US20140020795A1 - Method for producing hardened structural elements - Google Patents

Method for producing hardened structural elements Download PDF

Info

Publication number
US20140020795A1
US20140020795A1 US13/997,585 US201113997585A US2014020795A1 US 20140020795 A1 US20140020795 A1 US 20140020795A1 US 201113997585 A US201113997585 A US 201113997585A US 2014020795 A1 US2014020795 A1 US 2014020795A1
Authority
US
United States
Prior art keywords
blank
cooling
temperature
forming
zinc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/997,585
Other languages
English (en)
Inventor
Harald Schwinghammer
Andreas Sommer
Siegfried Kolnberger
Martin Rosner
Thomas Kurz
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Voestalpine Stahl GmbH
Original Assignee
Voestalpine Stahl GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from DE102010056264.5A external-priority patent/DE102010056264C5/de
Priority claimed from DE102010056265.3A external-priority patent/DE102010056265C5/de
Priority claimed from DE102011053941.7A external-priority patent/DE102011053941B4/de
Priority claimed from DE102011053939.5A external-priority patent/DE102011053939B4/de
Application filed by Voestalpine Stahl GmbH filed Critical Voestalpine Stahl GmbH
Assigned to VOESTALPINE STAHL GMBH reassignment VOESTALPINE STAHL GMBH ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KOLNBERGER, SIEGFRIED, KURZ, THOMAS, ROSNER, MARTIN, SCHWINGHAMMER, HARALD, SOMMER, ANDREAS
Publication of US20140020795A1 publication Critical patent/US20140020795A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/005—Modifying the physical properties by deformation combined with, or followed by, heat treatment of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching

Definitions

  • the invention relates to a method for producing hardened, corrosion-protected components.
  • press-hardened components composed of sheet steel are used.
  • These press-hardened components composed of sheet steel are high-strength components that are particularly used as safety components in the region of the vehicle body.
  • the use of these high-strength steel components makes it possible to reduce the material thickness relative to a normal-strength steel and thus to achieve low vehicle body weights.
  • a sheet steel blank is heated to a temperature greater than the so-called austenitization temperature and if need be, kept at this temperature until a desired degree of austenitization is achieved. Then, this heated blank is transferred to a forming die and in this forming die, is shaped into the finished component in a one-step forming process and in so doing, by means of the cooled forming die, simultaneously cooled at a speed that is greater than the critical hardening speed. This produces the hardened component.
  • the component is formed until it is almost completely finished. This formed component is then likewise heated to a temperature greater than the austenitization temperature and if need be, kept at this temperature for a desired, necessary period of time.
  • this heated component is transferred and inserted into a forming die that already has the dimensions of the component or the final dimensions of the component, if need be taking into account the thermal expansion of the preformed component.
  • the preformed component is consequently cooled in this die at a speed that is greater than the critical hardening speed and is thus hardened.
  • the direct method is somewhat simpler to implement, but only permits shapes that can actually be produced by means of a one-step forming process, i.e. relatively simple profile shapes.
  • the indirect process is somewhat more complex, but is also able to produce more complex shapes.
  • the corrosion protection layer can be composed either of rather infrequently used aluminum or aluminum alloys or of significantly more frequently used zinc-based coatings.
  • zinc has the advantage that it provides not just a barrier protection layer like aluminum does, but also a cathodic corrosion protection.
  • zinc-coated press-hardened components fit better into the overall corrosion protection concept of vehicle bodies since in the construction technique that is currently popular, they are generally galvanized as a whole. In this respect, it is possible to reduce or eliminate contact corrosion.
  • microcracks in the coating can also occur, which are also undesirable, but far less pronounced.
  • the zinc/iron phase diagram shows that above 782° C., there is a larger region in which liquid zinc-iron phases occur as long as the iron content is low, in particular less than 60%. But this is also the temperature range in which the austenitized steel is hot formed. It is also noted that if the forming occurs at a temperature greater than 782° C., then there is a high risk of stress corrosion due to liquid zinc, which presumably penetrates into the grain boundaries of the base steel, resulting in macrocracks in the base steel. Furthermore, at iron contents of less than 30% in the coating, the maximum temperature for the forming of a safe product without macrocracks is less than 782° C. This is the reason why direct forming methods are not used with these steels, but instead the indirect forming method is used. This is intended to bypass the above-mentioned problem.
  • EP 1 439 240 B1 has disclosed a method for hot forming a coated steel product; the steel material has a zinc or zinc alloy coating on the surface of the steel material and the steel base material with the coating is heated to a temperature of 700° C. to 1000° C. and hot formed; before the steel base material with the zinc or zinc alloy coating is heated, the coating has an oxide layer that is chiefly composed of zinc oxide in order to prevent the zinc from vaporizing during the heating.
  • a special process sequence is provided for this purpose.
  • EP 1 642 991 B1 has disclosed a method for hot forming a steel in which a component composed of a boron/manganese steel is heated to a temperature at the Ac 3 point or higher, is kept at this temperature, and then the heated steel sheet is formed into the finished component; the formed component is quenched through cooling from the forming temperature during the forming or after the forming in such a way that the cooling rate at the MS point at least corresponds to the critical cooling rate and the average cooling rate of the formed component from the MS point to 200° C. lies in the range from 25° C./s to 150° C./s.
  • the applicant's patent EP 1 651 789 B1 has disclosed a method for manufacturing hardened components out of sheet steel; according to this method, formed parts composed of a sheet steel that is provided with a cathodic corrosion-protection layer are cold formed and undergo a heat treatment for purposes of austenitization; before, during, or after the cold forming of the formed part, a final trimming of the formed part and required punching procedures or production of a hole pattern are carried out and the cold forming as well as the trimming and punching and arrangement of the hole pattern on the component are carried out 0.5% to 2% smaller than the dimensions that the final hardened component should have; the formed part, which has been cold formed for the heat treatment, is then heated in contact with atmospheric oxygen in at least some regions to a temperature that permits an austenitization of the steel material and the heated component is then transferred to a die and in this die, a so-called form hardening is carried out in which the contacting and pressing (holding) of the component by the form hardening dies cause the component to be cooled and
  • the scale reduction of the component with regard to its final geometry takes into account the thermal expansion of the component so that neither a calibration nor a forming are required during the form hardening.
  • the applicant's patent WO 2010/109012 A1 has disclosed a method for manufacturing partially hardened steel components in which a blank composed of a hardenable steel sheet is subjected to a temperature increase that is sufficient for a quench hardening and after a desired temperature is reached and if need be, after a desired holding time, the blank is transferred to a forming die in which the blank is formed into a component and quench hardened at the same time or the blank is cold formed and the component resulting from the cold forming is then subjected to a temperature increase, with the temperature increase being carried out so that a component temperature is reached that is required for a quench hardening and the component is then transferred to a die in which the heated component is cooled and thus quench hardened; during the heating of the blank or component for the purpose of increasing the temperature to a temperature required for the hardening, in the regions that should have a lower hardness and/or a higher ductility, absorption masses are placed or are spaced apart from these regions by a narrow gap; the
  • DE 10 2005 003 551 A1 has disclosed a method for hot forming and hardening a steel sheet in which a steel sheet is heated to a temperature above the Ac 3 point, then undergoes a cooling to a temperature in the range from 400° C. to 600° C., and is only formed after reaching this temperature range.
  • This reference does not mention the crack problem or a coating and also does not describe a martensite formation.
  • the object of the invention therein is the formation of intermediary structures, so-called bainite.
  • the object of the invention is to create a method for manufacturing sheet steel components with a corrosion protection layer in which the crack formation is reduced or eliminated and a sufficient corrosion protection is nevertheless achieved.
  • the invention takes a more advantageous course by using the direct method in which a blank coated with zinc or a zinc alloy is heated, is formed after the heating, and is quench hardened.
  • the forming must be carried out below the peritectic temperature of the iron/zinc system (melt, ferrite, gamma phase).
  • the composition of the steel alloy as part of the conventional composition of a manganese/boron steel (22 MnB5) is adjusted so that a quench hardening is carried out and in so doing, by means of a delayed transformation of the austenite into martensite, the presence of austenite is achieved even at the lower temperature below 780° C.
  • the cooling can take place with air jets; the blowing of the air jets can be controlled by means of pyrometers, which are provided, for example, outside the press and the furnace in a separate piece of equipment in the same way as the corresponding jets.
  • the cooling possibilities in this case are not limited to air jets; it is also possible to use cooled tables on which the blanks are correspondingly positioned so that the blanks come to lie on cooled regions of the table and are brought into thermally conductive contact, for example, by means of pressure or suction.
  • FIG. 1 shows the time/temperature curve in the cooling between the furnace and the forming procedure
  • FIG. 2 shows the zinc/iron diagram
  • FIG. 3 shows depictions of ground cross-sections of the surface of specimens, with and without intermediate cooling
  • FIG. 4 is a time temperature transformation diagram with a simplified depiction of the cooling curve.
  • a conventional boron/manganese steel (e.g. 22MnB5) for use as a press-hardened steel material is adjusted with regard to the transformation of the austenite into other phases so that the transformation moves into deeper regions and martensite can be produced.
  • the alloy elements boron, manganese, carbon, and optionally chromium and molybdenum are used as transformation inhibitors.
  • the alloy elements functioning as transformation inhibitors are adjusted to reliably achieve a quench hardening, i.e. a rapid cooling with a cooling speed that is greater than the critical hardening speed even below 780° C.
  • a quench hardening i.e. a rapid cooling with a cooling speed that is greater than the critical hardening speed even below 780° C.
  • a holding phase in the temperature range of the peritectic point can be provided according to the invention so that the solidification of the zinc coating is promoted and advanced before the subsequent forming procedure is carried out.
  • FIG. 1 shows a favorable temperature curve for an austenitized steel sheet
  • FIG. 3 shows the difference in the crack formation. Without intermediate cooling, cracks form that extend into the steel material; with the intermediate cooling, only surface cracks in the coating occur; these are not critical, however.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Articles (AREA)
  • Coating With Molten Metal (AREA)
  • Shaping Metal By Deep-Drawing, Or The Like (AREA)
US13/997,585 2010-12-24 2011-12-22 Method for producing hardened structural elements Abandoned US20140020795A1 (en)

Applications Claiming Priority (9)

Application Number Priority Date Filing Date Title
DE102010056265.3 2010-12-24
DE102010056264.5 2010-12-24
DE102010056264.5A DE102010056264C5 (de) 2010-12-24 2010-12-24 Verfahren zum Erzeugen gehärteter Bauteile
DE102010056265.3A DE102010056265C5 (de) 2010-12-24 2010-12-24 Verfahren zum Erzeugen gehärteter Bauteile
DE102011053941.7A DE102011053941B4 (de) 2011-09-26 2011-09-26 Verfahren zum Erzeugen gehärteter Bauteile mit Bereichen unterschiedlicher Härte und/oder Duktilität
DE102011053939.5A DE102011053939B4 (de) 2011-09-26 2011-09-26 Verfahren zum Erzeugen gehärteter Bauteile
DE102011053939.5 2011-09-26
DE102011053941.7 2011-09-26
PCT/EP2011/073880 WO2012085247A2 (de) 2010-12-24 2011-12-22 Verfahren zum erzeugen gehärteter bauteile

Publications (1)

Publication Number Publication Date
US20140020795A1 true US20140020795A1 (en) 2014-01-23

Family

ID=45470542

Family Applications (2)

Application Number Title Priority Date Filing Date
US13/997,416 Active 2034-09-30 US10640838B2 (en) 2010-12-24 2011-12-22 Method for producing hardened components with regions of different hardness and/or ductility
US13/997,585 Abandoned US20140020795A1 (en) 2010-12-24 2011-12-22 Method for producing hardened structural elements

Family Applications Before (1)

Application Number Title Priority Date Filing Date
US13/997,416 Active 2034-09-30 US10640838B2 (en) 2010-12-24 2011-12-22 Method for producing hardened components with regions of different hardness and/or ductility

Country Status (8)

Country Link
US (2) US10640838B2 (es)
EP (5) EP2656187B1 (es)
JP (2) JP2014507556A (es)
KR (3) KR20130132566A (es)
CN (5) CN103547687A (es)
ES (5) ES2858225T3 (es)
HU (5) HUE053150T2 (es)
WO (5) WO2012085251A2 (es)

