US20040245209A1 - Method for fabricating a carbon nanotube array and a biochip using the self-assembly of supramolecules and staining of metal compound - Google Patents

Method for fabricating a carbon nanotube array and a biochip using the self-assembly of supramolecules and staining of metal compound Download PDF

Info

Publication number
US20040245209A1
US20040245209A1 US10/859,530 US85953004A US2004245209A1 US 20040245209 A1 US20040245209 A1 US 20040245209A1 US 85953004 A US85953004 A US 85953004A US 2004245209 A1 US2004245209 A1 US 2004245209A1
Authority
US
United States
Prior art keywords
cnt
supramolecules
bioreceptor
biochip
thin film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/859,530
Other languages
English (en)
Inventor
Hee Jung
Dae Jung
Ki Kwon
Su Lee
Do Choi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Korea Advanced Institute of Science and Technology KAIST
Original Assignee
Korea Advanced Institute of Science and Technology KAIST
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Korea Advanced Institute of Science and Technology KAIST filed Critical Korea Advanced Institute of Science and Technology KAIST
Assigned to KOREA ADVANCED INSTITUTE OF SCIENCE AND TECHNOLOGY reassignment KOREA ADVANCED INSTITUTE OF SCIENCE AND TECHNOLOGY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CHOI, DO HWAN, JUNG, DAE HWAN, JUNG, HEE TAE, KWON, KI YOUNG, LEE, SU RIM
Publication of US20040245209A1 publication Critical patent/US20040245209A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B82—NANOTECHNOLOGY
    • B82B—NANOSTRUCTURES FORMED BY MANIPULATION OF INDIVIDUAL ATOMS, MOLECULES, OR LIMITED COLLECTIONS OF ATOMS OR MOLECULES AS DISCRETE UNITS; MANUFACTURE OR TREATMENT THEREOF
    • B82B3/00—Manufacture or treatment of nanostructures by manipulation of individual atoms or molecules, or limited collections of atoms or molecules as discrete units
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B32/00—Carbon; Compounds thereof
    • C01B32/15—Nano-sized carbon materials
    • C01B32/158—Carbon nanotubes
    • C01B32/16—Preparation
    • C01B32/162—Preparation characterised by catalysts
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B82—NANOTECHNOLOGY
    • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
    • B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B82—NANOTECHNOLOGY
    • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
    • B82Y40/00—Manufacture or treatment of nanostructures
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B82—NANOTECHNOLOGY
    • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
    • B82Y15/00—Nanotechnology for interacting, sensing or actuating, e.g. quantum dots as markers in protein assays or molecular motors
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B82—NANOTECHNOLOGY
    • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
    • B82Y5/00—Nanobiotechnology or nanomedicine, e.g. protein engineering or drug delivery
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B2202/00—Structure or properties of carbon nanotubes
    • C01B2202/08—Aligned nanotubes

