WO2011001949A1 - フィラーを含有するポリイミド前駆体溶液組成物及びそれを用いたポリイミド膜 - Google Patents
フィラーを含有するポリイミド前駆体溶液組成物及びそれを用いたポリイミド膜 Download PDFInfo
- Publication number
- WO2011001949A1 WO2011001949A1 PCT/JP2010/060998 JP2010060998W WO2011001949A1 WO 2011001949 A1 WO2011001949 A1 WO 2011001949A1 JP 2010060998 W JP2010060998 W JP 2010060998W WO 2011001949 A1 WO2011001949 A1 WO 2011001949A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- filler
- polyimide precursor
- solution composition
- precursor solution
- polyimide
- Prior art date
Abstract
Description
前記フィラーを含有する分散溶液と、溶媒と、テトラカルボン酸二無水物及び/またはその誘導体とジアミン化合物とを混合し、テトラカルボン酸二無水物及び/またはその誘導体とジアミン化合物を反応させてフィラーを含有するポリイミド前駆体溶液組成物を得る工程と
を含むことを特徴とする、フィラーが分散されたポリイミドの製造方法。
(第1工程)溶媒中、テトラカルボン酸二無水物及び/またはその誘導体と、ジアミン化合物とを反応させて、ポリイミド前駆体溶液組成物を得る工程と、
(第2工程)前記第1工程で得られるポリイミド前駆体組成物と、フィラーと溶媒とを混合して、フィラーを含有する分散液を得る工程と、
(第3工程)前記第2工程で得られるフィラーを含有する分散液と、溶媒と、テトラカルボン酸二無水物及び/またはその誘導体とジアミン化合物とを混合し、テトラカルボン酸二無水物及び/またはその誘導体とジアミン化合物を反応させて、フィラーを含有するポリイミド前駆体溶液組成物を得る工程と
(第4工程)第3工程で得られるフィラーを含有するポリイミド前駆体溶液組成物中の、ポリイミド前駆体をイミド化することにより、フィラーが分散されたポリイミドを得る工程と
を含むことを特徴とする。
上記第1工程では、テトラカルボン酸二無水物及び/またはその誘導体と、ジアミン化合物を溶媒の存在下で反応させ、ポリイミド前駆体溶液組成物が得られる。なお、このポリイミド前駆体溶液組成物は、使用する溶媒を含有する概念である場合もある。
本発明において「フィラーを含有する分散溶液」とは、上記フィラーを含有する前のポリイミド前駆体溶液組成物と溶媒とが混合された混合液中にフィラーが分散された溶液のことをいう。
上記AMCの製造方法は、次のとおりである。コバルトのスピネル型結晶構造を有する酸化物に、マグネシウムが固溶置換した触媒を用いて、CO及びH2を含む混合ガスを触媒粒子に供給して気相成長法により、AMCを製造する。
本発明において、「フィラーを含有するポリイミド前駆体溶液組成物」とは、上記フィラーを含有する分散溶液中、テトラカルボン酸二無水物及び/またはその誘導体とジアミン化合物をさらに溶解し、重合させてポリイミド前駆体とした組成物のことをいう。
第4工程においては、第3工程で得られるフィラーを含有するポリイミド前駆体溶液組成物中の、ポリイミド前駆体をイミド化することにより、フィラーが分散されたポリイミドを得ることができる。イミド化の方法は特に限定されず、公知の方法で行うことができる。
s-BPDA:3,3’,4,4’-ビフェニルテトラカルボン酸二無水物
ODA:オキシジアニリン(4,4’-ジアミノジフェニルエーテル)
PPD:p-フェニレンジアミン
BAPP:2,2-ビス〔4-(4-アミノフェノキシ)フェニル〕プロパン
MBAA:ビス(4-アミノ-3-カルボキシフェニル)メタン
NMP:N-メチル-2-ピロリドン
DMAc:N,N-ジメチルアセトアミド
PVP:ポリビニルピロリドン
引張り試験機(オリエンテック社製RTC-1225A)を用いて、ASTM D882に準拠して測定した。
引張り試験機(オリエンテック社製RTC-1225A)を用いて、ASTM D882に準拠して測定した。
引張り試験機(オリエンテック社製RTC-1225A)を用いて、ASTM D882に準拠して測定した。
ロレスタGP(三菱化学製)に接続した4探針プローブ(MCP-TP03P)を用いて、JIS K 7194に準拠して測定した。
ポリイミド前駆体溶液組成物のポリイミド換算した固形分濃度は、ポリイミド前駆体溶液組成物を350℃で30分間乾燥し、乾燥前の質量W1と乾燥後の質量W2とから次式によって求めた値である。
トキメック社製E型粘度計を用いて、30℃での溶液粘度を測定した。
フィラーを含有するポリイミド前駆体溶液組成物を、25℃の温度に調整された雰囲気中に保管し、1ヶ月後の溶液粘度変化が±10%以内のものを○、±10%を超えたものを×とした。
フィラーを含有するポリイミド前駆体溶液組成物の凝集物のサイズを、グラインドメーター線条法により観測した。
フィラーを含有するポリイミド前駆体溶液組成物を、25℃の温度に調整された雰囲気中に保管し、1ヶ月後の凝集物をグラインドメーター線条法により観測した。
フィラーを含有するポリイミド前駆体溶液組成物を、25℃の温度に調整された雰囲気中に14日間静置し、上層部及び下層部の固形分濃度を測定し、固形分濃度の差が±5%以内のものを○、±5%を超えたものを×とした。
(1-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、溶媒としてNMP400gを加え、これにODA40.50g(0.202モル)と、s-BPDA59.50g(0.202モル)とを加え、50℃で10時間撹拌して、固形分濃度18.2質量%、溶液粘度51.0Pa・sのポリイミド前駆体溶液組成物を得た。