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2527384A (en) * 2014-01-27 2015-12-23 Gm Global Tech Operations Inc Motor vehicle component
KR20160130831A (ko) * 2014-04-23 2016-11-14 제이에프이 스틸 가부시키가이샤 열간 프레스 성형품의 제조 방법 및 열간 프레스 성형품
EP3067128B1 (en) 2015-03-09 2017-09-13 Autotech Engineering, A.I.E. Press system for die quenching and method
US10385415B2 (en) 2016-04-28 2019-08-20 GM Global Technology Operations LLC Zinc-coated hot formed high strength steel part with through-thickness gradient microstructure
US10619223B2 (en) 2016-04-28 2020-04-14 GM Global Technology Operations LLC Zinc-coated hot formed steel component with tailored property
US10618094B2 (en) 2015-03-09 2020-04-14 Autotech Engineering S.L. Press systems and methods
US20210017617A1 (en) * 2017-12-22 2021-01-21 Voestalpine Stahl Gmbh Method for generating metallic components having customised component properties
US11459628B2 (en) 2017-12-22 2022-10-04 Voestalpine Stahl Gmbh Method for producing metallic components having adapted component properties
US11530469B2 (en) 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
US11613789B2 (en) 2018-05-24 2023-03-28 GM Global Technology Operations LLC Method for improving both strength and ductility of a press-hardening steel
US11612926B2 (en) 2018-06-19 2023-03-28 GM Global Technology Operations LLC Low density press-hardening steel having enhanced mechanical properties
US20230166314A1 (en) * 2020-04-20 2023-06-01 Nippon Steel Corporation Method for manufacturing hot-press-formed article, and hot-press-formed article

Families Citing this family (39)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5808724B2 (ja) * 2012-10-31 2015-11-10 アイシン高丘株式会社 アルミニウム合金材のダイクエンチ装置およびダイクエンチ方法
DE102013100682B3 (de) * 2013-01-23 2014-06-05 Voestalpine Metal Forming Gmbh Verfahren zum Erzeugen gehärteter Bauteile und ein Strukturbauteil, welches nach dem Verfahren hergestellt ist
MX2016002450A (es) * 2013-08-29 2016-06-24 Jfe Steel Corp Metodo para la fabricacion de una parte estampada en caliente, y parte estampada en caliente.
DE102013015032A1 (de) * 2013-09-02 2015-03-05 Salzgitter Flachstahl Gmbh Zinkbasierte Korrosionsschutzbeschichtung für Stahlbleche zur Herstellung eines Bauteils bei erhöhter Temperatur durch Presshärten
EP2988887A2 (en) * 2013-09-19 2016-03-02 Tata Steel IJmuiden BV Steel for hot forming
JP6167814B2 (ja) * 2013-09-30 2017-07-26 マツダ株式会社 自動変速機
DE102014101159B4 (de) 2014-01-30 2016-12-01 Thyssenkrupp Steel Europe Ag Verfahren zur Oberflächenbehandlung von Werkstücken
WO2015144318A1 (en) * 2014-03-28 2015-10-01 Tata Steel Ijmuiden B.V. Method for hot forming a coated steel blank
JP6260411B2 (ja) * 2014-03-31 2018-01-17 新日鐵住金株式会社 緩冷却鋼材
MX2017003759A (es) * 2014-09-22 2017-06-30 Arcelormittal Elemento de refuerzo para un vehiculo, metodo para producir el mismo y montaje de puerta.
JP6152836B2 (ja) * 2014-09-25 2017-06-28 Ｊｆｅスチール株式会社 熱間プレス成形品の製造方法
JP6056826B2 (ja) * 2014-09-30 2017-01-11 Ｊｆｅスチール株式会社 熱間プレス成形品の製造方法
DE102014114394B3 (de) * 2014-10-02 2015-11-05 Voestalpine Stahl Gmbh Verfahren zum Erzeugen eines gehärteten Stahlblechs
US20160145731A1 (en) * 2014-11-26 2016-05-26 GM Global Technology Operations LLC Controlling Liquid Metal Embrittlement In Galvanized Press-Hardened Components
JP6178301B2 (ja) * 2014-12-12 2017-08-09 Ｊｆｅスチール株式会社 熱間プレス成形品の製造方法
CN105772584B (zh) * 2014-12-22 2019-01-01 上海赛科利汽车模具技术应用有限公司 改善零件成型性能的热成型工艺及成型装置
CN104668326B (zh) * 2015-03-05 2016-08-24 山东大王金泰集团有限公司 一种高强度钢材零部件性能梯度化分布的热冲压方法
ES2808779T3 (es) * 2015-05-29 2021-03-01 Voestalpine Stahl Gmbh Método para el enfriamiento homogéneo y sin contacto de superficies calientes no continuas y dispositivo para ello
KR20180016980A (ko) 2015-06-03 2018-02-20 잘쯔기터 플래시슈탈 게엠베하 아연도금 강으로 제조된 변형-경화된 부품, 그 제조방법 및 부품의 변형-경화에 적합한 강 스트립 제조방법
WO2017017484A1 (en) * 2015-07-30 2017-02-02 Arcelormittal Method for the manufacture of a hardened part which does not have lme issues
WO2017017483A1 (en) 2015-07-30 2017-02-02 Arcelormittal Steel sheet coated with a metallic coating based on aluminum
WO2017017485A1 (en) 2015-07-30 2017-02-02 Arcelormittal A method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminium
DE102016102322B4 (de) * 2016-02-10 2017-10-12 Voestalpine Metal Forming Gmbh Verfahren und Vorrichtung zum Erzeugen gehärteter Stahlbauteile
DE102016102324B4 (de) * 2016-02-10 2020-09-17 Voestalpine Metal Forming Gmbh Verfahren und Vorrichtung zum Erzeugen gehärteter Stahlbauteile
DE102016114658B4 (de) * 2016-08-08 2021-10-14 Voestalpine Metal Forming Gmbh Verfahren zum Formen und Härten von Stahlwerkstoffen
CN106334875A (zh) * 2016-10-27 2017-01-18 宝山钢铁股份有限公司 一种带铝或者铝合金镀层的钢制焊接部件及其制造方法
CN106424280B (zh) * 2016-11-30 2017-09-29 华中科技大学 一种高强钢热成形差异化力学性能分布柔性控制方法
DE102017115755A1 (de) 2017-07-13 2019-01-17 Schwartz Gmbh Verfahren und Vorrichtung zur Wärmebehandlung eines metallischen Bauteils
EP3437750A1 (en) * 2017-08-02 2019-02-06 Autotech Engineering A.I.E. Press method for coated steels
CN109433960A (zh) * 2018-09-30 2019-03-08 苏州普热斯勒先进成型技术有限公司 热冲压高强钢汽车车身覆盖件及其制造方法、制造系统
EP3712292B1 (de) * 2019-03-19 2023-08-02 ThyssenKrupp Steel Europe AG Bauteil umfassend ein stahlsubstrat, eine zwischenschicht und eine korrosionsschutzbeschichtung, entsprechende verfahren und verwendungen
KR102448330B1 (ko) 2019-10-14 2022-09-27 오토테크 엔지니어링 에스.엘. 프레스 시스템 및 방법
EP3872230A1 (de) * 2020-02-28 2021-09-01 voestalpine Stahl GmbH Verfahren zum herstellen gehärteter stahlbauteile mit einer konditionierten zinklegierungskorrosionsschutzschicht
CN111822571A (zh) * 2020-07-12 2020-10-27 首钢集团有限公司 可定制零件的组织性能分区的热冲压方法
KR102553226B1 (ko) * 2020-12-21 2023-07-07 주식회사 포스코 전자기 검사 장치
CN113182374A (zh) * 2021-04-30 2021-07-30 合肥合锻智能制造股份有限公司 一种高强度结构件的热成型方法
DE102021122383A1 (de) 2021-08-30 2023-03-02 Audi Aktiengesellschaft Verfahren zur Herstellung eines warmumgeformten und pressgehärteten Stahlblechbauteils
WO2023074114A1 (ja) 2021-10-29 2023-05-04 Ｊｆｅスチール株式会社 熱間プレス部材
MX2024005036A (es) 2021-10-29 2024-05-10 Jfe Steel Corp Miembro prensado en caliente.

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SU330202A1 (ru) * Натеп Ская Устройство для принудительного охлаждения крупногабаритных изделий
US5272898A (en) * 1991-11-04 1993-12-28 Isoform Device for stamping materials in sheet form, especially sheet metal blanks
JP2007182608A (ja) * 2006-01-06 2007-07-19 Nippon Steel Corp 耐食性、耐疲労性に優れた高強度焼き入れ成形体の製造方法および製造設備

Family Cites Families (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19838332A1 (de) * 1998-08-24 2000-03-02 Schloemann Siemag Ag Verfahren und Vorrichtung zur Qualitätsüberwachung und -regelung des Galvannealed-Überzuges von Stahlbändern
FR2807447B1 (fr) * 2000-04-07 2002-10-11 Usinor Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue
CN100434564C (zh) 2001-10-23 2008-11-19 住友金属工业株式会社 热压成型方法,其电镀钢材及其制备方法
JP4085876B2 (ja) * 2003-04-23 2008-05-14 住友金属工業株式会社 熱間プレス成形品およびその製造方法
JP4325277B2 (ja) 2003-05-28 2009-09-02 住友金属工業株式会社 熱間成形法と熱間成形部材
KR100834555B1 (ko) 2003-07-29 2008-06-02 뵈스트알파인 스탈 게엠베하 경화 강판 부품의 제조 방법
AT412403B (de) * 2003-07-29 2005-02-25 Voestalpine Stahl Gmbh Korrosionsgeschütztes stahlblech
US20060196583A1 (en) * 2003-09-29 2006-09-07 Tohru Hayashi Steel parts for machine structure, material therefor, and method for manufacture thereof
JP2005177805A (ja) * 2003-12-19 2005-07-07 Nippon Steel Corp ホットプレス成形方法
JP4131715B2 (ja) * 2004-05-18 2008-08-13 トピー工業株式会社 熱処理部材の部分熱処理方法とその装置
JP2006051543A (ja) * 2004-07-15 2006-02-23 Nippon Steel Corp 冷延、熱延鋼板もしくはＡｌ系、Ｚｎ系めっき鋼板を使用した高強度自動車部材の熱間プレス方法および熱間プレス部品
JP4329639B2 (ja) * 2004-07-23 2009-09-09 住友金属工業株式会社 耐液体金属脆性に優れた熱処理用鋼板
DE102005003551B4 (de) 2005-01-26 2015-01-22 Volkswagen Ag Verfahren zur Warmumformung und Härtung eines Stahlblechs
JP2007016296A (ja) * 2005-07-11 2007-01-25 Nippon Steel Corp 成形後の延性に優れたプレス成形用鋼板及びその成形方法、並びにプレス整形用鋼板を用いた自動車用部材
WO2007048883A1 (fr) * 2005-10-27 2007-05-03 Usinor Procede de fabrication d'une piece a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue
JP4681492B2 (ja) * 2006-04-07 2011-05-11 新日本製鐵株式会社 鋼板熱間プレス方法及びプレス成形品
DE102007013739B3 (de) * 2007-03-22 2008-09-04 Voestalpine Stahl Gmbh Verfahren zum flexiblen Walzen von beschichteten Stahlbändern
JP5194986B2 (ja) * 2007-04-20 2013-05-08 新日鐵住金株式会社 高強度部品の製造方法および高強度部品
JP5092523B2 (ja) * 2007-04-20 2012-12-05 新日本製鐵株式会社 高強度部品の製造方法および高強度部品
WO2008153183A1 (ja) * 2007-06-15 2008-12-18 Sumitomo Metal Industries, Ltd. 成形品の製造方法
JP2009061473A (ja) 2007-09-06 2009-03-26 Sumitomo Metal Ind Ltd 高強度部品の製造方法
JP4890416B2 (ja) 2007-10-18 2012-03-07 アイシン高丘株式会社 ダイクエンチ工法におけるプレス加工装置及びプレス加工方法
JP2012512747A (ja) * 2008-12-19 2012-06-07 タタ、スティール、アイモイデン、ベスローテン、フェンノートシャップ 熱間成形技術を用いた被覆部品の製造方法
JP4825882B2 (ja) * 2009-02-03 2011-11-30 トヨタ自動車株式会社 高強度焼き入れ成形体及びその製造方法
DE102009015013B4 (de) * 2009-03-26 2011-05-12 Voestalpine Automotive Gmbh Verfahren zum Herstellen partiell gehärteter Stahlbauteile
DE102009017326A1 (de) * 2009-04-16 2010-10-21 Benteler Automobiltechnik Gmbh Verfahren zur Herstellung von pressgehärteten Bauteilen
DE102009051673B3 (de) * 2009-11-03 2011-04-14 Voestalpine Stahl Gmbh Herstellung von Galvannealed-Blechen durch Wärmebehandlung elektrolytisch veredelter Bleche
KR101171450B1 (ko) * 2009-12-29 2012-08-06 주식회사 포스코 도금 강재의 열간 프레스 성형방법 및 이를 이용한 열간 프레스 성형품
JP5740099B2 (ja) * 2010-04-23 2015-06-24 東プレ株式会社 熱間プレス製品の製造方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SU330202A1 (ru) * Натеп Ская Устройство для принудительного охлаждения крупногабаритных изделий
US5272898A (en) * 1991-11-04 1993-12-28 Isoform Device for stamping materials in sheet form, especially sheet metal blanks
JP2007182608A (ja) * 2006-01-06 2007-07-19 Nippon Steel Corp 耐食性、耐疲労性に優れた高強度焼き入れ成形体の製造方法および製造設備

Cited By (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9518316B2 (en) 2014-01-27 2016-12-13 GM Global Technology Operations LLC Motor vehicle component
GB2527384A (en) * 2014-01-27 2015-12-23 Gm Global Tech Operations Inc Motor vehicle component
KR101879307B1 (ko) * 2014-04-23 2018-07-17 제이에프이 스틸 가부시키가이샤 열간 프레스 성형품의 제조 방법
KR20160130831A (ko) * 2014-04-23 2016-11-14 제이에프이 스틸 가부시키가이샤 열간 프레스 성형품의 제조 방법 및 열간 프레스 성형품
US10618094B2 (en) 2015-03-09 2020-04-14 Autotech Engineering S.L. Press systems and methods
EP3266531B1 (en) 2015-03-09 2019-02-27 Autotech Engineering, A.I.E. Press systems and methods
EP3067128B1 (en) 2015-03-09 2017-09-13 Autotech Engineering, A.I.E. Press system for die quenching and method
US10385415B2 (en) 2016-04-28 2019-08-20 GM Global Technology Operations LLC Zinc-coated hot formed high strength steel part with through-thickness gradient microstructure
US10619223B2 (en) 2016-04-28 2020-04-14 GM Global Technology Operations LLC Zinc-coated hot formed steel component with tailored property
US20210017617A1 (en) * 2017-12-22 2021-01-21 Voestalpine Stahl Gmbh Method for generating metallic components having customised component properties
US11459628B2 (en) 2017-12-22 2022-10-04 Voestalpine Stahl Gmbh Method for producing metallic components having adapted component properties
US11613789B2 (en) 2018-05-24 2023-03-28 GM Global Technology Operations LLC Method for improving both strength and ductility of a press-hardening steel
US11612926B2 (en) 2018-06-19 2023-03-28 GM Global Technology Operations LLC Low density press-hardening steel having enhanced mechanical properties
US11951522B2 (en) 2018-06-19 2024-04-09 GM Global Technology Operations LLC Low density press-hardening steel having enhanced mechanical properties
US11530469B2 (en) 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
US20230166314A1 (en) * 2020-04-20 2023-06-01 Nippon Steel Corporation Method for manufacturing hot-press-formed article, and hot-press-formed article

Also Published As

Publication number Publication date
WO2012085248A3 (de) 2012-08-16
CN103384726B (zh) 2016-11-23
ES2829950T8 (es) 2021-06-10
CN103384726A (zh) 2013-11-06
ES2848159T3 (es) 2021-08-05
JP2014505791A (ja) 2014-03-06
HUE054867T2 (hu) 2021-10-28
WO2012085248A2 (de) 2012-06-28
KR20130132565A (ko) 2013-12-04
US10640838B2 (en) 2020-05-05
WO2012085256A3 (de) 2012-08-16
WO2012085251A3 (de) 2012-08-16
WO2012085256A2 (de) 2012-06-28
ES2829950T3 (es) 2021-06-02
WO2012085247A2 (de) 2012-06-28
ES2851176T3 (es) 2021-09-03
WO2012085253A2 (de) 2012-06-28
CN103547686A (zh) 2014-01-29
EP2656187A2 (de) 2013-10-30
HUE053150T2 (hu) 2021-06-28
WO2012085247A3 (de) 2012-08-16
WO2012085253A3 (de) 2012-08-16
CN103415630A (zh) 2013-11-27
CN103547687A (zh) 2014-01-29
CN103547686B (zh) 2016-11-23
EP2655675B1 (de) 2021-03-10
KR101582922B1 (ko) 2016-01-07
ES2858225T3 (es) 2021-09-29
JP2014507556A (ja) 2014-03-27
JP5727037B2 (ja) 2015-06-03
WO2012085251A2 (de) 2012-06-28
ES2858225T8 (es) 2022-01-05
EP2655673A2 (de) 2013-10-30
EP2655674A2 (de) 2013-10-30
HUE054465T2 (hu) 2021-09-28
EP2655672A2 (de) 2013-10-30
KR20130126962A (ko) 2013-11-21
HUE052381T2 (hu) 2021-04-28
EP2656187B1 (de) 2020-09-09
KR20130132566A (ko) 2013-12-04
EP2655674B1 (de) 2021-02-03
EP2655673B1 (de) 2021-02-03
EP2655672B1 (de) 2020-12-16
ES2853207T3 (es) 2021-09-15
HUE055049T2 (hu) 2021-10-28
EP2655675A2 (de) 2013-10-30
CN103392014B (zh) 2016-01-27
CN103392014A (zh) 2013-11-13
US20140027026A1 (en) 2014-01-30
CN103415630B (zh) 2015-09-23

Similar Documents

Publication Publication Date Title
US20140020795A1 (en) Method for producing hardened structural elements
KR101820273B1 (ko) 프레스 경화용 강 시트의 제조 방법, 빛 이 방법에 의해 획득되는 부품
KR101892661B1 (ko) 핫 스탬핑용 강판, 핫 스탬핑 방법 및 핫 스탬핑된 부품
CN107127238B (zh) 一种锌系镀覆钢板或钢带的热冲压成型方法
EP2581465B1 (en) Hot-stamp-molded article, process for production of steel sheet for hot stamping, and process for production of hot-stamp-molded article
CN109371325A (zh) 一种冷弯性能优良的锌系镀覆热成型钢板或钢带及其制造方法
US11976342B2 (en) Method for producing high-strength steel parts with improved ductility, and parts obtained by said method
US20170321314A1 (en) Method for producing an anti-corrosion coating for hardenable sheet steels and an anti-corrosion coating for hardenable sheet steels
JP2021501833A (ja) ホットスタンピングに使用される鋼、ホットスタンピング方法および成形された構成要素
CN102859020A (zh) 热处理钢材及其制造方法以及其原材料钢材
CN109112359A (zh) 一种锌基镀层钢板及其制造方法、热成型方法和部件
CN111945075A (zh) 一种高扩孔性能合金化热镀锌dh590钢及其制备方法
EP3899066B1 (en) A press hardened part with high resistance to delayed fracture and a manufacturing process thereof
CN107829038B (zh) 一种高强塑积、高可镀性细晶热镀锌双相钢及其生产方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: VOESTALPINE STAHL GMBH, AUSTRIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SCHWINGHAMMER, HARALD;SOMMER, ANDREAS;KOLNBERGER, SIEGFRIED;AND OTHERS;SIGNING DATES FROM 20130930 TO 20131007;REEL/FRAME:031406/0528

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION