US20070001336A1 - Cushion material formed of spring-structured resin-molded product, manufacturing method for the cushion material, and mold used for the manufacturing method - Google Patents

Cushion material formed of spring-structured resin-molded product, manufacturing method for the cushion material, and mold used for the manufacturing method Download PDF

Info

Publication number
US20070001336A1
US20070001336A1 US10/569,300 US56930006A US2007001336A1 US 20070001336 A1 US20070001336 A1 US 20070001336A1 US 56930006 A US56930006 A US 56930006A US 2007001336 A1 US2007001336 A1 US 2007001336A1
Authority
US
United States
Prior art keywords
cushion material
resin molded
molded article
dimensional structure
spring
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/569,300
Other languages
English (en)
Inventor
Sadao Nishibori
Tatsumi Kobayashi
Maki Shirai
Yuichiro Nakamura
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ein Co Ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of US20070001336A1 publication Critical patent/US20070001336A1/en
Assigned to EIN CO., LTD. TECHNICAL CENTER reassignment EIN CO., LTD. TECHNICAL CENTER ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KOBAYASHI, TATSUMI, NAKAMURA, YUICHIRO, NISHIBORI, SADAO, SHIRAI, MAKI
Abandoned legal-status Critical Current

Links

Images

Classifications

    • A—HUMAN NECESSITIES
    • A47—FURNITURE; DOMESTIC ARTICLES OR APPLIANCES; COFFEE MILLS; SPICE MILLS; SUCTION CLEANERS IN GENERAL
    • A47C—CHAIRS; SOFAS; BEDS
    • A47C27/00—Spring, stuffed or fluid mattresses or cushions specially adapted for chairs, beds or sofas
    • A47C27/12—Spring, stuffed or fluid mattresses or cushions specially adapted for chairs, beds or sofas with fibrous inlays, e.g. made of wool, of cotton
    • A47C27/122—Spring, stuffed or fluid mattresses or cushions specially adapted for chairs, beds or sofas with fibrous inlays, e.g. made of wool, of cotton with special fibres, such as acrylic thread, coconut, horsehair
    • A—HUMAN NECESSITIES
    • A47—FURNITURE; DOMESTIC ARTICLES OR APPLIANCES; COFFEE MILLS; SPICE MILLS; SUCTION CLEANERS IN GENERAL
    • A47C—CHAIRS; SOFAS; BEDS
    • A47C27/00—Spring, stuffed or fluid mattresses or cushions specially adapted for chairs, beds or sofas
    • A47C27/12—Spring, stuffed or fluid mattresses or cushions specially adapted for chairs, beds or sofas with fibrous inlays, e.g. made of wool, of cotton
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B62—LAND VEHICLES FOR TRAVELLING OTHERWISE THAN ON RAILS
    • B62J—CYCLE SADDLES OR SEATS; AUXILIARY DEVICES OR ACCESSORIES SPECIALLY ADAPTED TO CYCLES AND NOT OTHERWISE PROVIDED FOR, e.g. ARTICLE CARRIERS OR CYCLE PROTECTORS
    • B62J1/00—Saddles or other seats for cycles; Arrangement thereof; Component parts
    • B62J1/18—Covers for saddles or other seats; Paddings
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B62—LAND VEHICLES FOR TRAVELLING OTHERWISE THAN ON RAILS
    • B62J—CYCLE SADDLES OR SEATS; AUXILIARY DEVICES OR ACCESSORIES SPECIALLY ADAPTED TO CYCLES AND NOT OTHERWISE PROVIDED FOR, e.g. ARTICLE CARRIERS OR CYCLE PROTECTORS
    • B62J1/00—Saddles or other seats for cycles; Arrangement thereof; Component parts
    • B62J1/18—Covers for saddles or other seats; Paddings
    • B62J1/26—Paddings involving other resilient material, e.g. sponge rubber with inflatable compartments
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/02—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of forming fleeces or layers, e.g. reorientation of yarns or filaments
    • D04H3/03—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of forming fleeces or layers, e.g. reorientation of yarns or filaments at random
    • D04H3/037—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of forming fleeces or layers, e.g. reorientation of yarns or filaments at random reorientation by liquid
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/08—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of strengthening or consolidating
    • D04H3/16—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of strengthening or consolidating with bonds between thermoplastic filaments produced in association with filament formation, e.g. immediately following extrusion

Definitions

  • the present invention relates to a cushion material composed of a resin molded article having a spring structure, method of producing the same, and dies used in manufacture of the cushion material, more particularly to a method for producing a resin molded article with a spring structure which is excellent in shock resistance and load capacity, and has an ability to meet specific and non-specific needs in terms of shape and size in various industrial fields, that is, a material suitably used for producing any supports on which one can sit, rest or mount such as seats of automotive vehicles, motor cycles, bicycles, electric trains, and aircraft, saddles for horse riding, chairs, sofas and beds, and to a method for producing a cushion material which requires a low cost and burden for its disposal, and low production cost by simplifying production facilities, and improves the precision of molding, and apparatuses necessary for producing the cushion material.
  • a polyurethane foam is a mainstream material of cushions for seats and beds of automotive vehicles, motor cycles, bicycles, electric trains and aircraft.
  • cushions are used in some form or another in any supports on which one can sit, rest or mount regardless of whether they are exposed to vibrations during use or not.
  • polyurethane foam is widely used in various applications, and the wide spread of this material is ascribed to its being comparatively free from problems in production and cost.
  • a cushion pad for the seat of automobiles is disclosed, for example, in Japanese Patent No. 2995325 which proposes a cushion pad for the seat of automobiles.
  • a seat surface part is formed of a high resilience foam having a one layer structure
  • the high resilience foam is made of a polyurethane foam which contains 10 wt % or less of tolylene diisocyanate (TDI), and the remainder isocyanate formed by diphenylmethane diisocyanate.
  • Japanese Patent No. 2548477 proposes a cushion structure obtained by fusing polyester fibers with a high melting point to each other via a thermoplastic elastomer with a low melting point.
  • a cushion is proposed in Japanese Laid-Open Patent Publication (Kokai) No. 2000-51011, which is obtained by partially bonding synthetic fibers and natural fibers of 1 to 20 deniers with each other, via a synthetic rubber adhesive or cross-linking polyurethane.
  • polyurethane foam is so soft and elastic that, when man rests his weight on a seat made of polyurethane foam, he feels an upward thrust on his buttock, touching on a hard bottom, and vertical swing, and his feet may become numb and strongly tired if he rests on the seat for a long time.
  • a polyurethane seat for a car or motorcycle Take a polyurethane seat for a car or motorcycle as an example.
  • Demands with regard to the manufacture and structure of such a polyurethane seat are manifold, but the material itself is so uniform in density that, when a man sits on the seat, the distribution of pressures on the sitting surface changes from moment to moment, and thus polyurethane foam may not be suitable according to given functions assigned to the seat.
  • Manufacture of products of a polyurethane foam is generally achieved via blow foaming, and thus the product has a uniform spring property, or is conferred a number of roughly different spring properties. Therefore, it is difficult for the product of polyurethane foam to change its spring properties in accordance with given requirements.
  • the seat of a motor cycle must change its spring property according to the type of motor cycle, e.g., according to whether the motor cycle is for touring, road racing or motocross, or to the rider's posture during riding.
  • the rider must put or lift his weight on or off the seat as needed during racing, which, when repeated often over a long time, will cause the overall center of gravity to be elevated and unbalanced.
  • polyurethane foams are thermosetting resins. Therefore, polyurethane foams can only be recycled by crushing them into chips with a crusher, and bonding the chips into a material called chip foam (ribbon dead foam), or can only be burned for recovery of thermal energy.
  • the method of disposal of polyurethane foams includes landfilling and incineration.
  • stable lands cannot be created by using polyurethane foams since they are low in bulk density and soft, and hence landfill sites suitable therefor are limited.
  • Polyurethane foams may be processed into particles or powders to be disposed which requires, however, extra handling and costs.
  • incineration of polyurethane foams may generate hydrocyanic acid gases (hydrocyanic acid) which cause much damage to incinerators, and have to be eliminated at high costs.
  • hydrocyanic acid hydrocyanic acid gases
  • polyurethane foams have problems as described below.
  • Manufacture of a polyurethane foam mold is achieved by blowing a foaming material in a die (for example, for three minutes) and separating the mold from the die.
  • the separation process is complicated and molding time is long. It is difficult to clean polyurethane foams. This is because an amine catalyst used during manufacture is trapped in the foams, causing bad smell.
  • a polyurethane foam has a heat storage property, and is liable to be stuffy, and there is a fear that if the polyurethane foam is exposed to intensive light for a long time, it may start to burn. Its safety to environments is low.
  • TDI tolylene diisocyanate
  • the above-mentioned seat cushion pad for an automotive vehicle disclosed in Japanese Patent No. 2995325 is improved in the characteristics of the soft polyurethane foam, but still has the drawbacks of polyurethane foams.
  • the cushion structure proposed in the Japanese Patent No. 2548477 it is difficult to be recycled due to fusing polyester fibers with a high melting point via a thermoplastic elastomer with a low melting point, resulting in complicated manufacturing method and high cost for producing.
  • 2000-51011 offers advantages in that it has excellent air permeability and is cleanable, it suffers from disadvantages in that it has a low durability, a manufacturing method thereof is complicated, and a processing cost is remarkably high. Further, since the rubber adhesive and a crosslinkable polyurethane are thermoset resins, and the cushion is not of a single composition, it is difficult to recycle the cushion.
  • polyurethane foams have many problems as described above, there is no alternate agent to replace polyurethane that can be used not less suitably and cheaply than polyurethane as a cushion material of the seats of automotive vehicles, motor cycles, bicycles, electric trains, and aircraft, and of beds.
  • an object of the present invention is to provide a method for producing a cushion material composed of a resin molded article with a spring structure, that is, a material suitably used for producing any supports on which one can sit, rest or mount such as seats of automotive vehicles, motor cycles, bicycles, electric trains, and aircraft, saddles for horse riding, chairs, sofas and beds.
  • the object of the invention is to provide a method for producing a molded article which simplifies molding process, permits the manufacture of a mold comparatively freely in shape and size, requires a small cost for production, and readily produces a cushion which satisfies widely different requirements offered to springy articles such as: being resistant to sinking and, when a user sits on it, being capable of dispersing his weight uniformly over the sitting surface so that it does not fatigue the user even if he sits on it for a long time, and which is excellent in shock resistance and load capacity.
  • the object of the invention is to provide a method for producing a molded article which simplifies production facilities, lowers production cost, improves the precision of molding, reduces works required for processing, and can provide finished products in which ends of the product will not disintegrate of themselves even without deliberately resorting to trimming or rounding-off after molding.
  • the method of this invention for producing a cushion material composed of a resin molded article with a spring structure comprises the steps of forming a three-dimensional structure including voids at a predetermined bulk density which is obtained by contacting, entwining, and gathering adjacent ones of random loops or curls of continuous and/or short, solid and/or hollow filaments made from a thermoplastic resin; heating the three-dimensional structure placed in a female die directly and/or via the die to a temperature sufficiently high to soften the three-dimensional structure; compressing the three-dimensional structure by bringing a male die in tight contact with the female die; and hardening the three-dimensional structure by cooling.
  • the method preferably further comprises a step of removing superfluous ends of the three-dimensional structure protruding into strokes between the male and female dies using a heat cutter, to thereby thermally fuse the ends as well as to cut them off.
  • the “continuous and/or short filaments” preferably includes filaments made from general purpose plastics (polyolefins, polystyrene resins, methacryl resins, poly vinyl chloride, etc.) or engineering plastics (polyamide, polycarbonate, saturated polyester, polyacetal, etc.).
  • general purpose plastics polyolefins, polystyrene resins, methacryl resins, poly vinyl chloride, etc.
  • engineering plastics polyamide, polycarbonate, saturated polyester, polyacetal, etc.
  • thermoplastic elastomers such as polyethylene (PE hereinafter), polypropylene (PP hereinafter), and nylon.
  • the filaments are preferably made from a mixture obtained by adding a vinyl acetate resin (VAC hereinafter), ethylene vinyl acetate copolymer (EVA hereinafter), or styrene butadiene styrene (SBS hereinafter) to a polyolefin resin such as PE or PP.
  • VAC vinyl acetate resin
  • EVA ethylene vinyl acetate copolymer
  • SBS styrene butadiene styrene
  • the mixture ratio of the vinyl acetate content of the polyolefin resin to VAC or EVA is 70 to 97 wt % to 3 to 30 wt %, preferably 80 to 90 wt % to 10 to 20 wt %. If the VAC content were equal to or lower than 3 wt %, the impact resilience of the three-dimensional structure would be low.
  • the mixture ratio of the polyolefin resin to SBS is 50 to 97 wt % to 3 to 50 wt %, preferably 70 to 90 wt % to 10 to 30 wt %.
  • the polyolefin resin may be a regenerated resin.
  • the continuous and/or short filaments may be solid or hollow. If the continuous and/or short filaments are hollow, they are preferable because the air is entrapped in the hollow cavities of the filaments, and act as a spring which confers a characteristic spring property to the filaments. The air entrapped in the hollow cavities of the filaments also prevents the collapsing tendency of the filaments which would otherwise result from long and habitual use. The air entrapped in the hollow cavities of the filaments also preserves the rigidity of the three-dimensional structure.
  • the hollow cavities may be continuous with other ones or may be independent of each other. As one illustrative example, each of single hollow fibers may have hollow cavities with septa inserted between adjacent cavities.
  • the “solid continuous filaments and/or short filaments” preferably have a diameter of 0.3 to 3.0 mm, particularly 0.7 to 1.0 mm. If the solid continuous filaments have a diameter equal to or smaller than 0.3 mm, the filaments would lose resiliency and fuse to each other so strongly that their void ratio would become undesirably low. On the contrary, if the solid continuous filaments have a diameter equal to or larger than 3.0 mm, the filaments would become so resilient that they would not form loops and curls, nor fuse together, which would lead to the lowered strength. If the filaments include hollow filaments, they preferably have a diameter of 1.0 to 3.0 mm, particularly 1.5 to 2.0 mm.
  • the hollow filaments would lose the merit of reducing the weight of the product relative to its bulk. On the contrary, if the void ratio were equal to or higher than 80%, the hollow filaments would lose their cushioning activity.
  • the bulk density of the “resin molded article with a spring structure” may be 0.005 to 0.08 g/cm 3 , preferably 0.02 to 0.06 g/cm 3 . If the bulk density in question were 0.005 g/cm 3 or lower, the article would have a reduced strength. On the contrary, if the bulk density in question were 0.08 g/cm 3 or higher, the filaments would lose the merit of reducing the weight of the article with respect to its bulk.
  • the resin molded article with a spring structure may have a uniform density throughout its structure or may have a structure where high density and low density substructures repeat alternately at certain intervals.
  • the low density substructure may have a density of 0.005 to 0.03 g/cm 3 , preferably 0.008 to 0.03 g/cm 3 , most preferably 0.01 to 0.03 g/cm 3 .
  • the high density substructure may have a density of 0.03 to 0.08 g/cm 3 , preferably 0.04 to 0.07 g/cm 3 , most preferably 0.05 to 0.06 g/cm 3 .
  • the “cushion material” is preferably obtained by laminating multiple resin molded articles with a spring structure into a layered structure.
  • the cushion material is preferably used as a material of the seats of automotive vehicles, motor cycles, bicycles, electric trains and aircraft, saddles for horse riding, chairs, sofas and beds.
  • the cushion material may be used, in place of urethane foams, as a material of any supports on which one can sit, rest or mount regardless of whether they are exposed to vibrations or not.
  • the cushion material when used as a material of the seat of an automotive vehicle or motor cycle which is exposed to vigorous vibrations during use, it is preferred because it readily adapts to various individual requirements (e.g., suspension characteristic) of the vehicle because of its thickness being susceptible to external controls.
  • the “female die” is preferably made of concrete.
  • the concrete die dispenses with the use of a separating agent, and thus reduces the cost of molding.
  • the “male die” preferably consists of a product (base) to which the cushion material can be attached. Then, need for separate preparation of a male die can be safely avoided, which will allow the molding cost to be reduced, and precision of molding to be improved.
  • Cooling may consist of spontaneous cooling or forced cooling. Forced cooling is preferably based on the use of water.
  • the cushion material of the invention is more receptive to secondary processing than polyurethane, and can respond to needs from consumers with regard to particular functions more finely than polyurethane. Molding the cushion material is achieved by compression molding. Thus, it is possible to provide a product to match with the body shape of a given user, or in accordance with the order of a user which will further enhance the advantage of the product. Moreover, by adjusting the diameter of filaments constituting a resin molded article with a spring structure, material of the filaments, and their denier, bulk density and void ratio, it is possible to allow the resin molded particle to have a desired spring property.
  • individual filaments constituting the cushion material of the invention are equal in terms of spring property, they may be conferred different spring properties after having been differently compressed during compression molding. Therefore, it is possible to provide a cushion material in which different portions have different cushioning abilities and thus in which, when a weight is put thereon, the weight is supported in different manners according to the sites with which it is put into contact. Moreover, it is possible by adjusting the stroke of the male die to allow the mold to have a desired thickness.
  • the “male die” may be constituted with a base (which forms an element of the cushion material constituting the product) to which a resin molded article with a spring structure can be attached. Then, deliberate preparation of a male die dedicated for the purpose can be safely dispensed with, which will lead to the reduced production cost. Moreover, because part of the product is used as an element (molding part) of the molding apparatus, precision of molding will be improved. For raising or lowering the male die, it is preferable to use a pantograph type framework. As compared with a hydraulic cylinder or pneumatic cylinder which is used in a conventional apparatus for molding polyurethane, the framework in question is so simple that it will contribute to the reduction of production cost as well as to the simplification of production facilities.
  • the male die is preferably so constructed as to forbear a load weighing it or more. If the female die is made of concrete, it will be possible to safely dispense with the use of a separating agent which would be otherwise required, as well as to reduce production cost as compared with molding where metal dies are used for the same purpose. Moreover, since the molding process itself is simplified, and time required for molding is contracted, mass production of cushion materials will become possible. Cooling may consist of spontaneous cooling or forced cooling. Forced cooling is preferably based on the use of water.
  • ends of the article tend to disintegrate after molding, and thus require trimming or rounding-off subsequent to molding, which may be cumbersome.
  • the present article with a spring structure it is possible to trim ends of the article after compression molding by cutting and fusion using a heat cutter, and thus to dispense with the trimming process as above, which reduces superfluous works.
  • FIG. 1 shows a perspective view of a cushion material attached to a base 4 .
  • FIGS. 2 a and 2 b show frontal and rear views of the cushion material 1 attached to base 4 , respectively.
  • FIG. 3 shows a lateral view of a motor cycle 10 equipped with a seat composed of cushion material 1 .
  • FIGS. 4 a and 4 b show perspective views of base 4 viewed from different angles.
  • FIG. 5 illustrates a first step of the compression molding applied to the cushion material 1 .
  • FIG. 6 illustrates the first step of the compression molding applied to the cushion material 1 viewed from a different angle.
  • FIG. 7 illustrates a second step of the compression molding applied to the cushion material 1 .
  • FIG. 8 illustrates the second step of the compression molding applied to the cushion material 1 viewed from a different angle.
  • FIG. 9 illustrates a third step of the compression molding applied to the cushion material 1 .
  • FIG. 10 illustrates a step for attaching the cushion material 1 to a base.
  • FIG. 11 is a diagram schematically showing steps necessary for producing a resin molded article 30 having a spring structure.
  • FIG. 12 shows a perspective view of an apparatus for producing a resin molded article 30 having a spring structure according to the method of the invention.
  • FIG. 13 shows a perspective view of another apparatus for producing a resin molded article 30 having a spring structure according to the method of the invention.
  • FIG. 14 shows a perspective view of yet another apparatus for producing a resin molded article 30 having a spring structure according to the method of the invention.
  • FIGS. 15 a , 15 b and 15 c show the cross-sections of other resin molded articles 30 having a spring structure embodying the invention.
  • FIGS. 16 a , 16 b and 16 c show the cross-sections of yet other resin molded articles 30 having a spring structure embodying the invention.
  • FIGS. 17 a and 17 b show rear and perspective views of a molding die 622 , respectively.
  • FIGS. 18 a , 18 b and 18 c show the cross-sections of a resin molded article 30 having a spring structure and of threads 31 .
  • FIGS. 19 a and 19 b show the cross-sections of yet another cushion material 1 embodying the invention.
  • FIGS. 20 a and 20 b show the cross-sections of yet another cushion material 1 embodying the invention.
  • FIG. 21 illustrates another embodiment of compression molding necessary for molding a cushion material 1 .
  • FIGS. 22 a and 22 b illustrate yet another embodiment of compression molding necessary for molding a cushion material 1 .
  • FIGS. 23 a and 23 b illustrate an exemplary compression molding process applied to a cushion material 1 using a conventional apparatus.
  • FIG. 24 illustrates another exemplary compression molding process applied to a cushion material 1 .
  • FIGS. 25 a and 25 b illustrate yet another exemplary compression molding process applied to a cushion material 1 .
  • FIGS. 26 a and 26 b illustrate yet another exemplary compression molding process applied to a cushion material 1 using a conventional apparatuses.
  • the cushion material 1 is obtained by preparing a thermoplastic resin (e.g., thermoplastic elastomer) such as a blend obtained by mixing, for example, a polyolefin resin such as PE, PP, etc., with VAC, EVA or SBS, and by processing the blend into a resin molded article 30 with a spring structure or a three-dimensional structure, and subjecting the article or the structure to compression molding.
  • a thermoplastic resin e.g., thermoplastic elastomer
  • a blend obtained by mixing, for example, a polyolefin resin such as PE, PP, etc., with VAC, EVA or SBS
  • VAC polyolefin resin
  • the resin molded article 30 with a spring structure used in this embodiment of the invention is a three-dimensional structure having voids which is obtained by contacting, entwining, and gathering adjacent ones of random loops or curls of continuous and/or short filaments (simply filaments 31 hereinafter) made from the above-described blend.
  • the filaments exist as plural loops and curls (see the inset figure A of FIG. 1 which enlarges a part of interest).
  • the resin molded article 30 with a spring structure comprises hollow filaments 31 whose cross-section 31 a is shown in the figure (see the inset figure B of FIG. 1 which enlarges another part of interest).
  • the bulk density of the three-dimensional structure may be 0.005 to 0.03 g/cm 3 , preferably 0.008 to 0.03 g/cm 3 , most preferably 0.01 to 0.03 g/cm 3 .
  • the void ratio of the three-dimensional structure may be 96 to 99%, preferably 97 to 99%, most preferably 97 to 98%.
  • the cushion material 1 is obtained by subjecting the resin molded article 30 with a spring structure to compression molding.
  • the cushion material of this embodiment is mainly used as a material of the seat of an automotive bicycles (e.g., motor cycles 10 ).
  • the cushion material 1 has a bilayered structure consisting of two sheet layers (overlying sheet layer 2 and underlying sheet layer 3 ).
  • the two sheets may have the same spring property, or different spring properties.
  • the two sheet layers are preferably bonded to each other with an adhesive agent or double-faced tape. It is possible to cause the two sheet layers or different portions of each sheet layer to have different spring properties by appropriately adjusting the density of resin molded article 30 with a spring structure, its material, and/or the diameter of filaments of the article constituting the sheet layers.
  • the two layers preferably have different spring properties such that, for example, the overlying sheet layer gives a rigid feel while the underlying sheet layer a soft feel.
  • the overlying sheet layer 2 is less rigid or softer than the underlying sheet layer 3 .
  • the overlying sheet 2 preferably has the bulge of its upper surface modified to fit to the shape of rider's buttock when the rider takes a riding posture on the seat.
  • the underlying sheet layer 3 is fixed to base 4 , it must be harder than the overlying sheet layer 2 .
  • the cushion material is preferably constructed such that its shape is maintained via the hardness of the underlying sheet layer 3 .
  • the cushion material 1 has a characteristic suspension property due to the underlying sheet layer 3 .
  • a conventional seat of an automotive bicycles using urethane foam usually receives a strong counter force (kick back) from the road surface after it exerts a downward spring move towards the road.
  • the conventional seat of a motorcycle made from a polyurethane foam often contains coil springs intimately bonded to the polyurethane foam.
  • the seat has a bilayered structure: the softer overlying sheet layer 2 is for receiving human weight while the harder underlying sheet layer 3 is for absorbing downward spring properties. This structural feature can dispense with the use of coil springs.
  • the seat of this embodiment is advantageous in weight and structure, in simplicity and in that it does not require the introduction of any special facilities for absorbing downward spring properties. Moreover, the bulk of the seat is comparatively low, and thus the center of gravity lowers, which helps to stabilize the rider's posture during riding. Further, it is possible by adjusting the stroke of the male die to allow the cushion material 1 to have desired thickness for its different portions. Thus, it is possible by adjusting the stroke of the male die to produce cushion materials different in size, shape and profile to meet different suspension requirements.
  • the cushion material 1 is composed of a resin molded article 30 with a spring structure, its air permeability is so high that it naturally rejects the sojourn of moisture. Moreover, if cooled or warmed air transmitted through a duct from an air conditioner is permitted to pass through the cushion material of the seat of motorcycle 10 , the rider can cool or warm his body during riding. If the same equipment is incorporated in the seat of an automotive vehicle, the vehicle can enjoy the state-of-the art function without resorting to any special facilities for the purpose.
  • the shape of the cushion material 1 having a bilayered structure comprising the overlying sheet layer 2 and underlying sheet layer 3 is not limited to the one described above with reference to figures, but may take any shape as desired according to given applications.
  • the cushion material 1 may have a single-layered structure.
  • the cushion material may have a multiple-layered structure comprising two or more layers.
  • at least one underlying layer may be made of a synthetic rubber but at least one of the layers (preferably overlying layers) is preferably made of a thermoplastic resin.
  • the shape of a bulge is not limited to the one described above.
  • the shape, profile and size of a cushion material may be appropriately modified so as to finely meet given requirements such as product standards, functions, and individual customers' needs.
  • a kilt cushion material composed of a resin molded article with a spring structure (stitched manually or with a sewing machine) over another cushion material having a multiple-layered structure (e.g., the overlying sheet layer 2 of cushion material 1 ), and to use the assembly as a top-sheet of the seat (not illustrated here).
  • a kilt cushion material composed of a resin molded article with a spring structure (stitched manually or with a sewing machine) over another cushion material having a multiple-layered structure (e.g., the overlying sheet layer 2 of cushion material 1 ), and to use the assembly as a top-sheet of the seat (not illustrated here).
  • the seat of motorcycle it is possible to modify the size, shape and profile of the seat of motorcycle in accordance with the type of the motorcycle, or the body form of the rider.
  • the seat is for a motorcycle 10 or an automotive vehicle whose user (e.g., professional driver) is strict about driving posture, it is possible to modify the size, shape and profile of the seat in accordance with requirements from the user so that the seat can exactly fit to his driving posture and performance, which will confer the seat an additional merit.
  • Both the overlying sheet layer 2 and underlying sheet layer 3 have shapes corresponding with that of base 4 .
  • the base 4 forms a basement of the seat of motorcycle 10 .
  • the base 4 has a stopper portion 4 a on its frontal side and bulge 4 b on its rear side.
  • the bulge 4 b has, on its bottom surface, brackets 4 c with which the seat is fixed to the frame of motorcycle 10 .
  • the base 4 has several (e.g., six) cushions 4 d made from rubber attached to its bottom surface. Otherwise, many grooves and holes are formed as shown in the figures.
  • FIGS. 5 to 10 An apparatus for producing a cushion material 1 embodying the invention and method therefore will be described with reference to FIGS. 5 to 10 .
  • a method for producing a resin molded article 30 with a spring structure will be described later.
  • FIG. 5 shows a lateral view of a system for producing a cushion material 1 which is introduced for illustrating a first stage of compression molding required for molding the cushion material.
  • FIG. 6 shows a frontal view of the same system for illustrating the first stage of compression molding.
  • one or more resin molded articles 30 with a spring structure is placed in a female die 11 made of concrete (simply female die 11 hereinafter).
  • At least two resin molded articles 30 may have the same spring property or different spring properties from each other.
  • each resin molded article 30 is a three-dimensional structure having voids obtained by contacting, entwining, and gathering adjacent ones of random loops or curls of filaments 31 (see the inset figure C of FIG. 5 which enlarges a part of interest).
  • hot water preferably having a temperature of 70° C. or higher
  • a hot water feeder 13 is allowed to enter into the cavity 12 formed within the male die 11 , to thereby heat the resin molded articles 30 with a spring structure to soften them.
  • Feeding hot water into the cavity of female die 11 is for permitting the hot water to penetrate the resin molded articles 30 and to heat them from inside of the female die 11 .
  • the female die 11 itself may be heated with a heater.
  • a heat conductor e.g., heater
  • the female die 11 are covered with a thermally insulating material (e.g., with a box made of wood or of a foaming resin).
  • a thermally insulating material e.g., with a box made of wood or of a foaming resin.
  • the hot water feeder 13 may be substituted for a steam feeder 17 or the like. When a steam feeder 17 is used, steam inlets are formed on the wall of the female die 11 so that steam can enter the cavity 12 within the die via the inlets.
  • Steam is preferably injected into the die when closure of dies occurs to thereby heat the mold. This mode of heating is preferred because it allows the uniform transmission of a high temperature to the mold.
  • steam heating is preferred because steam not only heats the mold but also can apply a pressure on it. Steam heating is also effective for pressurizing a mold while heating it, when the mold has such a complicated structure as to reject uniform pressurization when mechanically pressurized.
  • Preparation of the female die 11 may be achieved, for example, as follows.
  • a framework is prepared from an appropriate material such as gypsum or the like.
  • the framework is reversed and fixed on a horizontal plate, a separating agent is applied on the framework or the plate, a concrete powder is kneaded with water to give a paste, the paste is poured into the space enclosed by the framework, and the framework is removed to give a concrete die.
  • the framework is reversed again to the original position, and the framework and horizontal plate are removed to isolate a concrete female die 11 .
  • the preparation process it is possible by forming a space below the horizontal plate attached to the framework, and by adjusting the height of the space to alter the strength, rigidity and thickness of concrete as desired. For example, to increase the thickness of concrete, it is only necessary to lower the fixing position of the plate. Since concrete is highly moldable, and easily produces a desired mold when poured into a framework to be hardened, the production cost of the concrete female die 1 is comparatively low ( 1/50 to 1/100 times as low as the production cost required for a similar die prepared via a conventional die). Concrete further allows the production of female molds 11 having complicated shapes, and mass production of the same mold with improved precision. For example, for molding molds of the same size, the same master framework can be used repeatedly.
  • the concrete die comes into close contact with a melt, only tight closure of mating dies allows the formation of a mold each of which external faces is polished as smooth as an abraded surface. If the framework has a negative relief pattern on its inner wall, the pattern will be transferred to the corresponding outer wall of a mold. Or, if mating dies are closed with a vinyl sheet placed in between, the external surfaces of the mold will have an impression reminiscent of the texture or surface print of the vinyl sheet.
  • the female die 11 is made of concrete, it can safely withstand a high pressure that is applied while a cushion material 1 is molded, and its durability is so high as to withstand repeated usage as many as several tens thousand times moldings.
  • the weight of the female die 11 is preferably 50 to 100 kg.
  • the male die 14 is constituted with a base 4 and male platform 14 a (see FIGS. 4 a and 4 b ).
  • the male die 14 is fixed at several points via fixtures to the distal end of a pantograph jack 15 .
  • the male die 14 being activated by the pantograph jack 15 , mates with the female die 11 to thereby apply a pressure from upward onto the resin molded article 30 with a spring structure placed in the cavity 12 of the female die 11 .
  • the male die 14 is preferably so sturdy as to withstand a pressure of 10 t or higher.
  • a plurality of (e.g., three) pantograph jacks 15 are attached to one male die 14 .
  • the pantograph jack 15 may be operated manually, or may be automatically operated being connected to a motor 15 a as needed.
  • the proximal end of pantograph jack 15 is fixed to a roof 18 , and the roof 18 is supported by pillars 19 on the top edges of the female die 11 .
  • Introduction of the pantograph jack 15 allows the structure of the system to be simplified which leads to the reduction of cost.
  • the pantograph jack 15 may be substituted for a hydraulic or pneumatic cylinders or the like.
  • the male die 14 preferably includes, as its element, a base 4 which also serves as an element of the product.
  • the base 4 is attached to the male die platform 14 a with the bottom surface of the former facing to the lower surface of the latter.
  • the upper surface of the male die platform 14 a is fixed via joining members to the pantograph jack 15 . Since part of the product (base 4 ) also comprises as an element (male die 14 ) of the molding apparatus, it is only necessary to prepare a female die 11 and separate preparation of a male die 14 can be safely dispensed with. With the conventional system for molding polyurethane foams, it is necessary to prepare male and female dies separately. However, with the system operating according to the method of the invention, since part of the product serves as an element of male die, preparation of a platen and punch is not needed, which leads to reduced costs and improved precision of molding.
  • FIG. 7 shows a lateral view of the system for producing a cushion material 1 which is introduced for illustrating a second stage of compression molding required for molding the cushion material
  • FIG. 8 shows a frontal sectional view of the same system for illustrating the second stage of the compression molding.
  • the pantograph jack 15 is activated to push the male die 14 (which is acted by the base 4 ) downward as indicated by the arrows in FIGS. 7 and 8 , to compress the mold.
  • the female die 11 is so adjusted as to allow the male die to enter into the cavity 12 to a deep level. Namely, the female die 11 can be adjusted so as to allow the male die 14 to enter into the cavity to a desired level.
  • the tapered angle of the inner lateral walls of the female die 11 is made smaller as needed than illustrated, it is possible to produce a cushion material whose profile has a desired slope angle.
  • the desired slope angle may include, for example, 1/50 to 1/400 (e.g., 1/200).
  • the slope angle may be inwardly or outwardly directed. If the female die 11 has a too large inward slope angle, it will be difficult to adjust the stroke between the two mating dies to a desired distance.
  • it is possible using the same pair of mating dies to produce various cushion materials 1 in accordance with given requirements. Particularly, it is possible to produce the same cushion materials 1 having various desired thickness.
  • a cushion material in accordance with a given personal order, that is, to produce cushion materials finely meeting personal needs of individual customers.
  • the parts of the seat facing the inner thighs of rider it is preferred to prepare the parts such that they have an enhanced density and rigidity at the cost of spring property. This improves the cushioning property and durability of the seat.
  • the outline of the seat is determined by the rider's riding posture, and is more or less constant.
  • the thickness of the seat may vary depending on the type (required suspension property) of the motorcycle.
  • a polyurethane foam is used as a cushion material, it is processed into a mold while foaming.
  • the mold undergoes uniform expansion during molding as long as the same dies are used.
  • it is necessary to prepare multiple pairs of mating dies if it is required to produce cushion materials having different densities and thickness. According to the production method of this invention, the problems encountered with the conventional method using polyurethane foams can be safely avoided.
  • FIG. 9 shows a flat view of the system for producing a cushion material 1 which is introduced for illustrating a third stage of compression molding required for molding the cushion material.
  • a heat cutter 16 is moved along the edges of the male die 14 to remove burrs 32 protruded from the edges of the male die 14 (see the inset figure of FIG. 9 which enlarges a part of interest) by cutting out those burrs as well as fusing the filament ends of the burrs.
  • the mold has its edges trimmed after molding to fit to a desired size, which complicates works involved in trimming.
  • the mold is easily trimmed. Particularly, since trimming is introduced at a stage subsequent to molding, it is possible to fuse the open ends of filaments of the burrs to prevent their disintegration during use, to dispense with the scaling step where the mold is tested for its size being as designed, and to simplify testing procedures subsequent to molding.
  • Cooled water is poured in the cavity 12 of female die 11 to harden the resin molded article 30 with a spring structure.
  • the water is poured abruptly at one time instead of being slowly poured little by little, which leads to the reduction of time required for hardening.
  • the mold is separated from the dies. Whether a given mold hardens or not is determined by slightly relaxing the pantograph jack 15 to see whether there is any spring-back from the mold. If it is found that there is no spring-back from the mold, the mold sufficiently hardens. Then, cycles of alternate heating and cooling the female die 11 and/or resin molded article are repeated. If a mold is composed of hollow filaments, it is possible to prevent 30 from occurring spring-back by keeping a thermally equilibrated condition in consideration of the air masses kept in the hollow cavities of filaments.
  • FIG. 10 which illustrates how a cushion material 1 is attached to a base
  • an overlying sheet 2 and underlying sheet 3 both prepared as described above are placed one over another, and the assembly is laid over a base 4 .
  • a heat-shaped vinyl leather sheet 5 is laid over the assembly, and fixed to the base 4 with a stapler.
  • fixation of the vinyl leather sheet 5 to the base 4 may be achieved via an adhesive tape.
  • the underlying sheet 3 is allowed, during molding, to have indents (or recesses) which engage with corresponding recesses (or indents) formed on the base 4 , it is possible for the assembly to be safely fixed to the base without requiring the use of a stapler or double-faced tape.
  • Layering of the overlying sheet 2 on the underlying sheet 3 may be stabilized by inserting a bonding agent or adhesive tape between the two opposite surfaces.
  • the two sheets may have indents or recesses on their opposing surfaces which will engage with each other when the two sheets are assembled. Then, assemblage of the two sheets does not require the use of a bonding agent or adhesive tape. It should noted, however, that assemblage of the overlying sheet 2 , underlying sheet 3 and base 4 may not require any deliberate fixation procedure, as far as they are covered with a vinyl leather sheet 5 in the finishing process.
  • a polyolefin resin such as PE, PP or the like and another resin such as VAC, EVA or SBS are fed, in appropriate amounts, via a supplier such as a tumbler, feeder or metering feeder, and the start resin is dry-blended, mixed, or dissolved in a solvent, kneaded and fragmented into pellets.
  • the powdery mixture or pellets are transferred to a hopper 21 of an extruder 20 .
  • start resins e.g., PP and SBS are mixed with a tumbler (KR mixer, Kato Scientific Instruments Co.) at 40 rpm for 15 minutes.
  • a mixture comprising the start resins is poured via a hopper 21 to a uni-axial (axis diameter being 65 m) extruder 20 .
  • the mixture is melted at a predetermined temperature (e.g., 200 to 260° C.), and the melt is kneaded and subjected to melt-extrusion at a predetermined speed through a plurality of nozzles, taken off by a winder 23 which will be described later, and formed into solid and/or hollow continuous filaments 31 having a predetermined diameter (e.g., 600 to 90,000 deniers, preferably 3,000 to 30,000 deniers, more preferably 6,000 to 10,000 deniers).
  • a predetermined diameter e.g., 600 to 90,000 deniers, preferably 3,000 to 30,000 deniers, more preferably 6,000 to 10,000 deniers.
  • the filaments 31 in a fused state are caused to form loops having a diameter of 1 to 10 mm, preferably 1 to 5 mm, and are taken off by the winder within a (water) bath 25 while bringing adjacent ones of the filaments into contact with each other within the water to be entwined forming random loops.
  • the contacted and entwined portions of the filaments are at least partially fused and bonded to one another.
  • the filaments 31 may comprise solid filaments and hollow filaments at a predetermined ratio.
  • the thickness and bulk density of the three-dimensional structure or a mass of random loops may be determined as appropriate by adjusting the stroke between take up rolls 24 , 24 of the winder 23 in the bath 25 .
  • the three-dimensional structure e.g., 10 to 200 mm in thickness and 2,000 mm in width
  • the three-dimensional structure obtained by processing filaments 31 so as to form a mass of random curls or loops, and hardening them in water, is applied to another pair of take-up rolls 26 , 26 to produce a resin molded article 30 with a spring structure.
  • the three-dimensional structure when it is required to have a comparatively high bulk density, should have a bulk density of 0.03 to 0.08 g/cm 3 , preferably 0.04 to 0.07 g/cm 3 , most preferably 0.05 to 0.06 g/cm 3 .
  • the three-dimensional structure when it is required to have a comparatively low void ratio, should have a void ratio of 91 to 97%, preferably 92 to 96%, most preferably 93 to 94%.
  • the take-off speed of the winder 23 is adjusted to a low take-off speed at intervals of e.g., 3 to 5 m by e.g., reducing the take-off speed of take up rolls 24 , 24 to a low predetermined level at certain predetermined regular intervals. Then, it is possible to obtain a resin molded article 30 with a spring structure comprising a series of alternate high-density portions and low-density portions repeating at regular intervals (e.g., 30 to 50 cm) in a longitudinal direction, the high-density portions being formed when filaments are taken off at a low take-off speed while the low-density portions being formed when filaments are taken off at a high take-off speed.
  • a three-dimensional structure such as a resin molded article 30 with a spring structure will hardly be bent by the take-up rolls 24 , 24
  • the resin molded article 30 with a spring structure obtained via the above-described processes are cut with a cutting device 27 into pieces having a desired length.
  • the bath 25 is equipped with inlet and outlet valves (not illustrated here).
  • FIG. 14 As seen from the frontal view of another apparatus shown in FIG. 14 where a cutting device 127 is placed in a water bath 125 , the cutting device 127 is put below a winder 123 , and a transport device 128 comprising a conveyor carrying multiple joining spikes on its surface is placed in the water bath 125 opposite to the winder.
  • the conveyor carries spring structure pieces obtained by cutting a three-dimensional structure at predetermined sites by piecing joining spikes into the pieces and thereby capturing them on its surface.
  • the elements corresponding with those of the foregoing embodiment are represented by similar numerals with, however, 1 being attached to the third place of the numerals.
  • a resin molded article 30 having a spring structure which has, for instance, a bulk density of 0.03 g/cm 3 and thickness of 50 mm.
  • the three-dimensional structure can be manufactured by using sub-structures which include one type of property or a combination of a plurality of types of properties different from each other.
  • Resin molded articles 30 with a spring structure representing embodiments other than the foregoing ones will be described below. Their molding is based on the viscosity of start resins.
  • a resin molded article 130 with a spring structure As shown in FIG. 15 a where the cushion property is weakened gradually or at predetermined regular intervals as a testing probe advances from the periphery to the core.
  • the periphery is constituted with a hard portion 130 a while the core with a soft portion 130 b .
  • This distribution of cushion property may be reversed as seen from a resin molded article 230 with a spring structure shown in FIG.
  • a resin molded article with a spring structure like the one 130 is suitable as a cushion material of the seat of a motorcycle 10 . Since the cushion material 1 has hard lateral surfaces, they adequately fit to the medial bulges of the rider's thighs when the rider mounts on the seat and takes a riding posture, which leads to stable driving.
  • a resin molded article with a spring structure like the one 230 is suitable as a material of a helmet.
  • a single three-dimensional structure of which the surface (contacts with the scalp) is soft while the core is rigid enables the production of caps (sun hats and helmets) which will not disturb the hair style. Such a cap is preferable because it prevents the penetration of sun beams but permits excellent air permeability.
  • the cushion material of a seat may achieve its assigned function as long as it has a sufficiently rigid external surface, depending on the weight applied on the seat and bending it undergoes when loaded with the weight.
  • a resin molded article with a spring structure by preparing plural thin three-dimensional structures each having a different density, and laminating them in an appropriate combination into a single layered structure, instead of preparing a single three-dimensional structure which comprises portions having different densities.
  • This method permits the amount of resins used for preparing a spring structure to be saved, and improves productivity. For example, it is possible to obtain a resin molded article with a spring structure 430 shown in FIG.
  • each cavity includes a clamp 530 b like a metal brace.
  • the clamp 530 b may be inserted into the cavity prior to or subsequent to compression molding.
  • the diameter of filaments 31 constituting a resin molded article 30 with a spring structure is not necessarily uniform. Even if a single cushion material is used as a seat, the weight imposed on a given portion differs depending on which part of the seat the portion occupies. Enhancing the rigidity of a given portion can be achieved by altering the bulk density of that portion as well as by modifying the diameter and/or hardness of filaments constituting the portion. For example, it is preferable to distribute thick and/or rigid filaments to a portion which comes into contact with the rider's buttock and sustains a large part of his weight during riding.
  • the molding die 622 has nozzles prepared as shown in FIG. 17 a such that nozzles 622 a corresponding to the central portion have a larger diameter than the remaining nozzles 622 b . If this molding die 622 is used, thick filaments 631 are extruded from its central portion together with normal thin filaments 31 extruded from the remaining portions as shown in FIG. 17 b . It is possible to obtain a spring structure where the rigidity is altered in a complicated manner, by using such a molding die as described above.
  • a cushion material which comprises filaments having the same thickness and bulk density with those of a comparable structure but is softer or harder than the comparable structure, by employing a filament material different from what is used in the comparable structure.
  • the cushion material 1 is used as the seat of a motorcycle 10 , it is possible to employ a different filament material in accordance with the weight of a user, which will increase the marketing value of the seat.
  • hollow filaments 731 with metal wires by not only entwining the former with the latter, but inserting the latter through the cavity of the former as shown in a sectional view of a combined filament of FIGS. 18 b and 18 c.
  • a female die 11 and male die 14 are closed to compress a mold to produce a resin molded article 30 with a spring structure
  • a cushion material 101 as shown in FIG. 19 a where a lower portion 101 a (plate-like portion) is rigid while an upper portion 101 b is soft.
  • the edges 101 c are preferably heated to be formed into rigid plate-like portions.
  • edge portions 101 c where filament ends are curled by heating are preferably processed to take a plate-like form during trimming.
  • the edge portions 101 can snugly mesh with the corresponding edges of a base 4 .
  • the edge portions 101 c are expanded, and allowed to return by spring property, to thereby mesh with the corresponding edges of the base.
  • This arrangement allows the cushion material to be attached to the base without requiring the use of a stapler, or to be detached from the latter.
  • the female die 11 When a female die 11 and male die 14 are closed to compress a mold to produce a resin molded article 30 with a spring structure, the female die 11 may be hotly burnt so as to raise the temperature of the die to such a high level as to melt the surface of a mold which, when hardened, forms a hard skin covering the mold (epidermis molding). With this method, it is possible to melt and harden only the superficial skin 201 a of a mold or resin molded article 30 with a spring structure as seen from a cushion material 201 of FIG. 19 b , which will dispense with later coating (e.g., coating with a vinyl leather 5 ). This method is also applicable for molding an instrument panel using a resin as a material.
  • the epidermis molding based on hot burning is preferably employed to form the superficial skin 201 a.
  • the cushion material 1 constituted with a resin molded article 30 with a spring structure of this embodiment is highly air-permeable, it is more preferable depending on given applications to dispense with the use of a vinyl leather 5 than to cover the cushion material 1 with the leather. If the use of a vinyl leather is omitted, a resin molded article 30 with a spring structure is preferably covered with a net 306 as seen from the cushion materials 301 shown in FIGS. 20 a and 20 b .
  • the net 306 may be applied over the cushion material 301 after compression molding.
  • the net 306 is preferably made of a water-repellent material (e.g., plastics).
  • the net 306 can maintain its excellent air permeability, and thus the seat is conveniently used even when the area is humid or the time is a wet season. Particularly such a seat is suitably used when incorporated in a buggy which usually runs on a sandy land.
  • the net 306 prevents the disintegration of a cushion material 301 so effectively that it improves the durability of the seat.
  • the mesh density of the net 306 is not limited to the one shown in the figure, but may be set to any desired level.
  • a vinyl leather sheet 5 may be applied over the net-covered cushion material. This is because, when the seat is incorporated in an electric train and is damaged intentionally, the seat can be prevented from the entry of foreign objects.
  • the female die 11 is placed downward while the male die 14 placed upwards, but positioning of the two dies may be reversed. If the reverse positioning is adopted, the female die 11 applies its weight on a mold during molding, and thus compression molding is achieved via pressures imposed by a compressor as well as via the weight of the female die.
  • Both the female die 11 and male die 14 are preferably made from concrete, metal or FRP (fiberglass reinforced plastics). If the heavier die is placed upward (pressing side) and allowed to mate with the opposite die placed downward, it is possible to exploit the weight of the upper die for compression molding. For example, compression molding may be achieved by placing one die made from heavier concrete upward, and the other die made from lighter concrete downward, or by placing one larger die upward and the other lighter die downward.
  • This embodiment incorporates a pantograph jack 15 to quickly apply a uniform pressure on a mold.
  • compression molding is achieved exploiting a pressure due to the heavier weight of a die placed upward, it may be possible to dispense with the use of a pantograph jack 15 .
  • a male die 114 is suspended with balancers 115 or the like each comprising a spring material, and compression molding is achieved by allowing the male die 114 to fall into the female die 111 due to its own weight as indicated by the arrows of the figure.
  • the male die 214 may be connected via a hinge 215 to the female die 211 as shown in FIG. 22 .
  • the male die 214 is opened to a predetermined angle, a resin melt is poured into the cavity within the female die 211 , the male die is moved as indicated by the arrow of the figure until it closes the cavity within the female die 211 , and thus compression molding is achieved by exploiting the weight of the male die 214 .
  • FIGS. 24 to 26 concern with other embodiments. With the systems shown in those figures, vertical positioning of the female die and male die may be reversed. With the systems, the concrete female die 11 placed upwards serves as a weight during compression molding. If the apparatus comprises a female die 111 suspended with balancers 115 made of a spring material, compression molding may be achieved by allowing the female die 111 to engage with the male die 114 due to its own weight as indicated by the arrows of the figure. Alternatively, the male die 214 may be connected via a hinge 215 to the female die 211 as shown in FIG. 22 .
  • the male die 214 is opened to a predetermined angle, the male die is moved as indicated by the arrows of the figure until it closes the cavity within the female die, and thus compression molding is achieved by exploiting the weight of the female die 211 in mating with the male die 214 .
  • the female die 11 is preferably made of concrete
  • a conventional apparatus adapted for molding polyurethane foams as profitably as the apparatus of the invention if the dies are modified such that their trimming margins can be increased, and accommodate the expansion of a mold as a result of molding, as shown in FIGS. 26 a and 26 b .
  • start resins liquids
  • an upper die 314 and lower die 314 are mated to be closed and the resins are allowed to foam in the cavity (foaming as a result of the mixture of two resins).
  • the apparatus may be modified as follows: a resin molded article 30 with a spring structure is placed in the cavity, the article is compressed by mating the two dies, and burrs protruded from the mating dies are removed via pressures generated as a result of intimate closure of the two mating dies. Then, it will be possible to obtain a cushion material 1 like the one representing an embodiment of the invention without resorting to a apparatus which incorporates concrete-made mating dies. Or, it is preferable to trim a mold with a heat cutter after the upper die has been removed.
  • the mating dies 311 , 314 of a conventional apparatus may be made from a metal such as iron.
  • the die is preferably made from concrete or metal, but may be made from a complex synthetic resin material such as FRP.
  • part e.g., lower die 311
  • a conventional apparatus start resins (liquids) are poured into the cavity, and an upper die (not illustrated) and lower die 311 are mated to be closed and the resins are allowed to foam in the cavity (foaming as a result of the mixture of two resins).
  • a resin molded article 30 with a spring structure is placed in a apparatus, and it may be compressed by mating a male die 314 with a lower die 311 equipped with a base 4 .
  • the temperature of atmosphere or temperature control is important for compression molding.
  • start resins soften and intermingle. However, the mixture does not occur at molecular levels because the resins do not melt completely.
  • the air masses entrapped in a mold are the same with those existent in the start resins.
  • a cushion material constituted with a resin molded article with a spring structure which has desired resistances to imposed weight and impact. Mass production of such a cushion material is also possible. Since the production of such cushion materials is based on compression molding, it is possible to freely modify the size and shape of individual products. If the cushion material is expected to be exposed to vertical vibrations, horizontal vibrations or complex vibrations, it is possible to confer bulges and recesses on both sides of a cushion material such that the cushion material can effectively absorb vibrations as much as possible.
  • burrs are cut as well as fused with a heat cutter which is moved along the edges of a male mold during closure of the two mating dies, trimming is quite easy. Particularly, since trimming is introduced at this stage of molding, disintegration of open filaments at the edges is safely prevented, and renewed trimming and scaling subsequent to molding which would be otherwise required can be safely dispensed with, which reduces works required for after-molding treatment.
  • a base to which a resin molded article with a spring structure is attached also acts as a male die, it is necessary to prepare only a female die for proper molding which will lead to reduced production costs. Furthermore, since the product itself is utilized as an element of the molding apparatus, precision of molding will be improved.
  • cushion materials different in property including their thickness by simply adjusting the stroke interval between the two mating dies and choosing an appropriate material (e.g., in filament diameter, texture, bulk density and void ratio). More specifically, according to the method of the invention, it is possible with a single apparatus to produce various cushion materials different in size, shape and density in accordance with individual requirements without resorting to multiple pairs of dies. For example, it is possible, when it is required to provide seats appropriate for the type of motorcycles or automotive vehicles, to provide seats whose thickness varies depending on the type (required suspension property) of the motorcycle or automotive vehicle.
  • cushion materials in which the distribution of spring properties and rigidities is adjusted as desired by simply varying the stroke width between the two mating dies, without modifying the physical properties of the cushion material itself.
  • a cushion material when a cushion material is used as a material of the seat of a motorcycle or automotive vehicle, it is possible to modify the cushion property of the cushion material in accordance with the type of motorcycle (for touring, road racing or motocross) without resorting to any complicated processes which would otherwise be required.
  • the cushion material is used as a material of the seat of a motorcycle for motocross, it may be prepared so as to absorb the weight of a rider. Then, the rider can steer the motorcycle while resting on the seat which will insure stability during riding.
  • the cushion material comprises two or more layers of sheets
  • it is possible to readily alter the properties of the cushion material by choosing appropriate constitutive resin molded articles with a spring structure (in terms of, e.g., diameter of filaments, material, bulk density, void ratio, etc.) or by adjusting the stroke width between the two mating dies.
  • a spring structure in terms of, e.g., diameter of filaments, material, bulk density, void ratio, etc.
  • combination of spring properties between the overlying layer and underlying layer can be altered as desired without resorting to any complicated processes: it is quite easy to combine overlying and underlying layers having the same spring property, as well as to combine an overlying layer having a certain rigidity with an underlying layer having a lower rigidity. It is also possible to combine overlying layers with underlying layers such that there is formed a stepwise stroke between adjacent layers to thereby produce a central ridge.
  • the cushion material is used as a material of the seat of a motorcycle or automotive vehicle, it is possible to modify the seat in accordance with the type of the motorcycle or automotive vehicle, or the body form of the rider.
  • the seat is for a motorcycle or automotive vehicle whose user (e.g., professional driver) is strict about driving posture, it is possible to modify the seat in accordance with requirements from the user so that the seat can exactly fit to his driving posture and performance.
  • the cushion material is used as a material of the seat of a motorcycle for motocross, it may be prepared so as to absorb the weight of a rider. Then, the rider can steer the motorcycle while resting on the seat which will insure stability during riding.
  • cushion materials are more easily produced than polyurethane foams undergoing secondary processing according to the conventional method.
  • a resin molded article of the present invention can be produced without generating toxic gases and hence insures good working conditions.
  • resins such as PE or the like may be recycled into edible oil containers of thermoplastic resins or biodegradable plastic films for agricultural use with an additional merit added.
  • Cushion materials made of a resin molded article with a spring structure themselves may be repeatedly recycled by melting used cushion materials and submitting the melt again to molding process.
  • the resin molded article according to the invention is so excellent in recyclability that it will not act as an undue load to environments even if it must be disposed of after use. Further, the resin molded article according to the invention can be manufactured at reduced costs since recycled resins can be used for producing the same.
  • the cushion material of the invention made of a resin molded article with a spring structure is highly durable and resistant to collapsing even after prolonged use, has a very small quantity of local sinking, and does not give a feeling of touching a hard bottom, and vertical swing. Moreover, the cushion material, when a user sits on it, uniformly receives the weight of the user on a whole region in contact with the cushion structure. Hence, the cushion material causes less fatigue of the user than a polyurethane foam-made cushion, and makes the user feel more relaxed. Thus, the cushion material of the invention can give a characteristic relaxed feeling to the user that can hardly be obtained from a polyurethane foam-made cushion.
  • the cushion material of the invention made of a resin molded article with a spring structure has such an excellent spring property that, when it is used as a material of the seat of an automotive vehicle or motorcycle, it will dispense with the use of coil springs which have been installed beneath the conventional seat of an automotive vehicle or motorcycle to absorb kick-backs from the road surface which would be otherwise a nuisance to the driver. This simplifies the structure of the seat, and lowers the center of gravity, which helps to stabilize the vehicle or motorcycle during running.
  • the resin molded article of the invention has a structure having completely continuous voids, it is so excellent in air permeability that it does not keep extra moisture. if cooled or warmed air transmitted through a duct from an air conditioner is permitted to pass through the cushion material of the seat of motorcycle, the rider can cool or warm his body during riding. Since the cushion material is resistant to water and will not degenerate when soaked with water, it may be profitably used as a material of the seat of a motorcycle. The cushion material may be washed with water, and will readily dry even when washed with water.
  • the method of the invention for producing a cushion material composed of a resin molded article having a spring structure is suitably used for providing a cushion material composed of a resin molded article with a spring structure, that is, a material suitably used as a supportive element of any supports on which one can sit, rest or mount such as seats of automotive vehicles, motor cycles, bicycles, electric trains, and aircraft, saddles for horse riding, chairs, sofas and beds, regardless of whether the seat is exposed to vibrations or not as a substitute for a conventional polyurethane foam-made cushion material.
  • the cushion material is used as a supportive element of a seat which is expected to receive no vibrations during use, it is only necessary to subject one surface of the cushion material to compression molding. On the contrary, if the cushion material is used as a supportive element of a seat which is expected to receive vigorous vibrations during use, for example, the seat of an automotive vehicle or motorcycle, it is preferable to overlap two or more cushion materials each comprising kilted resin molded article with a spring structure.
  • the molding apparatus uses, for compression molding, a pantograph jack instead of a hydraulic unit, the apparatus can have a simpler structure which will reduce production costs. Moreover, with this apparatus, it is easier to adjust the stroke width between mating dies.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Casting Or Compression Moulding Of Plastics Or The Like (AREA)
  • Mattresses And Other Support Structures For Chairs And Beds (AREA)
  • Moulds For Moulding Plastics Or The Like (AREA)
  • Laminated Bodies (AREA)
  • Springs (AREA)
US10/569,300 2003-08-26 2003-08-26 Cushion material formed of spring-structured resin-molded product, manufacturing method for the cushion material, and mold used for the manufacturing method Abandoned US20070001336A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2003/010798 WO2005018386A1 (ja) 2003-08-26 2003-08-26 スプリング構造樹脂成形品から成るクッション材及びその製造方法並びに前記製造方法に用いる型

Publications (1)

Publication Number Publication Date
US20070001336A1 true US20070001336A1 (en) 2007-01-04

Family

ID=34204224

Family Applications (1)

Application Number Title Priority Date Filing Date
US10/569,300 Abandoned US20070001336A1 (en) 2003-08-26 2003-08-26 Cushion material formed of spring-structured resin-molded product, manufacturing method for the cushion material, and mold used for the manufacturing method

Country Status (8)

Country Link
US (1) US20070001336A1 (zh)
EP (1) EP1665957B1 (zh)
CN (1) CN100586344C (zh)
AU (1) AU2003257560A1 (zh)
BR (1) BR0318457A (zh)
DE (1) DE60323166D1 (zh)
ES (1) ES2312865T3 (zh)
WO (1) WO2005018386A1 (zh)

Cited By (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009049116A1 (en) * 2007-10-11 2009-04-16 Nike International Ltd. Article of footwear with tubular sole assembly and method of manufacture
US20090124935A1 (en) * 2007-11-12 2009-05-14 Staszak Jeffrey R Bicycle Seat Sizer And Positioning Device
WO2009082483A1 (en) * 2007-12-21 2009-07-02 Compression Tech System and method of forming an article, and an article formed thereby
US20090212608A1 (en) * 2008-02-27 2009-08-27 Damon Rinard Bicycle seat system
WO2010028810A1 (de) * 2008-09-11 2010-03-18 Cepventures International Corporation Nachgiebiger aufbau für eine matratze, polster oder kissen
US20130020016A1 (en) * 2010-09-01 2013-01-24 C-Eng Co., Ltd. Method for forming cushions
US20150272332A1 (en) * 2014-03-31 2015-10-01 Tachi-S Co., Ltd. Cushion for seat and method of forming the same
US9221374B2 (en) 2013-09-27 2015-12-29 Ford Global Technologies, Llc Ventilated foam spring with twisting action for vehicle seat
US20160251789A1 (en) * 2013-10-29 2016-09-01 Toyobo Co., Ltd. Fibrous network structure having excellent compression durability
EP3351462A1 (en) * 2017-01-23 2018-07-25 Honda Motor Co., Ltd. Vehicle seat structure
EP3351464A1 (en) * 2017-01-23 2018-07-25 Honda Motor Co., Ltd. Vehicle seat structure
EP3441258A1 (en) * 2017-08-08 2019-02-13 Schukra Gerätebau GmbH Methods and devices for attaching a finishing element to a fiber cushion, and resulting fiber cushion
US10316444B2 (en) 2013-10-28 2019-06-11 Toyobo Co., Ltd. Elastic network structure with excellent quietness and lightweight properties
US10806272B2 (en) 2016-06-30 2020-10-20 Airweave Inc. Mattress core material and bed mattress
US20220314854A1 (en) * 2021-03-31 2022-10-06 Lear Corporation Seat support
US11518462B2 (en) * 2019-10-31 2022-12-06 Selle Italia S.R.L. Controlled deformation bicycle saddle
WO2023172483A1 (en) * 2022-03-08 2023-09-14 Lear Corporation Method for producing a vehicle interior component
US11807143B2 (en) 2021-12-02 2023-11-07 Lear Corporation Vehicle seating system and method for producing same
WO2023250026A1 (en) * 2022-06-22 2023-12-28 Lear Corporation Mesh structure and method of manufacture
EP4427904A1 (en) * 2023-03-06 2024-09-11 Lear Corporation Seat assembly, cushion, and tool and method of forming

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI597232B (zh) * 2012-05-07 2017-09-01 東洋紡股份有限公司 消音性與硬度優異之彈性網狀構造體
JP6311919B2 (ja) * 2014-02-13 2018-04-18 東洋紡株式会社 圧縮耐久性に優れた網状構造体
JP6311918B2 (ja) * 2014-02-13 2018-04-18 東洋紡株式会社 圧縮耐久性に優れた網状構造体
JP6318643B2 (ja) * 2013-10-29 2018-05-09 東洋紡株式会社 圧縮耐久性に優れた網状構造体
KR102288683B1 (ko) * 2015-04-28 2021-08-11 도요보 가부시키가이샤 망상 구조체
PL3290557T3 (pl) * 2015-04-28 2020-07-27 Toyobo Co., Ltd. Struktura typu siatki
JP2020141784A (ja) * 2019-03-05 2020-09-10 株式会社エアウィーヴ クッション部材およびその製造方法
CN112613131B (zh) * 2020-11-16 2024-03-19 南京航空航天大学 一种基于fsae的碳纤维座椅设计与加工方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5188791A (en) * 1990-04-02 1993-02-23 Savoie Refractaires Concrete composition for the manufacture of moulds, mould and process for the manufacture of a mould
US5234638A (en) * 1992-07-13 1993-08-10 Jang Jinn Fa Surfboard making process
US5366678A (en) * 1992-04-24 1994-11-22 Toyota Jidosha Kabushiki Kaisha Method of manufacturing cushion material
US5492662A (en) * 1994-10-17 1996-02-20 Kargol; James A. Process for forming multiple density body from fibrous polymeric material and vehicle seat component formed thereby

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3818252A1 (de) * 1988-05-28 1989-11-30 Borgers Johann Gmbh Co Kg Polsterteil fuer sitz-, liegemoebel od. dgl.
JP3686689B2 (ja) * 1994-08-23 2005-08-24 日本発条株式会社 繊維系クッション体の製造方法
JP3686692B2 (ja) * 1994-08-23 2005-08-24 日本発条株式会社 クッション体の製造方法
JPH0861413A (ja) * 1994-08-23 1996-03-08 Nhk Spring Co Ltd リサイクル可能なクッション体
JPH0938358A (ja) * 1995-07-31 1997-02-10 Achilles Corp クッション体の成形方法
JPH10128890A (ja) * 1996-10-31 1998-05-19 Itoki Crebio Corp クッション基体並びにクッション体及びそれらの製造方法
JP2000270975A (ja) * 1999-01-18 2000-10-03 Maruhachi Mawata Co Ltd 羽毛掛けふとん
JP2001197967A (ja) * 2000-01-20 2001-07-24 Maruhachi Mawata Co Ltd 羽毛掛けふとん
JP4499891B2 (ja) * 2000-08-16 2010-07-07 アイン興産株式会社 スプリング構造樹脂成形品及びその製造方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5188791A (en) * 1990-04-02 1993-02-23 Savoie Refractaires Concrete composition for the manufacture of moulds, mould and process for the manufacture of a mould
US5366678A (en) * 1992-04-24 1994-11-22 Toyota Jidosha Kabushiki Kaisha Method of manufacturing cushion material
US5234638A (en) * 1992-07-13 1993-08-10 Jang Jinn Fa Surfboard making process
US5492662A (en) * 1994-10-17 1996-02-20 Kargol; James A. Process for forming multiple density body from fibrous polymeric material and vehicle seat component formed thereby

Cited By (34)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090094858A1 (en) * 2007-10-11 2009-04-16 Ungari Joseph L Article of footwear with tubular sole assembly and method of manufacture
US7926204B2 (en) 2007-10-11 2011-04-19 Nike, Inc. Article of footwear with tubular sole assembly and method of manufacture
US20110154584A1 (en) * 2007-10-11 2011-06-30 Ungari Joseph L Article of footwear with tubular sole assembly and method of manufacture
WO2009049116A1 (en) * 2007-10-11 2009-04-16 Nike International Ltd. Article of footwear with tubular sole assembly and method of manufacture
US8650690B2 (en) 2007-10-11 2014-02-18 Nike, Inc. Article of footwear with tubular sole assembly and method of manufacture
US9314187B2 (en) 2007-11-12 2016-04-19 Trek Bicycle Corporation Bicycle seat sizer and positioning device
US20090124935A1 (en) * 2007-11-12 2009-05-14 Staszak Jeffrey R Bicycle Seat Sizer And Positioning Device
WO2009082483A1 (en) * 2007-12-21 2009-07-02 Compression Tech System and method of forming an article, and an article formed thereby
US20090212608A1 (en) * 2008-02-27 2009-08-27 Damon Rinard Bicycle seat system
WO2010028810A1 (de) * 2008-09-11 2010-03-18 Cepventures International Corporation Nachgiebiger aufbau für eine matratze, polster oder kissen
US9598803B2 (en) * 2010-09-01 2017-03-21 C-Eng Co., Ltd. Method for forming cushions
US8721825B2 (en) * 2010-09-01 2014-05-13 C-Eng Co., Ltd. Method for forming cushions
US20130020016A1 (en) * 2010-09-01 2013-01-24 C-Eng Co., Ltd. Method for forming cushions
US20140138016A1 (en) * 2010-09-01 2014-05-22 C-Eng Co., Ltd. Method for forming cushions
US9221374B2 (en) 2013-09-27 2015-12-29 Ford Global Technologies, Llc Ventilated foam spring with twisting action for vehicle seat
US10316444B2 (en) 2013-10-28 2019-06-11 Toyobo Co., Ltd. Elastic network structure with excellent quietness and lightweight properties
US20160251789A1 (en) * 2013-10-29 2016-09-01 Toyobo Co., Ltd. Fibrous network structure having excellent compression durability
US9938649B2 (en) * 2013-10-29 2018-04-10 Toyobo Co., Ltd. Fibrous network structure having excellent compression durability
US20150272332A1 (en) * 2014-03-31 2015-10-01 Tachi-S Co., Ltd. Cushion for seat and method of forming the same
US10806272B2 (en) 2016-06-30 2020-10-20 Airweave Inc. Mattress core material and bed mattress
EP3351462A1 (en) * 2017-01-23 2018-07-25 Honda Motor Co., Ltd. Vehicle seat structure
CN108340995A (zh) * 2017-01-23 2018-07-31 本田技研工业株式会社 车辆的座椅结构
JP2018118558A (ja) * 2017-01-23 2018-08-02 本田技研工業株式会社 車両のシート構造
CN108340996A (zh) * 2017-01-23 2018-07-31 本田技研工业株式会社 车辆的座椅结构
EP3351464A1 (en) * 2017-01-23 2018-07-25 Honda Motor Co., Ltd. Vehicle seat structure
CN108340995B (zh) * 2017-01-23 2020-09-08 本田技研工业株式会社 车辆的座椅结构
EP3441258A1 (en) * 2017-08-08 2019-02-13 Schukra Gerätebau GmbH Methods and devices for attaching a finishing element to a fiber cushion, and resulting fiber cushion
US11518462B2 (en) * 2019-10-31 2022-12-06 Selle Italia S.R.L. Controlled deformation bicycle saddle
US20220314854A1 (en) * 2021-03-31 2022-10-06 Lear Corporation Seat support
US11807143B2 (en) 2021-12-02 2023-11-07 Lear Corporation Vehicle seating system and method for producing same
WO2023172483A1 (en) * 2022-03-08 2023-09-14 Lear Corporation Method for producing a vehicle interior component
US20230286206A1 (en) * 2022-03-08 2023-09-14 Lear Corporation Method for producing a vehicle interior component
WO2023250026A1 (en) * 2022-06-22 2023-12-28 Lear Corporation Mesh structure and method of manufacture
EP4427904A1 (en) * 2023-03-06 2024-09-11 Lear Corporation Seat assembly, cushion, and tool and method of forming

Also Published As

Publication number Publication date
DE60323166D1 (de) 2008-10-02
CN1819788A (zh) 2006-08-16
EP1665957A4 (en) 2007-03-14
EP1665957B1 (en) 2008-08-20
WO2005018386A1 (ja) 2005-03-03
EP1665957A1 (en) 2006-06-07
AU2003257560A1 (en) 2005-03-10
ES2312865T3 (es) 2009-03-01
CN100586344C (zh) 2010-02-03
BR0318457A (pt) 2006-09-12

Similar Documents

Publication Publication Date Title
EP1665957B1 (en) Cushion material formed of spring-structured resin-molded product, manufacturing method for the cushion material, and mold used for the manufacturing method
US8932692B2 (en) Cushions comprising deformable members and related methods
US6409269B1 (en) Vehicle seat assembly with thermoformed fibrous suspension panel
US8628067B2 (en) Cushions comprising core structures and related methods
ES2694008T3 (es) Espumas compuestas a base de látex
AU779009B2 (en) Resin molded article having a spring structure and method of producing the resin molded article
MXPA06004139A (es) Resorte interior encerrado en espuma con componentes de espuma internos (triple caja).
JP5762418B2 (ja) クッションの成形方法
DE102010028554A1 (de) Fahrzeugsitzrahmen, -anordnung und -herstellungsverfahren
CN101304679A (zh) 使用竖直搭接纤维的座椅座垫
JPH0861414A (ja) クッション体とその製造方法
JP2003250667A (ja) スプリング構造樹脂成形品から成るクッション材及びその製造方法
RU2342895C2 (ru) Способ изготовления амортизирующего материала из формованного полимерного продукта (варианты) и амортизирующий материал (варианты)
TWI248860B (en) Cushion material composed of a resin molded article having a spring structure and a method of producing the same and dies used in manufacture of the cushion material
JP4011367B2 (ja) スプリング構造樹脂成形品から成るクッション材の製造方法
JPH0861413A (ja) リサイクル可能なクッション体
JP2003251090A (ja) スプリング構造樹脂成形品から成るクッション材の製造方法
JP2003310395A (ja) スプリング構造樹脂成形品から成るベッド、その製造方法並びにスプリング構造樹脂成形品からなるベッドクッション
JP2003253551A (ja) スプリング構造樹脂成形品から成るクッション材の製造方法
KR20060079843A (ko) 스프링구조 수지성형품으로 이루어진 쿠션재 및 그쿠션재의 제조방법 및 상기 제조방법에 이용되는 틀
JP2003250668A (ja) スプリング構造樹脂成形品から成るクッション材の製造方法
JP2003245926A (ja) スプリング構造樹脂成形品から成るクッション材の製造方法及び該製造方法において用いられるコンクリート製雌型
JP2000316677A (ja) クッション体とその製造方法および製造装置
Reynolds et al. Automotive cushioning through the ages

Legal Events

Date Code Title Description
AS Assignment

Owner name: EIN CO., LTD. TECHNICAL CENTER,JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NISHIBORI, SADAO;KOBAYASHI, TATSUMI;SHIRAI, MAKI;AND OTHERS;REEL/FRAME:024164/0353

Effective date: 20100315

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION