TWI823907B - 脫模用雙軸配向聚酯薄膜卷 - Google Patents
脫模用雙軸配向聚酯薄膜卷 Download PDFInfo
- Publication number
- TWI823907B TWI823907B TW108107976A TW108107976A TWI823907B TW I823907 B TWI823907 B TW I823907B TW 108107976 A TW108107976 A TW 108107976A TW 108107976 A TW108107976 A TW 108107976A TW I823907 B TWI823907 B TW I823907B
- Authority
- TW
- Taiwan
- Prior art keywords
- film
- thickness
- polyester
- layer
- mold release
- Prior art date
Abstract
本發明為一種脫模用聚酯薄膜,其特徵為:薄膜寬為400mm以上,且相對於連續測定薄膜長邊方向10,000m所得之厚度的平均值之偏差σ值(σMD)為0.15μm以下。提供一種可減低坯片成型時的支撐體剛性、或電極印刷時的歪斜量,且薄膜坯片成型時的陶瓷漿料塗布性最佳化之脫模用雙軸配向聚酯薄膜。
Description
本發明係關於一種薄膜漿料塗布時之膜厚均勻性優異之脫模用雙軸配向聚酯薄膜經捲取而成之脫模用雙軸配向聚酯薄膜卷。
從機械特性或熱特性、勁度(stiffness)或成本之觀點而言,雙軸配向聚酯薄膜係作為工業材料用途而使用於各種用途。尤其近來其係作為電子構件關聯的工程紙而使用於:積層陶瓷電容器坯片(green sheet)成型用的脫模薄膜、或液晶偏光板的隔離膜、乾膜光阻用基材、層間絕緣樹脂脫模用基材等。
隨著最近的智慧型手機的功能進步、或智慧型手錶、穿戴式裝置(wearable equipment)的普及,積層陶瓷電容器的小型高容量化正進一步發展中。關於積層陶瓷電容器之製造所使用的脫模薄膜,隨著坯片的薄膜化,而對於平滑性高、薄膜表面及內部沒有缺陷、薄膜的平面性優異之聚酯薄膜的需求持續增長。另一方面,因電動車生產量擴大、汽車IoT(Internet Of Things)化、為了對汽車搭載自動駕駛功能,而對於搭載於汽車的積層陶瓷電容器的需求急速擴大。對於該等汽車用積層陶瓷電容器,企求較以往的要求更嚴格的可靠度。特別是在作為積層陶瓷電容器的介電質零件的坯片成型 時,要更嚴格地管理因薄膜的厚度不均、或薄膜的平面特性,所導致在將薄膜作為基材使用之際,積層於其上的漿料厚度的不均度。
薄膜的厚度不均,已知如專利文獻1所示,在長邊方向實施15m之測定而判定、或對1m長進行每5mm之測定而判定的手法,係為周知的手法。又,如專利文獻2所示,在檢查偏光板之正交尼寇稜鏡法中,自偏光板洩漏之光的強度不均變強,會成為檢查的障礙,所以必須將厚度不均設為規定的範圍。已知如專利文獻3所示,藉由實施同時雙軸延伸並提高面配向而達成。
專利文獻1 日本特開2008-246685號公報
專利文獻2 日本特開2017-007175號公報
專利文獻3 日本特開2004-291240號公報
近年對於電容器之要求,傾向除了小型化、大容量化之外,還有高可靠度化。小型化,即可藉由電極之縮小化而達成。大容量化,即可藉由坯片之薄膜化而達成,此外,高可靠度化,可藉由設置電極或坯片之際提升相對於寬、長度、厚度方向的尺寸精度而達成。其中,漿料塗布時之塗布厚度均勻性,因在隨後實施電極印刷的步驟中,每個電極面積會變微小,因此作為決 定電容器的介電常數偏差(即電容器的靜電電容偏差)的重大要因之一可舉出電極圖案的歪斜和偏移的最小化。因此,對於薄膜之關於厚度不均最小化的要求變嚴格。尤其,發現到:在電容器製造時,持續監視漿料厚度,一邊修正模具之傾斜度等一邊以漿料實施薄膜塗布的步驟,係受到卷整個長度上的基底薄膜(base film)厚度不均影響的可能性高。因此,在本發明中,課題是減低特別是作為坯片成型時的支撐體使用之際的卷整個長度的薄膜厚度不均。
本案發明人等鑑於上述實情仔細探討的結果發現:藉由將薄膜的特性予以最佳化,而長邊、寬、厚度方向上的漿料的尺寸安定性優異之脫模用雙軸配向聚酯薄膜經捲取而成的脫模用雙軸配向聚酯薄膜卷,進而完成本發明。亦即,本發明的特徵為一種脫模用雙軸配向聚酯薄膜卷,其薄膜寬為400mm以上,且相對於連續測定薄膜長邊方向10,000m所得之厚度的平均值之偏差σ值(σMD)為0.15μm以下。
