Classifications

• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
  • H01L23/00—Details of semiconductor or other solid state devices
  • H01L23/34—Arrangements for cooling, heating, ventilating or temperature compensation ; Temperature sensing arrangements
  • H01L23/36—Selection of materials, or shaping, to facilitate cooling or heating, e.g. heatsinks
  • H01L23/367—Cooling facilitated by shape of device
  • H01L23/3677—Wire-like or pin-like cooling fins or heat sinks
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
  • H01L2224/00—Indexing scheme for arrangements for connecting or disconnecting semiconductor or solid-state bodies and methods related thereto as covered by H01L24/00
  • H01L2224/01—Means for bonding being attached to, or being formed on, the surface to be connected, e.g. chip-to-package, die-attach, "first-level" interconnects; Manufacturing methods related thereto
  • H01L2224/26—Layer connectors, e.g. plate connectors, solder or adhesive layers; Manufacturing methods related thereto
  • H01L2224/31—Structure, shape, material or disposition of the layer connectors after the connecting process
  • H01L2224/32—Structure, shape, material or disposition of the layer connectors after the connecting process of an individual layer connector
  • H01L2224/321—Disposition
  • H01L2224/32151—Disposition the layer connector connecting between a semiconductor or solid-state body and an item not being a semiconductor or solid-state body, e.g. chip-to-substrate, chip-to-passive
  • H01L2224/32221—Disposition the layer connector connecting between a semiconductor or solid-state body and an item not being a semiconductor or solid-state body, e.g. chip-to-substrate, chip-to-passive the body and the item being stacked
  • H01L2224/32225—Disposition the layer connector connecting between a semiconductor or solid-state body and an item not being a semiconductor or solid-state body, e.g. chip-to-substrate, chip-to-passive the body and the item being stacked the item being non-metallic, e.g. insulating substrate with or without metallisation
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
  • H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
  • H01L2924/095—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00 with a principal constituent of the material being a combination of two or more materials provided in the groups H01L2924/013 - H01L2924/0715
  • H01L2924/097—Glass-ceramics, e.g. devitrified glass
  • H01L2924/09701—Low temperature co-fired ceramic [LTCC]

Definitions

• the present invention relates to the structure of a thermal via provided in a ceramic substrate.
• WO 2002-045470 discloses a method for obtaining aluminum nitride with high thermal conductivity by reducing the residual carbon in an aluminum nitride molded body before firing it.
• JP 2002-158318 discloses a technique for promoting heat radiation by arranging a highly thermally conductive material on the periphery of a thermal via.
• a thermal via can be made larger in order to improve its heat radiating properties, but if it is too large there will be insufficient adhesion between the filler of the thermal via and the sides of the thermal via, and the filler may fall out if external pressure is applied.
• the present invention is a ceramic substrate having a thermal via passing through the substrate for purposes of radiating heat to the outside of the substrate, wherein the ceramic substrate has a reinforcing structure that divides the opening of the thermal via into two or more, and the height of the reinforcing structure is less than the height of the thermal via.
• the present invention is also directed to a method for manufacturing this ceramic substrate and to an electronic component comprising this ceramic substrate.
• Figures 1 A and 1 B show the structure of a ceramic substrate of one embodiment of the present invention, with Figure 1A being a top view and Figure 1 B a cross-sectional view;
• Figure 2A and 2B is a drawing explaining the relationship between the thermal via and reinforcing structure in the ceramic substrate of the present invention, with Figure 2A and 2B showing a top view and cross sectional view of one embodiment of the present invention and Figure 2C through Figure 2H showing views of comparative examples;
• Figure 3 is a drawing explaining the relationship between the thermal via and reinforcing structure in the ceramic substrate of the present invention, with Figure 3A and 3B show and top view and cross section of one embodiment of the present invention and Figure 3C through Figure 3D show comparative examples;
• Figure 4 is a drawing explaining the relationship between the thermal via and reinforcing structure in the ceramic substrate of the present invention, with Figure 4A and 4 B show one embodiment of the present invention and Figure 4C through Figure 4H show comparative examples;
• Figure 5 is a drawing explaining the relationship between the thermal via and
• Figure 7A - 7D is a drawing explaining a different method for manufacturing the ceramic substrate of the present invention.
• Figure 8A-8J is a drawing explaining the procedure for filling a via hole or the like in the ceramic substrate of the present invention with a filler composition
• Figure 9 is a diagram showing one example of an electronic component of the present invention.
• Figure 10 shows the shapes and the like of ceramic substrates prepared in the Examples of the present invention.
• the present invention relates to the structure of a ceramic substrate having a thermal via that passes through the substrate for purposes of radiating heat to the outside.
• the thermal via has a reinforcing structure that divides the opening of the via into two or more, and the height of this reinforcing structure is less than the height of the thermal via.
• An alumina, aluminum nitride, zirconium oxide or known silica, glass or other substrate can be used for the ceramic substrate of the present invention.
• the material of the reinforcing structure contained in the thermal via is not particularly limited as long as it can prevent dropout of the filler that fills the thermal via, but it is preferably of the same material as the ceramic substrate.
• the reinforcing structure in the thermal via of the present invention can have any structure as long as it divides the opening of the thermal via into two or more, and as long as the height of the reinforcing structure is less than the height of the thermal via.
• One embodiment of the ceramic substrate of the present invention, having a thermal via containing a reinforcing structure has the structure shown in Figure 1 for example.
• Figure 1 A shows a top view while Figure 1 B shows an a-a' cross-section.
• ceramic substrate 100 has substrate body 102 and thermal via 104, and thermal via 104 is divided equally into four by reinforcing structure 106 (in these Specifications, reinforcing structure 106a (shown vertically) and reinforcing structure 106b (shown horizontally) are together called 106).
• reinforcing structure 106 is formed vertically from opening 110 at one end (bottom) of the thermal via towards opening 108 at the other end (top), and its height a is less than that of the thermal via (the height a of the reinforcing structure and height h of the thermal via are as defined below).
• the reinforcing structure and thermal via are each shown formed as rectangles perpendicular to the thickness of the ceramic substrate (a form which is preferred in the present invention), but the present invention is not limited to this structure, and for example the reinforcing structure and thermal via may have a trapezoidal cross-section in which the top opening 108 is larger than the bottom opening 110.
• the terms "top opening” and "bottom opening” indicate, respectively, the side for mounting a component from which heat is to be radiated (such as a LED chip), and the side for not mounting such a component when the ceramic substrate is used as an electronic component.
• a top view in these specifications is a view seen from the side with the top opening.
• a thermal via having reinforcing structure 106 of the present invention is divided into two or more by the reinforcing structure.
