Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/16—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J3/00—Processes of treating or compounding macromolecular substances
  • C08J3/02—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques
  • C08J3/03—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques in aqueous media
  • C08J3/075—Macromolecular gels
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/49—Phosphorus-containing compounds
  • C08K5/51—Phosphorus bound to oxygen
  • C08K5/52—Phosphorus bound to oxygen only
  • C08K5/5205—Salts of P-acids with N-bases
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F222/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical and containing at least one other carboxyl radical in the molecule; Salts, anhydrides, esters, amides, imides, or nitriles thereof
  • C08F222/10—Esters
  • C08F222/1006—Esters of polyhydric alcohols or polyhydric phenols
  • C08F222/102—Esters of polyhydric alcohols or polyhydric phenols of dialcohols, e.g. ethylene glycol di(meth)acrylate or 1,4-butanediol dimethacrylate
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]

Definitions

• the present invention relates to a gel composition, and particularly relates to a gel composition that can be used as an impact resistant absorbing material that contains ionic liquid, to an application thereof, and to a manufacturing method thereof.
• Impact resistant absorbing materials are widely used in various products that are incorporated into daily life in order to reduce impact to the body in products such as bedding and sporting goods (such as running shoes); in order to eliminate the effects of vibration on the characteristics of equipment for precision equipment and acoustic devices; or in order to prevent damage to products or the like during transportation in the field of packaging materials.
• Japanese Unexamined Patent Application 2001-151979 discloses a gel composition with excellent impact absorption characteristics produced by blending mineral oil, castor oil, or cottonseed oil or the like as a softening agent with a triblocked styrene based elastomer and a diblocked styrene based elastomer. Furthermore, Japanese Patent Disclosure H7-3165 discloses a manufacturing method for a porous silicone gel suitable for use as an impact resistant material for sports shoes.
• Ionic liquids are also referred to as ambient temperature molten salts and are liquids at ambient temperature. They are primarily used as electrolytic solutions for various electrochemical devices such as lithium rechargeable batteries and the like because of the high ionic conductivity and non- volatility. Furthermore, the development of gel electrolytes using ionic liquids has also been under investigation recently in order to prevent liquid leaking from the device.
• Japanese Unexamined Patent Application 2005-179551 discloses a gel electrolyte that is used as an electrolyte for electrochemical devices such as lithium rechargeable batteries and electrochromic display elements and the like.
• the level of impact absorption that is required of the impact resistant absorbing material varies depending on the application, and there has been demand for development of gel compositions that have high impact absorbency . Furthermore, impact resistant absorbing materials are used in various applications, so in addition to the impact absorbency, the addition of added value by providing properties corresponding to the application is also required.
• An objective of the present invention is to provide an improved gel composition usable as an impact resistant material, which has an impact absorbing performance and other added values, as well as a method for preparing this gel composition.
• the gel composition in one aspect of the present invention provides a gel composition usable as an impact resistant absorbing material, containing a polymer having, as a constituent unit, at least one of an acidic group or a basic group, and 50 weight % or more of an ionic liquid.
• the method of preparing the gel composition in another aspect of the present invention provides a method for preparing a gel composition usable as an impact resistant absorbing material, including: preparing a mixture liquid containing a monomer or polymer having, as a constituent unit, at least one of an acidic group or a basic group, a cross-linking agent and 50 weight % or more of an ionic liquid, and polymerizing and cross-linking said monomer or cross-linking said polymer in said mixture liquid to form a gel composition.
• the impact resistant absorbing material in another aspect of the present invention provides an impact resistant absorbing material that uses the gel composition of the first aspect of the present invention.
• the gel composition of the present invention and the impact resistant absorbing material made using this composition is a gel composition containing large quantities of ionic liquid, and therefore impact is effectively absorbed, and an impact resistant absorbing material can be provided that can demonstrate a practical level of impact absorbency while providing the added values of non- volatility and flame retardancy that are properties provided by the ionic liquid.
• the method of preparing the gel composition of the present invention can provide the aforementioned gel composition of the present invention using a simple process.
