ES2829950T8 - Procedimiento para producir componentes endurecidos - Google Patents
Procedimiento para producir componentes endurecidosInfo
- Publication number
- ES2829950T8 ES2829950T8 ES11811026T ES11811026T ES2829950T8 ES 2829950 T8 ES2829950 T8 ES 2829950T8 ES 11811026 T ES11811026 T ES 11811026T ES 11811026 T ES11811026 T ES 11811026T ES 2829950 T8 ES2829950 T8 ES 2829950T8
- Authority
- ES
- Spain
- Prior art keywords
- procedure
- hardened components
- producing hardened
- producing
- components
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/005—Modifying the physical properties by deformation combined with, or followed by, heat treatment of ferrous alloys
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/62—Quenching devices
- C21D1/673—Quenching devices for die quenching
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
- C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
- C23C2/29—Cooling or quenching
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Thermal Sciences (AREA)
- Physics & Mathematics (AREA)
- Crystallography & Structural Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Heat Treatment Of Articles (AREA)
- Coating With Molten Metal (AREA)
- Shaping Metal By Deep-Drawing, Or The Like (AREA)
Applications Claiming Priority (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102010056264.5A DE102010056264C5 (de) | 2010-12-24 | 2010-12-24 | Verfahren zum Erzeugen gehärteter Bauteile |
DE102010056265.3A DE102010056265C5 (de) | 2010-12-24 | 2010-12-24 | Verfahren zum Erzeugen gehärteter Bauteile |
DE102011053941.7A DE102011053941B4 (de) | 2011-09-26 | 2011-09-26 | Verfahren zum Erzeugen gehärteter Bauteile mit Bereichen unterschiedlicher Härte und/oder Duktilität |
DE102011053939.5A DE102011053939B4 (de) | 2011-09-26 | 2011-09-26 | Verfahren zum Erzeugen gehärteter Bauteile |
PCT/EP2011/073892 WO2012085256A2 (de) | 2010-12-24 | 2011-12-22 | Verfahren zum erzeugen gehärteter bauteile |
Publications (2)
Publication Number | Publication Date |
---|---|
ES2829950T3 ES2829950T3 (es) | 2021-06-02 |
ES2829950T8 true ES2829950T8 (es) | 2021-06-10 |
Family
ID=45470542
Family Applications (5)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
ES11811026T Active ES2829950T3 (es) | 2010-12-24 | 2011-12-22 | Procedimiento para producir componentes endurecidos |
ES11808645T Active ES2851176T3 (es) | 2010-12-24 | 2011-12-22 | Método para conformar y endurecer chapas de acero recubiertas |
ES11808211T Active ES2853207T3 (es) | 2010-12-24 | 2011-12-22 | Procedimiento para la fabricación de componentes endurecidos |
ES11811025T Active ES2858225T3 (es) | 2010-12-24 | 2011-12-22 | Procedimiento para producir elementos estructurales templados |
ES11807691T Active ES2848159T3 (es) | 2010-12-24 | 2011-12-22 | Método para producir componentes endurecidos con áreas de diferente dureza y/o ductilidad |
Family Applications After (4)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
ES11808645T Active ES2851176T3 (es) | 2010-12-24 | 2011-12-22 | Método para conformar y endurecer chapas de acero recubiertas |
ES11808211T Active ES2853207T3 (es) | 2010-12-24 | 2011-12-22 | Procedimiento para la fabricación de componentes endurecidos |
ES11811025T Active ES2858225T3 (es) | 2010-12-24 | 2011-12-22 | Procedimiento para producir elementos estructurales templados |
ES11807691T Active ES2848159T3 (es) | 2010-12-24 | 2011-12-22 | Método para producir componentes endurecidos con áreas de diferente dureza y/o ductilidad |
Country Status (8)
Country | Link |
---|---|
US (2) | US10640838B2 (es) |
EP (5) | EP2655675B1 (es) |
JP (2) | JP2014507556A (es) |
KR (3) | KR101582922B1 (es) |
CN (5) | CN103392014B (es) |
ES (5) | ES2829950T3 (es) |
HU (5) | HUE054465T2 (es) |
WO (5) | WO2012085247A2 (es) |
Families Citing this family (51)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5808724B2 (ja) * | 2012-10-31 | 2015-11-10 | アイシン高丘株式会社 | アルミニウム合金材のダイクエンチ装置およびダイクエンチ方法 |
DE102013100682B3 (de) * | 2013-01-23 | 2014-06-05 | Voestalpine Metal Forming Gmbh | Verfahren zum Erzeugen gehärteter Bauteile und ein Strukturbauteil, welches nach dem Verfahren hergestellt ist |
WO2015029653A1 (ja) * | 2013-08-29 | 2015-03-05 | Jfeスチール株式会社 | 熱間プレス成形部材の製造方法および熱間プレス成形部材 |
DE102013015032A1 (de) * | 2013-09-02 | 2015-03-05 | Salzgitter Flachstahl Gmbh | Zinkbasierte Korrosionsschutzbeschichtung für Stahlbleche zur Herstellung eines Bauteils bei erhöhter Temperatur durch Presshärten |
KR20160057457A (ko) * | 2013-09-19 | 2016-05-23 | 타타 스틸 이즈무이덴 베.뷔. | 열간 성형용 강 |
JP6167814B2 (ja) * | 2013-09-30 | 2017-07-26 | マツダ株式会社 | 自動変速機 |
DE102014000969A1 (de) * | 2014-01-27 | 2015-07-30 | GM Global Technology Operations LLC (n. d. Ges. d. Staates Delaware) | Kraftfahrzeugbauteil |
DE102014101159B4 (de) | 2014-01-30 | 2016-12-01 | Thyssenkrupp Steel Europe Ag | Verfahren zur Oberflächenbehandlung von Werkstücken |
WO2015144318A1 (en) * | 2014-03-28 | 2015-10-01 | Tata Steel Ijmuiden B.V. | Method for hot forming a coated steel blank |
JP6260411B2 (ja) * | 2014-03-31 | 2018-01-17 | 新日鐵住金株式会社 | 緩冷却鋼材 |
JP5825413B1 (ja) * | 2014-04-23 | 2015-12-02 | Jfeスチール株式会社 | 熱間プレス成形品の製造方法 |
US20170291476A1 (en) * | 2014-09-22 | 2017-10-12 | Arcelormittal | Reinforcement element for a vehicle, method for producing the same and door assembly |
JP6152836B2 (ja) * | 2014-09-25 | 2017-06-28 | Jfeスチール株式会社 | 熱間プレス成形品の製造方法 |
JP6056826B2 (ja) * | 2014-09-30 | 2017-01-11 | Jfeスチール株式会社 | 熱間プレス成形品の製造方法 |
DE102014114394B3 (de) * | 2014-10-02 | 2015-11-05 | Voestalpine Stahl Gmbh | Verfahren zum Erzeugen eines gehärteten Stahlblechs |
US20160145731A1 (en) * | 2014-11-26 | 2016-05-26 | GM Global Technology Operations LLC | Controlling Liquid Metal Embrittlement In Galvanized Press-Hardened Components |
JP6178301B2 (ja) * | 2014-12-12 | 2017-08-09 | Jfeスチール株式会社 | 熱間プレス成形品の製造方法 |
CN105772584B (zh) * | 2014-12-22 | 2019-01-01 | 上海赛科利汽车模具技术应用有限公司 | 改善零件成型性能的热成型工艺及成型装置 |
CN104668326B (zh) * | 2015-03-05 | 2016-08-24 | 山东大王金泰集团有限公司 | 一种高强度钢材零部件性能梯度化分布的热冲压方法 |
EP3266531B1 (en) | 2015-03-09 | 2019-02-27 | Autotech Engineering, A.I.E. | Press systems and methods |
EP3067129A1 (en) | 2015-03-09 | 2016-09-14 | Autotech Engineering, A.I.E. | Press systems and methods |
WO2016192993A1 (de) * | 2015-05-29 | 2016-12-08 | Voestalpine Stahl Gmbh | Verfahren zum kontaktlosen kühlen von stahlblechen und vorrichtung hierfür |
US20180171424A1 (en) | 2015-06-03 | 2018-06-21 | Salzgitter Flachstahl Gmbh | Deformation-hardened component made of galvanized steel, production method therefor and method for producing a steel strip suitable for the deformation-hardening of components |
WO2017017484A1 (en) * | 2015-07-30 | 2017-02-02 | Arcelormittal | Method for the manufacture of a hardened part which does not have lme issues |
WO2017017483A1 (en) | 2015-07-30 | 2017-02-02 | Arcelormittal | Steel sheet coated with a metallic coating based on aluminum |
WO2017017485A1 (en) | 2015-07-30 | 2017-02-02 | Arcelormittal | A method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminium |
DE102016102322B4 (de) * | 2016-02-10 | 2017-10-12 | Voestalpine Metal Forming Gmbh | Verfahren und Vorrichtung zum Erzeugen gehärteter Stahlbauteile |
DE102016102324B4 (de) * | 2016-02-10 | 2020-09-17 | Voestalpine Metal Forming Gmbh | Verfahren und Vorrichtung zum Erzeugen gehärteter Stahlbauteile |
US10385415B2 (en) | 2016-04-28 | 2019-08-20 | GM Global Technology Operations LLC | Zinc-coated hot formed high strength steel part with through-thickness gradient microstructure |
US10619223B2 (en) | 2016-04-28 | 2020-04-14 | GM Global Technology Operations LLC | Zinc-coated hot formed steel component with tailored property |
DE102016114658B4 (de) * | 2016-08-08 | 2021-10-14 | Voestalpine Metal Forming Gmbh | Verfahren zum Formen und Härten von Stahlwerkstoffen |
CN106334875A (zh) * | 2016-10-27 | 2017-01-18 | 宝山钢铁股份有限公司 | 一种带铝或者铝合金镀层的钢制焊接部件及其制造方法 |
CN106424280B (zh) * | 2016-11-30 | 2017-09-29 | 华中科技大学 | 一种高强钢热成形差异化力学性能分布柔性控制方法 |
DE102017115755A1 (de) * | 2017-07-13 | 2019-01-17 | Schwartz Gmbh | Verfahren und Vorrichtung zur Wärmebehandlung eines metallischen Bauteils |
EP3437750A1 (en) * | 2017-08-02 | 2019-02-06 | Autotech Engineering A.I.E. | Press method for coated steels |
DE102017131247A1 (de) * | 2017-12-22 | 2019-06-27 | Voestalpine Stahl Gmbh | Verfahren zum Erzeugen metallischer Bauteile mit angepassten Bauteileigenschaften |
DE102017131253A1 (de) | 2017-12-22 | 2019-06-27 | Voestalpine Stahl Gmbh | Verfahren zum Erzeugen metallischer Bauteile mit angepassten Bauteileigenschaften |
CN112513310A (zh) | 2018-05-24 | 2021-03-16 | 通用汽车环球科技运作有限责任公司 | 改善压制硬化钢的强度和延性的方法 |
US11612926B2 (en) | 2018-06-19 | 2023-03-28 | GM Global Technology Operations LLC | Low density press-hardening steel having enhanced mechanical properties |
CN109433960A (zh) * | 2018-09-30 | 2019-03-08 | 苏州普热斯勒先进成型技术有限公司 | 热冲压高强钢汽车车身覆盖件及其制造方法、制造系统 |
EP3712292B1 (de) * | 2019-03-19 | 2023-08-02 | ThyssenKrupp Steel Europe AG | Bauteil umfassend ein stahlsubstrat, eine zwischenschicht und eine korrosionsschutzbeschichtung, entsprechende verfahren und verwendungen |
US11530469B2 (en) | 2019-07-02 | 2022-12-20 | GM Global Technology Operations LLC | Press hardened steel with surface layered homogenous oxide after hot forming |
CN114555256A (zh) | 2019-10-14 | 2022-05-27 | 昂登坦工程有限公司 | 压制系统和方法 |
EP3872230A1 (de) * | 2020-02-28 | 2021-09-01 | voestalpine Stahl GmbH | Verfahren zum herstellen gehärteter stahlbauteile mit einer konditionierten zinklegierungskorrosionsschutzschicht |
KR20220151700A (ko) * | 2020-04-20 | 2022-11-15 | 닛폰세이테츠 가부시키가이샤 | 열간 프레스 성형품의 제조 방법 및 열간 프레스 성형품 |
CN111822571A (zh) * | 2020-07-12 | 2020-10-27 | 首钢集团有限公司 | 可定制零件的组织性能分区的热冲压方法 |
KR102553226B1 (ko) * | 2020-12-21 | 2023-07-07 | 주식회사 포스코 | 전자기 검사 장치 |
CN113182374A (zh) * | 2021-04-30 | 2021-07-30 | 合肥合锻智能制造股份有限公司 | 一种高强度结构件的热成型方法 |
DE102021122383A1 (de) | 2021-08-30 | 2023-03-02 | Audi Aktiengesellschaft | Verfahren zur Herstellung eines warmumgeformten und pressgehärteten Stahlblechbauteils |
WO2023074114A1 (ja) | 2021-10-29 | 2023-05-04 | Jfeスチール株式会社 | 熱間プレス部材 |
MX2024005036A (es) | 2021-10-29 | 2024-05-10 | Jfe Steel Corp | Miembro prensado en caliente. |
Family Cites Families (31)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2683168B1 (fr) * | 1991-11-04 | 1994-03-04 | Isoform | Dispositif d'emboutissage de materiaux en feuille, notamment de flans de tole. |
DE19838332A1 (de) * | 1998-08-24 | 2000-03-02 | Schloemann Siemag Ag | Verfahren und Vorrichtung zur Qualitätsüberwachung und -regelung des Galvannealed-Überzuges von Stahlbändern |
FR2807447B1 (fr) * | 2000-04-07 | 2002-10-11 | Usinor | Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue |
KR100678406B1 (ko) | 2001-10-23 | 2007-02-02 | 수미도모 메탈 인더스트리즈, 리미티드 | 강철재의 열간 프레스 성형방법 |
JP4085876B2 (ja) * | 2003-04-23 | 2008-05-14 | 住友金属工業株式会社 | 熱間プレス成形品およびその製造方法 |
JP4325277B2 (ja) | 2003-05-28 | 2009-09-02 | 住友金属工業株式会社 | 熱間成形法と熱間成形部材 |
KR100825975B1 (ko) | 2003-07-29 | 2008-04-28 | 뵈스트알파인 스탈 게엠베하 | 경화 강판 부품의 제조 방법 |
AT412403B (de) * | 2003-07-29 | 2005-02-25 | Voestalpine Stahl Gmbh | Korrosionsgeschütztes stahlblech |
EP1669469B1 (en) * | 2003-09-29 | 2008-12-17 | JFE Steel Corporation | Steel parts for machine structure, material therefor, and method for manufacture thereof |
JP2005177805A (ja) * | 2003-12-19 | 2005-07-07 | Nippon Steel Corp | ホットプレス成形方法 |
JP4131715B2 (ja) * | 2004-05-18 | 2008-08-13 | トピー工業株式会社 | 熱処理部材の部分熱処理方法とその装置 |
JP2006051543A (ja) * | 2004-07-15 | 2006-02-23 | Nippon Steel Corp | 冷延、熱延鋼板もしくはAl系、Zn系めっき鋼板を使用した高強度自動車部材の熱間プレス方法および熱間プレス部品 |
JP4329639B2 (ja) * | 2004-07-23 | 2009-09-09 | 住友金属工業株式会社 | 耐液体金属脆性に優れた熱処理用鋼板 |
DE102005003551B4 (de) | 2005-01-26 | 2015-01-22 | Volkswagen Ag | Verfahren zur Warmumformung und Härtung eines Stahlblechs |
JP2007016296A (ja) * | 2005-07-11 | 2007-01-25 | Nippon Steel Corp | 成形後の延性に優れたプレス成形用鋼板及びその成形方法、並びにプレス整形用鋼板を用いた自動車用部材 |
WO2007048883A1 (fr) * | 2005-10-27 | 2007-05-03 | Usinor | Procede de fabrication d'une piece a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue |
JP4733522B2 (ja) * | 2006-01-06 | 2011-07-27 | 新日本製鐵株式会社 | 耐食性、耐疲労性に優れた高強度焼き入れ成形体の製造方法 |
JP4681492B2 (ja) | 2006-04-07 | 2011-05-11 | 新日本製鐵株式会社 | 鋼板熱間プレス方法及びプレス成形品 |
DE102007013739B3 (de) * | 2007-03-22 | 2008-09-04 | Voestalpine Stahl Gmbh | Verfahren zum flexiblen Walzen von beschichteten Stahlbändern |
JP5194986B2 (ja) * | 2007-04-20 | 2013-05-08 | 新日鐵住金株式会社 | 高強度部品の製造方法および高強度部品 |
JP5092523B2 (ja) * | 2007-04-20 | 2012-12-05 | 新日本製鐵株式会社 | 高強度部品の製造方法および高強度部品 |
WO2008153183A1 (ja) * | 2007-06-15 | 2008-12-18 | Sumitomo Metal Industries, Ltd. | 成形品の製造方法 |
JP2009061473A (ja) * | 2007-09-06 | 2009-03-26 | Sumitomo Metal Ind Ltd | 高強度部品の製造方法 |
JP4890416B2 (ja) | 2007-10-18 | 2012-03-07 | アイシン高丘株式会社 | ダイクエンチ工法におけるプレス加工装置及びプレス加工方法 |
EP2379756A1 (en) * | 2008-12-19 | 2011-10-26 | Tata Steel IJmuiden B.V. | Method for manufacturing a coated part using hot forming techniques |
JP4825882B2 (ja) * | 2009-02-03 | 2011-11-30 | トヨタ自動車株式会社 | 高強度焼き入れ成形体及びその製造方法 |
DE102009015013B4 (de) * | 2009-03-26 | 2011-05-12 | Voestalpine Automotive Gmbh | Verfahren zum Herstellen partiell gehärteter Stahlbauteile |
DE102009017326A1 (de) * | 2009-04-16 | 2010-10-21 | Benteler Automobiltechnik Gmbh | Verfahren zur Herstellung von pressgehärteten Bauteilen |
DE102009051673B3 (de) * | 2009-11-03 | 2011-04-14 | Voestalpine Stahl Gmbh | Herstellung von Galvannealed-Blechen durch Wärmebehandlung elektrolytisch veredelter Bleche |
KR101171450B1 (ko) * | 2009-12-29 | 2012-08-06 | 주식회사 포스코 | 도금 강재의 열간 프레스 성형방법 및 이를 이용한 열간 프레스 성형품 |
JP5740099B2 (ja) * | 2010-04-23 | 2015-06-24 | 東プレ株式会社 | 熱間プレス製品の製造方法 |
-
2011
- 2011-12-22 WO PCT/EP2011/073880 patent/WO2012085247A2/de active Application Filing
- 2011-12-22 KR KR1020137019700A patent/KR101582922B1/ko active IP Right Grant
- 2011-12-22 EP EP11811025.3A patent/EP2655675B1/de active Active
- 2011-12-22 HU HUE11808645A patent/HUE054465T2/hu unknown
- 2011-12-22 EP EP11808645.3A patent/EP2655674B1/de active Active
- 2011-12-22 HU HUE11808211A patent/HUE054867T2/hu unknown
- 2011-12-22 JP JP2013545422A patent/JP2014507556A/ja active Pending
- 2011-12-22 KR KR1020137019703A patent/KR20130126962A/ko not_active Application Discontinuation
- 2011-12-22 KR KR1020137019701A patent/KR20130132566A/ko not_active Application Discontinuation
- 2011-12-22 US US13/997,416 patent/US10640838B2/en active Active
- 2011-12-22 WO PCT/EP2011/073892 patent/WO2012085256A2/de active Application Filing
- 2011-12-22 CN CN201180068528.7A patent/CN103392014B/zh active Active
- 2011-12-22 HU HUE11811026A patent/HUE052381T2/hu unknown
- 2011-12-22 CN CN201180068494.1A patent/CN103384726B/zh active Active
- 2011-12-22 WO PCT/EP2011/073889 patent/WO2012085253A2/de active Application Filing
- 2011-12-22 CN CN201180068492.2A patent/CN103547686B/zh active Active
- 2011-12-22 ES ES11811026T patent/ES2829950T3/es active Active
- 2011-12-22 ES ES11808645T patent/ES2851176T3/es active Active
- 2011-12-22 HU HUE11807691A patent/HUE053150T2/hu unknown
- 2011-12-22 CN CN201180068534.2A patent/CN103547687A/zh active Pending
- 2011-12-22 JP JP2013545421A patent/JP5727037B2/ja active Active
- 2011-12-22 ES ES11808211T patent/ES2853207T3/es active Active
- 2011-12-22 ES ES11811025T patent/ES2858225T3/es active Active
- 2011-12-22 EP EP11808211.4A patent/EP2655673B1/de active Active
- 2011-12-22 WO PCT/EP2011/073887 patent/WO2012085251A2/de active Application Filing
- 2011-12-22 CN CN201180068546.5A patent/CN103415630B/zh active Active
- 2011-12-22 ES ES11807691T patent/ES2848159T3/es active Active
- 2011-12-22 WO PCT/EP2011/073882 patent/WO2012085248A2/de active Application Filing
- 2011-12-22 US US13/997,585 patent/US20140020795A1/en not_active Abandoned
- 2011-12-22 EP EP11811026.1A patent/EP2656187B1/de active Active
- 2011-12-22 HU HUE11811025A patent/HUE055049T2/hu unknown
- 2011-12-22 EP EP11807691.8A patent/EP2655672B1/de active Active
Also Published As
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ES2829950T8 (es) | Procedimiento para producir componentes endurecidos | |
BR112015004373A2 (pt) | implante adequado para osteotomia do calcâneo | |
BR112013020540A2 (pt) | métodos para preparação de conjugados | |
CO6890100A2 (es) | Tratamientos de combinación para hepatitis c | |
ES2603028T8 (es) | Procedimiento para la preparación de (Z)-alfa-fluoro-beta-amino-acrilaldehídos sustituidos | |
BR112013030423A2 (pt) | método para produção de biocoque | |
BR112013025299A2 (pt) | conjunto de ancoragem | |
BR112013003535A2 (pt) | método para formar espuma | |
BRDI7105705S (pt) | Configuração aplicada em suporte para aparelhos eletrônicos | |
BR112013015360A2 (pt) | aparelho para produzir absorventes | |
BRPI1007459A2 (pt) | método para produção de manômeros olefínicos | |
BR112013007237A2 (pt) | ''método para produzir um anticorpo anti-ig-1r'' | |
BRPI1011731A2 (pt) | dispositivo para produzir fechos | |
BR112013012873A2 (pt) | processo para preparar uma n, n-dialquiletanolamina | |
BR112012021070A2 (pt) | método para produção de cadaverina | |
BR112012001294A2 (pt) | métodos para prover feição em agulha | |
BR112013024413A2 (pt) | compostos e métodos para a preparação de diarilpropanos | |
BRDI7105327S (pt) | Configuração aplicada em estojo para peças de dominó | |
BR112013015601A2 (pt) | método para produzir 2-(triazinilcarbonil) sulfonanilidas | |
BRPI1010841A2 (pt) | método para a fabricação de fluoroalquilnitrilas | |
BR112013014581A2 (pt) | método para a fabricação de um diorgano-di-halossilano | |
BR112012000579A2 (pt) | método para conclusão do poço | |
BR112013000898A2 (pt) | disposição para uma trava | |
ES2404690B1 (es) | Quitanieves avanzado | |
ES1074173Y (es) | Pieza para solados |