NMP745gにケッチェンブラック(ライオン社製、ケッチェンブラックECP-600JD、揮発分0.7質量%)30g及び上記(1-a)で得られたポリイミド前駆体溶液組成物225gを添加し、ボールミル(ボール径2mm及び6mmを併用)を用いて室温にて16時間混合を行い、カーボンブラックを含有する分散溶液を得た(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液166.7g及びNMP275.8gを加え、これにODA37.46g(総量0.202モル)と、s-BPDA55.04g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック5質量%を含有するポリイミド前駆体溶液組成物を得た。このカーボンブラック5質量%を含有するポリイミド前駆体溶液組成物は、固形分濃度19.2質量%、溶液粘度50.5Pa・sで、溶液安定性は○であった。
このカーボンブラック5質量%を含有するポリイミド前駆体溶液組成物を、基材のガラス板上にバーコーターによって塗布し、その塗膜を、減圧下25℃で30分間、脱泡及び予備乾燥した後で、常圧下、窒素ガス雰囲気下で熱風乾燥器に入れて、順次、120℃で60分間、150℃で30分間、200℃で10分間、250℃で10分間、400℃で10分間加熱処理をして、厚さが50μmのポリイミド膜を形成した。
(2-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
上記(1-a)と同様に調製し、固形分濃度18.3質量%、溶液粘度50.8Pa・sのポリイミド前駆体溶液組成物を得た。
上記(2-a)で得られたポリイミド前駆体溶液組成物を用いて、(1-b)と同様にフィラーを含有する分散溶液を製造した(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液333.3g及びNMP151.7gを加え、これにODA34.42g(総量0.202モル)と、s-BPDA50.58g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表1に示した。
上記(2-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表1に示した。
(3-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
溶媒としてNMPではなくDMAc400gを用いた以外は上記(1-a)と同様に調製し、固形分濃度17.9質量%、溶液粘度50.5Pa・sのポリイミド前駆体溶液組成物を得た。
上記(3-a)で得られたポリイミド前駆体溶液組成物を用いて、溶媒としてNMPではなくDMAc745gを用いた以外は(1-b)と同様に製造した(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液333.3g及びDMAc151.7gを加え、これにODA34.42g(総量0.202モル)と、s-BPDA50.58g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表1に示した。
上記(3-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表1に示した。
(4-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
上記(1-a)と同様に調製し、固形分濃度18.3質量%、溶液粘度51.2Pa・sのポリイミド前駆体溶液組成物を得た。
上記(4-a)で得られたポリイミド前駆体溶液組成物を用いて、フィラーを含有する分散溶液を(1-b)と同様に製造した(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液333.3g及びNMP151.7gを加え、これにODA31.39g(総量0.202モル)と、s-BPDA46.11g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック15質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表1に示した。
上記(4-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表1に示した。
(5-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
上記(1-a)と同様に調製し、固形分濃度18.0質量%、溶液粘度50.2Pa・sのポリイミド前駆体溶液組成物を得た。
上記(5-a)で得られたポリイミド前駆体溶液組成物を用いて、フィラーとしてケッチェンブラックではなくAMC(宇部興産社製)30gを用いた以外は(1-b)と同様に製造した(3質量%炭素繊維分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%炭素繊維分散液166.7g及びNMP275.8gを加え、これにODA37.46g(総量0.202モル)と、s-BPDA55.04g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対して炭素繊維5質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表1に示した。
上記(5-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表1に示した。
(6-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
上記(1-a)と同様に調製し、固形分濃度18.3質量%、溶液粘度50.8Pa・sのポリイミド前駆体溶液組成物を得た。
上記(6-a)で得られたポリイミド前駆体溶液組成物を用いて、フィラーを含有する分散溶液を(5-b)と同様に製造した(3質量%炭素繊維分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%炭素繊維分散液333.3g及びNMP151.7gを加え、これにODA34.42g(総量0.202モル)と、s-BPDA50.58g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対して炭素繊維10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表1に示した。
上記(6-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表1に示した。
(7-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
(1-a)と同様に調製し、固形分濃度18.2質量%、溶液粘度50.1Pa・sのポリイミド前駆体溶液組成物を得た。
上記(7-a)で得られたポリイミド前駆体溶液組成物を用いて、フィラーとしてケッチェンブラックではなくファーネスブラック(デグサ社製、スペシャルブラック4、pH3.0、揮発分14.0質量%)30gを用いた以外は(1-b)と同様に製造した(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液333.3g及びNMP151.7gを加え、これにODA34.42g(総量0.202モル)と、s-BPDA50.58g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表1に示した。
上記(7-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表1に示した。
(8-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
(1-a)と同様に調製し、固形分濃度18.4質量%、溶液粘度51.4Pa・sのポリイミド前駆体溶液組成物を得た。
上記(8-a)で得られたポリイミド前駆体溶液組成物を用いて、フィラーとしてケッチェンブラックではなく窒化ホウ素(電気化学工業社製、SP-2、平均粒径4μm)30gを用いた以外は(1-b)と同様に製造した(3質量%窒化ホウ素分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%窒化ホウ素分散液333.3g及びNMP151.7gを加え、これにODA34.42g(総量0.202モル)と、s-BPDA50.58g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対して窒化ホウ素10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表1に示した。
上記(8-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表1に示した。
(9-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
上記(1-a)と同様に調製し、固形分濃度18.2質量%、溶液粘度50.8Pa・sのポリイミド前駆体溶液組成物を得た。
上記(9-a)で得られたポリイミド前駆体溶液組成物を用いて、フィラーとしてケッチェンブラックではなくシリカ(電気化学工業社製、UFP-80、平均粒径34nm)30gを用いた以外は(1-b)と同様に製造した(3質量%シリカ分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%シリカ分散液333.3g及びNMP151.7gを加え、これにODA34.42g(総量0.202モル)と、s-BPDA50.58g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してシリカ10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表2に示した。
上記(9-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表2に示した。
(10-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、溶媒としてNMP400gを加え、これにPPD26.88g(0.249モル)と、s-BPDA73.12g(0.249モル)とを加え、50℃で10時間撹拌して、固形分濃度18.0質量%、溶液粘度49.7Pa・sのポリイミド前駆体溶液組成物を得た。
上記(10-a)で得られたポリイミド前駆体溶液組成物を用いて、フィラーを含有する分散溶液を(1-b)と同様に製造した(3質量%カーボン分散溶液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液333.3g及びNMP151.7gを加え、これにODA36.45g(0.182モル)と、s-BPDA60.86g(総量0.207モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表2に示した。
上記(10-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表2に示した。
(11-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、溶媒としてDMAc400gを加え、これにPPD26.88g(0.249モル)と、s-BPDA73.12g(0.249モル)とを加え、50℃で10時間撹拌して、固形分濃度18.0質量%、溶液粘度49.7Pa・sのポリイミド前駆体溶液組成物を得た。