Definitions

  • the present invention relates generally to a method for fabricating a carbon nanotube (CNT) nanoarray, which comprises the steps of forming a thin film of supramolecules on a substrate, inducing the self-assembly of the supramolecules by annealing to form a regular pattern, selectively staining the formed regular pattern with a metal compound, etching the metal compound-stained thin film to form a nanometer or smaller size metal catalyst pattern, and growing carbon nanotubes (CNTs) vertically on the formed metal catalyst pattern.
  • the invention also relates to a method for fabricating a biochip, including attachment of a bioreceptor to the above fabricated CNT array.
  • Korean patent No. KR 10/263671B1 discloses a method for forming nanometer-sized fine patterns using supramolecules as a patterning material.
  • the thickness of fine pattern remaining in a groove is ensured using one additional buffer layer in order to ensure a margin for excessive etching, and a spacer is also formed on the buffer layer in order to reduce the size of the groove.
  • the number of process steps is large, and the pattern size is a level of several tens of nanometers.
  • Korean patent publication No. KR 2002-0089528A discloses a small-sized, self-assembled structure for forming devices that are widely used in the microelectronic industry.
  • the self-assembly method disclosed in this application provides the ability to form arrays in association with a surface, but it is impossible for the self-assembly itself to determine the position of a device-forming material within the boundary along the surface.
  • an individual positioning technique is necessary, and a suitable positioning technique is used with the self-assembly method, to form a structure capable of functioning as an individual part in integrated electronic circuits.
  • the positioning technique permits one to determine the boundary of a structure by lithography, direct formation methods or other positioning techniques, so that a patterned substrate is formed and a device is assembled on the substrate by self-assembly.
  • a self-assembled structure can be combined with a structure formed by the conventional chemical or physical deposition technique, and an integrated electronic circuit can comprise integrated optical parts.
  • the self-assembled structure can be formed using nanoparticle dispersion in such a manner that the desired structure is obtained by adjustment according to a material surface state and temperature and concentration conditions.
  • a linker one end of which is bound to the substrate surface and the other end of which is chemically bound to nanoparticles, is used, and selective binding using the linker can be used to yield a self-assembly process of nanoparticles.
  • Another selective binding method is to use natural interaction, such as electrostatic and chemical interaction, to perform the self-assembly process of nanoparticles, in which the nanoparticles are deposited in micropores such that they are positioned within the boundary defined by porous regions.
  • the micropores can be found in certain materials, such as inorganic oxides or two-dimensional organic crystals, or suitable micropores can be formed by, for example, ion milling or chemical etching.
  • this method is disadvantage in that the process is complex, and a spacing between pattern remains at a level of several tens to hundreds of nanometers.
  • Korean patent publication No. 2003-0023191A discloses a method for forming a nanometer-sized ultrafine pattern using a self-assembled monomolecular layer.
  • This method comprises the steps of forming a layer of aromatic imine molecules with substituted end groups on a substrate, selectively binding and cutting the substituent groups of the aromatic imine molecule layer, and hydrolyzing the resulting aromatic imine molecule layer, thereby enabling the pattern to be formed in a short time.
  • the pattern size according to this method still remains at a level of several tens of nanometers.
  • the bottom-up methods are based on the formation of microstructures by the self-assembly of molecules, and among such basic technologies, a method of analyzing the microstructure of supramolecules by a scanning electronic microscope has been reported (Hudson, S. D. et al., Science , 278:449, 1997) and it has been reported that the orientation of supramolecules varies depending on the surface property of a substrate (Jung, H. T. et al., Macromolecules , 35:3717, 2002). However, these publications describe only the microstructure analysis of supramolecules and the orientation of supramolecules, respectively.
  • microarray protein chips are of high importance in current researches on diagnostic proteomics.
  • An early array technology U.S. Pat. No. 5,143,854 that utilized a photolithographic technique for a polypeptide array on the surface of a substrate has recently generated new interest and is the subject of ongoing work.
  • increasing importance is being attached to development of a microarray-type format in various immunoassays, including antigen-antibody pairs and enzyme-liked immunosorbent assays.
  • the lattice pattern of DNA oligonucleotides can be produced on the surface of a substrate by photolithography, but in the case of a protein consisting of several hundreds of amino acids, more highly integrated lattice patterns with high density (for example, an antibody can comprise about 1,400 amino acids) are required for the exact diagnosis of diseases on the substrate surface. It is not easy to satisfy this requirement.
  • a solution to such problems requires that the proteins be processed in such manner that they can be arrayed at high resolution without loss of their three-dimensional structure.
  • various approaches including inkjet printing, drop-on-demand technology, microcontact printing, and soft lithography have been proposed.
  • arrays formed by such methods are characterized by spacing dimensions of several tens of micrometers to several millimeters, and no techniques have been found that produce highly integrated diagnostic protein nanoarrays having a high density character, while maintaining the three-dimensional structure of the protein.
  • CNTs Because of their properties of excellent structural rigidity, chemical stability, ability to act as ideal one-dimensional (ID) “quantum wires” with either semiconducting or metallic behaviors, a large aspect ratio, and empty interior, CNTs exhibit a broad range of potential applications as a basic material of flat panel displays, transistors, energy reservoirs, etc., and as various sensors with nanosize.
  • ID one-dimensional
  • the CNT synthesis using known methods of CVD synthesis involves first depositing Fe, Ni, Co or the alloy of these three metals as a metal catalyst on a substrate, etching the deposited substrate with water-diluted HF, mounting the sample on a quartz boat, and then after inserting the quartz boat into the reactor of a CVD device, additionally etching the metal catalyst film using NH 3 gas at 750 ⁇ -1050° C. to form fine metal catalyst particles with nanosize. Since the CNT is synthesized on the fine metal catalyst particles, forming the fine metal catalyst particles is an important process in the CVD synthesis method. However, arranging the metal catalyst in a patterned form with regular intervals is impossible in such method. Therefore, it is important to array the metal catalyst for arranging the CNT vertically at regular intervals.
  • CNT attracts public attention as a biochip material and technique
  • the application of biological systems to CNT as a well-arranged and new nanomaterial, will create important fusion technologies in various fields, including for example disease diagnosis (hereditary diseases), proteomics and nanobiotechnology.
  • the most universal method for detecting the result of a reaction in a biochip is to use conventional fluorescent materials and isotopes (Toriba, A. et al., Biomed. Chromatogr ., 17:126, 2003; Syrzycka, M et al., Anal. Chim. Acta , 484:1, 2003; Rouse, J. H. et al., Nano Lett ., 3:59, 2003).
  • novel methods to easily and precisely measure an electrical or electrochemical signal are attempted, there are increased demands for CNT as a new material.
  • the present inventors have conducted intensive studies to develop a simpler method for forming a several nanometer-sized ultrahigh density pattern.
  • the inventors have discovered that by forming a metal catalyst pattern of several nanometer or smaller size, utilizing supramolecular self-assembly and selective metal compound staining techniques, and growing CNT vertically on the formed pattern, a CNT array can be produced in a ready and efficient manner.
  • the invention provides a method for fabricating a CNT array, by steps including arranging CNT on a nanopattern of metal catalyst formed by using supramolecular self-assembly and selective metal compound staining.
  • the invention additionally provides a method for fabricating a biochip, which includes the attachment of a bioreceptor to a CNT array fabricated in accordance with the invention.
  • FIG. 1 schematically shows a self-assembly process of supramolecules.
  • FIG. 1 a shows that disc-shaped dendrimers ( 1 ) and fan-shaped supramolecules ( 2 ) are self-assembled into cylindrical structures ( 3 ) which are then arranged into three-dimensional hexagonal structures ( 4 ).
  • FIG. 1 b shows that cone-shaped molecules ( 5 ) are self-assembled into spherical structures ( 6 ) which are arranged into a three-dimensional regular structures ( 7 ).
  • FIG. 2 schematically shows a process for forming a nanopattern and CNT array for the fabrication of a biochip according to one aspect of the present invention.
  • FIG. 3 is a schematic diagram showing the process of introducing carboxyl groups and removing the caps on the ends of the grown CNT.
  • FIG. 4 is a transmission electron microscope photograph showing that supramolecules are self-assembled into hexagonal pillar-shaped regular structures.
  • FIG. 5 is a scanning electron microscope photograph showing a nanopattern formed according to the present invention.
  • the present invention provides a method for fabricating a carbon nanotube (CNT) nanoarray, which includes the steps of: (a) forming on a substrate a thin film of a metal catalyst selected from the group consisting of Fe, Ni, Co, and alloys of such metals; (b) forming a thin film of supramolecules inducing self-assembly on the thin film of the metal catalyst; (c) self-assembling the supramolecules by annealing to form a regular structure; (d) selectively staining the formed regular structure with a metal compound; (e) removing a portion which is not stained with the metal compound, by etching, wherein the metal compound-stained thin film is used as a mask, thereby forming a nanopattern of supramolecules stained with the metal compound; (f) forming nanopattern of a metal catalyst by ion-milling using the nanopattern of the supramolecule as a mask; and (g) vertically arranging CNTs on the
  • a compound of the following formula ( 1 ) is used as the supramolecules, but it will be appreciated that any self-assembling supramolecules may also be used, without limitation.
  • Examples of the self-assembling supramolecules include disc-shaped dendrimers ( 1 ), fan-shaped supramolecules ( 2 ), stick-chain shaped or cone-shaped molecules ( 5 ).
  • An example of the fan-shaped supramolecules includes a compound of the following formula ( 2 )
  • an example of the disk-shaped supramolecules includes a compound of the following formula ( 3 )
  • an example of the cone-shaped supramolecules includes a compound of the following formula ( 4 ):
  • Such supramolecules are formed into a regular structure by physical secondary binding, such as by van der Waals forces, unlike polymers in which monomers are covalently bonded. Such supramolecules are self-assembled by suitable temperature or concentration, external magnetic field or electric field, etc., to form certain fine structures.
  • the supramolecules of formula ( 1 ) used in the present invention correspond to the fan-shaped dendrimers. As shown in FIG. 1 a , such fan-shaped dendrimers are self-assembled into plate-shaped structures ( 1 ), which are then assembled into pillar-shaped structures ( 3 ), which are formed into a three-dimensional hexagonal structure ( 4 ). In addition, as shown in FIG. 1 b , the cone-shaped supramolecules ( 5 ) are self-assembled into spheres ( 6 ), which are then arranged into a three-dimensional regular structure ( 7 ).
  • the thin film in the step (b) is preferably formed by spin-coating, rubbing, or solution spreading, which forms a thin film on the water surface, and the annealing in the above step (c) is preferably performed by heating the supramolecules above their liquid crystal transition temperature and then cooling them slowly.
  • the metal compound staining in the above step (d) is preferably performed by selectively staining the central portion of the thin film with ruthenium tetraoxide(RuO 4 ), and the step (e) is preferably performed by a reactive ion etching method.
  • Thin films in accordance with the invention include films that have a thickness that does not exceed about 5 mm, which may by way of example include films having a thickness in a range of from about 5 nm to about 5 mm, such as films with a thickness of from about 0.01 ⁇ m to about 500 ⁇ m.
  • the step of forming CNT on the nanopattern of the substrate can be performed by any suitable CNT growth method, e.g., any of CNT growth methods known in the art.
  • the CNTs are grown vertically on the substrate by plasma chemical vapor deposition, thermal chemical vapor deposition, electrophoresis or mechanical methods (Korean patent publication No. KR 2002-0001260A).
  • the present invention in another aspect can additionally include the step of exposing the carboxyl group by plasma treatment of the vertically synthesized CNT array end.
  • various bioreceptors can be bound chemically after the carboxyl group exposed on the end of CNT array by plasma treatment.
  • the present invention provides a method for fabricating a biochip, in which a bioreceptor selected from the group consisting of protein, peptide, amino acid, DNA, PNA, enzymatic substrate, ligand, cofactor, carbohydrate, lipid, oligonucleotide, and RNA, is attached to the CNT array fabricated by the above method.
  • a bioreceptor selected from the group consisting of protein, peptide, amino acid, DNA, PNA, enzymatic substrate, ligand, cofactor, carbohydrate, lipid, oligonucleotide, and RNA
  • the step of attaching the bioreceptor to CNTs is performed in any suitable manner, e.g., by either applying a charge of a polarity opposite to the net charge of the bioreceptor to CNTs (KR 2003-0014997A), or by using a binding aid.
  • the binding aid preferably includes a chemical substance having an aldehyde, amine or imine group attached to a carbon group end.
  • a method for fabricating a biochip which includes binding a bioreceptor having an amine group (NH 2 ) to the CNT array in which the carboxyl group is exposed on an upper end, by forming an amide bond. It is typically preferred to use a coupling agent and a coupling aid for inducing an amide bond in the broad practice of the present invention.
  • Bioreceptors such as proteins, peptides and amino acids, possess respective intrinsic isoelectric points, and have a net charge with a neutral ion, cation or anion according to the ion intensity or pH of solution. Also, by adjusting the condition of solution to adjust the electrostatic interaction and hydrophobic interaction between such bioreceptors and CNTs with a certain charge, the same or different kinds of bioreceptors can be moved or arranged on the desired positions of a chip.
  • the present invention provides a biochip, in which a bioreceptor selected from the group consisting of proteins, peptides, amino acids, DNAs, PNAs, enzymatic substrates, ligands, cofactors, carbohydrates, lipids, oligonucleotides, and RNAs, is attached to the above CNT array.
  • a bioreceptor selected from the group consisting of proteins, peptides, amino acids, DNAs, PNAs, enzymatic substrates, ligands, cofactors, carbohydrates, lipids, oligonucleotides, and RNAs
  • a protein-specific receptor that binds selectively to a target protein involved in diseases can be selectively attached to the CNT nanoarray on one chip by applying an electric field.
  • a bioreceptor that can interact with various target proteins involved in various diseases can be attached selectively to CNTs by applying electric fields of different polarities from each other to the CNTs. Accordingly, it is possible to diagnose a variety of diseases on one chip in one step at large amounts in a rapid manner.
  • bio-nanoarray is defined to include biochips and biosensors, in which a bioreceptor that binds to or reacts with a biomaterial is attached to a nanopattern.
  • a thin film is formed on a substrate, of Fe, Ni, Co, or an alloy thereof, as a metal catalyst for growing CNT vertically on a substrate by a suitable technique such as thermal deposition, e-beam deposition, sputter, etc.
  • the formed metal catalyst thin film is formed into a metal catalyst array by use of a nanopattern of supramolecules, as described herein (FIG. 2).
  • supramolecules are first dissolved in a tetrahydrofuran (THF) solvent at a 1-wt % concentration, and the resulting solution is applied on a substrate to form a thin film of supramolecules.
  • THF tetrahydrofuran
  • spin-coating, rubbing, or solution spreading that forms a thin film on the water surface is preferably used.
  • a silicon wafer having the metal catalyst (Fe, Ni, Co, or an alloy thereof) deposited thereon, is used as the substrate, and the modification of the substrate surface is not carried out (FIG. 2 a ).
  • the supramolecules are heated above their liquid crystal phase transition temperature such that they are self-assembled. Since the supramolecules used in the present invention have a liquid crystal phase transition temperature of about 230° C., they are heated to 240° C. and then cooled slowly. Thus, the supramolecules are self-assembled into pillar-shaped microstructures (FIG. 2 b ).
  • the properties of supramolecules can be modified by annealing, and starting materials suitable for annealing include supramolecules produced by pyrolysis. Also, the supramolecules used as the starting materials can undergo at least one preheating step under different conditions.
  • the additional treatment in annealing the supramolecules formed by laser pyrolysis improves their crystallinity and removes contaminants such as atomic carbon, and possibly can change their stoichiometry by combining additional oxygen, or atoms from gaseous or nongaseous compounds.
  • the supramolecules are preferably heated in an oven so as to provide uniform heating.
  • the treatment conditions are generally mild so that a significant amount of sintered particles are not caused. Thus, the heating temperature is preferably lower than the melting point of both the starting material and the product. If the thermal treatment involves a change in composition, the size and shape of the molecules can be changed even at mild heating temperatures.
  • Self-assembled structures are formed on the surface of material/substrate or within the surface.
  • the self-assembled structures are positioned within boundaries in the form of positioned islands, and each of the structures can serve as an element of circuits or devices having a plurality of elements.
  • each of the structures may be an element of integrated electronic circuits, and examples of this element include electrical parts, optical devices and photonic crystals.
  • a process of defining the boundary of the structure and a separate self-assembly process are required for the formation of the self-assembled structure.
  • the process of defining the boundary of the structure utilizes an external force in defining the structure boundary. It is generally impossible to define the structure boundary by the self-assembly process itself.
  • its self-assembly is based on the natural sensing function of the composition/material, which causes natural ordering in the resulting structure.
  • the positioning process can be conducted before or after the self-assembly process, the nature of treatment steps can also indicate certain orders.
  • the net effect results in a self-assembled structure having a region within the boundary, which is covered with nanoparticles, and also a region outside the boundary, which is not covered with the nanoparticles.
  • the process of defining the boundary is linked to the self-assembly process, by either activating the self-assembly process in the boundary or inactivating the region outside the boundary. Generally, to carry out the activating process or the inactivating process, the application of an external force is necessary.
  • RuO 4 solution and a substrate coated with a thin film of supramolecules are maintained in a glass container with the solution not being in direct contact with the substrate.
  • RuO 4 vapor in the RuO 4 solution is diffused into a gas phase, the supramolecular thin film on the substrate is stained with the Ru metal.
  • the stained RuO 4 vapor chemically selectively reacts with certain portions of the thin film.
  • RuO 4 is used in the present invention, osmium tetraoxide (OsO 4 ) or other metal compounds capable of selectively staining the structures formed by supramolecules may also be used in the present invention.
  • the substrate coated with the supramolecular thin film is subjected to the metal compound staining process and then an etching process, a portion of the supramolecular thin film on the substrate is removed so that nanopatterned devices are ultimately obtained.
  • an etching solution such as a KCN-KOH mixture solution or an HF aqueous solution, or by reactive ion etching (RIE).
  • a nanopattern of metal catalyst is finally formed on a substrate, when ion-milling is performed using the nanopattern stained with the formed metal compound as a mask, to form an array of Fe, Co, Ni or an alloy thereof, for use as a catalyst for CNT synthesis on a substrate.
  • CNT can be synthesized by known methods in the art. In one such method, C 2 H 2 , CH 4 , C 2 H 4 , C 2 H 6 , or CO gas is used as a reacting gas, and plasma chemical vapor deposition, thermal chemical vapor deposition, etc. is used to grow CNT vertically. If CNT is formed by metal catalyst nanopattern, CNT having very small diameter can be formed because the diameter of one pattern is below 10 nm.
  • the present invention also includes the process of introducing carboxyl groups to the vertically grown CNT ends for binding biomaterials by treating the CNT ends with plasma to open the end caps of the CNT (FIG. 3).
  • the CNT nanoarray formed according to an illustrative preferred embodiment of the present invention as described above can be used as important surface substrates in forming a desired array by reacting various bioreceptors with the CNT nanoarray, in order to produce biochips of high integration density and small size.
  • the biochips are fabricated by linking biomolecules directly to a substrate or linking the biomolecules to the substrate by means of linker molecules.
  • linker molecules e.g., DNAs, antibodies or enzymes
  • the desired bioarray can be fabricated by reacting carboxyl groups introduced to the CNT ends with amine groups of the above biomaterial and binding those to the CNT ends with by amide bonds.
  • a method for fabricating DNA chips as bionanoarray articles includes the step of attaching a previously prepared probe to the surface of a solid substrate by a spotting method.
  • an amine group-bound probe is dissolved in 1 ⁇ to 7 ⁇ , preferably 2 ⁇ to 5 ⁇ , and more preferably 3 ⁇ SSC buffer solution (0.45 M NaCl, 15 mM C 6 H 5 Na 3 O 7 , pH 7.0), and then spotted to a CNT end having an exposed carboxyl group by a microarrayer. Then, the probe is bound to the CNT end by the reaction between aldehyde and amine.
  • the concentration of the probe is more than 10 pmol/ ⁇ l, preferably more than 50 pmol/ ⁇ l, and more preferably more than 100 pmol/ ⁇ l.
  • the amine group bound to the probe is reacted with the carboxyl group introduced to the CNT end at a humidity of 70-90%, and preferably 80%, for 4-8 hours, preferably 5-7 hours, and most preferably about 6 hours, so that the probe is bound to the CNT end.
  • An amide coupling agent and EDC/NHS as an aid can be suitably used in the method.
  • the supramolecules of formula (1) used in the present invention were synthesized by a process as shown in reaction scheme (1) below.
  • the result of scanning electron microscopic analysis on such supramolecules confirmed that the supramolecules are regular cylindrical structures of nanometer- or smaller size (FIG. 4).
  • the above metal catalyst was deposited on a silicon wafer by using thermal deposition, e-beam deposition, sputter, etc. to form a thin film of Fe, Ni, Co, or an alloy thereof, as a metal catalyst for synthesizing CNT (FIG. 2 a ).
  • Example 2 The supramolecules synthesized in Example 1 were dissolved in a tetrahydrofuran (THF) solvent. The solution was spin-coated on the silicon wafer of Example 2 to form a thin film (FIG. 2 a ). In this Example, the spin-coating was performed at 2,000-3,000 rpm for 10-30 second. During this spin-coating, the thickness of the thin film can be suitably changed.
  • THF tetrahydrofuran
  • the thin film of supramolecules was heated to 240° C. and then cooled slowly, to form regular microstructures (FIG. 3 b ).
  • the supramolecules used in the present invention are self-assembled at 240° C., which can vary according to the kinds of supramolecules used. At this temperature, the supramolecules have a sufficient mobility for their self-assembly, and self-assembled into the most stable structures.
  • three-dimensional structures in which cylinders are arranged into a hexagonal shape are the most stable structures.
  • FIG. 4 is a transmission electron microscope photograph showing that supramolecules are self-assembled into hexagonal pillar-shaped regular structures.
  • the supramolecules can be stained with RuO 4 selectively at their central portions, the supramolecules were exposed to RuO 4 vapor for several minutes, to stain chemically their central portions with a RuO 4 metal compound (FIG. 2 c ).
  • the RuO 4 metal compound When the supramolecules was exposed to RuO 4 , the RuO 4 metal compound was diffused into air so that the supramolecular thin film was stained with the RuO 4 metal compound.
  • the RuO 4 metal compound chemically reacts with certain reactive groups (e.g., ether bonds, alcohols, benzene rings, and amines), and the supramolecules are stained with the RuO 4 metal compound at their portions corresponding to the central portions of the supramolecular cylinders.
  • the staining metal compound may be replaced with other metal compounds depending on the kinds of supramolecules employed in specific applications.
  • osmium tetroxide OsO 4
  • reactive groups such as carbon double bonds, alcohols, ether bonds, amines, etc.
  • FIG. 5 is a scanning electron microscope photograph showing the configuration of such dot-shaped structures.
  • the etching was carried out using CF 4 gas for about 100 seconds. This etching time cannot be considered to be common in all cases, since it varies depending on the apparatus employed. Thus, a test step for setting etching conditions was required.
  • the metal catalyst thin film was etched using the nanopattern of supramolecules stained with the metal compounds obtained by Examples 1-6, as a mask, thereby forming nanopattern of metal catalyst.
  • the metal catalyst thin film for CNT synthesis was formed between the substrate and the supramolecular thin film and the formed dot-shaped nanopattern serves as a mask in a subsequent etching step (FIG. 2 c ).
  • Reacting gas such as C 2 H 2 , CH 4 , C 2 H 4 , C 2 H 6 , CO etc. was supplied into a chamber and power having high frequency was applied to both electrodes to cause a glow electric discharge, thereby vertically synthesizing and growing CNT on the metal catalyst nanoarray formed in example 7.
  • the synthesized CNT formed a CNT array on the substrate by the regular arrangement of fixed metal catalyst (FIG. 2 e ).
  • the vertically grown CNT can be treated with plasma by a method similar to the described in the prior art (Huang, S. et al., J. Phys. Chem. B , 106:3543, 2002), and carboxyl groups can be introduced to the CNT by removing the caps of the end portions. Then, various bioreceptors can be chemically bound to the CNT.
  • the method of binding by applying a change of polarity opposite to the net charge of the bioreceptor to the CNT (KR 2003-0014997A) or using a binding aid can be used (FIG. 2 f ).
  • the preferred binding aid is a chemical substance having an aldehyde, amine or imine group attached to a carbon group end.
  • a biochip can be fabricated by binding a bioreceptor having an amine group (NH 2 ) by means of an amide bond to the end of the CNT array having an exposed carboxyl group formed in example 8.
  • EDC 1-ethyl-3-(3-dimethylamini-propyl) carbodiimide hydrochloride
  • NHS N-hydroxysuccinimide
  • NHSS N-hydroxysulfosuccinimide
  • the present invention provides a method for fabricating a CNT array, which involves forming a catalyst pattern for CNT synthesis using a pillar shaped nanopattern which is formed by using the supramolecular self-assembly and the selective metal compound staining as a mask, and arranging CNT on the pattern.
  • the present invention provides a method for fabricating a biochip by attaching a biomaterial or a biomaterial binding bioreceptor to the CNT nanoarray.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Nanotechnology (AREA)
  • Materials Engineering (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • General Physics & Mathematics (AREA)
  • Manufacturing & Machinery (AREA)
  • Inorganic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Composite Materials (AREA)
  • Carbon And Carbon Compounds (AREA)
  • Apparatus Associated With Microorganisms And Enzymes (AREA)
US10/859,530 2003-06-05 2004-06-02 Method for fabricating a carbon nanotube array and a biochip using the self-assembly of supramolecules and staining of metal compound Abandoned US20040245209A1 (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR1020030036530A KR100549103B1 (ko) 2003-06-05 2003-06-05 탄소나노튜브 어레이의 제작방법
KR10-2003-0036530 2003-06-05

Publications (1)

Publication Number Publication Date
US20040245209A1 true US20040245209A1 (en) 2004-12-09

Family

ID=33487906

Family Applications (1)

Application Number Title Priority Date Filing Date
US10/859,530 Abandoned US20040245209A1 (en) 2003-06-05 2004-06-02 Method for fabricating a carbon nanotube array and a biochip using the self-assembly of supramolecules and staining of metal compound

Country Status (4)

Country Link
US (1) US20040245209A1 (zh)
JP (1) JP3951141B2 (zh)
KR (1) KR100549103B1 (zh)
CN (1) CN1332270C (zh)

Cited By (33)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050287689A1 (en) * 2004-06-23 2005-12-29 Canon Kabushiki Kaisha Method for manufacturing carbon fibers, method for manufacturing electron-emitting device using the same, method for manufacturing electronic device, method for manufacturing image display device, and information display reproduction apparatus using the same
US20060240492A1 (en) * 2004-11-12 2006-10-26 Rusling James F Carbon nanotube based immunosensors and methods of making and using
WO2008000045A1 (en) * 2006-06-30 2008-01-03 University Of Wollongong Nanostructured composites
WO2008027571A2 (en) * 2006-08-30 2008-03-06 Liquidia Technologies, Inc. Nanoparticles having functional additives for self and directed assembly and methods of fabricating same
US20080176058A1 (en) * 2006-05-17 2008-07-24 Matthew Ralph Maschmann Vertical carbon nanotube device in nanoporous templates
CN100406377C (zh) * 2005-02-15 2008-07-30 三星Sdi株式会社 生长碳纳米管的方法以及制造场发射装置的方法
US20080226917A1 (en) * 2007-02-20 2008-09-18 Research Foundation Of State University Of New York Core-shell nanoparticles with multiple cores and a method for fabricating them
EP2006679A2 (en) * 2005-06-17 2008-12-24 HiPep Laboratories Biochip substrate and biochip
US20080316480A1 (en) * 2007-01-03 2008-12-25 Research Foundation Of State University Of New York Aggregates of plural transition metal nanoparticles and plural cyanine dye molecules
US7649665B2 (en) 2005-08-24 2010-01-19 The Trustees Of Boston College Apparatus and methods for optical switching using nanoscale optics
US20100173228A1 (en) * 2006-12-14 2010-07-08 University Of Wollongong Nanotube and Carbon Layer Nanostructured Composites
US7754964B2 (en) 2005-08-24 2010-07-13 The Trustees Of Boston College Apparatus and methods for solar energy conversion using nanocoax structures
US20100279179A1 (en) * 2007-06-20 2010-11-04 New Jersey Institute Of Technology System and Method for Directed Self-Assembly Technique for the Creation of Carbon Nanotube Sensors and Bio-Fuel Cells on Single Plane
US20100285514A1 (en) * 2009-01-27 2010-11-11 Jonathan Clay Claussen Electrochemical biosensor
US20100295023A1 (en) * 2009-04-06 2010-11-25 Purdue Research Foundation Field effect transistor fabrication from carbon nanotubes
US20100297435A1 (en) * 2009-01-28 2010-11-25 Kaul Anupama B Nanotubes and related manufacturing processes
US20100301260A1 (en) * 2009-05-27 2010-12-02 Tsinghua University Thermal interface material having a patterned carbon nanotube array and method for making the same
US7943847B2 (en) 2005-08-24 2011-05-17 The Trustees Of Boston College Apparatus and methods for solar energy conversion using nanoscale cometal structures
US7959974B2 (en) 2005-12-02 2011-06-14 Northwestern University Nanotube assembly
WO2012069993A3 (en) * 2010-11-23 2012-11-15 Hach Company Carbon nanotube sensor
WO2013037951A1 (en) * 2011-09-16 2013-03-21 Danmarks Tekniske Universitet Catalyst deposition for the preparation of carbon nanotubes
US8435798B2 (en) 2010-01-13 2013-05-07 California Institute Of Technology Applications and methods of operating a three-dimensional nano-electro-mechanical resonator and related devices
US8504305B2 (en) 1998-12-17 2013-08-06 Hach Company Anti-terrorism water quality monitoring system
US8815729B1 (en) * 2013-03-04 2014-08-26 Globalfoundries Inc. Methods of forming structures on an integrated circuit product
US8828869B1 (en) 2013-03-28 2014-09-09 Globalfoundries Inc. Methods of forming masking layers for use in forming integrated circuit products
US8958917B2 (en) 1998-12-17 2015-02-17 Hach Company Method and system for remote monitoring of fluid quality and treatment
US9056783B2 (en) 1998-12-17 2015-06-16 Hach Company System for monitoring discharges into a waste water collection system
WO2015101118A1 (zh) * 2013-12-31 2015-07-09 清华大学深圳研究生院 一种基于三维结构纳米阵列生物芯片的制备方法及其应用
US9110055B2 (en) 2006-11-17 2015-08-18 The Trustees Of Boston College Nanoscale sensors
CN105319854A (zh) * 2014-05-30 2016-02-10 三星电子株式会社 硬掩模组合物和通过使用该硬掩模组合物形成图案的方法
WO2017091802A1 (en) * 2015-11-27 2017-06-01 The Government Of The United States Of America, As Represented By The Secretary Of The Navy Pattern definition of nanocellulose sheets through selective ashing via lithographic masking
CN110146570A (zh) * 2019-05-09 2019-08-20 清华-伯克利深圳学院筹备办公室 酶电极及其制备方法、酶传感器、监测装置和治疗设备
CN114324568A (zh) * 2021-12-31 2022-04-12 浙江大学 鸟嘌呤肽核酸自组装纳米球基光子晶体的声场辅助制备方法

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100812854B1 (ko) * 2002-10-02 2008-03-11 더 마이터 코포레이션 패턴화된 과립 운동을 이용하는 로봇식 조작 시스템
JP4927319B2 (ja) * 2003-07-24 2012-05-09 韓国科学技術園 高密度カーボンナノチューブフィルムまたはパターンを用いたバイオチップの製造方法
KR100657221B1 (ko) * 2004-12-24 2006-12-14 한국기계연구원 콜로이드 자기조립에 의한 다공성 마스크의 제조방법 및그 용도
KR100704234B1 (ko) * 2005-08-18 2007-04-10 재단법인서울대학교산학협력재단 다공성 알루미나 나노틀을 이용한 규칙적으로 배열된 분자소자 어레이의 제조방법
KR100856577B1 (ko) 2006-05-22 2008-09-04 주식회사 에스티앤아이 탄소나노튜브 센서 및 그 제조방법
KR100811266B1 (ko) 2006-09-01 2008-03-07 주식회사 하이닉스반도체 하드 마스크를 이용한 선택적 식각 방법 및 이를 이용한메모리 소자의 소자분리 형성 방법
KR100923092B1 (ko) * 2007-11-30 2009-10-22 연세대학교 산학협력단 자기조립법을 이용한 상온 전도성 또는 반도체성 나노튜브의 제조방법
CN102539777B (zh) * 2010-12-10 2014-11-05 国家纳米科学中心 一种超分子自组装生物芯片及其制备方法和应用
KR20130032507A (ko) * 2011-09-23 2013-04-02 포항공과대학교 산학협력단 유기 금속을 포함하는 자기조립성 고분자를 포함하는 전극 및 그 제조 방법
JP2015500482A (ja) * 2011-12-05 2015-01-05 ザ トラスティーズ オブ ザ ユニバーシティ オブ ペンシルバニア グラフェン−生体分子バイオ電子デバイス
CN102816197B (zh) * 2012-08-24 2015-04-29 四川大学华西医院 一种新的嘧啶并嘧啶类核苷类似物、制备方法及其形成的超分子结构和应用
CN107105675B (zh) * 2014-10-28 2023-11-07 杨百翰大学 微生物抗性材料以及相关的装置、系统及方法
US10517995B2 (en) 2016-11-01 2019-12-31 Brigham Young University Super-hydrophobic materials and associated devices, systems, and methods

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5143854A (en) * 1989-06-07 1992-09-01 Affymax Technologies N.V. Large scale photolithographic solid phase synthesis of polypeptides and receptor binding screening thereof
US6401526B1 (en) * 1999-12-10 2002-06-11 The Board Of Trustees Of The Leland Stanford Junior University Carbon nanotubes and methods of fabrication thereof using a liquid phase catalyst precursor
US20030171257A1 (en) * 2001-12-19 2003-09-11 Stirbl Robert C. Method and related composition employing nanostructures
US20030224117A1 (en) * 2002-04-05 2003-12-04 Interantional Business Machines Corporation Thin films from metal-metal bonded complexes
US20040072994A1 (en) * 2002-10-15 2004-04-15 Herr Daniel J.C. Nanostructures including controllably positioned and aligned synthetic nanotubes, and related methods
US20040077156A1 (en) * 2002-10-18 2004-04-22 Loucas Tsakalakos Methods of defect reduction in wide bandgap thin films using nanolithography
US20040142183A1 (en) * 2003-01-17 2004-07-22 Lazarev Pavel I. Anisotropic film manufacturing

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3943272B2 (ja) * 1999-01-18 2007-07-11 双葉電子工業株式会社 カーボンナノチューブのフイルム化方法
JP4063451B2 (ja) * 1999-07-26 2008-03-19 双葉電子工業株式会社 カーボンナノチューブのパターン形成方法
KR20020003782A (ko) * 2000-07-04 2002-01-15 이정욱 탄소나노튜브의 제작 방법
JP3843447B2 (ja) * 2000-12-01 2006-11-08 日本電気株式会社 カーボンナノチューブのパターン形成方法
KR20020049547A (ko) * 2000-12-19 2002-06-26 류정열 차량 반자동변속기의 변속시스템

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5143854A (en) * 1989-06-07 1992-09-01 Affymax Technologies N.V. Large scale photolithographic solid phase synthesis of polypeptides and receptor binding screening thereof
US6401526B1 (en) * 1999-12-10 2002-06-11 The Board Of Trustees Of The Leland Stanford Junior University Carbon nanotubes and methods of fabrication thereof using a liquid phase catalyst precursor
US20030171257A1 (en) * 2001-12-19 2003-09-11 Stirbl Robert C. Method and related composition employing nanostructures
US20030224117A1 (en) * 2002-04-05 2003-12-04 Interantional Business Machines Corporation Thin films from metal-metal bonded complexes
US20040072994A1 (en) * 2002-10-15 2004-04-15 Herr Daniel J.C. Nanostructures including controllably positioned and aligned synthetic nanotubes, and related methods
US20040077156A1 (en) * 2002-10-18 2004-04-22 Loucas Tsakalakos Methods of defect reduction in wide bandgap thin films using nanolithography
US20040142183A1 (en) * 2003-01-17 2004-07-22 Lazarev Pavel I. Anisotropic film manufacturing

Cited By (57)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8504305B2 (en) 1998-12-17 2013-08-06 Hach Company Anti-terrorism water quality monitoring system
US8577623B2 (en) 1998-12-17 2013-11-05 Hach Company Anti-terrorism water quality monitoring system
US8958917B2 (en) 1998-12-17 2015-02-17 Hach Company Method and system for remote monitoring of fluid quality and treatment
US9056783B2 (en) 1998-12-17 2015-06-16 Hach Company System for monitoring discharges into a waste water collection system
US9069927B2 (en) 1998-12-17 2015-06-30 Hach Company Anti-terrorism water quality monitoring system
US9739742B2 (en) 2003-03-19 2017-08-22 Hach Company Carbon nanotube sensor
US8920619B2 (en) 2003-03-19 2014-12-30 Hach Company Carbon nanotube sensor
US20050287689A1 (en) * 2004-06-23 2005-12-29 Canon Kabushiki Kaisha Method for manufacturing carbon fibers, method for manufacturing electron-emitting device using the same, method for manufacturing electronic device, method for manufacturing image display device, and information display reproduction apparatus using the same
US20060240492A1 (en) * 2004-11-12 2006-10-26 Rusling James F Carbon nanotube based immunosensors and methods of making and using
CN100406377C (zh) * 2005-02-15 2008-07-30 三星Sdi株式会社 生长碳纳米管的方法以及制造场发射装置的方法
US20100130380A1 (en) * 2005-06-17 2010-05-27 Kiyoshi Nokihara Biochip substrate and biochip
EP2006679A2 (en) * 2005-06-17 2008-12-24 HiPep Laboratories Biochip substrate and biochip
US9778256B2 (en) * 2005-06-17 2017-10-03 Hipep Laboratories Biochip substrate and biochip
EP2006679A4 (en) * 2005-06-17 2009-08-05 Hipep Lab BIOPUCE SUBSTRATE AND BIOPUCE
US7943847B2 (en) 2005-08-24 2011-05-17 The Trustees Of Boston College Apparatus and methods for solar energy conversion using nanoscale cometal structures
US7754964B2 (en) 2005-08-24 2010-07-13 The Trustees Of Boston College Apparatus and methods for solar energy conversion using nanocoax structures
US7649665B2 (en) 2005-08-24 2010-01-19 The Trustees Of Boston College Apparatus and methods for optical switching using nanoscale optics
US8431816B2 (en) 2005-08-24 2013-04-30 The Trustees Of Boston College Apparatus and methods for solar energy conversion using nanoscale cometal structures
US7959974B2 (en) 2005-12-02 2011-06-14 Northwestern University Nanotube assembly
US20110212300A1 (en) * 2005-12-02 2011-09-01 Northwestern University Nanotube assembly
US8080314B2 (en) 2005-12-02 2011-12-20 Northwestern University Nanotube assembly
US20080176058A1 (en) * 2006-05-17 2008-07-24 Matthew Ralph Maschmann Vertical carbon nanotube device in nanoporous templates
US8679630B2 (en) 2006-05-17 2014-03-25 Purdue Research Foundation Vertical carbon nanotube device in nanoporous templates
US20100068461A1 (en) * 2006-06-30 2010-03-18 University Of Wollongong Nanostructured composites
WO2008000045A1 (en) * 2006-06-30 2008-01-03 University Of Wollongong Nanostructured composites
WO2008027571A3 (en) * 2006-08-30 2008-06-05 Liquidia Technologies Inc Nanoparticles having functional additives for self and directed assembly and methods of fabricating same
WO2008027571A2 (en) * 2006-08-30 2008-03-06 Liquidia Technologies, Inc. Nanoparticles having functional additives for self and directed assembly and methods of fabricating same
US20100055459A1 (en) * 2006-08-30 2010-03-04 Liquidia Technologies, Inc. Nanoparticles Having Functional Additives for Self and Directed Assembly and Methods of Fabricating Same
US9110055B2 (en) 2006-11-17 2015-08-18 The Trustees Of Boston College Nanoscale sensors
US20100173228A1 (en) * 2006-12-14 2010-07-08 University Of Wollongong Nanotube and Carbon Layer Nanostructured Composites
US7869030B2 (en) 2007-01-03 2011-01-11 Research Foundation Of State University Of New York Aggregates of plural transition metal nanoparticles and plural cyanine dye molecules
US20080316480A1 (en) * 2007-01-03 2008-12-25 Research Foundation Of State University Of New York Aggregates of plural transition metal nanoparticles and plural cyanine dye molecules
US9327314B2 (en) 2007-02-20 2016-05-03 The Research Foundation For The State University Of New York Core-shell nanoparticles with multiple cores and a method for fabricating them
US8343627B2 (en) 2007-02-20 2013-01-01 Research Foundation Of State University Of New York Core-shell nanoparticles with multiple cores and a method for fabricating them
US10006908B2 (en) 2007-02-20 2018-06-26 The Research Foundation For The State University Of New York Core-shell nanoparticles with multiple cores and a method for fabricating them
US20080226917A1 (en) * 2007-02-20 2008-09-18 Research Foundation Of State University Of New York Core-shell nanoparticles with multiple cores and a method for fabricating them
US10191042B2 (en) 2007-02-20 2019-01-29 The Research Foundation For The State University Of New York Core-shell nanoparticles with multiple cores and method for fabricating them
US8546027B2 (en) * 2007-06-20 2013-10-01 New Jersey Institute Of Technology System and method for directed self-assembly technique for the creation of carbon nanotube sensors and bio-fuel cells on single plane
US20100279179A1 (en) * 2007-06-20 2010-11-04 New Jersey Institute Of Technology System and Method for Directed Self-Assembly Technique for the Creation of Carbon Nanotube Sensors and Bio-Fuel Cells on Single Plane
US20100285514A1 (en) * 2009-01-27 2010-11-11 Jonathan Clay Claussen Electrochemical biosensor
US8715981B2 (en) 2009-01-27 2014-05-06 Purdue Research Foundation Electrochemical biosensor
US20100297435A1 (en) * 2009-01-28 2010-11-25 Kaul Anupama B Nanotubes and related manufacturing processes
US8872154B2 (en) 2009-04-06 2014-10-28 Purdue Research Foundation Field effect transistor fabrication from carbon nanotubes
US20100295023A1 (en) * 2009-04-06 2010-11-25 Purdue Research Foundation Field effect transistor fabrication from carbon nanotubes
US8642121B2 (en) * 2009-05-27 2014-02-04 Tsinghua University Thermal interface material having a patterned carbon nanotube array and method for making the same
US20100301260A1 (en) * 2009-05-27 2010-12-02 Tsinghua University Thermal interface material having a patterned carbon nanotube array and method for making the same
US8435798B2 (en) 2010-01-13 2013-05-07 California Institute Of Technology Applications and methods of operating a three-dimensional nano-electro-mechanical resonator and related devices
WO2012069993A3 (en) * 2010-11-23 2012-11-15 Hach Company Carbon nanotube sensor
WO2013037951A1 (en) * 2011-09-16 2013-03-21 Danmarks Tekniske Universitet Catalyst deposition for the preparation of carbon nanotubes
US8815729B1 (en) * 2013-03-04 2014-08-26 Globalfoundries Inc. Methods of forming structures on an integrated circuit product
US8828869B1 (en) 2013-03-28 2014-09-09 Globalfoundries Inc. Methods of forming masking layers for use in forming integrated circuit products
WO2015101118A1 (zh) * 2013-12-31 2015-07-09 清华大学深圳研究生院 一种基于三维结构纳米阵列生物芯片的制备方法及其应用
CN105319854A (zh) * 2014-05-30 2016-02-10 三星电子株式会社 硬掩模组合物和通过使用该硬掩模组合物形成图案的方法
WO2017091802A1 (en) * 2015-11-27 2017-06-01 The Government Of The United States Of America, As Represented By The Secretary Of The Navy Pattern definition of nanocellulose sheets through selective ashing via lithographic masking
US9720318B2 (en) 2015-11-27 2017-08-01 The United States Of America, As Represented By The Secretary Of The Navy Pattern definition of nanocellulose sheets through selective ashing via lithographic masking
CN110146570A (zh) * 2019-05-09 2019-08-20 清华-伯克利深圳学院筹备办公室 酶电极及其制备方法、酶传感器、监测装置和治疗设备
CN114324568A (zh) * 2021-12-31 2022-04-12 浙江大学 鸟嘌呤肽核酸自组装纳米球基光子晶体的声场辅助制备方法

Also Published As

Publication number Publication date
JP2005049334A (ja) 2005-02-24
CN1332270C (zh) 2007-08-15
CN1601383A (zh) 2005-03-30
JP3951141B2 (ja) 2007-08-01
KR20040105319A (ko) 2004-12-16
KR100549103B1 (ko) 2006-02-06

Similar Documents

Publication Publication Date Title
US20040245209A1 (en) Method for fabricating a carbon nanotube array and a biochip using the self-assembly of supramolecules and staining of metal compound
US20050269285A1 (en) Method for fabricating a nanopattern and a carbon nanotube bio-nanoarray using the self-assembly of supramolecules and UV etching
TWI272386B (en) Protein and peptide nanoarrays
Ginger et al. The evolution of dip‐pen nanolithography
US7670831B2 (en) Conductive carbon nanotubes dotted with metal and method for fabricating a biosensor using the same
EP1461619B1 (de) Verbesserte strukturiert-funktionale bindematrices für biomoleküle
JP4927319B2 (ja) 高密度カーボンナノチューブフィルムまたはパターンを用いたバイオチップの製造方法
Woodson et al. Functional nanostructures from surface chemistry patterning
WO2005083519A2 (en) Methods of patterning a surface using single and multilayer molecular films
TWI311155B (en) Direct write nanolithographic deposition of nucleic acids from scanning probe microscopic tips
DE102004027865B4 (de) Leitende Kohlenstoff-Nanotubes, dotiert mit einem Metall, und Verfahren zur Herstellung eines Biosensors, der diese benutzt
KR100532812B1 (ko) 블록 공중합체의 나노패턴을 이용한 나노-바이오칩의제조방법
KR100523765B1 (ko) 유기초분자의 나노패턴을 이용한 탄소나노튜브 어레이의제작방법
WO2008021614A2 (en) Coded particle arrays for high throughput analyte analysis
US20040235199A1 (en) Method for fabricating a nanoarray using the self-assembly of supramolecules and staining of metals
Castronovo et al. The atomic force microscopy as a lithographic tool: nanografting of DNA nanostructures for biosensing applications
KR100549104B1 (ko) 10나노 이하 사이즈의 바이오 나노어레이 제조방법
JP2005283433A (ja) 試料と相互作用する探針を有するプローブ、該プローブの製造方法、該プローブを用いた分子間の相互作用の測定方法及び測定装置
JP3837493B2 (ja) 自己組織化膜及びその製造方法。
Rabiee et al. Protein microarrays: materials and fabrication methods
Li Fabrication of protein nanoarrays via colloidal lithography
KR20080017738A (ko) 나노어레이 단백질 칩 및 이것의 제조 방법
Vega Functional nanostructures through the use of chemical affinity templates and their application in cellular and biodiagnostic assays
Zoller Nano-Structured Substrates for Single Cell Proteomics
Henderson et al. Nanoscale molecular arrayer

Legal Events

Date Code Title Description
AS Assignment

Owner name: KOREA ADVANCED INSTITUTE OF SCIENCE AND TECHNOLOGY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:JUNG, HEE TAE;JUNG, DAE HWAN;KWON, KI YOUNG;AND OTHERS;REEL/FRAME:014819/0401

Effective date: 20040705

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION