2010-11-17 熱アシスト記録用磁気記録媒体に用いられるＡｇ合金熱拡散制御膜、及び熱アシスト記録用磁気記録媒体、スパッタリングターゲット WO2011062192A1 (ja)