上記(11-a)で得られたポリイミド前駆体溶液組成物を用いて、フィラーを含有する分散溶液を(3-b)と同様に製造した(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液333.3g及びDMAc151.7gを加え、これにODA36.45g(0.182モル)と、s-BPDA60.86g(総量0.207モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表2に示した。
上記(11-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表2に示した。
(12-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
上記(3-a)と同様に調製し、固形分濃度17.9質量%、溶液粘度50.5Pa・sのポリイミド前駆体溶液組成物を得た。
DMAc895gにケッチェンブラック(ライオン社製、ケッチェンブラックECP-600JD、揮発分0.7質量%)30g及び上記で得られたポリイミド前駆体溶液組成物75gを添加し、ボールミル(ボール径2mm及び6mmを併用)を用いて室温にて16時間混合を行い、カーボンブラックを含有する分散溶液を得た(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液333.3g及びDMAc83.0gを加え、これにODA39.89g(総量0.202モル)と、s-BPDA58.61g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表2に示した。
上記(12-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表2に示した。
(13-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
上記(3-a)と同様に調製し、固形分濃度17.9質量%、溶液粘度50.5Pa・sのポリイミド前駆体溶液組成物を得た。
DMAc520gにケッチェンブラック(ライオン社製、ケッチェンブラックECP-600JD、揮発分0.7質量%)30g及び上記で得られたポリイミド前駆体溶液組成物450gを添加し、ボールミル(ボール径2mm及び6mmを併用)を用いて室温にて16時間混合を行い、カーボンブラックを含有する分散溶液を得た(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液333.3g及びDMAc106.7gを加え、これにODA36.85g(総量0.202モル)と、s-BPDA54.15g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表2に示した。
上記(13-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表2に示した。
(14-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
上記(3-a)と同様に調製し、固形分濃度17.9質量%、溶液粘度50.5Pa・sのポリイミド前駆体溶液組成物を得た。
DMAc575gにケッチェンブラック(ライオン社製、ケッチェンブラックECP-600JD、揮発分0.7質量%)50g及び上記(14-a)で得られたポリイミド前駆体溶液組成物375gを添加し、ボールミル(ボール径2mm及び6mmを併用)を用いて室温にて16時間混合を行い、カーボンブラックを含有する分散溶液を得た(5質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記5質量%カーボン分散液200.0g及びDMAc225.0gを加え、これにODA37.46g(総量0.202モル)と、s-BPDA55.04g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表2に示した。
上記(14-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表2に示した。
(15-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
上記(3-a)と同様に調製し、固形分濃度17.9質量%、溶液粘度50.5Pa・sのポリイミド前駆体溶液組成物を得た。
上記(15-a)で得られたポリイミド前駆体溶液組成物を用いて、フィラーを含有する分散溶液を(3-b)と同様に製造した(3質量%カーボン分散溶液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液166.7g及びDMAc245.8gを加え、これにBAPP53.88g(0.131モル)と、s-BPDA38.62g(総量0.146モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック5質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表2に示した。
上記(15-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表2に示した。
(16-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
上記(3-a)と同様に調製し、固形分濃度17.9質量%、溶液粘度50.5Pa・sのポリイミド前駆体溶液組成物を得た。
上記(16-a)で得られたポリイミド前駆体溶液組成物を用いて、フィラーを含有する分散溶液を(3-b)と同様に製造した(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液166.7g及びDMAc245.8gを加え、これにODA24.92g(総量0.140モル)及びMBAA15.27g(0.053モル)と、s-BPDA52.31g(総量0.193モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック5質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表2に示した。
上記(16-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表2に示した。
(1’-a)フィラーを含有するポリイミド前駆体溶液組成物の製造方法
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、溶媒としてNMP400gと、ケッチェンブラック(ライオン社製、ケッチェンブラックECP-600JD、揮発分0.7質量%)10gとを加え、1時間撹拌後、ODA40.50g(0.202モル)と、s-BPDA59.50g(0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラックを10質量%含有するポリイミド前駆体溶液組成物を得た。このカーボンブラックを10質量%含有するポリイミド前駆体溶液組成物は、固形分濃度20.3質量%、溶液粘度50.5Pa・sで、溶液安定性は×であった。
上記(1’-a)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表3に示した。
(2’-a)フィラーを含有するポリイミド前駆体溶液組成物の製造方法
フィラーとして、ケッチェンブラックではなくAMC(宇部興産社製)10gを用いた以外は(1’-a)と同様にして、ポリイミド前駆体溶液組成物全量に対して炭素繊維を10質量%含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表3に示した。
上記(2’-a)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表3に示した。
(3’-a)フィラーを含有するポリイミド前駆体溶液組成物の製造方法
フィラーとして、ケッチェンブラックではなく窒化ホウ素(電気化学工業社製、SP-2、平均粒径4μm)10gを用いた以外は(1’-a)と同様にして、ポリイミド前駆体溶液組成物全量に対して窒化ホウ素を10質量%含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表3に示した。
上記(3’-a)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表3に示した。
(4’-a)フィラーを含有する分散溶液の製造方法
NMP745gに窒化ホウ素(電気化学工業社製、SP-2、平均粒径4μm)30g及びPVP(日本触媒社製、K-30)30gを添加し、ボールミル(ボール径2mm及び6mmを併用)を用いて室温にて16時間混合を行い、窒化ホウ素を含有する分散溶液を得た(3質量%窒化ホウ素分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%窒化ホウ素分散液333.3g及びNMP151.7gを加え、これにODA34.42g(総量0.202モル)と、s-BPDA50.58g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対して窒化ホウ素を10質量%含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表3に示した。
上記(4’-b)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表3に示した。
(5’-a)フィラーを含有するポリイミド前駆体溶液組成物の製造方法
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、溶媒としてNMP400gを加え、これにODA40.50g(0.202モル)と、s-BPDA59.50g(0.202モル)とを加え、50℃で10時間撹拌して、固形分濃度18.5質量%、溶液粘度195.0Pa・sのポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物にケッチェンブラック(ライオン社製、ケッチェンブラックECP-600JD、揮発分0.7質量%)5gを添加後、3本ロールで処理し、ポリイミド前駆体溶液組成物全量に対してカーボンブラックを5質量%含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表3に示した。
上記(5’-a)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表3に示した。
(6’-a)フィラーを含有するポリイミド前駆体溶液組成物の製造方法
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、溶媒としてNMP400gを加え、これにODA40.50g(0.202モル)と、s-BPDA59.50g(0.202モル)とを加え、50℃で10時間撹拌して、固形分濃度18.5質量%、溶液粘度207.5Pa・sのポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物にAMC(宇部興産社製)5gを添加後、3本ロールで処理し、ポリイミド前駆体溶液組成物全量に対して炭素繊維5質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表3に示した。
上記(6’-a)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表3に示した。
(7’-a)フィラーを含有する分散溶液の製造方法
NMP400gにAMC(宇部興産社製)10g及びODA(分子量:200.26)40.50g(0.202モル)を添加し、ボールミル(ボール径2mm及び6mmを併用)を用いて室温にて16時間混合を行い、炭素繊維を含有する分散溶液を得た(2.2質量%炭素繊維分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記で得られた2.2質量%炭素繊維分散液450.5gにs-BPDA59.50g(0.202モル)を加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対して炭素繊維10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表3に示した。
上記(7’-b)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表3に示した。
(8’-a)フィラーを含有する分散溶液の製造方法
NMP400gにAMC(宇部興産社製)22.76g及びラウリルジメチルアミンオキシド(花王社製、アンヒトール20N、有効成分35%)32.51gを添加し、ボールミル(ボール径2mm及び6mmを併用)を用いて室温にて16時間混合を行い、炭素繊維を含有する分散溶液を得た(5質量%炭素繊維分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記5質量%炭素繊維分散液400gにODA40.50g(0.202モル)と、s-BPDA59.50g(0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対して炭素繊維10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表3に示した。
上記(8’-b)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表3に示した。
(9’-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
(3-a)と同様に調製し、固形分濃度17.9質量%、溶液粘度50.5Pa・sのポリイミド前駆体溶液組成物を得た。
DMAc932.5gにケッチェンブラック(ライオン社製、ケッチェンブラックECP-600JD、揮発分0.7質量%)30g及び上記で得られたポリイミド前駆体溶液組成物37.5gを添加し、ボールミル(ボール径2mm及び6mmを併用)を用いて室温にて16時間混合を行い、カーボンブラックを含有する分散溶液を得た(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液333.3g及びDMAc79.2gを加え、これにODA40.20g(総量0.202モル)と、s-BPDA59.05g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表3に示した。
上記(9’-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表3に示した。
(10’-a)フィラーを含有する前のポリイミド前駆体溶液組成物の調製
(3-a)と同様に調製し、固形分濃度17.9質量%、溶液粘度50.5Pa・sのポリイミド前駆体溶液組成物を得た。
DMAc220gにケッチェンブラック(ライオン社製、ケッチェンブラックECP-600JD、揮発分0.7質量%)30g及び上記で得られたポリイミド前駆体溶液組成物750gを添加し、ボールミル(ボール径2mm及び6mmを併用)を用いて室温にて16時間混合を行い、カーボンブラックを含有する分散溶液を得た(3質量%カーボン分散液)。
攪拌機、窒素ガス導入・排出管を備えた内容積500mlのガラス製の反応容器に、上記3質量%カーボン分散液333.3g及びDMAc126.7gを加え、これにODA34.42g(総量0.202モル)と、s-BPDA50.58g(総量0.202モル)とを加え、50℃で10時間撹拌して、ポリイミド前駆体溶液組成物全量に対してカーボンブラック10質量%を含有するポリイミド前駆体溶液組成物を得た。このポリイミド前駆体溶液組成物の特性を表3に示した。
上記(10’-c)で得られたポリイミド前駆体溶液組成物を用いて、(1-d)と同様にポリイミド膜を形成した。このポリイミド膜の特性等について結果を表3に示した。
12 頭頂部
13 胴部
21 集合体
Claims (8)
- ポリイミド前駆体溶液組成物を用いてフィラーを溶媒に分散させたことを特徴とするフィラーを含有する分散溶液。
- フィラーの濃度が、フィラーを含有する分散溶液全体の質量に対して1~7質量%であることを特徴とする請求項1記載のフィラーを含有する分散溶液。
- 電子導電性及び/または熱伝導性を有するフィラーの1つ以上をフィラーとして用いる請求項1または2記載のフィラーを含有する分散溶液。
- フィラーを含有する分散溶液中のポリイミド前駆体の濃度が、フィラー濃度に対して50~300質量%であることを特徴とする請求項1~3記載のフィラーを含有する分散溶液。
- 請求項1~4記載のフィラーを含有する分散溶液に、テトラカルボン酸二無水物及び/またはその誘導体と、ジアミン化合物とを溶解し、重合させて得られるフィラーを含有するポリイミド前駆体溶液組成物。
- 請求項5記載のフィラーを含有するポリイミド前駆体溶液組成物を用いて得られるポリイミド。
- フィラーを含有する分散溶液にテトラカルボン酸二無水物及び/またはその誘導体と、ジアミン化合物とを溶解し、重合して得られるフィラーを含有するポリイミド前駆体溶液組成物を用いるポリイミド膜の製造方法において、ポリイミド前駆体溶液組成物を用いてフィラーを溶媒に分散して前記フィラーを含有する分散溶液を得ることを特徴とするポリイミドの製造方法。
- 溶媒中、フィラーとポリイミド前駆体溶液組成物とを混合し、フィラーを含有する分散溶液を得る工程と、
前記フィラーを含有する分散溶液と、溶媒と、テトラカルボン酸二無水物及び/またはその誘導体とジアミン化合物とを混合し、テトラカルボン酸二無水物及び/またはその誘導体とジアミン化合物を反応させてフィラーを含有するポリイミド前駆体溶液組成物を得る工程と
を含むことを特徴とする、フィラーが分散されたポリイミドの製造方法。