• FIG. 1 is a schematic cross-section view showing the construction of a measuring apparatus that was used for measuring the impact absorbency of the gel composition of the embodiments of the present invention.
• the gel composition of one aspect of an example of the present invention contains an ionic liquid in a polymer structure known as a polymer network, and can be used as an impact resistant absorbing material.
• Conventional examples of impact resistant absorbing materials that use an ionic liquid or a gel composition as impact resistant absorbing material are not known, and with the present invention, using a gel composition containing an ionic liquid not only provides favorable impact absorbency, but also newly provides added values that were not achievable with a conventional impact resistant absorbing material.
• gel refers to a dispersion-based solution with high viscosity that has lost fluidity
• ionic liquid refers to a substance that is an electrolyte made from anions and cations and that exists as a liquid at ambient temperature and pressure (25°C, 1 arm. (1 x 10 5 Pa).
• ionic liquids are also generally referred to as "ambient temperature molten salts”.
• the ionic liquid that is included in the gel composition of an aspect of the present invention has the ability to effectively provide impact absorption capability while having the properties of an ionic liquid such as non- volatility, flame retardancy, ionic conductivity, and the like.
• the gel composition of an aspect of the present invention contains a large quantity of ionic liquid, such as 50 weight % or more of the total composition, and the characteristics of flexibility and ionic liquidity are comparatively clearly exhibited.
• the polymer that is used in the gel composition of an aspect of the present invention includes at least one constituent unit that is an acidic group or basic group.
• the acidic group can be for example carboxyl groups, hydroxyl groups, sulfonate groups, and the like.
• the basic group can be for example primary, secondary, and tertiary amine groups, primary, secondary, tertiary, and quaternary ammonium groups, amido groups, imidazole groups, imido groups, morpholine groups, and piperidyl groups and the like.
• the polymer that is used in the gel composition of an aspect of the present invention can be a homopolymer, copolymer, or multi-polymer with at least one type of monomer selected from vinyl-based derivatives or salts thereof that contain these acidic groups or basic groups, as well as phenyl resins, epoxy resins, and polysaccharides such as cellulose, starch, and hyaluronic acid, and the like.
• Polymers that contain these acidic groups or basic groups can easily form a gel by incorporating the ionic liquid in a polymer matrix by forming interactions such as hydrogen bonds with the ionic liquid when polymerization is performed in the presence of the ionic liquid.
• monomers which have a carboxyl group as the acidic group include acrylic acid, methacrylic acid, 2-acryloyloxy ethyl phthalate, 2- methacryloyloxyethyl phthalate, 2-acryloyloxyethyl hexahydrophthalate, 2- methacryloyloxyethyl hexahydrophthalate, 2-acryloyloxypropyl acrylate, 2- methacryloyloxypropyl acrylate, ethylene oxide modified succinate acrylate, ethylene oxide modified succinate methacrylate, propylene oxide modified succinate acrylate, and propylene oxide modified succinate methacrylate and the like.
• the solubility with the ionic liquid will be favorable, and bleed out will not easily occur. Furthermore, interactions such as hydrogen bonds are easily formed with the ionic liquid, and large quantities of ionic liquid are easily incorporated into the polymer matrix. Therefore, a gel composition containing large quantities of ionic liquid components can be provided. Furthermore, if an acrylic resin, such as an acrylic acid, homopolymer or copolymer are used as the polymer, the gel composition can be made adhesive. In addition, if such an acrylic resin is used, an adhesive layer is not required and the gel composition can be directly applied and used in the required location.
• an acrylic resin such as an acrylic acid, homopolymer or copolymer
• examples of monomers having a hydroxyl group as the acidic group include 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, 4-hydroxybutyl methacrylate, 2- hydroxybutyl acrylate, 2-hydroxybutyl methacrylate, epichlorohydrin (ECH) modified phenoxy acrylate, ECH modified phenoxy methacrylate, glycerol acrylate, glycerol methacrylate, ethylene glycol acrylate, ethylene glycol methacrylate, polyethylene glycol acrylate, polyethylene glycol methacrylate, propylene glycol acrylate, propylene glycol methacrylate, polypropylene glycol acrylate, polypropylene glycol methacrylate, 2- hydroxyethyl acrylamide, 2-hydroxypropyl acrylamide, 2-hydroxy butyl acrylamide, vinyl alcohol, acryl-
• examples of monomers having a sulfonate group as the acidic group include 2-acryloyloxy ethyl sulfonic acid, 2-methacryloxy ethyl sulfonic acid, sodium 2- acryloyloxy ethyl sulfonate, lithium 2-acryloyloxy ethyl sulfonate, ammonium 2- acryloyloxy ethyl sulfonate, imidazolium 2-acryloyloxy ethyl sulfonate, pyridinium 2- acryloyloxy ethyl sulfonate, sodium 2-methacryloxy ethyl sulfonate, lithium 2- methacryloxy ethyl sulfonate, ammonium 2-methacryloxy ethyl sulfonate, imidazolium 2- methacryloxy ethyl sulfonate, pyridinium 2-methacryloxy eth
• examples of monomers having a primary, secondary, and or tertiary amine group as the basic group include dimethylaminoethyl acrylate dimethylaminopropyl acrylate, dimethylaminobutyl acrylate, dimethylaminoethyl methacrylate, dimethylaminopropyl methacrylate, dimethylaminobutyl methacrylate, 2-hydroxy-3- dimethylaminopropyl acrylate, 2-hydroxy-3 -dimethylaminopropyl methacrylate, diethylaminoethyl acrylate, diethylaminopropyl acrylate, diethylaminobutyl acrylate, diethylaminoethyl methacrylate, diethylaminopropyl methacrylate, diethylaminobutyl methacrylate, 2-hydroxy-3 -diethylaminopropyl acrylate, 2-hydroxy-3 -diethylaminopropyl meth
• examples of monomers which have a primary, secondary, tertiary, or quaternary ammonium group as the basic group include acryloyloxyethyldimethyl ammonium fluoride, acryloyloxyethyldimethyl ammonium chloride, acryloyloxyethyldimethyl ammonium bromide, acryloyloxyethyldimethyl ammonium iodide, acryloyloxypropyldimethyl ammonium fluoride, acryloyloxypropyldimethyl ammonium chloride, acryloyloxypropyldimethyl ammonium bromide, acryloyloxypropyldimethyl ammonium iodide, acryloyloxybutyldimethyl ammonium chloride, acryloyloxybutyldimethyl ammonium bromide, acryloyloxybutyldimethyl ammonium iodide, methacryloxye
• examples of monomers having amide groups as the basic group include dimethyl acrylamide, dimethyl methacrylamide, diethyl acrylamide, dimethyl methacrylamide, isopropyl acrylamide, isopropyl methacrylamide, and the like.
• Examples of monomers having an imidazole group, imide group, formalin group, or piperidyl group as the basic group include vinyl imidazole, imidoacrylate, imidomethacrylate, acryloyl formalin, tetramethyl piperidyl acrylate, tetramethylpiperidyl methacrylate, pentamethylpiperidyl acrylate, pentamethylpiperidyl methacrylate, and the like.
• the gel composition of one aspect of the present invention contains an ionic liquid that accounts for 50 weight % or more of the total.
• the gel composition can be made soft, and can be provided with the properties of the ionic liquid such as non- volatility, flame retardancy, and ionic conductivity and the like in addition to the impact absorption capability intrinsic to the gel composition.
• the ionic liquid contains both ionic bonds between the cations and the anions and hydrogen bonds between the polymer structure and the ionic liquid, so friction will easily be generated due to vibration in the bonded regions, and therefore the impact energy is effectively converted to thermal energy because of the vibration and friction, and a higher impact absorption capacity can be demonstrated as compared to a conventional gel impact resistant absorbing material such as an organogel or the like that contains oil in a polymer without this structure.
• the impact absorption capability can be expected to increase as the ratio of ionic liquid in the gel composition increases. Therefore, the amount of ionic liquid in the gel composition is preferably 60 weight % or higher, 70 weight % or higher, or even 80 weight % or higher. If the amount is 70 weight % or higher, impact absorption properties comparable to those of a commercial impact resistant absorbing material can be obtained, and if the amount is approximately 80 weight % or higher, the impact absorption properties obtained can be made higher than those of a conventional impact resistant absorbing material that uses urethane rubber, organogel, or silicone rubber.
• the impact absorption capability will also increase and the properties of the ionic liquid can be made more pronounced.
• properties inherent to the ionic liquid such as non-volatility, ionic conductivity, flame retardancy, and the like, can be added to the impact absorption capability.
• the amount of ionic liquid in the gel composition is preferably an amount that can be supported by the gel composition, and the amount of ionic liquid is preferably 95 weight % or less of the total amount of the gel composition. Furthermore, if the amount is 90 weight % or less, a more stable structure can be obtained, but depending on the application, the amount of ionic liquid in the gel composition can be adjusted to match the required level of impact absorbency.
• the type of ionic liquid included in the gel composition of one aspect of the present invention is not restricted. The cations are not particularly restricted, and commonly known cations can also be used.
• Ri NH 3 + primary (Ri NH 3 + ), secondary (Ri R 2 NH 2 + ), tertiary (Ri R 2 R 3 NH + ), quaternary (Ri R 2 R 3 R 4 N + ) chain type ammonium cations (where in the formulas, Ri , R 2 , R3 , and R4 are independently straight chain or branched alkyl groups with between 1 and 15 carbon atoms, or are straight or branched alkyl groups with between 1 and 15 carbon atoms having one or more hydroxyl side chains, or a phenyl group) and cyclic ammonium cations can be used.
• Examples of cyclic ammonium cations include oxazolium, thiazolium, imidazolium, pyrazolium, pyrolinium, furazanium, triazolium, pyrolidinium, imidazolidinium, pyrazolidinium, pyrolinium, imidazolinium, pyrazolinium, pyrazinium, pyrimidinium, pyridazinium, piperidinium, piperazinium, morpholinium, indolium, and carbazolium.
• examples of other cations include chain-type phosphonium (RsR 6 RvP + and RSR 6 RVRSP + ), chain-type sulfonium cations (R9R10R11S ) (where in the formulas, R5, R 6 , Rv, Rs, R9, Rio, Rn independently represent straight chain or branched alkyl groups or phenyl groups with between 1 and 12 carbon atoms) and cyclic type sulfonium cations.
• examples of cyclic sulfonium cations include thiophenium, thiazoinium, and thiopyranium.
• the anion can be an ion of an inorganic acid such as phosphoric acid, sulfuric acid, or carbonic acid, or a fluorine-based ion or the like. Various combinations of cations and anions are possible.
• fluorine-based anions include tetrafluoroborate (BF 4 " ), hexafluorophosphate (PF 6 “ ), hexafluoroarsenate (AsF 6 " ), trifluoromethylsulfonate (CF3 SO3 " ), bis(fluorosulfanyl)imide [(FSO 2 ) 2 N “ ], bis(trifluoromethylsulfanyl)imide [(CF 3 SO 2 ) 2 N " ], bis(trifluoroethylsulfanyl)imide [(CF 3 CF 2 SO 2 ) 2 N " ], and tris(trifluoromethylsulfanylmethide) [(CF 3 SO 2 ) 3 C " ] .
• non-halogen-based anions are preferable, and in particular, if phosphate ions are used, costs will be lower and economics will be improved thereby, and high flame retardancy can be obtained compared to using fluorine-based ions.
• salts containing phosphate groups expressed by the general formulas [PO 4 3 " ], [RPO 4 2 " ], or [RR 5 PO 4 " ] (where R and R' represent straight chain or branched alkyl groups with between 1 and 8 carbon atoms or phenyl groups) can be used as phosphate based anions.
• R is a straight chain or branched alkyl group with between 1 and 8 carbon atoms or phenyl group.
• the gel composition of this aspect of the present embodiment can provide flame retardancy if a flame retardant ionic liquid is used.
• flame retardancy herein refers to a level corresponding to V-I or higher, more preferably V-O or higher according to the flame retardancy test method of Safety Standard UL-94 designated by, for example, US-based Underwriters Laboratories Inc. (UL), as well as to the property of extinguishing flames within a range between several seconds and several dozen seconds when removed from a burner after being in contact with a flame such as a burner for a fixed period of time as shown in the flame retardancy test examples of the following embodiments or self extinguishing properties according to method A as designated by JISK6911.
• the impact absorbency of the gel composition of this aspect of the present embodiment can be evaluated by measuring the surface hardness and by using a drop test and the like.
• the surface hardness test can be performed by measuring the Asker hardness defined by SRISOlOl (Society of Rubber Industry, Japan Standard Specification) measured using a Durometer (spring type hardness meter) manufactured by Asker Company.
• Asker C hardness is defined as a relative surface hardness using the hardness of a 55 g spring load as 0 and the hardness of a 455 g spring load as 100, using a probe with a 5.08 mm diameter semi-spherical shape.
• soft materials where the hardness is difficult to express using Asker C hardness can use "Asker F hardness".
• the gel composition of this aspect of the present embodiment tends to have a higher impact absorption effect if the surface hardness is softer, and for example, with a gel composition formed as a 10 mm thick sheet with an Asker C hardness of 75° or less, impact absorbency can be obtained that is at least equal to a conventional impact resistant absorbing material that uses urethane rubber, organogel, or silicone gel. Furthermore, if the Asker C hardness is 10° or less, a higher impact absorbency can be obtained. When measuring the impact absorbency of the gel composition using a drop test, the measurement can be performed using the following conditions for example.
• a weight with a set shape and weight is dropped naturally onto a plate from a fixed distance, and the acceleration (AO) of the vibration generated on the plate due to the impact shock is measured.
• the gel composition is attached to the plate, and similarly the weight is dropped and the acceleration (Am) of the vibration generated on the plate due to the impact shock is measured.
• the impact absorbency can be evaluated by the ratio of the two accelerations (Am/AO). The specific measurement conditions are described in the embodiments. Note, measurement of the impact absorbency is not restricted to the aforementioned method.
• the gel composition of this aspect can be manufactured by blending and ionic liquid, (monomer or polymer), and a cross-linking agent if necessary, and the monomer can be polymerized and crosslinked by means of irradiation with UV light or by heating the monomer, or the polymer can be crosslinked thereby.
• the ionic liquid may be a commercial product, but can also be synthesized using a method such as an acid ester method, a complex formation method, a neutralization method or the like. Furthermore, a plurality of types can be blended together and used instead of a single type.
• an amine is added by drops to an inorganic/organic phosphoric acid such as phosphoric acid or dibutyl phosphate or the like, which is diluted 5 : 1 using an organic solvent such as alcohol, under low-temperature conditions such as at 0 0 C, and then sufficiently mixing it at room temperature. Next, this solution is distilled under reduced pressure to evaporate off the solvent.
• an inorganic/organic phosphoric acid such as phosphoric acid or dibutyl phosphate or the like
• an organic solvent such as alcohol
• the monomer is a monomer that includes as constituent units at least one acidic group selected from the group consisting of carboxyl groups, hydroxyl groups, and sulfonate groups and the like, or a monomer that includes as constituent units at least one basic group selected from the group consisting of primary, secondary, and tertiary amine groups, primary, secondary, tertiary, and quaternary ammonium groups, amide groups, imidazole groups, imide groups, formalin groups, and piperidyl groups and the like.
• the monomer is not restricted to a single type, and two or more types can also be used.
• an acrylic acid monomer that is a monomer that contains a carboxyl group a monomer such as acrylic acid, ammonium acrylate, sodium acrylate, lithium acrylate, methacrylic acid, ammonium methacrylate, sodium methacrylate, lithium methacrylate, and the like can be used.
• the blending ratio of ionic liquid to monomer is 100 mass parts or more of ionic liquid to 100 mass parts of monomer such that, for example, 50 weight % or more of the final gel composition obtained is ionic liquid.
• a polymer can be used instead of the monomer. Furthermore, both monomers and polymers can be used, or a plurality of types of monomers and polymers can be used. In either case, 100 mass parts or more of ionic liquid are added to a total of 100 mass parts of monomer and polymer.
• the cross-linking agent can be for example 1 , 6-hexanediol diacrylate 1 , 6-hexanediol dimethacrylate, ECH modified 1 , 6- hexane diol diacrylate, ECH modified 1 , 6-hexane diol dimethacrylate, 1 , 9-nonanediol diacrylate, 1, 9-nonanediol dimethacrylate, ethylene glycol diacrylate, ethylene glycol dimethacrylate, polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, propylene glycol diacrylate, propylene glycol dimethacrylate, polypropylene glycol diacrylate, polypropylene glycol dime dim
• the polymerization method can be by either heat or radiation. If ultraviolet light (UV) with a wavelength between 200 nm and 400 nm is used as the radiation, polymer hardening can occur at room temperature, so the gel composition can be directly formed even on substrates with a relatively low melting point. Note, if UV polymerization is performed, a polymerization initiator is added. The amount of polymerization initiator that is added is between 0.01 mass parts and 1 mass parts per 100 mass parts of monomer.
• polymerization initiator examples include l-[4-(2-hydroxyethoxy)phenyl]- 2-hydroxy-2 -methyl- 1 -propane- 1 -one (IrgacureTM 2959, Ciba Specialty Chemicals), 1- hydroxycyclohexyl phenyl ketone (IrgacureTM 184, Ciba Specialty Chemicals), 2,2- trimethyl benzoyl diphenyl phosphine oxide (IrgacureTM 651, Ciba Specialty Chemicals), 2,4,6-trimethyl benzoyl diphenyl phosphine oxide (LucirinTM TPO, BASF), 2,4,6- trimethyl benzoyl phenyl ethoxy phosphine oxide (LucirinTM TPO-L, BASF), 2-benzyl-2- trimethyl amino- l-(4-morpholinophenyl) butane- 1 -one (IrgacureTM 369, Ciba Specialt
• a filler can also be added as a heat dissipating material or an electromagnetic wave absorbing material.
• the gel composition is essentially transparent, the composition can be colored by adding a pigment or colorant.
• a cohesion enhancing agent, surface wetting agent, leveling agent, antioxidant, preservative, and the like can also be added.
• the material can be in a sheet with a thickness between several millimeters and several dozen millimeters, or can be a film with a thickness fewer than several millimeters.
• a material can be formed to match the shape of the member that will be overlaid.
• a solution blend containing the aforementioned ionic liquid, monomer, cross-linking agent, and photoinitiator can be poured into a mold frame with good release properties such as silicone rubber and the like, and then a peeled transparent resin film can be laminated thereon.
• ultraviolet light (UV) is a radiated through the transparent resin film to polymerize the blended solution.
• a gel composition in the form of a sheet can be obtained by peeling the mold frame and resin film.
• the blended solution can also be coated onto the peeled resin film, and then laminated with a peeled resin film so as to be sandwiched between the resin films, and then the blended solution can be polymerized by irradiating it with ultraviolet light (UV). After polymerization a gel composition in the form of a film can be obtained by peeling off both films. Alternatively, the gel composition can be used as an impact resistant absorbing material by remaining sandwiched between the two resin films. Furthermore, the edges of the two resin films may be sealed in order to make a construction with a sealed gel composition.
• UV ultraviolet light
• the other film is peeled off and the gel composition surface on the peeled side is applied to the location where the impact resistant absorbing material is to be used. If an acrylic acid homopolymer or copolymer is used as the polymer of the gel composition, the gel composition itself will have adhesive strength, and can be used by direct application to the required location.
• the resin film used is not particularly restricted, but is preferably a film with flexibility.
• Examples include resin films made of polyethylene, polypropylene, vinyl chloride, polycarbonate, thermoplastic polyurethane, cellophane (registered trademark), vinylidene fluoride, polyethylene terephthalate (PET), polystyrene and vinylidene chloride acrylic, polyurethane, polyolefm, fluorine-based resins (PVdF, ETFE, and the like), polyimide, phenol resin, epoxy resin, polyamide, polyphenylene ether, and the like.
• Specific applications where the gel composition of this aspect of the present embodiment is used as an impact resistant absorbing material include shoe bottoms and liners for various types of shoes including running shoes, walking shoes, and other sports shoes and the like.
• Shoes using these impact resistant absorbing materials can reduce the impact on the body when worn. Furthermore, when used as the soles of work shoes in a factory, the conductivity of the ionic solution can demonstrate a static electricity eliminating effect. Furthermore, the material can also be used on sporting-goods such as grips for tennis rackets, baseball bats, and golf clubs and the like. Thereby the shock on the body (particularly on the hands and arms) generated during impact can be relieved.
• the material in care-giving products such as mats for care- giving beds will have the effect of preventing bedsores.
• the material can also be used as an impact resistant absorbing material for automotive members such as the areas around the engine, inside vehicle walls, seats, and child seats, as well as construction members, railroad members, guardrail corners, and helmets.
• a flame retardant impact resistant absorbing material can be provided.
• the material can be used as a member that is applied to a position on the inner or outer wall of the housing, or as a packaging material for precision equipment, but in this case, the material can provide not only impact adsorption, but the conductivity of the ionic liquid can also provide antistatic electricity effects.
• the gel composition can provide the effects of an impact absorbing member and the flame retardancy of the ionic liquid can act as a fire extinguisher.
• the ionic liquid is non-volatile, so stable properties can be achieved across a wide temperature range.
• the present invention is described below while referring to embodiments, but the scope of the present invention is not restricted to the contents of the embodiments.
• I. Method of Synthesizing Ionic Liquid The gel composition of the present embodiment was produced by synthesizing three types of ionic liquids under the following conditions, and then manufacturing the gel composition using the preparation methods described below.
• TrEA triethylamine
• TrEA-EtHPO 4 ZEt 2 PO 4 was used as the ionic liquid, and acrylic acid with a carboxyl group (COOH group) (AA) (special grade, manufactured by Wako Pure Chemical Industries, Ltd.) was used as the unsaturated monomer.
• acrylic acid with a carboxyl group (COOH group) (AA) (special grade, manufactured by Wako Pure Chemical Industries, Ltd.) was used as the unsaturated monomer.
• AA carboxyl group
• Polyethylene glycol diacrylate NK Ester A-
• Comparative Example 1 Comparative example 1 was a commercial impact resistant absorbing material (tradename:
• Sorbothane (registered trademark), manufactured by Sorbothane), a thermal hardening polyether-based polyurethane.
• Comparative Example 2 Comparative example 2 was a conventional organogel, manufactured under the following conditions.
• styrene-vinyl isoprene-styrene copolymer product name: Hybrar 5127 (manufactured by Kuraray Co., Ltd.) and 60 mass parts of liquid polybutene (product name: GLISSOPAL V1500 (manufactured by BASF) were dissolved in 291 mass parts of toluene, and then 50 mass parts of calcium carbonate (special grade, manufactured by Wako Pure Chemical Industries, Ltd.), 10 mass parts of carbon black (product name: #3030 (manufactured by Mitsubishi Chemical Corporation)), 1 mass part of stearic acid (special grade, manufactured by Wako Pure Chemical Industries, Ltd.), and 0.5 mass parts of Perbutyl P (manufactured by NOF Corporation) were added.
• calcium carbonate special grade, manufactured by Wako Pure Chemical Industries, Ltd.
• carbon black product name: #3030 (manufactured by Mitsubishi Chemical Corporation)
• stearic acid special grade, manufactured by Wako Pure Chemical Industries,
• the solution was applied using a knife coater to a peeled PET film, and then dried at 120 0 C for 20 minutes to obtain a film with a thickness of 100 ⁇ m.
