WO2005056653A1 - Partikelschaumstoffformteile aus expandierbaren, füllstoff enthaltenden polymergranulaten - Google Patents
Partikelschaumstoffformteile aus expandierbaren, füllstoff enthaltenden polymergranulaten Download PDFInfo
- Publication number
- WO2005056653A1 WO2005056653A1 PCT/EP2004/013748 EP2004013748W WO2005056653A1 WO 2005056653 A1 WO2005056653 A1 WO 2005056653A1 EP 2004013748 W EP2004013748 W EP 2004013748W WO 2005056653 A1 WO2005056653 A1 WO 2005056653A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- expandable
- range
- filler
- weight
- thermoplastic polymer
- Prior art date
Abstract
Description
Claims