根據本發明,可提供一種可減低坯片成型時之厚度偏差,且超薄膜坯片成型時之陶瓷漿料的塗布性最佳化之脫模用雙軸配向聚酯薄膜經捲取而成的脫模用雙軸配向聚酯薄膜卷。
以下針對本發明更詳細地說明。
本發明的脫模用雙軸配向聚酯薄膜卷係脫模用雙軸配向聚酯薄膜(以下有時簡稱為雙軸配向聚酯薄膜)經捲取至芯部等芯材而成者。在此,雙軸配向,係指將未延伸(未配向)薄膜,藉由常法,朝二維方向延伸的狀態,且意指以廣角X射線繞射表示雙軸配向的圖案者。延伸,可採用逐次雙軸延伸或同時雙軸延伸之任一方法。逐次雙軸延伸,可將朝長邊方向(縱向)及寬方向(橫向)延伸的步驟,實施縱向-橫向之各1次,也可實施縱向-橫向-縱向-橫向等之各2次。
本發明的雙軸配向聚酯薄膜中之聚酯為將二元酸與二醇作為構成成分的聚酯,作為芳香族二元酸,可使用對苯二甲酸、間苯二甲酸、鄰苯二甲酸、萘二羧酸、二苯基碸二羧酸、二苯醚二羧酸、二苯酮二羧酸、苯基茚烷二羧酸、間苯二甲酸磺酸鈉、二溴對苯二甲酸等。作為脂環族二元酸,可使用草酸、琥珀酸、己二酸、壬二酸、癸二酸、二聚酸等。就二醇而言,作為脂肪族二醇,可使用乙二醇、丙二醇、四亞甲二醇、丙二醇、四亞甲二醇、六亞甲二醇、新戊二醇、二乙二醇等,作為芳香族二醇,可使用萘二醇、2,2-雙(4-羥基二苯基)丙烷、2,2-雙(4-羥基乙氧苯基)丙烷、雙(4-羥苯基)碸、氫醌等,作為脂環族二醇,可使用環己烷二甲醇、環己烷二醇等。
上述聚酯,可採用周知的方法進行製造,固有黏度,較佳為使用下限0.5上限0.8者。更佳為下限0.55上限0.70。再者,固有黏度之測定係使用由在鄰氯酚中、25℃測定的溶液黏度,以下式計算的數值。
ηsp/C=[η]+K[η]2‧C
在此,ηsp=(溶液黏度/溶劑黏度)-1,C為溶劑每100ml的溶解聚合物質量(g/100ml,通常為1.2),K為赫金斯常數(定為0.343)。又,溶液黏度、溶劑黏度係使用奧士華黏度計進行測定。單位以[dl/g]表示。
本發明的雙軸配向聚酯薄膜,可為單層薄膜,也可為2層以上的積層構成。2層積層時包含聚酯A層及聚酯B層,3層的情況為包含聚酯A層及聚酯B層及聚酯C層之3層、或聚酯A層及聚酯B層及聚酯A層之3層的積層薄膜。此時,藉由控制構成表層的層(積層部)所含有的粒子量,可在不對內層部造成薄膜表面特性之不良影響的範圍,將在製膜步驟所產生的邊緣部分的回收原料、或其它製膜步驟的再生原料等適時混合而使用,能夠減少石油資源之消耗,同時還能夠得到成本優點,因此具有3層以上之層構係為最佳的實施形態。
又,本發明的雙軸配向聚酯薄膜,較佳為在C層含有回收原料及/或再生原料。據此,C層,較佳為層構成之中,厚度最厚的層。又,A層(更平滑的層)所含有的原料之熔融比電阻,較佳為1.0×106Ω‧cm以上1.0×108Ω‧cm以下,更佳為5.0×108Ω‧cm以下。具有如前述的熔融比電阻值之原料亦較佳為聚酯樹脂。作為 A層,較佳為構成後述之SRa(A)為1nm以上且小於15nm之表面的層。又,較佳為兼具上述之C層的原料組成或厚度相關特徴、及A層的原料相關特徴或表面形狀相關特徴之態樣。
本發明的雙軸配向聚酯薄膜,其2層以上之構成之中,構成表層的2層(即聚酯A層及聚酯B層)的表面,為了兼具表面的平滑性、及輸送或捲取等操控性,較佳為粗度不同的構成。亦即,較佳為一方的薄膜表面之中心線粗度SRa(A)為1nm以上且小於15nm,另一方的薄膜表面之中心線粗度SRa(B)為20nm以上40nm以下。若SRa(A)低於1nm,則在該表面積層脫模層,且在其上積層陶瓷漿料後之剝離步驟中,會變得難以進行剝離。又,若SRa(A)成為15nm以上,則漿料的表面狀態會變差且會產生厚度不均,結果變得容易在電容器的特性上產生偏差。若SRa(B)低於20nm,則在脫模層塗布後之捲取、或將陶瓷漿料塗布後之捲取,會變得容易產生黏結(blocking),且在繞出之際會產生靜電。聚酯A層及聚酯B層的表面,更佳為一方的薄膜表面之中心線粗度SRa(A)為2nm以上且小於12nm,另一方的薄膜表面之中心線粗度SRa(B)為25nm以上35nm以下。
本發明之雙軸配向聚酯薄膜的厚度,較佳為12μm以上,更佳為20μm以上,再佳為25μm以上。又,較佳為188μm以下,更佳為50μm以下,再佳為40μm以下。若厚度變得較12μm更薄,則用以保持陶瓷漿料的勁度會消失,在陶瓷漿料之塗布時變得無法支撐陶瓷 漿料,且有無法在後續步驟均勻地乾燥、或熱皺褶之抑制變不足的情況。若厚度超過188μm,則雖然對於熱皺褶之耐久性格外優異,但隨著卷長度變少,有作為形成陶瓷漿料的基材之每單位面積的單價變高的傾向,而且,縱向延伸中之升溫或延伸難以進行,成為使厚度不均惡化的主因。厚度之較佳的範圍為12μm以上188μm以下,更佳為20μm以上50μm以下,再佳為25μm以上40μm以下。
