WO2007063963A1 - 半導体装置 - Google Patents

半導体装置 Download PDF

Info

Publication number
WO2007063963A1
WO2007063963A1 PCT/JP2006/323997 JP2006323997W WO2007063963A1 WO 2007063963 A1 WO2007063963 A1 WO 2007063963A1 JP 2006323997 W JP2006323997 W JP 2006323997W WO 2007063963 A1 WO2007063963 A1 WO 2007063963A1
Authority
WO
WIPO (PCT)
Prior art keywords
channel
transistor
region
semiconductor device
semiconductor layer
Prior art date
Application number
PCT/JP2006/323997
Other languages
English (en)
French (fr)
Inventor
Tadahiro Ohmi
Akinobu Teramoto
Original Assignee
Tohoku University
Foundation For Advancement Of International Science
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tohoku University, Foundation For Advancement Of International Science filed Critical Tohoku University
Priority to EP06833800A priority Critical patent/EP1959492A4/en
Priority to US12/085,776 priority patent/US7800202B2/en
Priority to CN2006800453895A priority patent/CN101322240B/zh
Priority to JP2007548008A priority patent/JP5170531B2/ja
Publication of WO2007063963A1 publication Critical patent/WO2007063963A1/ja
Priority to KR1020087015273A priority patent/KR101269926B1/ko

Abstract

ＣＭＯＳ回路を構成するｐ型ＭＯＳトランジスタとｎ型ＭＯＳトランジスタの動作速度を実質的に同じにするために、ｎ型ＭＯＳトランジスタを（１００）面及び（１１０）面の双方にチャンネル領域を備えた三次元構造をとり、ｐ型ＭＯＳトランジスタを（１１０）面にのみチャンネル領域を備えたプレーナ構造とする。更に、両トランジスタのチャンネル領域及びゲート絶縁膜の面積が互いに等しくなるように構成する。これによって、ゲート絶縁膜等の面積を相互に等しくすると共に、ゲート容量をも等しくすることができる。

Description

半導体装置
技術分野
[0001] 本発明は、 IC, LSI等の半導体装置に関するものである。
背景技術
[0002] 図 10に従来の半導体装置の構成として、半導体装置に使用される電子回路の 1つ である CMOSインバータ回路を示す。図 10 (a)には、 CMOSインバータ回路の断面 を模式的に示し、図 10 (b)にはその平面図を示す。簡単のため、図 10(b)において は配線 8〜： L 1の表示を省略して!/、る。
[0003] 図 10 (a)において、 1は電子回路が形成される p型半導体基板、 2は p型半導体基 板 1に形成された n型不純物領域、 3a、 3bは n型不純物領域 2に形成された高濃度 p 型不純物領域、 4a、 4bは p型半導体基板 1に形成された高濃度 n型不純物領域、 5 はゲート電極 6と p型半導体基板 1、及びゲート電極 7と n型不純物領域 2とをそれぞ れ絶縁するための SiO等のゲート絶縁膜、 6、 7はゲート絶縁膜 5上に形成されたゲ
2
ート電極である。
[0004] ここで、 n型不純物領域 2、高濃度 p型不純物領域 3a、 3b、ゲート電極 7は、 pチャン ネル MOSFET (Metal Oxide Semiconductor Field Effect Transistor)を構成する。一 方、半導体基板 1、高濃度 n型不純物領域 4a、 4b、ゲート電極 6は、 nチャンネル M OSFETを構成する。 8は nチャンネル MOSFET及び pチャンネル MOSFETのゲー ト電極 6, 7に接続され、 CMOSインバータ回路の入力信号としての共通の電圧を加 えるためのゲート配線である。 9は pチャンネル MOSFETのドレイン電極（高濃度 p型 不純物領域 3a)及び nチャンネル MOSFETのドレイン電極（高濃度 n型不純物領域 4b)に接続され、 CMOSインバータの出力信号を取り出す出力配線である。 10、 11 は、それぞれ nチャンネル MOSFETのソース電極（高濃度 n型不純物領域 4a)、 チ ヤンネル MOSFETのソース電極 (高濃度 p型不純物領域 3b)に電源電位を供給す るための電源配線である。
[0005] この CMOSインバータ回路の動作について説明する。図 10 (a)の pチャンネル MO SFETと nチャンネル MOSFETとから構成される CMOSインバータ回路は、 nチャン ネル'トランジスタのソース電極に接続された電源配線 10を接地（0V)し、 pチャンネ ル 'トランジスタのソース電極に接続された電源配線 11に電源電圧（例えば 5V)を与 える。そして、入力信号としてゲート配線 8に 0Vを与えると、 nチャンネル 'トランジスタ が OFFになり、 pチャンネノレ'トランジスタが ONになる。したがって、出力酉 S線 9には、 電源配線 11と同じ電源電圧（5V)が出力される。一方、ゲート配線 8に 5Vを与えると 、上記の場合とは逆に、 nチャンネル 'トランジスタが ONになり、 pチャンネル 'トランジ スタが OFFになり、出力配線には、電源配線 10と同じ接地電圧 (0V)が出力される。