• the coating process was repeated until 37 layers were formed, and then the film was cross-linked by heat pressing at 170 0 C for 20 minutes in order to obtain an organogel with a thickness of approximately 3 mm.
• Comparative Example 3 is a commercial silicone gel made by a padding approximately 30 mass % polydimethylsiloxane to a silicone rubber silicone gel, marketed under the product name Alpha gelTM and manufactured by Geltek.
• FIG. 1 shows a schematic cross-section view of the structure of an impact absorbency measuring apparatus 10.
• the measuring apparatus 10 has a base 11 with a horizontal surface, a rail 12 that extends in a perpendicular direction to the base, and a 10 mm thick metal plate 13 fixed to the rail 12 to the essentially parallel to the horizontal surface of the base 11.
• An acceleration detector 15 is provided on the back surface of the plate 13, and a iron plate 14 is attached such that it can move smoothly up and down along the rail 12 above the plate 13.
• the size of the iron plate 14 is 40 mm x 5 mm x 80 mm (width x depth x height), and the weight is 200 g.
• the 3 mm thick gel composition sheet 20 manufactured according to each embodiment was cut to a size of 40 mm x 5 mm to have essentially the same surface area as a iron plate 14, and then placed on the plate 13 and the iron plate 14 was dropped along the rail from a height of 60 cm and 10 cm.
• the setup was adjusted so that the shock resulting from dropping the iron plate 14 is uniformly received essentially across the entire surface 40 mm x 5 mm of the gel composition.
• the acceleration (Am) generated on the plate 13 by the shock of dropping it was measured using the acceleration detector 15 located on the back surface of the plate 13.
• the iron plate 14 dropping test was performed in similar manner without placing the gel composition 20 on the plate 13, and the acceleration (AO) of the plate 13 was measured.
• the impact absorbency of the gel composition was evaluated by comparing the acceleration values (Am/ AO).
• the "Asker C hardness”, “Asker F hardness”, or “Asker A hardness” was measured for the 10 mm thick gel composition sheets.
• "Asker C hardness” or “Asker F hardness” refers to the hardness measured using an Asker C hardness meter or an Asker F hardness meter, which are Durometers (spring type hardness meter) specified in The Society of Rubber Industry, Japan standard specification SRISOlOl.
• the Asker F hardness is measured for gel compositions that are too soft to be measured by an Asker C hardness meter, and the Asker A hardness is measured for gel compositions which are too hard to be measured by an Asker C hardness meter.
• the “Asker A hardness” refers to the hardness measured using a Type A durometer in conformance with JIS K 6253.
• a 50 mm long blue burner flame without a yellow tip was brought into contact with a round plate gel composition with a diameter of 25 mm and a thickness of 3 mm for 30 seconds.
• the condition of the gel composition immediately after removing the flame was visually confirmed. If the flame died immediately (at least within several seconds) without burning, an evaluation of "flame retardant” was made, and if the burning continued, an evaluation of "not flame retardant” was made.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Dispersion Chemistry (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Processes Of Treating Macromolecular Substances (AREA)
• Fluid-Damping Devices (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (2)

Family

ID=41255704

Family Applications (1)

Country Status (6)

Cited By (7)

Families Citing this family (16)

Citations (4)

Family Cites Families (18)

• 2008
  • 2008-05-02 JP JP2008120384A patent/JP2009269974A/ja not_active Withdrawn
• 2009
  • 2009-04-24 US US12/990,510 patent/US8461237B2/en not_active Expired - Fee Related
  • 2009-04-24 EP EP09739496.9A patent/EP2285900A4/en not_active Withdrawn
  • 2009-04-24 WO PCT/US2009/041693 patent/WO2009134694A2/en not_active Ceased
  • 2009-04-24 AU AU2009241418A patent/AU2009241418B2/en not_active Ceased
  • 2009-04-24 CN CN2009801235637A patent/CN102066486B/zh not_active Expired - Fee Related

Patent Citations (4)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events