US20230373156A9 - Method and apparatus for three-dimensional fabrication - Google Patents

Method and apparatus for three-dimensional fabrication Download PDF

Info

Publication number
US20230373156A9
US20230373156A9 US17/513,312 US202117513312A US2023373156A9 US 20230373156 A9 US20230373156 A9 US 20230373156A9 US 202117513312 A US202117513312 A US 202117513312A US 2023373156 A9 US2023373156 A9 US 2023373156A9
Authority
US
United States
Prior art keywords
build
region
polymerizable liquid
carrier
polymerization
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US17/513,312
Other languages
English (en)
Other versions
US20220048242A1 (en
Inventor
Joseph M. DeSimone
Alexander Ermoshkin
Edward T. Samulski
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Carbon Inc
Original Assignee
Carbon Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US14/572,128 external-priority patent/US9211678B2/en
Application filed by Carbon Inc filed Critical Carbon Inc
Priority to US17/513,312 priority Critical patent/US20230373156A9/en
Publication of US20220048242A1 publication Critical patent/US20220048242A1/en
Publication of US20230373156A9 publication Critical patent/US20230373156A9/en
Pending legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/10—Processes of additive manufacturing
    • B29C64/106—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material
    • B29C64/124—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material using layers of liquid which are selectively solidified
    • B29C64/129—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material using layers of liquid which are selectively solidified characterised by the energy source therefor, e.g. by global irradiation combined with a mask
    • B29C64/135—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material using layers of liquid which are selectively solidified characterised by the energy source therefor, e.g. by global irradiation combined with a mask the energy source being concentrated, e.g. scanning lasers or focused light sources
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F2/00—Filters implantable into blood vessels; Prostheses, i.e. artificial substitutes or replacements for parts of the body; Appliances for connecting them with the body; Devices providing patency to, or preventing collapsing of, tubular structures of the body, e.g. stents
    • A61F2/82—Devices providing patency to, or preventing collapsing of, tubular structures of the body, e.g. stents
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61M—DEVICES FOR INTRODUCING MEDIA INTO, OR ONTO, THE BODY; DEVICES FOR TRANSDUCING BODY MEDIA OR FOR TAKING MEDIA FROM THE BODY; DEVICES FOR PRODUCING OR ENDING SLEEP OR STUPOR
    • A61M37/00—Other apparatus for introducing media into the body; Percutany, i.e. introducing medicines into the body by diffusion through the skin
    • A61M37/0015—Other apparatus for introducing media into the body; Percutany, i.e. introducing medicines into the body by diffusion through the skin by using microneedles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C33/00—Moulds or cores; Details thereof or accessories therefor
    • B29C33/0061—Moulds or cores; Details thereof or accessories therefor characterised by the configuration of the material feeding channel
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C35/00—Heating, cooling or curing, e.g. crosslinking or vulcanising; Apparatus therefor
    • B29C35/02—Heating or curing, e.g. crosslinking or vulcanizing during moulding, e.g. in a mould
    • B29C35/08—Heating or curing, e.g. crosslinking or vulcanizing during moulding, e.g. in a mould by wave energy or particle radiation
    • B29C35/0888—Heating or curing, e.g. crosslinking or vulcanizing during moulding, e.g. in a mould by wave energy or particle radiation using transparant moulds
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/10—Processes of additive manufacturing
    • B29C64/106—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material
    • B29C64/124—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material using layers of liquid which are selectively solidified
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/10—Processes of additive manufacturing
    • B29C64/106—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material
    • B29C64/124—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material using layers of liquid which are selectively solidified
    • B29C64/129—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material using layers of liquid which are selectively solidified characterised by the energy source therefor, e.g. by global irradiation combined with a mask
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/30—Auxiliary operations or equipment
    • B29C64/386—Data acquisition or data processing for additive manufacturing
    • B29C64/393—Data acquisition or data processing for additive manufacturing for controlling or regulating additive manufacturing processes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/40—Structures for supporting 3D objects during manufacture and intended to be sacrificed after completion thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y10/00—Processes of additive manufacturing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y30/00—Apparatus for additive manufacturing; Details thereof or accessories therefor
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y50/00—Data acquisition or data processing for additive manufacturing
    • B33Y50/02—Data acquisition or data processing for additive manufacturing for controlling or regulating additive manufacturing processes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y80/00—Products made by additive manufacturing
    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/0037—Production of three-dimensional images
    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/004—Photosensitive materials
    • G03F7/027—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds
    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/004—Photosensitive materials
    • G03F7/038—Macromolecular compounds which are rendered insoluble or differentially wettable
    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/26—Processing photosensitive materials; Apparatus therefor
    • G03F7/38—Treatment before imagewise removal, e.g. prebaking
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F2240/00—Manufacturing or designing of prostheses classified in groups A61F2/00 - A61F2/26 or A61F2/82 or A61F9/00 or A61F11/00 or subgroups thereof
    • A61F2240/001—Designing or manufacturing processes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C33/00—Moulds or cores; Details thereof or accessories therefor
    • B29C2033/0005—Moulds or cores; Details thereof or accessories therefor with transparent parts, e.g. permitting visual inspection of the interior of the cavity
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C35/00—Heating, cooling or curing, e.g. crosslinking or vulcanising; Apparatus therefor
    • B29C35/02—Heating or curing, e.g. crosslinking or vulcanizing during moulding, e.g. in a mould
    • B29C35/08—Heating or curing, e.g. crosslinking or vulcanizing during moulding, e.g. in a mould by wave energy or particle radiation
    • B29C35/0805—Heating or curing, e.g. crosslinking or vulcanizing during moulding, e.g. in a mould by wave energy or particle radiation using electromagnetic radiation
    • B29C2035/0827—Heating or curing, e.g. crosslinking or vulcanizing during moulding, e.g. in a mould by wave energy or particle radiation using electromagnetic radiation using UV radiation
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2067/00—Use of polyesters or derivatives thereof, as moulding material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2071/00—Use of polyethers, e.g. PEEK, i.e. polyether-etherketone or PEK, i.e. polyetherketone or derivatives thereof, as moulding material
    • B29K2071/02—Polyalkylene oxides, e.g. PEO, i.e. polyethylene oxide, or derivatives thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/0005—Condition, form or state of moulded material or of the material to be shaped containing compounding ingredients
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/0058—Liquid or visquous
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2827/00—Use of polyvinylhalogenides or derivatives thereof as mould material
    • B29K2827/12—Use of polyvinylhalogenides or derivatives thereof as mould material containing fluorine
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2883/00—Use of polymers having silicon, with or without sulfur, nitrogen, oxygen, or carbon only, in the main chain, as mould material
    • B29K2883/005—LSR, i.e. liquid silicone rubbers, or derivatives thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
    • B29K2995/0018—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds having particular optical properties, e.g. fluorescent or phosphorescent
    • B29K2995/0026—Transparent
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
    • B29K2995/0037—Other properties
    • B29K2995/0059—Degradable
    • B29K2995/006—Bio-degradable, e.g. bioabsorbable, bioresorbable or bioerodible
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
    • B29K2995/0037—Other properties
    • B29K2995/0065—Permeability to gases
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2031/00—Other particular articles
    • B29L2031/753—Medical equipment; Accessories therefor
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2031/00—Other particular articles
    • B29L2031/753—Medical equipment; Accessories therefor
    • B29L2031/7532—Artificial members, protheses
    • B29L2031/7534—Cardiovascular protheses
    • G—PHYSICS
    • G05—CONTROLLING; REGULATING
    • G05B—CONTROL OR REGULATING SYSTEMS IN GENERAL; FUNCTIONAL ELEMENTS OF SUCH SYSTEMS; MONITORING OR TESTING ARRANGEMENTS FOR SUCH SYSTEMS OR ELEMENTS
    • G05B2219/00—Program-control systems
    • G—PHYSICS
    • G05—CONTROLLING; REGULATING
    • G05B—CONTROL OR REGULATING SYSTEMS IN GENERAL; FUNCTIONAL ELEMENTS OF SUCH SYSTEMS; MONITORING OR TESTING ARRANGEMENTS FOR SUCH SYSTEMS OR ELEMENTS
    • G05B2219/00—Program-control systems
    • G05B2219/30—Nc systems
    • G05B2219/49—Nc machine tool, till multiple
    • G05B2219/49016—Desktop manufacturing [DTM]; Solid freeform machining [SFM]; Solid freeform fabrication [SFF]

Definitions

  • the present invention concerns methods and apparatus for the fabrication of solid three-dimensional objects from liquid polymerizable materials.
  • construction of a three-dimensional object is performed in a step-wise or layer-by-layer manner.
  • layer formation is performed through solidification of photo curable resin under the action of visible or UV light irradiation.
  • Two techniques are known: one in which new layers are formed at the top surface of the growing object; the other in which new layers are formed at the bottom surface of the growing object.
  • an elastic separation layer is used to achieve “non-destructive” separation of solidified material at the bottom construction plane.
  • Other approaches such as the B9CreatorTM 3-dimensional printer marketed by B9Creations of Deadwood, S. Dak., USA, employ a sliding build plate. See, e.g., M. Joyce, US Patent App. 2013/0292862 and Y. Chen et al., US Patent App. 2013/0295212 (both Nov. 7, 2013); see also Y. Pan et al., J. Manufacturing Sci. and Eng. 134, 051011-1 (October 2012). Such approaches introduce a mechanical step that may complicate the apparatus, slow the method, and/or potentially distort the end product.
  • Described herein are methods, systems and apparatus (including associated control methods, systems and apparatus), for the generally continuous production of a three-dimensional object.
  • the three-dimensional object is produced from a liquid interface.
  • continuous liquid interphase printing A schematic representation is given in FIG. 1 herein.
  • the interface is between first and second layers or zones of the same polymerizable liquid.
  • the first layer or zone (sometimes also referred to as a “dead zone”) contains an inhibitor of polymerization (at least in a polymerization-inhibiting amount); in the second layer or zone the inhibitor has been consumed (or has not otherwise been incorporated or penetrated therein) to the point where polymerization is no longer substantially inhibited.
  • the first and second zones do not form a strict interface between one another but rather there is a gradient of composition that can also be described as forming an interphase between them as opposed to a sharp interface, as the phases are miscible with one another, and further create a (partially or fully overlapping) gradient of polymerization therebetween (and also between the three-dimensional object being fabricated, and the build surface through which the polymerizable liquid is irradiated).
  • the three-dimensional object can be fabricated, grown or produced continuously from that gradient of polymerization (rather than fabricated layer-by-layer).
  • the creation of fault or cleavage lines in the object being produced which may occur in layer-by-layer techniques such as described in Y. Pan et al. or J. Joyce et al. (noted above), may be reduced or obviated.
  • fault or cleavage lines can be intentionally introduced when desired as discussed further below.
  • the first layer or zone is provided immediately on top of, or in contact with, a build plate.
  • the build plate is transparent to the irradiation which initiates the polymerization (e.g., patterned radiation), but the build plate is preferably semipermeable to the polymerization inhibitor and allows the inhibitor of polymerization (e.g., oxygen) to pass partly or fully therethrough (e.g., to continuously feed inhibitor to the “dead zone”).
  • the build plate is preferably “fixed” or “stationary” in the sense that it need not slide, retract, rebound or the like to create separate or sequential steps (as in a layer-by layer process).
  • minor motion of the build plate in the x and/or y directions that does not unduly disrupt the gradient of polymerization, but still permits continuous polymerization from the liquid interface, may still be accommodated in some embodiments, as also discussed below.
  • the present invention provides a method of forming a three-dimensional object, comprising: providing a carrier and an optically transparent member having a build surface, said carrier and said build surface defining a build region therebetween; filling said build region with a polymerizable liquid; irradiating said build region through said optically transparent member to form a solid polymer from said polymerizable liquid while concurrently advancing said carrier away from said build surface to form said three-dimensional object from said solid polymer, while also concurrently (i) continuously maintaining a dead zone of polymerizable liquid in contact with said build surface, and (ii) continuously maintaining a gradient of polymerization zone between said dead zone and said solid polymer and in contact with each thereof, said gradient of polymerization zone comprising said polymerizable liquid in partially cured form (e.g., so that the formation of fault or cleavage lines between layers of solid polymer in said three-dimensional object is reduced).
  • the optically transparent member comprises a semipermeable member, and said continuously maintaining a dead zone is carried out by feeding an inhibitor of polymerization through said optically transparent member, thereby creating a gradient of inhibitor in said dead zone and optionally in at least a portion of said gradient of polymerization zone; in other embodiments, the optically transparent member comprises a semipermeable member, and is configured to contain a sufficient amount (or “pool”) of inhibitor to continuously maintain the dead zone for a sufficient length of time, to produce the article being fabricated without additional feeding of inhibitor during the process (which “pool” may be replenished or recharged between production runs).
  • the optically transparent member is comprised of a semipermeable fluoropolymer, a rigid gas-permeable polymer, porous glass, or a combination thereof.
  • the irradiating step is carried out with a two-dimensional radiation pattern projected into said build region, wherein said pattern varies over time while said concurrently advancing step continues for a time sufficient to form said three-dimensional object (i.e., during which time said gradient of polymerization zone is maintained).
  • the thickness of the gradient of polymerization zone is in some embodiments at least as great as the thickness of the dead zone.
  • the dead zone has a thickness of from 0.01, 0.1, 1, 2, or 10 microns up to 100, 200 or 400 microns, or more, and/or said gradient of polymerization zone and said dead zone together have a thickness of from 1 or 2 microns up to 400, 600, or 1000 microns, or more.
  • the gradient of polymerization zone is maintained (while polymerizing steps continue) for a time of at least 5, 10, 15, 20 or 30 seconds, up to 5, 10, 15 or 20 minutes or more, or until completion of the three-dimensional product.
  • the method may further comprise the step of disrupting said gradient of polymerization zone for a time sufficient to form a cleavage line in said three-dimensional object (e.g., at a predetermined desired location for intentional cleavage, or at a location in said object where prevention of cleavage or reduction of cleavage is non-critical), and then reinstating said gradient of polymerization zone (e.g. by pausing, and resuming, the advancing step, increasing, then decreasing, the intensity of irradiation, and combinations thereof).
  • the method may further comprise heating said polymerizable liquid as it is supplied to the build region and/or within the build region (e.g., by an amount as given in the Examples below) to reduce the viscosity thereof in the build region (e.g., by an amount as given in the Examples below).
  • the method may be carried out and the apparatus implemented wherein said carrier has at least one channel formed therein, and said filling step is carried out by passing or forcing said polymerizable liquid into said build region through said at least one channel (e.g., wherein said carrier has a plurality of channels formed therein, and wherein different polymerizable liquids are forced through different ones of said plurality of channels; e.g., further comprising concurrently forming at least one, or a plurality of, external feed conduits separate from said object, each of said at least one feed conduits in fluid communication with a channel in said carrier, to supply at least one, or a plurality of different, polymerizable liquids from said carrier to said build zone).
  • the semipermeable member has a thickness of from 0.1 or 1 millimeters to 10 or 100 millimeters; and/or said semipermeable member has a permeability to oxygen of at least 10 Barrers.
  • a first particular aspect of the invention is a method of forming a three-dimensional object.
  • the method comprises the steps of:
  • the build plate comprising an (optionally but in some embodiments preferably, fixed) semipermeable member, said semipermeable member comprising a build surface and (optionally but in some embodiments preferably) a feed surface separate from said build surface (e.g., on the opposite side, or edge of the semipermeable member, and/or on the top thereof but at location separate from the build region), with the build surface and the carrier defining a build region there between, and with the feed surface in fluid contact with a (liquid or gas) polymerization inhibitor;
  • Steps (b) and (d), or steps (b) through (d) can be repeated in a continuous or stepwise fashion (concurrently, sequentially, or in any combination thereof), with the build surface remaining stationary throughout, to produce on each repetition a subsequent polymerized region adhered to a previous polymerized region until the repeated deposition of polymerized regions adhered to one another forms said three-dimensional object (e.g., with said solid polymerized region remaining in contact with said polymerizable liquid during said continuing and/or repeating, for example through a gradient of polymerization zone, and for example for a time of at least 10, 20, or 30 seconds, or at least 1 or 2 minutes, and/or through the fabrication of at least 0.5, 1, 2, 3, 4 or 5 centimeters in height of the product, until completion of the (finished or intermediate product until completion of the (finished or intermediate) three-dimensional object being formed).
  • an embodiment of the present invention comprises a method of forming a three-dimensional object, comprising: (a) providing a carrier and a fixed semipermeable member, said semipermeable member comprising a build surface and (optionally but in some embodiments preferably) a feed surface separate from said build surface, with said build surface and said carrier defining a build region there between, and with said feed surface in fluid contact with a polymerization inhibitor; (b) filling said build region with a polymerizable liquid, said polymerizable liquid contacting said build segment, (c) irradiating said build region through said build plate to produce a solid polymerized region in said build region, while (d) forming or maintaining a liquid film release layer comprised of said polymerizable liquid between said solid polymerized region and said build surface, the polymerization of which liquid film is inhibited by said polymerization inhibitor; and (e) unidirectionally advancing said carrier with said polymerized region adhered thereto away from said build surface on said stationary build plate to
  • advancing is without forming an air, gas or vapor pocket or gap between the polymerized region and said build surface, but instead maintaining liquid contact therewith through said polymerizable liquid; in other embodiments, advancing is carried out with forming air, gas, or vapor pockets or bubbles, such as when the object being created is a foamed object, or if the inhibitor is a gas and is supplied at a sufficient pressure to form gas pockets or bubbles, though in these embodiments it is less preferred that a gas or vapor gap that completely separates the three-dimensional object from the polymerizable liquid be formed (unless intentionally so for the reasons discussed below)).
  • the method generally further comprises: (f) continuing and/or repeating steps (b) through (e) to produce a subsequent polymerized region adhered to a previous polymerized region until the continued or repeated deposition of polymerized regions adhered to one another forms said three-dimensional object (e.g., with said solid polymerized region remaining in contact with said polymerizable liquid during said continuing and/or repeating, for example through a gradient of polymerization zone, and for example for a time of at least 10, 20, or 30 seconds, or at least 1 or 2 minutes, and/or through the fabrication of at least 0.5, 1, 2, 3, 4 or 5 centimeters in height of the product, until completion of the (finished or intermediate product until completion of the (finished or intermediate) three-dimensional object being formed).
  • Advancing can be carried out at any suitable cumulative or average rate.
  • the rate may be constant or variable (e.g., a predetermined variable pattern, or adjusted by control factors as discussed below).
  • Advancing may be carried out continuously rather than in interrupted “steps”.
  • the advancing step may be carried out at a rate of at least 0.1, 1, 10, 100 or 100 microns per second, or more, up to, for example, the point at which the heat of the polymerization reaction reaches the degradation temperature of the polymerized reaction product.
  • advancing may be in an uninterrupted manner, e.g., without the need for forming a complete gap between the build plate or polymerizable liquid, on the one hand, and the carrier or object on the other, to facilitate re-filling of polymerizable liquid between steps.
  • the polymerizable liquid is heated during the filling step, e.g., heated sufficiently to reduce the viscosity thereof, and in some embodiments, enhancing the photopolymerization cure chemistry, and thereby increase the speed or rate at which steps (b) through (d) may be repeated.
  • the polymerizable liquid is cooled, such as with a peltier cooler, contacting to a heat sink, contacting with a chilling element containing a chilled liquid circulated therethrough, contacting to or circulating through a heat exchanger, etc., or combinations thereof, to dissipate the heat derived from the photopolymerization process in adjacent regions in the build object.
  • a second aspect of the present invention is an apparatus for forming a three-dimensional object from a polymerizable liquid.
  • the apparatus generally comprises:
  • a build plate connected to the support, the build plate comprising a fixed semipermeable member, the semipermeable member comprising a build surface and (optionally but in some embodiments preferably) a feed surface separate from the build surface, with the build surface and the carrier defining a build region therebetween;
  • a liquid polymer supply operatively associated with the build plate and configured to supply liquid polymer into the build region for solidification polymerization
  • a radiation source operatively associated with the build plate and configured to irradiate the build region through the build plate and form a solid polymerized region therein from the liquid polymer;
  • a controller operatively associated with the carrier and the radiation light source for advancing the carrier away from the build plate during or after polymerization of liquid in the build zone (e.g., a controller configured to maintain a gradient of polymerization zone between said build surface and a solid polymerized material on said carrier over time while the three-dimensional object is formed).
  • the apparatus further comprises a (one or more) heater operatively associated with the build plate (e.g., by positioning the build plate and the heater in a common vessel or container which then serves as an oven or heated chamber; by connecting a heating element directly to the build plate, immersing a heater in the polymerizable liquid, etc.), and/or operatively associated with the liquid polymer supply, which heater in some embodiments may be coupled to a controller (e.g., as discussed in the Examples below).
  • a controller e.g., as discussed in the Examples below.
  • a polydimethylsiloxane (PDMS) coating is applied to the sliding build surface.
  • the PDMS coating is said to absorb oxygen and create a thin lubricating film of unpolymerized resin through its action as a polymerization inhibitor.
  • the PDMS coated build surface is directly replenished with oxygen by mechanically moving (sliding) the surface from beneath the growing object, while wiping unpolymerized resin therefrom with a wiper blade, and then returning it to its previous position beneath the growing object.
  • auxiliary means of providing an inhibitor such as oxygen are provided (e.g., a compressor to associated channels)
  • the process still employs a layer-by-layer approach with sliding and wiping of the surface. Since the PDMS coating may be swollen by the resin, this swelling, along with these mechanical steps, may result in tearing of or damage to the PDMS coating.
  • FIG. 1 is a schematic illustration of one embodiment of a method of the present invention.
  • FIG. 2 is a perspective view of one embodiment of an apparatus of the present invention.
  • FIG. 3 A provides a side sectional view of a first alternate embodiment of a rigid build plate for use in the present invention.
  • FIG. 3 B provides a side sectional view of a second alternate embodiment of a rigid build plate for use in the present invention.
  • FIG. 4 illustrates various alternate carriers for use in the present invention.
  • FIG. 5 A schematically illustrates a polymerization inhibitor in a rigid build plate aiding to establish a non-polymerized film on the surface thereof.
  • FIG. 5 B illustrates the embodiment of FIG. 5 A , with application of UV radiation.
  • FIG. 5 C illustrates the embodiment of FIGS. 5 A- 5 B , after separation of the two plates.
  • FIG. 5 D illustrates an experiment similar to FIGS. 5 A to 5 C , except that clean glass is employed.
  • FIG. 5 E illustrates the embodiment of FIG. 5 D , with application of UV radiation.
  • FIG. 5 F illustrates the embodiment of FIGS. 5 D to 5 E , after separation of the two plates.
  • FIG. 5 G illustrates an experiment similar to FIGS. 5 A to 5 C , and FIGS. 5 D to 54 , except that glass treated with a release layer was used.
  • FIG. 5 H illustrates the embodiment of FIG. 5 G , with application of UV radiation.
  • FIG. 5 I illustrates the embodiment of FIGS. 5 G to 5 H , after separation of the two plates.
  • FIG. 6 A schematically illustrates a structure for showing the migration of an inhibitor (in this case oxygen) through a build plate from a feed surface on the back of the plate to a build surface on the front of a plate to aid in establishing a non-polymerized film on the build surface.
  • an inhibitor in this case oxygen
  • FIG. 6 B shows the structure of a pair of samples of FIG. 6 A being exposed to a nitrogen environment.
  • FIG. 6 C shows the structure of one sample of FIG. 6 B being exposed to UV radiation immediately after being taken from the nitrogen environment.
  • FIG. 6 D shows separation of the structure of FIG. 6 C , with the adhesive completely cured.
  • FIG. 6 E shows the structure of a second sample of FIG. 6 B being exposed to UV radiation, ten minutes after being taken from the nitrogen environment, during which time the sample was exposed to an atmosphere environment.
  • FIG. 6 F shows separation of the structure of FIG. 6 F , with the adhesive only cured adjacent the metal plate.
  • FIG. 7 schematically illustrates a growing three-dimensional object being advanced away from a build surface, and the gap that must be filled therebetween before subsequent polymerization can be carried out.
  • FIG. 8 schematically illustrates an embodiment of the invention which provides for the application of pressure to speed the filling of the gap shown in FIG. 8 .
  • FIG. 9 illustrates a rod or fiber that can be produced by the methods and apparatus of the present invention.
  • FIG. 10 is a photograph of a microneedle array fabricated with methods and apparatus of the present invention.
  • the diameter of the carrier on which the array is held is approximately the same as a United States twenty-five cent coin (or “quarter”). Essentially the same carrier is used in the additional examples illustrated below.
  • FIG. 11 is a photograph of a second microneedle array fabricated with methods and apparatus of the present invention.
  • FIG. 12 is a photograph of a ring structure being fabricated with methods and apparatus of the present invention. Note the extensive “overhang” during fabrication.
  • FIG. 13 is a photograph of the completed ring of FIG. 12 .
  • FIG. 14 is a photograph of four chess piece structures fabricated with methods and apparatus of the present invention.
  • FIG. 15 is a photograph of a rectangular prism structure fabricated with methods and apparatus of the present invention.
  • FIG. 16 is a photograph of a coil structure fabricated by methods and apparatus of the present invention. Note the extensive “overhang” during fabrication through to the completed structure.
  • FIG. 17 illustrates the effects of dye and photoinitiator on cure time.
  • FIG. 18 is a photograph of a chess piece similar to those shown FIG. 14 above, but made with a dyed resin by the methods of the present invention.
  • FIG. 19 schematically illustrates the fabrication of a plurality of articles on the carrier, the carrier having a release layer thereon.
  • FIG. 20 schematically illustrates the release of a plurality of articles from the carrier with a release layer.
  • FIG. 21 is a photograph of an array of prisms fabricated by methods and apparatus of the present invention, on a release layer.
  • FIG. 22 is a photograph of the prisms shown in FIG. 21 after release.
  • FIG. 23 is a photograph of a cylindrical caged structure produced by methods and apparatus of the present invention.
  • FIG. 24 is a photograph of an array similar to that of FIG. 21 , and produced by essentially the same methods, except that it comprises a polyethylene glycol polymer.
  • FIG. 25 is a photograph of a cylindrical cage structure similar to that of FIG. 23 , and produced by substantially the same methods, except that it comprises a polyethylene glycol polymer. The part was noted to be flexible.
  • FIG. 26 schematically illustrates an embodiment of an apparatus of the present invention in which one or more heaters are included to reduce the viscosity of the polymerizable liquid.
  • FIG. 27 schematically illustrates an embodiment of an apparatus of the present invention in which the build region is filled with polymerizable liquid fed through the carrier.
  • FIG. 28 schematically illustrates an embodiment of the invention in which external conduits are formed to facilitate feeding one or multiple polymerizable liquids from the carrier to the build region.
  • FIG. 29 is a first flow chart illustrating control systems and methods for carrying out the present invention.
  • FIG. 30 is a second flow chart illustrating control systems and methods for carrying out the present invention.
  • FIG. 31 is a third flow chart illustrating control systems and methods for carrying out the present invention.
  • spatially relative terms such as “under,” “below,” “lower,” “over,” “upper” and the like, may be used herein for ease of description to describe an element's or feature's relationship to another element(s) or feature(s) as illustrated in the figures. It will be understood that the spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. For example, if the device in the figures is inverted, elements described as “under” or “beneath” other elements or features would then be oriented “over” the other elements or features. Thus the exemplary term “under” can encompass both an orientation of over and under.
  • the device may otherwise be oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein interpreted accordingly.
  • the terms “upwardly,” “downwardly,” “vertical,” “horizontal” and the like are used herein for the purpose of explanation only, unless specifically indicated otherwise.
  • first, second, etc. may be used herein to describe various elements, components, regions, layers and/or sections, these elements, components, regions, layers and/or sections should not be limited by these terms. Rather, these terms are only used to distinguish one element, component, region, layer and/or section, from another element, component, region, layer and/or section. Thus, a first element, component, region, layer or section discussed herein could be termed a second element, component, region, layer or section without departing from the teachings of the present invention.
  • the sequence of operations (or steps) is not limited to the order presented in the claims or figures unless specifically indicated otherwise.
  • the liquid can include a monomer, particularly photopolymerizable and/or free radical polymerizable monomers, and a suitable initiator such as a free radical initiator, and combinations thereof.
  • suitable initiator such as a free radical initiator
  • examples include, but are not limited to, acrylics, methacrylics, acrylamides, styrenics, olefins, halogenated olefins, cyclic alkenes, maleic anhydride, alkenes, alkynes, carbon monoxide, functionalized oligomers, multifunctional cute site monomers, functionalized PEGs, etc., including combinations thereof.
  • liquid resins, monomers and initiators include but are not limited to those set forth in U.S. Pat. Nos. 8,232,043; 8,119,214; 7,935,476; 7,767,728; 7,649,029; WO 2012129968 A1; CN 102715751 A; JP 2012210408 A.
  • the polymerizable liquid comprises a free radical polymerizable liquid (in which case an inhibitor may be oxygen as described below), in other embodiments the polymerizable liquid comprises an acid catalyzed, or cationically polymerized, polymerizable liquid. In such embodiments the polymerizable liquid comprises monomers contain groups suitable for acid catalysis, such as epoxide groups, vinyl ether groups, etc.
  • suitable monomers include olefins such as methoxyethene, 4-methoxystyrene, styrene, 2-methylprop-1-ene, 1,3-butadiene, etc.; heterocycloic monomers (including lactones, lactams, and cyclic amines) such as oxirane, thietane, tetrahydrofuran, oxazoline, 1,3, dioxepane, oxetan-2-one, etc., and combinations thereof.
  • olefins such as methoxyethene, 4-methoxystyrene, styrene, 2-methylprop-1-ene, 1,3-butadiene, etc.
  • heterocycloic monomers including lactones, lactams, and cyclic amines
  • a suitable (generally ionic or non-ionic) photoacid generator (PAG) is included in the acid catalyzed polymerizable liquid, examples of which include, but are not limited to onium salts, sulfonium and iodonium salts, etc., such as diphenyl iodide hexafluorophosphate, diphenyl iodide hexafluoroarsenate, diphenyl iodide hexafluoroantimonate, diphenyl p-methoxyphenyl triflate, diphenyl p-toluenyl triflate, diphenyl p-isobutylphenyl triflate, diphenyl p-tert-butylphenyl triflate, triphenylsulfonium hexafluororphosphate, triphenylsulfonium hexafluoroarsenate, triphenylsulfonium
  • suitable resins includes photocurable hydrogels like poly(ethylene glycols) (PEG) and gelatins.
  • PEG hydrogels have been used to deliver a variety of biologicals, including Growth factors; however, a great challenge facing PEG hydrogels crosslinked by chain growth polymerizations is the potential for irreversible protein damage.
  • Conditions to maximize release of the biologicals from photopolymerized PEG diacrylate hydrogels can be enhanced by inclusion of affinity binding peptide sequences in the monomer resin solutions, prior to photopolymerization allowing sustained delivery.
  • Gelatin is a biopolymer frequently used in food, cosmetic, pharmaceutical and photographic industries. It is obtained by thermal denaturation or chemical and physical degradation of collagen.
  • gelatin There are three kinds of gelatin, including those found in animals, fish and humans. Gelatin from the skin of cold water fish is considered safe to use in pharmaceutical applications. UV or visible light can be used to crosslink appropriately modified gelatin. Methods for crosslinking gelatin include cure derivatives from dyes such as Rose Bengal.
  • Photocurable silicone resins A suitable resin includes photocurable silicones.
  • UV cure silicone rubber such as SilioprenTM UV Cure Silicone Rubber can be used as can LOCTITETM Cure Silicone adhesives sealants.
  • Applications include optical instruments, medical and surgical equipment, exterior lighting and enclosures, electrical connectors/sensors, fiber optics and gaskets.
  • Biodegradable resins are particularly important for implantable devices to deliver drugs or for temporary performance applications, like biodegradable screws and stents (U.S. Pat. Nos. 7,919,162; 6,932,930).
  • Biodegradable copolymers of lactic acid and glycolic acid (PLGA) can be dissolved in PEG dimethacrylate to yield a transparent resin suitable for use.
  • Polycaprolactone and PLGA oligomers can be functionalized with acrylic or methacrylic groups to allow them to be effective resins for use.
  • Photocurable polyurethanes A particularly useful resin is photocurable polyurethanes.
  • a photopolymerizable polyurethane composition comprising (1) a polyurethane based on an aliphatic diisocyanate, poly(hexamethylene isophtalate glycol) and, optionally, 1,4-butanediol; (2) a polyfunctional acrylic ester; (3) a photoinitiator; and (4) an anti-oxidant, can be formulated so that it provides a hard, abrasion-resistant, and stain-resistant material (U.S. Pat. No. 4,337,130).
  • Photocurable thermoplastic polyurethane elastomers incorporate photoreactive diacetylene diols as chain extenders.
  • High performance resins are used. Such high performance resins may sometimes require the use of heating to melt and/or reduce the viscosity thereof, as noted above and discussed further below.
  • Examples of such resins include, but are not limited to, resins for those materials sometimes referred to as liquid crystalline polymers of esters, ester-imide, and ester-amide oligomers, as described in U.S. Pat. Nos. 7,507,784; 6,939,940.
  • thermoset resins are sometimes employed as high-temperature thermoset resins, in the present invention they further comprise a suitable photoinitiator such as benzophenone, anthraquinone, amd fluoroenone initiators (including derivatives thereof), to initiate cross-linking on irradiation, as discussed further below.
  • a suitable photoinitiator such as benzophenone, anthraquinone, amd fluoroenone initiators (including derivatives thereof), to initiate cross-linking on irradiation, as discussed further below.
  • Particularly useful resins for dental applications include EnvisionTEC's Clear Guide, EnvisionTEC's E-Denstone Material.
  • Particularly useful resins for hearing aid industries include EnvisionTEC's e-Shell 300 Series of resins.
  • Particularly useful resins include EnvisionTEC's HTM140IV High Temperature Mold Material for use directly with vulcanized rubber in molding/casting applications.
  • a particularly useful material for making tough and stiff parts includes EnvisionTEC's RC31 resin.
  • a particularly useful resin for investment casting applications includes EnvisionTEC's Easy Cast EC500.
  • the liquid resin or polymerizable material can have solid particles suspended or dispersed therein. Any suitable solid particle can be used, depending upon the end product being fabricated.
  • the particles can be metallic, organic/polymeric, inorganic, or composites or mixtures thereof.
  • the particles can be nonconductive, semi-conductive, or conductive (including metallic and non-metallic or polymer conductors); and the particles can be magnetic, ferromagnetic, paramagnetic, or nonmagnetic.
  • the particles can be of any suitable shape, including spherical, elliptical, cylindrical, etc.
  • the particles can comprise an active agent or detectable compound as described below, though these may also be provided dissolved solubilized in the liquid resin as also discussed below. For example, magnetic or paramagnetic particles or nanoparticles can be employed.
  • the liquid resin can have additional ingredients solubilized therein, including pigments, dyes, active compounds or pharmaceutical compounds, detectable compounds (e.g., fluorescent, phosphorescent, radioactive), etc., again depending upon the particular purpose of the product being fabricated.
  • additional ingredients include, but are not limited to, proteins, peptides, nucleic acids (DNA, RNA) such as siRNA, sugars, small organic compounds (drugs and drug-like compounds), etc., including combinations thereof.
  • Inhibitors of polymerization may be in the form of a liquid or a gas.
  • gas inhibitors are preferred.
  • the specific inhibitor will depend upon the monomer being polymerized and the polymerization reaction.
  • the inhibitor can conveniently be oxygen, which can be provided in the form of a gas such as air, a gas enriched in oxygen (optionally but in some embodiments preferably containing additional inert gases to reduce combustibility thereof), or in some embodiments pure oxygen gas.
  • the inhibitor can be a base such as ammonia, trace amines (e.g. methyl amine, ethyl amine, di and trialkyl amines such as dimethyl amine, diethyl amine, trimethyl amine, triethyl amine, etc.), or carbon dioxide, including mixtures or combinations thereof.
  • Polymerizable liquids carrying live cells may carry live cells as “particles” therein.
  • Such polymerizable liquids are generally aqueous, and may be oxygenated, and may be considered as “emulsions” where the live cells are the discrete phase.
  • Suitable live cells may be plant cells (e.g., monocot, dicot), animal cells (e.g., mammalian, avian, amphibian, reptile cells), microbial cells (e.g., prokaryote, eukaryote, protozoal, etc.), etc.
  • the cells may be of differentiated cells from or corresponding to any type of tissue (e.g., blood, cartilage, bone, muscle, endocrine gland, exocrine gland, epithelial, endothelial, etc.), or may be undifferentiated cells such as stem cells or progenitor cells.
  • the polymerizable liquid can be one that forms a hydrogel, including but not limited to those described in U.S. Pat. Nos. 7,651,683; 7,651,682; 7,556,490; 6,602,975; 5,836,313; etc.
  • FIG. 2 A non-limiting embodiment of an apparatus of the invention is shown in FIG. 2 . It comprises a radiation source 11 such as a digital light processor (DLP) providing electromagnetic radiation 12 which though reflective mirror 13 illuminates a build chamber defined by wall 14 and a rigid build plate 15 forming the bottom of the build chamber, which build chamber is filled with liquid resin 16 .
  • the bottom of the chamber 15 is constructed of rigid build plate comprising a rigid semipermeable member as discussed further below.
  • the top of the object under construction 17 is attached to a carrier 18 .
  • the carrier is driven in the vertical direction by linear stage 19 , although alternate structures can be used as discussed below.
  • a liquid resin reservoir, tubing, pumps liquid level sensors and/or valves can be included to replenish the pool of liquid resin in the build chamber (not shown for clarity) though in some embodiments a simple gravity feed may be employed.
  • Drives/actuators for the carrier or linear stage, along with associated wiring, can be included in accordance with known techniques (again not shown for clarity).
  • the drives/actuators, radiation source, and in some embodiments pumps and liquid level sensors can all be operatively associated with a suitable controller, again in accordance with known techniques.
  • Build plates 15 used to carry out the present invention generally comprise or consist of a (typically rigid or solid, stationary, and/or fixed) semipermeable (or gas permeable) member, alone or in combination with one or more additional supporting substrates (e.g., clamps and tensioning members to rigidify an otherwise flexible semipermeable material).
  • the rigid semipermeable member can be made of any suitable material that is optically transparent at the relevant wavelengths (or otherwise transparent to the radiation source, whether or not it is visually transparent as perceived by the human eye—i.e., an optically transparent window may in some embodiments be visually opaque), including but not limited to porous or microporous glass, and the rigid gas permeable polymers used for the manufacture of rigid gas permeable contact lenses.
  • the rigid semipermeable member is formed of a material that does not swell when contacted to the liquid resin or material to be polymerized (i.e., is “non-swellable”).
  • Suitable materials for the rigid semipermeable member include rigid amorphous fluoropolymers, such as those described in U.S. Pat. Nos. 5,308,685 and 5,051,115.
  • such fluoropolymers are particularly useful over silicones that would potentially swell when used in conjunction with organic liquid resin inks to be polymerized.
  • silicone based window materials maybe suitable.
  • the solubility or permeability of organic liquid resin inks can be dramatically decreased by a number of known parameters including increasing the crosslink density of the window material or increasing the molecular weight of the liquid resin ink.
  • the build plate may be formed from a thin film or sheet of material which is flexible when separated from the apparatus of the invention, but which is clamped and tensioned when installed in the apparatus (e.g., with a tensioning ring) so that it is rendered rigid in the apparatus.
  • Particular materials include TEFLON AF® fluoropolymers, commercially available from DuPont. Additional materials include perfluoropolyether polymers such as described in U.S. Pat. Nos. 8,268,446; 8,263,129; 8,158,728; and 7,435,495.
  • the terms “stationary” or “fixed” with respect to the build plate is intended to mean that no mechanical interruption of the process occurs, or no mechanism or structure for mechanical interruption of the process (as in a layer-by-layer method or apparatus) is provided, even if a mechanism for incremental adjustment of the build plate (for example, adjustment that does not lead to or cause collapse of the gradient of polymerization zone) is provided).
  • the semipermeable member typically comprises a top surface portion, a bottom surface portion, and an edge surface portion.
  • the build surface is on the top surface portion; and the feed surface may be on one, two, or all three of the top surface portion, the bottom surface portion, and/or the edge surface portion.
  • the feed surface is on the bottom surface portion, but alternate configurations where the feed surface is provided on an edge, and/or on the top surface portion (close to but separate or spaced away from the build surface) can be implemented with routine skill.
  • the semipermeable member has, in some embodiments, a thickness of from 0.01, 0.1 or 1 millimeters to 10 or 100 millimeters, or more (depending upon the size of the item being fabricated, whether or not it is laminated to or in contact with an additional supporting plate such as glass, etc., as discussed further below.
  • the permeability of the semipermeable member to the polymerization inhibitor will depend upon conditions such as the pressure of the atmosphere and/or inhibitor, the choice of inhibitor, the rate or speed of fabrication, etc.
  • the permeability of the semipermeable member to oxygen may be from 10 or 20 Barrers, up to 1000 or 2000 Barrers, or more.
  • a semipermeable member with a permeability of 10 Barrers used with a pure oxygen, or highly enriched oxygen, atmosphere under a pressure of 150 PSI may perform substantially the same as a semipermeable member with a permeability of 500 Barrers when the oxygen is supplied from the ambient atmosphere under atmospheric conditions.
  • the semipermeable member may comprise a flexible polymer film (having any suitable thickness, e.g., from 0.001, 0.01, 0.1 or 1 millimeters to 5, 10, or 100 millimeters, or more), and the build plate may further comprise a tensioning member (e.g., a peripheral clamp and an operatively associated strain member or stretching member, as in a “drum head”; a plurality of peripheral clamps, etc., including combinations thereof) connected to the polymer film and to fix and rigidify the film (e.g., at least sufficiently so that the film does not stick to the object as the object is advanced and resiliently or elastically rebound therefrom).
  • a tensioning member e.g., a peripheral clamp and an operatively associated strain member or stretching member, as in a “drum head”; a plurality of peripheral clamps, etc., including combinations thereof
  • the film has a top surface and a bottom surface, with the build surface on the top surface and the feed surface preferably on the bottom surface.
  • the semipermeable member comprises: (i) a polymer film layer (having any suitable thickness, e.g., from 0.001, 0.01, 0.1 or 1 millimeters to 5, 10 or 100 millimeters, or more), having a top surface positioned for contacting said polymerizable liquid and a bottom surface, and (ii) a rigid, gas permeable, optically transparent supporting member (having any suitable thickness, e.g., from 0.01, 0.1 or 1 millimeters to 10, 100, or 200 millimeters, or more), contacting said film layer bottom surface.
  • the supporting member has a top surface contacting the film layer bottom surface, and the supporting member has a bottom surface which may serve as the feed surface for the polymerization inhibitor.
  • Any suitable materials that are semipermeable that is, permeable to the polymerization inhibitor may be used.
  • the polymer film or polymer film layer may, for example, be a fluoropolymer film, such as an amorphous thermoplastic fluoropolymer like TEFLON AF1600TM or TEFLON AF2400TM fluoropolymer films, or perfluoropolyether (PFPE), particularly a crosslinked PFPE film, or a crosslinked silicone polymer film.
  • PFPE perfluoropolyether
  • the supporting member comprises a silicone or crosslinked silicone polymer member such as a polydmiethylxiloxane member, a rigid gas permeable polymer member, or a porous or microporous glass member.
  • Films can be laminated or clamped directly to the rigid supporting member without adhesive (e.g., using PFPE and PDMS materials), or silane coupling agents that react with the upper surface of a PDMS layer can be utilized to adhere to the first polymer film layer.
  • UV-curable, acrylate-functional silicones can also be used as a tie layer between UV-curable PFPEs and rigid PDMS supporting layers.
  • the semipermeable member allows inhibitor to pass therethrough, it can simply be configured to contain a sufficient amount (or “pool”) of inhibitor to continuously maintain the dead zone for a sufficient length of time, to produce the article being fabricated without additional feeding of inhibitor during the process (which “pool” may be replenished or recharged between production runs).
  • the size and internal volume of the member can be configured as appropriate for the particular article being fabricated to contain a sufficient pool of inhibitor.
  • the carrier When configured for placement in the apparatus, the carrier defines a “build region” on the build surface, within the total area of the build surface. Because lateral “throw” (e.g., in the X and/or Y directions) is not required in the present invention to break adhesion between successive layers, as in the Joyce and Chen devices noted previously, the area of the build region within the build surface may be maximized (or conversely, the area of the build surface not devoted to the build region may be minimized). Hence in some embodiments, the total surface area of the build region can occupy at least fifty, sixty, seventy, eighty, or ninety percent of the total surface area of the build surface.
  • the various components are mounted on a support or frame assembly 20 .
  • the support or frame assembly is comprised of a base 21 to which the radiation source 11 is securely or rigidly attached, a vertical member 22 to which the linear stage is operatively associated, and a horizontal table 23 to which wall 14 is removably or securely attached (or on which the wall is placed), and with the build plate rigidly fixed, either permanently or removably, to form the build chamber as described above.
  • the build plate can consist of a single unitary and integral piece of a rigid semipermeable member, or can comprise additional materials.
  • a porous or microporous glass can be laminated or fixed to a rigid semipermeable material.
  • a semipermeable member as an upper portion can be fixed to a transparent lower member having purging channels formed therein for feeding gas carrying the polymerization inhibitor to the semipermeable member (through which it passes to the build surface to facilitate the formation of a release layer of unpolymerized liquid material, as noted above and below).
  • Such purge channels may extend fully or partially through the base plate: For example, the purge channels may extend partially into the base plate, but then end in the region directly underlying the build surface to avoid introduction of distortion. Specific geometries will depend upon whether the feed surface for the inhibitor into the semipermeable member is located on the same side or opposite side as the build surface, on an edge portion thereof, or a combination of several thereof.
  • any suitable radiation source can be used, depending upon the particular resin employed, including electron beam and ionizing radiation sources.
  • the radiation source is an actinic radiation source, such as one or more light sources, and in particular one or more ultraviolet light sources.
  • Any suitable light source can be used, such as incandescent lights, fluorescent lights, phosphorescent or luminescent lights, a laser, light-emitting diode, etc., including arrays thereof.
  • the light source preferably includes a pattern-forming element operatively associated with a controller, as noted above.
  • the light source or pattern forming element comprises a digital (or deformable) micromirror device (DMD) with digital light processing (DLP), a spatial modulator (SLM), or a microelectromechanical system (MEMS) mirror array, a mask (aka a reticle), a silhouette, or a combination thereof.
  • DMD digital (or deformable) micromirror device
  • DLP digital light processing
  • SLM spatial modulator
  • MEMS microelectromechanical system
  • the light source comprises a spatial light modulation array such as a liquid crystal light valve array or micromirror array or DMD (e.g., with an operatively associated digital light processor, typically in turn under the control of a suitable controller), configured to carry out exposure or irradiation of the polymerizable liquid without a mask, e.g., by maskless photolithography.
  • a spatial light modulation array such as a liquid crystal light valve array or micromirror array or DMD (e.g., with an operatively associated digital light processor, typically in turn under the control of a suitable controller), configured to carry out exposure or irradiation of the polymerizable liquid without a mask, e.g., by maskless photolithography.
  • FIG. 4 Alternate carriers and actuator/drive arrangements are shown in FIG. 4 . Numerous variations can be employed, including a take-up reel, an XYZ drive assembly (e.g., as commonly used on an automated microscope stage), etc.
  • the drive assembly will generally comprise a worm gear and motor, a rack and pinion and motor, a hydraulic, pneumatic, or piezoelectric drive, or the like, adapted to move or advance the carrier away from the build surface in the vertical or “Z” direction only.
  • a spool or take-up reel can be utilized, with associated drives or actuators and guides (not shown), particularly when the product being fabricated is an elongated rod or fiber (discussed further below).
  • a pair of take-up reels with associated guides, and associated drives or actuators can be mounted on the linear stage to provide movement in either the X and/or Y direction in addition to or in combination with, movement in the Z direction provided by linear stage 19 .
  • an XYZ drive assembly like that used in an automated microscope can be used in place of linear stage 19 to move or advance the carrier away from the build surface in the X, Y, and/or Z direction, e.g., at an angle, or at changing angles, or combinations of directions at various stages.
  • advancement away from the build plate can be carried out solely in the Z (or vertical) direction, or in at least the Z direction, by combining movement in the Z direction with movement in the X and/or Y directions.
  • such movement may be carried out for purposes such as reducing “burn in” or fouling in a particular zone of the build surface.
  • lateral movement (including movement in the X and/or Y direction or combination thereof) of the carrier and object (if such lateral movement is present) is preferably not more than, or less than, 80, 70, 60, 50, 40, 30, 20, or even 10 percent of the width (in the direction of that lateral movement) of the build region.
  • the carrier is mounted on an elevator to advance up and away from a stationary build plate
  • the converse arrangement may be used: That is, the carrier may be fixed and the build plate lowered to thereby advance the carrier away therefrom.
  • the build plate is “stationary” in the sense that no lateral (X or Y) movement is required to replenish the inhibitor thereon, or no elastic build plate that must be stretched and then rebound (with associated over-advance, and back-up of, the carrier) need be employed.
  • adhesion of the article to the carrier may sometimes be insufficient to retain the article on the carrier through to completion of the finished article or “build.”
  • an aluminum carrier may have lower adhesion than a poly(vinyl chloride) (or “PVC”) carrier.
  • PVC poly(vinyl chloride)
  • any of a variety of techniques can be used to further secure the article to a less adhesive carrier, including but not limited to the application of adhesive tape such as “Greener Masking Tape for Basic Painting #2025 High adhesion” to further secure the article to the carrier during fabrication.
  • Soluble sacrificial layers may be established between the carrier and the three-dimensional object, so that that sacrificial layer may be subsequently solubilized to conveniently release the three-dimensional object from the carrier once fabrication is complete.
  • a soluble sacrificial layer or release layer may be established between the carrier and the three-dimensional object, so that that sacrificial layer may be subsequently solubilized to conveniently release the three-dimensional object from the carrier once fabrication is complete.
  • Any suitable sacrificial layer such as an adhesive, that may be coated or otherwise provided on the carrier may be employed, and any suitable solvent (e.g., polar and non-polar organic solvents, aqueous solvents, etc.
  • the sacrificial layer and its corresponding solvent should be chosen so that the particular material from which the three-dimensional object is formed is not itself unduly attacked or solubilized by that solvent.
  • the sacrificial layer may be applied to the carrier by any suitable technique, such as spraying, dip coating, painting, etc.
  • suitable materials for the soluble sacrificial release layer include but are not limited to: cyanoacrylate adhesive (acetone solvent); poly(vinylpyrrolidone) (water and/or isopropyl alcohol solvent); lacquers (acetone solvent); polyvinyl alcohol, polyacrylic acid, poly(methacrylic acid), polyacrylamide, polyalkylene oxides such as poly(ethylene oxide), sugars and saccharides such as sucrose and dextran (all water or aqueous solvents); etc. Lower surface energy solvents are in some embodiments particularly preferred.
  • the actuator/drive and/or associated controller are configured to only advance the carrier away from the build plate (e.g., is unidirectional), as discussed further below.
  • the actuator/drive and/or associated controller are configured as a continuous drive (as opposed to a step-wise drive), as also discussed below.
  • the present invention provides a method of forming a three-dimensional object, comprising the steps of: (a) providing a carrier and a build plate, said build plate comprising a semipermeable member, said semipermeable member comprising a build surface and a feed surface separate from said build surface, with said build surface and said carrier defining a build region therebetween, and with said feed surface in fluid contact with a polymerization inhibitor; then (concurrently and/or sequentially) (b) filling said build region with a polymerizable liquid, said polymerizable liquid contacting said build segment, (c) irradiating said build region through said build plate to produce a solid polymerized region in said build region, with a liquid film release layer comprised of said polymerizable liquid formed between said solid polymerized region and said build surface, the polymerization of which liquid film is inhibited by said polymerization inhibitor; and (d) advancing said carrier with said polymerized region adhered thereto away from said build surface on said stationary build plate to create
  • the method includes (e) continuing and/or repeating steps (b) through (d) to produce a subsequent polymerized region adhered to a previous polymerized region until the continued or repeated deposition of polymerized regions adhered to one another forms said three-dimensional object.
  • the method can be carried out in a continuous fashion, though it will be appreciated that the individual steps noted above may be carried out sequentially, concurrently, or a combination thereof. Indeed, the rate of steps can be varied over time depending upon factors such as the density and/or complexity of the region under fabrication.
  • the present invention in some embodiments permits elimination of this “back-up” step and allows the carrier to be advanced unidirectionally, or in a single direction, without intervening movement of the window for re-coating, or “snapping” of a pre-formed elastic release-layer.
  • the advancing step is carried out sequentially in uniform increments (e.g., of from 0.1 or 1 microns, up to 10 or 100 microns, or more) for each step or increment. In some embodiments, the advancing step is carried out sequentially in variable increments (e.g., each increment ranging from 0.1 or 1 microns, up to 10 or 100 microns, or more) for each step or increment.
  • the size of the increment, along with the rate of advancing, will depend in part upon factors such as temperature, pressure, structure of the article being produced (e.g., size, density, complexity, configuration, etc.)
  • the advancing step is carried out continuously, at a uniform or variable rate.
  • the rate of advance (whether carried out sequentially or continuously) is from about 0.1 1, or 10 microns per second, up to about to 100, 1,000, or 10,000 microns per second, again depending again depending on factors such as temperature, pressure, structure of the article being produced, intensity of radiation, etc
  • the filling step is carried out by forcing said polymerizable liquid into said build region under pressure.
  • the advancing step or steps may be carried out at a rate or cumulative or average rate of at least 0.1, 1, 10, 50, 100, 500 or 1000 microns per second, or more.
  • the pressure may be whatever is sufficient to increase the rate of said advancing step(s) at least 2, 4, 6, 8 or 10 times as compared to the maximum rate of repetition of said advancing steps in the absence of said pressure.
  • a pressure of 10, 20, 30 or 40 pounds per square inch (PSI) up to, 200, 300, 400 or 500 PSI or more may be used.
  • PSI pounds per square inch
  • both the feed surface and the polymerizable liquid can be in fluid contact with the same compressed gas (e.g., one comprising from 20 to 95 percent by volume of oxygen, the oxygen serving as the polymerization inhibitor.
  • the size of the pressure vessel can be kept smaller relative to the size of the product being fabricated and higher pressures can (if desired) be more readily utilized.
  • the irradiating step is in some embodiments carried out with patterned irradiation.
  • the patterned irradiation may be a fixed pattern or may be a variable pattern created by a pattern generator (e.g., a DLP) as discussed above, depending upon the particular item being fabricated.
  • a pattern generator e.g., a DLP
  • each irradiating step may be any suitable time or duration depending on factors such as the intensity of the irradiation, the presence or absence of dyes in the polymerizable material, the rate of growth, etc.
  • each irradiating step can be from 0.001, 0.01, 0.1, 1 or 10 microseconds, up to 1, 10, or 100 minutes, or more, in duration.
  • the interval between each irradiating step is in some embodiments preferably as brief as possible, e.g., from 0.001, 0.01, 0.1, or 1 microseconds up to 0.1, 1, or 10 seconds.
  • the build surface is flat; in other the build surface is irregular such as convexly or concavely curved, or has walls or trenches formed therein. In either case the build surface may be smooth or textured.
  • Curved and/or irregular build plates or build surfaces can be used in fiber or rod formation, to provide different materials to a single object being fabricated (that is, different polymerizable liquids to the same build surface through channels or trenches formed in the build surface, each associated with a separate liquid supply, etc.
  • Carrier Feed Channels for Polymerizable liquid While polymerizable liquid may be provided directly to the build plate from a liquid conduit and reservoir system, in some embodiments the carrier include one or more feed channels therein.
  • the carrier feed channels are in fluid communication with the polymerizable liquid supply, for example a reservoir and associated pump. Different carrier feed channels may be in fluid communication with the same supply and operate simultaneously with one another, or different carrier feed channels may be separately controllable from one another (for example, through the provision of a pump and/or valve for each). Separately controllable feed channels may be in fluid communication with a reservoir containing the same polymerizable liquid, or may be in fluid communication with a reservoir containing different polymerizable liquids. Through the use of valve assemblies, different polymerizable liquids may in some embodiments be alternately fed through the same feed channel, if desired.
  • the methods and apparatus of the invention can include process steps and apparatus features to implement process control, including feedback and feed-forward control, to, for example, enhance the speed and/or reliability of the method.
  • a controller for use in carrying out the present invention may be implemented as hardware circuitry, software, or a combination thereof.
  • the controller is a general purpose computer that runs software, operatively associated with monitors, drives, pumps, and other components through suitable interface hardware and/or software.
  • Suitable software for the control of a three-dimensional printing or fabrication method and apparatus as described herein includes, but is not limited to, the ReplicatorG open source 3d printing program, 3DPrintTM controller software from 3D systems, Slic3r, Skeinforge, KIS Slicer, Repetier-Host, PrintRun, Cura, etc., including combinations thereof.
  • Process parameters to directly or indirectly monitor, continuously or intermittently, during the process include, but are not limited to, irradiation intensity, temperature of carrier, polymerizable liquid in the build zone, temperature of growing product, temperature of build plate, pressure, speed of advance, pressure, force (e.g., exerted on the build plate through the carrier and product being fabricated), strain (e.g., exerted on the carrier by the growing product being fabricated), thickness of release layer, etc.
  • Known parameters that may be used in feedback and/or feed-forward control systems include, but are not limited to, expected consumption of polymerizable liquid (e.g., from the known geometry or volume of the article being fabricated), degradation temperature of the polymer being formed from the polymerizable liquid, etc.
  • Process conditions to directly or indirectly control, continuously or step-wise, in response to a monitored parameter, and/or known parameters include, but are not limited to, rate of supply of polymerizable liquid, temperature, pressure, rate or speed of advance of carrier, intensity of irradiation, duration of irradiation (e.g. for each “slice”), etc.
  • the temperature of the polymerizable liquid in the build zone, or the temperature of the build plate can be monitored, directly or indirectly with an appropriate thermocouple, non-contact temperature sensor (e.g., an infrared temperature sensor), or other suitable temperature sensor, to determine whether the temperature exceeds the degradation temperature of the polymerized product. If so, a process parameter may be adjusted through a controller to reduce the temperature in the build zone and/or of the build plate. Suitable process parameters for such adjustment may include: decreasing temperature with a cooler, decreasing the rate of advance of the carrier, decreasing intensity of the irradiation, decreasing duration of radiation exposure, etc.
  • the intensity of the irradiation source e.g., an ultraviolet light source such as a mercury lamp
  • a photodetector to detect a decrease of intensity from the irradiation source (e.g., through routine degradation thereof during use). If detected, a process parameter may be adjusted through a controller to accommodate the loss of intensity. Suitable process parameters for such adjustment may include: increasing temperature with a heater, decreasing the rate of advance of the carrier, increasing power to the light source, etc.
  • control of temperature and/or pressure to enhance fabrication time may be achieved with heaters and coolers (individually, or in combination with one another and separately responsive to a controller), and/or with a pressure supply (e.g., pump, pressure vessel, valves and combinations thereof) and/or a pressure release mechanism such as a controllable valve (individually, or in combination with one another and separately responsive to a controller).
  • a pressure supply e.g., pump, pressure vessel, valves and combinations thereof
  • a pressure release mechanism such as a controllable valve
  • the controller is configured to maintain the gradient of polymerization zone described herein (see, e.g., FIG. 1 ) throughout the fabrication of some or all of the final product.
  • the specific configuration e.g., times, rate or speed of advancing, radiation intensity, temperature, etc.
  • Configuration to maintain the gradient of polymerization zone may be carried out empirically, by entering a set of process parameters or instructions previously determined, or determined through a series of test runs or “trial and error”; configuration may be provided through pre-determined instructions; configuration may be achieved by suitable monitoring and feedback (as discussed above), combinations thereof, or in any other suitable manner.
  • Three-dimensional products produced by the methods and processes of the present invention may be final, finished or substantially finished products, or may be intermediate products subject to further manufacturing steps such as surface treatment, laser cutting, electric discharge machining, etc.
  • Intermediate products include products for which further additive manufacturing, in the same or a different apparatus, may be carried out).
  • a fault or cleavage line may be introduced deliberately into an ongoing “build” by disrupting, and then reinstating, the gradient of polymerization zone, to terminate one region of the finished product, or simply because a particular region of the finished product or “build” is less fragile than others.
  • Numerous different products can be made by the methods and apparatus of the present invention, including both large-scale models or prototypes, small custom products, miniature or microminiature products or devices, etc.
  • Examples include, but are not limited to, medical devices and implantable medical devices such as stents, drug delivery depots, functional structures, microneedle arrays, fibers and rods such as waveguides, micromechanical devices, microfluidic devices, etc.
  • the product can have a height of from 0.1 or 1 millimeters up to 10 or 100 millimeters, or more, and/or a maximum width of from 0.1 or 1 millimeters up to 10 or 100 millimeters, or more.
  • the product can have a height of from 10 or 100 nanometers up to 10 or 100 microns, or more, and/or a maximum width of from 10 or 100 nanometers up to 10 or 100 microns, or more.
  • the ratio of height to width of the product is at least 2:1, 10:1, 50:1, or 100:1, or more, or a width to height ratio of 1:1, 10:1, 50:1, or 100:1, or more.
  • the product has at least one, or a plurality of, pores or channels formed therein, as discussed further below.
  • the processes described herein can produce products with a variety of different properties.
  • the products are rigid; in other embodiments the products are flexible or resilient.
  • the products are a solid; in other embodiments, the products are a gel such as a hydrogel.
  • the products have a shape memory (that is, return substantially to a previous shape after being deformed, so long as they are not deformed to the point of structural failure).
  • the products are unitary (that is, formed of a single polymerizable liquid); in some embodiments, the products are composites (that is, formed of two or more different polymerizable liquids). Particular properties will be determined by factors such as the choice of polymerizable liquid(s) employed.
  • the product or article made has at least one overhanging feature (or “overhang”), such as a bridging element between two supporting bodies, or a cantilevered element projecting from one substantially vertical support body.
  • overhang such as a bridging element between two supporting bodies, or a cantilevered element projecting from one substantially vertical support body.
  • UV curable adhesive A drop of ultraviolet (UV) curable adhesive was placed on a metal plate and covered with 10 mm thick plate of TEFLON® AF fluoropolymer (a amorphous, glassy polymer) as shown in FIG. 5 a .
  • UV radiation was supplied to the adhesive from the side of Teflon AF as shown in FIG. 5 b . After UV exposure the two plates were separated. It was found that no force was required to separate the two plates.
  • the adhesive was cured only next to the metal plate, and that a thin film of uncured adhesive was present on the Teflon AF fluoropolymer plate and also on the cured portion of the adhesive as shown in FIG. 5 c.
  • FIGS. 5 d - 5 f Two controlled experiments were also performed where clean glass ( FIGS. 5 d - 5 f ) and also glass treated with release layer ( FIGS. 5 g - 5 i ) was used. It was confirmed that considerable force was needed to separate clean glass from the metal and it was found that adhesive remained on the glass. Less force was needed to separate the treated glass, while adhesive remained on the metal plate.
  • Teflon AF has a very high oxygen permeability coefficient. Constant supply of oxygen through 10 mm think Teflon AF is sufficient to prevent a thin layer of acrylate adhesive from polymerization.
  • the thickness of uncured adhesive layer in the above experiment was on the order of 10 microns and it can be increased or decreased by varying the amount of photo initiator present in the adhesive.
  • Samples 1 and 2 were prepared in a similar manner wherein a drop of UV curable adhesive was placed on a metal plate and covered with 10 mm thick plate of TEFLON® AF fluoropolymer as shown in FIG. 6 a . Both samples were exposed to a nitrogen environment to eliminate any presence of oxygen as shown in FIG. 6 b . Next both samples were brought into a standard atmosphere environment and Sample 1 was immediately exposed to UV radiation while Sample 2 was exposed to UV radiation 10 minutes after being in the atmosphere environment. Both samples were exposed to the same amount of UV radiation as shown in FIG. 6 C and FIG. 6 E . Upon examination of the samples after UV exposure it was discovered that the adhesive was cured completely in Sample 1 as shown in FIG. 6 D and only next to the metal plate in Sample 2 as shown in FIG.
  • a highly oxygen permeable, and UV transparent material is used as the bottom of a chamber filled with photocurable resin in a device of the invention.
  • the top of an object is attached to a support plate which is moved up at a substantially constant speed while the bottom portion of the object is constantly being formed just above the bottom of the chamber.
  • the gap between the bottom of the object and the bottom of the chamber is always filled with resin.
  • the resin in the gap is constantly replenished with supply resin contained in the chamber.
  • the speed of the object's formation depends on the viscosity of the resin ⁇ atmospheric pressure P, the height of the gap between the object and the bottom of the chamber h, and the linear dimension L of the object's bottom surface. Simple calculations are performed to estimate this speed using the theory of viscous flow between two parallel plates.
  • the time ⁇ which is required to fill the gap shown on FIG. 7 is given by the equation:
  • the gap of uncured resin can be controlled by altering the physical environment in the enclosed chamber contacting feed surface.
  • an atmosphere of pure oxygen, or enriched in oxygen e.g., 95% oxygen 5% carbon dioxide
  • oxygen e.g., 95% oxygen 5% carbon dioxide
  • the methods of the present invention can be used to make an elongate rod or fiber as shown in FIG. 9 , the rod or fiber having (for example) a width or diameter of 0.01 or 0.1 to 10 or 100 millimeters. While a circular cross-section is shown, any suitable cross-section can be utilized, including elliptical, polygonal (triangular, square, pentagonal, hexagonal, etc.) irregular, and combinations thereof.
  • the rod or fiber can have a plurality of elongated pores or channels formed therein (e.g., 1, 10, 100 1,000, 10,000 or 100,000 or more) of any suitable diameter (e.g., 0.1 or 1 microns, up to 10 or 100 microns or more) and any suitable cross-section as described above.
  • Unpolymerized liquid in the pores or channels can be removed (if desired) by any suitable technique, such as blowing, pressure, vacuum, heating, drying and combinations thereof.
  • the length of the rod or fiber can be increased by utilizing a take-up reel as described above, and the speed of fabrication of the rod or fiber can be increased by carrying out the polymerization under pressure as described above.
  • a plurality of such rods or fibers can be constructed concurrently from a single build plate by providing a plurality of independent carriers or take-up reels.
  • Such rods or fibers can be used for any purpose, such as utilizing each pore or channel therein as an independent channel in a microfluidic system.
  • An apparatus that can be used to carry out the present invention was assembled as described above, with a LOCTITETM UV Curing Wand System as the ultraviolet light source, a build plate comprised of 0.0025 inch thick Teflon AF 2400 film from Biogeneral clamped in a window and tensioned to substantial rigidity with a tensioning ring, optical components: from Newport Corporation, Edmund Optics, and Thorlabs, a DLP LightCrafter Development Kit from Texas Instruments as the digital projector, a THK Co., LTD ball screw linear stage serving as an elevator for the carrier, a continuous servo from Parallax Inc as the elevator and carrier drive or motor, a motion controller based on a Propeller microcontroller from Parallax Inc., a position controller based on a magnetic encoder from Austria Microsystems, motion control software written in SPIN language created by Parallax, open source Slic3r 3D slicing software, and image control software written using Qt framework and Visual C++.
  • the array of microneedles shown in FIG. 10 was made.
  • the carrier was advanced unidirectionally by the ball screw at a continuous rate of 10 microns per second and successive exposures were carried out every 2 microns along the building height at a duration of 0.2 seconds per exposure.
  • the total number of successive exposures was 350 and the total fabrication time was 70 seconds.
  • the 2000 micron microneedle array shown in FIG. 11 was made in like manner as described in example 6 above, with 1000 successive exposures over a total fabrication time of 200 seconds.
  • microneedles for example with microneedles having widths of from 5 to 500 micrometers and heighths of 5 to 2000 micrometers or more, can be fabricated in like manner. While a square cross-section is shown, any suitable cross-section can be utilized, including circular, elliptical, polygonal (triangular, rectangular, pentagonal, hexagonal, etc.) irregular, and combinations thereof.
  • the spacing between microneedles can be varied as desired, for example from 5 to 100 micrometers, and the microneedles or other microstructures can be arranged with respect to one another in any suitable pattern, e.g., square, rectangular, hexagonal, etc.
  • a ring was fabricated using the apparatus described in Example 5 above, trimethylolpropane triacrylate as the polymerizable liquid, and Diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide as photoinitiator.
  • the carrier was advanced unidirectionally by the ball screw at a continuous rate of 20 microns per second and successive exposures were carried every 10 microns along the building height at a duration of 0.5 seconds per exposure. The total number of successive exposures was 1040 and the total fabrication time was 520 seconds.
  • FIG. 12 shows the ring during fabrication
  • FIG. 13 shows the ring after fabrication. Note the absence of supports for extensively overhung elements during fabrication.
  • the chess piece shown in FIG. 14 was made using the apparatus described in the examples above, trimethylolpropane triacrylate as the polymerizable liquid, and Diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide as photoinitiator.
  • the carrier was advanced unidirectionally by the ball screw at a continuous rate of 20 microns per second and successive exposures were carried every 10 microns along the building height at a duration of 0.5 seconds per exposure. The total number of successive exposures was 1070 and the total fabrication time was 535 seconds.
  • the ribbed rectangular prism shown in FIG. 15 was made using the apparatus described in the Examples above, trimethylolpropane triacrylate as the polymerizable liquid, and Diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide as the photoinitiator.
  • the carrier was advanced unidirectionally by the worm gear at a continuous rate of 20 microns per second and successive exposures were carried every 10 microns along the building height at a duration of 0.5 second per exposure.
  • the total number of successive exposures was 800 and the total fabrication time was 400 seconds.
  • the coil or spiral shown in FIG. 16 was made using the apparatus described in the examples above, trimethylolpropane triacrylate as the polymerizable liquid, and Diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide as the photoinitiator.
  • the carrier was advanced unidirectionally by the ball screw at a continuous rate of 20 microns per second and successive exposures were carried every 10 microns along building height at a duration of 0.5 seconds per exposure. The total number of successive exposures was 970 and the total fabrication time was 485 seconds.
  • FIG. 18 A chess piece made with such a dye-containing resin is shown in FIG. 18 .
  • a deficiency of prior techniques is that the requirement to “break” adhesion from the build plate, e.g., by sliding the build plate, or by using an elastic build plate, made it problematic to employ a release layer or soluble adhesive layer on the carrier that might prematurely fail during the fabrication process.
  • the present invention facilitates the employment of a release layer on the carrier during fabrication.
  • the surface of the carrier can be coated with a release layer, i.e., a soluble sacrificial layer (e.g., cyanoacrylate adhesive), and array of objects can be printed as shown in FIG. 19 .
  • a release layer i.e., a soluble sacrificial layer (e.g., cyanoacrylate adhesive)
  • Any suitable thickness of release layer can be used, for example from 100 nanometers to 1 millimeter.
  • Submerging the carrier with the fabricated objects into an appropriate solvent (e.g., acetone for cyanoacrylate adhesive) that selectively dissolves or solubilizes the release layer then releases the objects from the carrier as shown in FIG. 20 .
  • the array of rectangular prisms with dimensions of 200 ⁇ 200 ⁇ 1000 micrometers shown in FIG. 21 was made using the apparatus described above, trimethylolpropane triacrylate as the polymerizable liquid, diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide as the photoinitiator, and cyanoacrylate adhesive as release layer.
  • the carrier was advanced by the ball screw at a continuous rate of 10 microns per second and successive exposures were carried every 10 microns along the building height at a duration of 1 second per exposure. The total number of successive exposures was 100 and the total fabrication time was 100 seconds.
  • the cyanoacrylate release layer was then dissolved by acetone to produce free floating prisms as shown in FIG. 22 .
  • the cylindrical cage structure of FIG. 23 was made using the apparatus described in the Example above, trimethylolpropane triacrylate as the polymerizable liquid, and diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide as photoinitiator.
  • the carrier was advanced by the ball screw at a continuous rate of 20 microns per second and successive exposures were carried out every 10 micron along the building height at a duration of 0.5 seconds per exposure.
  • the total number of successive exposures was 1400 and the total fabrication time was 700 seconds. No removable supporting structures for cantilevered features or “overhangs” were used.
  • FIG. 24 and FIG. 25 are photographs of array structures and cage structures, respectively, produced in like manner as those described above, except that they were fabricated using PEG (Poly(ethylene glycol) diacrylate, average Mn 700) as the polymerizable liquid and 5% of Diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide as the photoinitiator. Processing conditions were otherwise the same as for the previously fabricated triacrylate parts.
  • PEG Poly(ethylene glycol) diacrylate, average Mn 700
  • Diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide Diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide
  • the cylindrical cage structure produced in Example 23 above and shown in FIG. 25 was manually positioned between two glass microscope slides and pressure manually applied until the cylindrical cage structure was deformed and substantially flat. Manual pressure was then released, and the cage structure returned to its previous substantially cylindrical form.
  • the flexibility, resiliency, and shape memory properties of the articles make them attractive for a variety of uses, including but not limited to stents for various biomedical applications.
  • Stents are typically used as adjuncts to percutaneous transluminal balloon angioplasty procedures, in the treatment of occluded or partially occluded arteries and other blood vessels.
  • a guiding catheter or sheath is percutaneously introduced into the cardiovascular system of a patient through a femoral artery and advanced through the vasculature until the distal end of the guiding catheter is positioned at a point proximal to the lesion site.
  • a guidewire and a dilatation catheter having a balloon on the distal end are introduced through the guiding catheter with the guidewire sliding within the dilatation catheter.
  • the guidewire is first advanced out of the guiding catheter into the patient's vasculature and is directed across the vascular lesion.
  • the dilatation catheter is subsequently advanced over the previously advanced guidewire until the dilatation balloon is properly positioned across the vascular lesion.
  • the expandable balloon is inflated to a predetermined size with a radiopaque liquid at relatively high pressure to radially compress the atherosclerotic plaque of the lesion against the inside of the artery wall and thereby dilate the lumen of the artery.
  • the balloon is then deflated to a small profile so that the dilatation catheter can be withdrawn from the patient's vasculature and blood flow resumed through the dilated artery.
  • Balloon angioplasty sometimes results in short or long term failure. That is, vessels may abruptly close shortly after the procedure or restenosis may occur gradually over a period of months thereafter.
  • implantable intraluminal prostheses commonly referred to as stents, are used to achieve long term vessel patency.
  • a stent functions as scaffolding to structurally support the vessel wall and thereby maintain luminal patency, and are transported to a lesion site by means of a delivery catheter.
  • Types of stents may include balloon expandable stents, spring-like, self-expandable stents, and thermally expandable stents.
  • Balloon expandable stents are delivered by a dilation catheter and are plastically deformed by an expandable member, such as an inflation balloon, from a small initial diameter to a larger expanded diameter.
  • Self-expanding stents are formed as spring elements which are radially compressible about a delivery catheter. A compressed self-expanding stent is typically held in the compressed state by a delivery sheath. Upon delivery to a lesion site, the delivery sheath is retracted allowing the stent to expand.
  • Thermally expandable stents are formed from shape memory alloys which have the ability to expand from a small initial diameter to a second larger diameter upon the application of heat to the alloy.
  • Intraluminal prostheses such as stents have been developed using various polymeric materials and/or coatings of polymeric materials to overcome the limitations of conventional metallic prostheses.
  • various mechanical properties e.g., modulus, hoop strength, flexibility, etc.
  • intraluminal prostheses used to deliver pharmacological agents it would be desirable to be able to adjust the elution rate of a pharmacological agent therefrom.
  • methods of manufacturing polymeric intraluminal prostheses include annealing the polymeric material to selectively modify the crystallinity or crystalline structure thereof is accomplished by the methods described herein, including but not limited to those set forth in connection with cylindrical cage structures as described above.
  • Pharmacological agents disposed on or within the polymeric material may include, but are not limited to, agents selected from the following categories: antineoplastics, antimitotics, antimflammatories, antiplatelets, anticoagulants, antifibrins, antithrombins, antiproliferatives, antibiotics, antioxidants, immunosuppressives, antiallergic substances, and combinations thereof.
  • the degree of molecular crosslinking of the polymeric material of an intraluminal prostheses may be modified by subjecting the polymeric material to chemical treatment and/or irradiation.
  • the polymeric material may be subjected to chemical treatment and/or irradiation before, during and/or after annealing. Such treatments may also act as a sterilization step.
  • hypodermic injection including intravascular, intramuscular, etc.
  • hypodermic needles do not deliver doses to the optimum location to elicit an immune response; they penetrate into muscle, a region known to have a lower density of immunologically sensitive cells than skin.
  • Transdermal patches are effective for select time-released drugs (like nicotine and motion sickness medications), but the epidermis (specifically the stratum corneum) limits the diffusion of most drugs (>500 Da) through the skin. Clearly, the ability to transport therapeutics effectively into the body remains a significant challenge.
  • controller image processing unit in some embodiments is constantly updating images of cross sectional layers of the part.
  • the maximum speed of image update f can in some embodiments vary from 1 frame per second up to 1000 frames per second, depending on the hardware.
  • the advancement dz of the part carrier during one image frame should be less than delta. If the fabrication speed is v then dz is given by
  • fabrication speed v should be less than the maximum fabrication speed v max given by
  • Two chess piece parts similar to those illustrated above were made with a carrier advancement speed of 250 mm/hour and 500 mm/hour.
  • the maximum frame rate of the particular IPU used to make the parts was approximately 1 frame per second.
  • the estimated resolution of these parts was 50 micrometers at 250 mm/hour, and 100 micrometer at 500 mm/hour.
  • fabrication rate can be increased by heating the polymerizable liquid, or resin, to reduce the viscosity thereof, to facilitate filling of the build zone with the polymerizable liquid or migration of the polymerizable liquid into the build zone (with or without increased pressure).
  • Some resins, such as high performance resins including those noted above, may be solid at room temperature and pressure, and heating may be a convenient way to liquefy the same.
  • Heating may be carried out by any suitable technique, such as with closed-oven infrared heaters operatively associated with a temperature sensor and controller, as schematically illustrated in FIG. 26 .
  • Resistive heaters may be used, for example submersed in the polymerizable liquid on the build plate.
  • Thermoelectric devices or Peltier heaters can be used, for example contacting the build plate and/or the polymerizable liquid.
  • the polymerizable liquid can be pre-heated, in a storage reservoir and/or through various feed lines.
  • One or more temperature sensors can be employed to detect ambient (in chamber) temperature, build plate temperature, carrier temperature, polymerizable liquid temperature (e.g., at any point, such as on the build plate), etc.
  • the polymerizable liquid is heated by at least 5, 10, 20, 40, 60, 80, or 100 degrees Centigrade or more above room temperature.
  • such polymerizable liquids can have a viscosity when heated (e.g., by the amount described above) of not more than 1,000, 100, 10 or 1 centipoise. Specific end viscosity desired to be achieved will depend on factors such as the rate of fabrication desired, size and shape of the article being fabricated, the presence or absence of increased pressure, etc.
  • Viscosity can be measured by any suitable technique, for example by a Brookfield viscometer having a cone and plate geometry, with a cone angle of 1 degree, a 40 millimeter diameter, operated at 60 revolutions per minute.
  • Coolers can optionally be included if desired to more rapidly correct temperature (with heaters, or without heaters, e.g., to aid in dissipating heat generated exothermically by rapid photopolymerization.
  • any suitable cooler configuration can be used, generally operatively associated with a controller and temperature sensor as noted above.
  • Heat exchangers, heat sinks, refrigerants, thermoelectric devices such as Peltier coolers (which may also serve as Peltier heaters), etc. may be employed.
  • the speed of the object's formation depends on the linear dimension L of the object's bottom surface, viscosity of the resin ⁇ , atmospheric pressure P, and the height of the gap between the object and the bottom of the chamber h.
  • the time ⁇ which is required to fill the gap between the object and the bottom of the chamber is:
  • polymerizable liquid or resin
  • the pump can comprise any suitable pumping device, including but not limited to syringe pumps, gear pumps, peristaltic pumps, etc.
  • the rate at which pump operates is controlled by a controller and depends on part geometry and speed of fabrication.
  • viscosity of the resin atmospheric pressure P, and the height of the gap between the object and the bottom of the chamber h is no longer limited by above equation but it is rather controlled by the rate at which resin pump operates, the rate of the curing reaction and the ability to mitigate heat removal from the curing reaction.
  • the pump in this example could comprise a syringe pump, gear pump, or peristaltic pump.
  • the pump operation could be included into feedback loop controlled by central processing unit where pumping rates depend on part geometry and desired fabrication speed.
  • resin delivery rate changes based on the cross sectional area of the part.
  • a process to control resin delivery rate is described below. If the build speed is v and the cross section of the part A varies with time t as AO then resin delivery rate can be adjusted to correspond, in whole or in part, to:
  • a central processing unit (CPU) serving as a controller can in real time calculate the current cross section of the part, then calculate delivery rate based on a rule such as the equation above and communicate the calculated rate to a resin delivery pump controller (RDPC).
  • the RDPC can then adjust the speed of the resin delivery pump based on the data received from CPU.
  • feed-forward control system can be used alone or in combination with other feed forward and feed-back control systems (e.g., temperature and/or pressure control) as described above.
  • feed forward and feed-back control systems e.g., temperature and/or pressure control
  • polymerizable liquid is supplied through one or more channels formed in the carrier, it may be desired that some, or all, of the article being fabricated be solid throughout. In such cases, separate or external feed conduits in fluid communication with a (or each) channel supplying polymerizable liquid may be concurrently fabricated adjacent the article being fabricated (In contrast to one or more internal feed channels formed within the article being produced.
  • the polymerizable liquid can then be provided through the external feed conduit(s) to the build plate and fabrication zone.
  • multiple such feed conduits may be constructed, e.g., 2, 10, 100, or 1000 or more, depending on the size of the article being fabricated.
  • Such external feed conduits may be used in combination, concurrently or sequentially (e.g., alternatively), with internal feed channels (i.e., channels formed within the article being fabricated).
  • Articles can be fabricated using multiple resins by feeding the different resins through the build platform, and using them to create tubes or channels to deliver the resin to the correct area of the part being fabricated.
  • FIG. 28 illustrates the method that can be used to feed resin through the build platform, use it to fabricate the resin delivery channels in the necessary shape, and when necessary, feed extra resin to fabricate the part itself.
  • the channel is cured shut and another channel can begin feeding the next resin to continue fabricating the part.
  • a method and apparatus as described above may be controlled by a software program running in a general purpose computer with suitable interface hardware between that computer and the apparatus described above. Numerous alternatives are commercially available. Non-limiting examples of one combination of components is shown in FIGS. 29 - 31 , where “Microcontroller” is Parallax Propeller, the Stepper Motor Driver is Sparkfun EasyDriver, the LED Driver is a Luxeon Single LED Driver, the USB to Serial is a Parallax USB to Serial converter, and the DLP System is a Texas Instruments LightCrafter system.
US17/513,312 2013-02-12 2021-10-28 Method and apparatus for three-dimensional fabrication Pending US20230373156A9 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US17/513,312 US20230373156A9 (en) 2013-02-12 2021-10-28 Method and apparatus for three-dimensional fabrication

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
US201361763746P 2013-02-12 2013-02-12
US201361865841P 2013-08-14 2013-08-14
PCT/US2014/015486 WO2014126830A2 (en) 2013-02-12 2014-02-10 Method and apparatus for three-dimensional fabrication
US14/572,128 US9211678B2 (en) 2013-02-12 2014-12-16 Method and apparatus for three-dimensional fabrication
US14/937,151 US10093064B2 (en) 2013-02-12 2015-11-10 Method for three-dimensional fabrication
US16/105,378 US10596755B2 (en) 2013-02-12 2018-08-20 Method for three-dimensional fabrication
US16/824,077 US11235516B2 (en) 2013-02-12 2020-03-19 Method and apparatus for three-dimensional fabrication
US17/513,312 US20230373156A9 (en) 2013-02-12 2021-10-28 Method and apparatus for three-dimensional fabrication

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
US16/824,077 Continuation US11235516B2 (en) 2013-02-12 2020-03-19 Method and apparatus for three-dimensional fabrication

Publications (2)

Publication Number Publication Date
US20220048242A1 US20220048242A1 (en) 2022-02-17
US20230373156A9 true US20230373156A9 (en) 2023-11-23

Family

ID=50156961

Family Applications (1)

Application Number Title Priority Date Filing Date
US17/513,312 Pending US20230373156A9 (en) 2013-02-12 2021-10-28 Method and apparatus for three-dimensional fabrication

Country Status (12)

Country Link
US (1) US20230373156A9 (de)
EP (2) EP3358405A1 (de)
JP (1) JP6423801B2 (de)
KR (1) KR20150117274A (de)
CN (1) CN105122136B (de)
BR (1) BR112015018105A2 (de)
CA (1) CA2898098A1 (de)
DK (1) DK2956821T3 (de)
ES (1) ES2667676T3 (de)
HK (1) HK1215475A1 (de)
MX (1) MX350841B (de)
WO (1) WO2014126830A2 (de)

Families Citing this family (105)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9841750B2 (en) 2014-05-13 2017-12-12 Autodesk, Inc. Dynamic real-time slice engine for 3D printing
US9782934B2 (en) 2014-05-13 2017-10-10 Autodesk, Inc. 3D print adhesion reduction during cure process
US10073424B2 (en) 2014-05-13 2018-09-11 Autodesk, Inc. Intelligent 3D printing through optimization of 3D print parameters
JP6720092B2 (ja) 2014-06-23 2020-07-08 カーボン，インコーポレイテッド 多様な硬化機構を有する材料からのポリウレタン三次元物体製造方法
US9975295B2 (en) 2014-08-12 2018-05-22 Carbon, Inc. Acceleration of stereolithography
US10166725B2 (en) 2014-09-08 2019-01-01 Holo, Inc. Three dimensional printing adhesion reduction using photoinhibition
ES2819229T3 (es) * 2014-11-10 2021-04-15 Univ Berlin Tech Procedimiento y dispositivo para producir un objeto multicelular tridimensional
US20160167301A1 (en) * 2014-12-12 2016-06-16 Autodesk, Inc. Polymeric photoinitiators for 3d printing applications
WO2016126779A1 (en) * 2015-02-05 2016-08-11 Carbon3D, Inc. Method of additive manufacturing by fabrication through multiple zones
CN107438513B (zh) * 2015-02-05 2020-12-29 卡本有限公司 通过间歇曝光的增材制造方法
US11000992B2 (en) 2015-02-20 2021-05-11 Carbon, Inc. Methods and apparatus for continuous liquid interface printing with electrochemically supported dead zone
US10391711B2 (en) * 2015-03-05 2019-08-27 Carbon, Inc. Fabrication of three dimensional objects with multiple operating modes
WO2016149151A1 (en) * 2015-03-13 2016-09-22 Carbon3D, Inc. Three-dimensional printing with concurrent delivery of different polymerizable liquids
EP3290186A4 (de) * 2015-04-28 2019-01-02 Gold Array Technology Beijing LLC Lichthärtender 3d-drucker und 3d-druckverfahren
WO2016172805A1 (en) * 2015-04-30 2016-11-03 Fortier, Raymond Improved stereolithography system
WO2016172804A1 (en) * 2015-04-30 2016-11-03 Fortier, Raymond Improved stereolithography system
WO2016172788A1 (en) * 2015-04-30 2016-11-03 Fortier, Raymond Improved stereolithography system
WO2016172784A1 (en) * 2015-04-30 2016-11-03 Fortier, Raymond Improved stereolithography system
US10471655B2 (en) * 2015-09-04 2019-11-12 Carbon, Inc. Cyanate ester dual resins for additive manufacturing
EP3347399B1 (de) * 2015-09-09 2020-12-09 Carbon, Inc. Doppelhärtende epoxidharze zur generativen fertigung
WO2017059082A1 (en) * 2015-09-30 2017-04-06 Carbon, Inc. Method and apparatus for producing three-dimensional objects
ITUB20154169A1 (it) 2015-10-02 2017-04-02 Thelyn S R L Metodo e apparato di foto-indurimento a substrato auto-lubrificante per la formazione di oggetti tridimensionali.
US11141919B2 (en) 2015-12-09 2021-10-12 Holo, Inc. Multi-material stereolithographic three dimensional printing
WO2017112653A1 (en) * 2015-12-22 2017-06-29 Carbon, Inc. Dual precursor resin systems for additive manufacturing with dual cure resins
WO2017112483A2 (en) * 2015-12-22 2017-06-29 Carbon, Inc. Accelerants for additive manufacturing with dual cure resins
US10343331B2 (en) 2015-12-22 2019-07-09 Carbon, Inc. Wash liquids for use in additive manufacturing with dual cure resins
WO2017116990A1 (en) 2015-12-31 2017-07-06 Formlabs, Inc. Systems and methods of flexible substrates for additive fabrication
CN105797266A (zh) * 2016-03-07 2016-07-27 李媚 一种微结构体及其制备方法
JP6792835B2 (ja) * 2016-03-11 2020-12-02 ナガセケムテックス株式会社 光造形用トレイ
US11465339B2 (en) 2016-05-31 2022-10-11 Northwestern University Method for the fabrication of three-dimensional objects and apparatus for same
JP7169270B2 (ja) 2016-06-20 2022-11-10 ビー９クリエーションズ エルエルシー 三次元付加製造生産時間を削減するためのシステムおよび方法
CN106079495B (zh) * 2016-06-22 2018-09-25 西安理工大学 面曝光3d打印约束基板防粘附增透功能膜及其制备方法
CN106042388A (zh) * 2016-07-25 2016-10-26 东莞中国科学院云计算产业技术创新与育成中心 3d打印装置及其系统控制方法与其工作方法
US10241401B2 (en) * 2016-08-01 2019-03-26 Macdermid Graphics Solutions Llc Method of making a flexographic printing plate
US11130286B2 (en) 2016-09-07 2021-09-28 Canon Kabushiki Kaisha Three-dimensional manufacturing apparatus, three-dimensional manufactured object producing method, and container for three-dimensional manufacturing apparatus
JP6866152B2 (ja) * 2016-12-22 2021-04-28 キヤノン株式会社 三次元造形装置および三次元造形方法
JP6844623B2 (ja) 2016-09-28 2021-03-17 Ａｇｃ株式会社 モノマー組成物および含フッ素ポリマーの製造方法
US11117316B2 (en) 2016-11-04 2021-09-14 Carbon, Inc. Continuous liquid interface production with upconversion photopolymerization
WO2018083500A1 (en) * 2016-11-07 2018-05-11 The University Of Nottingham Additive manufacturing
EP3538367A4 (de) 2016-11-08 2020-07-01 Formlabs, Inc. Multimaterialtrennschichten zur generativen fertigung
PL3548523T3 (pl) * 2016-12-05 2022-11-28 Covestro Deutschland Ag Sposób i system wytwarzania obiektu poprzez strukturę warstwową w procesie tłoczenia
DE102016225652A1 (de) 2016-12-20 2018-06-21 Piezocryst Advanced Sensorics Gmbh Verfahren zur Herstellung eines Sensorgehäuses für einen Kraft- oder Drucksensor sowie Sensorgehäuse, Kraft- oder Drucksensor und Verwendung einer additiven Fertigungsvorrichtung
US10935891B2 (en) 2017-03-13 2021-03-02 Holo, Inc. Multi wavelength stereolithography hardware configurations
JP7195267B2 (ja) * 2017-03-30 2022-12-23 ダウ シリコーンズ コーポレーション 多孔質シリコーン物品の製造方法及びシリコーン物品の使用
KR101973259B1 (ko) * 2017-04-11 2019-04-26 울산과학기술원 3차원 구조체의 제조방법 및 그를 이용한 3차원 구조체
US10429736B2 (en) * 2017-04-27 2019-10-01 Macdermid Graphics Solutions Llc Method of making a flexographic printing plate
EP3396455B1 (de) 2017-04-28 2022-10-05 Technische Universität Wien Lichthärtbare zusammensetzung
US10316213B1 (en) 2017-05-01 2019-06-11 Formlabs, Inc. Dual-cure resins and related methods
IT201700050248A1 (it) * 2017-05-09 2018-11-09 Graf Synergy Srl Procedimento per la stampa tridimensionale, particolarmente per la realizzazione di finestre, elementi lastriformi per pavimenti o simili
GB2564956B (en) 2017-05-15 2020-04-29 Holo Inc Viscous film three-dimensional printing systems and methods
CN107042940B (zh) * 2017-06-09 2018-09-14 苏州三峰激光科技有限公司 存储罐及3d打印装置
US10245785B2 (en) 2017-06-16 2019-04-02 Holo, Inc. Methods for stereolithography three-dimensional printing
US11084222B2 (en) 2017-06-30 2021-08-10 Autodesk, Inc. Systems and methods for determining dynamic forces in a liquefier system in additive manufacturing
WO2019009906A1 (en) * 2017-07-06 2019-01-10 Hewlett-Packard Development Company, L.P. PRINTING IN THREE DIMENSIONS (3D)
US10688737B2 (en) * 2017-09-14 2020-06-23 General Electric Company Method for forming fiber-reinforced polymer components
JPWO2019059184A1 (ja) * 2017-09-22 2020-10-15 コニカミノルタ株式会社 樹脂組成物、およびこれを用いた立体造形物の製造方法、立体造形物、ならびに対象物把持用アタッチメントおよびこれを用いた産業用ロボット
US11692093B2 (en) 2017-09-22 2023-07-04 Konica Minolta, Inc. Resin composition, method for producing three-dimensional molding using same, and three-dimensional molding
JP7309315B2 (ja) * 2017-09-22 2023-07-18 コニカミノルタ株式会社 樹脂組成物、およびこれを用いた立体造形物の製造方法、ならびに立体造形物
US20200333704A1 (en) * 2017-10-17 2020-10-22 Canon Kabushiki Kaisha Imprint apparatus and article manufacturing method
US11772323B2 (en) 2017-12-14 2023-10-03 Carnegie Mellon University Directed polymerization method to generate complex, three dimensional (3D) structures in soft materials
WO2019140160A1 (en) * 2018-01-12 2019-07-18 University Of Florida Research Foundation, Inc. Three-dimensional fabrication at inert immiscible liquid interface
PL234153B1 (pl) 2018-02-26 2020-01-31 Chuptys Janusz Contissi Drukarka do druku przestrzennego
WO2019167895A1 (ja) * 2018-03-01 2019-09-06 コニカミノルタ株式会社 樹脂組成物、およびこれを用いた立体造形物の製造方法、ならびに立体造形物
CN110281523B (zh) * 2018-03-19 2021-09-21 比亚迪股份有限公司 用于光固化成型的3d打印装置及其载物台
EP3552806A1 (de) * 2018-04-09 2019-10-16 Nederlandse Organisatie voor toegepast- natuurwetenschappelijk onderzoek TNO Verfahren und vorrichtung zur herstellung eines objekts mittels generativer fertigung
JP7163958B2 (ja) * 2018-04-17 2022-11-01 コニカミノルタ株式会社 重合性組成物及び立体造形物の製造方法
WO2019214552A1 (zh) * 2018-05-05 2019-11-14 宁波市石生科技有限公司 阻粘元件、三维打印装置及三维打印方法
JP2021523036A (ja) * 2018-05-07 2021-09-02 フォームラブス, インコーポレーテッドFormlabs, Inc. 積層造形のための多材料分離層
JP7173137B2 (ja) * 2018-05-23 2022-11-16 コニカミノルタ株式会社 立体造形用重合性組成物、およびこれを用いた立体造形物の製造方法、ならびに立体造形物
CN116009350A (zh) 2018-06-01 2023-04-25 福姆实验室公司 改进的立体光刻技术及相关系统和方法
JP7393367B2 (ja) * 2018-06-26 2023-12-06 アルケマ フランス 多段ポリマーをベースとする硬化性組成物
JP7350836B2 (ja) 2018-07-18 2023-09-26 アルケマ フランス 重合性イオン種をベースとする硬化性組成物を用いて調製された物品
FR3085682B1 (fr) 2018-09-11 2020-10-16 Arkema France Compositions reticulables ayant une faible viscosite pour revetements et materiaux a haut indice de refraction et a temperature de deflexion thermique elevee
FR3090296B1 (fr) 2018-12-19 2020-12-11 Oreal Applicateur pour appliquer un produit cosmétique sur les cils et/ou sourcils.
FR3090300B1 (fr) 2018-12-19 2021-08-06 Oreal Applicateur pour appliquer un produit cosmétique sur les cils et/ou sourcils.
FR3090295B1 (fr) 2018-12-19 2021-09-10 Oreal Procédé de génération d’un modèle numérique d’applicateur de produit cosmétique
FR3090298B1 (fr) 2018-12-19 2021-04-30 Oreal Applicateur pour appliquer un produit cosmétique (F) sur les cils et/ou sourcils.
FR3090299B1 (fr) 2018-12-19 2021-04-30 Oreal Applicateur comportant un organe d’application fabriqué par synthèse additive
FR3090297B1 (fr) 2018-12-19 2021-10-15 Oreal Applicateur cosmétique en spirale
FR3090294B1 (fr) 2018-12-19 2021-04-30 Oreal Applicateur pour appliquer un produit cosmétique sur les cils et/ou sourcils
FR3090301B1 (fr) 2018-12-19 2021-05-14 Oreal Applicateur comportant un organe d’application à branche ouverte
WO2020139858A1 (en) 2018-12-26 2020-07-02 Holo, Inc. Sensors for three-dimensional printing systems and methods
JP2022515664A (ja) 2018-12-31 2022-02-21 アルケマ フランス （メタ）アクリレート官能化分岐ポリアルファオレフィン
CN112789127B (zh) * 2019-02-27 2023-11-07 惠普发展公司，有限责任合伙企业 用于3d打印生坯部件的固化时间
FR3095443B1 (fr) 2019-04-26 2021-03-19 Arkema France Compositions réticulables ayant une faible viscosité pour revêtements et matériaux à haut indice de réfraction et à température de déflexion thermique élevée
JP2022541473A (ja) 2019-07-17 2022-09-26 アルケマ フランス （メタ）アクリレート官能化オリゴマー並びにそのようなオリゴマーを調製及び使用する方法
US20220298131A1 (en) 2019-07-31 2022-09-22 Arkema France Method of making glycerol carbonate (meth)acrylate and curable compositions based thereon
EP4048712A1 (de) 2019-10-23 2022-08-31 Arkema France Multi(meth)acrylat-funktionalisierte oligomere und verfahren zu ihrer herstellung und verwendung
FR3105791B1 (fr) 2019-12-31 2022-12-16 Arkema France Composition réticulable comprenant un mono(méth)acrylate ayant un cycle 1,3-dioxolane
EP3876034A1 (de) 2020-03-04 2021-09-08 Arkema France Härtbare zusammensetzung mit einem photoinitiator
EP3875552A1 (de) 2020-03-04 2021-09-08 Lambson Limited Photoinitiator emulsionen
FR3108908B1 (fr) 2020-04-01 2022-03-25 Arkema France Matériaux élastiques préparés à partir de compositions liquides durcissables
FR3108907B1 (fr) 2020-04-01 2022-07-08 Arkema France Matériaux élastiques préparés à partir de compositions liquides durcissables par énergie
FR3111637B1 (fr) 2020-06-18 2022-09-02 Arkema France Compositions et procédés de formation de matériaux imprimables 3d capables d’une faible perte diélectrique
FR3111902B1 (fr) 2020-06-30 2023-03-10 Arkema France Oligomères contenant un amide fonctionnalisés par (méth)acrylate
US11413819B2 (en) 2020-09-03 2022-08-16 NEXA3D Inc. Multi-material membrane for vat polymerization printer
FR3118051A1 (fr) 2020-12-21 2022-06-24 Arkema France Compositions durcissables par rayonnement actinique contenant un polyamide
FR3118965B1 (fr) 2021-01-20 2023-12-01 Arkema France Thioxanthone polymérisable
EP4053115A1 (de) 2021-03-01 2022-09-07 Arkema France Flüssige typ-ii-photoinitiatoren
EP4151410A1 (de) 2021-09-17 2023-03-22 Arkema France Lichtempfindliche zusammensetzung
EP4177282A1 (de) 2021-11-04 2023-05-10 Arkema France Urethan-(meth)acrylat auf der basis von polyglycerin
FR3131585A1 (fr) 2021-12-30 2023-07-07 Arkema France Époxydes cycloaliphatiques polymériques
EP4206183A1 (de) 2021-12-31 2023-07-05 Arkema France Polyhydroxylierte photoinitiatoren
EP4249518A1 (de) 2022-03-25 2023-09-27 Arkema France Polymerisierbare fotoinitiatoren
IT202200009341A1 (it) * 2022-05-06 2023-11-06 Materias S R L Processo per la produzione di una struttura tridimensionale

Family Cites Families (54)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
USRE31406E (en) 1972-06-16 1983-10-04 Syntex (U.S.A.) Inc. Oxygen permeable contact lens composition, methods and article of manufacture
US4337130A (en) 1980-06-25 1982-06-29 E. I. Du Pont De Nemours And Company Photocurable polyurethane film coatings
US5236637A (en) 1984-08-08 1993-08-17 3D Systems, Inc. Method of and apparatus for production of three dimensional objects by stereolithography
DE3616681A1 (de) 1986-05-16 1987-11-19 Bayer Ag 1-aralkylpyrazole
US5051115A (en) 1986-05-21 1991-09-24 Linde Aktiengesellschaft Pressure swing adsorption process
US5141665A (en) 1987-03-31 1992-08-25 Sherman Laboratories, Inc. Cleaning, conditioning, storing and wetting system and method for rigid gas permeable contact lenses and other contact lenses
US4923906A (en) 1987-04-30 1990-05-08 Ciba-Geigy Corporation Rigid, gas-permeable polysiloxane contact lenses
US5070170A (en) 1988-02-26 1991-12-03 Ciba-Geigy Corporation Wettable, rigid gas permeable, substantially non-swellable contact lens containing block copolymer polysiloxane-polyoxyalkylene backbone units, and use thereof
JPH01233443A (ja) 1988-03-15 1989-09-19 Fujitsu Ltd パターン形成方法
GB9008577D0 (en) 1990-04-17 1990-06-13 Pilkington Diffractive Lenses Rigid gas permeable lenses
US5122441A (en) * 1990-10-29 1992-06-16 E. I. Du Pont De Nemours And Company Method for fabricating an integral three-dimensional object from layers of a photoformable composition
US5162469A (en) 1991-08-05 1992-11-10 Optical Research Inc. Composition for rigid gas permeable contact lenses
US5296283A (en) 1992-01-13 1994-03-22 E. I. Du Pont De Nemours And Company Protective coating for machine-readable markings
DE69329594T2 (de) 1992-02-28 2001-05-31 Univ Texas Photopolymerinierbare, biologisch abbaubare hydrogele als gewebekontaktmaterialien und trägerstoffe für kontrollierte freisetzung
US5310571A (en) 1992-09-01 1994-05-10 Allergan, Inc. Chemical treatment to improve oxygen permeability through and protein deposition on hydrophilic (soft) and rigid gas permeable (RGP) contact lenses
US5836313A (en) 1993-02-08 1998-11-17 Massachusetts Institute Of Technology Methods for making composite hydrogels for corneal prostheses
US5374500A (en) 1993-04-02 1994-12-20 International Business Machines Corporation Positive photoresist composition containing photoacid generator and use thereof
JPH07299874A (ja) * 1994-04-28 1995-11-14 Hikari Syst Kenkyusho:Kk 高ｎａ光学系を用いた光造形装置
JPH08150662A (ja) * 1994-11-30 1996-06-11 Olympus Optical Co Ltd 粉末混合光硬化性樹脂を用いた光造形装置及び光造形方法
US5691541A (en) 1996-05-14 1997-11-25 The Regents Of The University Of California Maskless, reticle-free, lithography
US6312134B1 (en) 1996-07-25 2001-11-06 Anvik Corporation Seamless, maskless lithography system using spatial light modulator
JPH10249943A (ja) * 1997-03-10 1998-09-22 Hitachi Ltd 光造形装置
US6238852B1 (en) 1999-01-04 2001-05-29 Anvik Corporation Maskless lithography system and method with doubled throughput
US6248509B1 (en) 1999-07-27 2001-06-19 James E. Sanford Maskless photoresist exposure system using mems devices
JP3433158B2 (ja) * 2000-05-31 2003-08-04 三洋電機株式会社 光造形装置
KR100583095B1 (ko) 2000-06-30 2006-05-24 주식회사 하이닉스반도체 광산 발생제와 함께 광 라디칼 발생제(ｐｒｇ)를 포함하는포토레지스트 조성물
US6939940B2 (en) 2000-09-13 2005-09-06 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Liquid crystalline thermosets from ester, ester-imide, and ester-amide oligomers
DE10119817A1 (de) * 2001-04-23 2002-10-24 Envision Technologies Gmbh Vorrichtung und Verfahren für die zerstörungsfreie Trennung ausgehärteter Materialschichten von einer planen Bauebene
US6932930B2 (en) 2003-03-10 2005-08-23 Synecor, Llc Intraluminal prostheses having polymeric material with selectively modified crystallinity and methods of making same
US8268446B2 (en) 2003-09-23 2012-09-18 The University Of North Carolina At Chapel Hill Photocurable perfluoropolyethers for use as novel materials in microfluidic devices
JP4044505B2 (ja) 2003-09-29 2008-02-06 独立行政法人科学技術振興機構 光酸発生剤
JP2007509716A (ja) 2003-10-29 2007-04-19 ジェンティス インコーポレイテッド 組織工学用の重合可能なエマルション
AU2004318602B2 (en) 2003-12-19 2009-12-10 The University Of North Carolina At Chapel Hill Methods for fabricating isolated micro- and nano- structures using soft or imprint lithography
KR20070015130A (ko) 2004-01-23 2007-02-01 더 유니버시티 오브 노쓰 캐롤라이나 엣 채플 힐 전기화학 전지에 사용하기 위한 액체 물질
US7649029B2 (en) 2004-05-17 2010-01-19 3M Innovative Properties Company Dental compositions containing nanozirconia fillers
US7097302B2 (en) 2004-07-03 2006-08-29 Mcgregor Scott D Rigid gas permeable contact lens with 3-part curvature
US7556490B2 (en) 2004-07-30 2009-07-07 Board Of Regents, The University Of Texas System Multi-material stereolithography
US8119214B2 (en) 2004-09-01 2012-02-21 Appleton Papers Inc Encapsulated cure systems
KR100637450B1 (ko) 2005-02-16 2006-10-23 한양대학교 산학협력단 플루오로알킬술폰늄염의 광산발생기가 치환된 화합물과 이를 중합한 공중합체
US7344731B2 (en) 2005-06-06 2008-03-18 Bausch & Lomb Incorporated Rigid gas permeable lens material
EP2537657A3 (de) 2005-08-09 2016-05-04 The University of North Carolina At Chapel Hill Verfahren und Materialien zur Herstellung mikrofluidischer Vorrichtungen
DE602005013536D1 (de) 2005-11-18 2009-05-07 Agfa Graphics Nv Verfahren zur Herstellung einer Lithografiedruckform
US20070191506A1 (en) 2006-02-13 2007-08-16 3M Innovative Properties Company Curable compositions for optical articles
WO2007124092A2 (en) 2006-04-21 2007-11-01 Cornell Research Foundation, Inc. Photoacid generator compounds and compositions
US7524615B2 (en) 2006-08-14 2009-04-28 Gary Ganghui Teng Negative laser sensitive lithographic printing plate having specific photosensitive composition
US7892474B2 (en) * 2006-11-15 2011-02-22 Envisiontec Gmbh Continuous generative process for producing a three-dimensional object
US7862176B2 (en) 2007-11-24 2011-01-04 Truform Optics Method of fitting rigid gas-permeable contact lenses from high resolution imaging
US7902526B2 (en) 2008-04-28 2011-03-08 Massachusetts Institute Of Technology 3D two-photon lithographic microfabrication system
US8246888B2 (en) * 2008-10-17 2012-08-21 Stratasys, Inc. Support material for digital manufacturing systems
IT1395683B1 (it) * 2009-08-03 2012-10-16 Dws Srl Macchina stereolitografica perfezionata
CN102715751A (zh) 2011-03-30 2012-10-10 朱雪兵 凝胶垫及其紫外固化生产方法
JP2015514318A (ja) * 2012-03-22 2015-05-18 ザ リージェンツ オブ ザ ユニバーシティ オブ コロラド，ア ボディー コーポレイトＴＨＥ ＲＥＧＥＮＴＳ ＯＦ ＴＨＥ ＵＮＩＶＥＲＳＩＴＹ ＯＦ ＣＯＬＯＲＡＤＯ，ａ ｂｏｄｙ ｃｏｒｐｏｒａｔｅ 液体デポジションフォトリソグラフィ
US9120270B2 (en) * 2012-04-27 2015-09-01 University Of Southern California Digital mask-image-projection-based additive manufacturing that applies shearing force to detach each added layer
US9636873B2 (en) * 2012-05-03 2017-05-02 B9Creations, LLC Solid image apparatus with improved part separation from the image plate

Also Published As

Publication number Publication date
CA2898098A1 (en) 2014-08-21
WO2014126830A2 (en) 2014-08-21
EP3358405A1 (de) 2018-08-08
BR112015018105A2 (pt) 2017-07-18
WO2014126830A3 (en) 2014-11-13
EP2956821B1 (de) 2018-04-11
EP2956821A2 (de) 2015-12-23
KR20150117274A (ko) 2015-10-19
MX2015010374A (es) 2016-04-07
EP2956821B8 (de) 2018-06-27
HK1215475A1 (zh) 2016-08-26
JP2016509962A (ja) 2016-04-04
CN105122136A (zh) 2015-12-02
CN105122136B (zh) 2020-03-24
MX350841B (es) 2017-09-18
US20220048242A1 (en) 2022-02-17
JP6423801B2 (ja) 2018-11-14
ES2667676T3 (es) 2018-05-14
DK2956821T3 (en) 2018-06-14

Similar Documents

Publication Publication Date Title
US11235516B2 (en) Method and apparatus for three-dimensional fabrication
US20230373156A9 (en) Method and apparatus for three-dimensional fabrication
US11141910B2 (en) Continuous liquid interphase printing
US20200094470A1 (en) Acceleration of stereolithography
US11786711B2 (en) Continuous liquid interphase printing
US20240082553A1 (en) Continuous liquid interphase printing

Legal Events

Date Code Title Description
STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION