SI2830821T1 - Metoda za spajanje kovinskih delov - Google Patents

Metoda za spajanje kovinskih delov

Info

Publication number
SI2830821T1
SI2830821T1 SI201330498A SI201330498A SI2830821T1 SI 2830821 T1 SI2830821 T1 SI 2830821T1 SI 201330498 A SI201330498 A SI 201330498A SI 201330498 A SI201330498 A SI 201330498A SI 2830821 T1 SI2830821 T1 SI 2830821T1
Authority
SI
Slovenia
Prior art keywords
metal parts
joining metal
joining
parts
metal
Prior art date
Application number
SI201330498A
Other languages
English (en)
Inventor
Per Sjodin
Kristian Walter
Original Assignee
Alfa Laval Corporate Ab
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Alfa Laval Corporate Ab filed Critical Alfa Laval Corporate Ab
Publication of SI2830821T1 publication Critical patent/SI2830821T1/sl

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/24—Selection of soldering or welding materials proper
    • B23K35/30—Selection of soldering or welding materials proper with the principal constituent melting at less than 1550 degrees C
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B22F1/10—Metallic powder containing lubricating or binding agents; Metallic powder containing organic material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/0008—Soldering, e.g. brazing, or unsoldering specially adapted for particular articles or work
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/0008—Soldering, e.g. brazing, or unsoldering specially adapted for particular articles or work
    • B23K1/0012—Brazing heat exchangers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/19—Soldering, e.g. brazing, or unsoldering taking account of the properties of the materials to be soldered
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/20—Preliminary treatment of work or areas to be soldered, e.g. in respect of a galvanic coating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/20—Preliminary treatment of work or areas to be soldered, e.g. in respect of a galvanic coating
    • B23K1/203—Fluxing, i.e. applying flux onto surfaces
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K20/00—Non-electric welding by applying impact or other pressure, with or without the application of heat, e.g. cladding or plating
    • B23K20/002—Non-electric welding by applying impact or other pressure, with or without the application of heat, e.g. cladding or plating specially adapted for particular articles or work
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K20/00—Non-electric welding by applying impact or other pressure, with or without the application of heat, e.g. cladding or plating
    • B23K20/24—Preliminary treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/001—Interlayers, transition pieces for metallurgical bonding of workpieces
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/001—Interlayers, transition pieces for metallurgical bonding of workpieces
    • B23K35/004—Interlayers, transition pieces for metallurgical bonding of workpieces at least one of the workpieces being of a metal of the iron group
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/001—Interlayers, transition pieces for metallurgical bonding of workpieces
    • B23K35/007—Interlayers, transition pieces for metallurgical bonding of workpieces at least one of the workpieces being of copper or another noble metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
    • B23K35/0222—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape for use in soldering, brazing
    • B23K35/0244—Powders, particles or spheres; Preforms made therefrom
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
    • B23K35/0222—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape for use in soldering, brazing
    • B23K35/0244—Powders, particles or spheres; Preforms made therefrom
    • B23K35/025—Pastes, creams, slurries
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/24—Selection of soldering or welding materials proper
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/34—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material comprising compounds which yield metals when heated
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/36—Selection of non-metallic compositions, e.g. coatings, fluxes; Selection of soldering or welding materials, conjoint with selection of non-metallic compositions, both selections being of interest
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/36—Selection of non-metallic compositions, e.g. coatings, fluxes; Selection of soldering or welding materials, conjoint with selection of non-metallic compositions, both selections being of interest
    • B23K35/3612—Selection of non-metallic compositions, e.g. coatings, fluxes; Selection of soldering or welding materials, conjoint with selection of non-metallic compositions, both selections being of interest with organic compounds as principal constituents
    • B23K35/3613—Polymers, e.g. resins
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/36—Selection of non-metallic compositions, e.g. coatings, fluxes; Selection of soldering or welding materials, conjoint with selection of non-metallic compositions, both selections being of interest
    • B23K35/362—Selection of compositions of fluxes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/36—Selection of non-metallic compositions, e.g. coatings, fluxes; Selection of soldering or welding materials, conjoint with selection of non-metallic compositions, both selections being of interest
    • B23K35/365—Selection of non-metallic compositions of coating materials either alone or conjoint with selection of soldering or welding materials
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C1/00—Making non-ferrous alloys
    • C22C1/02—Making non-ferrous alloys by melting
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C19/00—Alloys based on nickel or cobalt
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C23C30/005—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process on hard metal substrates
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28D—HEAT-EXCHANGE APPARATUS, NOT PROVIDED FOR IN ANOTHER SUBCLASS, IN WHICH THE HEAT-EXCHANGE MEDIA DO NOT COME INTO DIRECT CONTACT
    • F28D9/00—Heat-exchange apparatus having stationary plate-like or laminated conduit assemblies for both heat-exchange media, the media being in contact with different sides of a conduit wall
    • F28D9/0062—Heat-exchange apparatus having stationary plate-like or laminated conduit assemblies for both heat-exchange media, the media being in contact with different sides of a conduit wall the conduits for one heat-exchange medium being formed by spaced plates with inserted elements
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D53/00—Making other particular articles
    • B21D53/02—Making other particular articles heat exchangers or parts thereof, e.g. radiators, condensers fins, headers
    • B21D53/04—Making other particular articles heat exchangers or parts thereof, e.g. radiators, condensers fins, headers of sheet metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K2101/00—Articles made by soldering, welding or cutting
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K2103/00—Materials to be soldered, welded or cut
    • B23K2103/02—Iron or ferrous alloys
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K2103/00—Materials to be soldered, welded or cut
    • B23K2103/08—Non-ferrous metals or alloys
    • B23K2103/12—Copper or alloys thereof
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C24/00—Coating starting from inorganic powder
    • C23C24/08—Coating starting from inorganic powder by application of heat or pressure and heat
    • C23C24/10—Coating starting from inorganic powder by application of heat or pressure and heat with intermediate formation of a liquid phase in the layer
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28D—HEAT-EXCHANGE APPARATUS, NOT PROVIDED FOR IN ANOTHER SUBCLASS, IN WHICH THE HEAT-EXCHANGE MEDIA DO NOT COME INTO DIRECT CONTACT
    • F28D9/00—Heat-exchange apparatus having stationary plate-like or laminated conduit assemblies for both heat-exchange media, the media being in contact with different sides of a conduit wall
    • F28D9/0012—Heat-exchange apparatus having stationary plate-like or laminated conduit assemblies for both heat-exchange media, the media being in contact with different sides of a conduit wall the apparatus having an annular form
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F21/00—Constructions of heat-exchange apparatus characterised by the selection of particular materials
    • F28F21/08—Constructions of heat-exchange apparatus characterised by the selection of particular materials of metal
    • F28F21/081—Heat exchange elements made from metals or metal alloys
    • F28F21/082—Heat exchange elements made from metals or metal alloys from steel or ferrous alloys
    • F28F21/083—Heat exchange elements made from metals or metal alloys from steel or ferrous alloys from stainless steel
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F21/00—Constructions of heat-exchange apparatus characterised by the selection of particular materials
    • F28F21/08—Constructions of heat-exchange apparatus characterised by the selection of particular materials of metal
    • F28F21/089—Coatings, claddings or bonding layers made from metals or metal alloys
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F3/00—Plate-like or laminated elements; Assemblies of plate-like or laminated elements
    • F28F3/02—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations
    • F28F3/04—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element
    • F28F3/042—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element in the form of local deformations of the element
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T29/00—Metal working
    • Y10T29/49—Method of mechanical manufacture
    • Y10T29/4935—Heat exchanger or boiler making
    • Y10T29/49366—Sheet joined to sheet
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12778—Alternative base metals from diverse categories
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12986—Adjacent functionally defined components
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/25—Web or sheet containing structurally defined element or component and including a second component containing structurally defined particles
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/25—Web or sheet containing structurally defined element or component and including a second component containing structurally defined particles
    • Y10T428/259—Silicic material
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/26—Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension
    • Y10T428/266—Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension of base or substrate
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/27—Web or sheet containing structurally defined element or component, the element or component having a specified weight per unit area [e.g., gms/sq cm, lbs/sq ft, etc.]
    • Y10T428/273—Web or sheet containing structurally defined element or component, the element or component having a specified weight per unit area [e.g., gms/sq cm, lbs/sq ft, etc.] of coating
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2922—Nonlinear [e.g., crimped, coiled, etc.]
    • Y10T428/2924—Composite
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2982—Particulate matter [e.g., sphere, flake, etc.]
SI201330498A 2012-03-28 2013-03-27 Metoda za spajanje kovinskih delov SI2830821T1 (sl)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EP12161742.7A EP2644312B1 (en) 2012-03-28 2012-03-28 A novel brazing concept
EP13715637.8A EP2830821B1 (en) 2012-03-28 2013-03-27 Method for joining metal parts
PCT/EP2013/056530 WO2013144211A1 (en) 2012-03-28 2013-03-27 Method for joining metal parts

Publications (1)

Publication Number Publication Date
SI2830821T1 true SI2830821T1 (sl) 2017-03-31

Family

ID=47997546

Family Applications (5)

Application Number Title Priority Date Filing Date
SI201231477T SI2644312T1 (sl) 2012-03-28 2012-03-28 Nov koncept trdega spajkanja
SI201331600T SI2830817T1 (sl) 2012-03-28 2013-03-27 Nov koncept trdega spajkanja
SI201330938T SI2830820T1 (sl) 2012-03-28 2013-03-27 Nov koncept spajkanja
SI201331603T SI2830818T1 (sl) 2012-03-28 2013-03-27 Ploščni toplotni izmenjevalnik
SI201330498A SI2830821T1 (sl) 2012-03-28 2013-03-27 Metoda za spajanje kovinskih delov

Family Applications Before (4)

Application Number Title Priority Date Filing Date
SI201231477T SI2644312T1 (sl) 2012-03-28 2012-03-28 Nov koncept trdega spajkanja
SI201331600T SI2830817T1 (sl) 2012-03-28 2013-03-27 Nov koncept trdega spajkanja
SI201330938T SI2830820T1 (sl) 2012-03-28 2013-03-27 Nov koncept spajkanja
SI201331603T SI2830818T1 (sl) 2012-03-28 2013-03-27 Ploščni toplotni izmenjevalnik

Country Status (26)

Country Link
US (7) US10421141B2 (sl)
EP (8) EP2644312B1 (sl)
JP (8) JP6317323B2 (sl)
KR (8) KR101656164B1 (sl)
CN (7) CN104203487B (sl)
AP (5) AP2014007938A0 (sl)
AU (7) AU2013241754B2 (sl)
BR (7) BR112014023761B1 (sl)
CA (7) CA2864189C (sl)
CL (5) CL2014002510A1 (sl)
CR (5) CR20140404A (sl)
DK (5) DK2644312T3 (sl)
ES (5) ES2706986T3 (sl)
HU (2) HUE033296T2 (sl)
IL (5) IL234792A (sl)
MX (5) MX2014011231A (sl)
MY (7) MY173768A (sl)
NZ (7) NZ630078A (sl)
PH (7) PH12014502001A1 (sl)
PL (3) PL2830818T3 (sl)
PT (3) PT2830821T (sl)
RU (7) RU2585146C1 (sl)
SG (7) SG11201405953PA (sl)
SI (5) SI2644312T1 (sl)
WO (7) WO2013144210A1 (sl)
ZA (4) ZA201406337B (sl)

Families Citing this family (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ES2706986T3 (es) 2012-03-28 2019-04-02 Alfa Laval Corp Ab Nuevo concepto de soldadura fuerte
ES2756850T3 (es) 2013-09-26 2020-04-27 Alfa Laval Corp Ab Método para unir partes de metal utilizando una capa depresora del punto de fusión
EP2853332A1 (en) * 2013-09-26 2015-04-01 Alfa Laval Corporate AB A novel brazing concept
DE102014225516B3 (de) * 2014-11-21 2016-03-31 Fontaine Engineering Und Maschinen Gmbh Verfahren und Vorrichtung zum Beschichten eines Metallbandes
KR101780108B1 (ko) * 2015-06-22 2017-09-19 두산중공업 주식회사 천이 액상 확산 접합을 위한 열 교환기용 플레이트
EP3225353B1 (en) * 2016-03-31 2019-06-12 Alfa Laval Corporate AB Method for joining heat transfer plates of a plate heat exchanger
CN106736045B (zh) * 2016-12-07 2019-09-13 苏州长风航空电子有限公司 一种铠装热电偶高温硬钎焊保护剂的制备方法
SI3372937T1 (sl) 2017-03-10 2022-04-29 Alfa Laval Corporate Ab Paket plošč naprave za toplotno izmenjavo in toplotni izmenjevalnik
EP3800422B1 (en) 2017-03-10 2023-10-25 Alfa Laval Corporate AB Plate for a heat exchanger device
DK3372938T3 (da) 2017-03-10 2020-12-21 Alfa Laval Corp Ab Pladepakke ved anvendelse af en varmevekslerplade med integreret drænkanal og varmeveksler, der indbefatter en sådan pladepakke
SE541917C2 (en) * 2018-01-16 2020-01-07 Swep Int Ab Method for producing a brazed plate heat exchanger
US11065628B2 (en) 2018-07-09 2021-07-20 Kennametal Inc. Centrifuge tile assembly
SE543338C2 (en) * 2019-04-04 2020-12-08 Swep Int Ab Stencil device and method for stencil printing of brazing material onto a heat exchanger plate and use thereof
SE543405C2 (en) * 2019-05-29 2021-01-05 Alfa Laval Corp Ab Method for joining metal parts
JP7460881B2 (ja) * 2019-11-01 2024-04-03 ダイキン工業株式会社 プレート型冷媒配管、及び、冷凍装置
CN110961830B (zh) * 2019-12-13 2021-09-28 郑州机械研究所有限公司 耐磨药皮组合物、耐磨焊丝及其制备方法与应用
RU2754339C1 (ru) * 2020-12-29 2021-09-01 федеральное государственное бюджетное образовательное учреждение высшего образования "Московский государственный технический университет имени Н.Э. Баумана (национальный исследовательский университет)" (МГТУ им. Н.Э. Баумана) Металлополимерная композиция для соединения пластин паянного пластинчатого теплообменника из нержавеющей стали
SE2250767A1 (en) 2022-06-22 2023-12-23 Alfa Laval Corp Ab Plate heat exchanger
EP4343253A1 (en) 2022-09-20 2024-03-27 Alfa Laval Corporate AB Method for the assembly of a plate and fin heat exchanger and a plate and fin heat exchanger
EP4343257A1 (en) 2022-09-20 2024-03-27 Alfa Laval Corporate AB A plate heat exchanger
EP4343252A1 (en) 2022-09-20 2024-03-27 Alfa Laval Corporate AB A plate heat exchanger

Family Cites Families (108)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3073269A (en) 1957-12-24 1963-01-15 Gen Electric Metallic brazing mixture
US3457066A (en) * 1959-04-10 1969-07-22 Gen Electric Nickel base alloy
US3262762A (en) 1963-12-27 1966-07-26 Du Pont High temperature-resistant materials of aluminum, boron, carbon, nitrogen and silicon, and their preparation
SU199651A1 (ru) * 1965-12-04 1967-07-13 Всесоюзный заочный машиностроительный институт Высокотемпературной пайки стали
US3645725A (en) * 1969-05-02 1972-02-29 Armco Steel Corp Austenitic steel combining strength and resistance to intergranular corrosion
JPS5338696B2 (sl) * 1972-06-05 1978-10-17
US3839025A (en) * 1973-07-16 1974-10-01 American Metal Climax Inc High temperature alloy
US4295890A (en) * 1975-12-03 1981-10-20 Ppg Industries, Inc. Submicron beta silicon carbide powder and sintered articles of high density prepared therefrom
US4005988A (en) * 1975-12-19 1977-02-01 United Technologies Corporation Interlayer for transient liquid phase diffusion bonding
US4029476A (en) 1976-02-12 1977-06-14 A. Johnson & Co. Inc. Brazing alloy compositions
US4129462A (en) * 1977-04-07 1978-12-12 The United States Of America As Represented By The United States Department Of Energy Gamma prime hardened nickel-iron based superalloy
SU659326A1 (ru) 1977-08-22 1979-04-30 Ордена Ленина И Трудового Красного Знамени Институт Электросварки Имени Е.О.Патона Ан Украинской Сср Припой дл пайки нержавеющих жаропрочных сталей и сплавов на основе никел
US4129464A (en) * 1977-08-24 1978-12-12 Cabot Corporation High yield strength Ni-Cr-Mo alloys and methods of producing the same
FR2511908A1 (fr) * 1981-08-26 1983-03-04 Snecma Procede de brasage-diffusion destine aux pieces en superalliages
US4410604A (en) * 1981-11-16 1983-10-18 The Garrett Corporation Iron-based brazing alloy compositions and brazed assemblies with iron based brazing alloys
JPS5910491A (ja) 1982-07-08 1984-01-19 Toshihiro Aono 金属基材の接合方法
US4516716A (en) 1982-11-18 1985-05-14 Gte Products Corporation Method of brazing with iron-based and hard surfacing alloys
JPS63140781A (ja) 1986-12-01 1988-06-13 Hitachi Ltd Ｆｅ基合金接合用材料
SE458884B (sv) * 1987-05-29 1989-05-16 Alfa Laval Thermal Ab Permanent sammanfogad plattvaermevaexlare med sammanhaallande organ vid portarna
JPS6478688A (en) 1987-09-21 1989-03-24 Mitsubishi Heavy Ind Ltd Surface joining method for co or co base alloy
DE3904776A1 (de) 1989-02-17 1990-08-23 Ver Schmiedewerke Gmbh Verfahren zur herstellung eines hochfesten und zaehen metallischen schichtverbundwerkstoffes
JPH03110083A (ja) 1989-09-26 1991-05-10 Ube Ind Ltd 繊維強化金属基複合材料の板材と金属板との接合方法
US5013612A (en) * 1989-11-13 1991-05-07 Ford Motor Company Braze material for joining ceramic to metal and ceramic to ceramic surfaces and joined ceramic to metal and ceramic to ceramic article
CA2030427A1 (en) * 1989-12-19 1991-06-20 Jonathan S. Stinson Method of enhancing bond joint structural integrity of spray cast articles
JPH06234082A (ja) 1990-06-28 1994-08-23 Kankoku Kikai Kenkyusho ベースメタルより溶融温度が高い挿入材を使用した液相拡散接合方法
US5273708A (en) * 1992-06-23 1993-12-28 Howmet Corporation Method of making a dual alloy article
US5348215A (en) * 1992-11-04 1994-09-20 Kevin Rafferty Method of bonding hard metal objects
WO1995008654A1 (fr) 1993-09-24 1995-03-30 The Ishizuka Research Institute, Ltd. Materiau composite et procede pour sa production
JPH0790465A (ja) 1993-09-24 1995-04-04 Ishizuka Kenkyusho:Kk 耐火物・金属複合体およびその製法
IL118089A (en) 1995-05-22 2001-06-14 Allied Signal Inc Nickel-chrome solder alloys
US6200690B1 (en) * 1995-05-22 2001-03-13 Alliedsignal Inc. Nickel-chromium-based brazing alloys
JP3388664B2 (ja) 1995-12-28 2003-03-24 シャープ株式会社 多結晶半導体の製造方法および製造装置
US5895533A (en) 1996-02-16 1999-04-20 Japan Atomic Energy Research Institute Beryllium-copper bonding material
US6624225B1 (en) * 1996-06-03 2003-09-23 Liburdi Engineering Limited Wide-gap filler material
US5919577A (en) 1996-06-04 1999-07-06 Nippon Steel Corporation Fe-based alloy foil for liquid-phase diffusion bonding of Fe-based materials by enabling bonding in oxidizing atmospheres
SE9603486D0 (sv) * 1996-09-23 1996-09-23 Hoeganaes Ab Surface coating method
US6098871A (en) * 1997-07-22 2000-08-08 United Technologies Corporation Process for bonding metallic members using localized rapid heating
JPH11287576A (ja) 1998-03-31 1999-10-19 Hisaka Works Ltd ブレージングプレート式熱交換器
FR2781399B1 (fr) 1998-07-23 2000-08-18 Sochata Energy 1 Soc Procede de brasage-diffusion de pieces en superalliage
JP2000225491A (ja) 1999-02-05 2000-08-15 Zexel Corp アルミニウム部材のろう付け用フラックス混合物及びろう付け方法並びに熱交換器
US6403158B1 (en) * 1999-03-05 2002-06-11 General Electric Company Porous body infiltrating method
SE513784C2 (sv) 1999-03-09 2000-11-06 Alfa Laval Ab Permanent sammanfogad plattvärmeväxlare
US20040124231A1 (en) * 1999-06-29 2004-07-01 Hasz Wayne Charles Method for coating a substrate
CN1175955C (zh) 2000-04-19 2004-11-17 陈晴祺 高尔夫钎焊焊材
JP2002107089A (ja) * 2000-09-29 2002-04-10 Hisaka Works Ltd プレート式熱交換器
SE523855C2 (sv) 2000-11-10 2004-05-25 Alfa Laval Corp Ab Järnbaserat lodmaterial för sammanfogning av elememt och lödd produkt framställd härmed
US6464129B2 (en) * 2000-12-22 2002-10-15 Triumph Group, Inc. Method of diffusion bonding superalloy components
FR2822741B1 (fr) * 2001-03-29 2003-06-27 Snecma Services Poudre d'apport de brasage diffusion de piece en alliage a base de nickel, cobalt ou fer
US7146308B2 (en) * 2001-04-05 2006-12-05 Dekang Lin Discovery of inference rules from text
US6692586B2 (en) * 2001-05-23 2004-02-17 Rolls-Royce Corporation High temperature melting braze materials for bonding niobium based alloys
US7063250B2 (en) 2001-05-31 2006-06-20 Mitsubishi Heavy Industries, Ltd. Coating forming method and coating forming material, and abrasive coating forming sheet
SE524928C2 (sv) 2001-06-05 2004-10-26 Alfa Laval Corp Ab Järnbaserat lodmaterial för sammanfogning av element genom lödning samt lödd produkt framställd härmed
JP3458849B2 (ja) 2001-08-03 2003-10-20 株式会社日立製作所 コバルト基合金およびこの合金を用いた弁，原子炉プラント
JP2003053523A (ja) 2001-08-14 2003-02-26 Mitsubishi Alum Co Ltd 熱交換器およびその製造方法
US20040035910A1 (en) 2001-11-21 2004-02-26 Dockus Kostas F. Low temperature fluxless brazing
US7015451B2 (en) 2002-01-25 2006-03-21 Masimo Corporation Power supply rail controller
JP3866119B2 (ja) 2002-03-01 2007-01-10 トライアンフ グループ、 インク 超合金部品の拡散接合方法
US20030200835A1 (en) * 2002-04-02 2003-10-30 Snecma Services Diffusion-brazing filler powder for parts made of an alloy based on nickel, cobalt or iron
US8776371B2 (en) * 2002-05-03 2014-07-15 Alfa Laval Corporate Ab Method of brazing thin heat exchanging plates and brazed plate heat exchanger produced according to the method
FR2840839B1 (fr) 2002-06-14 2005-01-14 Snecma Moteurs Materiau metallique susceptible d'etre use par abrasion; pieces, carter; procede d'elaboration dudit materiau
EP1572415B1 (en) 2002-12-13 2006-07-26 Corus Aluminium Walzprodukte GmbH Brazing sheet product having a clad layer and a coated layer of iron alloy and method of its manufacture
US7182884B2 (en) * 2003-01-30 2007-02-27 Mitsuru Akashi Bio-liquid crystal polymer and shaped material using same
CN1764614A (zh) 2003-02-07 2006-04-26 戴蒙得创新股份有限公司 预置铜焊合金的金刚石工具镶件及其制造方法
US20050067061A1 (en) * 2003-09-26 2005-03-31 General Electric Company Nickel-based braze alloy compositions and related processes and articles
SE527509C2 (sv) * 2003-10-17 2006-03-28 Alfa Laval Corp Ab Lödd plattvärmeväxlare med plattor av i huvudsak rostfritt stål och förfarande för tillverkning av en sådan plattvärmeväxlare
US7222422B2 (en) * 2004-02-16 2007-05-29 General Electric Company Method for refurbishing surfaces subjected to high compression contact
US7565996B2 (en) * 2004-10-04 2009-07-28 United Technologies Corp. Transient liquid phase bonding using sandwich interlayers
US20060090820A1 (en) 2004-11-01 2006-05-04 Metglas, Inc. Iron-based brazing filler metals
US7335427B2 (en) 2004-12-17 2008-02-26 General Electric Company Preform and method of repairing nickel-base superalloys and components repaired thereby
SE529913C2 (sv) * 2005-05-26 2008-01-08 Alfa Laval Corp Ab Förfarande för lödning av föremål av rostfritt stål, förfarande för lödning av värmeväxlare av rostfritt stål samt lött föremål samt lödd värmeväxlare
DK2446996T3 (en) * 2005-05-26 2017-07-24 Alfa Laval Corp Ab STAINLESS STEEL HEAT EXCHANGE OF STAINLESS STEEL WITH STAINLESS STEEL HEADWARE MATERIAL
DE102006013503A1 (de) 2006-03-23 2008-01-24 Esk Ceramics Gmbh & Co. Kg Plattenwärmetauscher, Verfahren zu dessen Herstellung und dessen Verwendung
JP2008006480A (ja) 2006-06-30 2008-01-17 Sumitomo Light Metal Ind Ltd 熱交換器用ブレージングフィン材並びに熱交換器及びその製造方法
US7326892B1 (en) * 2006-09-21 2008-02-05 General Electric Company Process of microwave brazing with powder materials
SE530724C2 (sv) 2006-11-17 2008-08-26 Alfa Laval Corp Ab Lodmaterial, förfarande för att löda med detta lodmaterial, lött föremål framställt med förfarandet samt lodpasata innefattande lodmaterialet
SE531988C2 (sv) 2006-11-17 2009-09-22 Alfa Laval Corp Ab Lodmaterial samt förfarande för lödning med detta material
US7775416B2 (en) * 2006-11-30 2010-08-17 General Electric Company Microwave brazing process
JP5509597B2 (ja) 2006-12-28 2014-06-04 Ｊｓｒ株式会社 耐油耐候性ゴム用組成物及びゴム成形体
GB0704817D0 (en) 2007-03-13 2007-04-18 Jarvis Rail Ltd Railbond
US20110180199A1 (en) * 2007-04-17 2011-07-28 United Technologies Corporation Powder -metallurgy braze preform and method of use
JP2009031545A (ja) * 2007-07-27 2009-02-12 Seiko Epson Corp プロジェクタ
US20090026182A1 (en) 2007-07-27 2009-01-29 Honeywell International, Inc. In-situ brazing methods for repairing gas turbine engine components
US8491837B2 (en) * 2007-09-03 2013-07-23 Ihi Corporation Ni-based brazing composition, braze repair method, and braze-repair structure
JP5152727B2 (ja) * 2007-12-21 2013-02-27 ハリマ化成株式会社 アルミニウムろう付け用ペースト組成物
JP2009192191A (ja) 2008-02-18 2009-08-27 Hitachi Cable Ltd 熱交換器及びその製造方法
JP5642061B2 (ja) * 2008-03-19 2014-12-17 ホガナス アクチボラグ （パブル） 鉄−クロム系鑞材
SI2257758T1 (sl) * 2008-04-04 2014-10-30 Alfa Laval Corporate Ab Ploĺ äśati toplotni izmenjevalec
JP2009269043A (ja) * 2008-05-01 2009-11-19 Mitsubishi Alum Co Ltd 耐湿ろう付性に優れるアルミニウム合金ろう付用塗料、ろう付用アルミニウム合金板及びそれを用いた自動車熱交換器用アルミニウム合金部材、並びに自動車熱交換器
JP4716269B2 (ja) 2008-05-02 2011-07-06 サーモス株式会社 真空構造体の封止方法
US8087565B2 (en) * 2008-09-08 2012-01-03 General Electric Company Process of filling openings in a component
JP2010104999A (ja) 2008-10-28 2010-05-13 Hitachi Cable Ltd ろう付け用複合材及びろう付け製品
RU2528939C2 (ru) * 2008-11-25 2014-09-20 Солвей Флуор Гмбх Антикоррозийный флюс
US9186742B2 (en) * 2009-01-30 2015-11-17 General Electric Company Microwave brazing process and assemblies and materials therefor
US20100215983A1 (en) 2009-02-20 2010-08-26 Kennametal Inc. Brazed Claddings for Cast Iron Substrates
CN101566271B (zh) 2009-05-19 2013-03-27 山东大学 一种金属陶瓷复合耐磨材料及其制备方法
JP5003983B2 (ja) 2009-09-07 2012-08-22 独立行政法人日本原子力研究開発機構 二層ろう接による積層構造強化法
DE102010016367A1 (de) * 2010-04-08 2011-10-13 Vacuumschmelze Gmbh & Co. Kg Hartgelöteter Gegenstand und Verfahren zum Hartlöten zweier oder mehrerer Teile
JP5623783B2 (ja) 2010-05-13 2014-11-12 日本発條株式会社 大気接合用ろう材、接合体、および、集電材料
JP5516075B2 (ja) 2010-05-26 2014-06-11 三菱電機株式会社 プレート式熱交換器
JP5675186B2 (ja) 2010-06-23 2015-02-25 三菱重工業株式会社 接合品の製造方法、及び燃焼器の製造方法
KR100992961B1 (ko) 2010-07-30 2010-11-08 주식회사 동화엔텍 플레이트형 열교환기 제조방법
JP2012052160A (ja) 2010-08-31 2012-03-15 Mitsubishi Alum Co Ltd ろう付性に優れるフラックスレスろう付用部材およびアルミニウム材のフラックスレスろう付け方法
JP5619538B2 (ja) * 2010-09-06 2014-11-05 株式会社ティラド 細流路インナーフィンを有する熱交換器のフラックスレスろう付け方法およびそれに用いるアルミニウムクラッド材
JP5645307B2 (ja) 2010-12-09 2014-12-24 日本発條株式会社 大気接合用ろう材、接合体、および、集電材料
CN102120281A (zh) * 2011-02-15 2011-07-13 洛阳双瑞精铸钛业有限公司 一种钛铝材质涡轮增压器转子与钢轴的钎焊方法
EP2607332A1 (de) * 2011-12-19 2013-06-26 Sika Technology AG Abbindebeschleuniger für Bindemittel auf Basis von Calciumsulfat
ES2706986T3 (es) 2012-03-28 2019-04-02 Alfa Laval Corp Ab Nuevo concepto de soldadura fuerte
ES2756850T3 (es) * 2013-09-26 2020-04-27 Alfa Laval Corp Ab Método para unir partes de metal utilizando una capa depresora del punto de fusión

Also Published As

Publication number Publication date
JP6444960B2 (ja) 2018-12-26
AU2013241804B2 (en) 2015-06-18
PT2830820T (pt) 2018-03-12
PT2830821T (pt) 2017-03-01
KR101627446B1 (ko) 2016-06-03
CA2868674C (en) 2019-03-19
EP2830817B1 (en) 2019-08-28
SG11201405953PA (en) 2014-11-27
SG11201406090TA (en) 2014-11-27
CA2868635C (en) 2019-08-20
IL234791A (en) 2017-01-31
MX2014011231A (es) 2014-11-10
ES2617219T3 (es) 2017-06-15
RU2592331C2 (ru) 2016-07-20
US20150093188A1 (en) 2015-04-02
MX2014010903A (es) 2014-10-15
AU2013241754B2 (en) 2015-06-04
US9694434B2 (en) 2017-07-04
EP2830820B1 (en) 2018-01-10
PH12014502127A1 (en) 2014-12-10
RU2585888C2 (ru) 2016-06-10
CN104203487A (zh) 2014-12-10
IL234793A (en) 2017-09-28
BR112014023761B1 (pt) 2018-07-24
EP2644312B1 (en) 2018-10-31
CA2868227A1 (en) 2013-10-03
CN104302439A (zh) 2015-01-21
CL2014002567A1 (es) 2015-01-16
CN104185532A (zh) 2014-12-03
AP2014007944A0 (en) 2014-09-30
AP2014007939A0 (en) 2014-09-30
CA2868635A1 (en) 2013-10-03
US9694435B2 (en) 2017-07-04
JP6042458B2 (ja) 2016-12-14
CL2014002509A1 (es) 2015-01-16
NZ629124A (en) 2016-06-24
EP2830820A1 (en) 2015-02-04
JP2015518555A (ja) 2015-07-02
US9849534B2 (en) 2017-12-26
EP2830816B1 (en) 2019-11-13
SG11201406138TA (en) 2014-11-27
RU2014142883A (ru) 2016-05-20
KR20140129275A (ko) 2014-11-06
EP2830821B1 (en) 2016-12-28
WO2013144308A1 (en) 2013-10-03
ZA201406628B (en) 2016-08-31
EP2830816A1 (en) 2015-02-04
NZ630078A (en) 2016-10-28
EP2830818A1 (en) 2015-02-04
NZ629673A (en) 2016-09-30
WO2013144251A1 (en) 2013-10-03
HUE033296T2 (en) 2017-11-28
ZA201406337B (en) 2017-08-30
IL234790A (en) 2017-03-30
AU2013241815B2 (en) 2015-07-02
ES2755278T3 (es) 2020-04-22
PL2830818T3 (pl) 2020-03-31
KR20170005892A (ko) 2017-01-16
CL2014002566A1 (es) 2015-01-16
AU2013241809B2 (en) 2015-06-18
ES2706986T3 (es) 2019-04-02
CR20140447A (es) 2014-11-11
SG11201406089XA (en) 2014-11-27
EP2830818B1 (en) 2019-09-04
WO2013144210A1 (en) 2013-10-03
EP2830815A1 (en) 2015-02-04
HUE037304T2 (hu) 2018-08-28
CN104302439B (zh) 2017-04-12
SI2830817T1 (sl) 2019-12-31
NZ629346A (en) 2015-08-28
PH12014502128B1 (en) 2014-12-10
DK2830818T3 (da) 2019-12-09
PH12014502001B1 (en) 2014-11-24
BR112014021587B1 (pt) 2018-05-15
SI2830818T1 (sl) 2019-12-31
US20150030837A1 (en) 2015-01-29
IL234792A (en) 2017-02-28
SI2830820T1 (sl) 2018-03-30
DK2830821T3 (en) 2017-04-10
US20150044501A1 (en) 2015-02-12
JP6121519B2 (ja) 2017-04-26
RU2014143253A (ru) 2016-05-20
CA2868633A1 (en) 2013-10-03
RU2585146C1 (ru) 2016-05-27
JP6317323B2 (ja) 2018-04-25
PH12014502001A1 (en) 2014-11-24
PH12014502000B1 (en) 2014-11-24
PL2830821T3 (pl) 2017-05-31
KR101692599B1 (ko) 2017-01-03
MY183524A (en) 2021-02-24
DK2644312T3 (en) 2019-02-25
PH12014502120A1 (en) 2014-12-10
CA2868674A1 (en) 2013-10-03
ES2661872T3 (es) 2018-04-04
KR20140129237A (ko) 2014-11-06
PH12014502018A1 (en) 2014-11-24
JP2017080812A (ja) 2017-05-18
KR101634477B1 (ko) 2016-06-28
WO2013144222A1 (en) 2013-10-03
JP2015517913A (ja) 2015-06-25
ZA201406626B (en) 2016-08-31
BR112014023755B1 (pt) 2018-08-28
MX2014010976A (es) 2014-10-06
US20150034286A1 (en) 2015-02-05
MY174995A (en) 2020-06-01
MY168027A (en) 2018-10-11
MX360752B (es) 2018-11-15
KR20140129236A (ko) 2014-11-06
SI2644312T1 (sl) 2019-01-31
RU2014143186A (ru) 2016-05-20
CA2864958A1 (en) 2013-10-03
SG11201406135YA (en) 2014-11-27
CL2014002510A1 (es) 2015-01-16
CN104185533B (zh) 2017-05-17
CR20140448A (es) 2014-11-11
WO2013144211A1 (en) 2013-10-03
RU2014143279A (ru) 2016-05-20
JP2015518425A (ja) 2015-07-02
KR20140130714A (ko) 2014-11-11
MY169213A (en) 2019-03-18
DK2830816T3 (en) 2020-02-17
PH12014502120B1 (en) 2014-12-10
JP6198811B2 (ja) 2017-09-20
PH12014502127B1 (en) 2014-12-10
KR101660617B1 (ko) 2016-09-27
PL2830820T3 (pl) 2018-04-30
US20150044507A1 (en) 2015-02-12
EP2830821A1 (en) 2015-02-04
EP2644312A1 (en) 2013-10-02
JP2015514016A (ja) 2015-05-18
PH12014502119A1 (en) 2014-12-10
PH12014502000A1 (en) 2014-11-24
PH12014502119B1 (en) 2014-12-10
AP2014007938A0 (en) 2014-09-30
CA2868227C (en) 2017-03-21
AU2013241754A1 (en) 2014-09-04
CL2014002544A1 (es) 2015-01-16
BR112014023758B1 (pt) 2018-12-04
CN104203487B (zh) 2018-07-06
MY168502A (en) 2018-11-12
AU2013241720A1 (en) 2014-09-04
US10421141B2 (en) 2019-09-24
US20150086776A1 (en) 2015-03-26
NZ630086A (en) 2016-06-24
AU2013241809A1 (en) 2014-10-16
KR102071484B1 (ko) 2020-01-30
KR20140129273A (ko) 2014-11-06
WO2013144216A1 (en) 2013-10-03
CN104302440A (zh) 2015-01-21
JP2015517914A (ja) 2015-06-25
CR20140446A (es) 2014-11-11
US10112249B2 (en) 2018-10-30
MX2014010902A (es) 2014-10-15
CN104203489A (zh) 2014-12-10
KR20140121891A (ko) 2014-10-16
EP2830817A1 (en) 2015-02-04
RU2602693C2 (ru) 2016-11-20
CA2864189C (en) 2017-02-14
CN104185532B (zh) 2017-04-26
JP2015513656A (ja) 2015-05-14
US10131011B2 (en) 2018-11-20
MY173768A (en) 2020-02-19
BR112014023770B1 (pt) 2018-10-16
CA2867427A1 (en) 2013-10-03
BR112014023762B1 (pt) 2019-02-05
KR101656164B1 (ko) 2016-09-08
JP6139657B2 (ja) 2017-05-31
AU2013241804A1 (en) 2014-10-09
AU2013241720B2 (en) 2015-10-22
EP2830819A1 (en) 2015-02-04
CN104185533A (zh) 2014-12-03
MY172129A (en) 2019-11-14
CR20140445A (es) 2014-11-11
IL234789A (en) 2017-02-28
AP2014007923A0 (en) 2014-09-30
BR112014021589B1 (pt) 2018-09-11
NZ627987A (en) 2017-04-28
US20150060030A1 (en) 2015-03-05
CA2864958C (en) 2016-10-18
ES2754307T3 (es) 2020-04-16
PT2830818T (pt) 2019-11-22
RU2583204C1 (ru) 2016-05-10
SG11201405793YA (en) 2014-11-27
SG11201406140RA (en) 2014-11-27
PH12014502128A1 (en) 2014-12-10
CA2864189A1 (en) 2013-10-03
AU2013241868A1 (en) 2014-10-16
CN104203488A (zh) 2014-12-10
CN104203489B (zh) 2018-04-06
JP2015514017A (ja) 2015-05-18
DK2830820T3 (en) 2018-04-16
RU2581937C1 (ru) 2016-04-20
ZA201406436B (en) 2016-05-25
CR20140404A (es) 2014-11-26
MX2014010904A (es) 2014-10-15
CN104302440B (zh) 2017-12-15
RU2585886C2 (ru) 2016-06-10
US10335881B2 (en) 2019-07-02
AU2013241803A1 (en) 2014-10-16
AU2013241815A1 (en) 2014-10-16
AU2013241868B2 (en) 2015-07-09
CA2867427C (en) 2020-04-07
CN104203488B (zh) 2017-09-12
JP6117332B2 (ja) 2017-04-19
AP2014007929A0 (en) 2014-09-30
AU2013241803B2 (en) 2015-07-09
NZ628064A (en) 2017-04-28
KR101627447B1 (ko) 2016-06-03
KR20140129272A (ko) 2014-11-06
WO2013144194A1 (en) 2013-10-03
CA2868633C (en) 2019-07-09

Similar Documents

Publication Publication Date Title
ZA201406337B (en) Method for joining metal parts
ZA201501833B (en) Method for obtaining 1-kestone
EP2823926A4 (en) WELDING METHOD
IL243428A0 (en) A method for combining metal parts
HUE062051T2 (hu) Eljárás sajtolva keményített acél darabok gyártására
HUP1200540A2 (en) Method for welding simulation
PL2529856T3 (pl) Zespoły części metalowych i sposób ich wytwarzania
EP2839906A4 (en) PROCESS FOR PRODUCING METALLIC POWDER
EP2896476A4 (en) METHOD FOR MANUFACTURING METALLIC MICROPARTICLES
EP2692474A4 (en) PROCESS FOR MARKING METAL ELEMENT
EP2821174A4 (en) PROCESS FOR ASSEMBLING METALLIC MATERIALS
EP2800801A4 (en) LUBRICATING GREASE AND METHOD OF APPLYING THE LUBRICANT
HUE038597T2 (hu) Eljárás vezetékek hegesztésére
EP2896474A4 (en) METHOD FOR MANUFACTURING METAL MICROPARTICLES
EP2868419A4 (en) SPOT WELDING PROCESS
ZA201503479B (en) Improved method for metal production
EP2880048A4 (en) METHOD
GB201202198D0 (en) Method
PT2785310T (pt) Método para fotodepilação melhorada com base em nanocomplexos metálicos
EP2835206A4 (en) WELDING METHOD
SG2013088851A (en) Machining method
EP2811038A4 (en) PROCESS FOR SLAG REDUCTION
ZA201307383B (en) Metal separation method
GB201104302D0 (en) Metal joints
GB201210147D0 (en) Method