WO2006085549A1 - 高濃度浸炭・低歪焼入れ部材およびその製造方法 - Google Patents
高濃度浸炭・低歪焼入れ部材およびその製造方法 Download PDFInfo
- Publication number
- WO2006085549A1 WO2006085549A1 PCT/JP2006/302161 JP2006302161W WO2006085549A1 WO 2006085549 A1 WO2006085549 A1 WO 2006085549A1 JP 2006302161 W JP2006302161 W JP 2006302161W WO 2006085549 A1 WO2006085549 A1 WO 2006085549A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- surface layer
- concentration
- carburizing
- temperature
- low
- Prior art date
Abstract
Description
Claims