WO2004031260A1 - Verfahren zur herstellung von mono- und diestern des polytetrahydrofurans und der tetrahydrofuran-copolymere - Google Patents
Verfahren zur herstellung von mono- und diestern des polytetrahydrofurans und der tetrahydrofuran-copolymere Download PDFInfo
- Publication number
- WO2004031260A1 WO2004031260A1 PCT/EP2003/009807 EP0309807W WO2004031260A1 WO 2004031260 A1 WO2004031260 A1 WO 2004031260A1 EP 0309807 W EP0309807 W EP 0309807W WO 2004031260 A1 WO2004031260 A1 WO 2004031260A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- thf
- tetrahydrofuran
- polytetrahydrofuran
- starting
- polymerization
- Prior art date
Abstract
Description
Claims