TWI778151B - 非水電解質二次電池 - Google Patents
非水電解質二次電池 Download PDFInfo
- Publication number
- TWI778151B TWI778151B TW107136688A TW107136688A TWI778151B TW I778151 B TWI778151 B TW I778151B TW 107136688 A TW107136688 A TW 107136688A TW 107136688 A TW107136688 A TW 107136688A TW I778151 B TWI778151 B TW I778151B
- Authority
- TW
- Taiwan
- Prior art keywords
- negative electrode
- positive electrode
- secondary battery
- electrolyte secondary
- separator
- Prior art date
Abstract
本發明的課題在於提供在小型電池的內部收納更多的電極，而且使充放電特性安定化之非水電解質二次電池。
本發明的解決手段為一種非水電解質二次電池，係中介著隔板對向配置正極與負極，收納於收納容器而成，其特徵為：前述負極由包含鋰與鋁的合金所構成，於前述負極與隔板之間設有特定寬幅的間隙。
Description
本發明係關於非水電解質二次電池。
負極使用鋰-鋁合金的硬幣型非水電解質二次電池，能量密度高，可以增大容量所以適宜使用。於此非水電解質二次電池，負極例如在鋁材與不銹鋼材之覆蓋材所構成的負極罐貼附鋰，藉由與鋁合金化而得(例如參照下列專利文獻1)。
此外，藉由與具有耐熱性的電解液或隔板或密合墊等構件組合，可以提供適於迴焊實裝的非水電解質二次電池(例如參照下列專利文獻2)。
[先前技術文獻]
[專利文獻]
[專利文獻1] 日本特開平11-121042號公報
[專利文獻2] 日本特開2004-095399號公報
[發明所欲解決之課題]
隨著這樣的硬幣型非水電解質二次電池的用途擴展，要求維持實裝面積的同時使容量增加。此時，使電池尺寸於厚度方向上增大，於其中收納電極與電解液的話，充電時由於容易析出金屬鋰而有充放電特性變得不安定的問題。特別是為了實裝於基板，接受伴隨著迴焊焊接的熱處理的場合，進行電解液的蒸發或分解的話，會有如前所述的充電異常進而變得顯著的問題。
本發明有鑑於這樣的問題而完成之發明，課題在於提供在小型電池的內部收納更多的電極，而且使充放電特性安定化之非水電解質二次電池。
[供解決課題之手段]
[1] 為了解決前述課題，相關於本發明之一型態之非水電解質二次電池，係中介著隔板對向配置正極與負極，收納於收納容器而成，其特徵為：前述負極由包含鋰與鋁的合金所構成，於前述負極與隔板之間設有特定寬幅的間隙。
在本型態，在包含鋰的負極與隔板之間設有特定寬幅的間隙，所以即使進行充電而於負極側多少產生金屬鋰的析出，也不會使充放電特性變得不安定。此外，可以提供往基板等實裝時進行迴焊實裝，即使由於經歷伴隨著迴焊焊接的熱履歷，於電極或電解液的一部分產生蒸發或分解的場合，也不會產生充電異常的非水電解質二次電池。
特別是在維持實裝面積同時增加容量的目的下使電池尺寸在厚度方向增大的場合，於電池內容納電極與電解液的場合，進行迴焊實裝的話，於充電時在負極側攜出金屬鋰的可能性變高，但藉著設置前述間隙，可以提供充放電特性不會變得不安定的非水電解質二次電池。
[2] 在前述一型態之非水電解質二次電池，特徵為正極罐為有底圓筒狀，負極罐於前述正極罐的開口部內側中介著密合墊被固定，藉著設置把前述正極罐的開口部斂縫(fullering)於前述負極罐側之斂縫部使前述收納容器密封，於前述受納容器收納正極與負極與隔板與前述電解液。
藉著中介著密合墊設斂縫部使正極罐與負極罐為密封構造的非水電解質二次電池，由正極罐與負極罐構成的收納容器為密封構造，所以因迴焊焊接等而產生的電極或電解液的分解物等不會往外部逃避而存在於收納容器的內部，有對電池性能造成影響之虞。但是，若為設有前述特定寬幅的間隙的構造的話，難以受到前述金屬鋰析出的影響，難以受到電極或電解液之分解物加上金屬鋰析出導致的影響。
[3] 在前述一型態之非水電解質二次電池，較佳為前述正極罐的外徑為4～6mm的場合，前述間隙的間隔為0.34mm以上0.39mm以下。
於本型態之非水電解質二次電池，藉著中介著密合墊設斂縫部使正極罐與負極罐為密封構造之非水電解質二次電池，前述間隙的寬幅太大的場合會有負極罐的中心成為凹下構造的場合。於這一點，在外徑4～6mm的正極罐的場合，前述間隙的寬幅為0.34mm以上0.39mm以下的話，產生的凹部大小為電池的容許範圍，可以提供即使受到迴焊實裝等的加熱也沒有外觀問題的非水電解質二次電池。
[發明之效果]
根據本型態，可以提供即使產生往負極側之金屬鋰的析出、迴焊實裝導致產生電極或電解液的一部份蒸發或分解等的場合，充放電特性也安定的非水電解質二次電池。
特別是在維持實裝面積同時增加容量的目的下使電池尺寸在厚度方向增大的場合，於電池內容納電極與電解液的場合，於充電時在負極側攜出金屬鋰的可能性變高，但藉著設置間隙，可以提供充放電特性安定的非水電解質二次電池。
以下，舉本發明的實施型態之非水電解質二次電池之例，參照圖1同時詳述其構成。又，本發明所說明的非水電解質二次電池，是作為正極或負極使用的活性物質與隔板收納於收納容器內而成的二次電池。此外，在使用於以下說明的圖式，為了要使各構件為可以辨識的大小而適當改變表示各構件之比例尺，所以各構件的相對大小當然不限於圖面所示的型態。
圖1所示之本實施型態之非水電解質二次電池1，是所謂的硬幣(鈕扣)型的電池。此非水電解質二次電池1，具備有底圓筒狀之正極罐12、塞住正極罐12的開口部之有蓋圓筒狀的蓋狀之負極罐22、與沿著正極罐12的內周面而設的密合墊40，以及使正極罐12的開口部周緣斂縫於內側而構成的薄型(扁平型)收納容器2。於收納容器2內，被形成正極罐12與負極罐22所包圍的收納空間，於此收納空間正極10與負極20中介著隔板30對向配置，進而被充填著電解液50。
正極罐12的材質使用從前公知者，例如可以舉出SUS316L或SUS329JL、或者NAS64等不銹鋼。於本型態，正極罐12的外徑被形成在4mm～6mm之範圍。
負極罐22的材質，與正極罐12的材質同樣，可以舉出使用從前公知的不銹鋼，例如可以舉出SUS316L或SUS329JL、或者SUS304-BA等不銹鋼。
於本型態，正極10中介著正極集電體14被導電連接於正極罐12的內面。於正極10的上部載置著隔板30。於隔板30的上方設有負極20。負極20，係於負極罐22的底面藉由覆蓋層壓接等手段而一體化的硬質鋁層24被壓接鋰，然後二者合金化之鋰-鋁合金。亦及，負極20中介著負極罐22底面的硬質鋁層24被導電連接於負極罐22的內面。
密合墊40，被連接於隔板30的外周，密合墊40保持著隔板30。此外，於正極10，被含浸著充填於收納容器2內的電解液50。
(正極)
於正極10，正極活性物質的種類沒有特別限定，例如可以選擇錳氧化物或者含鋰的錳氧化物作為正極活性物質。
正極10中的正極活性物質的含量，考慮非水電解質二次電池1所要求的放電容量等而決定，可以在50～95質量百分比(質量%)的範圍。正極活性物質的含量在前述較佳的範圍的下限值以上的話，容易得到充分的放電容量，在較佳的上限值以下的話，容易使正極10成形。
正極10，亦可含有結合劑(以下亦把用於正極10的結合劑稱為「正極結合劑」)。
正極結合劑，可以使用從前公知的物質，例如可以選擇聚四氟乙烯(PTFE)、聚偏二氟乙烯(PVDF)、丁苯橡膠(Styrene-Butadiene Rubber，SBR)、聚丙烯酸(PA)、羧甲基纖維素(Carboxymethyl Cellulose, CMC)、聚乙烯醇(PVA)等。
此外，正極結合劑亦可單獨使用前述之中的1種，或者，亦可組合2種以上使用。於正極10，正極結合劑的含量，例如可以為1～20質量%。
正極集電體14，可以使用從前公知者，可以舉出把碳作為導電填充物之導電性樹脂接著劑等。
此外，在本實施型態，正極活性物質，除了前述之鋰錳氧化物以外，亦可含有其他正極活性物質，例如鉬氧化物、鋰鐵磷氧化物、鋰鈷氧化物、鋰鎳氧化物、釩氧化物等，其他氧化物之任何一種以上。
(負極)
負極20，可以舉出鋰箔(鋰金屬薄片)、鋰-鋁合金、接觸鋰或電化學摻雜鋰的碳等，若為含有鋰與鋁的合金(鋰-鋁合金)的話，可以防止鋰的樹枝狀晶(dendrite)往負極表面析出所以較佳。鋰-鋁合金，藉由在被形成於負極罐22的硬質鋁層24壓接鋰箔的狀態下接觸於電解液，可使鋰與鋁合金化。
(隔板)
隔板30，中介於正極10與負極20之間，具有大的離子透過度且使用具有機械強度之絕緣膜。
隔板30，可無任何限制地適用從前用於非水電解質二次電池的隔板，例如可以舉出鹼玻璃、硼矽酸玻璃、石英玻璃、含鉛玻璃等玻璃、聚苯硫醚(PPS)、聚醚醚酮(PEEK)、聚對苯二甲酸乙二酯(PET)、聚醯胺醯亞胺(PAI)、聚醯胺、聚醯亞胺(PI)等樹脂構成的不織布等。其中，以玻璃製不織布為佳，硼矽酸玻璃製不織布更佳。玻璃製不織布機械強度優異同時具有大的離子透過度，所以可謀求減低內電阻而提高放電容量。
隔板30的厚度考慮非水電解質二次電池1的大小或隔板30的材質等而決定，例如可以為5～300μm。
(密合墊)
密合墊40例如由熱變形溫度230℃以上的樹脂構成為佳。用於密合墊40的樹脂材料的熱變形溫度為230℃以上的話，可以防止由於迴焊焊接處理或非水電解質二次電池1之使用中的加熱而使密合墊顯著變形、電解液50漏出。
密合墊40，如圖1所示，沿著正極罐12的內周面被形成為圓環狀，該環狀溝41的內部被配置負極罐22的外周端部22a。
密合墊40，係由在正極罐12的開口部內周側具有無間隙地插入的外徑之環狀的外緣部40A，與環狀的內緣部40B，與連接這些外緣部40A及內緣部40B的下端部彼此之底壁部40C所構成。亦即，於密合墊40的外周緣上面側被形成可插入負極罐22的外周端部22a的環狀溝41。
藉著使圖1所示的正極罐12的開口部12a之周緣部12b斂縫(填隙)於內側亦即負極罐22側挾入密合墊40而構成密封收納空間的構造之收納容器2。
以上所述的密封墊40的材質，例如可以舉出聚苯硫醚(PPS)、聚對苯二甲酸乙二酯(PET)、聚醯胺、液晶高分子(LCP)、四氟乙烯-全氟代烷基乙烯基醚共聚物樹脂(PFA)、聚醚醚酮(PEEK)、聚醚腈樹脂(PEN)、聚醚酮樹脂(PEK)、聚丙烯酸酯樹脂、聚對苯二甲酸丁二酯樹脂(PBT)、聚對苯二甲酸環己二甲酯樹脂、聚醚碸樹脂(PES)、聚氨基雙馬來醯亞胺樹脂、聚醚亞胺樹脂、氟樹脂等。此外，可以適切地使用在這些材料把玻璃纖維、雲母晶鬚、陶瓷微粉末等以30質量%以下的添加量添加者。藉著使用這樣的材質，可以防止佳熱導致密合墊顯著變形，而漏出電解液50。又，非水電解質二次電池1在不特別要求耐熱性的場合，密合墊40亦可選擇前述以外的材料。
(負極與隔板間之間隙)
於本型態之非水電解質二次電池1，負極20的底面與隔板30之間設有特定寬幅(特定厚度)的間隙d。
非水電解質二次電池1，以正極罐12的外徑為4～6mm的場合，間隙d的寬幅(厚度)在0.34mm以上0.39mm以下的範圍為佳。間隙d的寬幅未滿0.34mm的場合，承受相當於迴焊焊接時的加熱的話，有對充放電曲線產生不良影響之虞。此外，間隙d的寬幅超過0.39mm的場合，藉由歛縫加工密封正極罐12的開口部12a而形成收納容器2的話，負極罐12的中心部形成凹部狀的較大的凹部。此凹部之凹下量未滿0.006mm的話，即使目視，凹部也不醒目，但超過0.01mm的凹下量之凹部的話，凹部便得醒目，有成為形狀不良之虞。正極罐12的外徑為4～6mm的場合，間隙d的寬幅0.39mm程度時凹下量成為0.006mm程度，所以不成問題，但間隙d的寬幅超過0.44mm的話，凹下量會超過0.01mm。考慮這些的話，間隙d的寬幅以在0.34mm以上0.39mm以下之範圍為佳。此外，間隙d的寬幅0.37mm程度時凹下量為0.004mm變得更小，所以間隙d的寬幅0.37mm以下為更佳。在本型態，負極20的底面與隔板30的上面分別為平面，所以負極20的底面與隔板30的上面之間被形成寬幅均一的間隙d。
「電解液」
電解液50通常是把支撐鹽溶解於非水溶媒。
於本型態之非水電解質二次電池1，構成電解液50的非水溶媒，可以選擇以四乙二醇二甲醚(TEG)為主溶媒，以二乙氧乙烷(DEE)為副溶媒者。非水溶媒，通常考慮電解液50要求的耐熱性或黏度等而決定。構成甘醇二甲醚系溶媒之主溶媒，可以利用四乙二醇二甲醚、三乙二醇二甲醚、五乙二醇二甲醚、二乙二醇二甲醚等。
在本型態，採用使用了含四乙二醇二甲醚(TEG)及二乙氧乙烷(DEE)的非水溶媒之電解液50。藉著採用這樣的構成，DEE及TEG溶媒和於構成支撐鹽的鋰離子。
此時，DEE的供體數(donar number)比TEG還要高，DEE較高選擇性地與鋰離子溶媒和。如此，DEE及TEG溶媒和於構成支撐鹽的鋰離子，保護鋰離子。藉此，例如即使於高溫高濕環境下水分侵入非水電解質二次電池內部的場合，也可以防止水分與鋰反應，所以可得抑制放電容量降低，提高保存特性的效果。
支撐鹽可以使用在非水電解質二次電池之電解液作為支撐鹽使用的公知之鋰化合物，例如可以舉出LiCH3
SO3
、LiCF3
SO3
、LiN(CF3
SO2
)2
、LiN(C2
F5
SO2
)2
、LiC(CF3
SO2
)3
、LiN(CF3
SO3
)2
、LiN(FSO2
)2
等有機酸鋰鹽；LiPF6
、LiBF4
、LiB(C6
H5
)4
、LiCl、LiBr等無機酸鋰鹽等之鋰鹽。其中，具有鋰離子導電性的化合物之鋰鹽為佳，LiN(CF3
SO2
)2
、LiN(FSO2
)2
、LiBF4
為更佳，由耐熱性以及與水分的反應性較低，可以充分發揮保存特性的觀點來看，以LiN(CF3
SO2
)2
為特佳。
支撐鹽，亦可單獨使用前述之中的1種，或者，亦可組合2種以上使用。電解液50中的支撐鹽的含量，可以考慮支撐鹽的種類等而決定。
根據以上說明之本型態之非水電解質二次電池1，因為非水溶媒含有四乙二醇二甲醚(TEG)與二乙氧乙烷(DEE)為主體，所以具有耐得住迴焊焊接的耐熱性，可提供即使承受伴隨著迴焊焊接的加熱，也少有溶媒氣化之虞，少有收納容器的2內壓上升之虞，且難以在收納容器2產生變形之構成。
此外，溶媒為含有四乙二醇二甲醚與二乙氧乙烷為主體的甘醇二甲醚系溶媒的話，可以因這些溶媒的沸點高而提高電解液之耐熱性。
又，於先前的實施型態，較佳為使用不銹鋼製的正極罐與不銹鋼製的負極罐，以具備將這些歛縫之收納容器之硬幣型構造的非水電解質二次電池為例進行說明，但本型態並不限定於此構造。
例如，陶瓷製的容器本體開口部，藉由使用金屬製的封口構件之縫焊接等加熱處理而以陶瓷製蓋體密封的構造之非水電解質二次電池也可以適用本發明構造。
[實施例]
試做圖1所示的構成之非水電解質二次電池，進行了後述的評估試驗。
作為正極10，首先於市售的鋰錳氧化物
(Li1.14
Co0.06
Mn1.80
O4
)，以鋰錳氧化物：石墨：聚丙烯酸=90：8：2(質量比)的比例混合作為導電輔助劑之石墨與作為結合劑之聚丙烯酸而作為正極合劑。將此正極合劑13mg以2ton/cm2
的加壓力加壓，加壓成形為直徑4mm、厚度1mm的圓盤型錠。
把得到的錠(正極)使用含碳的導電性樹脂接著劑接著於不銹鋼(SUS316L：t=0.20mm)製的外徑4.8mm的正極罐的內面，將這些一體化而得正極單元。此後，將此正極單元在大氣中以120℃×11小時的條件進行減壓加熱乾燥。其次，把密封劑塗布於正極單元之正極罐的開口部內側面。
接著，以如下方式製作了負極之鋰-鋁合金。首先，準備鋰箔(外徑4mm、厚度0.1mm)。
接著準備藉由覆蓋層貼合厚度0.13mm的硬質鋁層於不銹鋼(SUS304AL(JIS1050)：t=0.20mm)製的負極罐的內面的構造之負極罐。對此負極罐之硬質鋁層藉由壓接鋰箔而得負極單元。其後，經後述製程，得到鋰與鋁被合金化的負極。
其次，使玻璃纖維構成的不織布乾燥之後，被沖壓為直徑4mm的圓盤型作為隔板。接著，將此隔板載置於正極錠之上，於負極罐的開口部配置PEEK樹脂製的密合墊。
(電解液的製作)
以質量比1：1混合四乙二醇二甲醚(TEG)，二乙氧乙烷(DEE)之各溶媒作為非水溶媒，於得到的非水溶媒溶解LiTFSI(1M)作為支撐鹽而得電解液。
於如前所述準備的正極罐與負極罐，把以前述步驟調整的各例之電解液，每1個電池合計填充4.5μL。
其次，以隔板抵接於正極的方式把負極單元歛縫於正極單元。接著，藉著嵌合正極罐的開口部而密封正極罐與負極罐之後，在25℃靜置7日，得到非水電解質二次電池。密封正極罐與負極罐的密合墊由聚醚醚酮樹脂(PEEK樹脂)構成。
準備了根據前述之製造方法，在負極與隔板之間形成0.22mm的間隙之試樣1。此外，使正極的厚度與鋰箔的厚度，在維持正極與負極的容量平衡的情況下分別變更，準備了負極與隔板之間形成0.24mm間隙的試樣2、負極與隔板之間形成0.3mm間隙的試樣3、負極與隔板之間形成0.34mm間隙的試樣4、負極與隔板之間形成0.37mm間隙的試樣5、負極與隔板之間形成0.44mm間隙的試樣6。
根據前述製造方法，準備了負極與隔板之間形成0.04mm間隙的試樣7、負極與隔板之間形成0.14mm間隙的試樣8、負極與隔板之間形成0.24mm間隙的試樣9、負極與隔板之間形成0.34mm間隙的試樣10、負極與隔板之間形成0.39mm間隙的試樣11、負極與隔板之間形成0.51mm間隙的試樣12、負極與隔板之間形成0.61mm間隙的試樣13。
「評估試驗」
(凹下量測定試驗)
針對試樣1～試樣6之非水電解質二次電池，使正極罐與負極罐歛縫密封之後，測定了形成於負極罐的中央部的凹部之凹下量。其結果顯示於以下之表1與圖3。
由表1所示結果，可知試樣1～4其凹下量幾乎為零，非水電解質二次電池的外觀完全沒有問題。試樣5被形成0.004mm之凹下，但目視看起來幾乎無法確認凹部，外徑4～6mm之非水電解質二次電池的外觀並無問題。
對這些試樣，試樣6可以目視確認凹部的存在，非水電解質二次電池的外觀有問題。由此結果，顯示出藉由目視無法確認凹部凹下量之間隙到0.37mm為止的話，可知外徑4～6mm的非水電解質二次電池，即使增大負極與隔板之間的間隙也沒有問題。
「充電試驗」
使用試樣7～試樣13之非水電解質二次電池，針對各個，施以在160～200℃預備加熱10分鐘後，在260℃加熱10秒進行正式加熱之相當於迴焊焊接的熱處理之後，以充電電流max：0.02mA、充電電壓：3.1V、充電時間：96(hr)的條件進行了充電試驗。其結果顯示於以下表2。
表2所示的有充電異常，意味著在各試樣充電時，描繪以充電時間(hr)為橫軸，以充電電壓(V)為縱軸的圖4所示之圖的場合，產生電壓的大幅變動。表2所示之沒有充電異常，意味著在描繪圖4所示之圖的場合，可以不產生電壓變動而充電。
如表2所示結果，把間隙設定在0.34mm～0.61mm之試樣10～13，沒有發生充電異常，但在間隙設定在0.04mm～0.24mm之試樣7～19發生充電異常。
結果，有鑑於先前根據表1與圖3所說明的結果，於外徑4～6mm之非水電解質二次電池，針對負極與隔板之間隙在0.34mm以上0.39mm以下的話不會發生充電異常，可得外觀沒有問題的非水電解質二次電池。
1‧‧‧非水電解質二次電池
2‧‧‧收納容器
10‧‧‧正極
12‧‧‧正極罐
12a‧‧‧開口部
12B‧‧‧周緣部
14‧‧‧正極集電體
20‧‧‧負極
22‧‧‧負極罐
24‧‧‧硬質鋁層
30‧‧‧隔板
40‧‧‧密合墊
41‧‧‧環狀溝
50‧‧‧電解液
圖1係顯示相關於第1實施型態的非水電解質二次電池之剖面圖。
圖2係顯示測定使用實施例製作之複數非水電解質二次電池於負極側設的間隙(空間)大小與凹下量的關係的結果之圖。
圖3係顯示測定使用實施例製作非水電解質二次電池進行充電的場合之充電電壓之圖。
1‧‧‧非水電解質二次電池
2‧‧‧收納容器
10‧‧‧正極
12‧‧‧正極罐
12a‧‧‧開口部
12b‧‧‧周緣部
14‧‧‧正極集電體
20‧‧‧負極
22‧‧‧負極罐
24‧‧‧硬質鋁層
30‧‧‧隔板
40‧‧‧密合墊
40A‧‧‧外緣部
40B‧‧‧內緣部
40C‧‧‧底壁部
41‧‧‧環狀溝
50‧‧‧電解液
d‧‧‧間隙
Claims (2)
- 一種非水電解質二次電池，係中介著隔板對向配置正極與負極，收納於收納容器而成，其特徵為：前述負極由包含鋰與鋁的合金所構成，於前述負極與隔板之間設有特定寬幅的間隙；前述正極罐的外徑為4~6mm的場合，前述間隙的間隔為0.34mm以上0.39mm以下。
- 如申請專利範圍第1項之非水電解質二次電池，其中前述正極罐為有底圓筒狀，前述負極罐於前述正極罐的開口部內側中介著密合墊被固定，藉著設置把前述正極罐的開口部斂縫(fullering)於前述負極罐側之斂縫部使前述收納容器密封，於前述收納容器收納正極與負極與隔板與前述電解液。