本發明的雙軸配向聚酯薄膜,也可含有粒子。此時含有的粒子之體積平均粒徑較佳為1.3μm以下。若粒子的體積平均粒徑超過1.3μm,則在延伸時於粒子與聚合物之界面產生空隙(即孔隙)的機會變高,因此有時也會在表面結構產生凹凸之偏差,有漿料的厚度偏差變大的情況。此外,本發明中之超薄膜坯片,係指厚度小於1μm者。
在本發明使用的粒子,可使用球狀二氧化矽、凝聚二氧化矽、碳酸鈣、氧化鋁、鈦酸鋇、氧化鈦等無機粒子、交聯聚苯乙烯樹脂粒子、交聯矽酮樹脂粒子、交聯丙烯酸樹脂粒子、交聯苯乙烯-丙烯酸樹脂粒子、交聯聚酯粒子、聚醯亞胺粒子、三聚氰胺樹脂粒子等有機粒子。該等粒子,除了有在薄膜表面形成突起的作用之外,也可成為形成孔隙的核材料,因此較理想為同時選定粒徑與其種類。較佳為使用粒子之彈性高的有機粒子。有機粒子,特佳為前述的有機粒子之中,選自交聯聚苯乙烯樹脂粒子、交聯矽酮樹脂粒子、交聯丙烯 酸樹脂粒子、交聯苯乙烯-丙烯酸樹脂粒子、交聯聚酯粒子之中的有機粒子。在無機粒子方面,特佳為球狀二氧化矽、氧化鋁。
粒子的形狀、粒徑分布,較佳為均勻者,特佳為粒子形狀近似球形者。體積形狀係數(volume shape factor),較佳為f=0.3~π/6,更佳為f=0.4~π/6。體積形狀係數f係以下述式表示。
f=V/Dm3
在此,V為粒子體積(μm3),Dm為粒子的投影面中之最大徑(μm)。
再者,體積形狀係數f,在粒子為球時,係取最大的π/6(=0.52)。又,較佳為視需要藉由進行過濾等,而除去凝聚粒子或粗大粒子等。其中,可適當使用以乳化聚合法等合成之交聯聚苯乙烯樹脂粒子、交聯矽酮樹脂粒子、交聯丙烯酸樹脂粒子,從體積形狀係數接近真球、粒徑分布極為均勻、均勻地形成薄膜表面突起之觀點而言,特佳為交聯聚苯乙烯粒子、交聯矽酮、甚至球狀二氧化矽等。
本發明的雙軸配向聚酯薄膜,其薄膜寬為400mm以上,且相對於連續測定薄膜長邊方向10,000m所得之厚度的平均值之偏差σ值(σMD)為0.15μm以下。
以下依序進行說明。
本發明的雙軸配向聚酯薄膜,其薄膜寬為400mm以上,且相對於連續測定薄膜長邊方向10,000m所得之厚度的平均值之偏差σ值(σMD)為0.15μm以下。在此所言 之連續測定薄膜長邊方向10,000m所得之厚度為將薄膜連續地進行非接觸測定之際的厚度。薄膜寬及長邊方向的長度表示支撐體的尺寸,該支撐體係以一定的批次製造積層陶瓷電容器之際所需者。亦即,發現:坯片的成型性,可藉由抑制在該尺寸內的厚度之偏差,而變良好。又,在下述中,有時將σMD值視為長邊方向的薄膜厚度不均。
以往雙軸配向聚酯薄膜的厚度,係在製膜中,使非接觸厚度計朝寬方向掃描薄膜而進行測定、或是以接觸式的厚度計測定自薄膜卷於長邊方向採取20m左右而得的試料,但在本發明中係藉由如上述在長邊方向10,000m進行連續測定,而發現以往無法確認之厚度不均現象。對於該厚度不均現象,藉由減低偏差,本發明可發揮下述效果:可減低薄膜陶瓷漿料塗布時之漿料厚度不均,減低靜電電容之偏差,而且,可抑制短路之機率。此外,若σMD超過0.15μm,則在薄膜陶瓷漿料之塗布中,漿料的厚度不均會變大,上述的效果將減少。
本發明的雙軸配向聚酯薄膜,較佳為一方的薄膜表面之中心線粗度SRa(A)為1nm以上且小於15nm,另一方的薄膜表面之中心線粗度SRa(B)為20nm以上40nm以下。本發明的雙軸配向聚酯薄膜,考慮漿料塗布厚度與操控性之平衡,在任一表面皆可實施脫模處理,而且,在進行脫模處理之前也可進行平坦化處理,減低脫模層表面的粗度。
以下針對本發明的雙軸配向聚酯薄膜之製造方法進行說明,但本發明不應被解釋為限於該等例。
作為使聚酯含有非活性粒子的方法,例如,將非活性粒子依規定比例以漿料的形態分散於二醇成分之乙二醇中,且將該乙二醇漿料在聚酯聚合結束前之任意階段進行添加。此時,在添加粒子之際,例如,若不先將在合成粒子時所得之水溶膠或醇溶膠乾燥而添加,則粒子的分散性良好,可抑制粗大突起之產生,而為較佳。又,將粒子的水漿料直接與規定的聚酯丸粒混合,並供給至排氣形式的雙軸混練擠製機而使其與聚酯揉合的方法,也對本發明之製造為有效。
將如前述進行所準備的含粒子之母粒與實質上未含粒子等之丸粒,以規定的比例混合,乾燥之後,供給至周知的熔融積層用擠製機。本發明之雙軸配向聚酯薄膜的製造時之擠製機,可使用單軸、雙軸的擠製機。又,為了省略丸粒的乾燥步驟,也可使用在擠製機設置抽真空管線之排氣式擠製機。又,對於擠製量最多的C層,可使用將熔融丸粒的功能、及保持經熔融的丸粒在一定溫度的功能以各別的擠製機分擔之所謂的串列式擠製機。串列式擠製機,係使高吐出時之聚合物溫度安定化,結果可減少聚合物之黏度偏差,因此適宜作為減低厚度不均的製程。
用擠製機進行熔融並擠製而得的聚合物,係藉由過濾器進行過濾。即使是極小的異物進到薄膜中也會成為粗大突起缺陷,因此就過濾器而言,使用例如 3μm以上的異物可捕捉95%以上之高精度的捕捉效率者較為有效。另一方面,若過濾器的捕捉效率過高,則將造成壓力上升之程度變高,因此小於3μm的異物可捕捉95%以上之更高精度之捕捉效率的過濾器之使用,有時在厚度不均之抑制方面為較不佳的實施形態。接著,從狹縫狀的縫模擠出成薄片狀,在鑄模輥(casting roll)上進行冷卻固化,製作未延伸薄膜。例如,3層積層的情況,係使用3台的擠製機、3層的歧管或匯流器(例如具有矩形匯流部的匯流器)積層為3層,從模頭擠出薄片。此時的模頭,較佳為可利用加熱器自動調整模頭的間隙。從模頭擠出的薄片係以鑄模輥進行冷卻,製作未延伸薄膜。此時,從背壓的安定化及厚度變動的抑制之觀點而言,在聚合物流路設置靜態混合器、齒輪泵的方法,係作為抑制本發明中之長邊方向的厚度不均之手段為有效。齒輪泵,有阻斷擠製步驟中之壓力變動的功能,故其係為了均勻地控制長邊方向厚度所必需,藉由將內建在齒輪泵的齒輪之轉速設為一定,可將長邊方向的厚度不均抑制為小。在本發明中,將捲好的中間製品之重量換算的厚度回饋而控制齒輪泵的轉速也較為有效。其係因為伴隨過濾器壓力之上升,吐出會減少,因此薄膜厚度相對於長邊方向而言會逐漸地變薄。
關於鑄模輥的旋轉精度,鑄模輥偏心等所致之鑄模輥表面的速度變動或表面的凹凸有時會影響長邊方向的厚度不均。以往鑄模輥表面的速度變動係大幅影響長邊方向的厚度不均,因此為了減低前述而在鑄模 輥端面任意圓周上的處所貼附平衡錘來控制偏心之不均係為較佳的實施形態。又,將用以使鑄模鼓輪(casting drum)旋轉的馬達定為2台,依驅動與制動將功能劃分開等,在以抑制長邊方向的厚度不均為前提下,亦為較佳的實施形態。在本發明中,為了控制σMD值,需要更進一步提升精度,因此在評價鑄模輥的旋轉精度時,將感測器至鑄模表面為止的距離在整個鑄模圓周上測定1圈之際的凹凸狀態之最大值與最小值的差作為變位(deflection),該感測器至鑄模表面為止的距離係藉由設置在設有鑄模鼓輪的地面的感測器所測得。此數值,為50μm以內較理想,為30μm以內是更理想的形態,因可使本發明中之長邊方向的厚度不均(σMD)變良好。此時的鑄模圓周上之凹凸的變位,具體而言係在設有鑄模裝置的地面設置雷射位移計,來測量鑄模輥與雷射位移計的測定部之距離。
落在鑄模輥的未延伸薄膜,係使用釘扎裝置,利用靜電力使其與鑄模密合。釘扎裝置,係對未延伸薄膜整個寬,將電荷由靜電施加導線賦予至鑄模輥上,藉由對於鑄模輥與薄膜之界面的靜電,使薄膜與鑄模輥密合。此時,為了將電荷的強度設成於寬方向為一定,較佳為靜電施加導線至薄膜的距離在未延伸薄膜整個寬上相等。又,為了保持鑄模輥與薄膜之密合性為適當的強度,較佳為調整靜電施加之電流的強度。
又,雖會為了提高藉由橫向延伸機進行延伸之際的夾子之握持力,而將未延伸薄膜端部調整成端 部的厚度變得較中央更厚,但端部的密合性差,利用鑄模輥之冷卻效率變差,結果,導致端部結晶化,成為破裂的原因,因此較理想的步驟為除了附加整個寬的釘扎裝置之外,還額外附加僅於端部附加釘扎裝置之所謂的邊緣釘扎裝置,藉此使未延伸薄膜的端部與鑄模密合,並抑制邊緣部分之冷卻不均,因其可抑制在鑄模之落點上的振動,使長邊方向的厚度不均變良好。再者,在將邊緣釘扎裝置應用於未延伸薄膜之際,只要從與未延伸薄膜的邊緣部分端部距離5mm以上的處所開始實施,即可進行有效的釘扎。其原因為在由邊緣釘扎裝置施加靜電時,可預防洩漏電流對鑄模輥進行異常放電。又,邊緣釘扎的處理寬度,隨著未延伸薄膜的邊緣厚度輪廓進行調整,而其範圍設定為20mm以上且小於100mm時,可進行有效的邊緣部之成型。
與鑄模輥密合而冷卻的薄膜,係使用抽離輥,自鑄模輥剝離薄膜,導入其次的延伸步驟。可對於此時的抽離輥通水以冷卻薄膜,也可驅動抽離輥。
延伸方法,可為同時雙軸延伸,也可為逐次雙軸延伸。在同時雙軸延伸中,同時實施縱向橫向的延伸之際,風速不均或沿著薄膜流動的氣流(伴隨氣流)會作為外部擾動而於寬方向的延伸時造成影響,還有對長邊方向也造成影響,因此逐次雙軸延伸係為較合宜適用的形態。