[0006] これらの CMOS型回路において、トランジスタを流れる電流は、出力が変化しない 場合には、ほとんど流れず、主に出力が変化する場合に流れる。すなわち、ゲート配 線 8が 0Vになったとき、 pチャンネル 'トランジスタを通して出力配線 9を充電するため の出力電流が流れ、他方、ゲート配線 8が 5Vになったとき、 nチャンネル 'トランジスタ を通して出力配線 9の電荷を放電するための出力電流が流れる。このように、図 10 (a )の CMOS回路は、入力と逆極性の信号を出力するインバータ回路となっている。こ れらのインバータ回路はスイッチングの際の立ち上がり速度と立ち下り速度を同一に するために、 pチャンネル 'トランジスタと nチャンネル 'トランジスタに同じ電流を流さな ければならない。
[0007] し力し、例えば（100)面での pチャンネル 'トランジスタのキャリアである正孔は、 nチ ヤンネル'トランジスタのキャリアである電子より移動度が小さぐその比は 1 : 3である。 そのため pチャンネル ·トランジスタと nチャンネル ·トランジスタの面積を同一にした場 合には、それらの電流駆動能力に差が生じ、動作速度は同一とはならない。このため 図 10 (b)に示すように、 pチャンネル 'トランジスタのドレイン電極 3a、ソース電極 3b、 ゲート電極 7の面積を、 nチャンネル 'トランジスタのドレイン電極 4b、ソース電極 4a、 ゲート電極 6の面積よりもその移動度の比に対応して大きくし、電流駆動能力をほぼ 同じにすることにより、スイッチング速度を同等にしていた。しかし、このため pチャンネ ル 'トランジスタの占める面積は nチャンネル 'トランジスタの 3倍の大きさとなり、 pチヤ ンネル'トランジスタと nチャンネル 'トランジスタの占める面積とがアンバランスとなり、 半導体装置の集積度の向上の障害となっていた。 [0008] pチャンネル 'トランジスタの電流駆動能力を向上させる先行文献として下記特許文 献 1がある。特許文献 1では、（110)面を使うことで pチャンネル 'トランジスタの電流 駆動能力を向上させている。また、特許文献 2では、 SOI基板を用い、 Accumulation 型の pチャンネル 'トランジスタを SOI基板上に形成し、 pチャンネル 'トランジスタの電 流駆動能力を向上させることが述べられているが、任意の基板を用いた場合は、 ON 状態で同じ大きさの nチャンネル 'トランジスタと pチャンネル 'トランジスタの電流駆動 能力を実際に、同等にするのは不可能である。また、特許文献 2に開示された acc醒 ulation型のトランジスタは、ゲート電極の他に基板電極を必須とし、かつ両電極にチ ヤンネル領域に空乏層を形成してチャンネルをピンチオフさせるような電圧を加えな ければならず、構造上および回路上の煩雑さが伴うという欠点があった。
[0009] 特許文献 1：特開 2003— 115587号公報
特許文献 2 :特開平 07— 086422号公報
発明の開示
発明が解決しょうとする課題
[0010] 上記したように（100)面の結晶面を使用する CMOS回路においては、同一面積の nチャンネル ·トランジスタと pチャンネル ·トランジスタの電流駆動能力が異なり、スイツ チング速度が異なる。このスイッチング速度（立ち上がり、立ち下り）を同じくするため には、 pチャンネル 'トランジスタのチャンネル幅を大きくする必要がある。そのため、 n チャンネル 'トランジスタと pチャンネル 'トランジスタの占める面積がアンバランスとなり 、半導体装置の集積度の向上の障害となっていた。
[0011] 先出願の特許文献 1においては、 pチャンネル 'トランジスタ電流駆動能力を向上さ せているが、 nチャンネル 'トランジスタと pチャンネル 'トランジスタの大きさを同じくす ることには不十分であった。
[0012] 本発明は、 CMOS回路を構成する導電型の異なる一対のトランジスタのスィッチン グ速度を実質的に同じまたは同等としかつ電極の面積を実質的に同じまたは同等と することによって、集積度を高くできる半導体装置を得ることを目的としている。
[0013] 本発明の他の目的は、構造上および回路上の煩雑さのない accumulation型トラン ジスタを提供することにある。 課題を解決するための手段
[0014] 請求項 1、 2に係る半導体装置は、 SOI(Silicon on Insulator)基板上にチャンネル導 電型の異なるトランジスタを少なくとも一対有する回路を備えた半導体装置において 、 SOI基板上に設けた第 1の半導体層とその表面の少なくとも一部を覆う第 1のゲート 絶縁層とを用いて nチャンネル 'トランジスタを形成するとともに前記 SOI基板上に設 けた第 2の半導体層とその表面の少なくとも一部を覆う第 2のゲート絶縁層を用いて p チャンネル 'トランジスタを形成し、前記第 1の半導体層のチャネルを形成する第 1の 領域の表面が（110)面または（110)面から ± 10° 以内の面を有するようにするとと もに前記第 1の半導体層の側面においてチャネルを形成する第 2の領域の表面を（1 10)面から ± 10° 以内の面とは異なりかつ（110)面から ± 10° 以内の面よりも電子 の移動度が大き 、一つまたは複数の面を有するようにし、前記第 2の半導体層のチ ャネルを形成する第 3の領域の表面が（110)面または（110)面から ± 10° 以内の 面を有するようにし、前記第 1の領域の表面の面積と前記第 2の領域の表面の面積と の和が前記第 3の領域の表面の面積と実質的に等しいか同等となりかつ前記 nチヤ ンネル'トランジスタと前記 pチャンネル 'トランジスタの動作速度が実質的に等 U、か 同等となるように、前記第 1の領域の表面の幅および長さ、前記第 2の領域の表面の 高さおよび長さ、ならびに前記第 3の領域の表面の幅および長さを定めたことを特徴 とする。ここで、ゲート長 Lは、同一にしておいて、幅および高さを変化させて、面積を 調整するのが好まし 、。前記 nチャンネル 'トランジスタと前記 pチャンネル 'トランジス タはともに normally offであり、かつ前記 nチャンネル 'トランジスタを inversion型ま たは accumulation型とし、前記 pチャンネル 'トランジスタを inversion型または accu mulation型とする。
