WO2011020823A1 - Verfahren zur herstellung von halogenarmen polybiphenylsulfon-polymeren - Google Patents
Verfahren zur herstellung von halogenarmen polybiphenylsulfon-polymeren Download PDFInfo
- Publication number
- WO2011020823A1 WO2011020823A1 PCT/EP2010/061924 EP2010061924W WO2011020823A1 WO 2011020823 A1 WO2011020823 A1 WO 2011020823A1 EP 2010061924 W EP2010061924 W EP 2010061924W WO 2011020823 A1 WO2011020823 A1 WO 2011020823A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- polybiphenylsulfone
- reaction
- polymer
- halogen
- Prior art date
Abstract
Description
Claims