使用逐次延伸製造本發明的聚酯薄膜之際,最初的長邊方向之延伸,在以抑制傷痕之產生為前 提、及以抑制長邊方向的厚度不均為前提下是較為重要的,延伸溫度為90℃以上130℃以下,較佳為100℃以上120℃以下。若延伸溫度變得較90℃更低,則薄膜容易斷裂,若延伸溫度變得較130℃更高,則薄膜表面變得容易受到熱損傷。又,從防止延伸不均、及損傷之觀點而言,延伸較佳為分成2階段以上進行,總倍率,係朝長度方向2.8倍以上5.0倍以下,較佳為3.3倍以上4.0倍以下,朝寬方向3.5倍以上5倍以下,較佳為4.0倍以上4.5倍以下。在將縱向延伸倍率設定為前述數值之際,較理想為設定多個延伸區間,藉此設為不易引起延伸輥與薄膜打滑的狀態,因其可抑制打滑所致的延伸張力之變動。此時,較佳為在1個延伸區間之延伸倍率設為3.0倍以下,因其可確保適當的延伸張力。若超出該溫度、倍率範圍,則會引起延伸不均或薄膜斷裂等之問題,難以得到作為本發明特徵的薄膜。
在逐次延伸中,長邊方向的延伸過程,因薄膜與輥接觸時,輥的圓周速率與薄膜的速度差,而在薄膜打滑之際容易產生傷痕,而且也是長邊方向厚度不均之要因,故較佳為輥圓周速率可依每個輥個別地設定之驅動方式。在長邊方向之延伸過程中,輸送輥的材質,可依以下任一者而作選擇:在延伸前將未延伸薄膜加熱至玻璃轉移點以上;或者以保持在小於玻璃轉移點的溫度之狀態輸送至延伸區,在延伸時一口氣加熱。在延伸前將未延伸薄膜加熱至玻璃轉移點以上之際,加熱所致的黏著會誘發延伸不均,因此以防止前述為前提下,較 佳為選自非黏著性矽酮輥、陶瓷、鐵氟龍(註冊商標)。又,升溫過程中之輸送輥的溫度,較佳為以材質與輸送溫度的組合進行選定,在至未延伸薄膜超過玻璃轉移點為止,為了抑制加熱所致的黏著,較佳為將輸送輥設為鍍硬鉻的金屬輥且將輸送溫度設定為小於80℃。此時,較佳為在延伸步驟使用紅外線加熱器來補全熱量。
又,延伸輥對薄膜施加的負荷最多,且係在該製程造成傷痕和長邊方向厚度不均之原因的延伸不均較容易產生的步驟,因此延伸輥的表面粗度Ra較佳為0.005μm以上1.0μm以下,更佳為0.1μm以上0.6μm以下。若Ra較1.0μm更大,則延伸時輥表面的凸凹變得容易轉印於薄膜表面,另一方面,若較0.005μm更小,則輥與薄膜表面黏著,且薄膜容易受到熱損傷。為了控制表面粗度,適當調整研磨劑的粒度、研磨次數等係較為有效的。
在逐次延伸中,在以減低長邊方向的厚度不均為前提下,將縱向延伸倍率設定為低於橫向延伸倍率係為較佳的延伸條件。
接著,是將未延伸薄膜以保持在小於玻璃轉移點的溫度之狀態輸送至延伸區,而在延伸時一口氣加熱之際,預熱區的輸送輥,較佳為使用以硬鉻或碳化鎢進行表面處理之表面粗度Ra為0.2μm以上0.6μm以下的金屬輥,以抑制造成熱皺褶或長邊方向的厚度不均之原因的黏著。
接著,將該朝長邊方向延伸的單軸延伸薄膜,以橫向延伸機加熱至90℃以上且小於120℃後,朝寬方向延伸3倍以上且小於6倍,作為雙軸延伸(雙軸配向)薄膜。該橫向延伸機,係在烘箱的每個房間實施自我循環,將溫風噴吹至薄膜,藉以使薄膜升溫,實施延伸和熱固定。此時,為了防止由在烘箱內進行熱處理的薄膜析出的寡聚物附著於冷卻的烘箱,可在烘箱內實施供氣、排氣而置換空氣。此時,在供氣至烘箱內的空氣與循環氣流匯流之際,若空氣的溫度接近室外空氣,則匯流後的空氣會產生溫度不均,使長邊方向、及寬方向的厚度不均惡化,因此較佳為供氣氣流與循環氣流相同,或是用與加熱循環氣流的熱交換器之能力匹配的溫度進行加熱。
又,在以調節烘箱內的供氣、排氣量為前提下,在被輸送的薄膜上下流動之空氣的方向,較佳為相對於薄膜的移動方向為同一方向。在烘箱之各室中,自我循環的空氣、還有由上游往與薄膜輸送方向同一方向流動的伴隨氣流、對烘箱外進行的供氣或排氣,會導致STN內部的空氣之流動複雜地變化。此時,室間的空氣之流動,例如,由上游至下游之流動,會因為室間的壓力差,而變成由下游至上游之流動。在空氣的溫度依室間而不同時,室間的空氣之流動也與薄膜的伸縮不均相關聯。因此,關於烘箱之吸氣量、排氣量的條件,可藉由使排氣量多於供氣量,而誘導空氣朝同一方向流動。