[0015] 請求項 3に係る半導体装置は、前記 nチャンネル 'トランジスタと前記 pチャンネル ·ト ランジスタとをともに inversion型としたものである。
[0016] 請求項 4に係る半導体装置は、前記 nチャンネル 'トランジスタと前記 pチャンネル ·ト ランジスタとをともに accumulation型としたものである。
[0017] 請求項 5に係る半導体装置は、前記 nチャンネル ·トランジスタを inversion型とし、前 記 pチャンネル 'トランジスタを accumulation型としたものである。 [0018] 請求項 6に係る半導体装置は、前記 nチャンネル 'トランジスタを accumulation型 とし、前記 pチャンネル 'トランジスタを inversion型としたものである。
[0019] 請求項 7に係る半導体装置は、前記第 2のゲート絶縁膜上に設けられる第 2のゲー ト電極と前記第 2の半導体層との仕事関数差により前記第 2の半導体層に形成される 空乏層の厚さが前記第 2の半導体層の膜厚よりも大きくなるように前記第 2のゲート電 極の材料および前記第 2の半導体層の不純物濃度を選んだものである。
[0020] 請求項 8に係る半導体装置は、前記第 1のゲート絶縁膜上に設けられる第 1のゲー ト電極と前記第 1の半導体層との仕事関数差により前記第 1の半導体層に形成される 空乏層の厚さが前記第 1の半導体層の膜厚よりも大きくなるように前記第 1のゲート電 極の材料および前記第 1の半導体層の不純物濃度を選んだものである。
[0021] 請求項 9に係る半導体装置は、前記ゲート絶縁膜が、マイクロ波励起のプラズマで 形成された SiO , Si Nおよび金属シリコン合金の酸化膜、金属シリコン合金の窒化
2 3 4
膜を少なくとも一種類、含有するものである。
[0022] 請求項 10に係る半導体装置は、前記ゲート絶縁膜がマイクロ波励起のプラズマを 用いて 600°C以下の温度で形成されものである。
[0023] 請求項 11に係る半導体装置は、チャンネル長を構成する前記第 1の領域の表面の 長さ、前記第 2の領域の表面の長さ、および前記第 3の領域の表面の長さをすベて 互いに実質的に等しいように定めたものであり、これによりチャンネル領域の幅のみ を定めればよくなり、かつ製造上も簡便にかつ生産性も向上する。
[0024] 請求項 12に係る半導体装置は、異なる導電型のトランジスタを少なくとも一対有す る回路を備えた半導体装置において、 SOI基板上に設けた第 1の半導体層とその表 面の少なくとも一部を覆う第 1のゲート絶縁層とを用 ヽてー導電型のトランジスタを形 成するとともに前記 SOI基板上に設けた第 2の半導体層とその表面の少なくとも一部 を覆う第 2のゲート絶縁層を用いて他の導電型のトランジスタを形成し、前記第 1の半 導体層のチャネルを形成する第 1の領域の表面を第 1の結晶面を有するようにすると ともに前記第 1の領域の表面と交差する面に設けられた前記第 1の半導体層の側面 においてチャネルを形成する第 2の領域の表面を前記第 1の結晶面とは異なりかつ キャリアの移動度も異なる第 2の結晶面を有するようにし、前記第 2の半導体層のチヤ ネルを形成する第 3の領域の表面を前記第 1の結晶面を有するようにし、前記第 1の 領域の表面における相互コンダクタンス gmを gml、前記第 2の領域の表面における 相互コンダクタンス gmを gmlより大きい gm2 (即ち、 gm2>gml)とし、前記第 3の領 域の表面における相互コンダクタンス gmを gmlより大きいが gm2よりは小さい gm3 ( 即ち、 gm2>gm3 >gml)とし、前記第 1の領域の表面の長さを Ll、幅を W1とし、 前記第 2の領域の表面の長さを Ll、幅を W2とし、前記第 3の領域の表面の長さを L 2、幅を W3とし、 Wl, W2, W3, LI, L2のうちどれ力 3つを所定の値としたときに、 Wl X L1 +W2 X L1 =W3 X L2を実質的に満足し、かつ
(gml XWl/Ll) + (gm2 XW2/Ll) =gm3 XW3/L2
を実質的に満足するように Wl, W2, W3, LI, L2のうち残余の 2つを定めることによ つて、
前記一導電型のトランジスタと前記他の導電型のトランジスタとを、チャンネル領域の 面積を互いに実質的に等しいか同等としつつ動作速度を互いに実質的に等しいか 同等となるようにしたものである。ここで、前記の第 2の領域は、第 1の半導体層の側 面を傾斜面または垂直面とした部分に形成され、かつ両側面の一方のみを用いても 、両方の上から一部または底部までを用いて形成されても良 、。
[0025] 請求項 13に係る半導体装置は、前記 L1と前記 L2とを等しくすることによって、 W1, W2, W3のうちどれか 1つを所定の値として、
W1 +W2=W3 X L2を実質的に満足し、かつ
gml XWl +gm2 XW2= gm3 X W3
を実質的に満足するように Wl, W2, W3のうち残余の 2つを定めるようにしたもので ある。