• the thermal via can be divided into only two by either the reinforcing structure 106a (shown vertically) or the reinforcing structure 106b (shown horizontally) in Figure 1 , or the reinforcing structure can be arranged so as to divide the thermal via into three or more.
• the position of the reinforcing structure in the thermal via is also not particularly limited. That is, in one embodiment of the present invention the through hole of thermal via 104 was divided uniformly as shown in Figure 1 , but the reinforcing structure does not have to be designed this way in the present invention.
• the position of the reinforcing structure in the thermal via in the vertical direction (thickness) of the ceramic substrate is also not particularly limited, and the position can be selected appropriately within a range that prevents dropout of the filler that fills the via hole.
• the reinforcing structure is preferably formed as a rectangle extending vertically from the bottom opening 1 10 of the thermal via towards the top opening 108 as shown in Figure 1 B.
• the reinforcing structure is provided inside the thermal via in substrate body 102 of the present invention.
• this reinforcing body fulfill all of the following conditions (i) through (iii):
• the "height a of the reinforcing structure” is the height of the reinforcing structure in the thermal via in the vertical direction (thickness direction) of the ceramic substrate.
• the “height h of the thermal via” in specification (i) is the height of the thermal via (through hole) in the ceramic substrate in the vertical direction (thickness direction).
• the "height a of the reinforcing structure” and “height h of the thermal via” are explained with reference to Figure 2A through Figure 2H.
• Figure 2 is only an example, however, and the present invention is not limited thereby.
• Figure 2A and 2B show the same thermal via with reinforcing structure as in Figure 1 above, which is desirable in the present invention
• Figure 2C and 2D show a thermal via without a reinforcing structure
• Figure 2E and 2F show an example with a step 202 (which is not a reinforcing structure) in the side of the thermal via
• Figure 2G and 2H show an example with a reinforcing structure in which the reinforcing structure divides the thermal via into multiple holes and has the same height as the height h of the thermal via.
• the cross-sections are the a-a' cross section and d-d' cross-section, respectively, in the top view.
• the "height a of the reinforcing structure” signifies the height (shown as a) of reinforcing structure 106 in thermal via 104 in the direction of thickness (vertical direction) of the ceramic substrate.
• the "height h of the thermal via” signifies the height (shown as h) in the direction of thickness (vertical direction) of the ceramic substrate extending from one opening (top opening) 108 to the other opening (bottom opening) 110 regardless of whether there is a reinforcing structure 106.
• the "top area b of the reinforcing structure” in specification (ii) signifies the area of the top of the reinforcing structure facing the top opening in the thermal via.
• the "opening area s of the thermal via” in specification (ii) signifies the area of the top opening of the thermal via in the ceramic substrate.
• the "top area b of the reinforcing structure” is explained with reference to Figure 3A through Figure 3D, while the “opening area s of the thermal via” is explained with reference to Figure 4A through Figure 4H.
• Figures 3 and 4 are only examples, however, and the present invention is not limited thereby.
• Figure 3A and Figure 4A show the same thermal via with reinforcing structure as in Figure 1 above, which is desirable in the present invention
• Figure 4C shows an example of a thermal via without a reinforcing structure
• Figure 4E shows an example with a step 202 (which is not a reinforcing structure) in the side of the thermal via
• Figure 3C and Figure 4G show examples with a reinforcing structure in which the reinforcing structure divides the thermal via into multiple holes and has the same height as the height h of the thermal via.
• the cross-sections are the a-a' cross-section and b-b' cross-section, respectively, of the top view
• the cross- sections are the a-a' cross-section and d-d' cross-section, respectively, of the top view.
• top area b of the reinforcing structure signifies the area of the top plane surface of reinforcing structure 106 in thermal via 104 that faces towards top opening 108 (the cross filled with dots in the top views of Figure 3A and Figure 3C and the part indicated by b throughout (same hereinafter) and the part shown by a heavy line in the cross-sections of Figure 3A and Figure 3C and the part indicated by b throughout (same hereinafter)).
• the "top area s of the thermal via” signifies the area of top opening 108 whether or not there is a reinforcing structure 106.
• the "opening area s of the thermal via” in specification (iii) is as described under (ii) above.
• the "side area t of the thermal via” in specification (iii) is the area including the whole side face of the thermal via hole and the sides of the reinforcing structure if one is present.
• the "side area t of the thermal via” is explained in more detail with reference to Figure 5A through Figure 5E. However, Figure 5 is only an example, and the present invention is not limited thereby.
• Figure 5A shows an example of a thermal via with reinforcing structure which is desirable in the present invention as in Figure 1
• Figure 5D shows an example of a thermal via without reinforcing structure
• Figure 5F shows an example having a step 202 (which is not a reinforcing structure) in the side of the thermal via
• Figure 5H shows an example with a reinforcing structure in which the reinforcing structure divides the thermal via into multiple holes and has the same height as the height h of the thermal via.
• cross- sections (5B) and (5C) are the a1-a1 ' and a2-a2' cross-sections, respectively, in the top view, while in Figure 5H the cross-section is the d- d' cross-section in the top view.
• the "side area t of the thermal via” is the area including the side 502 of the thermal via itself and the side area 504 of the reinforcing structure.
• the area 502 of the thermal via in the vertical direction (direction of thickness).
• the side of the thermal via hole has a step as in Figure 5F, it is the side area t including the area 502 of the thermal via in the vertical direction (direction of thickness) and the area 502 of the step part.
• the height a of the reinforcing structure is the same as the height h of the thermal via as shown in Figure 5D, it is a combination of the area 502 of the entire side surface of the thermal via hole and the area 504 of the entire side surface of the reinforcing structure.
• the thermal via of the ceramic substrate of the present invention can be filled with a filler in order to increase thermal conductivity.
• This filler is composed of a filler composition containing a material with good thermal conductivity.
• the filler composition includes a metal and a vehicle, and may optionally include thermally conductive materials other than metals.
• the metal is not particularly limited but is preferably a material including one or two or more metals selected from the group consisting of silver, palladium, gold, platinum, copper, aluminum and nickel. These metals may be used in various forms including spheres, flakes and the like.
• the average particle size of the metal is not particularly limited but is preferably 0.5 to 8 ⁇ m or more preferably 1 to 6 ⁇ m. 5 2.
• the filler composition may include a thermally conductive material.
• the thermally conductive material other than metal is not particularly limited, but is preferably selected from the group consisting of silicon carbide (SiC), aluminum nitride (AIN),o diamond and graphite. 3. Vehicle
• the type of vehicle is not particularly limited.
• an organic mixture of a binder resin such as ethyl cellulose resin, acrylic resin, rosin modified resin, polyvinyl butyral resin or the like
• an5 organic solvent such as butyl carbitol acetate (BCA), terpineol, ester alcohol, BC, TPO, etc.
• BCA butyl carbitol acetate
• terpineol terpineol
• ester alcohol BC, TPO, etc.
• the content percentages of the metal, vehicle and thermally conductive material in the filler composition are 70 to 96 wt% or preferably 80 to 94 wt% of metal, 4 to 40 wt% or preferably 6 to 20 wt% of vehicle o and 0 to 10 wt% or preferably 0.2 to 5 wt% of thermally conductive material based on the total weight of the composition.
• the filler composition of the present invention may also contain glass powder or the like as an additional component.
• Glass powder is compounded to improve the adhesive force between the fired ceramic and 5 the sintered composition.
• the content of glass powder is preferably 0.1 to 10 wt% or more preferably 0.2 to 5 wt% based on the total weight of the composition.
• the average particle size of the glass powder is preferably 0.1 ⁇ m to 5 ⁇ m or more preferably 0.3 ⁇ m to 3 ⁇ m.
• the filler composition of the present invention can be suitably produced mixing the aforementioned components with a triple roll mill or the like.
• the ceramic substrate manufacturing method of the first embodiment is a method for manufacturing a ceramic substrate having a thermal via that passes through the substrate for purposes of radiating heat to the outside. Specifically, it includes (1 ) a step of providing the ceramic substrate and (2) a step of forming a thermal via having a reinforcing structure in the ceramic substrate by cutting with a sandblaster or laser, which is a step of forming a thermal via wherein the reinforcing structure thereof divides the opening of the thermal via into two or more, and the height of the reinforcing structure is less than the height of the thermal via.
• Step 1 (see Figure 6) of the manufacturing method of this embodiment is explained.
• 6A ceramic substrate body 602 is prepared (this substrate is a commercial ceramic substrate such as a Tokuyama, Asahi Technoglass AIN substrate, Kyocera AI2O3 substrate or the like).
• the target ceramic substrate body can also be prepared as necessary by firing a green sheet consisting of a suitable material. Firing can be under suitable conditions and by suitable procedures according to the type of green sheet.
• 6Ba via hole having reinforcing structure 106 is formed in ceramic substrate body 602.
• a sandblasting process, laser process, electron beam process or the like can be adopted for forming via-hole 104 with reinforcing structure 106 in ceramic substrate body 602.
• a through hole having reinforcing structure 106 is formed by these methods in the ceramic substrate body to make a thermal via.
• fine sand 606 is blown through mask 604 having the shape of reinforcing structure 106 to thereby form a specific structure (reinforcing structure 608 for example as in the aforementioned Figure 6B) by sandblasting.
• a ceramic substrate used for an electronic component will also have a small- diameter circuit via-hole for conduction purposes in addition to the thermal via.
• the large-diameter via hole 104 constitutes a thermal via (including reinforcing structure 106) for radiating the heat of a mounted component, while the small-diameter via-hole 610 is a circuit via-hole.
• the sandblasting process can be applied through mask 612 (which lacks the shape of the reinforcing structure) until reinforcing structure 106 reaches the specified height.
• the laser or electron beam can be scanned to cut ceramic substrate body 602 until reinforcing structure 106 reaches the specified height.
• the conditions for laser or electron beam processing differ depending on the ceramic substrate body being cut.
• the conditions for exposing the ceramic substrate body can be selected appropriately from conventional technologies.
• the size of the thermal via is not particularly limited, but preferably the area of through hole on a plane parallel to the surface of the substrate is 4 mm 2 or more. More specifically, if the thermal via is circular it preferably has a relatively large diameter of 2.5 mm or more.
• This method is a method for using a green sheet to manufacture a ceramic substrate having a thermal via passing through the substrate for radiating heat to the outside, wherein the thermal via also has a reinforcing structure.
• it comprises (1 ),7A, a step of preparing (7a) a ceramic green sheet having a thermal via not formed with a reinforcing structure that divides the opening of the thermal via into two or more and (7b) a ceramic green sheet formed with a reinforcing structure that divides the opening of the thermal via into two or more, (2)7B, a step of laminating these ceramic green sheets together to form a laminated green sheet having a reinforcing structure that divides the opening of the thermal via into two or more and has a height less than the height of the thermal via, and (3)7C, a step of firing this laminated green sheet.
• Step 1 is a step of preparing the green sheets of (a) and (b) above. First, green sheets 702 and 704 without through holes (Figure 7A) are prepared as the
• the green sheets may consist of a mixture of 50 to 65 wt% CaO-SiO 2 -AI 2 Os- B 2 O3 glass and 50 to 35 wt% alumina.
• a mixture of MgO-Si ⁇ 2 -AI 2 ⁇ 3-B 2 ⁇ 3 glass and alumina, a mixture of SiO 2 -B 2 Os glass and alumina, a mixture of PbO-SiO 2 -B 2 Os glass and alumina, or cordierite crystallized glass or another low-temperature fired ceramic material that is fired at 800 to 1000 0 C can be used.
• through holes 706, 708 and 710 as the via holes are provided at specific positions on green sheet 702 corresponding to (a) and green sheet 704 corresponding to (b) (see Figure 7B).
• Through holes 708 are formed in the green sheet corresponding to (b) leaving part 712 for the reinforcing structure.
• Through hole 706 forms the part of the opening without reinforcing structure 106 in thermal via 104
• through holes 708 form the part of the opening with reinforcing structure 106 in thermal via 104.
• Through hole 710 is a circuit via hole. All through holes can be formed by punching process.
• One means of forming the through holes for the via holes is a method of forming through holes of a specific size by punching the green sheet as described above, but as explained in the first embodiment, other methods are to form the through holes by sandblasting or laser or electron beam processing.
• multiple green sheets (a) and (b) can be prepared and laminated in order to obtain a green sheet of the desired thickness.
• Step 2 is a step of laminating the green sheets of (a) and (b) to form a green sheet having a reinforcing structure ( Figure 7C).
• the resulting green sheets are laminated and pressed for bonding ( Figure 7C).
• these green sheets are laminated to form a laminate having the desired reinforcing structure.
• the green sheets obtained by Step 1 are heated and pressed for bonding under conditions of for example 60 to 150 0 C, 0.1 to
• Step 3 is a step of firing the green sheet laminate obtained in Step
• Step 2 The laminate obtained in Step 2 is fired.
• the green sheet laminate can be fired for example under conditions of 800 to 1000 0 C
• a ceramic substrate used for an electronic component has a small-diameter circuit via hole e for conduction purposes in addition to the thermal via.
• large-diameter via hole 104 is a through hole having reinforcing structure 106 and constituting a thermal via for radiating heat from a mounted component, while small-diameter via hole 610 is a circuit via hole.
• the via hole can be filled with a filler. More efficient heat diffusion as well as conduction for circuit can be achieved by means of this filler.
• the via hole can be filled with a filler composition after Step 2 in the 1 st embodiment and between Step 2 and Step 3 in the 2 nd embodiment. Specifically this is done as follows.
• Figure 8A through Figure 8H show the filling procedure of the 1 st embodiment
• Figure 8A' through Figure 8H' show the filling procedure of the 2 nd embodiment.
• through holes 104, 610 and 708 in a laminate of green sheets 702 and 703 are filled with a filler composition.
• the filler composition may be that explained above. Normally, filling is achieved by a printing process.
• through hole 104 contains reinforcing structure 106, while in the 2 nd embodiment through hole 708 contains part 712, which will be the reinforcing structure.
• the through holes 104, 610 and 708 in ceramic substrate 102 or green sheets 702 and 704 can be filled at the same time that the wiring pattern is printed.
• the aforementioned filler composition can also be used for the wiring pattern.
• screen mask 804 having formed thereon a printing pattern for filling through holes 104, 610 and 708 and for printing the part that will be wiring pattern 802 is set on ceramic substrate body 102 or green sheet 702, filler composition 806 is supplied above this screen mask, and squeegee 808 is slid along the top surface of this screen mask to simultaneously fill the through holes and print the wiring pattern ( Figure 8A and Figure 8A' through Figure 8B and Figure 8B'). It is also desirable to simultaneously form a conductor pattern other than the wiring pattern, corresponding to component mounting land 812 or the like, by printing on the upper surface of the opening of the part corresponding to thermal via 104.
• the parts corresponding to surface layer wiring pattern 802, component mounting land 812 and the like can also be printed after the green sheet is fired.
• the part that will be reverse wiring pattern 810 is printed on the lower surface of the via hole opening on ceramic substrate body 102 and green sheet 704 ( Figure 8E and Figure 8F' through Figure 8G and Figure 8H').
• Screen mask 814 having formed thereon the printing pattern for printing the part corresponding to reverse wiring pattern 810 is set on the bottom of ceramic substrate body 102 or green sheet 704, filler composition 806 is supplied above the screen mask and squeegee 808 is slid along the upper surface of the screen mask.
• the filler composition of the present invention can be applied to the parts corresponding to surface layer wiring pattern 802, reverse wiring pattern 810 and mounting land 812, and filled into through holes 104, 610 and 708 ( Figure 8G and Figure 8H').
• the filler composition or the filler composition and green sheet are fired ( Figure 8I and Figure 8J').
• the conditions for drying and firing the filler composition in the present invention can be determined suitable for the substrate and the application by using official notice as necessary.
• the composition can be first filled and printed by a printing process, dried for 5 to 60 minutes at a temperature in the range of 70 0 C to 200 0 C, and then fired in a belt oven, box oven or the like with a total firing time of 20 to 120 minutes and maintained for 5 to 30 minutes at a top temperature in the range of 450°C to 900 0 C.
• FIG. 9 is a vertical cross-section showing a model view of one example using a ceramic substrate of one embodiment of the present invention.
• the present invention is not limited to the embodiment shown in Figure 9, however, and can be applied to various types of electronic components having via holes.
• this electronic component has substrate 102 with specific dimensions and via holes 104 and 610 at specific positions thereon. Resistors and various other circuit components (not shown) and wiring patterns 802, 810 and the like are formed on one or both surfaces of the substrate, and mounted component 902 (an LED chip or the like for example) is mounted on mounting land 812. Via hole 104 and via-hole 610 are filled with filler 904, which is formed of the filler composition described above.
• the large-diameter via hole 104 is a thermal via for radiating the heat from mounted component 902, while the small-diameter via hole 610 is a circuit via hole.
• an electronic component such as that shown in Figure 9 can be manufactured by using conventional methods to form various circuit components to obtain an electronic circuit substrate on which mounted components can then be mounted as necessary.
• an electronic circuit substrate is a ceramic substrate having various circuits formed and the filler filled by the aforementioned procedures, but without any mounted components.
• the electronic component and electronic circuit substrate of the present invention may comprise a single-layer substrate such as that described above, or may have multiple substrates of specific dimensions laminated together with various circuit components and via-holes at specific positions on each substrate.
• the conduction via holes do not have to be at the same position on each substrate, but may be formed at different positions.
• the thermal via is preferably formed at the same position on each substrate in order to efficiently transmit heat to the back of the substrate.
• the ceramic substrate of the present invention it is possible to prevent dropout of the filler that fills the large-diameter thermal via in the electronic component, and to thereby maintain good electrical and thermal conductivity of the via hole.
• An electronic component manufactured using the ceramic substrate of the present invention can be used for various applications. For example, it can be used for the high-frequency circuit of a mobile phone, the heat-sink circuit of an LED or the like.
• the substrate material, filler materials, substrate, printing on the substrate, drying and firing and evaluation conditions are as follows. (1 ) Substrate
• a 2-inch square, 0.635 mm thick AIN substrate (Asahi Technoglass substrate 230 VWm K) was used.
• the aforementioned filler composition was filled into the via hole on the substrate, dried and fired under the following conditions.
• Printing Using a 150 ⁇ m-thick stainless steel metal mask, Newlong automatic printer, flat urethane squeegee (hardness 70) Drying: 20 minutes at 10O 0 C in a box-type air oven Firing: 10 minutes, peak temperature 550 0 C, belt oven (5) Substrate evaluation method The resulting substrate with filled via holes was surface polished.
• the polishing process consisted of 4 steps: surface grinding to remove a thin layer of the substrate surface, lapping, polishing and ultrasound cleaning.
• Lapping is a polishing process using rough free polishing powder.
• Polishing is a polishing process using fine free polishing powder.
• Ultrasound cleaning is performed to remove residual fine particles from the surface. Following ultrasound cleaning, the number of places where filler was retained after surface polishing was counted.
• the thermal via with reinforcing structure of the present invention had a much higher filler retention rate than the thermal vias outside the scope of the present invention.

Landscapes

• Engineering & Computer Science (AREA)
• Computer Hardware Design (AREA)
• Materials Engineering (AREA)
• Physics & Mathematics (AREA)
• Condensed Matter Physics & Semiconductors (AREA)
• General Physics & Mathematics (AREA)
• Chemical & Material Sciences (AREA)
• Microelectronics & Electronic Packaging (AREA)
• Power Engineering (AREA)
• Structure Of Printed Boards (AREA)
• Compositions Of Oxide Ceramics (AREA)
• Production Of Multi-Layered Print Wiring Board (AREA)
• Printing Elements For Providing Electric Connections Between Printed Circuits (AREA)

Priority Applications (2)

Applications Claiming Priority (2)

Publications (2)

Family

ID=40637680

Family Applications (1)

Country Status (5)

Families Citing this family (10)

Family Cites Families (23)

• 2007
  • 2007-12-11 US US12/001,267 patent/US20090146295A1/en not_active Abandoned
• 2008
  • 2008-12-11 CN CN2008801186744A patent/CN101874299B/zh not_active Expired - Fee Related
  • 2008-12-11 JP JP2010538144A patent/JP2011507276A/ja active Pending
  • 2008-12-11 WO PCT/US2008/086338 patent/WO2009076494A2/en not_active Ceased
  • 2008-12-12 TW TW097148703A patent/TW201023307A/zh unknown