本發明的雙軸配向聚酯薄膜,可進一步對於各方向進行1次以上再度延伸,也可以同時雙軸進行再度延伸。作為抑制長邊方向厚度不均的方法,可舉出利用長邊方向的再度延伸步驟,減緩在之前的橫向延伸步驟所產生的曲折(bowing)。此時,可利用長邊方向再度縱向延伸前的輸送輥,在80℃~100℃的溫度進行加熱,也可使用未加熱的輥進行輸送。再者,亦可不施加延伸倍率地通過再度縱向延伸步驟。再度縱向延伸後,進一步實施橫向延伸,且在延伸之後進行薄膜的熱處理,而該熱處理,可在烘箱中、加熱的輥上等以往周知的任意方法和位置進行。熱處理溫度,通常可設為150℃以上且小於245℃之任意的溫度,熱處理時間,通常較佳為在1秒鐘以上60秒鐘以下進行。可在使薄膜朝其長邊方向及/或寬方向進行鬆弛的同時進行熱處理。又,熱處理後,可在0℃以上150℃以下之低於熱處理溫度的溫度,使其朝寬方向鬆弛0%以上10%以下。
熱處理後的薄膜,可設置例如中間冷卻區和除冷區,而調整尺寸變化率或平面性。又,尤其是為了賦予特定的熱收縮性,也可在熱處理時或之後的中間冷卻區和除冷區中,朝縱方向及/或橫方向進行鬆弛。此時,在以使寬方向的厚度不均變良好為前提下,烘箱內部之寬方向的溫度差較佳為控制在5℃以內。
雙軸延伸後的薄膜,在輸送步驟進行冷卻後,切割邊緣後進行捲取,得到中間製品。在該輸送步驟,可測定寬方向的薄膜厚度,將該數據回饋而使用, 來調整模具厚度等,藉此進行薄膜厚度之調整,而且,可利用缺點檢測器進行異物偵測。厚度之測定,可利用β射線、X射線、光干涉式進行。測定可為:使1個測定裝置在寬方向橫向行進,而測定整個寬的厚度之方法;或使多個測定裝置在寬方向分割的區間內橫向行進,而測定整個寬的厚度之方法;在測定範圍較廣之際,係在寬方向固定多個測定裝置,而測定整個寬的厚度。又,關於測定的時點,可在上述輸送步驟內測定、或使用將中間製品分切後之雙軸配向聚酯薄膜卷而在離線實施。
中間製品係藉由分切步驟,分切為適當的寬、長度,並捲取至芯部,而得到雙軸配向聚酯薄膜的卷。芯部為塑膠或紙構成之圓筒形的捲芯部。由於對於厚度不均而言亦較佳使用溫濕度所致的伸縮少且捲取壓力所致的變形少之芯部,故較佳為使用塑膠製者。更佳為使用將塑膠以玻璃纖維或碳纖維強化的芯部。又,使用紙作為芯部之際,也可藉由在表面含浸樹脂而提高強度。分切步驟中之薄膜的切割步驟,係為用以去除中間製品之不需要的部分,而得到具有所需的製品寬之聚酯薄膜卷的步驟。在該切割步驟,對於中間製品的寬方向,同時切割3處至10處。使用於該切割的方式,可自以下的方式選定:以下刀片與上刀片的剪切而進行切割之方式、或在行經路線間之空中進行切割之切割方式。
薄膜寬,係利用該分切步驟分切後之薄膜的寬,藉由將前述切割步驟中之切割位置於寬方向進行 調節,可得到具有所需的製品寬之聚酯薄膜卷。又,本發明中之薄膜長邊方向的長度,係以設置於分切步驟之任意的卷上的測長器而進行測量。如前述,將中間製品在寬方向切割,並以任意的長度捲取至芯部而成者,於本發明中稱為聚酯薄膜卷。
藉由上述方法得到的脫模用雙軸配向聚酯薄膜卷係將長邊方向厚度不均少的薄膜捲取而成,因此該薄膜,可適當地使用作為脫模用途,特別是作為積層陶瓷電容器的成型用構件,甚至作為汽車用積層陶瓷電容器的成型用構件。再者,本發明中之脫模用途,係指將自本發明的雙軸配向聚酯薄膜卷所得到的薄膜作為成型用構件而使用於基材,並將構件成型,自成型後的構件剝離之用途。在此所言之構件,可舉出積層陶瓷電容器中之坯片、多層電路基板中之層間絕緣樹脂(電氣絕緣樹脂)、光學關聯構件中之聚碳酸酯(此時係在溶液製膜中使用)等。
以下採用實施例詳細地說明本發明。
關於本發明的測定方法、評價方法係如下所述。
(1)長邊方向之薄膜厚度不均(σMD)
使用設置於回捲檢查機的基恩斯公司製SI-T80,針對製品卷寬方向中央部,測定10,000m長邊方向的厚度。回捲速度為50m/分鐘、採樣周期為20毫秒,根據 此厚度數據,求出相對於平均值之偏差σ,並將其作為長邊方向的薄膜厚度不均。
(2)薄膜表面粗度表面的中心線粗度(SRa值)
使用三維細微表面形狀測定器(小坂製作所製ET-350K)進行測定,由得到之表面的輪廓曲線,依據JIS‧B0601(1994),求出算術平均粗度(中心線粗度)SRa值。測定條件係如下所述。
X方向測定長度:0.5mm
X方向進給速度:0.1mm/秒鐘
Y方向進給節距(pitch):5μm
Y方向線數:40條
截斷(cutoff):0.25mm
觸針壓:0.02mN
高度(Z方向)擴大倍率:5萬倍
再者,X方向係於樣本的寬方向進行測定,Y方向係於樣本的長邊方向進行測定。
(3)聚酯樹脂之熔融比電阻
將聚酯樹脂150g投入至經純水置換的50φ試驗管,在180℃減壓乾燥3小時。之後,在290℃、50鐘氮氣流通下進行熔融,將電極插入至熔融聚合物中。從對電極間施加5,000V的電壓時之電流量,算出電阻值,藉此求出熔融比電阻。此外,在2片銅板(22cm2)之間夾持鐵氟龍(註冊商標)的間隔物,使銅板間成為9mm而作成電極。
(實施例1)
(1)聚酯丸粒之作成
(聚酯A之作成)
在255℃將對苯二甲酸86.5質量份與乙二醇37.1質量份,一邊餾出水,一邊進行酯化反應。酯化反應結束後,添加三甲基磷酸0.02質量份、乙酸鎂0.06質量份、乙酸鋰0.01質量份、三氧化二銻0.0085質量份,接著,在減壓下,加熱而升溫至290℃,並進行聚縮合反應,得到固有黏度0.63dl/g的聚酯丸粒A。測定該料片之熔融比電阻的結果為7.0×107Ω‧cm。
(聚酯B之作成)
與上述同樣地製造聚酯時,在進行酯交換後,添加體積平均粒徑0.2μm、體積形狀係數f=0.51、莫氏硬度7的球狀二氧化矽,進行聚縮合反應,得到相對於聚酯含有1質量%的粒子之含二氧化矽的母粒(聚酯B)。
再者,聚酯B所使用的球狀二氧化矽係為單分散二氧化矽粒,其係一邊攪拌乙醇與矽酸乙酯之混合溶液,一邊對該混合溶液添加包含乙醇、純水、及作為鹼性觸媒之氨水的混合溶液,將得到的反應液攪拌並進行矽酸乙酯之水解反應及該水解生成物之聚縮合反應後,進行反應後之攪拌而得到的。
(聚酯C、D之作成)
再者,另外,利用晶種法使包含二乙烯苯80質量%、乙基乙烯苯15質量%、苯乙烯5質量%的單體進行吸附,使藉此方法所得到之體積平均粒徑0.3μm、體積形狀係數f=0.51、莫氏硬度3之二乙烯苯/苯乙烯共聚合交聯粒子(交聯度80%)的水漿料,利用排氣式雙軸混練機而包含於上述之實質上未含有粒子之均聚酯丸粒,分別得到體積平均粒徑各為0.3μm、0.8μm之相對於聚酯含有1質量%的二乙烯苯/苯乙烯共聚合交聯粒子的母粒(聚酯C、聚酯D)。
(聚酯E之作成)
製造聚酯A時,在進行酯交換後,將以碳酸氣體法作成之(體積平均粒徑體積平均粒徑1.1μm、莫氏硬度3)碳酸鈣10質量份與乙二醇90質量份進行濕式粉碎,得到碳酸鈣/乙二醇分散漿料。該碳酸鈣的體積平均粒徑為1.1μm。另一方面,對於對苯二甲酸二甲酯100質量份、及乙二醇64質量份,加入作為觸媒之乙酸錳0.04質量份、及三氧化二銻0.03質量份,進行酯交換反應,之後,對於反應生成物,加入作為磷化合物之磷酸三甲酯0.04質量份,之後,進一步加入之前製備的漿料1質量份,進行聚縮合反應,得到相對於聚酯含有1質量%的碳酸鈣的母粒(聚酯E)。
另一方面,將下述處方之薄膜製得後的薄膜加以回收並丸粒化者,作為回收原料A。此外,以下 所記載的比率,表示相對於薄膜全體質量之質量比(質量%)。
聚酯A:93.4
聚酯D:0.6
聚酯G:6.0
(2)聚酯丸粒之調合
供給於A層、B層、C層之各層擠製機的聚酯丸粒,係採用以下的比率進行調合。此外,以下所記載的比率,係為相對於構成各層之聚酯丸粒的質量比(單位:質量%)。
A層
聚酯A:87.5
聚酯B:12.5
B層
聚酯A:60.0
回收原料A:40.0
C層
聚酯A:65.0
聚酯C:30.0
聚酯D:5.0
(3)雙軸配向聚酯薄膜之製造
將前述之針對各層進行調合的原料在摻合機內進行攪拌後,關於A層及C層的原料,係將攪拌後的原料供 給至A層及C層用之附有排氣口的雙軸擠製機,而關於B層的原料,係在160℃減壓乾燥8小時,並供給至B層用的單軸擠製機。此外,B層係以串列式擠製機於275℃進行熔融擠製,並利用3μm以上的異物可捕捉95%以上之高精度的過濾器進行過濾後,以矩形之不同種3層用匯流器進行匯流積層,作成包含層A、層B、層C的3層積層。之後,使用經由保持在285℃之縫模對於未延伸薄膜之整個寬進行靜電施加之靜電施加鑄模法,並捲繞於表面溫度30℃之鑄模鼓輪而冷卻固化,而得到未延伸積層薄膜。此時,鑄模係進行對準調整,變位為25μm。
對該未延伸積層薄膜實施逐次延伸(長邊方向、寬方向)。首先,實施長邊方向之延伸,在105℃進行輸送後,於120℃朝長邊方向延伸3.8倍而成為單軸延伸薄膜。
將該單軸延伸薄膜,在拉幅機內朝橫方向以115℃延伸4.0倍,接著,在230℃進行熱固定,此時,朝寬方向鬆弛5%,以輸送步驟進行冷卻後,在切割邊緣後進行捲取,得到厚度31μm之雙軸延伸薄膜的中間製品。拉幅機的烘箱,係對來自烘箱外之供氣、排氣進行調整,使空氣朝一定方向流動。將該中間製品以分切機進行分切,得到厚度31μm之雙軸延伸薄膜的卷。測定該雙軸延伸薄膜之積層厚度的結果為A層:6.5μm、B層:23.5μm、C層:1.0μm。由得到的製品採取數據,將其特性評價結果示於表1。
(4)脫模層之塗布
其次,對於該雙軸延伸薄膜的卷,塗布交聯底漆層(Dow Corning Toray(股)製商品名BY24-846)經調整為固體成分1質量%的塗布液並且乾燥,使乾燥後的塗布厚度成為0.1μm的方式利用凹版塗布機進行塗布,且在100℃進行20秒鐘乾燥硬化。之後,在1小時以內,將加成反應型矽酮樹脂(Dow Corning Toray(股)製商品名LTC750A)100質量份、及鉑觸媒(Dow Corning Toray(股)製商品名SRX212)2質量份經調整為固體成分5質量%的塗布液,使乾燥後的塗布厚度成為0.1μm的方式利用凹版塗布進行塗布,且在120℃進行30秒鐘乾燥硬化後進行捲取,得到脫模薄膜。
(5)坯片之成型塗布
對於鈦酸鋇(Fuji Titanium Industry(股)製商品名HPBT-1)100質量份、聚乙烯醇縮丁醛(積水化學(股)製商品名BL-1)10質量份、鄰苯二甲酸二丁酯5質量份及甲苯-乙醇(質量比30:30)60質量份,加入數量平均粒徑2mm的玻璃珠,以噴射磨機混合、分散20小時後,進行過濾,而製備糊狀的陶瓷漿料。將得到的陶瓷漿料,使乾燥後的厚度成為0.5μm的方式在脫模薄膜上利用模塗布機進行塗布並且乾燥,並於塗布的中央部以非接觸方式連續測定乾燥後的漿料厚度。之後進行捲取,得到坯片。此時,評價漿料厚度不均σ值,將小於0.13定為良 好,將0.13以上且小於0.15定為尚可,將超過0.15者定為不良。實施例1的實施形態中之漿料厚度不均為坯片的成型性為良好。此時,良好為實用上沒有問題的等級。
(實施例2~4)
改變延伸倍率或厚度的製膜條件,除此以外係與實施例1同樣地實施,且將得到的結果示於表1。
(實施例5)
因應聚合物過濾器壓力之上升,降低齒輪泵的轉速控制,修正厚度的中心值。改變延伸倍率和厚度的製膜條件,除此以外係與實施例1同樣地實施,且將得到的結果示於表1。
(實施例6)
將邊緣釘扎裝置應用於鑄模薄片。釘扎係於未延伸薄片的5mm內側至50mm內側的範圍進行靜電施加。製膜條件係採用與實施例1相同的條件實施製膜。將得到的結果示於表。
(比較例1、2)
改變延伸倍率和厚度的製膜條件,除此以外係與實施例1同樣地實施,且將得到的結果示於表2。漿料厚度不均與實施例1~4相比惡化,且評價成為尚可。
(比較例3)
將縱向延伸倍率及橫向延伸倍率各自變更為4.5倍、4.5倍,除此以外係與實施例1同樣地實施。雖目的是藉由設定成高倍率,而平坦化在步驟以前所產生的不均,但結果為σMD惡化。σMD,實施厚度不均的頻率解析,結果確認到:似乎是縱向延伸所致之延伸不均的周期。
(比較例4)
冷卻水之流路劣化,結果,鑄模之變位成為50μm。採用該鑄模,改變延伸倍率和厚度的製膜條件,除此以外係與實施例1同樣地實施,且將得到的結果示於表2。漿料厚度不均的評價為不良。
(比較例5)
作為A層所含有的原料,使用熔融比電阻為5.0×108者。以反射光觀察鑄模後的薄片,結果,有橫段狀的延伸不均。在測定長邊方向的薄膜厚度不均σMD時,看到原數據之波形有周期性的厚度不均。因為其係顯著的厚度不均,所以未實施矽酮塗布及漿料塗布。
(比較例6)
採用比較例5的實施形態,應用邊緣釘扎裝置,但沒有在比較例5所看到的針對鑄模不良之改善效果。
(比較例7)
藉由增加在熱固定區的空氣之換氣次數,而除去烘箱內的寡聚物,所以在熱固定區各室進行吸排氣,但其它的製膜條件係與實施例1相同。結果,周期為不定,但看到薄膜厚度不均惡化的狀態。漿料的厚度不均為尚可。
本發明的雙軸配向聚酯薄膜,整個長邊方向的平面特性優異,因此可適當地用於脫模用途。尤其,可與加工時之張力對抗,在面內之伸縮行為經均勻化,因此可特別適當地用於將多層陶瓷電容器中之坯片作為構件使用的脫模用途。
Claims (3)
- 一種脫模用雙軸配向聚酯薄膜卷,其特徵為:薄膜寬為400mm以上,且相對於連續測定薄膜長邊方向10,000m所得之厚度的平均值之偏差σ值(σMD)為0.15μm以下,一方的薄膜表面之中心線粗度SRa(A)為1nm以上且小於15nm,另一方的薄膜表面之中心線粗度SRa(B)為20nm以上40nm以下,構成該SRa(A)為1nm以上且小於15nm之薄膜表面的層(A層)含有熔融比電阻為1.0×106Ω‧cm以上1.0×108Ω‧cm以下的聚酯樹脂,脫模用雙軸配向聚酯薄膜係作為積層陶瓷電容器的成型用構件使用。
- 如請求項1之脫模用雙軸配向聚酯薄膜卷,其中該脫模用雙軸配向聚酯薄膜具有3層以上之層構成。
- 如請求項1或2之脫模用雙軸配向聚酯薄膜卷,其中該脫模用雙軸配向聚酯薄膜係作為汽車用積層陶瓷電容器的成型用構件使用。