[0026] 請求項 14に係る半導体装置は、前記第 2の領域を前記第 1の領域表面と実質的に 垂直な面であつて前記第 1の領域表面の両側に延びる前記第 1の半導体層の両側 面の部分を用い、その領域の高さを Hとして、前記 W2を 2Hとおくようにしたものであ る。
[0027] 請求項 15にかかる半導体装置は、前記一導電型のトランジスタをと前記他の導電 型のトランジスタとを前記第 1の結晶面を（110)面または（110)面から ± 10° 以内 の面としたものである。
[0028] 請求項 16に係る半導体装置は、前記一導電型のトランジスタおよび前記他の導電 型のトランジスタを、それぞれ nチャンネル 'トランジスタ、及び、 pチャンネル 'トランジ スタとしたものである。
発明の効果
[0029] 本発明によれば、上記の構成により、同一の電流駆動能力を有する pチャンネル M OSトランジスタと nチャンネル MOSトランジスタが得られる。即ち、電子回路の ρチヤ ンネル MOSトランジスタをプレーナ構造とする一方、 nチャンネル MOSトランジスタ を三次元構造にすることにより、両トランジスタのチャンネル面積を同じくすることがで きること力ら、スイッチング速度が同等で、集積度を高くできる半導体装置を得られる 効果がある。
図面の簡単な説明
[0030] [図 1]本発明の第 1の実施例の半導体装置を示す図であり、（a)は斜視図、（b)及び（ c)は、図 1(a)の A—A'線及び B— B'線に沿う断面図である。
[図 2] (a)、（b)、及び、（c)は本発明の他の三つの実施例に係る半導体装置の断面 図である。
[図 3]本発明の第 1の実施例の効果を示す図である。
[図 4] (a)、 (b)、 (c)、及び（d)は本発明にお ヽて使用される accumulation型トランジ スタの動作原理を示す図である。
[図 5] (a)及び (b)は本発明による accumulation型トランジスタの構造を示す断面図お よびバンド構造を示す図である。
[図 6]本発明による accumulation型トランジスタの lZf雑音を示す図である。
[図 7] (a)及び（b)は本発明による accumulation型トランジスタにおいて、ゲート電極の 仕事関数と SOI層の厚さとの関係を示す図である。
[図 8]本発明の実施例による accumulation型トランジスタの空乏層厚さと基板不純物 濃度の関係図である。
[図 9]本発明による accumulation型トランジスタのドレイン電圧 ドレイン電流特性を示 す図である。 [図 10] (a)及び (b)は、それぞれ従来例の半導体装置の断面図及び平面図である。
[図 11] (a)、 (b)、及び (c)は、熱酸化によってゲート絶縁膜を形成した場合と、ラジカ ル酸ィ匕によってゲート絶縁膜を形成した場合とにおけるチャンネル方位と Sファクター の関係を比較して説明するための図である。
符号の説明
[0031] 1 p型半導体基板
2 n型不純物領域
3a, 3b 高濃度 p型不純物領域
4a, 4b 高濃度 p型不純物領域
5 ゲート絶縁膜
6, 7 ゲート電極
8 ゲート配線
9 出力配線
10, 11 電源配線
12 支持基板
13 埋め込み酸化膜
14 SOI(Silicon on Insulator)層
15 ゲート絶縁膜
16 ゲート電極
17 ソース'ドレイン層（NMOSトランジスタ）
18 ソース'ドレイン層 (PMOSトランジスタ）
19 ゲート配線
20 出力配線
21 , 22 電源配線
発明を実施するための最良の形態
[0032] 以下、本発明の半導体装置について、図面を参照して説明する。
[0033] (実施例 1)
実施例 1について図 1を用いて説明する。図 1 (a)に本発明の第 1の実施例による 半導体装置の概略斜視図、図 1 (b)に図 1 (a)における A—A'線の断面図、図 1 (c) に図 1 (a)における B— B'線の断面図をそれぞれ示す。図 1の実施例は、同一ディメ ンジョンで電流駆動能力がバランスするように設計した SOI型三次元構造 CMOSデ バイスであり、 pチャンネル MOSトランジスタはホール移動度が大きくなる（110)面に のみ作製し、 nチャンネル MOSトランジスタは電子移動度がやや劣る（110)面にカロ えて電子移動度の大きい側壁の（100)面をもゲートを構成するように作製したもので ある。すなわち、 nチャンネル 'トランジスタは三次元構造、 pチャンネル 'トランジスタ はプレーナ構造にしたものである。
[0034] 図 1 (b) （c)に示すように、支持基板 12上に 200nm厚さの埋め込み酸ィ匕膜 13で 分離された所定の厚さの（110)面方位のシリコンすなわち n型 (基板リン (P)濃度 101 7cm_3)の SOI(Silicon on Insulator)層 14 n 14 pを有する基板を準備する。ここ で、 SOI層 14- n及び 14— pの表面は、チャンネルの長さ方向が〈110〉方向になるよ うにするのが好ましい。これは、（110)面でのホールの移動による飽和電流量が〈11 0〉方向で最大になる力もである。他方、（100)面での電子の移動による飽和電流量 は結晶方向依存性が小さいことを考慮しておく必要がある。
[0035] 図示された例では、 SOI層のうち、 nチャンネル 'トランジスタを形成する領域 14— n および pチャンネル 'トランジスタを形成する領域 14— p以外はエッチングにより除去 されており、この結果、各領域 14 n 14 pが酸化膜 13上に分離'形成されている SOI層は i層として両方の領域に共通にしても良いし、 p型として、後に pチャンネル 'トランジスタを形成する領域 14— pを n型に変換してもよい。このとき、閾値調整用の 不純物注入を行い、基板濃度調整を行っても良い。例えば、 100 世代のときは、 4 X 1018cm_3とする。分離された各領域の側面は、（100)面になっている。これらの 側面のうち、 nチャンネル 'トランジスタ領域 14— nのチャンネル領域の側面を除く側 面には、図 1 (b)に示すように、公知の方法で厚い酸化膜 25が形成されている。
[0036] 例えば、厚い酸ィ匕膜 25は以下の手法によって形成できる。まず、 CVD法により、 Si Oを 45nm以上、堆積した後、ダメージが小さい異方性のエッチングを用いて、側壁
2
に酸ィ匕膜を残しながらエッチングした後、トランジスタ領域 14— n領域以外にマスクを して、ウエットエッチングにより、 nチャンネル 'トランジスタ領域 14— nのチャンネル領 域の側面側壁の厚い酸化膜を除去し、トランジスタ領域 14 pの側壁に厚い酸化膜 25に残す。
[0037] 図 1 (b)では、酸化膜 25の形成後、洗浄を行い、続いて、ゲート酸化をマイクロ波励 起のプラズマ装置で行い、 7nmの SiO膜 15を nチャンネル 'トランジス領域 14— nの
2
チャンネル領域上面および側面、 pチャンネル 'トランジスタ領域 14 pのチャンネル 領域上面にそれぞれ形成する。このとき、所望の電気的容量を得るための膜厚を形 成しても良い。また、ゲート絶縁膜 15は、 Si N、 HfO、 ZrO、 La O等の金属酸化
3 4 x x 2 3
物、 Pr Si N等の金属窒化物等の高誘電率材料を用いても良い。
[0038] その後、リンまたは硼素、または、リン、砒素の合計濃度を 102Gcm_3以上含有する 多結晶シリコンを形成し、所望のゲート長、ゲート幅にエッチングし、ゲート電極 16を 形成する。 その後、 NMOSトランジスタ領域のソース'ドレイン層 17にはヒ素を 4 X 1 015cm_2、 PMOSトランジスタ領域のソース'ドレイン層 18には硼素を 4 X 1015cm_2 、イオン注入し、活性化を行う。
[0039] さらに、 SiO膜を CVDで形成し、図 1 (c)に示すように、配線層としてゲート配線 19
2
、出力配線 20、電源配線 21及び電源配線 22を形成することで、同一基板上に inver sion型 (即ち、 inversion-mode) PMOSトランシスタ ΙΟΟρと inversion型 (即ち、 inversio n- mode) NMOSトランジスタ 100ηが形成できる。ここで、 nチャンネル 'トランジス領 域 14 nのチャンネル領域上面および側面の合計面積と pチャンネル 'トランジスタ 領域 14— pのチャンネル領域上面の面積とを等しくし、かつ両トランジスタの動作速 度が等しくなるようにする。
[0040] ここで、両トランジスタ 100ρ、 100ηのチャンネル領域の長さ Lを等しくし、 nチャンネ ル 'トランジス領域 14 nのチャンネル領域上面の幅を Wn、側面の高さを Hとし、 pチ ヤンネル'トランジスタ領域 14— pのチャンネル領域上面の幅を Wpとする。そして式（ 1)が成立するようにする。
[0041] 両トランジスタの動作速度が等しくなるには式 (2)が成立することが必要である。ここ で、 NMOSトランジスタの（100)及び（110)面における相互コンダクタンスをそれぞ れ gmn (100)及び gmn (110)とし、 PMOトランジスタの（110)面における相互コン ダクタンスを gmp (l lO)とすると、これら相互コンダクタンス gmn (100)、 gmn(l lO) 、及び、 gmp (l lO)はいずれも既知である。また、たとえば、 Wnを適当な値に定めれ ば、必要な Hおよび Wpが式（1)および式（2)の連立方程式の解として得られる。尚、 SOI層は（551)面のような（110)面から ± 10° 以内で傾けたような面方位であれば 、 NMOSトランジスタと PMOSトランジスタがほぼ同一の電流駆動能力を持つ。
[0042] このような条件の下に、例えば、 Wnを 22nmとし、 gmn (l lO)は約 0. 7gmn (100) 、gmp (110)は 0. 8gmn(100)とすれば、、 Hは 5. 5nm、 Wpは 33nmとなる。なお、 図示の実施例ではチャンネル長を両トランジスタとも 25nmとした。
[0043] [数 1]
Wp =2H+Wn ( 1 )
gmp(H0)xWp = gmn (100) x2H+gmp(l 10)xwn ( 2 )
面積及びゲート面積をほぼ同一にし、両トランジスタの電流駆動能力、ひいては動作 速度をほぼ同一とすることが出来、フルバランスト CMOSを得ることができる。この構 造によって、図 10の従来例と比べて、所要面積で半分以下にすることができ、動作 速度を 1桁程度高速ィ匕することが可能となる。さらに、 pn両トランジスタのゲート面積 を同一とすることで、両トランジスタのゲート容量が同一となり、図 3に示すように、これ らのトランジスタで構成したアナログスィッチのオフセット雑音を 15dBも低減すること ができる。ここで、図 1 (c)に示した実施例は、前述した通り、 PMOSトランジスタ及び NMOSトランジスタの双方を inversion型のトランジスタによって構成したものである。
[0045] 図 2 (a)、（b)、及び、（c)は、図 1 (c)以外の三つの実施例を示しており、図 1 (c)に 相当する方向の断面図である。図 2 (a)は nチャンネル 'トランジスタ（即ち、 NMOSト ランジスタ） 101ηおよび pチャンネル 'トランジスタ（即ち、 PMOSトランジスタ） 101p がともに accumulation型の例であり、図 2 (b)は nチャンネル 'トランジスタ（即ち、 NM OSトランジスタ） 102ηが accumulation型で pチャンネル 'トランジスタ（PMOSトランジ スタ） 102pカ¾lversion型の例である。図 2 (b)の構成は、同一導電型の well (nゥエル )と同一導電型 (p+型）のゲート電極によって形成されるのでプロセスが簡単ィ匕する 利点があり、また、 accumulationモードの nチャンネル 'トランジスタを用いることで CM OS全体の lZfノイズを低減できる。また、図 2 (c)は nチャンネル 'トランジスタ（NMO Sトランジスタ） 103n力 nversion型で pチャンネル 'トランジスタ（PMOSトランジスタ） 1 03pが accumulation型の例である。この例のものは、同一導電型の well (pゥエル）と 同一導電型 (n+型）のゲート電極によって形成されるのでプロセスが簡単ィ匕する利 点があり、また、 n+型のポリシリコンゲート電極だけを用いるので、薄膜ィ匕によるポロ ンの拡散 (ボロンはゲート酸ィ匕膜へ拡散しやすくそのためにキャリアの界面移動度が 劣化するという現象が生じる）を防止できる。後に述べるように、 accumulation型のトラ ンジスタを用いることにより、 inversion型に比べ電流駆動能力が大きくなる（図 9)と云 う利点もある。
[0046] ここで、図 4乃至図 9を参照して、図 2 (a)、（b)の nチャンネル 'トランジスタ（NMOS トランジスタ） 102η, 103ηを例にとって、本発明による accumulation型トランジスタに ついて説明する。
[0047] 図 4 (a)〜（d)には、 accumulation型 nチャンネル 'トランジスタ（NMOSトランジスタ） の動作原理が示されている。まず、図 4 (a)に示すように、ゲート電圧 Vgがゼロの場 合、空乏層（depletion-layer)が SOI層の全体に拡がっている。図 4 (b)に示すように、 ゲート電圧 Vgが印加されると、空乏層がチャンネル上面まで後退してバルタ電流 Ibul kが流れ出す。続いて、ゲート電圧が増加すると、図 4 (c)及び (d)に示すように、蓄積 電流 Iaccも流れ出す。
[0048] この現象を図 5 (a)及び (b)を用いて説明すると、 SOI構造をとり、ゲート電極と SOI 層との仕事関数差で発生する空乏層幅を SOI層の厚さよりも大きくなるようにすれば 、図 5 (a)に示すような accumulation構造でノーマリオフ型の MOSトランジスタが可能 となる。ここで、図示のような nチャンネル 'トランジスタでは p +ポリシリコン (仕事関数 5. 2eV)をゲート電極に用い、 pチャンネル 'トランジスタでは n+ポリシリコン (仕事関 数 4. leV)をゲート電極に用いることで SOI層との仕事関数差を生じさせることが出 来る。
[0049] 図 9に示すように、シリコンの（110)面上に accumulation構造の nチャンネル 'トラン ジスタを形成することにより、シリコン（100)面上に構成した通常の nチャンネル 'トラ ンジスタと比較して同等の電流駆動能力を実現することが出来る。また、シリコンの（1 10)面上に accumulation構造の pチャンネル 'トランジスタを形成することにより、シリコ ン（100)面上に形成した pチャンネル 'トランジスタと比較して 2. 5倍の電流駆動能力 を実現することが出来る。
[0050] また、図 6に示すように、 lZf雑音も低減することができる。本発明の accumulation 型デバイスは、 pn接合障壁によってノーマリオフを実現するのではなぐゲート電極と SOI層の仕事関数差、 SOI層の厚さ、ドレイン電圧、ソース'ドレイン間距離を最適化 し、ゲート図 5 (a)に示すようにゲート電圧が Ovのときにソース'ドレイン間に空乏層が 存在しバリアが形成されるようにすれば、ノーマリオフとなる。図 5 (b)に示すように、ォ ン時にはチャンネルは蓄積層に形成されるので、通常の反転層を形成する inversion 型の MOSトランジスタに比べてチャネル領域の垂直電界が小さくなるため、実効移 動度を大きくすることが出来る。このため、 SOI層の不純物濃度が高くなつても移動 度の劣化が発生しない。さらに、オン時には蓄積層だけでなく SOI層全体 (バルタ部 )にも電流が流れるため、 SOI層の不純物濃度が高いほど電流駆動能力を大きくす ることが出来る。
[0051] 通常の MOSトランジスタでは、微細化に伴って、チャネル領域の不純物濃度を高く するとチャネル移動度が劣化してしまうのに比べると、本発明の accumulation型デバ イスは微細化には非常に有利である。電流駆動能力をできるだけ大きくし、微細化に 対してパンチスルー耐性を持たせてノーマリオフを実現するためには、 accumulation 型 nチャンネル 'トランジスタには仕事関数のできるだけ大き!/、ゲート電極を、 accumul ation型 pチャンネル 'トランジスタには仕事関数のできるだけ小さ!/、ゲート電極を用い ることが好ましい。
[0052] 本発明の accumulation型デバイスは、このようにゲート電極材料と SOI層の仕事関 数差を大きくすることによって SOI層に空乏層を形成し、ドレイン電極に印加した電 圧によるチャネル方向の電界がソース端に影響しないようにしてパンチスルー耐性を 持たせる。 SOI層の厚さが厚いほど電流駆動能力が大きくなるが、仕事関数差によつ て発生したゲートからの電界が SOI層の下端 (底面）にまで影響を及ぼしに《なる。 そこで、仕事関数差を大きくすることが本発明の accumulation型デバイスで最も重要 な要件である。
[0053] 図 7 (a)に accumulation型 nチャンネル 'トランジスタにおいて、ゲート電極の仕事関 数を 5. 2eVと 6. OeVのものを用いたときに許される（ノーマリオフとなる） SOI層の厚 さを示す。ゲート絶縁膜は EOTで 0. 5nmと 1. Onmの場合を示している。ノーマリオ フとするのに許される各微細化世代 (ゲート長)での SOI層の厚さは仕事関数が大き くなるほど厚くなり、 22nm世代では、 5. 2eVと 6. OeVでは約 2倍の厚さとなる。図 7 ( b)には 5. 2eVと 6. OeVのゲート電極を使用した場合のバンド図を示す (絶縁膜厚 1 nm) 0この図に示すように、仕事関数が大きくなると SOI層を厚く出来、電流駆動能 力が増大する。
[0054] 図 8に、空乏層厚さと基板不純物濃度の相関図を示す。この図を参照すると、本発 明の accumulation型 nチャンネル 'トランジスタ 102η、 103ηで、ゲート電極 16を Ρ+多 結晶シリコンで形成すると、その仕事関数はおよそ 5. 15eVであり、基板の 1017cm_ 3の n型シリコン層 14ηの仕事関数は、およそ 4. 25eVであるので、およそ 0. 9eVの 仕事関数差が発生する。このときの空乏層厚さは約 90nm程度であるので、 SOI層 は厚さを 45nmとしても完全に空乏化している。図 8に示すのは、仕事関数差が 0. 9 Vの時の基板不純物濃度と空乏層厚の関係である。ここで、基板不純物濃度と SOI 膜厚は、 SOI膜厚が空乏層厚さより薄い範囲で選ぶことが可能である。また、ゲート 電極材料は、仕事関数差を考慮し、 SOI層が完全空乏化するものであれば、多結晶 シリコンでなぐ W、 Pt、 Ni、 Ge、 Ru、およびそのシリサイドを用いてもかまわない。
[0055] 本発明の半導体装置のゲート絶縁膜は、マイクロ波励起による高密度プラズマを用 い、ラジカル酸化、ラジカル窒化、またはラジカル酸窒化によって形成するのが好ま しいことを、図 11を用いて説明する。図 11 (a)は熱酸化によってゲート絶縁膜を形成 した場合とラジカル酸ィ匕によってゲート絶縁膜を形成した場合との、チャンネル方位 による Sファクターを示すグラフである。
[0056] デバイスとしては、図 11 (b)〖こ示すような、 Accumulationモードの三次元 pチャンネ ル MOSトランジスタを 10個用いて測定した。チャンネル領域の表面は（100)面であ り、その方位はく 110〉方向である。チャンネル領域の諸元は図 11 (a)に記載の通り である。チャンネル領域の表面の結晶面が（100)面でその結晶方位がく 110〉方向 のとき、チャンネル領域の側面にそれと同じ結晶面が現れるから、この場合のチャン ネル領域側面の結晶面は（110)面である。 [0057] 図 11 (c)に示すように、チャンネル表面の方位を〈110〉方向力 45° k回転させる と方位は〈100〉方向となる。このようにして 180° 回転した時の、 15° ごとの Sファタ ターが図 11 (a)に示されている。 Sファクターとは、ドレイン電流を 10倍にするために 必要なゲート電圧を示すもので、小さいほど良いわけである力 理論値は 60mVZd ecである。図 11 (a)に示すように、熱酸化（900°Cdry雰囲気)でゲート絶縁膜を形成 すると 80〜100mVZdecと理論値の 1. 3倍〜 1. 7倍になり、かつ結晶面の方位に よるばらつきも大き 、が、ラジカル酸化 (Krと酸素のプラズマで 400°Cで酸化）では 6 4〜69mVZdecと理論値の 1. 06倍〜 1. 15倍にすぎず、従来の熱酸化膜にくらべ て圧倒的に優れて!/ヽることがゎカゝる。ラジカル窒化およびラジカル酸窒化でゲート絶 縁膜を形成した場合も同様であることを確認した。
[0058] 本発明の CMOS構造においては、 SOI層として好ましくは（110)面から ± 10° 以 内で傾けたような面方位とし、 accumulation型トランジスタでは SOI層の厚さはゲート 電極と SOI層の仕事関数差による空乏層の厚さよりも薄い構造とする。これらの構造 とすることで、電流駆動能力を向上させ、 NMOSトランジスタと PMOSトランジスタが ほぼ同一の電流駆動能力を持つようにバランスさせる。また、 NMOSトランジスタと P MOSトランジスタを同じ半導体基板に構成することにより絶縁分離の面積分を小さく 出きる禾 IJ点もある。このように、 NMOSトランジスタと PMOSトランジスタがほぼ同一の 電流駆動能力を持つようにバランスさせることで、集積度を高くできる半導体装置を 得られる。
産業上の利用可能性
[0059] 以上本発明を実施例に基づき具体的に説明したが、本発明は前記実施例に限定 されるものではなぐその要旨を逸脱しない範囲で種々変更可能であることはいうま でもない。例えば、本発明は、インバータ回路として論理回路に適用できるだけでな ぐ他の電子回路にも適用できる。

Claims

請求の範囲
[1] 異なる導電型のトランジスタを少なくとも一対有する回路を備えた半導体装置にお いて、 SOI基板上に設けた第 1の半導体層とその表面の少なくとも一部を覆う第 1の ゲート絶縁層とを用いて nチャンネル 'トランジスタを形成するとともに前記 SOI基板上 に設けた第 2の半導体層とその表面の少なくとも一部を覆う第 2のゲート絶縁層を用 V、て pチャンネル 'トランジスタを形成し、前記第 1の半導体層のチャネルを形成する 第 1の領域の表面が（110)面または（110)面から ± 10° 以内の面を有するようにす ると共に、前記第 1の半導体層の側面においてチャネルを形成する第 2の領域の表 面を（110)面から ± 10° 以内の面とは異なりかつ（110)面から ± 10° 以内の面よ りも電子の移動度が大きい一つまたは複数の面を有するようにし、前記第 2の半導体 層のチャネルを形成する第 3の領域の表面が（110)面または（110)面から ± 10° 以内の面を有するようにし、前記第 1の領域の表面の面積と前記第 2の領域の表面 の面積との和が前記第 3の領域の表面の面積と実質的に等しいか同等となりかつ前 記 nチャンネル 'トランジスタと前記 pチャンネル 'トランジスタの動作速度が実質的に 等しいか同等となるように、前記第 1の領域の表面の幅および長さ、前記第 2の領域 の表面の高さおよび長さ、ならびに前記第 3の領域の表面の幅および長さを定めたこ とを特徴とする半導体装置。
[2] 請求項 1に記載の半導体装置にお!、て、前記 nチャンネル 'トランジスタと前記 pチ ヤンネル'トランジスタはともに normally offであり、かつ前記 nチャンネル 'トランジス タを inversion型または accumulation型とし、前記 pチャンネル 'トランジスタを inver sion型または accumulation型としたことを特徴とする半導体装置。
[3] 請求項 2に記載の半導体装置にお 、て、前記 nチャンネル 'トランジスタと前記 pチ ヤンネル'トランジスタとをともに inversion型としたことを特徴とする半導体装置。
[4] 請求項 2に記載の半導体装置にお 、て、前記 nチャンネル 'トランジスタと前記 pチ ヤンネル'トランジスタとをともに accumulation型としたことを特徴とする半導体装置
[5] 請求項 2に記載の半導体装置にぉ 、て、前記 nチャンネル 'トランジスタを inversio n型とし、前記 pチャンネル 'トランジスタを accumulation型としたことを特徴とする半 導体装置。
[6] 請求項 2に記載の半導体装置にぉ 、て、前記 nチャンネル 'トランジスタを accumul ation型とし、前記 pチャンネル 'トランジスタを inversion型としたことを特徴とする半 導体装置。
[7] 請求項 4または 5に記載の半導体装置において、前記第 2のゲート絶縁膜上に設け られる第 2のゲート電極と前記第 2の半導体層との仕事関数差により前記第 2の半導 体層に形成される空乏層の厚さが前記第 2の半導体層の膜厚よりも大きくなるように 前記第 2のゲート電極の材料および前記第 2の半導体層の不純物濃度を選ぶことを 特徴とする半導体装置。
[8] 請求項 4または 6に記載の半導体装置において、前記第 1のゲート絶縁膜上に設け られる第 1のゲート電極と前記第 1の半導体層との仕事関数差により前記第 1の半導 体層に形成される空乏層の厚さが前記第 1の半導体層の膜厚よりも大きくなるように 前記第 1のゲート電極の材料および前記第 1の半導体層の不純物濃度を選ぶことを 特徴とする半導体装置。
[9] 前記第 1および第 2のゲート絶縁膜が、マイクロ波励起のプラズマで形成された SiO
, Si Nおよび金属シリコン合金の酸ィ匕膜、金属シリコン合金の窒化膜を少なくとも
2 3 4
一種類、含有することを特徴とする請求項 1乃至請求項 8のいずれか一つに記載の 半導体装置。
[10] 前記第 1および第 2のゲート絶縁膜が 600°C以下の温度で形成されたことを特徴と する請求項 9に記載の半導体装置。
[11] 請求項 1〜10のいずれか一つに記載の半導体装置において、チャンネル長を構 成する前記第 1の領域の表面の長さ、前記第 2の領域の表面の長さ、および前記第
3の領域の表面の長さをすベて互 、に実質的に等 、ように定めたことを特徴とする 半導体装置。
[12] 異なる導電型のトランジスタを少なくとも一対有する回路を備えた半導体装置にお いて、 SOI基板上に設けた第 1の半導体層とその表面の少なくとも一部を覆う第 1の ゲート絶縁層とを用いて一導電型のトランジスタを形成するとともに前記 SOI基板上 に設けた第 2の半導体層とその表面の少なくとも一部を覆う第 2のゲート絶縁層を用 、て他の導電型のトランジスタを形成し、前記第 1の半導体層のチャネルを形成する 第 1の領域の表面を第 1の結晶面を有するようにするとともに前記第 1の領域の表面 と交差する面に設けられた前記第 1の半導体層の側面においてチャネルを形成する 第 2の領域の表面を前記第 1の結晶面とは異なりかつキャリアの移動度も異なる第 2 の結晶面を有するようにし、前記第 2の半導体層のチャネルを形成する第 3の領域の 表面を前記第 1の結晶面を有するようにし、前記第 1の領域の表面における相互コン ダクタンス gmを gml、前記第 2の領域の表面における相互コンダクタンス gmを gml より大きい gm2 (即ち、 gm2>gml)とし、前記第 3の領域の表面における相互コンダ クタンス gmを gmlより大きいが gm2よりは小さい gm3 (即ち、 gml <gm3く gm2)と し、前記第 1の領域の表面の長さを Ll、幅を Wl、前記第 2の領域の表面の長さを L 1、幅を W2とし、前記第 3の領域の表面の長さを L2、幅を W3とし、 Wl, W2, W3, LI, L2のうちどれ力 3つを所定の値としたときに、
Wl X L1 +W2 X L1 =W3 X L2を実質的に満足し、かつ
(gml XWl/Ll) + (gm2 XW2/Ll) =gm3 XW3/L2
を実質的に満足するように Wl, W2, W3, LI, L2のうち残余の 2つを定めることによ つて、
前記一導電型のトランジスタと前記他の導電型のトランジスタとを、チャンネル領域の 面積を互いに実質的に等しいか同等としつつ動作速度を互いに実質的に等しいか 同等となるようにしたことを特徴とする半導体装置。
[13] 請求項 12に記載の半導体装置において、前記 L1と前記 L2とを等しくすることによ つて、 Wl, W2, W3のうちどれか 1つを所定の値として、
W1 +W2=W3 X L2を実質的に満足し、かつ
gml XWl +gm2 XW2= gm3 X W3
を実質的に満足するように Wl, W2, W3のうち残余の 2つを定めることを特徴とする 半導体装置。
[14] 請求項 12または 13に記載の半導体装置において、前記第 2の領域を前記第 1の 領域表面と実質的に垂直な面であって前記第 1の領域表面の両側に延びる前記第 1の半導体層の両側面の部分を用い、その領域の高さを Hとして、前記 W2を 2Hとお くようにしたことを特徴とする半導体装置。
[15] 請求項 14に記載の半導体装置において、前記一導電型のトランジスタをと前記他 の導電型のトランジスタとを前記第 1の結晶面を（110)面または（110)面から士 10
° 以内の面としたことを特徴とする半導体装置。
[16] 請求項 15に記載の半導体装置において、前記一導電型のトランジスタおよび前記 他の導電型のトランジスタを、それぞれ nチャンネル 'トランジスタ、及び、 pチャンネル
•トランジスタとしたことを特徴とする半導体装置。
PCT/JP2006/323997 2005-12-02 2006-11-30 半導体装置 WO2007063963A1 (ja)